CN103930534B - 变速机用润滑油组合物 - Google Patents
变速机用润滑油组合物 Download PDFInfo
- Publication number
- CN103930534B CN103930534B CN201280056146.7A CN201280056146A CN103930534B CN 103930534 B CN103930534 B CN 103930534B CN 201280056146 A CN201280056146 A CN 201280056146A CN 103930534 B CN103930534 B CN 103930534B
- Authority
- CN
- China
- Prior art keywords
- quality
- oil
- kinematic viscosity
- variable
- speed motor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
变速机用润滑油组合物，其特征在于，配合有1质量%以上且80质量%以下的40℃运动粘度为0.5mm2/s以上且20mm2/s以下、粘度指数为200以上的基础油。根据本组合物，由于粘度指数高、进而具有高剪切稳定性，因而适宜作为无级变速机用。
Description
技术领域
本发明涉及变速机用润滑油组合物。
背景技术
近年来，作为可用于汽车等中的变速机，开发了金属带式和环式的无级变速机，并已被实用化。这类无级变速机中使用的润滑油为了提高省燃耗性而谋求低粘度化和高粘度指数化。另一方面，对于初期粘度低的润滑油，由于容易受到剪切所致的粘度降低的影响，因而期望剪切所致的粘度降低小。
因此，提出了通过使用粘度较高的基础油并与难以受到剪切的粘度指数改进剂并用来使省燃耗性和剪切稳定性平衡的润滑油。例如，专利文献1～3中公开了通过提高基础油粘度、使用低分子量的PMA（聚甲基丙烯酸酯）或OCP（烯烃共聚物）而使剪切所致的粘度降低减小的润滑油组合物。
现有技术文献
专利文献
专利文献1：日本特开2006-117852号公报
专利文献2：日本特开2001-262176号公报
专利文献3：日本特开2008-37963号公报。
发明内容
发明要解决的技术问题
近年来，无级变速机中使用的润滑油为了提高省燃耗性而开展高粘度指数化，进而为了确保泵排出压力也需求高剪切稳定性。然而，专利文献1～3中公开的润滑油中，粘度指数均不怎么提高，特别是低温行驶时的燃耗改善困难。另外，若添加分子量大的粘度指数改进剂，则剪切所致的粘度降低变大。
本发明的目的在于提供初期粘度指数高、且兼具高的剪切稳定性的变速机用润滑油组合物。
用于解决技术问题的手段
为了解决前述课题，本发明提供如下述的变速机用润滑油组合物。
（1）变速机用润滑油组合物，其特征在于，配合有1质量%以上且80质量%以下的40℃运动粘度为0.5mm2/s以上且20mm2/s以下的基础油，粘度指数为200以上。
（2）上述本发明的变速机用润滑油组合物，其特征在于，100℃运动粘度为0.5mm2/s以上且10mm2/s以下。
（3）上述本发明的变速机用润滑油组合物，其特征在于，进一步配合有100℃运动粘度为50mm2/s以上且200mm2/s以下的聚α烯烃。
（4）上述本发明的变速机用润滑油组合物，其特征在于，进一步含有耐磨损剂、极压剂、摩擦调节剂和粘度指数改进剂的至少任一种。
（5）上述本发明的变速机用润滑油组合物，其特征在于，用于无级变速机。
根据本发明，可以提供初期粘度指数高、且兼具高的剪切稳定性的变速机用润滑油组合物。因此，本发明的变速机用润滑油组合物特别适宜作为无级变速机（CVT：Continuously Variable Transmission）用。
具体实施方式
本发明的变速机用润滑油组合物（以下，也简称为“本组合物”）的特征在于，配合有1质量%以上且80质量%以下的40℃运动粘度为0.5mm2/s以上且20mm2/s以下、粘度指数为200以上的基础油。以下，对本组合物进行详细说明。
作为本组合物的基础油，使用40℃运动粘度为0.5mm2/s以上且20mm2/s以下的基础油。40℃运动粘度若小于0.5mm2/s，则润滑性不足，40℃运动粘度若超过20mm2/s，则省燃耗性差。
作为这类基础油，可以是矿物油也可以是合成油。对这些基础油的种类没有特别限制，可以从以往作为汽车用变速机用润滑油的基础油使用的矿物油和合成油中适宜选择任意种类使用。
作为矿物油系基础油，可举出例如，石蜡基系矿物油、中间基系矿物油、萘基系矿物油。另外，作为合成系基础油，可举出例如，聚α烯烃（PAO）、聚丁烯、多元醇酯、二元酸酯、磷酸酯、聚苯醚、聚乙二醇、烷基苯、和烷基萘等。作为上述PAO，可举出例如，α-烯烃均聚物、α-烯烃共聚物。这些基础油可以单独使用1种，也可以组合2种以上使用。
另外，上述矿物油系基础油中，作为低粘度的基础油，可适宜使用灯油或轻油。
本组合物的特征在于，配合有以组合物总量基准计为1质量%以上且80质量%以下的上述基础油。
这里，基础油的配合比例若小于1质量%，则无法充分发挥本发明的效果。另一方面，基础油的配合比例若超过80质量%，则聚合物的添加量减小、粘度指数降低，故不优选。因此，基础油的配合比例优选为10质量%以上且70质量%以下、更优选为30质量%以上且70质量%以下，进一步优选为50质量%以上且70质量%以下。
另外，本组合物的100℃运动粘度优选为0.5mm2/s以上且10mm2/s以下。
本组合物的100℃运动粘度若小于0.5mm2/s，则润滑性可能变得不足。另一方面，本组合物的100℃运动粘度若超过10mm2/s，则省燃耗性可能降低。因此，本组合物的100℃运动粘度更优选为3mm2/s以上且9mm2/s以下、进一步优选为5mm2/s以上且8mm2/s以下。
本组合物的特征在于，配合有规定量的上述基础油，粘度指数为200以上。
粘度指数若小于200，则即使剪切稳定性高，润滑油的粘度的温度依赖性也变高，在实际使用上存在问题。因此，本组合物的粘度指数优选为210以上、更优选为220以上。
为了使粘度指数为200以上，可以使用高粘度指数的基础油，但有效的是配合粘度指数改进剂（VII：Viscosity Index Improver）。作为粘度指数改进剂，可举出例如，非分散型聚甲基丙烯酸酯、分散型聚甲基丙烯酸酯、烯烃系共聚物、分散型烯烃系共聚物、苯乙烯系共聚物。这些粘度指数改进剂的质量平均分子量，例如对于分散型和非分散型聚甲基丙烯酸酯来说，优选为5000以上且300000以下。另外，对于烯烃系共聚物来说，优选为800以上且100000以下。它们可以单独使用1种、也可以组合2种以上使用。
粘度指数改进剂的配合量没有特别限定，以组合物总量基准计，优选为0.5质量%以上且15质量%以下、更优选为1质量%以上且10质量%以下。
本组合物中，优选配合100℃运动粘度为50mm2/s以上且200mm2/s以下的聚α烯烃（高粘度PAO）。
通过配合这类高粘度（高分子量）的PAO，变得容易调整润滑油组合物的最终粘度。另外，通过配合高粘度的PAO，也有助于改进作为组合物的粘度指数。其中，配合的PAO的100℃运动粘度若小于50mm2/s，则即使剪切稳定性高，润滑油的粘度的温度依赖性也变高，在实际使用上存在问题。另外，配合的PAO的100℃运动粘度若超过200mm2/s，则组合物整体的粘度过度上升，省燃耗性可能降低。因此，配合的PAO的100℃运动粘度更优选为65mm2/s以上且180mm2/s以下，进一步优选为80mm2/s以上且150mm2/s以下。
另外，以组合物总量基准计，上述的PAO的配合量优选为5质量%以上且30质量%以下、更优选为7质量%以上且25质量%以下。
在不阻碍发明效果的范围内，还可以对本组合物配合以下所示的各种添加剂。具体地，可以适宜配合倾点降低剂（PPD：Pour Point Depressant）、耐磨损剂、极压剂、清洁分散剂和摩擦调节剂等使用。
作为倾点降低剂，可举出例如，质量平均分子量为5000以上且50000以下的聚甲基丙烯酸酯（PMA）。它们可以单独使用1种、也可以组合2种以上使用。倾点降低剂的配合量没有特别限定，以组合物总量基准计，优选为0.1质量%以上且2质量%以下、更优选为0.1质量%以上且1质量%以下。
作为耐磨损剂和极压剂，可举出例如，硫系化合物和磷系化合物。作为硫系化合物，可举出例如，硫化烯烃、硫化油脂、硫化酯、硫代碳酸酯类、二硫代氨基甲酸酯类、多硫化物类。作为磷系化合物，可举出例如，亚磷酸酯类、磷酸酯类、膦酸酯类、和它们的胺盐或金属盐。它们可以单独使用1种、也可以组合2种以上使用。
这些耐磨损剂・极压剂的配合量没有特别限定，以组合物总量基准计，优选为0.1质量%以上且20质量%以下。
作为清洁分散剂，可以使用无灰系分散剂或金属系清洁剂。
作为无灰系分散剂，可举出例如，琥珀酰亚胺化合物、硼系酰亚胺化合物、曼尼希(Mannich)系分散剂、酰胺系化合物。它们可以单独使用1种、也可以组合2种以上使用。无灰系分散剂的配合量没有特别限定，以组合物总量基准计，优选为0.1质量%以上且20质量%以下。
作为金属系清洁剂，可举出例如，碱金属磺酸盐、碱金属苯酚盐、碱金属水杨酸盐、碱金属萘酸盐、碱土类金属磺酸盐、碱土类金属苯酚盐、碱土类金属水杨酸盐、碱土类金属萘酸盐。它们可以单独使用1种、也可以组合2种以上使用。金属系清洁剂的配合量没有特别限定，以组合物总量基准计，优选为0.1质量%以上且10质量%以下。
作为摩擦调节剂，可举出例如，脂肪酸酯、脂肪酰胺、脂肪酸、脂肪族醇、脂肪族胺、脂肪族醚。具体可举出：分子中具有至少1个碳原子数6至30的烷基或烯基的摩擦调节剂。例如，可优选使用油酸或油胺。它们可以单独使用1种、也可以组合2种以上使用。
摩擦调节剂的配合量没有特别限定，以组合物总量基准计，优选为0.01质量%以上且2质量%以下、更优选为0.01质量%以上且1质量%以下。
实施例
接着，列举实施例和比较例进一步详细进行说明，但本发明并不受这些记载内容的任何限制。
〔实施例1～10、比较例1～2〕
以表1所示的配合制备各润滑油组合物，作为试样油。另外，通过下述方法求出各试样油的性状和性能。
（1）闪点：
依照JIS K 2265进行测定。
（2）运动粘度（40℃、100℃）和粘度指数：
依照JIS K 2283进行测定。
（3）BF粘度：
依照JPI-5S-26-85进行测定。
（4）超声波剪切稳定度试验（Sonic Test）：
依照JPI-5S-29-88进行测定（测定温度：40℃和100℃、照射时间：1小时）。表1中示出Sonic Test前后的运动粘度和粘度指数。
[表1]
・灯油A
使用市售品（闪点：44℃、40℃运动粘度：0.892mm2/s）。
・灯油B
使用市售品（闪点：42℃、40℃运动粘度：0.987mm2/s）。
・灯油C
使用市售品（闪点：84℃、40℃运动粘度：1.621mm2/s）。
・轻油
使用市售品（闪点：84℃、40℃运动粘度：1.660mm2/s、100℃运动粘度：0.805mm2/s、粘度指数：30）。
・异链烷烃
使用异链烷烃系基础油（闪点：87℃、40℃运动粘度：2.560mm2/s）。
・链烷烃A
使用链烷烃系基础油（闪点：101℃、40℃运动粘度：2.166mm2/s）。
・链烷烃B
使用链烷烃系基础油（闪点：138℃、40℃运动粘度：4.320mm2/s、100℃运动粘度：1.540mm2/s、粘度指数：83）。
・低分子量PAO
使用市售品（闪点：156℃、40℃运动粘度：5.100mm2/s、100℃运动粘度：1.800mm2/s、粘度指数：128）。
・低粘度基础油
使用API II类的基础油（闪点：170℃、40℃运动粘度：7.680mm2/s、100℃运动粘度：2.278mm2/s、粘度指数：108）。
・高粘度基础油A
使用API II类的基础油（闪点：212℃、40℃运动粘度：20.500mm2/s、100℃运动粘度：4.500mm2/s、粘度指数：116）。
・高粘度基础油B
使用API II类的基础油（闪点：222℃、40℃运动粘度：30.600mm2/s、100℃运动粘度：5.200mm2/s、粘度指数：104）。
・高分子量PAO
使用市售品（闪点：283℃、40℃运动粘度：1240mm2/s、100℃运动粘度：100.0mm2/s、粘度指数：170）。
・粘度指数改进剂（VII）
聚甲基丙烯酸酯（Mw：30，000）
聚甲基丙烯酸酯（Mw：160，000）
・其它添加剂
使用将极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装（additive
package）。
〔评价结果〕
实施例1～10的本发明的试样油的初期粘度指数均超过200，显示出优异的初期性状，并且在Sonic
Test后运动粘度和粘度指数也基本未降低。这表明本发明的试样油的剪切稳定性极其优异，可以长时间稳定使用。另外，可知BF粘度也低、低温特性优异。
另一方面，比较例1～2的试样油由于未配合本发明规定的低粘度基础油，因而不仅初期粘度指数低，进而剪切稳定性也差。另外，低温特性也差。
应予说明，实施例1～4中，即使使用灯油、轻油等闪点低的基础油，也可使最终的闪点为100℃以上，可耐受充分使用。
Claims (41)
1.变速机用润滑油组合物，其特征在于，配合有1质量%以上且80质量%以下的40℃运动粘度为0.5mm2/s以上且20mm2/s以下的基础油、5质量%以上且30质量%以下的100℃运动粘度为50mm2/s以上且200mm2/s以下的聚α烯烃和质量平均分子量为5000以上且300000以下的非分散型或分散型聚甲基丙烯酸酯作为粘度指数改进剂，粘度指数为220以上，所述润滑油组合物的100℃运动粘度为6.985mm2/s以上且10mm2/s以下。
2.权利要求1所述的变速机用润滑油组合物，其特征在于，100℃运动粘度为6.985mm2/s以上且7.537mm2/s以下。
3.权利要求1或2所述的变速机用润滑油组合物，其特征在于，进一步含有耐磨损剂、极压剂、摩擦调节剂、和粘度指数改进剂的至少任一种。
4.权利要求1或2所述的变速机用润滑油组合物，其特征在于，用于无级变速机。
5.权利要求1所述的变速机用润滑油组合物，其特征在于，所述基础油为矿物油系基础油和合成系基础油中的至少任一者。
6.权利要求5所述的变速机用润滑油组合物，其特征在于，所述矿物油系基础油为石蜡基系矿物油、中间基系矿物油、和萘基系矿物油中的至少任一者。
7.权利要求5所述的变速机用润滑油组合物，其特征在于，所述矿物油系基础油为灯油和轻油中的任一者。
8.权利要求5所述的变速机用润滑油组合物，其特征在于，所述合成系基础油为聚α烯烃（PAO）、聚丁烯、多元醇酯、二元酸酯、磷酸酯、聚苯醚、聚乙二醇、烷基苯、和烷基萘中的至少任一者。
9.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有以组合物总量基准计为10质量%以上且70质量%以下的所述基础油。
10.权利要求9所述的变速机用润滑油组合物，其特征在于，配合有以组合物总量基准计为30质量%以上且70质量%以下的所述基础油。
11.权利要求10所述的变速机用润滑油组合物，其特征在于，配合有以组合物总量基准计为50质量%以上且70质量%以下的所述基础油。
12.权利要求1所述的变速机用润滑油组合物，其特征在于，100℃运动粘度为6.985mm2/s以上且9mm2/s以下。
13.权利要求12所述的变速机用润滑油组合物，其特征在于，100℃运动粘度为6.985mm2/s以上且8mm2/s以下。
14.权利要求1所述的变速机用润滑油组合物，其特征在于，所述粘度指数改进剂的配合量以组合物总量基准计为0.5质量%以上且15质量%以下。
15.权利要求14所述的变速机用润滑油组合物，其特征在于，所述粘度指数改进剂的配合量以组合物总量基准计为1质量%以上且10质量%以下。
16.权利要求1所述的变速机用润滑油组合物，其特征在于，所述聚α烯烃的100℃运动粘度为65mm2/s以上且180mm2/s以下。
17.权利要求16所述的变速机用润滑油组合物，其特征在于，所述聚α烯烃的100℃运动粘度为80mm2/s以上且150mm2/s以下。
18.权利要求1所述的变速机用润滑油组合物，其特征在于，所述聚α烯烃的配合量以组合物总量基准计为7质量%以上且25质量%以下。
19.权利要求1所述的变速机用润滑油组合物，其特征在于，进一步配合有倾点降低剂，
所述倾点降低剂是质量平均分子量为5000以上且50000以下的聚甲基丙烯酸酯。
20.权利要求1所述的变速机用润滑油组合物，其特征在于，进一步配合有倾点降低剂，
所述倾点降低剂的配合量以组合物总量基准计为0.1质量%以上且2质量%以下。
21.权利要求20所述的变速机用润滑油组合物，其特征在于，所述倾点降低剂的配合量以组合物总量基准计为0.1质量%以上且1质量%以下。
22.权利要求3所述的变速机用润滑油组合物，其特征在于，所述耐磨损剂和所述极压剂是硫化烯烃、硫化油脂、硫化酯、硫代碳酸酯类、二硫代氨基甲酸酯类、多硫化物类、亚磷酸酯类、磷酸酯类、和膦酸酯类中的至少任一者。
23.权利要求3所述的变速机用润滑油组合物，其特征在于，所述耐磨损剂和所述极压剂的配合量以组合物总量基准计为0.1质量%以上且20质量%以下。
24.权利要求3所述的变速机用润滑油组合物，其特征在于，所述摩擦调节剂为脂肪酸酯、脂肪酰胺、脂肪酸、脂肪族醇、脂肪族胺、和脂肪族醚中的至少任一者。
25.权利要求24所述的变速机用润滑油组合物，其特征在于，所述摩擦调节剂是分子中具有至少1个碳原子数6至30的烷基或烯基的摩擦调节剂。
26.权利要求25所述的变速机用润滑油组合物，其特征在于，所述摩擦调节剂为油酸和油胺中的至少任一者。
27.权利要求3所述的变速机用润滑油组合物，其特征在于，所述摩擦调节剂的配合量以组合物总量基准计为0.01质量%以上且2质量%以下。
28.权利要求27所述的变速机用润滑油组合物，其特征在于，所述摩擦调节剂的配合量以组合物总量基准计为0.01质量%以上且1质量%以下。
29.权利要求1所述的变速机用润滑油组合物，其特征在于，进一步配合有清洁分散剂。
30.权利要求29所述的变速机用润滑油组合物，其特征在于，所述清洁分散剂为无灰系分散剂，
所述无灰系分散剂为琥珀酰亚胺化合物、硼系酰亚胺化合物、曼尼希系分散剤、和酰胺系化合物中的至少任一者。
31.权利要求30所述的变速机用润滑油组合物，其特征在于，所述无灰系分散剂的配合量以组合物总量基准计为0.1质量%以上且20质量%以下。
32.权利要求29所述的变速机用润滑油组合物，其特征在于，所述清洁分散剂为金属系清洁剂，
所述金属系清洁剂为碱金属磺酸盐、碱金属苯酚盐、碱金属水杨酸盐、碱金属萘酸盐、碱土类金属磺酸盐、碱土类金属苯酚盐、碱土类金属水杨酸盐、和碱土类金属萘酸盐中的至少任一者。
33.权利要求32所述的变速机用润滑油组合物，其特征在于，所述金属系清洁剂的配合量以组合物总量基准计为0.1质量%以上且10质量%以下。
34.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的灯油10.00质量%、和API II类的基础油49.31质量%，
所述灯油的闪点为44℃，所述灯油的40℃运动粘度为0.892mm2/s，所述API
II类的基础油的40℃运动粘度为7.680mm2/s，所述API II类的基础油的闪点为170℃，所述API II类的基础油的100℃运动粘度为2.278mm2/s，所述API
II类的基础油的粘度指数为108，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃20.00质量%，
配合有质量平均分子量为30000的聚甲基丙烯酸酯10.00质量%，
作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。
35.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的灯油11.00质量%、和API II类的基础油48.31质量%，
所述灯油的闪点为42℃，所述灯油的40℃运动粘度为0.987mm2/s，所述API
II类的基础油的40℃运动粘度为7.680mm2/s，所述API II类的基础油的闪点为170℃，所述API II类的基础油的100℃运动粘度为2.278mm2/s，所述API
II类的基础油的粘度指数为108，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃20.00质量%，
配合有质量平均分子量为30000的聚甲基丙烯酸酯10.00质量%，
作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。
36.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的灯油15.00质量%、和API II类的基础油44.31质量%，
所述灯油的闪点为84℃，所述灯油的40℃运动粘度为1.621mm2/s，所述API
II类的基础油的40℃运动粘度为7.680mm2/s，所述API II类的基础油的闪点为170℃，所述API II类的基础油的100℃运动粘度为2.278mm2/s，所述API
II类的基础油的粘度指数为108，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃20.00质量%，
配合有质量平均分子量为30000的聚甲基丙烯酸酯10.00质量%，
作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。
37.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的轻油15.00质量%、和API II类的基础油44.31质量%，
所述轻油的闪点为84℃，所述轻油的40℃运动粘度为1.660mm2/s，所述轻油的100℃运动粘度为0.805mm2/s，所述轻油的粘度指数为30，所述API II类的基础油的40℃运动粘度为7.680mm2/s，所述API
II类的基础油的闪点为170℃，所述API
II类的基础油的100℃运动粘度为2.278mm2/s，所述API II类的基础油的粘度指数为108，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃20.00质量%，
配合有质量平均分子量为30000的聚甲基丙烯酸酯10.00质量%，
作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。
38.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的链烷烃20.00质量%、和API II类的基础油39.31质量%，
所述链烷烃的闪点为101℃，所述链烷烃的40℃运动粘度为2.166mm2/s，所述API
II类的基础油的40℃运动粘度为7.680mm2/s，所述API II类的基础油的闪点为170℃，所述API II类的基础油的100℃运动粘度为2.278mm2/s，所述API
II类的基础油的粘度指数为108，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃20.00质量%，
配合有质量平均分子量为30000的聚甲基丙烯酸酯10.00质量%，
作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。
39.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的闪点为138℃、40℃运动粘度为4.320mm2/s、100℃运动粘度为1.540mm2/s、粘度指数为83的链烷烃58.81质量%，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃20.50质量%，
配合有质量平均分子量为30000的聚甲基丙烯酸酯10.00质量%，
作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。
40.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的闪点为170℃、40℃运动粘度为7.680mm2/s、100℃运动粘度为2.278mm2/s、粘度指数为108的API II类的基础油66.21质量%，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃7.40质量%，
配合有质量平均分子量为30000的聚甲基丙烯酸酯15.70质量%，
作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。
41.权利要求1所述的变速机用润滑油组合物，其特征在于，配合有作为所述基础油的闪点为170℃、40℃运动粘度为7.680mm2/s、100℃运动粘度为2.278mm2/s、粘度指数为108的API II类的基础油57.91质量%，
配合有作为其它基础油的闪点为222℃、40℃运动粘度为30.600mm2/s、100℃运动粘度为5.200mm2/s、粘度指数为104的API II类的基础油10.00质量%，
配合有闪点为283℃、40℃运动粘度为1240mm2/s、100℃运动粘度为100mm2/s、粘度指数为170的聚α烯烃7.40质量%，配合有质量平均分子量为30000的聚甲基丙烯酸酯14.00质量%，作为其他添加剂，配合极压剂、耐磨损剂、清洁分散剂、倾点降低剂和摩擦调节剂混合而成的变速机油用添加剂套装10.69质量％。