CN103741470A - 涤纶热轧胶粘阻燃无纺布阻燃乳液 - Google Patents
涤纶热轧胶粘阻燃无纺布阻燃乳液 Download PDFInfo
- Publication number
- CN103741470A CN103741470A CN201410025285.4A CN201410025285A CN103741470A CN 103741470 A CN103741470 A CN 103741470A CN 201410025285 A CN201410025285 A CN 201410025285A CN 103741470 A CN103741470 A CN 103741470A
- Authority
- CN
- China
- Prior art keywords
- retardant
- fire
- flame
- gluing
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种涤纶热轧胶粘阻燃无纺布阻燃乳液，复配成A、B双组，A:阻燃剂80-125kg、丙烯酸酯胶粘剂：80-125kg、复合乳化剂1.0-1.5kg、水100-200kg;B:交联剂20-37.5kg。本发明的技术效果是：该配方可以均匀涂布在涤纶热轧无纺基布上制成涤纶热轧胶粘阻燃无纺布，以便提高产品质量，降低成本，生产性价比高的涤纶热轧胶粘阻燃无纺布。但迄今为止国内市场未见此类阻燃乳胶产品。
Description
技术领域
本发明涉及一种阻燃乳液，尤其涉及一种涤纶热轧胶粘阻燃无纺布阻燃乳液。
背景技术
涤纶热轧胶粘无纺布强度高、弹性好、尺寸稳定，具有耐光、耐热、耐摩擦和耐酸、耐碱，化学稳定性好等优良性能，因而广泛应用在工农业生产、国防、建筑和人们生活中的各个方面。但是涤纶的极限氧指数（LOI）为20 %~22 %，容易燃烧，且火焰传播速度快，并释放出大量黑色的烟尘及一些有害气体，不但污染环境，还给救生和消防工作带来困难，不能满足一些应用领域对其阻燃性能的要求。因此提高涤纶胶粘无纺布的阻燃性能，对确保人们生命、财产安全，减少火灾事故的发生有着重要意义和广阔的应用前景。
阻燃剂是能够提高易燃或可燃物难燃性、自熄性或消烟性，使易燃的高聚物不容易着火或着火后使其燃烧速度变慢的一种助剂。用于高聚物的阻燃剂种类繁多，按阻燃剂所含阻燃元素可分为卤系、磷系…等阻燃剂。应该指出的是含氯、溴的有机卤化物阻燃剂虽然阻燃效果好，但燃烧时易产生大量含卤毒烟，为了促进涤纶阻燃行业的持续性发展，无卤、低烟、低毒的环保型无卤阻燃整理剂是当前和今后阻燃整理研究的发展方向。
涤纶的阻燃改性一般采用与阻燃剂共聚、共混和后整理等方法。而后整理法根据产品不同所使用的方法各不相同，又可分为浸轧烘干法、刷涂法、喷雾法和有机溶剂法等。涤纶热轧胶粘阻燃无纺布目前主要使用的是浸渍烘干法。整理工艺流程第一步先将涤纶热轧无纺基布（T）喷淋丙烯酸酯类胶粘剂，烘干后得到涤纶热轧胶粘无纺布（TB）；第二步再将涤纶热轧胶粘无纺布在阻然剂中浸渍，通过物理吸附或化学键合使阻燃剂固着在涤纶热轧胶粘无纺布上，再通过干燥后得到涤纶热轧胶粘阻燃无纺布（TBP）。该整理工艺经过上胶和浸渍阻燃剂两道工序，不但费时费电，增加能耗成本，而且难以准确控制阻然剂的浸渍量和阻燃无纺布的克重，也易降低产品挺度和改变产品色泽。相关企业迫切希望采用喷淋法一步将丙烯酸酯乳液胶粘剂和阻燃剂均匀涂布在涤纶热轧无纺基布上制成涤纶热轧胶粘阻燃无纺布，以便提高产品质量，降低成本，生产性价比高的涤纶热轧胶粘阻燃无纺布。但迄今为止国内市场未见此类阻燃乳胶产品。
发明内容
本发明的目的在于提供一种涤纶热轧胶粘阻燃无纺布阻燃乳液，本发明以无毒、挥发性小、高度环化的无卤磷酸酯等阻燃剂、改性丙烯酸酯乳液胶粘剂、乳化剂和交联剂等为原料，复配成A、B双组分无卤磷酸酯阻燃乳液胶粘剂，首次采用喷淋法一步将阻燃剂和丙烯酸酯乳液胶粘剂均匀喷涂在涤纶热轧无纺基布上制成涤纶热轧胶粘阻燃无纺布。
本发明是这样实现的，其特征在于：为A、B双组分复配样品,
A: 阻燃剂 80-125kg、 丙烯酸酯胶粘剂：80-125kg、复合乳化剂1.0-2.0 kg、水100-200 kg;
B: 交联剂20-37.5 kg
所述的阻燃剂：无卤磷系阻燃剂[如：磷酸三(丁氧基乙基)酯(TBEP)；异丙基化磷酸三苯酯(IPPP)；高效环化磷酸酯（如：RF-204；RF-204-70等）；含磷、氮的非卤消烟透明阻燃剂（如：RF-2057；RF-202）；间苯二酚-双(磷酸二苯酯) ( RDP)；双酚A-双(磷酸二苯酯) ( BDP)；间苯二酚-双( 2, 6-二甲苯基磷酸酯) ( RXP)等。
复合乳化剂：即由非离子型和阴离子型表面活性剂复合而成.①非离子型（0.5-2.0Kg）：十二烷基二乙醇酰胺、聚氧乙烯脂肪醇醚、 聚氧乙烯烷基酚米或十二烷基醇酰胺磷酸酯。
②阴离子型(0.1-1.0Kg)：十二烷基硫酸钠、十二烷基磺酸钠或十二烷基苯磺酸钠。
改性丙烯酸酯胶粘剂配方：丙烯酸丁酯 30-40份
丙烯酸乙酯 10-20份
甲基丙丙烯酸甲酯 35-45份
苯乙烯 10-20份
甲基丙丙烯酸 1- 2份
N-羟甲基丙烯酰胺 1- 2份
复合乳化剂 1- 3份
碳酸氢钠 1- 2份
硫代硫酸铵 0.5- 1份
水 40-60份
合成固含量约为质量分数45-52﹪的丙烯酸酯胶粘剂。
B: 交联剂：高度醚化和部分醚化的三聚氰胺类树酯（如：顺昌化工SC-A03; SC-A25; 大连恒星精细化工有限公司生产的80A等）。
通过该配方制备成无纺布阻燃乳生产工艺：
在室温下，将水、复合乳化剂搅拌溶解；加入丙烯酸酯乳胶充分乳化；用适量水稀释阻燃剂，加氨水调pH=7.0-8.0后与上述乳液混并搅拌均即为A组分；生产时加入B组分（交联剂）并搅拌均匀即可。
本发明的技术效果是：该配方可以均匀涂布在涤纶热轧无纺基布上制成涤纶热轧胶粘阻燃无纺布，以便提高产品质量，降低成本，生产性价比高的涤纶热轧胶粘阻燃无纺布。但迄今为止国内市场未见此类阻燃乳胶产品。
具体实施方式
实施例1
一种涤纶热轧胶粘阻燃无纺布阻燃乳液，复配成A、B双组，
A: 阻燃剂 80kg、 丙烯酸酯胶粘剂：80kg、复合乳化剂1.0 kg、水100 kg;B: 交联剂20kg。其中阻燃剂可以选用异丙基化磷酸三苯酯(IPPP)、高效环化磷酸酯（如：RF-204）；含磷、氮的非卤消烟透明阻燃剂（如：RF-2057；RF-202）；间苯二酚-双( 2, 6-二甲苯基磷酸酯) ( RXP)、）；间苯二酚-双(磷酸二苯酯) ( RDP)等，其中丙烯酸酯胶粘剂包括：
丙烯酸丁酯 30份
丙烯酸乙酯 10份
甲基丙丙烯酸甲酯 45份
苯乙烯 20份
甲基丙丙烯酸 1份
N-羟甲基丙烯酰胺 1份
复合乳化剂 2份
碳酸氢钠 1份
硫代硫酸铵 0.5份
水 60份
合成固含量约为45﹪的丙烯酸酯胶粘剂。
所述交联剂采用高度醚化和部分醚化的三聚氰胺类树酯，优选顺昌化工SC-A03; SC-A25; 大连恒星精细化工有限公司生产的80A。
实施例2
一种涤纶热轧胶粘阻燃无纺布阻燃乳液，复配成A、B双组，
A: 阻燃剂 125kg、 丙烯酸酯胶粘剂：125kg、复合乳化剂1.5 kg、水200 kg;B: 交联剂37.5kg。其中阻燃剂可以选用异丙基化磷酸三苯酯(IPPP)； 高效环化磷酸酯（如： RF-204-70）；含磷、氮的非卤消烟透明阻燃剂（如：RF-2057；RF-202）；间苯二酚-双( 2, 6-二甲苯基磷酸酯) ( RXP)）；间苯二酚-双(磷酸二苯酯) ( RDP)等，其中丙烯酸酯胶粘剂包括：
丙烯酸丁酯 40份
丙烯酸乙酯 20份
甲基丙丙烯酸甲酯 35份
苯乙烯 10份
甲基丙丙烯酸 2份
N-羟甲基丙烯酰胺 2份
复合乳化剂 3份
碳酸氢钠 2份
硫代硫酸铵 1份
水 40份
合成固含量约为52﹪的丙烯酸酯胶粘剂。
所述交联剂采用高度醚化和部分醚化的三聚氰胺类树酯，优选顺昌化工SC-A03; SC-A25; 大连恒星精细化工有限公司生产的80A。
实施例3
一种涤纶热轧胶粘阻燃无纺布阻燃乳液，复配成A、B双组，
A: 阻燃剂 100kg、 丙烯酸酯胶粘剂：100kg、复合乳化剂1.2 kg、水150 kg; B: 交联剂30kg。其中阻燃剂可以选用异丙基化磷酸三苯酯(IPPP)；高效环化磷酸酯（如：RF-204；RF-204-70等）；含磷、氮的非卤消烟透明阻燃剂（如：RF-2057；RF-202）；间苯二酚-双( 2, 6-二甲苯基磷酸酯) ( RXP）；间苯二酚-双(磷酸二苯酯) ( RDP)等，其中丙烯酸酯胶粘剂包括：
丙烯酸丁酯 35份
丙烯酸乙酯 15份
甲基丙丙烯酸甲酯 40份
苯乙烯 15份
甲基丙丙烯酸 1.5份
N-羟甲基丙烯酰胺 1.5份
复合乳化剂 2.0份
碳酸氢钠 1.5份
硫代硫酸铵 0.8份
水 50份
合成固含量约为50﹪的丙烯酸酯胶粘剂。
所述交联剂采用高度醚化和部分醚化的三聚氰胺类树酯，优选顺昌化工SC-A03; SC-A25; 大连恒星精细化工有限公司生产的80A。
阻燃性能：
符合我国纺织品燃烧性能的试验方法标准；
GB/ T 14 6 45一19 9 3 纺织织物姗烧性能45。方向损毁囱积和接焰次数测定；
涤纶阻燃整理后的行业评测标准
阻燃织物的应用行业类型 级别 续燃时间/s 阴然时间/s 损毁长度/cm
阻燃机织物 B1 级 ≤5/s ≤5/s ≤15cm
B2 级 ≤15/s ≤10/s ≤20cm
公共场所阻燃制品及组件 1 级 ≤5/s ≤5/s ≤15cm
2 级 ≤15/s ≤15/s ≤20cm
阻燃防护服 / ≤5/s ≤5/s ≤15cm
建筑内部装修用防火织物
地下或高层民用建筑装饰用布 / ≤5/s ≤5/s ≤15/cm
一般民用窗帘、家具包布等 / ≤15/s ≤10/s ≤20/ cm
用A、B 复配的阻燃乳液胶粘剂就可按①、②式用110 g/m2、 140g/m2的涤纶热轧无纺基布分别上40、60 g 的阻燃乳胶就能生产出150 g和200 g的涤纶热轧胶粘阻燃无纺布产品。① CT110 + 40 → CTP150，② CT140 + 60 → CTP200。
Claims (6)
1.一种涤纶热轧胶粘阻燃无纺布阻燃乳液，其特征在于：复配成A、B双组，
A: 阻燃剂 80-125kg、 丙烯酸酯胶粘剂：80-125kg、复合乳化剂1.0-2.0kg、水100-200 kg;
B: 交联剂20-37.5 kg。
2.根据权利要求1所述的涤纶热轧胶粘阻燃无纺布阻燃乳液，其特征在于：所述的阻燃剂包括无卤磷系阻燃剂、高效环化磷酸酯、含磷、氮的非卤消烟透明阻燃剂、双酚A-双(磷酸二苯酯) ( BDP)、间苯二酚-双( 2, 6-二甲苯基磷酸酯) ( RXP)、）；间苯二酚-双(磷酸二苯酯) ( RDP)。
3.根据权利要求2所述的涤纶热轧胶粘阻燃无纺布阻燃乳液，其特征在于：所述无卤磷系阻燃剂优选磷酸三(丁氧基乙基)酯(TBEP)；异丙基化磷酸三、苯酯(IPPP)；所述高效环化磷酸酯优选RF-204；RF-204-70；所述含磷、氮的非卤消烟透明阻燃剂优选RF-2057；RF-202）。
4.根据权利要求1所述的涤纶热轧胶粘阻燃无纺布阻燃乳液，其特征在于：所述复合乳化剂：即由0.5-2.0Kg非离子型和0.1-1.0Kg阴离子型表面活性剂复合而成.①非离子型：十二烷基二乙醇酰胺、聚氧乙烯脂肪醇醚、 聚氧乙烯烷基酚米或十二烷基醇酰胺磷酸酯 ②阴离子型：十二烷基硫酸钠、十二烷基磺酸钠或十二烷基苯磺酸钠。
5.根据权利要求1所述的涤纶热轧胶粘阻燃无纺布阻燃乳液，其特征在于：所述丙烯酸酯胶粘剂配方：
丙烯酸丁酯 30-40份
丙烯酸乙酯 10-20份
甲基丙丙烯酸甲酯 35-45份
苯乙烯 10-20份
甲基丙丙烯酸 1- 2份
N-羟甲基丙烯酰胺 1- 2份
复合乳化剂 2- 3份
碳酸氢钠 1- 2份
硫代硫酸铵 0.5- 1份
水 40-60份
合成固含量约为质量分数45-52﹪的丙烯酸酯胶粘剂。
6.根据权利要求1所述的涤纶热轧胶粘阻燃无纺布阻燃乳液，其特征在于：交联剂：高度醚化和部分醚化的三聚氰胺类树酯，优选顺昌化工SC-A03; SC-A25; 大连恒星精细化工有限公司生产的80A。