CN105316940A - 一种浸渍胶、阻燃聚酯油毡基布及其制备方法、防水卷材 - Google Patents
一种浸渍胶、阻燃聚酯油毡基布及其制备方法、防水卷材 Download PDFInfo
- Publication number
- CN105316940A CN105316940A CN201510780898.3A CN201510780898A CN105316940A CN 105316940 A CN105316940 A CN 105316940A CN 201510780898 A CN201510780898 A CN 201510780898A CN 105316940 A CN105316940 A CN 105316940A
- Authority
- CN
- China
- Prior art keywords
- polyester felt
- flame
- flame retardant
- base cloth
- retardant polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种浸渍胶、阻燃聚酯油毡基布及其制备方法、防水卷材,属于防水卷材技术领域,其可解决现有的采用聚酯油毡基布生产防水卷材,防水卷材易与沥青摩擦起火的问题。本发明的浸渍胶中加入了阻燃剂,采用该浸渍胶浸轧无纺布后得到的聚酯油毡基布具有阻燃性,阻燃聚酯油毡基布可达到离火即灭的效果。采用该阻燃聚酯油毡基布生产防水卷材过程中,不会产生电火花。做成的防水卷材在应用过程中,可有效防止意外起火。本发明的阻燃聚酯油毡基布适用于各种防水卷材。
Description
技术领域
本发明属于防水卷材技术领域,具体涉及一种浸渍胶、阻燃聚酯油毡基布及其制备方法、防水卷材。
背景技术
聚酯油毡基布属于无纺布,又可以称之为胎基布,油毡基布,防水基布。聚酯油毡基布是以100%涤纶短纤维经梳理成网、针刺加固、浸胶定型等工序加工而成的一种无纺布制品。
防水卷材一般将聚酯油毡基布浸泡在200℃的沥青中做成。聚酯油毡基布作为沥青防水材料的胎基布,在建筑行业以得到广泛应用。
发明人发现现有技术中至少存在如下问题:生产防水卷材过程中,防水卷材与沥青的摩擦力较大,容易产生电火花,严重时甚至引起起火。此外,防水卷材在施工的时候常用烘烤施工方法,如果烘烤到防水卷材的断面,也容易引起燃烧。
发明内容
本发明针对现有的采用聚酯油毡基布生产防水卷材,防水卷材易与沥青摩擦起火的问题,提供一种浸渍胶、阻燃聚酯油毡基布及其制备方法、防水卷材。
解决本发明技术问题所采用的技术方案是:
一种浸渍胶,用于浸轧无纺布,包括阻燃剂和胶黏剂,其中,所述阻燃剂与所述胶黏剂的重量比为1:0.8-1.2。
优选的,所述阻燃剂包括磷系阻燃剂、氮系阻燃剂、有机氮磷系阻燃剂中的任意一种。
优选的,所述阻燃剂包括织物阻燃剂。
更优选的,所述阻燃剂选自阻燃剂Doher-601、织物用阻燃剂LM-8007中的一种或两种的混合。
优选的,所述胶黏剂包括丙烯酸脂胶、淀粉胶中的任意一种或两种的混合物。
优选的,所述浸渍胶还包括水,所述阻燃剂与水的重量比为1:6-10。
本发明还提供一种阻燃聚酯油毡基布的制备方法,包括以下步骤:
将无纺布进行热定型处理;
将上述经过热定型处理的无纺布浸轧至上述的浸渍胶中;
烘干上述无纺布,得到聚酯油毡基布。
优选的,所述热定型处理的温度为170℃-180℃。
优选的,所述烘干的温度为150℃-160℃。
其中,用含丙烯酸脂胶的浸渍胶做出的聚酯油毡基布不吸水,可有效防止聚酯油毡基布做成卷材后施工渗水。
本发明还提供一种阻燃聚酯油毡基布,所述聚酯油毡基布由上述的方法制成。
本发明还提供一种防水卷材,包括上述的阻燃聚酯油毡基布。
本发明的浸渍胶中加入了阻燃剂,采用该浸渍胶浸轧无纺布后得到的聚酯油毡基布具有阻燃性,阻燃聚酯油毡基布可达到离火即灭的效果。采用该阻燃聚酯油毡基布生产防水卷材过程中,不会产生电火花。做成的防水卷材在应用过程中,可有效防止意外起火。本发明的阻燃聚酯油毡基布适用于各种防水卷材。
具体实施方式
为使本领域技术人员更好地理解本发明的技术方案,下面结合具体实施方式对本发明作进一步详细描述。
实施例1:
本实施例提供一种浸渍胶,用于浸轧无纺布,包括阻燃剂和胶黏剂,其中,所述阻燃剂与所述胶黏剂的重量比为1:0.8-1.2。
本实施例的浸渍胶中加入了阻燃剂,采用该浸渍胶浸轧无纺布后得到的聚酯油毡基布具有阻燃性,阻燃聚酯油毡基布可达到离火即灭的效果。采用该阻燃聚酯油毡基布生产防水卷材过程中,不会产生电火花。做成的防水卷材在应用过程中,可有效防止意外起火。本发明的阻燃聚酯油毡基布适用于各种防水卷材。
实施例2:
本实施例提供一种浸渍胶,包括50kg有机氮磷系阻燃剂(阻燃剂Doher-601,道尔化学),50kg丙烯酸脂胶(或称丙烯酸乳液)以及400kg水
实施例3:
本实施例提供一种浸渍胶,包括50kg有机氮磷系阻燃剂(纤维织物用高效阻燃剂LM-8007,青岛联美化工),50kg丙烯酸脂胶以及400kg水。
实施例4:
本实施例提供一种浸渍胶,包括50kg有机氮磷系阻燃剂(其中,道尔化学阻燃剂Doher-601,25kg,青岛联美化工纤维织物用高效阻燃剂LM-8007,25kg),50kg丙烯酸乳液以及400kg水。
实施例5
本实施例提供一种阻燃聚酯油毡基布,其制备方法如下:
对原料无纺布(170g/m2)进行热定型处理,定型温度170℃;
将上述经过热定型处理的无纺布浸轧至实施例2的浸渍胶中;
烘干(烘干温度150℃)上述无纺布,得到聚酯油毡基布。
实施例6
本实施例提供一种阻燃聚酯油毡基布,其制备方法如下:
对原料无纺布(170g/m2)进行热定型处理,定型温度175℃;
将上述经过热定型处理的无纺布浸轧至实施例3的浸渍胶中;
烘干(烘干温度155℃)上述无纺布,得到聚酯油毡基布。
实施例7
本实施例提供一种阻燃聚酯油毡基布,其制备方法如下:
对原料无纺布(170g/m2)进行热定型处理,定型温度180℃;
将上述经过热定型处理的无纺布浸轧至实施例4的浸渍胶中;
烘干(烘干温度160℃)上述无纺布,得到聚酯油毡基布。
将实施例5-7的聚酯油毡基布,根据《GBT18840-2002沥青防水卷材用胎基》进行测试,测试结果见表1。
表1
将实施例5-7的聚酯油毡基布,按照GB/T5455《纺织织物阻燃性能测定垂直法》进行测试,达到GB17591—2006《阻燃织物》B1级。
表2
实施例8、9
本实施例提供一种浸渍胶,用于浸轧无纺布,包括阻燃剂和胶黏剂,其中,所述阻燃剂与所述胶黏剂的重量比分别为1:0.8,1:1.2。
实施例10、11
本实施例提供一种浸渍胶,其制备方法与实施例2类似,其与实施例2的区别在于:阻燃剂分别为磷系阻燃剂、氮系阻燃剂。
实施例12
本实施例提供一种浸渍胶,其制备方法与实施例2类似,其与实施例2的区别在于:胶黏剂为淀粉胶。
实施例13、14
本实施例提供一种浸渍胶,其制备方法与实施例2类似,其与实施例2的区别在于:所述阻燃剂与水的重量分别比为1:6,1:10。
经测试,实施例8~14浸渍胶浸渍得到的阻燃聚酯油毡基布与实施例5的阻燃聚酯油毡基布性能接近。其中实施例12的浸渍胶浸渍得到的阻燃聚酯油毡基布,用于制备防水卷材后,防水卷材表面产生少量孔洞,其孔洞位置处防水效果略有降低。
显然,上述各实施例的具体实施方式还可进行许多变化;例如:市售的不同型号的丙烯酸脂胶(或称丙烯酸乳液),均能达到上述实施例的技术效果,阻燃剂或胶黏剂的型号可以根据实际情况进行选择,或者阻燃剂与水的比例可以根据实际生产进行调整。
可以理解的是,以上实施方式仅仅是为了说明本发明的原理而采用的示例性实施方式,然而本发明并不局限于此。对于本领域内的普通技术人员而言,在不脱离本发明的精神和实质的情况下,可以做出各种变型和改进,这些变型和改进也视为本发明的保护范围。
Claims (9)
1.一种浸渍胶,用于浸轧无纺布,其特征在于,包括阻燃剂和胶黏剂,其中,所述阻燃剂与所述胶黏剂的重量比为1:0.8-1.2。
2.根据权利要求1所述的浸渍胶,其特征在于,所述阻燃剂包括磷系阻燃剂、氮系阻燃剂、有机氮磷系阻燃剂中的任意一种。
3.根据权利要求1所述的浸渍胶,其特征在于,所述胶黏剂包括丙烯酸脂胶、淀粉胶中的任意一种或两种的混合物。
4.根据权利要求1所述的浸渍胶,其特征在于,所述浸渍胶还包括水,所述阻燃剂与水的重量比为1:6-10。
5.一种阻燃聚酯油毡基布的制备方法,其特征在于,包括以下步骤:
将无纺布进行热定型处理;
将上述经过热定型处理的无纺布浸轧至权利要求1-4任一项所述的浸渍胶中;
烘干上述无纺布,得到聚酯油毡基布。
6.根据权利要求5所述的阻燃聚酯油毡基布的制备方法,其特征在于,所述热定型处理的温度为170℃-180℃。
7.根据权利要求5所述的阻燃聚酯油毡基布的制备方法,其特征在于,所述烘干的温度为150℃-160℃。
8.一种阻燃聚酯油毡基布,其特征在于,由权利要求5-7任意一项所述的方法制成。
9.一种防水卷材,其特征在于,包括权利要求8所述的阻燃聚酯油毡基布。