CN103524817A - 一种耐寒耐油改性氯丁橡胶电缆料 - Google Patents
一种耐寒耐油改性氯丁橡胶电缆料 Download PDFInfo
- Publication number
- CN103524817A CN103524817A CN201310511433.9A CN201310511433A CN103524817A CN 103524817 A CN103524817 A CN 103524817A CN 201310511433 A CN201310511433 A CN 201310511433A CN 103524817 A CN103524817 A CN 103524817A
- Authority
- CN
- China
- Prior art keywords
- parts
- chloroprene rubber
- carbon black
- rubber
- cold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种电缆料,具体涉及一种耐寒耐油改性氯丁橡胶电缆料,该电缆料包含以下重量份的原料:氯丁橡胶30-34,丁腈橡胶(N41)20-23,丁苯橡胶10-12,聚偏二氯乙烯12-14,N774炭黑10-14,N330炭黑26-29,己二酸二甲酯4-5,环氧大豆油3-5,硅酸铝15-20,碳酸钙14-18,防老剂MB1-3,松香3-5,硫磺1-2,氧化锌4-6,3-氨丙基三甲氧基硅烷1-2,三氧化二锑5-7,硬脂酸钡2-5,四丙基溴化铵1-2,助剂4-5;该电缆料结合了氯丁橡胶、丁腈橡胶、丁苯橡胶以及聚偏二氯乙烯等原料的优点,提升了传统氯丁橡胶电缆料的性能,使其具备优良的耐寒耐油性能,同时还具有阻燃、耐老化等性能,能够适应特定的使用环境条件,市场应用前景广阔。
Description
技术领域
本发明涉及一种电缆料,具体涉及一种耐寒耐油改性氯丁橡胶电缆料及其制备方法。
背景技术
随着经济的发展,电缆的需求市场广阔,推动着电缆料生产技术的进步,电缆料不仅用途广泛,而且对其性能指标有特殊的要求,比如绝缘性、拉伸强度、使用温度、阻燃性能等指标均有严格的要求,不断的提高电缆料的性能,是经济和社会发展的迫切需求,传统的电缆料多存在阻燃性差、高温易变形、力学性能差、使用寿命短等问题,给实际使用带来很多不便,甚至威胁到人们的生命财产安全,因此,急需改变原有电缆料配方,改进材料性能,以适应电缆市场多样的需求。
发明内容
本发明的目的在于,提供一种耐寒耐油改性氯丁橡胶电缆料,提升了传统氯丁橡胶材料的性能,使其具备优越的耐寒耐油性能,能够适应特定的使用环境条件,为了实现上述目的,本发明采用的技术方案如下:
一种耐寒耐油改性氯丁橡胶电缆料,其特征在于,该电缆料包含以下重量份的组分:氯丁橡胶30-34,丁腈橡胶(N41)20-23,丁苯橡胶10-12,聚偏二氯乙烯12-14,N774炭黑10-14,N330炭黑26-29,己二酸二甲酯4-5,环氧大豆油3-5,硅酸铝15-20,碳酸钙14-18,防老剂MB 1-3,松香3-5,硫磺1-2,氧化锌4-6,3-氨丙基三甲氧基硅烷1-2,三氧化二锑5-7,硬脂酸钡2-5,四丙基溴化铵1-2,助剂4-5。
所述的助剂包含以下重量份的原料:天青石20-24,交联剂TAC3-4,二缩三丙二醇二丙烯酸酯2-3,硬酯酸锌2-3,纳米二氧化硅3-4,氟化锆1-2,甲基三乙氧基硅烷1-2,促进剂TMTD 1-2,海泡石粉8-10,聚异丁烯2-3,防老剂ODA 1-2,花椒籽油1-2;制备方法是将天青石、海泡石放入煅烧炉中在550-570℃下煅烧3-4小时,冷却,粉碎成50-100目后放入12-15%盐酸溶液中浸泡2-3小时,过滤出天青石、海泡石粉末,清水洗净、烘干,粉碎成200-300目粉末,与其它剩余成分混合,研磨分散1-2小时,即得。
所述的一种耐寒耐油改性氯丁橡胶电缆料,其制备方法如下:
(1)将氯丁橡胶、丁腈橡胶(N41)、丁苯橡胶投入密炼机中,塑炼12-15min,当密炼机温度达到110-130℃时,开始出料,塑炼料冷却备用;
(2)将步骤(1)得到的混合料投入密炼机中,加入硬脂酸钡、防老剂MB、松香,混炼4-5min后,加入硅酸铝、碳酸钙,混炼3-4min,随后先加入2/3的N330炭黑,混炼3-5min,再将余下的N330炭黑全部加入,翻炼2-3min,最后加入环氧大豆油,混炼4-5min,当密炼机温度达到80-100℃时,开始出料,当混合料完全冷却后,投入开炼机中,加入氧化锌、硫磺,薄通6-8次即可,开炼机工作温度≤60℃;
(3)将聚偏二氯乙烯、己二酸二甲酯、三氧化二锑、3-氨丙基三甲氧基硅烷、N774炭黑混合,送入双螺杆挤出机造粒;
(4)将步骤(2)、步骤(3)得到的物料送入密炼机中,在100-130℃下混炼2-3min,冷却后送入开炼机中开炼,加入其他剩余成分,薄通6-7次,即得本发明橡胶料。
本发明结合了氯丁橡胶、丁腈橡胶、丁苯橡胶以及聚偏二氯乙烯等原料的优点,提升了传统氯丁橡胶电缆料的性能,使其具备优良的耐寒耐油性能,同时还具有阻燃、耐老化等性能,能够适应特定的使用环境条件,市场应用前景广阔。
具体实施方式
实施例
本实施例的电缆料包含以下重量份的原料:氯丁橡胶34,丁腈橡胶(N41)23,丁苯橡胶12,聚偏二氯乙烯14,N774炭黑14,N330炭黑28,己二酸二甲酯5,环氧大豆油5,硅酸铝20,碳酸钙18,防老剂MB 3,松香5,硫磺2,氧化锌6,3-氨丙基三甲氧基硅烷2,三氧化二锑6,硬脂酸4,四丙基溴化铵2,助剂5。
所述的助剂包含以下重量份的原料:天青石24,交联剂TAC4,二缩三丙二醇二丙烯酸酯3,硬酯酸锌3,纳米二氧化硅4,氟化锆2,甲基三乙氧基硅烷2,促进剂TMTD 2,海泡石粉10,聚异丁烯3,防老剂ODA 2,花椒籽油2;制备方法是将天青石、海泡石放入煅烧炉中在570℃下煅烧4小时,冷却,粉碎成80目后放入15%盐酸溶液中浸泡3小时,过滤出天青石、海泡石粉末,清水洗净、烘干,粉碎成300目粉末,与其它剩余成分混合,研磨分散2小时,即得。
所述的一种耐寒耐油改性氯丁橡胶电缆料,其制备方法如下:
(1)将氯丁橡胶、丁腈橡胶(N41)、丁苯橡胶投入密炼机中,塑炼15min,当密炼机温度达到125℃时,开始出料,塑炼料冷却备用;
(2)将步骤(1)得到的混合料投入密炼机中,加入硬脂酸钡、防老剂MB、松香,混炼5min后,加入硅酸铝、碳酸钙,混炼4min,随后先加入2/3的N330炭黑,混炼5min,再将余下的N330炭黑全部加入,翻炼3min,最后加入环氧大豆油,混炼5min,当密炼机温度达到100℃时,开始出料,当混合料完全冷却后,投入开炼机中,加入氧化锌、硫磺,薄通8次即可,开炼机工作温度≤60℃;
(3)将聚偏二氯乙烯、己二酸二甲酯、三氧化二锑、3-氨丙基三甲氧基硅烷、N774炭黑混合,送入双螺杆挤出机造粒;
(4)将步骤(2)、步骤(3)得到的物料送入密炼机中,在120℃下混炼3min,冷却后送入开炼机中开炼,加入其他剩余成分,薄通7次,即得本发明橡胶料。
本发明制备的电缆料,力学性能得到有效改善,拉伸强度、断裂伸长率等指标获得提高,具备良好的耐寒耐油能力。
本发明电缆料的性能测试结果为:拉伸强度为18.1Mpa,断裂伸长率为435%,经IRM902油121℃×168h处理后,拉伸强度和断裂伸长率分别为17.6Mpa、421%,热变形率为11.8%,在经136℃×168h热空气老化后,拉伸强度保持率97.6%,断裂伸长率保持率为98.3%,低温冲击脆化温度达到-40℃,在-70℃条件下弯曲后不开裂,测试得到的氧指数为35%。
Claims (2)
1.一种耐寒耐油改性氯丁橡胶电缆料,其特征在于,该电缆料由以下重量份的原料组成:氯丁橡胶30-34,丁腈橡胶(N41)20-23,丁苯橡胶10-12,聚偏二氯乙烯12-14,N774炭黑10-14,N330炭黑26-29,己二酸二甲酯4-5,环氧大豆油3-5,硅酸铝15-20,碳酸钙14-18,防老剂MB 1-3,松香3-5,硫磺1-2,氧化锌4-6,3-氨丙基三甲氧基硅烷1-2,三氧化二锑5-7,硬脂酸钡2-5,四丙基溴化铵1-2,助剂4-5;
所述的助剂包含以下重量份的原料:天青石20-24,交联剂TAC3-4,二缩三丙二醇二丙烯酸酯2-3,硬酯酸锌2-3,纳米二氧化硅3-4,氟化锆1-2,甲基三乙氧基硅烷1-2,促进剂TMTD 1-2,海泡石粉8-10,聚异丁烯2-3,防老剂ODA 1-2,花椒籽油1-2;制备方法是将天青石、海泡石放入煅烧炉中在550-570℃下煅烧3-4小时,冷却,粉碎成50-100目后放入12-15%盐酸溶液中浸泡2-3小时,过滤出天青石、海泡石粉末,清水洗净、烘干,粉碎成200-300目粉末,与其它剩余成分混合,研磨分散1-2小时,即得。
2.如权利要求1所述的一种耐寒耐油改性氯丁橡胶电缆料,其制作工艺如下:
(1)将氯丁橡胶、丁腈橡胶(N41)、丁苯橡胶投入密炼机中,塑炼12-15min,当密炼机温度达到110-130℃时,开始出料,塑炼料冷却备用;
(2)将步骤(1)得到的混合料投入密炼机中,加入硬脂酸钡、防老剂MB、松香,混炼4-5min后,加入硅酸铝、碳酸钙,混炼3-4min,随后先加入2/3的N330炭黑,混炼3-5min,再将余下的N330炭黑全部加入,翻炼2-3min,最后加入环氧大豆油,混炼4-5min,当密炼机温度达到80-100℃时,开始出料,当混合料完全冷却后,投入开炼机中,加入氧化锌、硫磺,薄通6-8次即可,开炼机工作温度≤60℃;
(3)将聚偏二氯乙烯、己二酸二甲酯、三氧化二锑、3-氨丙基三甲氧基硅烷、N774炭黑混合,送入双螺杆挤出机造粒;
(4)将步骤(2)、步骤(3)得到的物料送入密炼机中,在100-130℃下混炼2-3min,冷却后送入开炼机中开炼,加入其他剩余成分,薄通6-7次,即得本发明橡胶料。