CN103433993B - 防潮天花装饰板的生产方法 - Google Patents

防潮天花装饰板的生产方法 Download PDF

Info

Publication number
CN103433993B
CN103433993B CN201310380105.XA CN201310380105A CN103433993B CN 103433993 B CN103433993 B CN 103433993B CN 201310380105 A CN201310380105 A CN 201310380105A CN 103433993 B CN103433993 B CN 103433993B
Authority
CN
China
Prior art keywords
temperature
hot pressing
pressure
proof
pressing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310380105.XA
Other languages
English (en)
Other versions
CN103433993A (zh
Inventor
钱秀英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHENZHEN STYLE DECORATION CO., LTD.
Original Assignee
钱秀英
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CN201510459679.5A priority Critical patent/CN105150353A/zh
Priority to CN201310380105.XA priority patent/CN103433993B/zh
Priority to CN201510458974.9A priority patent/CN105235047A/zh
Priority to CN201510460870.1A priority patent/CN105291245A/zh
Priority to CN201510459124.0A priority patent/CN105291244A/zh
Application filed by 钱秀英 filed Critical 钱秀英
Priority to CN201510458492.3A priority patent/CN105291243A/zh
Priority to CN201510459680.8A priority patent/CN105479583A/zh
Publication of CN103433993A publication Critical patent/CN103433993A/zh
Application granted granted Critical
Publication of CN103433993B publication Critical patent/CN103433993B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种防潮天花装饰板的生产方法，其特征在于：是将木材碎料或农作物收货后产生的各类秸秆、坚果壳等碎粒与防潮脲醛树脂胶黏剂混合压制成板材，然后板材再与三聚氰胺浸渍纸或三氧化二铝耐磨纸高温压贴而成；板材成型采用三次冷压和三次热压，两次散热养生；所述的冷压温度为室温，压力为2.5MPa，热压压力为1.5～2.0MPa；第一次热压的温度为130～135℃；第二次热压的温度为125～130℃，第三次热压的温度为120～120℃；所述的散热养生为恒温室自然通风冷却至室温，时间为3～4h；板材表面贴三聚氰胺浸渍纸或三氧化二铝耐磨纸是在150℃，压力为1.5Mpa下进行。

Description

防潮天花装饰板的生产方法
技术领域
本发明涉及一种人造板的生产方法，特别是防潮性能优异的用于生产天花装饰材料的人造板的生产方法。
背景技术
目前天花的装饰材料主要采用石膏板，它是一种重量轻、强度较高、厚度较薄、加工方便以及隔音绝热和防火等性能较好的建筑材料，是当前着重发展的新型轻质板材之一。随着国家鼓励以林业生产中的三剩物、木材加工、竹材加工和人造板生产中产生锯屑、刨花、树皮、砂光粉、枝丫材，农作物收货后产生的各类秸秆、坚果壳等为原料生产人造板，越来越多的厂家开始尝试采用林、农副产物生产刨花板、密度板，人造板的价格越来越被消费者接受。因此采用人造板制成的天花装饰材料逐渐进入了老百姓的家庭。刨花板和密度板的生产方法是采用胶黏剂与纤维颗粒混合均匀，然后压制成板材。而胶黏剂的主要成份是脲醛树脂，其生产原料之一是有“人类健康隐形杀手”之称的甲醛。每生产一立方米刨花板和密度板用到的胶黏剂为100～400kg，即使脲醛树脂中甲醛的残留量为0.05mg/Kg，那么每立方米人造板残留的甲醛仍在5mg以上。刨花板和密度板耐水性差，吸湿后因产生膨胀力差异而使板材翘曲变形，而天花板是最容易受到潮气攻击的一个建筑结构，因此目前采用的刨花板和密度板制成的天花装饰材料受潮后易起鼓、变形，使用寿命短。
发明内容
本发明的目的是提供一种密度板的生产方法，通过本发明的生产方法可以提高人造板的防水、防潮性能，并能够降低甲醛释放量，非常适合于制作天花装饰材料。
本发明的技术方案是：
防潮天花装饰板的生产方法，是将木材碎料或农作物收货后产生的各类秸秆、坚果壳等碎粒与防潮脲醛树脂胶黏剂混合压制成板材，然后板材再与三聚氰胺浸渍纸或三氧化二铝耐磨纸高温压贴而成；板材成型采用三次冷压和三次热压，两次散热养生；所述的冷压温度为室温，压力为2.5MPa，热压压力为1.5～2.0MPa；第一次热压的温度为130～135℃；第二次热压的温度为125～130℃，第三次热压的温度为120～120℃；所述的散热养生为恒温室自然通风冷却至室温，时间为3～4h；板材表面贴三聚氰胺浸渍纸或三氧化二铝耐磨纸是在150℃，压力为1.5Mpa下进行。
所述的防潮脲醛树脂胶黏剂原料和重量份数包括：
脲醛树脂 46；
聚丙烯酸酯乳液 10；
聚二甲基硅氧烷 0.6；
300目轻质碳酸钙 30；
EVA乳胶 5。
该防潮脲醛树脂胶的生产方法是首先制备脲醛树脂，甲醛为一次性投料，尿素分三次投料；脲醛树脂的生产分成预聚合、聚合和后期聚合三个阶段，后期聚合以后加入聚丙烯酸酯乳液、聚二甲基硅氧烷和EVA乳胶，搅拌反应完全以后加入填料得到防潮脲醛树脂胶。
所述的预聚合阶段：聚合反应釜中一次性加入甲醛溶液，用甲酸调节pH值为2～2.5，加入甲醛溶液重量15%的尿素，升温至46℃，保温反应60min。
所述的聚合阶段：预聚合阶段结束，加碱调节反应液的pH值为8～8.5，加入甲醛溶液重量30%的尿素，40～60min内加完，然后升温反应液至88～92℃，保温反应90min。
所述的聚合后期阶段：聚合阶段结束，加入甲醛溶液重量30～40%的尿素，40～60min内加完，然后降低反应温度至70～85℃，反应60～90min，降温至室温，得到脲醛树脂。
聚合后期阶段或者采用过滤，除去不容物，得到低甲醛残留量脲醛树脂以后，加入聚丙烯酸酯乳液、聚二甲基硅氧烷和EVA乳胶，搅拌混合均匀以后加入填料，用三辊式研磨机研磨30min，得到防潮脲醛树脂胶黏剂。
所述的聚丙烯酸酯乳液为广州奇盛化工有限公司型号为M-862通用纯丙乳液，其全部采用丙烯酸酯为原料，经过乳液聚合而成，具有优良的防水性能和耐候性，与脲醛树脂一起作为胶黏剂的原料，可以改善脲醛树脂的耐水性，提高胶黏剂的防潮性能。
所述的聚二甲基硅氧烷为道康宁公司生产，型号为XIAMETER®PMX-200的硅油，具有高表面活性剂，在胶黏剂中作为消泡剂和流平剂，提高胶黏剂对基材的润湿性，增强粘接强度。并且由于聚二甲基硅氧烷高度疏水，能够提高胶黏剂的防水、防潮性能。
轻质碳酸钙可以稀释胶黏剂主要成分的分量，降低生产成本，由于脲醛树脂分量被稀释，单位体积的人造板含有的脲醛树脂减少，能够减少甲醛释放量。并且轻质碳酸钙能大幅度提高聚合物材料力学强度、尺寸稳定性和热变形温度，对提高胶黏剂与基材的胶合强度起到关键作用。
所述的EVA乳胶是乙烯-醋酸乙稀共聚乳液，来自于塞拉尼斯公司生产牌号为Ateva®的EVA胶乳。与聚乙烯相比，EVA由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，在人造板的热压生产过程中能提高人造板的密封性，提高防水、防潮性能。
本发明产生的积极效果：
1.本发明的防潮天花装饰板的生产方法使用的胶黏剂的原料之一脲醛树脂的生产采用一次加入甲醛，三次加入尿素的工艺，聚合反应速率始终保持平稳，避免了聚合反应凝胶效应的产生，甲醛单体几乎或者完全反应，所得脲醛树脂甲醛残留量低，因而制成的胶黏剂甲醛释放量少，最终人造板的甲醛残留量低，有利于保护消费者的健康。
2.本发明的防潮天花装饰板的生产方法使用的胶黏剂在脲醛树脂上加入聚丙烯酸酯乳液、聚二甲基硅氧烷和EVA乳胶，提高了脲醛树脂的耐水性，制成的胶黏剂防水、防潮性能好，能够提高人造板的密封性能，使水分、潮气难以渗入人造板内部，提高人造板的耐水性。
3. 本发明的防潮天花装饰板的生产方法采用三次冷压、三次热压和两次散热养生工艺，在多次冷、热压及散热过程，可以把人造板中的甲醛释放出来，并通过抽气系统收集处理，因此最终得到的人造板甲醛残留量低，并且三次冷压、三次热压和两次散热养生工艺使胶黏剂与纤维贴合得更紧，密封更全面，最终得到的人造板防水、防潮性能更好。
具体实施方式
实施例1
脲醛树脂的生产，包括如下步骤：
预聚合阶段：聚合反应釜中一次性加入甲醛溶液，用甲酸调节pH值为2～2.5，加入甲醛溶液重量15%的尿素，升温至46℃，保温反应60min。
聚合阶段：预聚合阶段结束，加碱调节反应液的pH值为8～8.5，加入甲醛溶液重量30%的尿素，40～60min内加完，然后升温反应液至88～92℃，保温反应90min。
聚合后期阶段：聚合阶段结束，加入甲醛溶液重量30～40%的尿素，40～60min内加完，然后降低反应温度至70～85℃，反应60～90min，降温至室温，得到脲醛树脂；
得到的脲醛树脂46份，搅拌下加入聚丙烯酸酯乳液10份，聚二甲基硅氧烷0.6份和EVA乳胶5份，搅拌混合均匀后，加入30份轻质碳酸钙，用三辊式研磨机研磨30min，得到防潮脲醛树脂胶黏剂。
实施例2
1m³锯屑加入150kg实施例1得到的防潮脲醛树脂胶黏剂，用搅拌机搅拌均匀，放入板材模具中，常温下用压缩机压缩，压力为2.5Mpa；然后放入热压机中，在130～135℃，1.5Mpa下热压；将板材放入恒温室自然通风冷却3～4h，用压缩机常温压缩，压力为2.5Mpa；放入热压机中，第二次热压，温度为125～130℃，压力为1.5Mpa，将板材放入恒温室自然通风冷却3～4h；用压缩机常温压缩，压力为2.5Mpa；再放入热压机中，第三次热压，温度为120～120℃，压力为1.5Mpa；然后升温至150℃，板材双面在1.5Mpa压力下表面贴三聚氰胺浸渍纸，鼓风冷却至室温，得到防潮天花装饰板。
实施例3
1m³坚果壳颗粒加入180kg实施例1得到的防潮脲醛树脂胶黏剂，用搅拌机搅拌均匀，放入板材模具中，常温下用压缩机压缩，压力为2.5Mpa；然后放入热压机中，在130～135℃，1.8Mpa下热压；将板材放入恒温室自然通风冷却3～4h，用压缩机常温压缩，压力为2.5Mpa；放入热压机中，第二次热压，温度为125～130℃，压力为1.8Mpa，将板材放入恒温室自然通风冷却3～4h；用压缩机常温压缩，压力为2.5Mpa；再放入热压机中，第三次热压，温度为120～120℃，压力为1.8Mpa；然后升温至150℃，板材双面在1.5Mpa压力下表面贴三氧化二铝耐磨纸，鼓风冷却至室温，得到防潮天花装饰板。
实施例4
1m³桑枝屑加入200kg实施例1得到的防潮脲醛树脂胶黏剂，用搅拌机搅拌均匀，放入板材模具中，常温下用压缩机压缩，压力为2.5Mpa；然后放入热压机中，在130～135℃，2.0Mpa下热压；将板材放入恒温室自然通风冷却3～4h，用压缩机常温压缩，压力为2.5Mpa；放入热压机中，第二次热压，温度为125～130℃，压力为2.0Mpa，将板材放入恒温室自然通风冷却3～4h；用压缩机常温压缩，压力为2.5Mpa；再放入热压机中，第三次热压，温度为120～120℃，压力为2.0Mpa；然后升温至150℃，板材双面在1.5Mpa压力下表面贴三聚氰胺浸渍纸，鼓风冷却至室温，得到防潮天花装饰板。
按照GB/T 11718-2009《中密度纤维板》，厚度9～13mm，对实施例中的人造板进行性能测试，各项检测结果如下表所示：
项目 甲醛释放量mg/m³（气候箱法） 内结合强度/MPa 防潮性能（沸腾试验后内结合强度）/Mpa 吸水厚度膨胀率/%
实施例1 0.41 - - -
实施例2 0.048 0.72 0.48 1.62
实施例3 0.026 0.85 0.63 1.37
实施例4 0.012 0.97 0.81 1.11
从表中看出，本发明的防潮天花装饰板的生产方法采用三次冷压、三次热压，两次散热养生的生产工艺能降低甲醛释放量，并能够提高人造板的防潮性能；采用本发明的方法制成的人造板适合用于生产天花装饰材料。

Claims (1)

1.防潮天花装饰板的生产方法，其特征在于：是将木材碎料或农作物收 获后产生的各类秸秆和坚果壳碎粒与防潮脲醛树脂胶黏剂混合压制成板材，然后板材再与三聚氰胺浸渍纸或三氧化二铝耐磨纸高温压贴而成；板材成型采用三次冷压和三次热压，两次散热养生；所述的冷压温度为室温，压力为2.5MPa，热压压力为1.5～2.0MPa；第一次热压的温度为130～135℃；第二次热压的温度为125～130℃，第三次热压的温度为120～125℃；所述的散热养生为恒温室自然通风冷却至室温，时间为3～4h；板材表面贴三聚氰胺浸渍纸或三氧化二铝耐磨纸是在150℃，压力为1.5Mpa下进行；
所述的防潮脲醛树脂胶黏剂原料和重量份数如下：
脲醛树脂 46；
聚丙烯酸酯乳液 10；
聚二甲基硅氧烷 0.6；
300目轻质碳酸钙 30；
EVA乳胶 5。
CN201310380105.XA 2013-08-28 2013-08-28 防潮天花装饰板的生产方法 Active CN103433993B (zh)