CN1033528C - 一种可溶性棉布的制造方法 - Google Patents
一种可溶性棉布的制造方法 Download PDFInfo
- Publication number
- CN1033528C CN1033528C CN 91110511 CN91110511A CN1033528C CN 1033528 C CN1033528 C CN 1033528C CN 91110511 CN91110511 CN 91110511 CN 91110511 A CN91110511 A CN 91110511A CN 1033528 C CN1033528 C CN 1033528C
- Authority
- CN
- China
- Prior art keywords
- cotton
- hours
- cotton cloth
- concentration
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种可溶性棉布的制造方法，将棉布在20～40%的氢氧化钠溶液中碱化处理1.5～2.5小时，压干，称重，接着将其在一氯醋酸∶酒精＝1∶1.5～2.5的混合液中，在75～90℃的温度下醚化反应2～4小时，然后在10～20%的稀盐酸中进行中和反应，接着用78%的酒精洗涤除盐，最后进行烘干，使其含水率≤10%。该棉布可作为精密仪器防潮的包装材料、妇婴卫生用品的吸湿村料、缝制核辐射防护服；还可作为止血纱布和皮肤大面积溃疡或疮伤病人的医疗服装。
Description
本发明涉及一种变性棉布的制造方法，尤其是用无机物和低分子量的有机化合物处理棉布，制造可溶性棉布的方法。
众所周知，普通棉布是不溶于水的，可以反复洗涤，但在一些特定的场合，如：精密仪器的防潮包装、妇婴卫生用品、核辐射防护服装以及大面积皮肤溃疡或疮伤病人的医疗服装，都不能使用普通的棉布。目前，虽有可溶性的止血纱布问世，但其只限于医疗领域使用。
本发明的目的在于提供一种能完全溶于水，便于销毁的变性棉布制造方法。
本发明的目的是通过以下方式完现的：即利用无机化合物和低分子量的有机化合物对棉布进行化学处理，使其改性。具体地说，将棉布置于浓度为20～40％的氢氧化钠溶液中浸泡1.5～2.5小时，每隔30分钟翻动一次，取出压干，称重，其重量为原棉布重量的2.5～3.5倍，接着将一氯醋酸∶酒精＝1∶1.5～2.5的混合液徐徐倒入盛有碱化棉布的醚化反应器中，搅匀，加盖密闭，在75～90℃的的温度下反应2～4小时，然后将棉布取出并置入盛有浓度为10～20％稀盐酸的容器中进行中和反应，直至溶液呈中性为止，用浓度为78％的酒精溶液将棉布洗涤除盐4～5次，再用浓度为95％的酒精洗涤除盐一次，最后将上述棉布进行烘干，使其含水率≤10％。
在本发明中，醚化反应最好在78～82℃的温度下反应2.5～3小时。由本发明制得的可溶性棉布其性能指标为：溶解度≥97％，游离纤维≤3％，酸碱度呈中性，含盐量≤3％，含水率≤10％。
本发明的可溶性棉布具有以下理化性能： 1、具有水溶性，在冷热水中极易膨胀，糊化，溶解，溶液呈粘性；2、无臭、无毒，对人体生理无害；3、具有止血功效，遇血(含组织液)能迅速吸收膨胀，促进凝血因子活化并堵塞毛细管末端而起止血作用，4、能吸附核放射尘埃，具有遇水溶解而便于销毁处理的性能；5、不溶于酸液及乙醇等有机溶剂，6、属于一种高分子阳离子型电解质，其溶解液遇重金属盐会产生沉淀作用。
由本发明制造的可溶性棉布用途广泛，在工业方面，可作为精密仪器防潮的包装材料、妇婴卫生用品的吸湿衬料，这可缝制核辐射防护服。在医学方面，经消毒的可溶性棉布可作为止血纱布使用，还可缝制患有大面积皮肤溃疡或疮伤病人的医疗服装，当换药更衣时容易被生理盐水或蒸馏水洗掉，使病人既无痛苦，并可保护伤口新长出来的组织不受破坏，缩短了愈合期。
下面结合实施例对本发明作更为详细的说明。
实施例1：
将棉布放入事先配好的浓度为30％的氢氧化钠溶液中，在55℃的温度下保持恒温1.5小时，每隔30分钟翻动一次，然后将碱化棉布取出，放入脱水机内压干(脱碱)，压干后称重，其重量为原棉布重量的3倍，接着，把事先配好的一氯醋酸∶酒精＝1∶2.5的混合液徐徐倒入盛有碱化棉布的醚化反应器内，搅匀，加盖密闭，在78±2℃的温度下反应4小时，然后将棉布取出并置入盛有浓度为15％，稀盐酸的容器中进行中和反应，直至用pH试纸测试溶液呈中性为止；接着用浓度为78％的酒精洗涤4次除盐，再用浓度为95％的酒精洗涤除盐一次，最后将上述棉布烘干，使其含水率为8％，如本产品用于医疗方面时，需将其在高温高压下消毒，再用塑料袋密封包装，如用于工业方面时，则不需消毒。
实施例2：
将棉布在25％浓度的氢氧化钠溶液中，在50℃的温度下浸泡2小时，压干，称重后在醚化反应器中，添加一氯醋酸∶酒精＝1∶2的混合液，在82±2℃的温度下反应3小时，其余工序与实施例1相同。
实施例3：
将棉布在35％浓度的氢氧化钠溶液中，在45℃的温度下浸泡2.5小时，压干，称重后在醚化反应器中，添加一氯醋酸∶酒精＝1∶1.5的混合液中，在88±2℃的温度下反应2小时，其余工序与实施例1相同。
Claims (2)
1、一种可溶性棉布的制造方法，其特征在于：将棉布置于浓度为20～40％的氢氧化钠溶液中在45～55℃的温度下浸泡1.5～2.5小时，每隔30分钟翻动一次，取出压干，称重，其重量为原棉布重量的2.5～3.5倍；接着将一氯醋酸∶酒精＝1∶1.5～2.5的混合液徐徐倒入盛有碱化棉布的醚化反应器中，搅匀，加盖密闭，在75～90℃的温度下反应2～4小时；然后将棉布取出并置入盛有浓度为10～20％稀盐酸的容器中进行中和反应，直至溶液呈中性为止；用浓度为78％的酒精溶液将棉布洗涤除盐4～5次，再用浓度为95％的酒精洗涤除盐一次；最后将上述棉布进行烘干，使其含水率≤10％。
2、根据权利要求1所述的可溶性棉布的制造方法，其特征在于：醚化反应在78～82℃的温度下反应2.5～3小时。