CN1061061A - 一种可溶性棉布的制造方法 - Google Patents
一种可溶性棉布的制造方法 Download PDFInfo
- Publication number
- CN1061061A CN1061061A CN 91110511 CN91110511A CN1061061A CN 1061061 A CN1061061 A CN 1061061A CN 91110511 CN91110511 CN 91110511 CN 91110511 A CN91110511 A CN 91110511A CN 1061061 A CN1061061 A CN 1061061A
- Authority
- CN
- China
- Prior art keywords
- cotton
- concentration
- hours
- temperature
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种可溶性棉布的制造方法,将棉布在20~
40%的氢氧化钠溶液中碱化处理1.5~2.5小时,压
干,称重,接着将其在一氯醋酸∶酒精=1∶1.5~2.5
的混合液中,在75~90℃的温度下醚化反应2~4小
时,然后在10~20%的稀盐酸中进行中和反应,接着
用78%的酒精洗涤除盐,最后进行烘干,使其含水率
≤10%。该棉布可作为精密仪器防潮的包装材料、
妇婴卫生用品的吸湿衬料、缝制核辐射防护服;还可
作为止血纱布和皮肤大面积溃疡或疮伤病人的医疗
服装。
Description
本发明涉及一种变性棉布的制造方法,尤其是用无机物和低分子量的有机化合物处理棉布,制造可溶性棉布的方法。
众所周知,普通棉布是不溶于水的,可以反复洗涤,但在一些特定的场合,如:精密仪器的防潮包装、妇婴卫生用品、核辐射防护服装以及大面积皮肤溃疡或疮伤病人的医疗服装,都不能使用普通的棉布。目前,虽有可溶性的止血纱布问世,但其只限于医疗领域使用。
本发明的目的在于提供一种能完全溶于水,便于销毁的变性棉布的制造方法。
本发明的目的是通过以下方式完现的:即利用无机化合物和低分子量的有机化合物对棉布进行化学处理,使其改性。具体地说,将棉布置于浓度为20~40%的氢氧化钠溶液中浸泡1.5~2.5小时,每隔30分钟翻动一次,取出压干,称重,其重量为原棉布重量的2.5~3.5倍,接着将一氯醋酸∶酒精=1∶1.5~2.5的混合液徐徐倒入盛有碱化棉布的醚化反应器中,搅匀,加盖密闭,在75~90℃的温度下反应2~4小时,然后将棉布取出并置入盛有浓度为10~20%稀盐酸的容器中进行中和反应,直至溶液呈中性为止,用浓度为78%的酒精溶液将棉布洗涤除盐4~5次,再用浓度为95%的酒精洗涤除盐一次,最后将上述棉布进行烘干,使其含水率≤10%。
在本发明中,醚化反应最好在78~82℃的温度下反应2.5~3小时。
由本发明制得的可溶性棉布其性能指标为:溶解度≥97%,游离纤维≤3%,酸碱度呈中性,含盐量≤3%,含水率≤10%。
本发明的可溶性棉布具有以下理化性能:1、具有水溶性,在冷热水中极易膨胀,糊化,溶解,溶液呈粘性;2、无臭、无毒,对人体生理无害;3、具有止血功效,遇血(含组织液)能迅速吸收膨胀,促进凝血因子活化并堵塞毛细管末端而起止血作用;4、能吸附核放射尘埃,具有遇水溶解而便于销毁处理的性能;5、不溶于酸液及乙醇等有机溶剂;6、属于一种高分子阳离子型电解质,其溶解液遇重金属盐会产生沉淀作用。
由本发明制造的可溶性棉布用途广泛,在工业方面,可作为精密仪器防潮的包装材料、妇婴卫生用品的吸湿衬料,还可缝制核辐射防护服。在医学方面,经消毒的可溶性棉布可作为止血纱布使用,还可缝制患有大面积皮肤溃疡或疮伤病人的医疗服装,当换药更衣时容易被生理盐水或蒸馏水洗掉,使病人既无痛苦,并可保护伤口新长出来的组织不受破坏,缩短了愈合期。
下面结合实施例对本发明作更为详细的说明。
实施例1:
将棉布放入事先配好的浓度为30%的氢氧化钠溶液中,在55℃的温度下保持恒温1.5小时,每隔30分钟翻动一次,然后将碱化棉布取出,放入脱水机内压干(脱碱),压干后称重,其重量为原棉布重量的3倍;接着,把事先配好的一氯醋酸∶酒精=1∶2.5的混合液徐徐倒入盛有碱化棉布的醚化反应器内,搅匀,加盖密闭,在78±2℃的温度下反应4小时,然后将棉布取出并置入盛有浓度为15%稀盐酸的容器中进行中和反应,直至用PH试纸测试溶液呈中性为止;接着用浓度为78%的酒精洗涤4次除盐,再用浓度为95%的酒精洗涤除盐一次,最后将上述棉布烘干,使其含水率为8%。如本产品用于医疗方面时,需将其在高温高压下消毒,再用塑料袋密封包装;如用于工业方面时,则不需消毒。
实施例2:
将棉布在25%浓度的氢氧化钠溶液中,在50℃的温度下浸泡2小时,压干,称重后在醚化反应器中,添加一氯醋酸∶酒精=1∶2的混合液,在82±2℃的温度下反应3小时,其余工序与实施例1相同。
实施例3:
将棉布在35%浓度的氢氧化钠溶液中,在45℃的温度下浸泡2.5小时,压干,称重后在醚化反应器中,添加一氯醋酸∶酒精=1∶1.5的混合液中,在88±2℃的温度下反应2小时,其余工序与实施例1相同。
Claims (2)
1、一种可溶性棉布的制造方法,其特征在于:将棉布置于浓度为20~40%的氢氧化钠溶液中在45~55℃的温度下浸泡1.5~2.5小时,每隔30分钟翻动一次,取出压干,称重,其重量为原棉布重量的2.5~3.5倍,接着将一氯醋酸∶酒精=1∶1.5~2.5的混合液徐徐倒入盛有碱化棉布的醚化反应器中,搅匀,加盖密闭,在75~90℃的温度下反应2~4小时,然后将棉布取出并置入盛有浓度为10~20%稀盐酸的容器中进行中和反应,直至溶液呈中性为止,用浓度为78%的酒精溶液将棉布洗涤除盐4~5次,再用浓度为95%的酒精洗涤除盐一次,最后将上述棉布进行烘干,使其含水率≤10%。
2、根据权利要求1所述的可溶性棉布的制造方法,其特征在于:醚化反应在78~82℃的温度下反应2.5~3小时。