CN103224619A - 粉末涂料用聚酯树脂及其制备方法 - Google Patents
粉末涂料用聚酯树脂及其制备方法 Download PDFInfo
- Publication number
- CN103224619A CN103224619A CN201210021274XA CN201210021274A CN103224619A CN 103224619 A CN103224619 A CN 103224619A CN 201210021274X A CN201210021274X A CN 201210021274XA CN 201210021274 A CN201210021274 A CN 201210021274A CN 103224619 A CN103224619 A CN 103224619A
- Authority
- CN
- China
- Prior art keywords
- parts
- reactant
- acid number
- powder coating
- polyester resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及粉末涂料领域，具体涉及一种与环氧树脂70:30固化的室内粉末涂料用聚酯树脂及其制备方法，该聚酯树脂的组分及重量配比为：新戊二醇20～30份，乙二醇5～8份，二乙二醇10～20份，三羟甲基丙烷1～3份，对苯二甲酸50～60份，偏苯三酸酐2～3份，催化剂0.2～0.5份，固化促进剂1～3份。用该聚酯树脂制备的粉末涂料具有高流平性、高填料量等优点，特别适用于制作亚光粉。
Description
技术领域
本发明涉及粉末涂料领域，具体涉及一种与环氧树脂70:30固化的室内粉末涂料用聚酯树脂及其制备方法。
背景技术
粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有不用溶剂、无污染、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。聚酯粉末涂料与其它类型粉末涂料相比，具有独特性质。表现在耐候性、耐紫外旋光性能比环氧树脂好。另外由于聚酯树脂带有极性基团，所以上粉率比环氧树脂高，烘烤过程中不易泛黄，光泽度高，流平性好，漆膜丰满，颜色浅等特性，因而具有很好的装饰性。
发明内容
本发明目的在于提供一种制备具有高流平性、高填料量等优点的室内粉末涂料用聚酯树脂。
本发明采用的技术方案是：本发明的一种室内粉末涂料用聚酯树脂的组分及重量配比为：新戊二醇20～30份，乙二醇5～8份，二乙二醇10～20份，三羟甲基丙烷1～3份，对苯二甲酸50～60份，偏苯三酸酐10～20份，催化剂0.2～0.5份，固化促进剂1～3份。
制备权利要求1所述的一种粉末涂料用聚酯树脂的方法，包括以下步骤：
a、在反应釜中，将釜温升至80℃，加入新戊二醇20～30份，乙二醇5～8份，二乙二醇10～20份，三羟甲基丙烷1～3份，对苯二甲酸50～60份，催化剂0.2～0.5份；
b、将反应釜温度按2～3℃/15分钟升温速率逐步提升到235℃，并在235℃温度下进行反应100～120分钟，直至反应物的酸值为7～10mgKOH/g；
c、待检测反应物的酸值为7～10mgKOH/g后，在0.090～0.095MPa真空下进行30～60分钟的缩聚反应，直至反应物的酸值为45～48mgKOH/g；
d、待检测反应物的酸值为45～48mgKOH/g后，加入偏苯三酸酐10～20份，在釜温235℃条件下进行30～60分钟的反应，直至反应物的酸值为28～32mgKOH/g；
e、待检测反应物的酸值为28～32mgKOH/g后，加入固化促进剂1～3份，在温度降至180～200℃条件下进行至少30分钟的混合后出料。
所述的催化剂为单丁基氧化锌。
所述的固化促进剂为18/16叔胺。
本发明的优点是：由本发明聚酯树脂制备的粉末涂料具有高流平性、高填料量等优点，特别适用于制作亚光粉。
具体实施方式
在聚酯反应釜中，将釜温加热到80℃,投入新戊二醇、乙二醇、二乙二醇、三羟甲基丙烷、对苯二甲酸、催化剂单丁基氧化锌，将反应釜温度按2～3℃/15分钟升温速率逐步提升到235℃，并在235℃温度下进行反应100～120分钟，直至反应物的酸值为7～10mgKOH/g；待检测反应物的酸值为7～10mgKOH/g后，在0.090～0.095MPa真空下进行30～60分钟的缩聚反应，直至反应物的酸值为45～48mgKOH/g；待检测反应物的酸值为45～48mgKOH/g后，加入偏苯三酸酐，在釜温235℃条件下进行30～60分钟的反应，直至反应物的酸值为28～32mgKOH/g；待检测反应物的酸值为28～32mgKOH/g后，加入固化促进剂18/16叔胺，在温度降至180～200℃条件下进行至少30分钟的混合后出料。
实施例1：
在聚酯反应釜中，将釜温加热到80℃,投入新戊二醇20份、乙二醇5份、二乙二醇10份、三羟甲基丙烷1份、对苯二甲酸50份、催化剂单丁基氧化锌0.2份，将反应釜温度按2℃/15分钟升温速率逐步提升到235℃，并在235℃温度下进行反应110分钟，直至反应物的酸值为7mgKOH/g；待检测反应物的酸值为7mgKOH/g后，在0.09MPa真空下进行45分钟的缩聚反应，直至反应物的酸值为45mgKOH/g；待检测反应物的酸值为45mgKOH/g后，加入偏苯三酸酐10份，在釜温235℃条件下进行45分钟的反应，直至反应物的酸值为28mgKOH/g；待检测反应物的酸值为28mgKOH/g后，加入固化促进剂18/16叔胺1份，在温度降至180℃条件下进行35分钟的混合后出料。
所制得的聚酯树脂的酸值为28mgKOH/g，玻璃化温度为50℃，软化点为103℃。
实施例2：
在聚酯反应釜中，将釜温加热到80℃,投入新戊二醇25份、乙二醇6份、二乙二醇15份、三羟甲基丙烷2份、对苯二甲酸55份、催化剂单丁基氧化锌0.4份，将反应釜温度按2℃/15分钟升温速率逐步提升到235℃，并在235℃温度下进行反应110分钟，直至反应物的酸值为9mgKOH/g；待检测反应物的酸值为9mgKOH/g后，在0.095MPa真空下进行45分钟的缩聚反应，直至反应物的酸值为47mgKOH/g；待检测反应物的酸值为47mgKOH/g后，加入偏苯三酸酐15份，在釜温235℃条件下进行45分钟的反应，直至反应物的酸值为30mgKOH/g；待检测反应物的酸值为30mgKOH/g后，加入固化促进剂18/16叔胺2份，在温度降至180℃条件下进行45分钟的混合后出料。
所制得的聚酯树脂的酸值为30mgKOH/g，玻璃化温度为55℃，软化点为108℃。
实施例3：
在聚酯反应釜中，将釜温加热到80℃,投入新戊二醇30份、乙二醇8份、二乙二醇20份、三羟甲基丙烷3份、对苯二甲酸60份、催化剂单丁基氧化锌0.5份，将反应釜温度按3℃/15分钟升温速率逐步提升到235℃，并在235℃温度下进行反应120分钟，直至反应物的酸值为10mgKOH/g；待检测反应物的酸值为10mgKOH/g后，在0.095MPa真空下进行45分钟的缩聚反应，直至反应物的酸值为48mgKOH/g；待检测反应物的酸值为48mgKOH/g后，加入偏苯三酸酐20份，在釜温235℃条件下进行45分钟的反应，直至反应物的酸值为32mgKOH/g；待检测反应物的酸值为32mgKOH/g后，加入固化促进剂18/16叔胺3份，在温度降至200℃条件下进行30分钟的混合后出料。
所制得的聚酯树脂的酸值为32mgKOH/g，玻璃化温度为60℃，软化点为110℃。
Claims (4)
1.粉末涂料用聚酯树脂，其特征在于， 该聚酯树脂的组分及重量配比为：新戊二醇20～30份，乙二醇5～8份，二乙二醇10～20份，三羟甲基丙烷1～3份，对苯二甲酸50～60份，偏苯三酸酐10～20份，催化剂0.2～0.5份，固化促进剂1～3份。
2.制备权利要求1所述的一种室内粉末涂料用聚酯树脂的方法，其特征在于，包括以下步骤：
a、在反应釜中，将釜温升至80℃，加入新戊二醇20～30份，乙二醇5～8份，二乙二醇10～20份，三羟甲基丙烷1～3份，对苯二甲酸50～60份，催化剂0.2～0.5份；
b、将反应釜温度按2～3℃/15分钟升温速率逐步提升到235℃，并在235℃温度下进行反应100～120分钟，直至反应物的酸值为7～10mgKOH/g；
c、待检测反应物的酸值为7～10mgKOH/g后，在0.090～0.095MPa真空下进行30～60分钟的缩聚反应，直至反应物的酸值为45～48mgKOH/g；
d、待检测反应物的酸值为45～48mgKOH/g后，加入偏苯三酸酐10～20份，在釜温235℃条件下进行30～60分钟的反应，直至反应物的酸值为28～32mgKOH/g；
e、待检测反应物的酸值为28～32mgKOH/g后，加入固化促进剂1～3份，在温度降至180～200℃条件下进行至少30分钟的混合后出料。
3.根据权利要求2所述的一种室内粉末涂料用聚酯树脂的方法，其特征在于，所述的催化剂为单丁基氧化锌。
4.根据权利要求2所述的一种室内粉末涂料用聚酯树脂的方法，其特征在于，所述的固化剂为18/16叔胺。