CN103212448A - 一种堇青石蜂窝陶瓷载体涂层的制备方法 - Google Patents

一种堇青石蜂窝陶瓷载体涂层的制备方法 Download PDF

Info

Publication number
CN103212448A
CN103212448A CN2013101003267A CN201310100326A CN103212448A CN 103212448 A CN103212448 A CN 103212448A CN 2013101003267 A CN2013101003267 A CN 2013101003267A CN 201310100326 A CN201310100326 A CN 201310100326A CN 103212448 A CN103212448 A CN 103212448A
Authority
CN
China
Prior art keywords
honeycomb ceramic
ceramic carrier
cordierite honeycomb
preparation
carrier
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN2013101003267A
Other languages
English (en)
Inventor
杨忠辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU ZHONGHUI HONEYCOMB CERAMICS CO Ltd
Original Assignee
SUZHOU ZHONGHUI HONEYCOMB CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU ZHONGHUI HONEYCOMB CERAMICS CO Ltd filed Critical SUZHOU ZHONGHUI HONEYCOMB CERAMICS CO Ltd
Priority to CN2013101003267A priority Critical patent/CN103212448A/zh
Publication of CN103212448A publication Critical patent/CN103212448A/zh
Withdrawn legal-status Critical Current

Abstract

一种堇青石蜂窝陶瓷载体涂层的制备方法，称取一定量的拟薄水铝石粉，加入去离子水搅拌成拟薄水铝石粉悬浮液，在冷却回流的情况下，按比例滴加一定量的2mol/L-4mol/L的硝酸胶溶剂进行解胶，并控制成胶温度和回流搅拌时间，制备溶胶；将酸洗、水洗预处理后的堇青石蜂窝陶瓷载体，浸渍在溶胶中20min-40min后，取出，吹尽残留在孔道中的胶液，室温自然干燥过夜后，100℃-120℃烘干12h-20h，马弗炉中500℃-550℃焙烧3h-5h。采用本发明的钯铈铝蜂窝陶瓷催化剂的制备方法所得的催化剂氧化活性得到显著提高。使蜂窝陶瓷载体涂覆后形成的氧化铝涂层的比表面积增大，达到了作为催化剂载体的要求。

Description

一种堇青石蜂窝陶瓷载体涂层的制备方法
技术领域
本发明属于陶瓷材料领域，涉及一种蜂窝陶瓷的制备方法，具体涉及一种堇青石蜂窝陶瓷载体涂层的制备方法。
背景技术
堇青石蜂窝陶瓷体具有机械强度高、压力降小、热膨胀系数低、热稳定性好等特点，被用作三效催化剂的载体，但是堇青石蜂窝陶瓷载体的比表面积很小，所以必须在堇青石蜂窝陶瓷载体表面再涂覆一层高比表面积的活性涂层。
γ-Al2O3是应用最为广泛的涂层材料之一，车用整体式三元催化剂就是以涂覆有γ-Al2O3涂层的蜂窝陶瓷体作为催化剂载体，目前，为了提高涂层的热稳定性和助催化作用，在涂层中还加入了活性助剂组分CeO2-ZrO2-M2O3固溶体。在γ-Al2O3蜂窝陶瓷载体涂层的制备过程中，铝溶胶的性能直接影响着氧化铝涂层的稳定性和可涂覆性，决定着氧化铝涂层的比表面积以及涂层与蜂窝载体的结合强度。因此，铝溶胶的性能是车用整体式三元催化剂制备过程中的关键因素之一。制备铝溶胶的方法较多，其中以拟薄水铝石为原料，通过酸胶溶方法制备铝溶胶的工艺便于控制，易于定量化，更适宜工业化生产，但利用该方法制备铝溶胶过程中的影响因素较多。
发明内容
为了克服现有技术的不足，本发明提供了一种堇青石蜂窝陶瓷载体涂层的制备方法。
本发明的堇青石蜂窝陶瓷载体涂层的制备方法，包括下述步骤：
称取一定量的拟薄水铝石粉，加入去离子水搅拌成拟薄水铝石粉悬浮液，在冷却回流的情况下，按比例滴加一定量的2mol/L-4mol/L的硝酸胶溶剂进行解胶，并控制成胶温度和回流搅拌时间，制备溶胶；
将酸洗、水洗预处理后的堇青石蜂窝陶瓷载体，浸渍在溶胶中20min-40min后，取出，吹尽残留在孔道中的胶液，室温自然干燥过夜后，100℃-120℃烘干12h-20h，马弗炉中500℃-550℃焙烧3h-5h。
优选的，滴加的硝酸胶溶剂浓度为3mol/L。
优选的，室温自然干燥过夜后，110℃烘干15h。
优选的，马弗炉中520℃焙烧4h。
本发明经铝溶胶涂覆形成氧化铝涂层后，堇青石蜂窝陶瓷载体孔径明显减小，形成微孔，孔隙率增大，从而使蜂窝陶瓷载体涂覆后形成的氧化铝涂层的比表面积增大，达到了作为催化剂载体的要求。
具体实施方式
下面结合实施例对本发明的堇青石蜂窝陶瓷载体涂层的制备方法进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1
称取一定量的拟薄水铝石粉，加入去离子水搅拌成拟薄水铝石粉悬浮液，在冷却回流的情况下，按比例滴加一定量的2mol/L的硝酸胶溶剂进行解胶，并控制成胶温度和回流搅拌时间，制备溶胶；
将酸洗、水洗预处理后的堇青石蜂窝陶瓷载体，浸渍在溶胶中20min后，取出，吹尽残留在孔道中的胶液，室温自然干燥过夜后，100℃烘干20h，马弗炉中500℃焙烧5h。
实施例2
称取一定量的拟薄水铝石粉，加入去离子水搅拌成拟薄水铝石粉悬浮液，在冷却回流的情况下，按比例滴加一定量的4mol/L的硝酸胶溶剂进行解胶，并控制成胶温度和回流搅拌时间，制备溶胶；
将酸洗、水洗预处理后的堇青石蜂窝陶瓷载体，浸渍在溶胶中40min后，取出，吹尽残留在孔道中的胶液，室温自然干燥过夜后，120℃烘干12h，马弗炉中550℃焙烧3h。
实施例3
称取一定量的拟薄水铝石粉，加入去离子水搅拌成拟薄水铝石粉悬浮液，在冷却回流的情况下，按比例滴加一定量的3mol/L的硝酸胶溶剂进行解胶，并控制成胶温度和回流搅拌时间，制备溶胶；
将酸洗、水洗预处理后的堇青石蜂窝陶瓷载体，浸渍在溶胶中30min后，取出，吹尽残留在孔道中的胶液，室温自然干燥过夜后，110℃烘干15h，马弗炉中520℃焙烧4h。
上述实施例不以任何方式限制本发明，凡是采用等同替换或等效变换的方式获得的技术方案均落在本发明的保护范围内。

Claims (4)

1.一种堇青石蜂窝陶瓷载体涂层的制备方法，其特征在于，包括下述步骤：
称取一定量的拟薄水铝石粉，加入去离子水搅拌成拟薄水铝石粉悬浮液，在冷却回流的情况下，按比例滴加一定量的2mol/L-4mol/L的硝酸胶溶剂进行解胶，并控制成胶温度和回流搅拌时间，制备溶胶；
将酸洗、水洗预处理后的堇青石蜂窝陶瓷载体，浸渍在溶胶中20min-40min后，取出，吹尽残留在孔道中的胶液，室温自然干燥过夜后，100℃-120℃烘干12h-20h，马弗炉中500℃-550℃焙烧3h-5h。
2.根据权利要求1所述的堇青石蜂窝陶瓷载体涂层的制备方法，其特征在于：滴加的硝酸胶溶剂浓度为3mol/L。
3.根据权利要求1所述的堇青石蜂窝陶瓷载体涂层的制备方法，其特征在于：室温自然干燥过夜后，110℃烘干15h。
4.根据权利要求1所述的堇青石蜂窝陶瓷载体涂层的制备方法，其特征在于：马弗炉中520℃焙烧4h。
CN2013101003267A 2013-03-26 2013-03-26 一种堇青石蜂窝陶瓷载体涂层的制备方法 Withdrawn CN103212448A (zh)