CN103085214A - 一种含有新型冷却工艺的酚醛模塑料加工方法 - Google Patents
一种含有新型冷却工艺的酚醛模塑料加工方法 Download PDFInfo
- Publication number
- CN103085214A CN103085214A CN2013100069074A CN201310006907A CN103085214A CN 103085214 A CN103085214 A CN 103085214A CN 2013100069074 A CN2013100069074 A CN 2013100069074A CN 201310006907 A CN201310006907 A CN 201310006907A CN 103085214 A CN103085214 A CN 103085214A
- Authority
- CN
- China
- Prior art keywords
- cooling
- temperature
- degree
- minutes
- temperature region
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种含有新型冷却工艺的酚醛模塑料加工方法,其步骤包括混料、挤出、压片、冷却、粉碎、筛选,所述冷却步骤包括二级暖风区冷却:高温区冷却,经压片后得到的料片,在10米长的暖风道中,缓慢行进2~3分钟,其中暖风道温度为45~50度;低温区冷却,经高温区冷却后的料片,在15米长的冷风道中,缓慢行进2~3分钟,其中冷风道上方顶吹风温度为10~15度。本发明的优点在于:减少了酚醛模塑料生产过程中产生的成品细粉料,同时提高了利用酚醛模塑料制造各种成品的机械强度。
Description
技术领域
本发明涉及一种酚醛模塑料的加工方法,特别涉及一种不同于以往冷却工艺的酚醛模塑料的加工方法。
背景技术
酚醛模塑料,俗称电木粉,是一种硬而脆的热固性塑料,以酚醛树脂为基材的塑料的总称,是最重要的热固性塑料之一,广泛用作电绝缘材料、家具零件、日用品、工艺品等。
现有的酚醛模塑料加工方法是:由成品细粉、酚醛树脂、玻璃纤维等原材料混合后,经过挤出、压片、强制冷却、粉碎、筛选等工艺步骤制得。其中压片为双辊压成片,强制冷却为在输送钢带上进行冷却,粉碎为达到冷却要求后使用粉碎机经行粉碎。
然而,在粉碎过程中,粉碎机刀片打碎料片时,会产生大量的成品细粉料,粒度远远小于使用要求,不符合要求的成品细粉料占成品粉料的10~30%。这样不仅造成了很大的浪费、增加了生产成本;而且利用现有工艺方法得到的酚醛模塑料制造的各种成品,其机械强度往往不高。
发明内容
本发明的目的是提供一种含有新型冷却工艺的酚醛模塑料加工方法,以减少酚醛模塑料生产过程中产生的成品细粉料,同时提高利用酚醛模塑料制造各种成品的机械强度。
为实现上述目的,本发明通过以下技术方案实现:
一种含有新型冷却工艺的酚醛模塑料加工方法,其步骤包括混料、挤出、压片、冷却、粉碎、筛选,所述冷却步骤包括二级暖风区冷却:
1)高温区冷却:经压片后得到的料片,在10米长的暖风道中,缓慢行进2~3分钟,其中暖风道温度为45~50度;
2) 低温区冷却:经高温区冷却后的料片,在15米长的冷风道中,缓慢行进2~3分钟,其中冷风道上方顶吹风温度为10~15度。
特别地,所述高温区冷却子步骤中,控制温度在45~50度之间的方法为:10米长的暖风道顶部,通过每隔2米安装一个板式换热器,每个板式换热器外接一个模温机,工作前提前20分钟进行预热;暖风道侧面架设可变频的风机,通过暖风道内的温控测量及反馈,来控制温度在45~50度之间,同时抽去换热带来的水气。
特别地,所述低温区冷却子步骤中,控制温度在10~15度之间的方法为:15米长的冷风道顶端连接有变风量风机,外部设有一个大型板式换热箱,大型板式换热箱外接一个工艺冷冻机组及一个模温机,通过风道内的温控测量及反馈,来自动控制风量大小及冷热源切换,来控制温度在10~15度之间。
本发明的有益效果在于:减少了酚醛模塑料生产过程中产生的成品细粉料,同时提高了利用酚醛模塑料制造各种成品的机械强度。
具体实施方式
实施例1 | 实施例2 | 实施例3 | 实施例4 | |
成品细粉 | 100 | 100 | 100 | 100 |
酚醛树脂 | 10 | 10 | 10 | 10 |
玻璃纤维 | 15 | 15 | 15 | 15 |
时间(分钟) | 2 | 3 | 2 | 3 |
风道1温度(度) | 46 | 49 | 48 | 49 |
时间(分钟) | 3 | 2 | 2 | 3 |
风道2温度(度) | 11 | 12 | 13 | 11 |
粉料比例(%) | 6 | 6.5 | 7.8 | 5.9 |
弯曲强度(Mp) | 200 | 198 | 205 | 200 |
结论 | 合格 | 合格 | 合格 | 合格 |
以上原料组分均以重量计。
实施例1:
一种含有新型冷却工艺的酚醛模塑料加工方法,其步骤包括混料(成品细粉100份、酚醛树脂10份、玻璃纤维15份)、挤出、压片、冷却、粉碎、筛选,所述冷却步骤包括二级暖风区冷却:
1)高温区冷却:经压片后得到的料片,在10米长的暖风道中,缓慢行进2分钟,其中暖风道温度为46度;
2) 低温区冷却:经高温区冷却后的料片,在15米长的冷风道中,缓慢行进3分钟,其中冷风道上方顶吹风温度为11度。
特别地,所述高温区冷却子步骤中,控制温度在45~50度之间的方法为:10米长的暖风道顶部,通过每隔2米安装一个板式换热器,每个板式换热器外接一个模温机,工作前提前20分钟进行预热;暖风道侧面架设可变频的风机,通过暖风道内的温控测量及反馈,来控制温度在45~50度之间,同时抽去换热带来的水气。
特别地,所述低温区冷却子步骤中,控制温度在10~15度之间的方法为:15米长的冷风道顶端连接有变风量风机,外部设有一个大型板式换热箱,大型板式换热箱外接一个工艺冷冻机组及一个模温机,通过风道内的温控测量及反馈,来自动控制风量大小及冷热源切换,来控制温度在10~15度之间。
实施例2:
除了步骤1)中缓慢行进3分钟,其中暖风道温度为49度,步骤2)中缓慢行进2分钟,其中冷风道上方顶吹风温度为12度之外,其他条件及实施步骤均与实施例1相同。
实施例3:
除了步骤1)中缓慢行进2分钟,其中暖风道温度为48度,步骤2)中缓慢行进2分钟,其中冷风道上方顶吹风温度为13度之外,其他条件及实施步骤均与实施例1相同。
实施例4:
除了步骤1)中缓慢行进3分钟,其中暖风道温度为49度,步骤2)中缓慢行进3分钟,其中冷风道上方顶吹风温度为11度之外,其他条件及实施步骤均与实施例1相同。
Claims (3)
1.一种含有新型冷却工艺的酚醛模塑料加工方法,其步骤包括混料、挤出、压片、冷却、粉碎、筛选,其特征在于:所述冷却步骤包括二级暖风区冷却:
高温区冷却:经压片后得到的料片,在10米长的暖风道中,缓慢行进2~3分钟,其中暖风道温度为45~50度;
低温区冷却:经高温区冷却后的料片,在15米长的冷风道中,缓慢行进2~3分钟,其中冷风道上方顶吹风温度为10~15度。
2.如权利要求1所述的含有新型冷却工艺的酚醛模塑料加工方法,其特征在于:所述高温区冷却子步骤中,控制温度在45~50度之间的方法为:10米长的暖风道顶部,通过每隔2米安装一个板式换热器,每个板式换热器外接一个模温机,工作前提前20分钟进行预热;暖风道侧面架设可变频的风机,通过暖风道内的温控测量及反馈,来控制温度在45~50度之间,同时抽去换热带来的水气。
3.如权利要求1所述的含有新型冷却工艺的酚醛模塑料加工方法,其特征在于:所述低温区冷却子步骤中,控制温度在10~15度之间的方法为:15米长的冷风道顶端连接有变风量风机,外部设有一个大型板式换热箱,大型板式换热箱外接一个工艺冷冻机组及一个模温机,通过风道内的温控测量及反馈,来自动控制风量大小及冷热源切换,来控制温度在10~15度之间。