CN102875187B - 一种高强度加气混凝土砌块 - Google Patents
一种高强度加气混凝土砌块 Download PDFInfo
- Publication number
- CN102875187B CN102875187B CN201210304881.7A CN201210304881A CN102875187B CN 102875187 B CN102875187 B CN 102875187B CN 201210304881 A CN201210304881 A CN 201210304881A CN 102875187 B CN102875187 B CN 102875187B
- Authority
- CN
- China
- Prior art keywords
- building block
- powder
- parts
- concrete block
- aerated concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种高强度加气混凝土砌块，其是由下述重量份的原料按照加气混凝土砌块常规制造工艺制得：矾矿尾渣28-32、水泥5-10、生石灰10-15、改性纳米粉5-10、电石渣5-10、石膏3-5、铝粉0.05-0.1、平平加0.002-0.008、碳酸氢钙0.03-0.08、纯碱0.003-0.005、硬脂酸钙0.5-0.8、硬脂酸锌0.3-0.5、硅酸钠0.01-0.03、羟丙基甲基纤维素钠0.05-0.1、水适量。本发明通过添加纳米粉末矿粉，减轻了砖的容重，同时，减少了能源消耗；本发明砖隔热与隔音性能均好，较现有高强度加气混凝土砌块有明显提高。同时本发明通过优化配方用料，本发明的强度、抗冻性有了明显提高。
Description
技术领域
本发明涉及砌块领域，确切地说是一种高强度加气混凝土砌块。
背景技术
加气混凝土是一种新型的墙体建材，它的独特之处在于它是一种非常轻型的保温隔热的新型建筑墙材。气混凝土技术始于一百年前，而我国的该项技术开始的比较晚，比国外整整落后了四十年，但是，我国的加气混凝土行业的发展确实非常迅速的。现在国内的加气混凝土技术工艺水平已经可以达到了国际先进水平。
加气混凝土最大优势就是节约土地资源，不用浪费大量的耕地，而且它的原料的来源非常的广泛，灰沙，矿渣，矾矿尾渣和煤矸石等等都是做加气混凝土的原材料。而且加气混凝土的性能特点非常的优越，有非常好的可加工能力和隔热和保温能力，而且可塑性非常的强，可铇可锯，有非常好的加工特性。
根据权威人士统计，前几年国内的的加气混凝土行业生产企业有300多家。各个厂家的生产能力也不一样，有年产两万立方的也有年产十万立方的少数也有年产三十万立方的。而现在加气混凝土行业热已经慢慢的发展开来，现在粗略的统计，国内的的加气混凝土生产厂家数量是以前的好几倍。
加气混凝土的应用非常的广泛，主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和州周围的填充围墙。
逐渐，加气混凝土已成为建筑材料行业的主导展品，国家现在已经对粘土实心砖的进行禁止停产。逐渐取而代之的就是加气混凝土砌块，蒸压砖。然而一般常规加气混凝土制造的加气混凝土砌块的强度较低。
平平加又名脂肪醇聚氧乙烯醚 ，属非离子型表面活性剂，外观为乳白色或米黄色软膏状，分子量较高时，呈固体状(可根据要求制成片状固体)，易溶于水、乙醇、乙二醇等，有浊点,1%水溶液PH值为中性。能耐酸、耐碱、耐硬水、耐热、耐重金属盐。对各种染料有强力的匀染性、缓染性、渗透性、扩散性，煮练时具助练性能，可与各类表面活性剂和染料同溶使用。
赤泥是制铝工业提取氧化铝时排出的污染性废渣，一般平均每生产1吨氧化铝，附带产生 1.0～2.0吨赤泥。中国作为世界第4大氧化铝生产国，每年排放的赤泥高达数百万吨。
赤泥矿物成分复杂，采用多种方法对其进行分析，主要有以下几种方法：偏光显微镜、扫描显微镜、差热分析仪、X衍射、化学全分析、红外吸收光谱和穆斯堡尔谱法等七种方法进行测定，其结果是赤泥的主要矿物为文石和方解石，含量为60%~65%，其次是蛋白石、三水铝石、针铁矿，含量最少的是钛矿石、菱铁矿、天然碱、水玻璃、铝酸钠和火碱。其矿物成分复杂，且不符合天然土的矿物组合。在这些矿石中，文石、方解石和菱铁矿，既是骨架，又有一定的胶结作用；而针铁矿、三水铝石、蛋白石、水玻璃起胶结作用和填充作用。
发明内容
本发明的目的是提供一种强度高、容重小的高强度加气混凝土砌块。
上述目的通过以下方案实现：
一种高强度加气混凝土砌块，其特征在于，其是由下述重量份的原料按照加气混凝土砌块常规制造工艺制得：矾矿尾渣28-32、水泥5-10、生石灰10-15、改性纳米粉5-10、电石渣2-4、石英粉1-2、石膏3-5、铝粉0.05-0.1、平平加0.002-0.008、碳酸氢钙0.01-0.02、纯碱 0.003-0.005、硬脂酸钙0.5-0.8、硬脂酸锌0.3-0.5、硅酸钠0.01-0.03、羟丙基甲基纤维素钠0.05-0.1、水适量；
改性纳米粉的制备方法为：由8-9重量份碳酸钙、1-2重量份陶粒、1-2重量份页岩、2-4重量份赤泥、3-6重量份凹凸棒土混匀后在600-700℃下烧损4-5小时，后研磨成纳米粉末，拌入相当于粉体重量1-2%的环氧亚麻子油、1-2%的木质素磺酸钙拌搅均匀，烘干，粉碎成粉末后即得。
所述的一种高强度加气混凝土砌块，其特征在于：制备工艺包括以下步骤：原材料混匀、浇筑入模、预养、脱模、切割、蒸汽养护、入库。
所述的一种高强度加气混凝土砌块，其特征在于：制备工艺包括以下步骤：
（1）按重量份称取矾矿尾渣与石膏，在加入适量的水后在700-1000rpm下搅拌混合2-3min后研磨得矾矿尾渣石膏混合浆料，再加入其余原料在1800-2800rpm下搅拌混合4-6min，得混合料浆；
（2）将所得混合料浆浇筑入模成型，后在40-50℃下预养1.5-3小时，脱模，吊运至切割部切割，得砌块坯；
（3）将砌块坯放入反应釜中蒸汽养护，入库即得。
所述的一种高强度加气混凝土砌块，其特征在于：所述的蒸汽养护工艺的时长为8-12小时，温度为43-47℃。
所述的一种高强度加气混凝土砌块，其特征在于：所述的矾矿尾渣细度为100-200目，所述的电石渣细度为100-200目。
本发明的有益效果为：
1、本发明通过添加纳米粉末矿粉，减轻了砖的容重，同时，减少了能源消耗；本发明砖隔热与隔音性能均好，较现有高强度加气混凝土砌块有明显提高。同时本发明通过优化配方用料，本发明的强度、抗冻性有了明显提高；羟丙基甲基纤维素钠的加入能有效减小砌块裂缝的产生。
2、本砌块的容重为500-700kg/m3,保温性能好,在砌块内部具有大量的气孔和微孔,因而有良好的保温隔热性能，抗压强度为4.6-7MPa。
具体实施方式
实施例1
一种高强度加气混凝土砌块，其是由下述重量（kg）的原料按照加气混凝土砌块常规制造工艺制得：细度为180目的矾矿尾渣29、水泥5、生石灰10、改性纳米粉5、电石渣2、石英粉1、石膏3、铝粉0.1、平平加0.008、碳酸氢钙0.01、纯碱 0.003、硬脂酸钙0.5、硬脂酸锌0.3、硅酸钠0.013、羟丙基甲基纤维素钠 0.1、水适量；
改性纳米粉的制备方法为：由8kg碳酸钙、1kg陶粒、1kg页岩、4kg赤泥、3kg凹凸棒土混匀后在700℃下烧损5小时，后研磨成纳米粉末，拌入相当于粉体重量2%的环氧亚麻子油、2%的木质素磺酸钙拌搅均匀，烘干，粉碎成粉末后即得；
所述的电石渣的制备方法为：将碎玻璃磨细后，过100目筛即得。
所述的一种高强度加气混凝土砌块的制备工艺包括以下步骤：原材料混匀、浇筑入模、预养、脱模、切割、蒸汽养护、入库。
本砌块的平均容重为620kg/m3,保温性能好,在砌块内部具有大量的气孔和微孔,因而有良好的保温隔热性能，抗压强度为5.8MPa。
实施例2
一种高强度加气混凝土砌块，其是由下述重量（kg）的原料按照加气混凝土砌块常规制造工艺制得：细度为180目的矾矿尾渣30、水泥10、生石灰15、改性纳米粉5、电石渣2、石英粉1、石膏3、铝粉0.1、平平加0.002、碳酸氢钙0.01、纯碱 0.005、硬脂酸钙0.8、硬脂酸锌0.3、硅酸钠0.01、羟丙基甲基纤维素钠0.05、水适量；
改性纳米粉的制备方法为：由9kg碳酸钙、1.5kg陶粒、2kg页岩、2.5kg赤泥、3kg凹凸棒土混匀后在600℃下烧损4小时，后研磨成纳米粉末，拌入相当于粉体重量1%的环氧亚麻子油、1%的木质素磺酸钙拌搅均匀，烘干，粉碎成粉末后即得；
所述的电石渣的制备方法为：将碎玻璃磨细后，过100目筛即得。
所述的一种高强度加气混凝土砌块，制备工艺包括以下步骤：
（1）按重量比例称取矾矿尾渣与石膏，在加入适量的水后在800rpm下搅拌混合2min后研磨得矾矿尾渣石膏混合浆料，再加入其余原料在2500rpm下搅拌混合5min，得混合料浆；
（2）将所得混合料浆浇筑入模成型，后在50℃下预养2小时，脱模，吊运至切割部切割，得砌块坯；
（3）将砌块坯放入反应釜中蒸汽养护，入库即得。
本砌块的平均容重为650kg/m3,保温性能好,在砌块内部具有大量的气孔和微孔,因而有良好的保温隔热性能，抗压强度为6.9MPa。
实施例3
一种高强度加气混凝土砌块，其是由下述重量（kg）的原料按照加气混凝土砌块常规制造工艺制得：细度为180目的矾矿尾渣28、水泥10、生石灰15、改性纳米粉5、细度为100目的电石渣2、细度为100目的石英粉1、石膏3、铝粉0.1、平平加0.002、碳酸氢钙0.02、纯碱 0.005、硬脂酸钙0.8、硬脂酸锌0.3、硅酸钠0.01、羟丙基甲基纤维素钠0.05、水适量；
改性纳米粉的制备方法为：由8kg碳酸钙、1kg陶粒、2kg页岩、2.5kg赤泥、3kg凹凸棒土混匀后在700℃下烧损4小时，后研磨成纳米粉末，拌入相当于粉体重量1%的环氧亚麻子油、1%的木质素磺酸钙拌搅均匀，烘干，粉碎成粉末后即得；
所述的电石渣的制备方法为：将碎玻璃磨细后，过100目筛即得。
所述的一种高强度加气混凝土砌块，制备工艺包括以下步骤：
（1）按重量比例称取矾矿尾渣与石膏，在加入适量的水后在800rpm下搅拌混合2min后研磨得矾矿尾渣石膏混合浆料，再加入其余原料在2500rpm下搅拌混合5min，得混合料浆；
（2）将所得混合料浆浇筑入模成型，后在50℃下预养2小时，脱模，吊运至切割部切割，得砌块坯；
（3）将砌块坯放入反应釜中蒸汽养护12小时，温度为45℃，后入库，即得。在应用前所得产品至少要在库房停放五天以上。
本砌块的平均容重为700kg/m3,保温性能好,在砌块内部具有大量的气孔和微孔,因而有良好的保温隔热性能，平均值抗压强度为5.8MPa。
Claims (4)
1.一种高强度加气混凝土砌块，其特征在于，其是由下述重量份的原料按照加气混凝土砌块常规制造工艺制得：矾矿尾渣28-32、水泥5-10、生石灰10-15、改性纳米粉5-10、电石渣2-4、石英粉1-2、石膏3-5、铝粉0.05-0.1、平平加0.002-0.008、碳酸氢钙0.01-0.02、纯碱 0.003-0.005、硬脂酸钙0.5-0.8、硬脂酸锌0.3-0.5、硅酸钠0.01-0.03、羟丙基甲基纤维素钠0.05-0.1、水适量；所述的矾矿尾渣细度为100-200目，所述的电石渣细度为100-200目；
改性纳米粉的制备方法为：由8-9重量份碳酸钙、1-2重量份陶粒、1-2重量份页岩、2-4重量份赤泥、3-6重量份凹凸棒土混匀后在600-700℃下烧损4-5小时，后研磨成纳米粉末，拌入相当于粉体重量1-2%的环氧亚麻子油、1-2%的木质素磺酸钙搅拌均匀，烘干，粉碎成粉末后即得。
2.根据权利要求1所述的一种高强度加气混凝土砌块，其特征在于：制备工艺包括以下步骤：原材料混匀、浇筑入模、预养、脱模、切割、蒸汽养护、入库。
3.根据权利要求1所述的一种高强度加气混凝土砌块，其特征在于：制备工艺包括以下步骤：
（1）按重量份称取矾矿尾渣与石膏，在加入适量的水后在700-1000rpm下搅拌混合2-3min后研磨得矾矿尾渣石膏混合浆料，再加入其余原料在1800-2800rpm下搅拌混合4-6min，得混合料浆；
（2）将所得混合料浆浇筑入模成型，后在40-50℃下预养1.5-3小时，脱模，吊运至切割部切割，得砌块坯；
（3）将砌块坯放入反应釜中蒸汽养护，入库即得。
4.根据权利要求2或3所述的一种高强度加气混凝土砌块，其特征在于：所述的蒸汽养护工艺的时长为8-12小时，温度为43-47℃。