CN102721785B - 转炉渣硫磺容量法测定方法 - Google Patents

转炉渣硫磺容量法测定方法 Download PDF

Info

Publication number
CN102721785B
CN102721785B CN201110080219.3A CN201110080219A CN102721785B CN 102721785 B CN102721785 B CN 102721785B CN 201110080219 A CN201110080219 A CN 201110080219A CN 102721785 B CN102721785 B CN 102721785B
Authority
CN
China
Prior art keywords
sulphur
sample
vessel slag
potassiumiodate
standard solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110080219.3A
Other languages
English (en)
Other versions
CN102721785A (zh
Inventor
陈国明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Baosteel Industry Technological Service Co Ltd
Original Assignee
Shanghai Baosteel Industry Inspection Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Baosteel Industry Inspection Corp filed Critical Shanghai Baosteel Industry Inspection Corp
Priority to CN201110080219.3A priority Critical patent/CN102721785B/zh
Publication of CN102721785A publication Critical patent/CN102721785A/zh
Application granted granted Critical
Publication of CN102721785B publication Critical patent/CN102721785B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及转炉渣成分分析，尤其涉及一种助熔剂转炉渣硫磺的测定方法。一种转炉渣硫磺容量法测定用的助熔剂，它包括下列重量份的物质：WO3？1份和CuO？1份。一种转炉渣硫磺容量法测定方法，先在预处理过的瓷舟内均匀地铺上0.5克WO3，再把准确称好的试样平铺在WO3上，再在试样上盖0.5克CuO，也要均匀铺开。然后把装有试样的瓷舟放入管式炉炉管中间，炉温为1400℃，塞上塞子保温50秒，马上通氧气，使硫生成二氧化硫,生成的二氧化硫,被盐酸溶液吸收,用含碘化钾的淀粉溶液作指示剂,用碘酸钾标准溶液滴定,定量硫。本发明能大大提高硫的转化率和测定的工作效率。

Description

转炉渣硫磺容量法测定方法
技术领域
本发明涉及转炉渣成分分析，尤其涉及转炉渣硫磺的测定方法，另一方面涉及一种助熔剂。
背景技术
从已掌握的标准、文献内容来看，国内外目前在用碘酸钾滴定容量法测定转炉渣硫磺时，所用的助熔剂为WO3。由于所用助熔剂的限制，燃烧后瓷舟中试样呈海绵状，燃烧不完全，硫的释放速度慢，分析一个试样需三十分钟，硫的转化率低只有65％左右，线性范围狭窄，分析精度低。
另有报道表明，可用铜或锡作添加剂，但是对碳的测定值接近标准值而且精度高，效果最好。但实际用铜助熔时，硫的测定值明显偏低，铜助熔硫的测定值最差。
发明内容
本发明旨在解决上述问题，提供一种转炉渣硫磺容量法测定用的助熔剂及其测定方法。本发明能大大提高硫的转化率和测定的工作效率。
为解决上述问题，一种转炉渣硫磺容量法测定用的助熔剂，它包括下列重量份的物质：WO31份和CuO1份。
一种转炉渣硫磺容量法测定方法，它包括所述的助溶剂，并包括下列步骤：
步骤一，先在预处理过的瓷舟内均匀地铺上1重量份的WO3；
步骤二，把准确称好的试样平铺在WO3上，
步骤三，再在试样上盖1重量份的CuO，也要均匀铺开；
步骤四，把装有试样的瓷舟放入管式炉炉管中间，炉温为1400℃，塞上塞子保温50秒，马上通氧气，使硫生成二氧化硫,生成的二氧化硫通入盐酸溶液内，从而被吸收；
步骤五，用含碘化钾的淀粉溶液作指示剂,用碘酸钾标准溶液滴定,定量硫，硫含量的计算：
S(％)＝V1×f/m1×100
式中：V1:碘酸钾标准溶液滴定数，mL
m1:试样称取量，g；
f＝0.01×B×m2/V2
式中：f：1mL碘酸钾标准溶液相当于硫的量，g；
B：标准试样中硫的含量，％；
m2:标准试样的称取量，g；
V2:碘酸钾标准溶液的使用量，mL。
本发明采用WO3和CuO并用，采用WO3、试样、CuO三层的结构，解决了以前由于受炉温和助熔剂的限制燃烧后瓷舟中试样呈海绵状，燃烧不完全，硫的释放速度慢，分析一个试样需三十分钟，硫的转化率低只有65％左右。线性范围狭窄，分析精度低。
本发明由于操作简单，便于掌握,分析一个试样只需5分钟，能使工作效率提高600％。硫的转化率达到85％左右，线性范围宽，分析精度高。在钢铁行业有较好的推广前景。
具体实施方式
把WO3和CuO按1:1的比例进行配制，使它们之间产生一种交互作用，来达到试样熔融状态良好。
具体操作是：先在预处理过的瓷舟内均匀地铺上0.5克WO3，再把准确称好的试样平铺在WO3上，再在试样上盖0.5克CuO，也要均匀铺开。然后把装有试样的瓷舟放入管式炉炉管中间，炉温为1400℃，塞上塞子保温50秒，马上通氧气，使硫生成二氧化硫,生成的二氧化硫,被盐酸溶液吸收,用含碘化钾的淀粉溶液作指示剂,用碘酸钾标准溶液滴定,定量硫。
硫含量的计算：
S(％)＝V1×f/m1×100。
式中：V1:碘酸钾标准溶液滴定数(mL)
m1:试样称取量(g)。
f＝0.01×B×m2/V2
式中：f：1mL碘酸钾标准溶液相当于硫的量(g)
B：标准试样中硫的含量(％)
m2:标准试样的称取量(g)
V2:碘酸钾(KIO3)标准溶液的使用量(mL)。
本发明和现有技术比较表
精密度和准确度

Claims (1)

1.一种转炉渣硫磺容量法测定方法，其特征在于，包括下列步骤：
步骤一，先在预处理过的瓷舟内均匀地铺上1重量份的WO3；
步骤二，把准确称好的试样平铺在WO3上，
步骤三，再在试样上盖1重量份的CuO，也要均匀铺开；
步骤四，把装有试样的瓷舟放入管式炉炉管中间，炉温为1400℃，塞上塞子保温50秒，马上通氧气，使硫生成二氧化硫,生成的二氧化硫通入盐酸溶液内，从而被吸收；
步骤五，用含碘化钾的淀粉溶液作指示剂,用碘酸钾标准溶液滴定,定量硫，硫含量的计算：
S(％)＝V1×f/m1×100
式中：V1:碘酸钾标准溶液滴定数，mL
m1:试样称取量，g；
f＝0.01×B×m2/V2
式中：f：1mL碘酸钾标准溶液相当于硫的量，g；
B：标准试样中硫的含量，％；
m2:标准试样的称取量，g；
V2:碘酸钾标准溶液的使用量，mL。
CN201110080219.3A 2011-03-31 2011-03-31 转炉渣硫磺容量法测定方法 Active CN102721785B (zh)