CN102432959A - 一种环保型发泡板 - Google Patents
一种环保型发泡板 Download PDFInfo
- Publication number
- CN102432959A CN102432959A CN2011102361354A CN201110236135A CN102432959A CN 102432959 A CN102432959 A CN 102432959A CN 2011102361354 A CN2011102361354 A CN 2011102361354A CN 201110236135 A CN201110236135 A CN 201110236135A CN 102432959 A CN102432959 A CN 102432959A
- Authority
- CN
- China
- Prior art keywords
- parts
- foaming plate
- lubricant
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种环保型发泡板。这种环保型发泡板是用废旧PVC塑料粉末、木粉、石粉、PVC树脂、发泡剂、调节剂、稳定剂和润滑剂等原料,经均匀混合、用挤出机及模具挤制成平板状毛坯、对平板状毛坯边沿进行修整等步骤而制成。这种环保型发泡板,不仅可回收、使用寿命长、有利于健康,而且使用前不需进行脱模处理,劳动强度低。可用作建筑模板的,也可用作生产家具的板材。
Description
技术领域
本发明涉及一种板材。具体说,是用作建筑模板的发泡板,也可用作生产家具的板材。
背景技术
目前,建筑用模板主要有竹制复合板、五夹板和钢板等,竹制复合板和五夹板易燃、易受白蚁侵蚀,在潮湿环境中易腐烂,通常使用三次左右就要废弃,不能回收,使用寿命短。其中的五夹板中含有有害物质甲醛,长期接触,对健康不利。钢板虽然不具有以上问题,但由于表面粗糙,每次使用前都需涂上一层油脂,进行脱模处理。又由于钢板重量比较重,使用时,劳动强度较大。
发明内容
本发明要解决的问题是提供一种环保型发泡板。这种发泡板,不仅可回收、使用寿命长、有利于健康,而且使用前不需进行脱模处理,劳动强度低。
为解决上述问题,采取以下技术方案:
本发明的环保型发泡板特点是由以下重量份的原料制成:
废旧PVC塑料粉末20~60份;
木粉3~5份;
石粉8~50份;
PVC树脂20~30份;
发泡剂0.5~1.8份;
调节剂4~9份;
稳定剂1.5~4.5份;
润滑剂0.5~2份。
其中:所述发泡剂是偶氮二甲酰胺;所述调节剂是丙烯酸酯类加工助剂;所述稳定剂是硬质酸铝或三碱式硫酸铝;所述润滑剂是聚乙烯蜡。
先将废旧PVC塑料粉末、木屑、石粉、PVC树脂、发泡剂、调节剂、稳定剂和润滑剂投入温度为105~125℃的混料机中混合均匀,得到混合料。
然后,将混合机中的混合料倒出并冷却至38~42℃。
之后,用温度为130~180℃的挤出机和温度为160~180℃的模具,将混合料加工成平板状毛坯。
最后,用切割机对平板状毛坯的边沿进修整,得到环保型发泡板。
采取上述方案,具有以下优点:
由上述方案可以看出,由于本发明的环保型发泡板由废旧塑料、木屑、石粉和树脂等原料制成,不仅不易燃、可避免白蚁的侵害,而且在潮湿环境中也不会腐烂,经试用可重复使用十五次以上,使用寿命较长。又由于本发明的发泡板由废旧塑料、木屑、石粉和树脂等原料制成,损坏后可回收作为生产新发泡板的原料,使得其生产成本仅是传统建筑模板的50%,从而大大降低了生产成本和使用成本。另外,由于这种发泡板的原料中不含有害物质甲醛,即使长期接触,也不会对健康造成危害。再一方面,由于本发明的环保型发泡板由废旧塑料、木屑、石粉和树脂等原料制成,不仅重量轻,而且由于表面光洁度高,使用时可省去脱模处理步骤,从而可降低施工人员的劳动强度。
具体实施方式
以下结合实施例对本发明做进一步详细说明:
实施例一
先选取20重量份的废旧PVC塑料粉末、15重量份的木粉、50重量份的石粉、20重量份的PVC树脂、1.8重量份的发泡剂、4重量份的调节剂、4.5重量份的稳定剂和2重量份的润滑剂,待用。
其中,所述发泡剂是偶氮二甲酰胺;所述调节剂是丙烯酸酯类加工助剂;所述稳定剂是硬质酸铝;所述润滑剂是聚乙烯蜡;所述木粉是粒径为500目的木粉。
然后,将废旧PVC塑料粉末、木粉、石粉、PVC树脂、发泡剂、调节剂、稳定剂和润滑剂投入温度为105℃的混料机中混合均匀,得到混合料。
之后,将混合机中的混合料倒出并冷却至38℃。
之后,用温度为135℃的双螺杆挤出机和温度为160℃的模具,将混合料加工成平板状毛坯。
最后,用切割机对平板状毛坯的边沿进修整,得到环保型发泡板。
实施例二
先选取40重量份的废旧PVC塑料粉末、10重量份的木粉、25重量份的石粉、25重量份的PVC树脂、1.3重量份的发泡剂、6重量份的调节剂、3重量份的稳定剂和1.2重量份的润滑剂,待用。
其中,所述发泡剂是偶氮二甲酰胺;所述调节剂是丙烯酸酯类加工助剂;所述稳定剂是硬质酸铝;所述润滑剂是聚乙烯蜡;所述木粉是粒径为800目的木粉。
然后,将废旧PVC塑料粉末、木粉、石粉、PVC树脂、发泡剂、调节剂、稳定剂和润滑剂投入温度为115℃的混料机中混合均匀,得到混合料。
之后,将混合机中的混合料倒出并冷却至40℃。
之后,用温度为158℃的双螺杆挤出机和温度为170℃的模具,将混合料加工成平板状毛坯。
最后,用切割机对平板状毛坯的边沿进修整,得到环保型发泡板。
实施例三
先选取60重量份的废旧PVC塑料粉末、3重量份的木粉、8重量份的石粉、30重量份的PVC树脂、0.5重量份的发泡剂、9重量份的调节剂、1.5重量份的稳定剂和0.5重量份的润滑剂,待用。
其中,所述发泡剂是偶氮二甲酰胺;所述调节剂是丙烯酸酯类加工助剂;所述稳定剂是硬质酸铝;所述润滑剂是聚乙烯蜡;所述木粉是粒径为1000目的木粉。
然后,将废旧PVC塑料粉末、木粉、石粉、PVC树脂、发泡剂、调节剂、稳定剂和润滑剂投入温度为125℃的混料机中混合均匀,得到混合料。
之后,将混合机中的混合料倒出并冷却至42℃。
之后,用温度为180℃的双螺杆挤出机和温度为180℃的模具,将混合料加工成平板状毛坯。
最后,用切割机对平板状毛坯的边沿进修整,得到环保型发泡板。
Claims (3)
1.一种环保型发泡板,其特征在于由以下重量份的原料制成:
废旧PVC塑料粉末20~60份;
木粉3~5份;
石粉8~50份;
PVC树脂20~30份;
发泡剂0.5~1.8份;
调节剂4~9份;
稳定剂1.5~4.5份;
润滑剂0.5~2份;
其中,所述发泡剂是偶氮二甲酰胺;所述调节剂是丙烯酸酯类加工助剂;所述稳定剂是硬质酸铝或三碱式硫酸铝;所述润滑剂是聚乙烯蜡;
先将废旧PVC塑料粉末、木屑、石粉、PVC树脂、发泡剂、调节剂、稳定剂和润滑剂投入温度为105~125℃的混料机中混合均匀,得到混合料;
然后,将混合机中的混合料倒出并冷却至38~42℃;
之后,用温度为130~180℃的挤出机和温度为160~180℃的模具,将混合料加工成平板状毛坯;
最后,用切割机对平板状毛坯的边沿进修整,得到环保型发泡板。
2.根据权利要求1所述的环保型发泡板,其特征在于所述挤出机是双螺杆挤出机。
3.根据权利要求1所述的环保型发泡板,其特征在于所述木粉是粒径为500~1000目的木粉。