CN102432344A - 一种铜红窑变釉料及其制备和使用方法 - Google Patents

一种铜红窑变釉料及其制备和使用方法 Download PDF

Info

Publication number
CN102432344A
CN102432344A CN2011103080875A CN201110308087A CN102432344A CN 102432344 A CN102432344 A CN 102432344A CN 2011103080875 A CN2011103080875 A CN 2011103080875A CN 201110308087 A CN201110308087 A CN 201110308087A CN 102432344 A CN102432344 A CN 102432344A
Authority
CN
China
Prior art keywords
glaze
weight parts
parts
copper red
dry powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011103080875A
Other languages
English (en)
Other versions
CN102432344B (zh
Inventor
林海啸
蔡世山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Gaocheng Creative Technology Group Co., Ltd.
Original Assignee
Shanghai Gaocheng Art Packaging Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Gaocheng Art Packaging Co Ltd filed Critical Shanghai Gaocheng Art Packaging Co Ltd
Priority to CN 201110308087 priority Critical patent/CN102432344B/zh
Publication of CN102432344A publication Critical patent/CN102432344A/zh
Application granted granted Critical
Publication of CN102432344B publication Critical patent/CN102432344B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种铜红窑变釉料及其制备和使用方法。所述的铜红窑变釉料，包括干粉和水，其特征在于，所述的干粉由长石60重量份、方解石13～18重量份、磷酸钙6～10重量份、石英12～15重量份、高岭土10重量份、氧化铜3～5重量份、氧化镁15～18重量份、氧化锡3～5重量份以及碳酸钡15～17重量份组成。本发明采用了特有的釉料配方以及制作工艺，得到了具有红色渗出效果的陶瓷产品，装饰效果较强。

Description

一种铜红窑变釉料及其制备和使用方法
技术领域
本发明涉及一种铜红窑变釉料及其制备和使用方法，属于陶瓷技术领域。
背景技术
随着陶瓷制品进入千家万户，陶瓷釉料为陶瓷制品不可缺少的装饰材料，现有的陶瓷釉料按照类别与用途可以大致分类如下：1、铅釉和无铅釉；2、生料釉与熔块釉；3、一次烧成或二次烧成用釉；4、瓷砖，餐具，卫生陶瓷与电瓷用釉；5、按施釉方法划分的浸釉、喷釉、浇釉；6、高温釉和低温釉；7、高膨胀釉和低膨胀釉；8、烧成气氛氧化焰、中性焰和还原焰；9、颜色釉与无色釉；10、透明釉与乳浊釉；11、光泽釉、无光釉、半无光釉或花纹釉等等。陶瓷釉料的稳定性、多样性，釉料装饰、花样装饰已成为我国陶瓷厂家追求的目标。
发明内容
本发明的目的是提供一种具有红色渗出效果的陶瓷釉料及其制备和使用方法。
    为了达到上述目的，本发明提供了一种铜红窑变釉料，包括干粉和水，其特征在于，所述的干粉由长石60重量份、方解石13～18重量份、磷酸钙6～10重量份、石英12～15重量份、高岭土10重量份、氧化铜3～5重量份、氧化镁15～18重量份、氧化锡3～5重量份以及碳酸钡15～17重量份组成。
    本发明还提供了上述铜红窑变釉料的制备方法，其特征在于，包括：将长石、方解石、磷酸钙（Ca2(PO4)3）、石英、高岭土、氧化铜、氧化镁、氧化锡以及碳酸钡按比例混合得到干粉，将干粉和水按照重量比100：45～55混合，研磨到150～250目，得到铜红窑变釉料。
    本发明还提供了上述铜红窑变釉料的使用方法，其特征在于，包括：将陶瓷釉料与水混合，所得混合液中陶瓷釉料的重量浓度为39～49%，将陶瓷坯体浸入到混合液中从而将混合液施加到陶瓷坯体上，在1280～1300℃于还原气氛中烧制8～10小时，得到具有红色渗出效果的陶瓷产品。
    本发明的优点是：
1、本发明采用了特有的陶瓷釉料配方以及制作工艺，得到了具有红色渗出效果的陶瓷产品，装饰效果较强。
2、制备和使用方法简单，生产成本低。
  具体实施方式
     下面结合实施例来具体说明本发明。实施例1-3中的陶瓷坯体为由市售的陶瓷基料烧制而成的素坯，所述的还原气氛为一氧化碳气氛。
实施例1
将钾长石60重量份、方解石13重量份、磷酸钙6重量份、石英12重量份、高岭土10重量份、氧化铜3重量份、氧化镁15重量份、氧化锡3重量份以及碳酸钡15重量份按比例混合得到干粉，将干粉和水按照重量比100：45混合，研磨到150目，得到铜红窑变釉料。
   将铜红窑变釉料与水混合，所得混合液中铜红窑变釉料的重量浓度为39%，将陶瓷坯体浸入到混合液中从而将混合液施加到陶瓷坯体上，在1280℃于还原气氛中烧制8小时，得到陶瓷产品，所得的陶瓷产品的釉面有多个红色点，所述红色点具有从陶瓷里面渗出的效果。
实施例2
将钠长石60重量份、方解石18重量份、磷酸钙10重量份、石英15重量份、高岭土10重量份、氧化铜5重量份、氧化镁18重量份、氧化锡5重量份以及碳酸钡17重量份按比例混合得到干粉，将干粉和水按照重量比100：55混合，研磨到250目，得到铜红窑变釉料。
   将铜红窑变釉料与水混合，所得混合液中铜红窑变釉料的重量浓度为49%，将陶瓷坯体浸入到混合液中从而将混合液施加到陶瓷坯体上，在1300℃于还原气氛中烧制10小时，得到陶瓷产品，所得的陶瓷产品的釉面有多个红色点，所述红色点具有从陶瓷里面渗出的效果。
实施例3
将钙长石60重量份、方解石15重量份、磷酸钙8重量份、石英13重量份、高岭土10重量份、氧化铜4重量份、氧化镁16重量份、氧化锡4重量份以及碳酸钡16重量份按比例混合得到干粉，将干粉和水按照重量比100：50混合，研磨到200目，得到铜红窑变釉料。
   将铜红窑变釉料与水混合，所得混合液中铜红窑变釉料的重量浓度为44%，将陶瓷坯体浸入到混合液中从而将混合液施加到陶瓷坯体上，在1290℃于还原气氛中烧制9小时，得到陶瓷产品，所得的陶瓷产品的釉面有多个红色点，所述红色点具有从陶瓷里面渗出的效果。

Claims (3)

1.一种铜红窑变釉料，包括干粉和水，其特征在于，所述的干粉由长石60重量份、方解石13～18重量份、磷酸钙6～10重量份、石英12～15重量份、高岭土10重量份、氧化铜3～5重量份、氧化镁15～18重量份、氧化锡3～5重量份以及碳酸钡15～17重量份组成。
2.权利要求1所述的铜红窑变釉料的制备方法，其特征在于，包括：将长石、方解石、磷酸钙、石英、高岭土、氧化铜、氧化镁、氧化锡以及碳酸钡按比例混合得到干粉，将干粉和水按照重量比100：45～55混合，研磨到150～250目，得到铜红窑变釉料。
3.权利要求1所述的铜红窑变釉料的使用方法，其特征在于，包括：将铜红窑变釉料与水混合，所得混合液中底釉的重量浓度为39～49%，将陶瓷坯体浸入到混合液中从而将混合液施加到陶瓷坯体上，在1280～1300℃于还原气氛中烧制8～10小时，得到具有红色渗出效果的陶瓷产品。
CN 201110308087 2011-10-12 2011-10-12 一种铜红窑变釉料及其制备和使用方法 Expired - Fee Related CN102432344B (zh)