CN102234353A - D113弱酸丙烯酸系阳离子交换树脂的制备方法 - Google Patents
D113弱酸丙烯酸系阳离子交换树脂的制备方法 Download PDFInfo
- Publication number
- CN102234353A CN102234353A CN2011100996305A CN201110099630A CN102234353A CN 102234353 A CN102234353 A CN 102234353A CN 2011100996305 A CN2011100996305 A CN 2011100996305A CN 201110099630 A CN201110099630 A CN 201110099630A CN 102234353 A CN102234353 A CN 102234353A
- Authority
- CN
- China
- Prior art keywords
- warming
- incubated
- hours
- water
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种D113弱酸丙烯酸系阳离子交换树脂的制备方法,主要是以丙烯腈、二乙烯苯、甲苯、甲酰等为主要原料,经过聚合和水解的工艺步骤制备出D113弱酸丙烯酸系阳离子交换树脂。
Description
技术领域
本发明涉及离子交换树脂的制备工艺,具体地说,是一种D 113弱酸丙烯酸系阳离子交换树脂的制备方法。
背景技术
交换树脂主要用于纯水、高纯水制备、废水处理、生化制品提取、稀有金属提取、湿法冶金中钨、钼、钒等的提取,具有机械强度好、耐热性高等特点。
发明内容
本发明目的在于提供一种D113弱酸丙烯酸系阳离子交换树脂的制备方法。
本发明目的是通过如下技术手段实现的:
一种D113弱酸丙烯酸系阳离子交换树脂的制备方法,包括如下步骤:
一、聚合:
1、投料量:丙烯腈358kg,二乙烯苯42kg,甲苯120kg,甲酰4kg。
2、操作步骤:
(1)按一定比例将水相配好,搅拌20分钟;
(2)停止搅拌,将混合好的单体加入开机搅拌,视粒度情况调好转速;
(3)缓慢升温至60℃,观察球体粒度及定型情况;
(4)定型时放热比较强烈,注意降温,放热后保持温度在70℃,保温2小时;
(5)用半小时升温至82℃,保温3小时;
(6)用1小时升温至96℃,保温5小时;
(7)用热水洗球数遍至水清澈为止;
(8)抽干水,烘干,分筛备用。
二、水解:
1、投料量:白球400kg,硫酸1600L(含量50%~60%)。
2、操作步骤:
(1)向反应釜中加入规定数量已配好的硫酸,再加入白球,开动搅拌;
(2)以2℃~3℃/min的升温速率升温至130℃,保温12小时,测水分大于44%合格;
(3)降温至45℃,水洗至中性;
(4)滤干,无游离水包装。
具体实施方式
下面结合实施例对本发明进一步描述,但并非用以限定本发明。
实施例1:
按照如下方法制备D113弱酸丙烯酸系阳离子交换树脂:
一、聚合:
1、投料量:丙烯腈358kg,二乙烯苯42kg,甲苯120kg,甲酰4kg。
2、操作步骤:
(1)按一定比例将水相配好,搅拌20分钟;
(2)停止搅拌,将混合好的单体加入开机搅拌,视粒度情况调好转速;
(3)缓慢升温至60℃,观察球体粒度及定型情况;
(4)定型时放热比较强烈,注意降温,放热后保持温度在70℃,保温2小时;
(5)用半小时升温至82℃,保温3小时;
(6)用1小时升温至96℃,保温5小时;
(7)用热水洗球数遍至水清澈为止;
(8)抽干水,烘干,分筛备用。
二、水解:
1、投料量:白球400kg,硫酸1600L(含量50%~60%)。
2、操作步骤:
(1)向反应釜中加入规定数量已配好的硫酸,再加入白球,开动搅拌;
(2)以2℃~3℃/min的升温速率升温至130℃,保温12小时,测水分大于44%合格;
(3)降温至45℃,水洗至中性;
(4)滤干,无游离水包装。
Claims (1)
1.一种D 113弱酸丙烯酸系阳离子交换树脂的制备方法,其特征在于,包括如下步骤:
(一)聚合:
(1)投料量:丙烯腈358kg,二乙烯苯42kg,甲苯120kg,甲酰4kg;
(2)操作步骤:
①按一定比例将水相配好,搅拌20分钟;
②停止搅拌,将混合好的单体加入开机搅拌,视粒度情况调好转速;
③缓慢升温至60℃,观察球体粒度及定型情况;
④定型时放热比较强烈,注意降温,放热后保持温度在70℃,保温2小时;
⑤用半小时升温至82℃,保温3小时;
⑥用1小时升温至96℃,保温5小时;
⑦用热水洗球数遍至水清澈为止;
⑧抽干水,烘干,分筛备用;
(二)水解:
(1)投料量:白球400kg,硫酸1600L(含量50%~60%);
(2)操作步骤:
①向反应釜中加入规定数量已配好的硫酸,再加入白球,开动搅拌;
②以2℃~3℃/min的升温速率升温至130℃,保温12小时,测水分大于44%合格;
③降温至45℃,水洗至中性;
④滤干,无游离水包装。