CN102120857A - 耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方 - Google Patents

耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方 Download PDF

Info

Publication number
CN102120857A
CN102120857A CN 201110097394 CN201110097394A CN102120857A CN 102120857 A CN102120857 A CN 102120857A CN 201110097394 CN201110097394 CN 201110097394 CN 201110097394 A CN201110097394 A CN 201110097394A CN 102120857 A CN102120857 A CN 102120857A
Authority
CN
China
Prior art keywords
parts
ethanol
fuel hose
methanol
compound formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110097394
Other languages
English (en)
Inventor
楮曙光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIELING LANTIAN RUBBER PRODUCTS CO Ltd
Original Assignee
TIELING LANTIAN RUBBER PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIELING LANTIAN RUBBER PRODUCTS CO Ltd filed Critical TIELING LANTIAN RUBBER PRODUCTS CO Ltd
Priority to CN 201110097394 priority Critical patent/CN102120857A/zh
Publication of CN102120857A publication Critical patent/CN102120857A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方，由氟橡胶、活性氧化镁、氢氧化钙、炭黑、硫化剂、促进剂、助剂、硅藻土及脱模剂935P组成，各组分重量份分别为：氟橡胶１００份、活性氧化镁８份、氢氧化钙６份、炭黑２０份、硫化剂２.４份、促进剂０.４５份、助剂１.２份、硅藻土８份、脱模剂935P０.３份；所述氟橡胶的门尼粘度（ML1+10121℃）为４０－４５，相对硬度为１.８５，该氟橡胶由偏氧乙烯VDF、聚四氟乙烯TFE和六氟丙烯HFP组成。使用本发明耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方制得燃油胶管内层胶硫化成型后具有渗透量小、抗溶胀性好，不会因为受乙醇、甲醇腐蚀溶胀而出现脱层堵塞现象。

Description

耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方
技术领域
本发明涉及一种耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方。
背景技术
汽车燃油胶管是汽车加油口与油箱、油箱与燃油蒸发器及燃油泵与发动机之间的连接软管。随着经济的高速发展，对石油产品需求量在剧增，能源的消费既受到环境因素影响又受到资源储量的限制，近几年我国加大力度开发应用车用乙醇甲醇汽油，并逐渐增加汽油中乙醇甲醇的比例。目前通用的三层结构汽车燃油胶管，由内至外依次是：丁腈橡胶层、芳纶线层、氯丁橡胶层，这种燃油胶管的缺点是抗渗透性不强、抗溶胀性差，主要表现在：胶管内层胶抗腐蚀性差，溶胀率超标，脱层堵塞现象经常发生。
发明内容
本发明要解决的技术问题是提供一种耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方，使用该胶料配方制得燃油胶管内层胶硫化成型后具有渗透量小、抗溶胀性好，不会因为受乙醇、甲醇腐蚀溶胀而出现脱层堵塞现象。
为解决上述技术问题，本发明耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方由氟橡胶、活性氧化镁、氢氧化钙、炭黑、硫化剂、促进剂、助剂、硅藻土及脱模剂935P组成，各组分重量份分别为：氟橡胶１００份、活性氧化镁８份、氢氧化钙６份、炭黑２０份、硫化剂２.４份、促进剂０.４５份、助剂１.２份、硅藻土８份、脱模剂935P０.３份；所述氟橡胶的门尼粘度（ML1+10121℃）为４０－４５，相对硬度为１.８５，该氟橡胶由偏氧乙烯VDF、聚四氟乙烯TFE和六氟丙烯HFP组成。
所述炭黑可以为炭黑N990。
所述硫化剂可以为双芬AF。
所述促进剂可以为BPP。
所述助剂可以为ATECOW　L-24。
本发明耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方中的氟橡胶由美国杜邦公司生产的VDF、TFE和HFP组成，VDF为偏氧乙烯、TFE为聚四氟乙烯、HFP为六氟丙烯；本发明使用的助剂ATECOW　L-24由上海亚特曼化工公司生产。
采用本发明耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方制得燃油胶管内层胶性能优越，详见表２，表３。
具体实施方式
下面结合实施例对本发明作进一步详细描述。
表１（详见下表）给出了本发明耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方，表１列出了胶料配方中的各组分及各组分所占的重量份数。
表２（详见下表）给出了按照表１所述胶料配方制得产品硫化成型后产品的技术指标。
表３（详见下表）给出了按照表１所述胶料配方制得产品硫化成型后在40℃*48h浸泡加醇气油（乙醇含量为２０%）后产品的技术指标变化情况。
表１：耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方
Figure 323498DEST_PATH_IMAGE002
表２：按照表１所述胶料配方制得产品硫化成型后产品的技术指标
检测项目 实测技术指标
硬度 72°
拉伸强度 13.7MPa
扯断伸长率% 340
表３：按照表１所述胶料配方制得产品硫化成型后在40℃*48h浸泡加醇气油（乙醇含量为２０%）后产品的技术指标变化情况
检测项目 技术指标
硬度 -8
拉伸强度% -18.6
扯断伸长率% -7
体积变化率% 15

Claims (5)

1.一种耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方，其特征在于：由氟橡胶、活性氧化镁、氢氧化钙、炭黑、硫化剂、促进剂、助剂、硅藻土及脱模剂935P组成，各组分重量份分别为：氟橡胶１００份、活性氧化镁８份、氢氧化钙６份、炭黑２０份、硫化剂２.４份、促进剂０.４５份、助剂１.２份、硅藻土８份、脱模剂935P０.３份；所述氟橡胶的门尼粘度（ML1+10121℃）为４０－４５，相对硬度为１.８５，该氟橡胶由偏氧乙烯VDF、聚四氟乙烯TFE和六氟丙烯HFP组成。
2.按照权利要求１所述的胶料配方，其特征在于：所述炭黑为炭黑N990。
3.按照权利要求１所述的胶料配方，其特征在于：所述硫化剂为双芬AF。
4.按照权利要求１所述的胶料配方，其特征在于：所述促进剂为BPP。
5.按照权利要求１所述的胶料配方，其特征在于：所述助剂为ATECOW　L-24。
CN 201110097394 2011-04-19 2011-04-19 耐乙醇甲醇汽车燃油胶管防渗透内层胶胶料配方 Pending CN102120857A (zh)