CN103275447A - 一种低硬度氟橡胶及其制备方法 - Google Patents
一种低硬度氟橡胶及其制备方法 Download PDFInfo
- Publication number
- CN103275447A CN103275447A CN2013101705005A CN201310170500A CN103275447A CN 103275447 A CN103275447 A CN 103275447A CN 2013101705005 A CN2013101705005 A CN 2013101705005A CN 201310170500 A CN201310170500 A CN 201310170500A CN 103275447 A CN103275447 A CN 103275447A
- Authority
- CN
- China
- Prior art keywords
- parts
- fluororubber
- viton
- low
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低硬度氟橡胶配方，采用氟橡胶的混炼胶（含有硫化剂和促进剂的弹性体），将其加工成低硬度的氟橡胶。本发明所述的一种低硬度氟橡胶，利用低门黏度，减少填料加入量，在保持较好物理机械性的同时，也具有较低的硬度。采用本发明所述的配方可大大节约企业的生产资源，降低企业的生产成本。
Description
技术领域
该发明涉及一种氟橡胶，特别涉及一种低硬度氟橡胶及其制备方法。
背景技术
氟橡胶显示出优异的耐化学药品性、耐溶剂性、耐油性、耐气候性、耐老化性和耐热性，因此在汽车工业、半导体工业、化学工业、航空航天业等各种领域中广泛使用。氟橡胶应用最广泛的是汽车领域，占应用总量的60—70%。在汽车零部件上，可作为发动机燃料软管、加油软管、燃料泵、空调装置O形圈，及喷射装置，动力活塞、气门杆、曲轴、空调压缩机的密封材料，现如今，氟橡胶已经是工业产业中不可缺少的材料之一，随着科学技术的发展，生产生活中所探索接触领域的不断拓展，其应用范围会越来越广泛。
发明内容
本发明的目的在于克服现有技术中的缺陷，提供一种低硬度氟橡胶及其制备方法，所述的低硬度氟胶具有较好的物理机械性，利用低门黏度，减少填料加入量，同时具有较低的硬度，其应用范围更加广泛。
本发明是通过以下技术方案予以实现的。
一种低硬度氟胶，其组成成分按重量份数计如下：
上述的一种低硬度氟橡胶的制备方法，其中，制备步骤如下：
在密炼机中加入氟橡胶、碳黑、氧化镁、氢氧化钙、二丁酯和氧化锌进行混合密炼，混炼温度的范围150—165℃，在压力10—12KN，密炼机转速50—55r/min的条件下，混炼1—1.5h。
本发明的有益效果为：利用低门黏度，减少填料加入量，在保持较好物理机械性的同时，可得到硬度值为50shore的低硬度氟橡胶。采用本发明所述的配方可大大节约企业的生产资源，降低企业的生产成本。
具体实施方式
以下通过具体实施例对本发明的具体实施方式作进一步详细的说明。
本发明所述氟橡胶型号为2601；所述炭黑N990购于扬中市瑞丰化工有限公司。
实施例1
一种低硬度氟橡胶的制备方法，制备步骤如下：在密炼机中加入100份氟橡胶、20份碳黑、3份氧化镁、6份氢氧化钙、9份二丁酯和3份氧化锌进行混合密炼，混炼温度的范围150℃，在压力10KN，密炼机转速50r/min的条件下，混炼1h，得到一种低硬度氟橡胶。
性能指标：硬度值为50shore。
实施例2
一种低硬度氟橡胶的制备方法，制备步骤如下：在密炼机中加入100份氟橡胶、21份碳黑、4份氧化镁、5份氢氧化钙、6份二丁酯和5份氧化锌进行混合密炼，混炼温度的范围150℃，在压力12KN，密炼机转速55r/min的条件下，混炼1.5h，得到一种低硬度氟橡胶。
性能指标：硬度值为60shore。
实施例3
一种低硬度氟橡胶的制备方法，制备步骤如下：在密炼机中加入100份氟橡胶、22份碳黑、2份氧化镁、7份氢氧化钙、7份二丁酯和4份氧化锌进行混合密炼，混炼温度的范围165℃，在压力11KN，密炼机转速52r/min的条件下，混炼1.3h，得到一种低硬度氟橡胶。
性能指标：硬度值为55shore。
综上所述，本发明具有较好的物理机械性，利用低门黏度，减少填料加入量，在保持较好物理机械性的同时，能够具有±50 shore的低硬度。采用本发明所述的配方可大大节约企业的生产资源，降低企业的生产成本。
这里本发明的描述和应用是说明性的，并非想将本发明的范围限制在上述实施例中，因此，本发明不受本实施例的限制，任何采用等效替换取得的技术方案均在本发明保护的范围内。
Claims (7)
1.一种低硬度氟胶配方，其特征在于，其组成成分按重量份数计如下：
氟橡胶 100份
碳黑 18—22份
氧化镁 2—4份
氢氧化钙 5—7份
二丁酯 6—10份
氧化锌 2—5份 。
2.如权利要求1所述的一种低硬度氟胶配方，其特征在于：
氟橡胶 100份
碳黑 20份
氧化镁 3份
氢氧化钙 6份
二丁酯 9份
氧化锌 3份。
3.如权利要求1所述的一种低硬度氟胶配方，其特征在于，制备步骤如下：在密炼机中加入氟橡胶、碳黑、氧化镁、氢氧化钙、二丁酯和氧化锌进行混合密炼。
4.如权利要求3所述的一种低硬度氟胶配方，其特征在于，混炼时，混炼温度的范围150—165℃。
5.如权利要求3所述的一种低硬度氟胶配方，其特征在于，混炼时，压力为10—12KN。
6.如权利要求3所述的一种低硬度氟胶配方，其特征在于，混炼时，密炼机转速50—55r/min。
7.如权利要求3所述的一种低硬度氟胶配方，其特征在于，混炼时，混炼时间为1—1.5h。