CN105237929A - 一种环保低成本丙烯酸酯胶料 - Google Patents

一种环保低成本丙烯酸酯胶料 Download PDF

Info

Publication number
CN105237929A
CN105237929A CN201510797251.1A CN201510797251A CN105237929A CN 105237929 A CN105237929 A CN 105237929A CN 201510797251 A CN201510797251 A CN 201510797251A CN 105237929 A CN105237929 A CN 105237929A
Authority
CN
China
Prior art keywords
acrylate
sizing material
environmental protection
low cost
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510797251.1A
Other languages
English (en)
Inventor
鞠建宏
尚世豪
邹惠芳
马妍
郭磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing 7425 Rubber & Plastic Co Ltd
Original Assignee
Nanjing 7425 Rubber & Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing 7425 Rubber & Plastic Co Ltd filed Critical Nanjing 7425 Rubber & Plastic Co Ltd
Priority to CN201510797251.1A priority Critical patent/CN105237929A/zh
Publication of CN105237929A publication Critical patent/CN105237929A/zh
Pending legal-status Critical Current

Abstract

一种环保低成本丙烯酸酯胶料，其特征是其由以下组分组成：丙烯酸酯橡胶：100份；硬脂酸：1-2份；防老剂445：1.5-3份；内脱模剂：1-2份；炭黑N-550：60-80份；聚酯增塑剂：10-20份；1#硫化剂：1-2.5份；硫化助剂：1-3份。本发明的环保低成本丙烯酸酯胶料选用耐油级别的乙烯丙烯酸酯橡胶(丙烯酸酯)和耐寒级别的乙烯丙烯酸酯橡胶(丙烯酸酯)两种不同杜邦牌号的生胶并用，通过配方调整，制备出了既满足了严格的耐IRM？903#油性能，又符合耐－40℃低温要求的丙烯酸酯胶料。

Description

一种环保低成本丙烯酸酯胶料
技术领域
本发明涉及一种环保低成本丙烯酸酯胶料，是一种环保耐高低温、耐IRM903#油的丙烯酸酯胶料配方，应用于汽车发动机的散热器胶管和空气输送管、耐高温气制动胶管、轴油封和动力转向管。
背景技术
中国专利CN104403188A、名称“耐高温丙烯酸酯油封胶料及制备方法”，由下列重量份原料制成：耐油级橡胶100份、纳米氮化硅预分散母10-20份、防老剂4451-3份、内脱模剂VAM1-2份、炭黑N-55060-80份、聚酯增塑剂5-10份、二胺氨基甲酸盐1-2份、促进剂DOTG3-5份。其不足之处：上述配方所用促进剂达不到环保要求，硫化胶性能无法达到：拉伸强度：≥14.5Mpa；拉断伸长率：≥200％。
丙烯酸酯现有配方所用内脱模剂为VAM和18D，价格较贵，不具备价格优势。一种级别的丙烯酸酯橡胶很难同时满足耐IRM903#油和耐－40℃低温的平衡。
发明内容
本发明的目的在于提供一种环保低成本丙烯酸酯胶料，以克服上述缺陷。本发明的环保低成本丙烯酸酯胶料是一种有着良好的耐高温、耐油和耐低温平衡的环保低成本丙烯酸酯胶料配方。
本发明的技术方案是：
一种环保低成本丙烯酸酯胶料，其特征是其由以下组分组成：
丙烯酸酯橡胶：100份；
硬脂酸：1-2份；
防老剂445：1.5-3份；
内脱模剂：1-2份；
炭黑N-550：60-80份；
聚酯增塑剂：10-20份；
1#硫化剂：1-2.5份；
硫化助剂：1-3份。
所述丙烯酸酯橡胶包扩耐油级别的丙烯酸酯和耐寒级别的丙烯酸酯并用橡胶。
所述内脱模剂是指D821、D-S、D384、D294中的任意一种或任意两种。
所述硫化助剂为环保硫化助剂ACT55。
所述环保低成本丙烯酸酯胶料的参数为：
硬度HS：75±5度；
拉伸强度：≥14.5Mpa；
拉断伸长率：≥200％；
脆性温度－40℃：无裂纹；
压缩永久变形(150℃×70小时)：≤25％；
耐热空气老化(150℃×70小时)后性能变化；
硬度变化；0—+5；
拉伸强度变化率，－10％以内；
拉断伸长率变化率，－10％以内；
耐IRM903#油150℃×70小时；
硬度变化，－25以内；
拉伸强度变化率，－25％以内；
拉断伸长率变化率，－25％以内；
体积变化率：40％以下；
耐动态臭氧100pphm×40℃，480h后无龟裂。
本发明的有益效果是：
(1)本发明的环保低成本丙烯酸酯胶料选用耐油级别的乙烯丙烯酸酯橡胶(丙烯酸酯)和耐寒级别的乙烯丙烯酸酯橡胶(丙烯酸酯)两种不同杜邦牌号的生胶并用，通过配方调整，制备出了既满足了严格的耐IRM903#油性能，又符合耐－40℃低温要求的丙烯酸酯胶料。
(2)本发明的环保低成本丙烯酸酯胶料选用D.O.G公司的两种低成本内脱模剂替代现有丙烯酸酯专属内脱模剂VAM和18D。
(3)本发明的环保低成本丙烯酸酯胶料选用环保助硫化剂替代促进剂二邻甲苯胍，使配方达到环保要求。
(4)本发明的环保低成本丙烯酸酯胶料配方中添加1-2份的内脱模剂有效的解决了混炼过程中丙烯酸酯胶料的粘辊问题。
(5)一种新型环保增塑剂的使用显著提高了丙烯酸酯胶料的耐低温性能。
(6)本发明的环保低成本丙烯酸酯胶料配方中所用配合剂符合环保标准。
(7)自主研发丙烯酸酯混炼胶价格明显低于丙烯酸酯市场价格。
具体实施方式
下面通过实施例说明本发明，但不言而喻，本发明不受这些实施例的限制。
一种环保低成本丙烯酸酯胶料，其由以下组分组成：
丙烯酸酯橡胶：100份；
硬脂酸：1-2份；
防老剂445：1.5-3份；
内脱模剂：1-2份；
炭黑N-550：60-80份；
聚酯增塑剂：10-20份；
1#硫化剂：1-2.5份；
硫化助剂：1-3份。
所述丙烯酸酯橡胶包扩耐油级别的丙烯酸酯和耐寒级别的丙烯酸酯并用橡胶。
所述内脱模剂是指D821、D-S、D384、D294中的任意一种或任意两种。
所述硫化助剂为环保硫化助剂ACT55。
所述环保低成本丙烯酸酯胶料的参数为：
硬度HS：75±5度；
拉伸强度：≥14.5Mpa；
拉断伸长率：≥200％；
脆性温度－40℃：无裂纹；
压缩永久变形(150℃×70小时)：≤25％；
耐热空气老化(150℃×70小时)后性能变化；
硬度变化；0—+5；
拉伸强度变化率，－10％以内；
拉断伸长率变化率，－10％以内；
耐IRM903#油150℃×70小时；
硬度变化，－25以内；
拉伸强度变化率，－25％以内；
拉断伸长率变化率，－25％以内；
体积变化率：40％以下；
耐动态臭氧100pphm×40℃，480h后无龟裂。
上述的目的可以用下述的丙烯酸酯胶料配方达到：
耐油级别的丙烯酸酯：50；
耐寒级别的丙烯酸酯：50；
硬脂酸：1-2；
防老剂445：1.5-3；
内脱模剂：1-2；
炭黑N-550：60-80；
聚酯增塑剂：10-20；
1#硫化剂：1-2.5；
环保助硫化剂：1-3。
实施例的组分如表1所示。
质量单位：克
表1.本发明实施例的组分表
序号 组分 实施例1 实施例2 实施例3
1 耐油级丙烯酸酯 50 50 50
2 耐寒级丙烯酸酯 50 50 50
3 硬脂酸 1 1.5 2
4 内脱模剂D821 0 0 1
5 内脱模剂D-S 1 0 0
6 内脱模剂D384 1 1 0
7 内脱模剂D294 0 0 1
8 防老剂445 3 1.5 2
9 炭黑N-550 60 70 80
10 聚酯增塑剂 20 15 10
11 1#硫化剂 2 2.5 1
12 ACT55 2 1 3
13 总量 190 192.5 200
上述实例的实验性能检测如表2所示：
表2.本发明实施例实验性能检测表
需要理解到的是：任何不超出本发明的设计思路的组合、增加或修改，均落入本发明的保护范围内，本发明请求保护的技术内容已经全部记载在权利要求书中。
上面所述的实施例仅仅是对本发明的优选实施方式进行描述，并非对本发明的构思和范围进行限定，在不脱离本发明设计构思前提下，本领域中普通工程技术人员对本发明的技术方案做出的各种变型和改进，均应落入本发明的保护范围，本发明请求保护的技术内容已经全部记载在权利要求书中。

Claims (5)

1.一种环保低成本丙烯酸酯胶料，其特征是其由以下组分组成：
丙烯酸酯橡胶：100份；
硬脂酸：1-2份；
防老剂445：1.5-3份；
内脱模剂：1-2份；
炭黑N-550：60-80份；
聚酯增塑剂：10-20份；
1#硫化剂：1-2.5份；
硫化助剂：1-3份。
2.根据权利要求1所述的环保低成本丙烯酸酯胶料，其特征是所述丙烯酸酯橡胶包扩耐油级别的丙烯酸酯和耐寒级别的丙烯酸酯并用橡胶。
3.根据权利要求1所述的环保低成本丙烯酸酯胶料，其特征是：所述内脱模剂是指D821、D-S、D384、D294中的任意一种或任意两种。
4.根据权利要求1所述的环保低成本丙烯酸酯胶料，其特征是：所述硫化助剂为环保硫化助剂ACT55。
5.根据权利要求1所述的环保低成本丙烯酸酯胶料，其特征是：所述环保低成本丙烯酸酯胶料的参数为：
硬度HS：75±5度；
拉伸强度：≥14.5Mpa；
拉断伸长率：≥200％；
脆性温度－40℃：无裂纹；
压缩永久变形(150℃×70小时)：≤25％；
耐热空气老化(150℃×70小时)后性能变化；
硬度变化；0—+5；
拉伸强度变化率，－10％以内；
拉断伸长率变化率，－10％以内；
耐IRM903#油150℃×70小时；
硬度变化，－25以内；
拉伸强度变化率，－25％以内；
拉断伸长率变化率，－25％以内；
体积变化率：40％以下；
耐动态臭氧100pphm×40℃，480h后无龟裂。
CN201510797251.1A 2015-11-18 2015-11-18 一种环保低成本丙烯酸酯胶料 Pending CN105237929A (zh)