CN101993589A - 一种硅橡胶热缩管及其制备方法 - Google Patents

一种硅橡胶热缩管及其制备方法 Download PDF

Info

Publication number
CN101993589A
CN101993589A CN2009101634450A CN200910163445A CN101993589A CN 101993589 A CN101993589 A CN 101993589A CN 2009101634450 A CN2009101634450 A CN 2009101634450A CN 200910163445 A CN200910163445 A CN 200910163445A CN 101993589 A CN101993589 A CN 101993589A
Authority
CN
China
Prior art keywords
rubber
silicon rubber
silicon
shrink tube
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2009101634450A
Other languages
English (en)
Other versions
CN101993589B (zh
Inventor
周和平
赵源
秦荣勤
李红伟
刘占理
廖雄兵
于英智
陈玲聪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Woer Heat Shrinkable Material Co Ltd
Original Assignee
Shenzhen Woer Heat Shrinkable Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Woer Heat Shrinkable Material Co Ltd filed Critical Shenzhen Woer Heat Shrinkable Material Co Ltd
Priority to CN200910163445.0A priority Critical patent/CN101993589B/zh
Publication of CN101993589A publication Critical patent/CN101993589A/zh
Application granted granted Critical
Publication of CN101993589B publication Critical patent/CN101993589B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种硅橡胶热缩管及其制备方法，为了克服现有的热缩管在耐高温、耐油及耐溶剂性能比较差，不能适应汽车、高速列车、军工及航天等行业的高耐油、耐溶剂的性能需求的问题，本发明提供一种硅橡胶热缩管，其材料主要包括硅橡胶、热缩性树脂、补强剂、交联剂、硅油及可选性硬脂酸锌；同时，本发明还提出以上述材料生产热缩管的方法，本发明提供的硅橡胶热缩管，有很好的稳定性和高耐热性、耐寒特性，可以应用于对耐热、耐寒、耐绝缘性能有更高要求的电力、电子工业场所。

Description

一种硅橡胶热缩管及其制备方法
技术领域
本发明涉及热缩管，尤其涉及硅橡胶热缩管及其制备方法。
背景技术
目前，用于生产热缩管的主要材料包括：①烯烃类聚合物或共聚物；②橡胶类材料或热塑弹性体苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)、苯乙烯-异戊二烯嵌段共聚物(SIS)中的一种或一种以上的材料；③其它附助材料。现有的热缩管虽然具有较好的阻燃性能及环保性能，但是在耐温、耐油及耐溶剂方面性能比较差，不能适应汽车、高速列车、军工及航天行业等的高耐油、耐溶剂的要求。
发明内容
为了克服现有的热缩管在耐高温、耐油及耐溶剂方面性能比较差，不能适应汽车、高速列车、军工及航天等行业的高耐油、耐溶剂的性能需求的问题，本发明提供一种硅橡胶热缩管，其材料主要包括硅橡胶、热缩性树脂、补强剂、交联剂、硅油及可选性硬脂酸锌；同时，本发明还提出以上述材料生产热缩管的方法，本发明提供的硅橡胶热缩管，有很好的稳定性和高耐热性、耐寒特性，可以应用于耐热、耐寒，高电绝缘性能的电力、电子工业场所。
本发明解决其技术问题所采用的技术方案是：本发明提供一种硅橡胶热缩管，其包括如下材料：
硅橡胶，通式为[R2SiO]m，其中R为Me、Ph、Vi、Et等有机或无机取代基，包括二甲基硅橡胶(MQ)、甲基乙烯基硅橡胶(VMQ)、甲基苯基乙烯基硅橡胶(PVMQ)中和一种或多种；
热塑性树脂，包括苯基硅树脂、亚苯基硅树脂、甲基硅树脂、乙烯基硅树脂、丙烯酸树脂、乙烯醋酸乙烯共聚物(EVA)、乙烯丙烯酸乙酯共聚物(EEA)、低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)中的一种或多种；
补强剂，通式为SiO2无机粉末物，包括沉淀化白炭黑、气相化白炭黑中的一种或多种；
交联剂，包括过氧化物类硫化剂和/或稀有金属催化加成性硫化剂类中的一种或多种，过氧化物类硫化剂包括2，5-二甲基-2，5-双己烷、2，4-二氯过氧化苯甲酰、过氧化二异丙苯，稀有金属催化加成性硫化剂类包括铂金催化硅氢加成性硫化剂；
硅油，包括甲基硅油、羟基硅油、含氢硅油、乙烯基硅油中的一种或几种；
另外，可选择性地加入硬脂酸锌。
本发明还提出以上述材料生产硅橡胶热缩管的制备方法，它包括以下生产步骤：第一.硅橡胶混炼胶的制备；第二.橡塑混炼；第三.加交联剂共混；第四.挤出硫化，第.五扩张定型。
本发明的有益效果是：本发明提供的硅橡胶热缩管，有很好的稳定性和高耐热性、耐寒特性，可以应用于对耐热、耐寒、耐绝缘性能有高要求的电力、电子工业场所。
具体实施方式
本发明提供一种硅橡胶热缩管，其配方以重量计包括如下材料：
硅橡胶100份，通式为[R2SiO]m，其中R为Me、Ph、Vi、Et等有机或无机取代基，包括二甲基硅橡胶(MQ)、甲基乙烯基硅橡胶(VMQ)、甲基苯基乙烯基硅橡胶(PVMQ)中和一种或多种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制；
热塑性树脂5-50份，包括苯基硅树脂、亚苯基硅树脂、甲基硅树脂、乙烯基硅树脂、丙烯酸树脂、乙烯醋酸乙烯共聚物(EVA)、乙烯丙烯酸乙酯共聚物(EEA)、低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)中的一种或多种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制；
补强剂10-55份，通式为SiO2无机粉末物，包括沉淀化白炭黑、气相化白炭黑中的一种或多种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制；
交联剂1-5份，包括过氧化物类硫化剂和/或稀有金属催化加成性硫化剂类中的一种或多种，所述过氧化物类硫化剂包括2，5-二甲基-2，5-双己烷、2，4-二氯过氧化苯甲酰、过氧化二异丙苯，所述稀有金属催化加成性硫化剂类包括铂金催化硅氢加成性硫化剂，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制；
硅油0.2-38份，包括甲基硅油、羟基硅油、含氢硅油、乙烯基硅油中的一种或几种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制；
另外，可选择性地加入硬脂酸锌，其含量为0.1-0.5份。
本发明还提出以上述材料生产硅橡胶热缩管的制备方法，它包括以下生产步骤：
第一.硅橡胶混炼胶的制备：将上述配方硅橡胶、补强剂、硅油及可选性的硬脂酸锌等加入真空捏合机中，在常温混炼均匀，然后在140℃抽真空0.5-2小时制成硅橡胶混炼胶，取出待用，此步骤的混炼胶称为混炼胶A；
第二.橡塑共混：将第一步骤中制成的混炼胶A加热至150-170，再加入热塑性树脂混合均匀，取出在双辊开炼机上开炼出片状物，此步骤的混炼胶称为片状混炼胶B；
第三.加交联剂共混：在双辊开炼机上将第二步骤制成的片状混炼胶B加入交联剂共混制成片状物，此步骤的混炼胶称为片状混炼胶C；
第四.挤出硫化：将第三步骤中制成的片状混炼胶C切成小条后在挤出机上挤出，再经热空气烘道中硫化定型或在模压设备中硫化定型而制成弹性胶管；
第五.扩张定型：将弹性胶管加热至树脂的熔点以上，使用外力使其扩张然后骤冷定型。

Claims (8)

1.一种硅橡胶热缩管，其特征是：其材料含量以重量计含有以下材料：硅橡胶100份，热塑性树脂5-50份，补强剂10-55份，交联剂1-5份，硅油0.2-38份。
2.根据权利要求1所述的一种硅橡胶热缩管，其特征是：其材料中还可以含有硬脂酸锌0.1-0.5份。
3.根据权利要求1所述的一种硅橡胶热缩管，其特征是：所述硅橡胶通式为[R2SiO]m，其中R为Me、Ph、Vi、Et等有机或无机取代基，包括二甲基硅橡胶(MQ)、甲基乙烯基硅橡胶(VMQ)、甲基苯基乙烯基硅橡胶(PVMQ)中和一种或多种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制。
4.根据权利要求1所述的一种硅橡胶热缩管，其特征是：所述热塑性树脂包括苯基硅树脂、亚苯基硅树脂、甲基硅树脂、乙烯基硅树脂、丙烯酸树脂、乙烯醋酸乙烯共聚物(EVA)、乙烯丙烯酸乙酯共聚物(EEA)、低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)中的一种或多种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制。
5.根据权利要求1所述的一种硅橡胶热缩管，其特征是：所述补强剂通式为SiO2无机粉末物，包括沉淀化白炭黑、气相化白炭黑中的一种或多种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制。
6.根据权利要求1所述的一种硅橡胶热缩管，其特征是：所述交联剂包括过氧化物类硫化剂和/或稀有金属催化加成性硫化剂类中的一种或多种，所述过氧化物类硫化剂包括2，5-二甲基-2，5-双己烷、2，4-二氯过氧化苯甲酰、过氧化二异丙苯，所述稀有金属催化加成性硫化剂类包括铂金催化硅氢加成性硫化剂，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制。
7.根据权利要求1所述的一种硅橡胶热缩管，其特征是：所述硅油包括甲基硅油、羟基硅油、含氢硅油、乙烯硅油中的一种或多种，当加入多种材料时，所述含量为各种材料的总含量而各种材料之间的配比不受限制。
8.一种硅橡胶热缩管的制备方法，其包括以下生产步骤：
第一.硅橡胶混炼胶的制备：按1至7任一权利要求所述将硅橡胶、补强剂、硅油及可选性的硬脂酸锌等加入真空捏合机中，在常温混炼均匀，然后在140℃抽真空0.5-2小时制成硅橡胶混炼胶，取出待用，此步骤的混炼胶称为混炼胶A；
第二.橡塑共混：将第一步骤中制成的混炼胶A加热至150-170，再加入热塑性树脂混合均匀，取出在双辊开炼机上开炼出片状物，此步骤的混炼胶称为片状混炼胶B；
第三.加交联剂共混：在双辊开炼机上将第二步骤制成的片状混炼胶B加入交联剂共混制成片状物，此步骤的混炼胶称为片状混炼胶C；
第四.挤出硫化：将第三步骤中制成的片状混炼胶C切成小条后在挤出机上挤出，再经热空气烘道中硫化定型或在模压设备中硫化定型而制成弹性胶管；
第五.扩张定型：弹性胶管加热至树脂的熔点以上，使用外力使其扩张然后骤冷定型。
CN200910163445.0A 2009-08-13 2009-08-13 一种硅橡胶热缩管及其制备方法 Active CN101993589B (zh)