CN101538770A - Terylene coral fleece blanket fabrics and processing method thereof - Google Patents
Terylene coral fleece blanket fabrics and processing method thereof Download PDFInfo
- Publication number
- CN101538770A CN101538770A CN200910025432A CN200910025432A CN101538770A CN 101538770 A CN101538770 A CN 101538770A CN 200910025432 A CN200910025432 A CN 200910025432A CN 200910025432 A CN200910025432 A CN 200910025432A CN 101538770 A CN101538770 A CN 101538770A
- Authority
- CN
- China
- Prior art keywords
- cloth
- speed
- terylene
- control
- setting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to terylene coral fleece blanket fabrics and a processing method thereof, which belongs to the technical field of terylene fiber products and comprises voile weave and ground weave, the raw material used by the voile weave is DTY terylene filament in 133dtex/192f, 111dtex/192f or 111dtex/144f, and the raw material used by the ground weave is FDY terylene filament of 75dtex/24f, wherein the mass percentage of the DTY terylene filament occupied in the fabrics is 60-70 percent, and the mass percentage of the FDY terylene filament occupied in the fabrics is 30-40 percent. The invention can lead villus of the fabrics to be straight so as to have excellent lodging resistance and warmth retention property, and can obtain 150-250g/m<2> of gram weight of thread count and be suitable to fabricate household wares such as bathrobe, sleepwear, sheet, and the like. The method can ensure the advantages of the terylene coral fleece blanket fabrics, and can lead the terylene coral fleece blanket fabrics to have better sterilizing, antistatic and anti-allergic effects so as to meet the serviceability.
Description
Technical field
The invention belongs to technical field of terylene fiber products, be specifically related to a kind of terylene coral fleece blanket fabrics, and relate to the processing method of this lining.
Background technology
Chinese invention patent Granted publication CN1266327C discloses a kind of terylene superfine-denier coral fleece, the raw material of its selection is: choose 0.58dtex or 0.58dtex following terylene thread or polyamide composite filaments and make suede yarn raw material, choose the polyester FDY filament of 111-167dtex and make end silk raw material, the shared mass percent of its medium staple yarn raw material is 60-80%, and silk raw material shared mass percent in the end is 40-20%.Though the woollen blanket that production method obtained that limits through this patent by above-mentioned raw materials have the lint style just as the seabed coral, warmth retention property is good and slim and graceful soft strong point, but the purposes relative narrower for example can not be made it such as house articles for use such as bathrobe, bathing gown, pyjamas, bedding such as sheets.In addition, (one or claim the fiber number of a branch of monofilament) is that the 167dtex/288f of 0.52D is the terylene low elastic interlaced yarn (specification the 3rd of this patent to the 4th page embodiment 1 and embodiment 2) of 150D/288F as 0.58dtex because the F number of the suede yarn raw material that uses of patent, therefore this terylene low elastic interlaced yarn is thinner relatively, thereby make the tall and straight weak effect of fine hair, lodging easily, in case the fine hair lodging, warmth retention property and texture often show as very shortcoming so.Also have, the thread count of the resulting woollen blanket of above-mentioned patent is dredged, and can't process grammes per square metre at 250g/m
2Following fabric, more particularly can't process common required grammes per square metre such as the house articles for use that are adapted to process aforesaid bathrobe, bathing gown, pyjamas, bedding is 150-250g/m
2Fabric, although the step b) of the claim 2 of this patent is defined as 200-1200g/m
2, but make a general survey of its four embodiment, the grammes per square metre that obtains is respectively 400g/m
2, 280g/m
2, 400g/m
2And 280g/m
2, whether the claim of not going for the time being to touch upon is able to the support by embodiment, promptly whether is woven 200-279g/m
2Product, yet be 150-250g/m if process grammes per square metre with raw material that patent is selected
2Fabric, not only lose the lint style, and fine hair can occur and seriously fall to take off phenomenon.Have, the resulting woollen blanket of technology of instructing by above-mentioned patent does not have antibiotic and effect antistatic again, thereby has the anxiety of the allergy when using.
In sum, in the prior art instruction to have by the choose reasonable raw material and adopt suitable processing method to process to be made the grammes per square metre of bathrobe, bathing gown trousers, pyjamas and sheet etc. be 150-250g/m
2And technology enlightenment with the desirable terylene coral fleece blanket fabrics of good antibiotic, antistatic and antianaphylactic taking, to this, the applicant has carried out long-term exploration, technical scheme described below produces under above-mentioned background.
Summary of the invention
It is 150-250g/m that task of the present invention is to provide a kind of house articles for use and grammes per square metre that can be suitable for processing such as bathrobe, bathing gown bath trousers, nightwear pyjama trousers and sheet
2Straight and upright and difficult lodging of fine hair and the good terylene coral fleece blanket fabrics of warmth retention property.
Task of the present invention also is to provide a kind of processing method of terylene coral fleece blanket fabrics, this method can not only ensure the described effect that terylene coral fleece blanket fabrics possesses, and can also make coral fleece blanket fabrics have antibiotic, antistatic and antiallergic effect and satisfy taking.
For task of the present invention is finished in embodiment, technical scheme provided by the present invention is: a kind of terylene coral fleece blanket fabrics, comprise suede yarn tissue and bottom silk organization, it is the DTY terylene thread of 133dtex/192f, 111dtex/192f or 111dtex/144f that described suede yarn is organized used raw material, and the used raw material of described bottom silk organization is the FDY terylene thread of 75dtex/24f, wherein: DTY terylene thread shared mass percent in lining is 60-70%, and described FDY silk shared mass percent in lining is 40-30%.
Finish an also task of the present invention for embodiment, technical scheme provided by the present invention is: a kind of processing method of terylene coral fleece blanket fabrics, and this method may further comprise the steps:
A) select materials, choose the raw material that is used to constitute suede yarn tissue and is used to constitute bottom silk organization respectively, obtain treating weaving raw material;
B) weave, will treat that weaving raw material is put to warp knitting machine and weaves, and control grey cloth grammes per square metre 150-250g/m
2, obtain waiting to cut open width of cloth grey cloth;
C) cut open the width of cloth, grade is cutd open width of cloth grey cloth cuts open the width of cloth and control hair is high, obtain treating the pre-setting grey cloth;
D) pre-setting is treated pre-setting grey cloth pre-setting, and the rotation speed of fan of control pre-setting temperature, cloth speed and setting machine obtains the pre-setting grey cloth;
E) dyeing or stamp dye or stamp to the pre-setting grey cloth, obtain pending stained clot-h or calico;
F) post processing, to the stained clot-h post processing: in cold chamber by fabric weight than adding softener, antistatic additive, smooth agent, leavening agent and antiseptic, and control treatment temperature and time, clean after the processing, dehydration, oven dry then and control bake out temperature and cloth speed, obtain treating the plucking stained clot-h, to the calico post processing: earlier calico is dried, evaporate again, evaporate after washing, when washing, in water-bath, add caustic soda and sodium hydrosulfite and insulation, finish the back in insulation and add softener by the fabric weight ratio, antistatic additive, smooth agent, leavening agent and antiseptic carry out impregnation process at normal temperatures, oven dry then and adjusting bake out temperature and cloth speed obtain treating the plucking calico;
G) plucking is treated the plucking stained clot-h or is treated the back side plucking of plucking calico, and plucking drum rotation speed and the cloth speed and the plucking number of times of control napper obtain treating the carding fabric;
H) carding of carding fabric is treated in carding, and the rotating speed and the cloth speed of control combing machine for fur, to the hair side bristle after the carding, obtains treating the cropping grey cloth then;
I) back side cropping of cropping grey cloth is treated in back side cropping, and control cropping roller speed and cloth speed obtain the grey cloth of the back side through cropping;
J) ring baking, to the grey cloth ring baking of the back side through cropping, control loop baking temperature and time obtains treating back typing grey cloth;
K) back typing will be treated the typing of back typing grey cloth, and the rotating speed of control back setting temperature and control cloth speed and control blower fan obtains the finished product terylene coral fleece blanket fabrics.
In a specific embodiment of the present invention, the raw material of the bottom silk organization steps A) is the DTY terylene thread of 133dtex/192f, 111dtex/192f or 111dtex/144f, the raw material of described bottom silk organization is the FDY terylene thread of 75dtex/24f, wherein, DTY silk shared mass percent in lining is 60-70%, and FDY silk shared mass percent in lining is 40-30%.
In another specific embodiment of the present invention, step B) warp knitting machine described in is woven as double rib warp loom and weaves, the rotating speed of warp knitting machine is 450-480n/min, histological structure be GB1:4-4-4-4/0-0-0-0/3-3-3-3/0-0-0-0//, GB2:0-1-1-1/1-0-0-0//, GB3:0-1-0-1/1-0-1-0//, GB4: empty comb, GB5:0-0-0-1/1-1-1-0//and GB6:0-0-4-4/4-4-0-0/0-0-3-3/3-3-0-0//, the mode that passes is for completely wearing.
In also specific embodiment of the present invention, step C) the control hair described in is high to be with the high 4-5mm of being controlled to be of hair.
The rotation speed of fan of control pre-setting temperature, cloth speed and the setting machine in another specific embodiment of the present invention, step D) is that the pre-setting temperature is controlled to be 200-210 ℃, the cloth speed control is made as 25-35m/min and rotation speed of fan is controlled to be 1400-1600n/min.
In another specific embodiment of the present invention, step e) the used dyestuff of the dyeing described in is disperse dyes, the input amount of disperse dyes is the 0.001%-0.1% of fabric weight ratio, and before dropping into dyestuff in the dyeing container, in container, add earlier as the glacial acetic acid 0.5-0.8g/L of auxiliary agent and the pH4-6 of dye leveller 0.5-1g/L and adjusting dye bath, the dye bath heating rate is 1-2 ℃/min, insulation 30-60min is cooled to 60-80 ℃ then grey cloth is gone out dye vat when being warming up to 120-130 ℃; The prescription of the printing paste that described stamp is used is Red-1 200-1.5g, disperse yellow 1-1.5g and disperse blue 0.3-0.5g contained in the printing paste of every 100g, and all the other are thickener.
More of the present invention and in specific embodiment, step F) softener described in is that 2-5%, antistatic additive are that 0.5-1.5%, smooth agent are that 0.5-1.5%, leavening agent are that 1-2% and antiseptic are 1-2%, described percentage is the percentage by fabric weight, described control treatment temperature and time are meant treatment temperature and time are controlled to be 80-120 ℃ and 20-30min respectively, and described control bake out temperature and cloth speed are that bake out temperature and cloth speed are controlled to be 160-180 ℃ and 25-40m/min respectively; The described caustic soda and sodium hydrosulfite and insulation of adding in water-bath is meant adding caustic soda 2.5-3.5g/L, sodium hydrosulfite 2.5-3.5g/L and in the time of 70-80 ℃ the insulation 25-35min, the addition of the described softener that adds by the fabric weight ratio after insulation finishes is 2-3%, antistatic additive is 0.4-0.6%, smooth agent is 0.5-1.5%, leavening agent is that 1.5-2.5% and antiseptic are 1-2%, the time of described impregnation process at normal temperatures is 30min, and described adjusting bake out temperature and cloth speed are that bake out temperature and cloth speed are adjusted to 170-175 ℃ respectively, 35-40m/min.
In of the present invention and then specific embodiment, the plucking number of times of the plucking of the back side step G) is 3-5 time, and the rotating speed of the plucking cylinder of described control napper and cloth speed are that the rotating speed of plucking cylinder and cloth speed are controlled to be 65-75n/min, 18-28m/min respectively; The rotating speed of the control combing machine for fur step H) and cloth speed are that the rotating speed with the carding roller of combing machine for fur is controlled to be 60-80n/min, the cloth speed control is made as 20-30m/min, described hair side bristle is meant that the rotating speed with the bristle roller is controlled to be left bristle roller 9-15n/min, right bristle roller 9-15n/min.
In again of the present invention and then specific embodiment, step I) control cropping roller speed described in and cloth speed are that the speed with the cropping roller is controlled to be 1000-1200n/min, and the cloth speed control is made as 15-25m/min; Step J) the control loop baking temperature and time described in is that ring baking temperature and ring baking time are controlled to be 100-140 ℃, 15-30min respectively; Step K) setting temperature is that the back setting temperature is controlled to be 175-180 ℃ after the control described in, and described control cloth speed is for to be made as 30-45m/min with the cloth speed control, and described control rotation speed of fan is that rotation speed of fan is controlled to be 600-800n/min.
One of advantage of technical scheme provided by the present invention, because it is reasonable to the material choice of suede yarn tissue and bottom silk organization, thereby the fine hair that can make lining is tall and straight and have desirable lodging resistance and warmth retention property, and the grammes per square metre that can obtain thread count is 150-250g/m
2Be suitable for making the house articles for use of bathing trousers, nightwear pyjama trousers and sheet etc. as bathrobe, bathing gown; Two, method can ensure outside the described advantage that terylene coral fleece blanket fabrics possesses, and also can make lining have good antibiotic, antistatic and antiallergic effect and uses and satisfy taking.
The specific embodiment
Embodiment 1:
A) select materials, choose the DTY terylene thread of 133dtex/192f and make suede yarn raw material, the FDY terylene thread of choosing 75dtex/24f is made the raw material of end tissue, wherein, described DTY terylene thread shared mass percent in lining is 65%, described FDY silk shared mass percent in lining is 35%, preferred but the non-GE209 type micro computer of being produced by Jiangsu Province, China Changzhou No.8 Textile Machinery Co., Ltd. that uses is monitored the warping machines warping with being limited in real time, warping head part is 490 * 3, speed of beaming is: 700m/min obtains treating weaving raw material;
B) weave, will be by steps A) weaving raw material adopts the model of being produced by Jiangsu Province, China Changzhou Karlmayer Textile Machinery Co., Ltd. is that E22 six sley bar La Sheer double rib warp looms are weaved in selected treating, and the grey cloth Gram Mass is 245g/m
2Fabric width is 160cm, loom is that the rotating speed of warp knitting machine is 475n/min, six sley bar looms adopt five sley bars to weave, one of them sley bar is the empty comb of GB4, so not only can improve loom speed, and can save cost, concrete histological structure be GB1:4-4-4-4/0-0-0-0/3-3-3-3/0-0-0-0//, GB2:0-1-1-1/1-0-0-0//, GB3:0-1-0-1/1-0-1-0//, GB4: empty comb, GB5:0-0-0-1/1-1-1-0//and GB6:0-0-4-4/4-4-0-0/0-0-3-3/3-3-0-0//, the mode that passes is 245g/m for completely wearing thereby obtain grammes per square metre
2With fabric width be 160cm wait to cut open width of cloth grey cloth;
C) cut open the width of cloth, to by step B) resultingly wait to cut open width of cloth grey cloth and cut open the width of cloth, what obtain matte Mao Gaowei 4.5mm treats the pre-setting grey cloth;
D) pre-setting, to by step C) the resulting pre-setting grey cloth for the treatment of adopts five the four segment type setting machines typings of U-828 of being produced by tw Taiwan Ligen Industry Co Ltd, 205 ℃ of control pre-setting temperature, cloth speed (grey cloth speed) 32m/min and control rotation speed of fan 1500n/min obtain the pre-setting grey cloth;
E) dyeing, to by step D) resulting pre-setting piece dyeing finishing, dyeing apparatus adopts high temperature double overflow dyeing machine, the used dyestuff that dyes is disperse dyes, specifically: be glacial acetic acid 0.6g/L and the dye leveller 0.8g/L that adds in the dye bath as auxiliary agent to dye vat earlier, and regulate the pH value to pH5, then at normal temperatures with disperse yellow 0.001% (the fabric weight ratio is owf), disperse blue 0.006% (fabric weight ratio) and disperse red 0.04% (fabric weight ratio), wait to move and grey cloth is introduced dye vat behind the 5-10min and lid closes the dye vat cylinder cap, the notion of alleged here operation is meant treats stained clot-h normally operation in dye vat, so that make the full and uniform fiber surface that is adsorbed on of dyestuff, opening steam valve heats up, 1 ℃/min of dye bath heating rate (speed), insulation 50min when being warming up to 125 ℃, be cooled to 70 ℃ then, grey cloth is gone out dye vat, obtain pending stained clot-h, high temperature double overflow dyeing machine described in this step is preferred but non-what be limited to is that to adopt the model of being produced by Jiangsu Province, China Wuxi City China foreign dyeing and finishing machinery Co., Ltd be SME-1000 high temperature and high speed pine formula dyeing machine, described dye leveller preferably adopts the GH1770C type dye leveller of being produced by the wide magnificent auxiliary chemicals in Changzhou Changzhou, Jiangsu Province, China Co., Ltd, and described disperse dyes preferably adopt Jiangsu Province, China Wuxi City DeSiDa Wuxi Dye Co., Ltd to produce, the moral department disperse dyes of selling;
F) post processing, to by step e) to carry out post processing be softness and antibacterial treatment to resulting stained clot-h, specifically: to cold chamber is to add softener 3% by the fabric weight ratio in the normal temperature cylinder, antistatic additive 1%, smooth agent 1%, leavening agent 1% and antiseptic 1.5%, behind the 30min that softens on the dipping, grey cloth is being gone out cylinder under 110 ℃, afterwards through cleaning, dry after the dehydration, bake out temperature is 170 ℃, cloth speed is 30m/min, the rotation speed of fan of dryer is 1450n/min, obtain treating the plucking stained clot-h, the GH6570B type finishing agent that softener described in this step adopts Changzhou, Jiangsu Province, China wide magnificent auxiliary chemicals Co., Ltd to produce, antistatic additive, it is GH7000-I type antistatic additive that smooth agent and leavening agent also all adopt the trade mark of being produced by the said firm, GH7300 type smooth agent and GH7600-II type leavening agent, described antiseptic preferably adopt by exploitation of Chinese Shandong Textile Research Institute and suitability for industrialized production, the trade mark of selling is the agent of AM101 type antibacterial fabric;
G) plucking, to by step F) the resulting back side for the treatment of the plucking stained clot-h model of being produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. that adopts preferably that industry widely uses is MB331 type 36 roller napper pluckings 4 times, the rotating speed of the plucking cylinder of napper is that 70n/min, cloth speed are 24m/min, obtains treating the carding fabric;
H) carding, to by step G) the carding fabric for the treatment of that obtains causes model that Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. that industry generally uses produces as the 24 roller combing machine for fur cardings of SME-485 type once, the swift rotating speed of combing machine for fur is that 70n/min, cloth speed are 25m/min, then hair side is carried out bristle, the rotating speed of control bristle roller: left bristle roller 10n/min, right bristle roller 10n/min obtains treating the cropping grey cloth;
I) back side cropping is to by step H) resultingly treat the shearing machine cropping of cropping grey cloth, burr is smooth, and the rotating speed of cropping roller and cloth speed are respectively 1100n/min and 20m/min, obtain the grey cloth of the back side through cropping;
J) ring baking, to by step I) the resulting back side is through a grey cloth ring baking of cropping (industry claims that the ring baking is for shaking), ring baking machine preferably adopts the model of being produced by grand the dyeing and finishing machinery Co., Ltd in Chinese Guangdong province Heshan City to shake the grain tube for the J8LX-300 type, 120 ℃ of ring baking temperature, cloth speed 20m/min obtains treating back typing grey cloth;
K) back typing, will be by step J) the resulting back typing grey cloth for the treatment of delivers to the i.e. back typing of five four segment type setting machines of U-828 HEAT SETTING of being produced by tw Taiwan Ligen Industry Co Ltd, the temperature of setting machine is 175 ℃, cloth speed is 35m/min, the rotation speed of fan of setting machine is 700n/min, and obtaining dyed color is 245g/m for red, grammes per square metre
2Fabric width be the terylene coral fleece blanket fabrics of 160cm and matte Mao Gaowei 4.5mm.
Embodiment 2:
A) select materials, choose the DTY terylene thread of 111dtex/192f and make suede yarn raw material, the FDY terylene thread of choosing 75dtex/24f is made the raw material of end tissue, wherein, described DTY terylene thread shared mass percent in lining is 60%, described FDY silk shared mass percent in lining is 40%, the GE209 type micro computer that uses Changzhou No.8 Textile Machinery Co., Ltd. to produce is monitored the warping machines warping in real time, warping head part is 470 * 3, speed of beaming is: 700m/min obtains treating weaving raw material;
B) weave, will be by steps A) weaving raw material adopts the model of being produced by Jiangsu Province, China Changzhou Karlmayer Textile Machinery Co., Ltd. is that E22 six sley bar La Sheer double rib warp looms are weaved in selected treating, and the grey cloth Gram Mass is 150g/m
2Fabric width is 155cm, the rotating speed of loom is 455n/min, six sley bar looms adopt five sley bars to weave, one of them sley bar is the empty comb of GB4, so not only can improve loom speed, and can save cost, concrete histological structure be GB1:4-4-4-4/0-0-0-0/3-3-3-3/0-0-0-0//, GB2:0-1-1-1/1-0-0-0//, GB3:0-1-0-1/1-0-1-0//, GB4: empty comb, GB5:0-0-0-1/1-1-1-0//and GB6:0-0-4-4/4-4-0-0/0-0-3-3/3-3-0-0//, the mode that passes is 150g/m for completely wearing thereby obtain grammes per square metre
2With fabric width be 155cm wait to cut open width of cloth grey cloth;
C) cut open the width of cloth, to by step B) resultingly wait to cut open width of cloth grey cloth and cut open the width of cloth, what obtain matte Mao Gaowei 4mm treats the pre-setting grey cloth;
D) pre-setting, to by step C) the resulting pre-setting grey cloth for the treatment of adopts five the four segment type setting machines typings of U-828 of being produced by tw Taiwan Ligen Industry Co Ltd, 210 ℃ of control pre-setting temperature, cloth speed (grey cloth speed) 25m/min and control rotation speed of fan 1600n/min obtain the pre-setting grey cloth;
E) dyeing, to by step D) resulting pre-setting piece dyeing finishing, dyeing apparatus adopts high temperature double overflow dyeing machine, the used dyestuff that dyes is disperse dyes, specifically: be glacial acetic acid 0.6g/L and the dye leveller 0.8g/L that adds in the dye bath as auxiliary agent to dye vat earlier, and regulate the pH value to pH4, then at normal temperatures with disperse yellow 0.03% (the fabric weight ratio is owf), disperse blue 0.02% (fabric weight ratio) and disperse red 0.035% (fabric weight ratio), wait to move and grey cloth is introduced dye vat behind the 5-10min and lid closes the dye vat cylinder cap, the notion of alleged here operation is meant treats stained clot-h normally operation in dye vat, so that make the full and uniform fiber surface that is adsorbed on of dyestuff, opening steam valve heats up, 1 ℃/min of dye bath heating rate (speed), insulation 50min when being warming up to 125 ℃, be cooled to 70 ℃ then, grey cloth is gone out dye vat, obtain pending stained clot-h, high temperature double overflow dyeing machine described in this step is preferred but non-what be limited to is that to adopt the model of being produced by Jiangsu Province, China Wuxi City China foreign dyeing and finishing machinery Co., Ltd be SME-1000 high temperature and high speed pine formula dyeing machine, described dye leveller preferably adopts the GH1770C type dye leveller of being produced by the wide magnificent auxiliary chemicals in Changzhou Changzhou, Jiangsu Province, China Co., Ltd, and described disperse dyes preferably adopt Jiangsu Province, China Wuxi City DeSiDa Wuxi Dye Co., Ltd to produce, the moral department disperse dyes of selling;
F) post processing, to by step e) to carry out post processing be softness and antibacterial treatment to resulting stained clot-h, specifically: to cold chamber is to add softener 3% by the fabric weight ratio in the normal temperature cylinder, antistatic additive 1%, smooth agent 1%, leavening agent 1% and antiseptic 1.5%, down gentlely on the dipping behind 30min, grey cloth gone out cylinder down at 95 ℃, afterwards through cleaning, dry after the dehydration, bake out temperature is 170 ℃, cloth speed is 30m/min, the rotation speed of fan of dryer is 1450n/min, obtain treating the plucking stained clot-h, the GH6570B type finishing agent that softener described in this step adopts Changzhou, Jiangsu Province, China wide magnificent auxiliary chemicals Co., Ltd to produce, antistatic additive, it is GH7000-I type antistatic additive that smooth agent and leavening agent also all adopt the trade mark of being produced by the said firm, GH7300 type smooth agent and GH7600-II type leavening agent, described antiseptic preferably adopt by exploitation of Chinese Shandong Textile Research Institute and suitability for industrialized production, the trade mark of selling is the agent of AM101 type antibacterial fabric;
G) plucking, to by step F) the resulting back side for the treatment of the plucking stained clot-h model of being produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. that adopts preferably that industry widely uses is MB 331E type 36 roller napper pluckings 4 times, the rotating speed of the plucking cylinder of napper is that 70n/min, cloth speed are 24m/min, obtains treating the carding fabric;
H) carding, to by step G) treating of the obtaining model that the carding fabric causes that industry generally uses is produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. is as the 24 roller combing machine for fur cardings of SME-485 type once, the swift rotating speed of combing machine for fur is that 70n/min, cloth speed are 25m/min, then hair side is carried out bristle, the rotating speed of control bristle roller: left bristle roller 10n/min, right bristle roller 10n/min obtains treating the cropping grey cloth;
I) back side cropping is to by step H) resultingly treat the shearing machine cropping of cropping grey cloth, hair will be cut smoothly, and the rotating speed of cropping roller and cloth speed are respectively 1100n/min and 20m/min, obtain the grey cloth of the back side through cropping;
J) ring baking, to by step I) the resulting back side is through a grey cloth ring baking of cropping (industry claims that the ring baking is for shaking), ring baking machine preferably adopts the model of being produced by grand the dyeing and finishing machinery Co., Ltd in Chinese Guangdong province Heshan City to shake the grain tube for the J8LX-300 type, 120 ℃ of ring baking temperature, cloth speed 20m/min obtains treating back typing grey cloth;
K) back typing, will be by step J) the resulting back typing grey cloth for the treatment of delivers to the i.e. back typing of five four segment type setting machines of U-828 HEAT SETTING of being produced by tw Taiwan Ligen Industry Co Ltd, the temperature of setting machine is 175 ℃, cloth speed is 35m/min, the rotation speed of fan of setting machine is 700n/min, and obtaining dyed color is 150g/m for red, grammes per square metre
2Fabric width be the terylene coral fleece blanket fabrics of 155cm and matte Mao Gaowei 4mm.
Embodiment 3:
A) select materials, choose the DTY terylene thread of 111dtex/144f and make suede yarn raw material, the FDY terylene thread of choosing 75dtex/24f is made the raw material of end tissue, wherein, described DTY terylene thread shared mass percent in lining is 65%, described FDY silk shared mass percent in lining is 35%, the GE209 type micro computer that uses Changzhou No.8 Textile Machinery Co., Ltd. to produce is monitored the warping machines warping in real time, warping head part is 470 * 3, speed of beaming is: 700m/min obtains treating weaving raw material;
B) weave, will be by steps A) weaving raw material adopts the model of being produced by Jiangsu Province, China Changzhou Karlmayer Textile Machinery Co., Ltd. is that E22 six sley bar La Sheer double rib warp looms are weaved in selected treating, and the grey cloth Gram Mass is 175g/m
2Fabric width is 155cm, the rotating speed of loom is 480n/min, six sley bar looms adopt five sley bars to weave, one of them sley bar is the empty comb of GB4, so not only can improve loom speed, and can save cost, concrete histological structure be GB1:4-4-4-4/0-0-0-0/3-3-3-3/0-0-0-0//, GB2:0-1-1-1/1-0-0-0//, GB3:0-1-0-1/1-0-1-0//, GB4: empty comb, GB5:0-0-0-1/1-1-1-0//and GB6:0-0-4-4/4-4-0-0/0-0-3-3/3-3-0-0//, the mode that passes is 175g/m for completely wearing thereby obtain grammes per square metre
2With fabric width be 155cm wait to cut open width of cloth grey cloth;
C) cut open the width of cloth, to by step B) resultingly wait to cut open width of cloth grey cloth and cut open the width of cloth, what obtain matte Mao Gaowei 4.5mm treats the pre-setting grey cloth;
D) pre-setting, to by step C) the resulting pre-setting grey cloth for the treatment of adopts five the four segment type setting machines typings of U-828 of being produced by tw Taiwan Ligen Industry Co Ltd, 200 ℃ of control pre-setting temperature, cloth speed (grey cloth speed) 25m/min and control rotation speed of fan 1400n/min obtain the pre-setting grey cloth;
E) dyeing, to by step D) resulting pre-setting piece dyeing finishing, dyeing apparatus adopts high temperature double overflow dyeing machine, the used dyestuff that dyes is disperse dyes, specifically: be glacial acetic acid 0.5g/L and the dye leveller 0.5g/L that adds in the dye bath as auxiliary agent to dye vat earlier, and regulate the pH value to pH5.5, then at normal temperatures with disperse yellow 0.05% (the fabric weight ratio is owf), disperse blue 0.01% (fabric weight ratio) and disperse red 0.01% (fabric weight ratio), wait to move and grey cloth is introduced dye vat behind the 5-10min and lid closes the dye vat cylinder cap, the notion of alleged here operation is meant treats stained clot-h normally operation in dye vat, so that make the full and uniform fiber surface that is adsorbed on of dyestuff, opening steam valve heats up, 1.5 ℃/min of dye bath heating rate (speed), insulation 30min when being warming up to 130 ℃, be cooled to 60 ℃ then, grey cloth is gone out dye vat, obtain pending stained clot-h, high temperature double overflow dyeing machine described in this step is preferred but non-what be limited to is that to adopt the model of being produced by Jiangsu Province, China Wuxi City China foreign dyeing and finishing machinery Co., Ltd be SME-1000 high temperature and high speed pine formula dyeing machine, described dye leveller preferably adopts the GH1770C type dye leveller of being produced by the wide magnificent auxiliary chemicals in Changzhou Changzhou, Jiangsu Province, China Co., Ltd, and described disperse dyes preferably adopt Jiangsu Province, China Wuxi City DeSiDa Wuxi Dye Co., Ltd to produce, the moral department disperse dyes of selling;
F) post processing, to by step e) to carry out post processing be softness and antibacterial treatment to resulting stained clot-h, specifically: to cold chamber is to add softener 2% by the fabric weight ratio in the normal temperature cylinder, antistatic additive 0.6%, smooth agent 1.6%, leavening agent 2% and antiseptic 1%, down gentlely on the dipping behind 25min, grey cloth gone out cylinder down at 80 ℃, afterwards through cleaning, dry after the dehydration, bake out temperature is 160 ℃, cloth speed is 40m/min, the rotation speed of fan of dryer is 1450n/min, obtain treating the plucking stained clot-h, the GH6570B type finishing agent that softener described in this step adopts Changzhou, Jiangsu Province, China wide magnificent auxiliary chemicals Co., Ltd to produce, antistatic additive, it is GH7000-I type antistatic additive that smooth agent and leavening agent also all adopt the trade mark of being produced by the said firm, GH7300 type smooth agent and GH7600-II type leavening agent, described antiseptic preferably adopt by exploitation of Chinese Shandong Textile Research Institute and suitability for industrialized production, the trade mark of selling is the agent of AM101 type antibacterial fabric;
G) plucking, to by step F) the resulting back side for the treatment of the plucking stained clot-h model of being produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. that adopts preferably that industry widely uses is MB331E type 36 roller napper pluckings 4 times, the rotating speed of the plucking cylinder of napper is that 70n/min, cloth speed are 24m/min, obtains treating the carding fabric;
H) carding, to by step G) treating of the obtaining model that the carding fabric causes that industry generally uses is produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. is as the 24 roller combing machine for fur cardings of SME-485 type once, the swift rotating speed of combing machine for fur is that 60n/min, cloth speed are 20m/min, then hair side is carried out bristle, the rotating speed of control bristle roller: left bristle roller 10n/min, right bristle roller 10n/min obtains treating the cropping grey cloth;
I) back side cropping is to by step H) resultingly treat the shearing machine cropping of cropping grey cloth, hair will be cut smoothly, can not have height hair phenomenon to take place, and the rotating speed of cropping roller and cloth speed are respectively 1100n/min and 20m/min, obtain the grey cloth of the back side through cropping;
J) ring baking, to by step I) the resulting back side is through a grey cloth ring baking of cropping (industry claims that the ring baking is for shaking), ring baking machine preferably adopts the model of being produced by grand the dyeing and finishing Co., Ltd in Chinese Guangdong province Heshan City to shake the grain tube for the J8LX-300 type, 120 ℃ of ring baking temperature, cloth speed 20m/min obtains treating back typing grey cloth;
K) back typing, will be by step J) the resulting back typing grey cloth for the treatment of delivers to the i.e. back typing of five four segment type setting machines of U-828 HEAT SETTING of being produced by tw Taiwan Ligen Industry Co Ltd, the temperature of setting machine is 175 ℃, cloth speed is 35m/min, the rotation speed of fan of setting machine is 700n/min, and obtaining dyed color and be brown, grammes per square metre is 175g/m
2Fabric width be 155cm and matte Mao Gaowei 4.5mm terylene coral fleece blanket fabrics.
Embodiment 4:
A) select materials, choose the DTY terylene thread of 133dtex/192f and make suede yarn raw material, the FDY terylene thread of choosing 75dtex/24f is made the raw material of end tissue, wherein, described DTY terylene thread shared mass percent in lining is 70%, described FDY silk shared mass percent in lining is 30%, the GE209 type micro computer that uses Changzhou No.8 Textile Machinery Co., Ltd. to produce is monitored the warping machines warping in real time, warping head part is 490 * 3, speed of beaming is: 700m/min obtains treating weaving raw material;
B) weave, will be by steps A) weaving raw material adopts the model of being produced by Jiangsu Province, China Changzhou Karlmayer Textile Machinery Co., Ltd. is that E22 six sley bar La Sheer double rib warp looms are weaved in selected treating, and the grey cloth Gram Mass is 250g/m
2Fabric width is 160cm, the rotating speed of loom is 475n/min, six sley bar looms adopt five sley bars to weave, one of them sley bar is the empty comb of GB4, so not only can improve loom speed, and can save cost, concrete histological structure be GB1:4-4-4-4/0-0-0-0/3-3-3-3/0-0-0-0//, GB2:0-1-1-1/1-0-0-0//, GB3:0-1-0-1/1-0-1-0//, GB4: empty comb, GB5:0-0-0-1/1-1-1-0//and GB6:0-0-4-4/4-4-0-0/0-0-3-3/3-3-0-0//, the mode that passes is 250g/m for completely wearing thereby obtain grammes per square metre
2With fabric width be 160cm wait to cut open width of cloth grey cloth;
C) cut open the width of cloth, to by step B) resultingly wait to cut open width of cloth grey cloth and cut open the width of cloth, what obtain matte Mao Gaowei 5mm treats the pre-setting grey cloth;
D) pre-setting, to by step C) the resulting pre-setting grey cloth for the treatment of adopts the U-828 type setting machine of being produced by tw Taiwan Ligen Industry Co Ltd, 210 ℃ of control pre-setting temperature, cloth speed (grey cloth speed) 35m/min and control rotation speed of fan 1500n/min obtain the pre-setting grey cloth;
E) dyeing, to by step D) resulting pre-setting piece dyeing finishing, dyeing apparatus adopts high temperature double overflow dyeing machine, the used dyestuff that dyes is disperse dyes, specifically: be glacial acetic acid 0.8g/L and the dye leveller 0.8g/L that adds in the dye bath as auxiliary agent to dye vat earlier, and regulate the pH value, then at normal temperatures with disperse yellow 0.002% (the fabric weight ratio is owf), disperse blue 0.07% (fabric weight ratio) and disperse red 0.005% (fabric weight ratio), wait to move and grey cloth is introduced dye vat behind the 5-10min and lid closes the dye vat cylinder cap, the notion of alleged here operation is meant treats stained clot-h normally operation in dye vat, so that make the full and uniform fiber surface that is adsorbed on of dyestuff, opening steam valve heats up, 2 ℃/min of dye bath heating rate (speed), insulation 40min when being warming up to 125 ℃, be cooled to 70 ℃ then, grey cloth is gone out dye vat, obtain pending stained clot-h, high temperature double overflow dyeing machine described in this step is preferred but non-what be limited to is that to adopt the model of being produced by Jiangsu Province, China Wuxi City China foreign dyeing and finishing machinery Co., Ltd be SME-1000 high temperature and high speed pine formula dyeing machine, described dye leveller preferably adopts the GH1770C type dye leveller of being produced by the wide magnificent auxiliary chemicals in Changzhou Changzhou, Jiangsu Province, China Co., Ltd, and described disperse dyes preferably adopt Jiangsu Province, China Wuxi City DeSiDa Wuxi Dye Co., Ltd to produce, the moral department disperse dyes of selling;
F) post processing, to by step e) to carry out post processing be softness and antibacterial treatment to resulting stained clot-h, specifically: to cold chamber is to add softener 5% by the fabric weight ratio in the normal temperature cylinder, antistatic additive 0.5%, smooth agent 0.5%, leavening agent 1.5% and antiseptic 2%, down gentlely on the dipping behind 20min, grey cloth gone out cylinder down at 120 ℃, afterwards through cleaning, dry after the dehydration, bake out temperature is 180 ℃, cloth speed is 25m/min, the rotation speed of fan of dryer is 1450n/min, obtain treating the plucking stained clot-h, the GH6570B type finishing agent that softener described in this step adopts Changzhou, Jiangsu Province, China wide magnificent auxiliary chemicals Co., Ltd to produce, antistatic additive, it is GH7000-I type antistatic additive that smooth agent and leavening agent also all adopt the trade mark of being produced by the said firm, GH7300 type smooth agent and GH7600-II type leavening agent, described antiseptic preferably adopt by exploitation of Chinese Shandong Textile Research Institute and suitability for industrialized production, the trade mark of selling is the agent of AM101 type antibacterial fabric;
G) plucking, to by step F) the resulting back side for the treatment of the plucking stained clot-h model of being produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. that adopts preferably that industry widely uses is MB331E type 36 roller napper pluckings 4 times, the rotating speed of the plucking cylinder of napper is that 70n/min, cloth speed are 24m/min, obtains treating the carding fabric;
H) carding, to by step G) treating of the obtaining model that the carding fabric causes that industry generally uses is produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. is as the 24 roller combing machine for fur cardings of SME-485 type once, the swift rotating speed of combing machine for fur is that 70n/min, cloth speed are 25m/min, then hair side is carried out bristle, the rotating speed of control bristle roller: left bristle roller 10n/min, right bristle roller 10n/min obtains treating the cropping grey cloth;
I) back side cropping is to by step H) resultingly treat the shearing machine cropping of cropping grey cloth, it is clear smooth that cropping is wanted, and the rotating speed of cropping roller and cloth speed are respectively 1100n/min and 20m/min, obtain the grey cloth of the back side through cropping;
J) ring baking, to by step I) the resulting back side is through a grey cloth ring baking of cropping (industry claims that the ring baking is for shaking), ring baking machine preferably adopts the model of being produced by grand the dyeing and finishing machinery Co., Ltd in Chinese Guangdong province Heshan City to shake the grain tube for the J8LX-300 type, 120 ℃ of ring baking temperature, cloth speed 20m/min obtains treating back typing grey cloth;
K) back typing, will be by step J) the resulting back typing grey cloth for the treatment of delivers to the i.e. back typing of five four segment type setting machines of U-828 HEAT SETTING of being produced by tw Taiwan Ligen Industry Co Ltd, the temperature of setting machine is 175 ℃, cloth speed is 35m/min, the rotation speed of fan of setting machine is 700n/min, and obtaining dyed color is that blue look, grammes per square metre are 250g/m
2Fabric width be the terylene coral fleece blanket fabrics of 160cm and matte Mao Gaowei 5mm.
Embodiment 5:
A) select materials, choose the DTY terylene thread of 133dtex/192f and make suede yarn raw material, the FDY terylene thread of choosing 75dtex/24f is made the raw material of end tissue, wherein, described DTY terylene thread shared mass percent in lining is 70%, described FDY silk shared mass percent in lining is 30%, the GE209 type micro computer that uses Changzhou No.8 Textile Machinery Co., Ltd. to produce is monitored the warping machines warping in real time, warping head part is 450 * 4, speed of beaming is: 700m/min obtains treating weaving raw material;
B) weave, will be by steps A) weaving raw material adopts the model of being produced by Jiangsu Province, China Changzhou Karlmayer Textile Machinery Co., Ltd. is that E22 six sley bar La Sheer double rib warp looms are weaved in selected treating, and the grey cloth Gram Mass is 185g/m
2Fabric width is 200cm, the rotating speed of loom is 475n/min, six sley bar looms adopt five sley bars to weave, one of them sley bar is the empty comb of GB4, so not only can improve loom speed, and can save cost, concrete histological structure be GB1:4-4-4-4/0-0-0-0/3-3-3-3/0-0-0-0//, GB2:0-1-1-1/1-0-0-0//, GB3:0-1-0-1/1-0-1-0//, GB4: empty comb, GB5:0-0-0-1/1-1-1-0//and GB6:0-0-4-4/4-4-0-0/0-0-3-3/3-3-0-0//, the mode that passes is 185g/m for completely wearing thereby obtain grammes per square metre
2With fabric width be 2m wait to cut open width of cloth grey cloth;
C) cut open the width of cloth, to by step B) resultingly wait to cut open width of cloth grey cloth and cut open the width of cloth, what obtain matte Mao Gaowei 5mm treats the pre-setting grey cloth;
D) pre-setting, to by step C) the resulting pre-setting grey cloth for the treatment of adopts five four segment type setting machines of U-828 of being produced by TaiWan, China Ligen Industry Co Ltd, 210 ℃ of control pre-setting temperature, cloth speed (grey cloth speed) 30m/min and control rotation speed of fan 1600n/min obtain the pre-setting grey cloth;
E) stamp, to by step D) resulting pre-setting grey cloth stamp, the prescription of the printing paste that stamp is used is the printing paste of every 100g or claims contained Red-1 200 g, disperse yellow 1g and disperse blue 0.4g in the stamp paste, all the other 97.6g are thickener, with printing machine required pattern is printed on the grey cloth, thickener described in this step preferably adopts by the Zhejiang Province dragon and wins the Luo Wang seed synthetic thickener that chemical industry Co., Ltd produces, and obtains pending calico;
F) post processing, to step e) resulting calico carries out post processing, specifically be to adopt the model of producing to evaporate grey cloth oven dry back earlier for the 130C cylinder steamer by Jiangsu Province, China Changzhou first Fabritex S.r.l., and after washing, in bathing, washing adds caustic soda 3g/L and sodium hydrosulfite 3g/L and insulation 25min during 75 ℃ of bath temperatures in when washing, insulation finishes the back and adds softener 2.5% successively by the fabric weight ratio, antistatic additive 0.5%, smooth agent 1%, leavening agent 2% and antiseptic 1.5%, make dipping 30min under the fabric normal temperature, oven dry then, bake out temperature is 172 ℃, cloth speed is 40m/min;
G) plucking is to by step F) the resulting calico back side preferably adopts the 36 roller napper pluckings 5 times that industry widely uses, and the rotating speed of the plucking cylinder of napper is 65n/min, and cloth speed is 18m/min, obtains treating the carding fabric;
H) carding, to by step G) treating of the obtaining model that the carding fabric causes that industry generally uses is produced by Lianyungang, Jiangsu Province hawk trip Fabritex S.r.l. is as the 24 roller combing machine for fur cardings of SME-485 type once, the swift rotating speed of combing machine for fur is 80n/min, cloth speed is 30m/min, then hair side is carried out bristle, the rotating speed of control bristle roller: left and right bristle roller is 15n/min respectively, obtains treating the cropping grey cloth;
I) back side cropping is to by step H) resultingly treat the shearing machine cropping of cropping grey cloth, the rotating speed of cropping roller and cloth speed are respectively 1000n/min and 15m/min, obtain the grey cloth of the back side through cropping;
J) ring baking, to by step I) the resulting back side is through a grey cloth ring baking of cropping (industry claims that the ring baking is for shaking), ring baking machine preferably adopts the model of being produced by grand the dyeing and finishing machinery Co., Ltd in Chinese Guangdong province Heshan City to shake the grain tube for the J8LX-300 type, ring baking temperature is 140 ℃, cloth speed is 15m/min, obtains treating back typing grey cloth;
K) back typing, will be again step J) the resulting back typing grey cloth for the treatment of delivers to the i.e. back typing of five four segment type setting machines of U-828 HEAT SETTING of being produced by tw Taiwan Ligen Industry Co Ltd, the temperature of setting machine is 180 ℃, cloth speed is 45m/min, the rotation speed of fan of setting machine is 800n/min, obtain dyed color for yellow, grammes per square metre is 185g/m
2With fabric width be 200cm and matte Mao Gaowei 5mm terylene coral fleece blanket fabrics.
Claims (10)
1, a kind of terylene coral fleece blanket fabrics, it is characterized in that comprising suede yarn tissue and bottom silk organization, it is the DTY terylene thread of 133dtex/192f, 111dtex/192f or 111dtex/144f that described suede yarn is organized used raw material, and the used raw material of described bottom silk organization is the FDY terylene thread of 75dtex/24f, wherein: DTY terylene thread shared mass percent in lining is 60-70%, and described FDY silk shared mass percent in lining is 40-30%.
2, a kind of processing method of terylene coral fleece blanket fabrics is characterized in that this method may further comprise the steps:
A) select materials, choose the raw material that is used to constitute suede yarn tissue and is used to constitute bottom silk organization respectively, obtain treating weaving raw material;
B) weave, will treat that weaving raw material is put to warp knitting machine and weaves, and control grey cloth grammes per square metre 150-250g/m2, obtain waiting to cut open width of cloth grey cloth;
C) cut open the width of cloth, grade is cutd open width of cloth grey cloth cuts open the width of cloth and control hair is high, obtain treating the pre-setting grey cloth;
D) pre-setting is treated pre-setting grey cloth pre-setting, and the rotation speed of fan of control pre-setting temperature, cloth speed and setting machine obtains the pre-setting grey cloth;
E) dyeing or stamp dye or stamp to the pre-setting grey cloth, obtain pending stained clot-h or calico;
F) post processing, to the stained clot-h post processing: in cold chamber by fabric weight than adding softener, antistatic additive, smooth agent, leavening agent and antiseptic, and control treatment temperature and time, clean after the processing, dehydration, oven dry then and control bake out temperature and cloth speed, obtain treating the plucking stained clot-h, to the calico post processing: earlier calico is dried, evaporate again, evaporate after washing, when washing, in water-bath, add caustic soda and sodium hydrosulfite and insulation, finish the back in insulation and add softener by the fabric weight ratio, antistatic additive, smooth agent, leavening agent and antiseptic carry out impregnation process at normal temperatures, oven dry then and adjusting bake out temperature and cloth speed obtain treating the plucking calico;
G) plucking is treated the plucking stained clot-h or is treated the back side plucking of plucking calico, and plucking drum rotation speed and the cloth speed and the plucking number of times of control napper obtain treating the carding fabric;
H) carding of carding fabric is treated in carding, and the rotating speed and the cloth speed of control combing machine for fur, to the hair side bristle after the carding, obtains treating the cropping grey cloth then;
I) back side cropping of cropping grey cloth is treated in back side cropping, and control cropping roller speed and cloth speed obtain the grey cloth of the back side through cropping;
J) ring baking, to the grey cloth ring baking of the back side through cropping, control loop baking temperature and time obtains treating back typing grey cloth;
K) back typing will be treated the typing of back typing grey cloth, and the rotating speed of control back setting temperature and control cloth speed and control blower fan obtains the finished product terylene coral fleece blanket fabrics.
3, the processing method of terylene coral fleece blanket fabrics according to claim 2, it is characterized in that steps A) described in the raw material of bottom silk organization be the DTY terylene thread of 133dtex/192f, 111dtex/192f or 111dtex/144f, the raw material of described bottom silk organization is the FDY terylene thread of 75dtex/24f, wherein, DTY silk shared mass percent in lining is 60-70%, and FDY silk shared mass percent in lining is 40-30%.
4, the processing method of terylene coral fleece blanket fabrics according to claim 2, it is characterized in that step B) described in warp knitting machine be woven as double rib warp loom and weave, the rotating speed of warp knitting machine is 450-480n/min, histological structure be GB1:4-4-4-4/0-0-0-0/3-3-3-3/0-0-0-0//, GB2:0-1-1-1/1-0-0-0//, GB3:0-1-0-1/1-0-1-0//, GB4: empty comb, GB5:0-0-0-1/1-1-1-0//and GB6:0-0-4-4/4-4-0-0/0-0-3-3/3-3-0-0//, the mode that passes is for completely wearing.
5, the processing method of terylene coral fleece blanket fabrics according to claim 2 is characterized in that step C) described in the control hair high be with the high 4-5mm of being controlled to be of hair.
6, the processing method of terylene coral fleece blanket fabrics according to claim 2 is characterized in that step D) described in the rotation speed of fan of control pre-setting temperature, cloth speed and setting machine be that the pre-setting temperature is controlled to be 200-210 ℃, the cloth speed control is made as 25-35m/min and rotation speed of fan is controlled to be 1400-1600n/min.
7, the processing method of terylene coral fleece blanket fabrics according to claim 2, it is characterized in that step e) described in the used dyestuff of dyeing be disperse dyes, the input amount of disperse dyes is the 0.001%-0.1% of fabric weight ratio, and before dropping into dyestuff in the dyeing container, in container, add earlier as the glacial acetic acid 0.5-0.8g/L of auxiliary agent and the pH4-6 of dye leveller 0.5-1g/L and adjusting dye bath, the dye bath heating rate is 1-2 ℃/min, insulation 30-60min is cooled to 60-80 ℃ then grey cloth is gone out dye vat when being warming up to 120-130 ℃; The prescription of the printing paste that described stamp is used is Red-1 200-1.5g, disperse yellow 1-1.5g and disperse blue 0.3-0.5g contained in the printing paste of every 100g, and all the other are thickener.
8, the processing method of terylene coral fleece blanket fabrics according to claim 2, it is characterized in that step F) described in softener be that 2-5%, antistatic additive are that 0.5-1.5%, smooth agent are that 0.5-1.5%, leavening agent are that 1-2% and antiseptic are 1-2%, described percentage is the percentage by fabric weight, described control treatment temperature and time are meant treatment temperature and time are controlled to be 80-120 ℃ and 20-30min respectively, and described control bake out temperature and cloth speed are that bake out temperature and cloth speed are controlled to be 160-180 ℃ and 25-40m/min respectively; The described caustic soda and sodium hydrosulfite and insulation of adding in water-bath is meant adding caustic soda 2.5-3.5g/L, sodium hydrosulfite 2.5-3.5g/L and in the time of 70-80 ℃ the insulation 25-35min, the addition of the described softener that adds by the fabric weight ratio after insulation finishes is 2-3%, antistatic additive is 0.4-0.6%, smooth agent is 0.5-1.5%, leavening agent is that 1.5-2.5% and antiseptic are 1-2%, the time of described impregnation process at normal temperatures is 30min, and described adjusting bake out temperature and cloth speed are that bake out temperature and cloth speed are adjusted to 170-175 ℃ respectively, 35-40m/min.
9, the processing method of terylene coral fleece blanket fabrics according to claim 2, it is characterized in that step G) described in the plucking number of times of back side plucking be 3-5 time, the rotating speed of the plucking cylinder of described control napper and cloth speed are that the rotating speed of plucking cylinder and cloth speed are controlled to be 65-75n/min, 18-28m/min respectively; The rotating speed of the control combing machine for fur step H) and cloth speed are that the rotating speed with the carding roller of combing machine for fur is controlled to be 60-80n/min, the cloth speed control is made as 20-30m/min, described hair side bristle is meant that the rotating speed with the bristle roller is controlled to be left bristle roller 9-15n/min, right bristle roller 9-15n/min.
10, the processing method of terylene coral fleece blanket fabrics according to claim 2 is characterized in that step I) described in control cropping roller speed and cloth speed be that speed with the cropping roller is controlled to be 1000-1200n/min, the cloth speed control is made as 15-25m/min; Step J) the control loop baking temperature and time described in is that ring baking temperature and ring baking time are controlled to be 100-140 ℃, 15-30min respectively; Step K) setting temperature is that the back setting temperature is controlled to be 175-180 ℃ after the control described in, and described control cloth speed is for to be made as 30-45m/min with the cloth speed control, and described control rotation speed of fan is that rotation speed of fan is controlled to be 600-800n/min.