CN101243198B - 用于电镀的具有优异的可加工性的钢板及其制造方法 - Google Patents
用于电镀的具有优异的可加工性的钢板及其制造方法 Download PDFInfo
- Publication number
- CN101243198B CN101243198B CN2006800305520A CN200680030552A CN101243198B CN 101243198 B CN101243198 B CN 101243198B CN 2006800305520 A CN2006800305520 A CN 2006800305520A CN 200680030552 A CN200680030552 A CN 200680030552A CN 101243198 B CN101243198 B CN 101243198B
- Authority
- CN
- China
- Prior art keywords
- steel plate
- steel
- rolling
- surface groups
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
- C21D8/0426—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
- C21D8/0473—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/004—Very low carbon steels, i.e. having a carbon content of less than 0,01%
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/008—Ferrous alloys, e.g. steel alloys containing tin
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0224—Two or more thermal pretreatments
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/004—Dispersions; Precipitations
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2005-0078433 | 2005-08-25 | ||
KR1020050078433A KR100711356B1 (ko) | 2005-08-25 | 2005-08-25 | 가공성이 우수한 아연도금용 강판 및 그 제조방법 |
KR1020050078433 | 2005-08-25 | ||
PCT/KR2006/003348 WO2007024114A1 (en) | 2005-08-25 | 2006-08-24 | Steel sheet for galvanizing with excellent workability, and method for manufacturing the same |
Publications (2)
Publication Number | Publication Date |
---|---|
CN101243198A CN101243198A (zh) | 2008-08-13 |
CN101243198B true CN101243198B (zh) | 2010-12-29 |
Family
ID=37771816
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN2006800305520A Expired - Fee Related CN101243198B (zh) | 2005-08-25 | 2006-08-24 | 用于电镀的具有优异的可加工性的钢板及其制造方法 |
Country Status (6)
Country | Link |
---|---|
US (1) | US20110073223A1 (ko) |
EP (1) | EP1929059A4 (ko) |
JP (1) | JP5388577B2 (ko) |
KR (1) | KR100711356B1 (ko) |
CN (1) | CN101243198B (ko) |
WO (1) | WO2007024114A1 (ko) |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN104264075B (zh) * | 2005-12-09 | 2018-01-30 | Posco公司 | 具有优异成形性和涂覆特性的高强度冷轧钢板,由其制成的锌基金属镀钢板及制造方法 |
KR100797238B1 (ko) * | 2006-12-26 | 2008-01-23 | 주식회사 포스코 | 가공성이 우수한 심가공용 박강판의 제조방법 |
WO2011068328A2 (ko) * | 2009-12-04 | 2011-06-09 | 주식회사 포스코 | 내열성이 우수한 가공용 냉연강판 및 그 제조방법 |
JP4998757B2 (ja) * | 2010-03-26 | 2012-08-15 | Jfeスチール株式会社 | 深絞り性に優れた高強度鋼板の製造方法 |
KR20120127095A (ko) * | 2011-05-13 | 2012-11-21 | 주식회사 포스코 | 표면특성이 우수한 고강도 고인성 선재 및 그 제조방법 |
GB2529174A (en) | 2014-08-12 | 2016-02-17 | Ibm | Batch compression management of messages |
US20210343458A1 (en) * | 2018-11-02 | 2021-11-04 | Nippon Steel Corporation | Non-oriented electrical steel sheet |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1322256A (zh) * | 1999-09-28 | 2001-11-14 | 日本钢管株式会社 | 高强度热轧钢板及其制造方法 |
JP2002146475A (ja) * | 2000-11-02 | 2002-05-22 | Kawasaki Steel Corp | 合金化溶融亜鉛めっき鋼板 |
CN1358878A (zh) * | 2000-11-27 | 2002-07-17 | 住友金属工业株式会社 | 超低碳钢板及其制造方法 |
Family Cites Families (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS62250126A (ja) * | 1986-04-23 | 1987-10-31 | Kawasaki Steel Corp | プレス成形性の優れた冷延鋼板の製造方法 |
JPS63243226A (ja) * | 1987-03-31 | 1988-10-11 | Kawasaki Steel Corp | 耐2次加工脆性に優れた超深絞り用冷延鋼板の製造方法 |
JP2576894B2 (ja) * | 1988-12-15 | 1997-01-29 | 日新製鋼株式会社 | プレス成形性に優れた溶融亜鉛めっき高張力冷延鋼板およびその製造方法 |
AU624992B2 (en) * | 1989-09-11 | 1992-06-25 | Kawasaki Steel Corporation | Cold-rolled steel sheet for deep drawings and method of producing the same |
JPH0441658A (ja) * | 1990-06-07 | 1992-02-12 | Nippon Steel Corp | 耐パウダリング性に優れた焼付硬化性高強度合金化溶融亜鉛めっき鋼板およびその製造方法 |
JPH0570838A (ja) * | 1991-09-13 | 1993-03-23 | Kawasaki Steel Corp | 深絞り用熱延鋼板の製造方法 |
JP2800541B2 (ja) * | 1992-02-21 | 1998-09-21 | 日本鋼管株式会社 | 深絞り用高強度溶融亜鉛メッキ鋼板の製造方法 |
JPH0657337A (ja) * | 1992-08-10 | 1994-03-01 | Nippon Steel Corp | 成形性に優れた高強度合金化溶融亜鉛めっき鋼板の製造方法 |
JP2980785B2 (ja) * | 1992-08-31 | 1999-11-22 | 新日本製鐵株式会社 | 焼付硬化性と成形性とに優れた冷延鋼板あるいは溶融亜鉛メッキ冷延鋼板およびそれらの製造方法 |
KR960013481B1 (ko) * | 1993-06-29 | 1996-10-05 | 니홍고오깡 가부시키가이샤 | 표면처리강판 및 그 제조방법 |
JP3229921B2 (ja) * | 1994-11-21 | 2001-11-19 | 川崎製鉄株式会社 | 耐孔あき性に優れる深絞り用の鋼板および表面処理鋼板 |
TW415967B (en) * | 1996-02-29 | 2000-12-21 | Kawasaki Steel Co | Steel, steel sheet having excellent workability and method of the same by electric furnace-vacuum degassing process |
EP0903419A4 (en) * | 1996-12-24 | 2000-03-22 | Kawasaki Steel Co | THIN STEEL SHEET WITH HIGH RECTANGULAR TUBE DRAWN CAPABILITY AND METHOD FOR PRODUCING THE SAME |
JPH10280092A (ja) * | 1997-04-10 | 1998-10-20 | Nippon Steel Corp | プレス成形性の時効劣化が小さい塗装焼付硬化性に優れた溶融亜鉛めっき鋼板とその製造方法 |
WO2000050658A1 (fr) * | 1999-02-22 | 2000-08-31 | Nippon Steel Corporation | Plaque d'acier galvanise a haute resistance, d'excellent comportement pour l'adhesion des placages de metal et la mise en forme sous presse, et plaque d'acier allie galvanise a haute resistance, et procede de production correspondant |
CA2330010C (en) * | 1999-02-25 | 2008-11-18 | Kawasaki Steel Corporation | Steel sheets, hot-dipped steel sheets and alloyed hot-dipped steel sheets as well as method of producing the same |
JP4356132B2 (ja) * | 1999-03-04 | 2009-11-04 | Jfeスチール株式会社 | 缶用鋼板用熱延母板およびその製造方法 |
JP4060997B2 (ja) | 1999-08-27 | 2008-03-12 | 新日本製鐵株式会社 | 曲げ性と深絞り性に優れた高強度冷延鋼板と高強度亜鉛めっき冷延鋼板およびその製造方法 |
JP4258918B2 (ja) * | 1999-11-01 | 2009-04-30 | Jfeスチール株式会社 | 無方向性電磁鋼板の製造方法 |
JP2001288550A (ja) * | 2000-01-31 | 2001-10-19 | Kobe Steel Ltd | 溶融亜鉛めっき鋼板 |
JP3958921B2 (ja) * | 2000-08-04 | 2007-08-15 | 新日本製鐵株式会社 | 塗装焼付硬化性能と耐常温時効性に優れた冷延鋼板及びその製造方法 |
JP4299451B2 (ja) | 2000-11-14 | 2009-07-22 | 新日本製鐵株式会社 | 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP2002155317A (ja) | 2000-11-16 | 2002-05-31 | Kawasaki Steel Corp | 深絞り性および耐2次加工脆性に優れた高強度溶融亜鉛めっき鋼板の製造方法 |
KR100478091B1 (ko) * | 2002-05-24 | 2005-03-24 | 주식회사 포스코 | 용융아연도금강판의 제조방법 |
JP2004256895A (ja) * | 2003-02-27 | 2004-09-16 | Jfe Steel Kk | 耐2次加工脆性に優れた高強度溶融亜鉛めっき鋼板の製造方法 |
-
2005
- 2005-08-25 KR KR1020050078433A patent/KR100711356B1/ko active IP Right Grant
-
2006
- 2006-08-24 JP JP2008527851A patent/JP5388577B2/ja not_active Expired - Fee Related
- 2006-08-24 EP EP06783735A patent/EP1929059A4/en not_active Withdrawn
- 2006-08-24 US US12/064,653 patent/US20110073223A1/en not_active Abandoned
- 2006-08-24 CN CN2006800305520A patent/CN101243198B/zh not_active Expired - Fee Related
- 2006-08-24 WO PCT/KR2006/003348 patent/WO2007024114A1/en active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1322256A (zh) * | 1999-09-28 | 2001-11-14 | 日本钢管株式会社 | 高强度热轧钢板及其制造方法 |
JP2002146475A (ja) * | 2000-11-02 | 2002-05-22 | Kawasaki Steel Corp | 合金化溶融亜鉛めっき鋼板 |
CN1358878A (zh) * | 2000-11-27 | 2002-07-17 | 住友金属工业株式会社 | 超低碳钢板及其制造方法 |
Also Published As
Publication number | Publication date |
---|---|
JP5388577B2 (ja) | 2014-01-15 |
WO2007024114A9 (en) | 2009-12-03 |
KR100711356B1 (ko) | 2007-04-27 |
EP1929059A4 (en) | 2012-06-13 |
EP1929059A1 (en) | 2008-06-11 |
KR20070023995A (ko) | 2007-03-02 |
JP2009506208A (ja) | 2009-02-12 |
WO2007024114A1 (en) | 2007-03-01 |
CN101243198A (zh) | 2008-08-13 |
US20110073223A1 (en) | 2011-03-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN109642294B (zh) | 钢板及其制造方法 | |
EP2128293B1 (en) | Low specific gravity and high strength steel sheets with excellent ridging resistance and manufacturing methods thereof | |
CN110114500B (zh) | 冲击特性优异的热压成型用镀覆钢板、热压成型部件及它们的制造方法 | |
EP2554699B1 (en) | Steel sheet with high tensile strength and superior ductility and method for producing same | |
JP4542515B2 (ja) | 成形性と溶接性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板、並びに、高強度冷延鋼板の製造方法、高強度溶融亜鉛めっき鋼板の製造方法、高強度合金化溶融亜鉛めっき鋼板の製造方法 | |
CN101243198B (zh) | 用于电镀的具有优异的可加工性的钢板及其制造方法 | |
JP2005139485A (ja) | 熱間成形加工用鋼板 | |
KR101461740B1 (ko) | 재질 및 두께 편차가 작고 내도금박리성이 우수한 열연강판 및 그 제조방법 | |
CN111684091B (zh) | 高强度冷轧钢板、高强度镀敷钢板以及它们的制造方法 | |
JP5126844B2 (ja) | 熱間プレス用鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法 | |
KR100733017B1 (ko) | 고강도 냉연강판 및 그 제조방법 | |
TW201315819A (zh) | 深擠壓性及鋼卷內材質均勻性優異之高強度冷軋鋼板及其製造方法 | |
CN101495661A (zh) | 具有优良机械性能和表面质量的高强度镀Zn钢板及其制造方法 | |
WO2017168948A1 (ja) | ホットプレス用鋼板およびその製造方法、ならびにホットプレス部材およびその製造方法 | |
TW200532032A (en) | High strength cold rolled steel sheet and method for manufacturing the same | |
JP5094888B2 (ja) | 延性に優れた高強度低比重鋼板の製造方法 | |
CN101460642A (zh) | 具有优良表面质量的镀Zn钢板及其制造方法 | |
JP4471688B2 (ja) | 延性に優れた高強度低比重鋼板およびその製造方法 | |
CN109154046B (zh) | 具有奥氏体基体的twip钢板 | |
CN108474084B (zh) | 加工性优异的热轧镀覆钢板及其制造方法 | |
JP7215518B2 (ja) | 熱間プレス部材およびその製造方法 | |
JP3921040B2 (ja) | 加工性の優れた高炭素鋼板の製造方法 | |
CN114207172B (zh) | 高强度钢板、高强度部件及其制造方法 | |
CN116507753A (zh) | 延展性优异的超高强度钢板及其制造方法 | |
JPH05247540A (ja) | 深絞り用高強度冷延鋼板およびその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
C06 | Publication | ||
PB01 | Publication | ||
C10 | Entry into substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
C14 | Grant of patent or utility model | ||
GR01 | Patent grant | ||
CF01 | Termination of patent right due to non-payment of annual fee | ||
CF01 | Termination of patent right due to non-payment of annual fee |
Granted publication date: 20101229 Termination date: 20200824 |