CN100363421C - 一种热固性丙烯酸乳液及其制备方法以及含有该乳液的涂料 - Google Patents
一种热固性丙烯酸乳液及其制备方法以及含有该乳液的涂料 Download PDFInfo
- Publication number
- CN100363421C CN100363421C CNB2005100331378A CN200510033137A CN100363421C CN 100363421 C CN100363421 C CN 100363421C CN B2005100331378 A CNB2005100331378 A CN B2005100331378A CN 200510033137 A CN200510033137 A CN 200510033137A CN 100363421 C CN100363421 C CN 100363421C
- Authority
- CN
- China
- Prior art keywords
- monomer
- emulsion
- acrylic
- consumption
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
编号 | 外观 | Tg(℃)计算值 | 冻融循环(次数) | 机械稳定性 | 储存稳定性 | 泡沫量 |
实施例1 | 微蓝乳液 | 15 | 3 | ○ | ○ | ◎ |
实施例2 | 微蓝乳液 | 40 | 2 | ○ | ○ | ◎ |
实施例3 | 微蓝乳液 | 30 | 3 | ○ | ○ | ◎ |
实施例4 | 微蓝乳液 | -15 | 3 | ◎ | ○ | ◎ |
实施例5 | 微蓝乳液 | 15 | 3 | ◎ | ○ | ◎ |
实施例6 | 蓝相乳液 | 0 | 3 | ○ | ◎ | ○ |
实施例7 | 蓝相乳液 | -10 | 3 | ○ | ◎ | ○ |
实施例8 | 蓝相乳液 | 20 | 2 | ◎ | ◎ | ○ |
实施例9 | 微蓝乳液 | 0 | 3 | ○ | ○ | ○ |
实施例10 | 微蓝乳液 | 0 | 3 | ○ | ◎ | ◎ |
实施例11 | 蓝相乳液 | -10 | 3 | ◎ | ◎ | ◎ |
对比例1 | 蓝相乳液 | 0 | 3 | ◎ | ◎ | × |
对比例2 | 蓝相乳液 | 5 | 3 | × | × | × |
对比例3 | 微蓝相乳液 | 50 | × | × | × | ○ |
对比例4 | 蓝相乳液 | -25 | 3 | ◎ | ◎ | × |
对比例5 | 蓝相乳液 | 15 | 3 | ◎ | ◎ | × |
实施例 | 低皂丙烯酸乳液 | 水性树脂 | 附着力促进剂 | 水性交联剂 | 催化剂 | 中和剂 | 助溶剂 | 水 |
实施例12 | 30(R01) | 10(A) | 0.5(E) | 6(H) | 0.2(L) | 0.1(O) | 14 | 39.2 |
实施例13 | 45(R02) | 2(C) | 1.0(G) | 9(I) | 0.3(L) | 0.2(P) | 13 | 31.0 |
实施例14 | 25(R03) | 20(B) | - | 15(J) | 0.2(M) | 0.1(O) | 10 | 27.9 |
实施例15 | 60(R04) | 1(D) | 2.0(F) | 7.5(H) | 0.3(M) | 0.2(P) | 12 | 18.0 |
实施例16 | 40(R05) | 2(B) | 2.0(F) | 12(J) | 0.3(L) | 0.2(O) | 6 | 37.8 |
实施例17 | 35(R06) | 2(A) | 1.0(E) | 12(H) | 0.2(M) | 0.1(P) | 14 | 35.7 |
实施例18 | 20(R07) | 15(A) | 0.5(G) | 6(H) | 0.2(M) | 0.1(P) | 15 | 43.2 |
实施例19 | 35(R08) | 10(C) | - | 10(J) | 0.3(L) | 0.2(P) | 10 | 33.8 |
实施例20 | 35(R09) | 5(D) | 1(F) | 10(I) | 0.3(N) | 0.1(O) | 15 | 34.6 |
实施例21 | 35(R10) | 10(B) | 2(G) | 55(K) | 0.3(N) | 0.2(Q) | 12 | 35.5 |
实施例22 | 50(R11) | 1(D) | 2(E) | 8(K) | 0.3(N) | 0.2(Q) | 13 | 25.5 |
对比例6 | 25(COR1) | 15(A) | 1(D) | 10(H) | 0.3(L) | 0.2(O) | 10 | 38.5 |
对比例7 | 35(COR2) | 10(B) | 2(E) | 5(J) | 0.3(L) | 0.1(P) | 15 | 35.4 |
对比例8 | 45(COR3) | 5(CC)) | 3(F) | 8(I) | 0.3(L) | 0.2(O) | 12 | 26.5 |
对比例9 | 45(COR4) | 0.5(D) | 2(E) | 15(J) | 0.3(L) | 0.2(O) | 13 | 22.5 |
对比例10 | 40(COR5) | 2(A) | 2(E) | 10(K) | 0.3(N) | 0.2(Q) | 14 | 30.5 |
实施例 | 底涂附着力 | 耐碱性 | 耐盐雾性 | 耐湿热性 | 耐水煮 | 面涂附着力 | 耐黄变性 | 后加工性 | 储存稳定性 |
实施例12 | ◎ | ◎ | ◎ | ◎ | ○ | ◎ | ◎ | ◎ | ○ |
实施例13 | ◎ | ○ | ◎ | ◎ | ○ | ◎ | ◎ | ◎ | ○ |
实施例14 | ◎ | ○ | △ | ○ | ◎ | ◎ | ◎ | ◎ | ○ |
实施例15 | ◎ | ◎ | ◎ | ◎ | ○ | ◎ | ◎ | ◎ | ○ |
实施例16 | ◎ | ○ | ○ | ○ | ○ | ◎ | ◎ | ◎ | ○ |
实施例17 | ◎ | ◎ | ○ | ○ | ○ | ○ | ○ | ◎ | ◎ |
实施例18 | ◎ | ○ | △ | △ | ○ | ○ | ○ | ◎ | ◎ |
实施例19 | ◎ | ○ | ○ | ◎ | ○ | ○ | ○ | ◎ | ◎ |
实施例20 | ◎ | ○ | ○ | ○ | ○ | ○ | ○ | ◎ | ○ |
实施例21 | ◎ | ○ | ◎ | ○ | ◎ | ◎ | ○ | ◎ | ◎ |
实施例22 | ◎ | ○ | ◎ | ○ | ◎ | ◎ | ○ | ◎ | ◎ |
对比例6 | ◎ | △ | × | × | △ | × | ○ | × | ◎ |
对比例7 | ○ | △ | △ | △ | △ | × | ○ | × | △ |
对比例8 | ○ | ○ | △ | △ | △ | × | ○ | × | × |
对比例9 | ◎ | ○ | × | △ | △ | △ | ○ | ○ | ◎ |
对比例10 | ○ | ◎ | ○ | △ | × | △ | ○ | ○ | ◎ |
Claims (17)