CA2905623A1 - High-strength plated steel plate for welded structural member, and method for producing the same - Google Patents

High-strength plated steel plate for welded structural member, and method for producing the same

Info

Publication number
CA2905623A1
CA2905623A1 CA2905623A CA2905623A CA2905623A1 CA 2905623 A1 CA2905623 A1 CA 2905623A1 CA 2905623 A CA2905623 A CA 2905623A CA 2905623 A CA2905623 A CA 2905623A CA 2905623 A1 CA2905623 A1 CA 2905623A1
Authority
CA
Canada
Prior art keywords
hot
phase
steel plate
base material
less
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
CA2905623A
Other languages
English (en)
French (fr)
Inventor
Kentaro Hirata
Yukio Katagiri
Shigeru Morikawa
Masaaki URANAKA
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Nisshin Co Ltd
Original Assignee
Nisshin Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nisshin Steel Co Ltd filed Critical Nisshin Steel Co Ltd
Publication of CA2905623A1 publication Critical patent/CA2905623A1/en
Abandoned legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
CA2905623A 2013-03-26 2014-03-13 High-strength plated steel plate for welded structural member, and method for producing the same Abandoned CA2905623A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2013064370A JP6049516B2 (ja) 2013-03-26 2013-03-26 溶接構造部材用高強度めっき鋼板およびその製造法
JP2013-064370 2013-03-26
PCT/JP2014/056620 WO2014156671A1 (ja) 2013-03-26 2014-03-13 溶接構造部材用高強度めっき鋼板およびその製造法

Publications (1)

Publication Number Publication Date
CA2905623A1 true CA2905623A1 (en) 2014-10-02

Family

ID=51623654

Family Applications (1)

Application Number Title Priority Date Filing Date
CA2905623A Abandoned CA2905623A1 (en) 2013-03-26 2014-03-13 High-strength plated steel plate for welded structural member, and method for producing the same

Country Status (10)

Country Link
US (2) US10100395B2 (enExample)
EP (1) EP2980237A4 (enExample)
JP (1) JP6049516B2 (enExample)
KR (1) KR102210135B1 (enExample)
CN (1) CN105121681B (enExample)
CA (1) CA2905623A1 (enExample)
MX (1) MX2015013538A (enExample)
MY (1) MY171301A (enExample)
TW (1) TWI618816B (enExample)
WO (1) WO2014156671A1 (enExample)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017115205A (ja) * 2015-12-24 2017-06-29 日新製鋼株式会社 めっき密着性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ合金めっき鋼板の製造方法
KR102075182B1 (ko) 2015-12-24 2020-02-10 주식회사 포스코 도금성이 우수한 고강도 용융 아연계 도금 강재 및 그 제조방법
JP2017145441A (ja) * 2016-02-16 2017-08-24 日新製鋼株式会社 黒色表面被覆高強度鋼板およびその製造方法
WO2017169939A1 (ja) * 2016-03-31 2017-10-05 Ｊｆｅスチール株式会社 薄鋼板およびめっき鋼板、並びに、熱延鋼板の製造方法、冷延フルハード鋼板の製造方法、熱処理板の製造方法、薄鋼板の製造方法およびめっき鋼板の製造方法
KR101858853B1 (ko) * 2016-12-19 2018-06-28 주식회사 포스코 용접성이 우수한 전봉강관용 열연강판 및 이의 제조방법
JP6816550B2 (ja) * 2017-02-17 2021-01-20 日本製鉄株式会社 曲げ加工性に優れた黒色表面被覆高強度溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板及びその製造方法
JP6809648B1 (ja) * 2019-01-29 2021-01-06 Ｊｆｅスチール株式会社 高強度鋼板及びその製造方法
JP7288184B2 (ja) * 2019-03-22 2023-06-07 日本製鉄株式会社 溶融Ｚｎ－Ａｌ－Ｍｇ系めっき鋼板の製造方法
JP7059979B2 (ja) * 2019-04-25 2022-04-26 Ｊｆｅスチール株式会社 スポット溶接部材
JP2021042419A (ja) * 2019-09-10 2021-03-18 日本電産株式会社 亜鉛合金及びその製造方法
US20230038535A1 (en) * 2019-12-18 2023-02-09 Arcelormittal Cold-rolled and annealed steel sheet and manufacturing method
JP7241889B2 (ja) * 2020-02-13 2023-03-17 日本製鉄株式会社 接合部品及びその製造方法
KR102451005B1 (ko) * 2020-10-23 2022-10-07 주식회사 포스코 열적 안정성이 우수한 고강도 강판 및 이의 제조방법
CN113388796B (zh) * 2021-08-16 2021-11-02 天津市新宇彩板有限公司 钢材表面热镀锌铝镁镀液及使用该镀液的镀覆方法
CN119013429A (zh) * 2022-03-24 2024-11-22 Jfe钢板株式会社 熔融Al-Zn类镀覆钢板及其制造方法
KR102818628B1 (ko) * 2023-01-18 2025-06-10 주식회사 포스코 가스 실드 아크 용접용 와이어
WO2024154855A1 (ko) * 2023-01-20 2024-07-25 주식회사 포스코 가스 실드 아크 용접 금속

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4085583B2 (ja) * 2001-02-27 2008-05-14 Ｊｆｅスチール株式会社 高強度冷延溶融亜鉛メッキ鋼板およびその製造方法
US6677058B1 (en) * 2002-07-31 2004-01-13 Nisshin Steel Co., Ltd. Hot-dip Zn plated steel sheet excellent in luster-retaining property and method of producing the same
JP2004315848A (ja) * 2003-02-27 2004-11-11 Nisshin Steel Co Ltd 溶融金属脆化による溶接加工割れのないＺｎ−Ａｌ−Ｍｇ系溶融めっき鋼板
JP2006307260A (ja) * 2005-04-27 2006-11-09 Toyo Kohan Co Ltd プラズマディスプレイ固定板用鋼板、プラズマディスプレイ固定用鋼板の製造方法及びプラズマディスプレイ固定板
JP4665692B2 (ja) * 2005-09-29 2011-04-06 Ｊｆｅスチール株式会社 曲げ剛性に優れた高強度薄鋼板およびその製造方法
JP4542515B2 (ja) 2006-03-01 2010-09-15 新日本製鐵株式会社 成形性と溶接性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板、並びに、高強度冷延鋼板の製造方法、高強度溶融亜鉛めっき鋼板の製造方法、高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5082432B2 (ja) * 2006-12-26 2012-11-28 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP4692519B2 (ja) * 2007-06-11 2011-06-01 Ｊｆｅスチール株式会社 高強度溶融亜鉛メッキ鋼板およびその製造方法
JP4377955B2 (ja) * 2007-12-27 2009-12-02 新日本製鐵株式会社 亜鉛めっき鋼板溶接用ステンレス鋼フラックス入り溶接ワイヤおよびこれを用いた亜鉛めっき鋼板のアーク溶接方法
JP5194841B2 (ja) * 2008-01-31 2013-05-08 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5264234B2 (ja) 2008-03-24 2013-08-14 日新製鋼株式会社 耐溶融金属脆化割れ性に優れたＺｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
JP5320798B2 (ja) * 2008-04-10 2013-10-23 新日鐵住金株式会社 時効性劣化が極めて少なく優れた焼付け硬化性を有する高強度鋼板とその製造方法
NZ594927A (en) * 2009-03-10 2013-01-25 Nisshin Steel Co Ltd Zinc-based alloy-plated steel material excellent in resistance to molten-metal embrittlement cracking
JP2010235989A (ja) * 2009-03-30 2010-10-21 Nisshin Steel Co Ltd 耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
JP5720208B2 (ja) * 2009-11-30 2015-05-20 新日鐵住金株式会社 高強度冷延鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板
JP5641741B2 (ja) * 2010-01-28 2014-12-17 日新製鋼株式会社 曲げ性および耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板
EP2610357B1 (en) * 2010-08-23 2019-12-18 Nippon Steel Corporation Cold-rolled steel sheet and process for production thereof
EP2682495B1 (en) * 2011-02-28 2019-01-02 Nisshin Steel Co., Ltd. STEEL SHEET HOT-DIP-COATED WITH Zn-Al-Mg-BASED SYSTEM, AND PROCESS OF MANUFACTURING SAME

Also Published As

Publication number Publication date
JP2014189812A (ja) 2014-10-06
US10100395B2 (en) 2018-10-16
MY171301A (en) 2019-10-08
CN105121681B (zh) 2017-04-26
KR102210135B1 (ko) 2021-02-01
KR20150133838A (ko) 2015-11-30
JP6049516B2 (ja) 2016-12-21
US20190010596A1 (en) 2019-01-10
CN105121681A (zh) 2015-12-02
MX2015013538A (es) 2016-02-05
EP2980237A4 (en) 2016-11-30
TW201443280A (zh) 2014-11-16
US20160032438A1 (en) 2016-02-04
EP2980237A1 (en) 2016-02-03
WO2014156671A1 (ja) 2014-10-02
TWI618816B (zh) 2018-03-21

Similar Documents

Publication Publication Date Title
US10100395B2 (en) High-strength plated steel plate for welded structural member, and method for producing the same
US8657969B2 (en) High-strength galvanized steel sheet with excellent formability and method for manufacturing the same
JP5403185B2 (ja) 引張強度９８０ＭＰａ以上有するめっき密着性、成形性と穴広げ性に優れた高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板とその製造方法
KR101813974B1 (ko) 고강도 용융 아연 도금 강판 및 그의 제조 방법
KR102331003B1 (ko) 용융 아연 도금 강판
JP7139361B2 (ja) 改善された延性を備えた高強度鋼製部品の製造方法、及び前記方法により得られた部品
CA2786381C (en) High-strength galvanized steel sheet having excellent formability and spot weldability and method for manufacturing the same
EP2589677A1 (en) High-strength hot-dip galvanized steel sheet with excellent processability and process for producing same
JP5741456B2 (ja) 合金化溶融亜鉛めっき鋼板およびその製造方法
JPWO2019106894A1 (ja) 高強度亜鉛めっき鋼板およびその製造方法
KR20190023093A (ko) 고강도 박강판 및 그 제조 방법
KR20190022769A (ko) 박강판 및 그의 제조 방법
JP5867278B2 (ja) 常中温域での成形性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP2014019928A (ja) 高強度冷延鋼板および高強度冷延鋼板の製造方法
KR20190026868A (ko) 박강판 및 그의 제조 방법
JP6384623B2 (ja) 高強度鋼板およびその製造方法
JP7311808B2 (ja) 鋼板及びその製造方法
JP2010235989A (ja) 耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
WO2006109522A1 (ja) 溶融亜鉛めっき鋼板、および合金化溶融亜鉛めっき鋼板
JP7677538B2 (ja) 鋼板、抵抗スポット溶接方法、抵抗スポット溶接部材、および鋼板の製造方法
JP3464611B2 (ja) 成形性と耐食性に優れた高強度溶融亜鉛メッキ熱延鋼板及びその製造方法
JP7659207B2 (ja) 鋼板及び溶接継手
RU2829770C1 (ru) Холоднокатаный и термообработанный стальной лист и способ его изготовления
WO2025115291A1 (ja) 鋼板、抵抗スポット溶接方法、抵抗スポット溶接部材、および鋼板の製造方法

Legal Events

Date Code Title Description
EEER Examination request

Effective date: 20181221

FZDE Discontinued

Effective date: 20220325

FZDE Discontinued

Effective date: 20220325