BR112017000005A2 - método para produzir uma chapa de aço revestida e chapa de aço revestida - Google Patents

método para produzir uma chapa de aço revestida e chapa de aço revestida

Info

Publication number
BR112017000005A2
BR112017000005A2 BR112017000005A BR112017000005A BR112017000005A2 BR 112017000005 A2 BR112017000005 A2 BR 112017000005A2 BR 112017000005 A BR112017000005 A BR 112017000005A BR 112017000005 A BR112017000005 A BR 112017000005A BR 112017000005 A2 BR112017000005 A2 BR 112017000005A2
Authority
BR
Brazil
Prior art keywords
steel sheet
coated steel
temperature
producing
martensite
Prior art date
Application number
BR112017000005A
Other languages
English (en)
Other versions
BR112017000005B1 (pt
Inventor
Fan Dongwei
Jo Jun Hyun
Ranjan MOHANTY Rashmi
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=52000882&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=BR112017000005(A2) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of BR112017000005A2 publication Critical patent/BR112017000005A2/pt
Publication of BR112017000005B1 publication Critical patent/BR112017000005B1/pt

Abstract

trata-se de um método para produzir uma chapa de aço revestida de elevada resistência que tem um limite de elasticidade ys > 800 mpa, uma resistência à tração ts > 1.180 mpa, e conformação e ductilidade melhoradas. o aço contém: 15% = c = 0,25%, 1,2% = si = 1,8%, 2% = mn = 2,4%, 0,1% = cr = 0,25%, al = 0,5%, sendo que o restante é fe e impurezas inevitáveis. a chapa é recozida a uma temperatura mais elevada que ac3 e menor que 1.000 °c por um tempo de mais de 30 s, depois, bruscamente arrefecida, resfriando-se a mesma a uma temperatura de resfriamento qt entre 250 °c e 350 °c, para obter uma estrutura que consiste em pelo menos 60% de martensita e um teor de austenita suficiente de modo que a estrutura final contenha 3% a 15% de austenita residual e 85% a 97% de martensita e bainita sem ferrita, depois, aquecida a uma temperatura de divisão pt entre 430 °c e 480 °c e mantida nessa temperatura durante um tempo de divisão pt entre 10 s e 90 s, em seguida, revestida e resfriada por imersão a quente à temperatura ambiente.
BR112017000005-9A 2014-07-03 2015-07-03 Método para produzir uma chapa de aço revestida e chapa de aço revestida BR112017000005B1 (pt)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
IBPCT/IB2014/002275 2014-07-03
PCT/IB2014/002275 WO2016001702A1 (en) 2014-07-03 2014-07-03 Method for producing a high strength coated steel sheet having improved strength, ductility and formability
PCT/IB2015/055039 WO2016001895A2 (en) 2014-07-03 2015-07-03 Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Publications (2)

Publication Number Publication Date
BR112017000005A2 true BR112017000005A2 (pt) 2017-11-07
BR112017000005B1 BR112017000005B1 (pt) 2021-04-13

Family

ID=52000882

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112017000005-9A BR112017000005B1 (pt) 2014-07-03 2015-07-03 Método para produzir uma chapa de aço revestida e chapa de aço revestida

Country Status (15)

Country Link
US (2) US20170152579A1 (pt)
EP (2) EP3831965A1 (pt)
JP (2) JP6623183B2 (pt)
KR (1) KR102455942B1 (pt)
CN (1) CN106471139B (pt)
BR (1) BR112017000005B1 (pt)
CA (1) CA2954146C (pt)
ES (1) ES2855500T3 (pt)
HU (1) HUE054278T2 (pt)
MA (2) MA53357A (pt)
MX (1) MX2016017399A (pt)
PL (1) PL3164522T3 (pt)
RU (1) RU2686729C2 (pt)
UA (1) UA118792C2 (pt)
WO (2) WO2016001702A1 (pt)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016001702A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel sheet having improved strength, ductility and formability
WO2016001706A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
WO2016001700A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength, ductility and formability
WO2016001710A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel having improved strength and ductility and obtained sheet
WO2018115933A1 (en) * 2016-12-21 2018-06-28 Arcelormittal High-strength cold rolled steel sheet having high formability and a method of manufacturing thereof
WO2018115936A1 (en) * 2016-12-21 2018-06-28 Arcelormittal Tempered and coated steel sheet having excellent formability and a method of manufacturing the same
WO2018115935A1 (en) * 2016-12-21 2018-06-28 Arcelormittal Tempered and coated steel sheet having excellent formability and a method of manufacturing the same
WO2019122963A1 (en) 2017-12-19 2019-06-27 Arcelormittal Cold rolled and heat treated steel sheet and a method of manufacturing thereof
CN110180957B (zh) * 2018-06-28 2020-11-03 镕凝精工新材料科技(上海)有限公司 一种镀锌钢板的热处理方法及热冲压工艺
CA3149331A1 (en) * 2019-08-07 2021-02-11 United States Steel Corporation High ductility zinc-coated steel sheet products
KR102321285B1 (ko) * 2019-12-18 2021-11-03 주식회사 포스코 가공성이 우수한 고강도 강판 및 그 제조방법
WO2022242859A1 (en) * 2021-05-20 2022-11-24 Nlmk Clabecq Method for manufacturing a high strength steel plate and high strength steel plate
JP2023054990A (ja) 2021-10-05 2023-04-17 国立大学法人京都大学 面発光レーザ素子

Family Cites Families (51)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB243069A (en) 1924-08-21 1925-11-23 Robert Benson North Improvements in and connected with magneto electric machines
US4159218A (en) 1978-08-07 1979-06-26 National Steel Corporation Method for producing a dual-phase ferrite-martensite steel strip
TW387832B (en) * 1997-06-20 2000-04-21 Exxon Production Research Co Welding methods for producing ultra-high strength weldments with weld metalshaving excellent cryogenic temperature practure toughness
BR9811051A (pt) * 1997-07-28 2000-08-15 Exxonmobil Upstream Res Co Placa de aço, e, processo para preparar a mesma
JP4608822B2 (ja) 2001-07-03 2011-01-12 Ｊｆｅスチール株式会社 プレス成形性と歪時効硬化特性に優れた高延性溶融亜鉛めっき鋼板およびその製造方法
US6746548B2 (en) 2001-12-14 2004-06-08 Mmfx Technologies Corporation Triple-phase nano-composite steels
WO2004022794A1 (en) * 2002-09-04 2004-03-18 Colorado School Of Mines Method for producing steel with retained austenite
KR100884104B1 (ko) 2004-01-14 2009-02-19 신닛뽄세이테쯔 카부시키카이샤 도금 밀착성 및 구멍 확장성이 우수한 용융 아연 도금 고강도 강판과 그 제조 방법
JP4510488B2 (ja) 2004-03-11 2010-07-21 新日本製鐵株式会社 成形性および穴拡げ性に優れた溶融亜鉛めっき複合高強度鋼板およびその製造方法
JP4367300B2 (ja) 2004-09-14 2009-11-18 Ｊｆｅスチール株式会社 延性および化成処理性に優れる高強度冷延鋼板およびその製造方法
JP4716358B2 (ja) * 2005-03-30 2011-07-06 株式会社神戸製鋼所 強度と加工性のバランスに優れた高強度冷延鋼板およびめっき鋼板
KR100992225B1 (ko) * 2005-12-06 2010-11-05 가부시키가이샤 고베 세이코쇼 내파우더링성이 우수한 고강도 합금화 용융 아연 도금 강판및 그 제조 방법
CN101351570B (zh) * 2005-12-28 2013-01-30 株式会社神户制钢所 超高强度薄钢板
JP4174592B2 (ja) * 2005-12-28 2008-11-05 株式会社神戸製鋼所 超高強度薄鋼板
EP1832667A1 (fr) 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP4974341B2 (ja) * 2006-06-05 2012-07-11 株式会社神戸製鋼所 成形性、スポット溶接性、および耐遅れ破壊性に優れた高強度複合組織鋼板
JP4291860B2 (ja) 2006-07-14 2009-07-08 株式会社神戸製鋼所 高強度鋼板およびその製造方法
JP4411326B2 (ja) * 2007-01-29 2010-02-10 株式会社神戸製鋼所 リン酸塩処理性に優れた高強度合金化溶融亜鉛めっき鋼板
EP1990431A1 (fr) 2007-05-11 2008-11-12 ArcelorMittal France Procédé de fabrication de tôles d'acier laminées à froid et recuites à très haute résistance, et tôles ainsi produites
EP2020451A1 (fr) 2007-07-19 2009-02-04 ArcelorMittal France Procédé de fabrication de tôles d'acier à hautes caractéristiques de résistance et de ductilité, et tôles ainsi produites
PL2028282T3 (pl) 2007-08-15 2012-11-30 Thyssenkrupp Steel Europe Ag Stal dwufazowa, płaski wyrób wytworzony ze stali dwufazowej i sposób wytwarzania płaskiego wyrobu
EP2031081B1 (de) * 2007-08-15 2011-07-13 ThyssenKrupp Steel Europe AG Dualphasenstahl, Flachprodukt aus einem solchen Dualphasenstahl und Verfahren zur Herstellung eines Flachprodukts
MX2010002581A (es) 2007-09-10 2010-04-30 Pertti J Sippola Metodo y aparato para la conformabilidad mejorada de acero galvanizado con resistencia a la traccion mejorada.
CN101821419B (zh) 2007-10-25 2015-03-18 杰富意钢铁株式会社 加工性优良的高强度热镀锌钢板及其制造方法
KR101018131B1 (ko) 2007-11-22 2011-02-25 주식회사 포스코 저온인성이 우수한 고강도 저항복비 건설용 강재 및 그제조방법
JP2009173959A (ja) * 2008-01-21 2009-08-06 Nakayama Steel Works Ltd 高強度鋼板およびその製造方法
CN101225499B (zh) * 2008-01-31 2010-04-21 上海交通大学 低合金超高强度复相钢及其热处理方法
JP5402007B2 (ja) * 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5418047B2 (ja) 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5315956B2 (ja) * 2008-11-28 2013-10-16 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5412182B2 (ja) 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5807368B2 (ja) 2010-06-16 2015-11-10 新日鐵住金株式会社 圧延方向に対して４５°の方向の均一伸びが極めて高い高強度冷延鋼板及びその製造方法
JP5136609B2 (ja) * 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5126326B2 (ja) * 2010-09-17 2013-01-23 Ｊｆｅスチール株式会社 耐疲労特性に優れた高強度熱延鋼板およびその製造方法
ES2535420T3 (es) * 2011-03-07 2015-05-11 Tata Steel Nederland Technology B.V. Proceso para producir acero conformable de alta resistencia y acero conformable de alta resistencia producido con el mismo
JP5821260B2 (ja) 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
UA112771C2 (uk) * 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
EP2524970A1 (de) * 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Hochfestes Stahlflachprodukt und Verfahren zu dessen Herstellung
JP2012240095A (ja) * 2011-05-20 2012-12-10 Kobe Steel Ltd 高強度鋼板の温間成形方法
JP5824283B2 (ja) 2011-08-17 2015-11-25 株式会社神戸製鋼所 室温および温間での成形性に優れた高強度鋼板
JP5834717B2 (ja) * 2011-09-29 2015-12-24 Ｊｆｅスチール株式会社 高降伏比を有する溶融亜鉛めっき鋼板およびその製造方法
JP5632904B2 (ja) * 2012-03-29 2014-11-26 株式会社神戸製鋼所 加工性に優れた高強度冷延鋼板の製造方法
JP2013237923A (ja) 2012-04-20 2013-11-28 Jfe Steel Corp 高強度鋼板およびその製造方法
JP2014019928A (ja) 2012-07-20 2014-02-03 Jfe Steel Corp 高強度冷延鋼板および高強度冷延鋼板の製造方法
KR20150029736A (ko) 2012-07-31 2015-03-18 제이에프이 스틸 가부시키가이샤 성형성 및 형상 동결성이 우수한 고강도 용융 아연 도금 강판, 그리고 그의 제조 방법
JP5857909B2 (ja) 2012-08-09 2016-02-10 新日鐵住金株式会社 鋼板およびその製造方法
WO2016001700A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength, ductility and formability
WO2016001702A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel sheet having improved strength, ductility and formability
WO2016001706A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
WO2016001710A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel having improved strength and ductility and obtained sheet
US9802074B2 (en) 2014-07-18 2017-10-31 Landscape Structures Inc. Outdoor fitness resistance mechanism and housing

Also Published As

Publication number Publication date
UA118792C2 (uk) 2019-03-11
CN106471139A (zh) 2017-03-01
RU2016151385A (ru) 2018-06-26
WO2016001895A3 (en) 2016-03-17
CA2954146A1 (en) 2016-01-07
ES2855500T3 (es) 2021-09-23
JP2017527690A (ja) 2017-09-21
EP3164522A2 (en) 2017-05-10
EP3164522B1 (en) 2021-03-03
HUE054278T2 (hu) 2021-08-30
US20200347477A1 (en) 2020-11-05
RU2686729C2 (ru) 2019-04-30
MA40196A (fr) 2017-05-10
EP3831965A1 (en) 2021-06-09
KR20170028328A (ko) 2017-03-13
RU2016151385A3 (pt) 2018-12-06
JP2020045573A (ja) 2020-03-26
KR102455942B1 (ko) 2022-10-17
BR112017000005B1 (pt) 2021-04-13
JP6623183B2 (ja) 2019-12-18
PL3164522T3 (pl) 2021-09-06
WO2016001895A2 (en) 2016-01-07
CA2954146C (en) 2022-07-12
JP6823148B2 (ja) 2021-01-27
MA53357A (fr) 2021-06-09
MX2016017399A (es) 2017-05-01
US11492676B2 (en) 2022-11-08
WO2016001702A1 (en) 2016-01-07
CN106471139B (zh) 2018-08-31
MA40196B1 (fr) 2021-03-31
US20170152579A1 (en) 2017-06-01

Similar Documents

Publication Publication Date Title
BR112017000005A2 (pt) método para produzir uma chapa de aço revestida e chapa de aço revestida
BR112017000007A2 (pt) "método para produzir uma chapa de aço de alta resistência e chapa de aço"
BR112017000023A2 (pt) ?método para produzir uma lâmina de aço revestida e lâmina de aço revestida?
BR112016030065A2 (pt) método para produzir uma folha de aço e folha de aço
BR112017000021A2 (pt) método para fabricar uma folha de aço e folha de aço
BR112017000019A2 (pt) "método para produzir uma folha de aço laminada a frio e folha de aço"
BR112017002189A2 (pt) método para produzir uma folha de aço, folha de aço e uso de uma folha de aço
BR112017000027A2 (pt) método para manufaturar uma chapa de aço de alta resistência e chapa de aço
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX2018007649A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tenga ductilidad y conformabilidad mejorada, y lamina de acero recubierta obtenida.
BR112016012424A2 (pt) Folha de aço martensítico, diretamente obtida após laminação a frio, recozimento e resfriamento e método para produzir uma folha de aço martensítico laminada a frio e recozida
BR112019003791A2 (pt) chapa de aço laminada a frio e tratada termicamente, junta soldada por pontos de resistência, método para a fabricação de uma chapa de aço laminada a frio e tratada termicamente e processo para a produção de uma junta soldada por pontos de resistência
BR112017010093A2 (pt) ?método para fabricar um produto de aço e produto de aço?
MX2020004787A (es) Hoja de acero tratada termicamente laminada en frio y un metodo de fabricacion de la misma.
BR112016029457A2 (pt) ?método para produzir uma chapa de aço revestida com alta resistência e chapa de aço revestida?
BR112017000008A2 (pt) método de fabricação de uma folha de aço e folha de aço e folha de aço
BR112017000026A2 (pt) ?método para fabricar uma chapa de aço e chapa de aço?
AU2015205937B2 (en) Pearlitic steel rail with high strength and toughness and producing method thereof
MX2015015332A (es) Acero de alta resistencia que exhibe buena ductilidad y metodo de produccion via temple y tratamiento de particion mediante baño de zinc.
GB2548049A (en) Hot rolled light-gauge martensitic steel sheet and method for making the same
BR112017003147A2 (pt) aço de baixa liga e alta resistência laminado a frio
BR112018013051A2 (pt) método para produzir uma chapa de aço recozida após galvanização e uma chapa de aço recozida após galvanização
BR112018012131A2 (pt) método para produzir uma chapa de aço e chapa de aço
BR112018012422A2 (pt) método para produzir uma folha de aço, processo para a produção de um componente, folha de aço, estrutura soldada que compreende pelo menos dez soldas por pontos de resistência de pelo menos dois componentes, utilização de uma folha de aço e utilização de uma soldagem por pontos de resistência
BR112018012133A2 (pt) método para produzir uma chapa de aço, processo para produzir uma solda por ponto de resistência, chapa de aço, estrutura soldada, uso de uma chapa de aço e uso de uma solda por ponto de resistência

Legal Events

Date Code Title Description
B06U Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 03/07/2015, OBSERVADAS AS CONDICOES LEGAIS.