ZA200703345B - Method for the hot-dip coating of iron-carbon-manganese steel strip in a zinc bath - Google Patents
Method for the hot-dip coating of iron-carbon-manganese steel strip in a zinc bath Download PDFInfo
- Publication number
- ZA200703345B ZA200703345B ZA200703345A ZA200703345A ZA200703345B ZA 200703345 B ZA200703345 B ZA 200703345B ZA 200703345 A ZA200703345 A ZA 200703345A ZA 200703345 A ZA200703345 A ZA 200703345A ZA 200703345 B ZA200703345 B ZA 200703345B
- Authority
- ZA
- South Africa
- Prior art keywords
- iron
- manganese
- strip
- zinc
- layer
- Prior art date
Links
- 239000011701 zinc Substances 0.000 title claims description 72
- 229910052725 zinc Inorganic materials 0.000 title claims description 69
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 title claims description 68
- 238000000034 method Methods 0.000 title claims description 29
- LAUCTMALVHLLAL-UHFFFAOYSA-N [Mn].[C].[Fe] Chemical compound [Mn].[C].[Fe] LAUCTMALVHLLAL-UHFFFAOYSA-N 0.000 title claims description 25
- 238000003618 dip coating Methods 0.000 title claims description 8
- 229910000617 Mangalloy Inorganic materials 0.000 title description 7
- 229910000831 Steel Inorganic materials 0.000 claims description 74
- 239000010959 steel Substances 0.000 claims description 74
- 239000010410 layer Substances 0.000 claims description 69
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims description 53
- 229910052782 aluminium Inorganic materials 0.000 claims description 50
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims description 44
- 239000011248 coating agent Substances 0.000 claims description 41
- 238000000576 coating method Methods 0.000 claims description 41
- AMWRITDGCCNYAT-UHFFFAOYSA-L hydroxy(oxo)manganese;manganese Chemical compound [Mn].O[Mn]=O.O[Mn]=O AMWRITDGCCNYAT-UHFFFAOYSA-L 0.000 claims description 36
- 239000011572 manganese Substances 0.000 claims description 36
- 229910052748 manganese Inorganic materials 0.000 claims description 30
- 238000010438 heat treatment Methods 0.000 claims description 28
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 claims description 26
- 229910001297 Zn alloy Inorganic materials 0.000 claims description 16
- 239000007789 gas Substances 0.000 claims description 16
- 229910052742 iron Inorganic materials 0.000 claims description 16
- 239000007788 liquid Substances 0.000 claims description 16
- LNRYQGINUXUWLV-UHFFFAOYSA-N [Mn].[Fe].[Zn] Chemical compound [Mn].[Fe].[Zn] LNRYQGINUXUWLV-UHFFFAOYSA-N 0.000 claims description 15
- 229910052757 nitrogen Inorganic materials 0.000 claims description 15
- 238000001816 cooling Methods 0.000 claims description 13
- 229910052739 hydrogen Inorganic materials 0.000 claims description 13
- 239000001257 hydrogen Substances 0.000 claims description 13
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 claims description 12
- 239000000203 mixture Substances 0.000 claims description 12
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 claims description 11
- 229910052710 silicon Inorganic materials 0.000 claims description 9
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims description 8
- 229910052799 carbon Inorganic materials 0.000 claims description 8
- 238000007654 immersion Methods 0.000 claims description 7
- 229910052802 copper Inorganic materials 0.000 claims description 6
- 229910052759 nickel Inorganic materials 0.000 claims description 6
- 229910052719 titanium Inorganic materials 0.000 claims description 5
- 229910052720 vanadium Inorganic materials 0.000 claims description 5
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 claims description 4
- 239000012535 impurity Substances 0.000 claims description 4
- 229910052750 molybdenum Inorganic materials 0.000 claims description 4
- 229910052758 niobium Inorganic materials 0.000 claims description 4
- 229910052698 phosphorus Inorganic materials 0.000 claims description 4
- 239000010703 silicon Substances 0.000 claims description 4
- 239000000126 substance Substances 0.000 claims description 4
- 229910052717 sulfur Inorganic materials 0.000 claims description 4
- 239000002344 surface layer Substances 0.000 claims description 4
- 238000003723 Smelting Methods 0.000 claims description 3
- DALUDRGQOYMVLD-UHFFFAOYSA-N iron manganese Chemical compound [Mn].[Fe] DALUDRGQOYMVLD-UHFFFAOYSA-N 0.000 claims description 3
- 229910045601 alloy Inorganic materials 0.000 claims description 2
- 239000000956 alloy Substances 0.000 claims description 2
- 238000000137 annealing Methods 0.000 description 18
- 239000012071 phase Substances 0.000 description 17
- 238000001953 recrystallisation Methods 0.000 description 15
- PXHVJJICTQNCMI-UHFFFAOYSA-N nickel Substances [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 7
- 229910052760 oxygen Inorganic materials 0.000 description 6
- 238000001556 precipitation Methods 0.000 description 6
- 229910000975 Carbon steel Inorganic materials 0.000 description 5
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 5
- 230000015572 biosynthetic process Effects 0.000 description 5
- 239000001301 oxygen Substances 0.000 description 5
- 239000010949 copper Substances 0.000 description 4
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 3
- 239000002390 adhesive tape Substances 0.000 description 3
- 239000010962 carbon steel Substances 0.000 description 3
- 239000011651 chromium Substances 0.000 description 3
- 238000005097 cold rolling Methods 0.000 description 3
- 230000007547 defect Effects 0.000 description 3
- 238000005098 hot rolling Methods 0.000 description 3
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N iron oxide Inorganic materials [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 description 3
- 239000010955 niobium Substances 0.000 description 3
- 230000003647 oxidation Effects 0.000 description 3
- 238000007254 oxidation reaction Methods 0.000 description 3
- 239000010936 titanium Substances 0.000 description 3
- 150000003751 zinc Chemical class 0.000 description 3
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 2
- 229910015372 FeAl Inorganic materials 0.000 description 2
- 238000005275 alloying Methods 0.000 description 2
- 229910052804 chromium Inorganic materials 0.000 description 2
- 230000007797 corrosion Effects 0.000 description 2
- 238000005260 corrosion Methods 0.000 description 2
- 239000013078 crystal Substances 0.000 description 2
- 230000002349 favourable effect Effects 0.000 description 2
- 235000013980 iron oxide Nutrition 0.000 description 2
- 230000005012 migration Effects 0.000 description 2
- 238000013508 migration Methods 0.000 description 2
- 230000009467 reduction Effects 0.000 description 2
- 238000001878 scanning electron micrograph Methods 0.000 description 2
- 238000009736 wetting Methods 0.000 description 2
- 229910000885 Dual-phase steel Inorganic materials 0.000 description 1
- 229910016583 MnAl Inorganic materials 0.000 description 1
- ZOKXTWBITQBERF-UHFFFAOYSA-N Molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 description 1
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 description 1
- NINIDFKCEFEMDL-UHFFFAOYSA-N Sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 description 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 1
- 239000000853 adhesive Substances 0.000 description 1
- 230000001070 adhesive effect Effects 0.000 description 1
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 1
- -1 aluminum nitrides Chemical class 0.000 description 1
- 229910001566 austenite Inorganic materials 0.000 description 1
- 230000004888 barrier function Effects 0.000 description 1
- 239000003795 chemical substances by application Substances 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 230000007423 decrease Effects 0.000 description 1
- 230000002939 deleterious effect Effects 0.000 description 1
- 230000000694 effects Effects 0.000 description 1
- 238000004070 electrodeposition Methods 0.000 description 1
- 238000001704 evaporation Methods 0.000 description 1
- 230000008020 evaporation Effects 0.000 description 1
- 229910052909 inorganic silicate Inorganic materials 0.000 description 1
- VBMVTYDPPZVILR-UHFFFAOYSA-N iron(2+);oxygen(2-) Chemical class [O-2].[Fe+2] VBMVTYDPPZVILR-UHFFFAOYSA-N 0.000 description 1
- WJZHMLNIAZSFDO-UHFFFAOYSA-N manganese zinc Chemical compound [Mn].[Zn] WJZHMLNIAZSFDO-UHFFFAOYSA-N 0.000 description 1
- 238000004519 manufacturing process Methods 0.000 description 1
- 229910000734 martensite Inorganic materials 0.000 description 1
- 229910052751 metal Inorganic materials 0.000 description 1
- 239000002184 metal Substances 0.000 description 1
- 150000001247 metal acetylides Chemical class 0.000 description 1
- 239000011733 molybdenum Substances 0.000 description 1
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium atom Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 description 1
- 239000003973 paint Substances 0.000 description 1
- 239000011574 phosphorus Substances 0.000 description 1
- 239000002244 precipitate Substances 0.000 description 1
- 239000007790 solid phase Substances 0.000 description 1
- 239000006104 solid solution Substances 0.000 description 1
- 238000007711 solidification Methods 0.000 description 1
- 230000008023 solidification Effects 0.000 description 1
- 230000000087 stabilizing effect Effects 0.000 description 1
- 239000011593 sulfur Substances 0.000 description 1
- 230000009466 transformation Effects 0.000 description 1
- 238000001771 vacuum deposition Methods 0.000 description 1
- GPPXJZIENCGNKB-UHFFFAOYSA-N vanadium Chemical compound [V]#[V] GPPXJZIENCGNKB-UHFFFAOYSA-N 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0224—Two or more thermal pretreatments
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S428/00—Stock material or miscellaneous articles
- Y10S428/922—Static electricity metal bleed-off metallic stock
- Y10S428/9335—Product by special process
- Y10S428/939—Molten or fused coating
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12785—Group IIB metal-base component
- Y10T428/12792—Zn-base component
- Y10T428/12799—Next to Fe-base component [e.g., galvanized]
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Coating With Molten Metal (AREA)
- Heat Treatment Of Strip Materials And Filament Materials (AREA)
- Heat Treatment Of Articles (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR0411190A FR2876711B1 (fr) | 2004-10-20 | 2004-10-20 | Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese |
Publications (1)
Publication Number | Publication Date |
---|---|
ZA200703345B true ZA200703345B (en) | 2008-04-30 |
Family
ID=34951699
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ZA200703345A ZA200703345B (en) | 2004-10-20 | 2007-04-23 | Method for the hot-dip coating of iron-carbon-manganese steel strip in a zinc bath |
Country Status (16)
Country | Link |
---|---|
US (1) | US7556865B2 (ru) |
EP (1) | EP1805341B1 (ru) |
JP (1) | JP4828544B2 (ru) |
KR (1) | KR100911639B1 (ru) |
CN (1) | CN100554487C (ru) |
AT (1) | ATE394517T1 (ru) |
BR (1) | BRPI0516997A (ru) |
CA (1) | CA2584449C (ru) |
DE (1) | DE602005006603D1 (ru) |
ES (1) | ES2306247T3 (ru) |
FR (1) | FR2876711B1 (ru) |
MX (1) | MX2007004728A (ru) |
PL (1) | PL1805341T3 (ru) |
RU (1) | RU2363756C2 (ru) |
WO (1) | WO2006042930A1 (ru) |
ZA (1) | ZA200703345B (ru) |
Families Citing this family (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2876708B1 (fr) | 2004-10-20 | 2006-12-08 | Usinor Sa | Procede de fabrication de toles d'acier austenitique fer-carbone-manganese laminees a froid a hautes caracteristiques mecaniques, resistantes a la corrosion et toles ainsi produites |
KR100742833B1 (ko) * | 2005-12-24 | 2007-07-25 | 주식회사 포스코 | 내식성이 우수한 고 망간 용융도금강판 및 그 제조방법 |
KR100742823B1 (ko) * | 2005-12-26 | 2007-07-25 | 주식회사 포스코 | 표면품질 및 도금성이 우수한 고망간 강판 및 이를 이용한도금강판 및 그 제조방법 |
EP1878811A1 (en) * | 2006-07-11 | 2008-01-16 | ARCELOR France | Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced |
DE102006039307B3 (de) | 2006-08-22 | 2008-02-21 | Thyssenkrupp Steel Ag | Verfahren zum Beschichten eines 6-30 Gew.% Mn enthaltenden warm- oder kaltgewalzten Stahlbands mit einer metallischen Schutzschicht |
EP2145027A1 (en) * | 2007-05-02 | 2010-01-20 | Corus Staal BV | Method for hot dip galvanising of ahss or uhss strip material, and such material |
EP2009127A1 (en) * | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation |
KR101079472B1 (ko) * | 2008-12-23 | 2011-11-03 | 주식회사 포스코 | 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 |
DE102009018577B3 (de) | 2009-04-23 | 2010-07-29 | Thyssenkrupp Steel Europe Ag | Verfahren zum Schmelztauchbeschichten eines 2-35 Gew.-% Mn enthaltenden Stahlflachprodukts und Stahlflachprodukt |
DE102009030489A1 (de) | 2009-06-24 | 2010-12-30 | Thyssenkrupp Nirosta Gmbh | Verfahren zum Herstellen eines warmpressgehärteten Bauteils, Verwendung eines Stahlprodukts für die Herstellung eines warmpressgehärteten Bauteils und warmpressgehärtetes Bauteil |
ATE554190T1 (de) * | 2009-08-25 | 2012-05-15 | Thyssenkrupp Steel Europe Ag | Verfahren zum herstellen eines mit einem metallischen, vor korrosion schützenden überzug versehenen stahlbauteils und stahlbauteil |
DE102009053260B4 (de) | 2009-11-05 | 2011-09-01 | Salzgitter Flachstahl Gmbh | Verfahren zum Beschichten von Stahlbändern und beschichtetes Stahlband |
DE102009044861B3 (de) * | 2009-12-10 | 2011-06-22 | ThyssenKrupp Steel Europe AG, 47166 | Verfahren zum Herstellen eines gut umformbaren Stahlflachprodukts, Stahlflachprodukt und Verfahren zur Herstellung eines Bauteils aus einem solchen Stahlflachprodukt |
IT1403129B1 (it) * | 2010-12-07 | 2013-10-04 | Ct Sviluppo Materiali Spa | Procedimento per la produzione di acciaio ad alto manganese con resistenza meccanica e formabilità elevate, ed acciaio così ottenibile. |
US9680080B2 (en) | 2011-07-18 | 2017-06-13 | Hamilton Sunstrand Corporation | Thermoelectric conversion of waste heat from generator cooling system |
KR101510505B1 (ko) | 2012-12-21 | 2015-04-08 | 주식회사 포스코 | 우수한 도금성과 초고강도를 갖는 고망간 용융아연도금강판의 제조방법 및 이에 의해 제조된 고망간 용융아연도금강판 |
CA2900063C (en) * | 2013-02-06 | 2018-12-04 | Arcelormittal | Thermal treatment process of a steel sheet comprising a low viscosity molten oxides bath |
US10590501B2 (en) * | 2013-02-06 | 2020-03-17 | Arcelormittal | Method of treatment of a running ferrous alloy sheet and treatment line for its implementation |
DE102013005301A1 (de) | 2013-03-21 | 2014-09-25 | Salzgitter Flachstahl Gmbh | Verfahren zur Verbesserung der Schweißbarkeit von hochmanganhaltigen Stahlbändern und beschichtetes Stahlband |
WO2015039685A1 (de) * | 2013-09-18 | 2015-03-26 | Thyssenkrupp Steel Ag | Verfahren und vorrichtung zur ermittlung der abriebeigenschaften eines beschichteten flachprodukts |
EP3047252B1 (de) * | 2013-09-18 | 2019-11-06 | ThyssenKrupp Steel Europe AG | Verfahren zur ermittlung der abriebeigenschaften von galvannealed stahlflachprodukten |
JP6164280B2 (ja) * | 2015-12-22 | 2017-07-19 | Jfeスチール株式会社 | 表面外観および曲げ性に優れるMn含有合金化溶融亜鉛めっき鋼板およびその製造方法 |
WO2017203309A1 (en) * | 2016-05-24 | 2017-11-30 | Arcelormittal | Twip steel sheet having an austenitic matrix |
WO2017203310A1 (en) | 2016-05-24 | 2017-11-30 | Arcelormittal | Method for producing a twip steel sheet having an austenitic microstructure |
WO2017203315A1 (en) | 2016-05-24 | 2017-11-30 | Arcelormittal | Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts |
PL3327153T3 (pl) * | 2016-11-23 | 2021-05-17 | Outokumpu Oyj | Sposób wytwarzania elementu składowego mającego złożony kształt |
WO2019092468A1 (en) | 2017-11-08 | 2019-05-16 | Arcelormittal | A hot-dip coated steel sheet |
DE102018128131A1 (de) * | 2018-11-09 | 2020-05-14 | Thyssenkrupp Ag | Gehärtetes Bauteil umfassend ein Stahlsubstrat und eine Korrosionsschutzbeschichtung, entsprechendes Bauteil zur Herstellung des gehärteten Bauteils sowie Herstellverfahren und Verwendung |
WO2021084304A1 (en) * | 2019-10-30 | 2021-05-06 | Arcelormittal | A press hardening method |
WO2021224662A1 (en) * | 2020-05-07 | 2021-11-11 | Arcelormittal | Annealing method of steel |
CN115074616A (zh) * | 2021-03-16 | 2022-09-20 | 上海梅山钢铁股份有限公司 | 一种冰箱底板用热镀铝锌钢板及其制造方法 |
US20220354999A1 (en) | 2021-05-10 | 2022-11-10 | Cilag Gmbh International | Bioabsorbable staple comprising mechanisms for slowing the absorption of the staple |
Family Cites Families (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
AT377287B (de) * | 1982-04-13 | 1985-02-25 | Ver Edelstahlwerke Ag | Kaltverfestigender austenitischer manganhartstahl und verfahren zur herstellung desselben |
JPH04259325A (ja) * | 1991-02-13 | 1992-09-14 | Sumitomo Metal Ind Ltd | 加工性に優れた高強度熱延鋼板の製造方法 |
JPH06240431A (ja) * | 1993-02-12 | 1994-08-30 | Kawasaki Steel Corp | 溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板及び複層めっき鋼板の製造方法 |
JPH07278772A (ja) * | 1994-04-11 | 1995-10-24 | Nippon Steel Corp | Mn含有高強度溶融亜鉛めっき鋼板の製造法 |
US6177140B1 (en) * | 1998-01-29 | 2001-01-23 | Ispat Inland, Inc. | Method for galvanizing and galvannealing employing a bath of zinc and aluminum |
FR2796083B1 (fr) * | 1999-07-07 | 2001-08-31 | Usinor | Procede de fabrication de bandes en alliage fer-carbone-manganese, et bandes ainsi produites |
JP2001140051A (ja) * | 1999-11-12 | 2001-05-22 | Kawasaki Steel Corp | 溶融めっき鋼帯及び合金化溶融めっき鋼帯の製造方法並びに溶融めっき装置 |
JP3716718B2 (ja) * | 2000-07-31 | 2005-11-16 | 住友金属工業株式会社 | 合金化溶融亜鉛めっき鋼板とその製造方法 |
US6572713B2 (en) * | 2000-10-19 | 2003-06-03 | The Frog Switch And Manufacturing Company | Grain-refined austenitic manganese steel casting having microadditions of vanadium and titanium and method of manufacturing |
JP3503594B2 (ja) * | 2000-12-05 | 2004-03-08 | 住友金属工業株式会社 | 耐黒変性に優れた溶融Zn−Al合金めっき鋼板とその製造方法 |
JP3636132B2 (ja) * | 2001-11-22 | 2005-04-06 | 住友金属工業株式会社 | 溶融亜鉛めっき鋼板の製造方法 |
JP3882679B2 (ja) * | 2002-05-23 | 2007-02-21 | Jfeスチール株式会社 | めっき外観の良好な深絞り性に優れた複合組織型高張力溶融亜鉛めっき冷延鋼板の製造方法 |
EP1587966B1 (en) * | 2003-01-15 | 2017-05-17 | Nippon Steel & Sumitomo Metal Corporation | High-strength hot-dip galvanized steel sheet and method for producing the same |
FR2876708B1 (fr) * | 2004-10-20 | 2006-12-08 | Usinor Sa | Procede de fabrication de toles d'acier austenitique fer-carbone-manganese laminees a froid a hautes caracteristiques mecaniques, resistantes a la corrosion et toles ainsi produites |
-
2004
- 2004-10-20 FR FR0411190A patent/FR2876711B1/fr not_active Expired - Fee Related
-
2005
- 2005-10-10 MX MX2007004728A patent/MX2007004728A/es active IP Right Grant
- 2005-10-10 ES ES05809221T patent/ES2306247T3/es active Active
- 2005-10-10 CN CNB2005800418609A patent/CN100554487C/zh active Active
- 2005-10-10 JP JP2007537321A patent/JP4828544B2/ja active Active
- 2005-10-10 PL PL05809221T patent/PL1805341T3/pl unknown
- 2005-10-10 DE DE602005006603T patent/DE602005006603D1/de active Active
- 2005-10-10 US US11/577,536 patent/US7556865B2/en active Active
- 2005-10-10 CA CA2584449A patent/CA2584449C/fr not_active Expired - Fee Related
- 2005-10-10 WO PCT/FR2005/002491 patent/WO2006042930A1/fr active IP Right Grant
- 2005-10-10 EP EP05809221A patent/EP1805341B1/fr active Active
- 2005-10-10 BR BRPI0516997-6A patent/BRPI0516997A/pt not_active IP Right Cessation
- 2005-10-10 RU RU2007118637/02A patent/RU2363756C2/ru not_active IP Right Cessation
- 2005-10-10 AT AT05809221T patent/ATE394517T1/de active
-
2007
- 2007-04-23 ZA ZA200703345A patent/ZA200703345B/en unknown
- 2007-05-18 KR KR1020077011318A patent/KR100911639B1/ko active IP Right Grant
Also Published As
Publication number | Publication date |
---|---|
CA2584449A1 (fr) | 2006-04-27 |
DE602005006603D1 (de) | 2008-06-19 |
FR2876711B1 (fr) | 2006-12-08 |
PL1805341T3 (pl) | 2008-10-31 |
RU2007118637A (ru) | 2008-11-27 |
RU2363756C2 (ru) | 2009-08-10 |
BRPI0516997A (pt) | 2008-09-30 |
JP4828544B2 (ja) | 2011-11-30 |
JP2008517157A (ja) | 2008-05-22 |
KR100911639B1 (ko) | 2009-08-12 |
US20080083477A1 (en) | 2008-04-10 |
EP1805341A1 (fr) | 2007-07-11 |
CN100554487C (zh) | 2009-10-28 |
MX2007004728A (es) | 2007-06-15 |
EP1805341B1 (fr) | 2008-05-07 |
US7556865B2 (en) | 2009-07-07 |
KR20070064373A (ko) | 2007-06-20 |
CA2584449C (fr) | 2010-08-24 |
FR2876711A1 (fr) | 2006-04-21 |
ES2306247T3 (es) | 2008-11-01 |
ATE394517T1 (de) | 2008-05-15 |
CN101072892A (zh) | 2007-11-14 |
WO2006042930A1 (fr) | 2006-04-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7556865B2 (en) | Hot-dip coating method in a zinc bath for strips of iron/carbon/manganese steel | |
AU2016200172B2 (en) | Method for Hot-Dip Coating a Flat Steel Product Containing 2 - 35 wt% of Mn and Flat Steel Product | |
US8592049B2 (en) | High strength hot dip galvanized steel sheet and high strength galvannealed steel sheet excellent in shapeability and plateability | |
KR100928860B1 (ko) | 표면 처리 강판 및 그 제조 방법 | |
KR101329925B1 (ko) | 도금밀착성이 우수한 고망간강 및 이로부터 용융아연도금강판을 제조하는 방법 | |
CN110100038B (zh) | 耐腐蚀性和加工性优异的热浸镀铝系钢材及其制造方法 | |
JP4119804B2 (ja) | 密着性の優れた高強度合金化溶融亜鉛めっき鋼板及びその製造方法 | |
EP2937436B1 (en) | Method for manufacturing high manganese hot-dip galvanized steel sheet with excellent coatability and ultra-high strength, and high manganese hot-dip galvanized steel sheet manufactured by said method | |
CN113272466B (zh) | 热浸镀锌钢板的制造方法 | |
ZA200703344B (en) | Process for manufacturing corrosion-resistant cold-rolled sheet of iron-carbon-manganese austenitic steel having high mechanical properties and sheet thus produced | |
CA2390808C (en) | High tensile strength hot-dipped steel sheet and method or producing the same | |
CN108474095B (zh) | 镀覆性优异的高强度热浸镀锌系钢材及其制造方法 | |
CN113122772A (zh) | 薄钢板和镀覆钢板、以及薄钢板和镀覆钢板的制造方法 | |
EP3034646A1 (en) | Production method for high-strength hot-dip galvanized steel sheets and production method for high-strength alloyed hot-dip galvanized steel sheets | |
KR20180087435A (ko) | 도금성 및 용접성이 우수한 오스테나이트계 용융 알루미늄 도금강판 및 그 제조방법 | |
KR101528010B1 (ko) | 도금성이 우수한 고망간강 용융아연도금강판 및 이의 제조방법 | |
KR101665807B1 (ko) | 도금성이 우수한 오스테나이트계 고강도 고망간 용융 알루미늄 도금강판 및 그의 제조방법 | |
CN109371320A (zh) | 镀锌钢板及其制造方法 | |
JP4940813B2 (ja) | TS×Elの値が21000MPa・%以上である溶融亜鉛めっき鋼板の製造方法 | |
JP3548491B2 (ja) | 耐食性が良好でプレス加工性の良い高強度合金化溶融亜鉛めっき鋼板 | |
KR102031459B1 (ko) | 도금성이 우수한 초고강도 고망간 용융아연도금강판 및 그 제조방법 |