BRPI0516997A - processo de revestimento à têmpera quente em um banho de zinco das cintas em aço ferro - carbono - manganês - Google Patents
processo de revestimento à têmpera quente em um banho de zinco das cintas em aço ferro - carbono - manganêsInfo
- Publication number
- BRPI0516997A BRPI0516997A BRPI0516997-6A BRPI0516997A BRPI0516997A BR PI0516997 A BRPI0516997 A BR PI0516997A BR PI0516997 A BRPI0516997 A BR PI0516997A BR PI0516997 A BRPI0516997 A BR PI0516997A
- Authority
- BR
- Brazil
- Prior art keywords
- belt
- iron
- zinc
- manganese
- carbon
- Prior art date
Abstract
PROCESSO DE REVESTIMENTO à TEMPERA QUENTE EM UM BANHO DE ZINCO DAS CINTAS EM AçO FERRO - CARBONO - MANGANêS. A invenção tem por objeto um revestimento à têmpera a quente em um banho líquido à base de zinco, compreendendo alumínio, de uma cinta em aço austenítico ferro - carbono - manganês, em passagem, segundo o qual se faz essa cinta sofrer um tratamento térmico em um forno no interior do qual reina uma atmosfera redutora face ao ferro, para se obter uma cinta coberta de uma fina camada de manganês, depois se fazer passar essa cinta coberta da fina camada de óxido de manganês nesse banho, o teor em alumínio nesse banho sendo ajustado em um valor pelo menos igual ao teor necessário para que o alumínio reduza completamente a camada de óxido de manganês, de maneira a formar na superfície da cinta esse revestimento que compreende uma camada de liga ferro - manganês - zinco, e uma camada superficial de zinco.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR0411190A FR2876711B1 (fr) | 2004-10-20 | 2004-10-20 | Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese |
PCT/FR2005/002491 WO2006042930A1 (fr) | 2004-10-20 | 2005-10-10 | Procédé de revêtement au trempé à chaud dans un bain de zinc des bandes en acier fer-carbone-manganèse |
Publications (1)
Publication Number | Publication Date |
---|---|
BRPI0516997A true BRPI0516997A (pt) | 2008-09-30 |
Family
ID=34951699
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BRPI0516997-6A BRPI0516997A (pt) | 2004-10-20 | 2005-10-10 | processo de revestimento à têmpera quente em um banho de zinco das cintas em aço ferro - carbono - manganês |
Country Status (16)
Country | Link |
---|---|
US (1) | US7556865B2 (pt) |
EP (1) | EP1805341B1 (pt) |
JP (1) | JP4828544B2 (pt) |
KR (1) | KR100911639B1 (pt) |
CN (1) | CN100554487C (pt) |
AT (1) | ATE394517T1 (pt) |
BR (1) | BRPI0516997A (pt) |
CA (1) | CA2584449C (pt) |
DE (1) | DE602005006603D1 (pt) |
ES (1) | ES2306247T3 (pt) |
FR (1) | FR2876711B1 (pt) |
MX (1) | MX2007004728A (pt) |
PL (1) | PL1805341T3 (pt) |
RU (1) | RU2363756C2 (pt) |
WO (1) | WO2006042930A1 (pt) |
ZA (1) | ZA200703345B (pt) |
Families Citing this family (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2876708B1 (fr) * | 2004-10-20 | 2006-12-08 | Usinor Sa | Procede de fabrication de toles d'acier austenitique fer-carbone-manganese laminees a froid a hautes caracteristiques mecaniques, resistantes a la corrosion et toles ainsi produites |
KR100742833B1 (ko) * | 2005-12-24 | 2007-07-25 | 주식회사 포스코 | 내식성이 우수한 고 망간 용융도금강판 및 그 제조방법 |
KR100742823B1 (ko) * | 2005-12-26 | 2007-07-25 | 주식회사 포스코 | 표면품질 및 도금성이 우수한 고망간 강판 및 이를 이용한도금강판 및 그 제조방법 |
EP1878811A1 (en) | 2006-07-11 | 2008-01-16 | ARCELOR France | Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced |
DE102006039307B3 (de) | 2006-08-22 | 2008-02-21 | Thyssenkrupp Steel Ag | Verfahren zum Beschichten eines 6-30 Gew.% Mn enthaltenden warm- oder kaltgewalzten Stahlbands mit einer metallischen Schutzschicht |
JP5586024B2 (ja) * | 2007-05-02 | 2014-09-10 | タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップ | Ahssまたはuhssストリップ材料の溶融亜鉛めっき方法、及びそのような材料 |
EP2009127A1 (en) * | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation |
KR101079472B1 (ko) * | 2008-12-23 | 2011-11-03 | 주식회사 포스코 | 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법 |
DE102009018577B3 (de) | 2009-04-23 | 2010-07-29 | Thyssenkrupp Steel Europe Ag | Verfahren zum Schmelztauchbeschichten eines 2-35 Gew.-% Mn enthaltenden Stahlflachprodukts und Stahlflachprodukt |
DE102009030489A1 (de) | 2009-06-24 | 2010-12-30 | Thyssenkrupp Nirosta Gmbh | Verfahren zum Herstellen eines warmpressgehärteten Bauteils, Verwendung eines Stahlprodukts für die Herstellung eines warmpressgehärteten Bauteils und warmpressgehärtetes Bauteil |
ES2384135T3 (es) * | 2009-08-25 | 2012-06-29 | Thyssenkrupp Steel Europe Ag | Procedimiento para fabricar un componente de acero provisto de un recubrimiento metálico de protección contra la corrosión y componente de acero |
DE102009053260B4 (de) | 2009-11-05 | 2011-09-01 | Salzgitter Flachstahl Gmbh | Verfahren zum Beschichten von Stahlbändern und beschichtetes Stahlband |
DE102009044861B3 (de) * | 2009-12-10 | 2011-06-22 | ThyssenKrupp Steel Europe AG, 47166 | Verfahren zum Herstellen eines gut umformbaren Stahlflachprodukts, Stahlflachprodukt und Verfahren zur Herstellung eines Bauteils aus einem solchen Stahlflachprodukt |
IT1403129B1 (it) * | 2010-12-07 | 2013-10-04 | Ct Sviluppo Materiali Spa | Procedimento per la produzione di acciaio ad alto manganese con resistenza meccanica e formabilità elevate, ed acciaio così ottenibile. |
US9680080B2 (en) | 2011-07-18 | 2017-06-13 | Hamilton Sunstrand Corporation | Thermoelectric conversion of waste heat from generator cooling system |
KR101510505B1 (ko) | 2012-12-21 | 2015-04-08 | 주식회사 포스코 | 우수한 도금성과 초고강도를 갖는 고망간 용융아연도금강판의 제조방법 및 이에 의해 제조된 고망간 용융아연도금강판 |
JP6194019B2 (ja) * | 2013-02-06 | 2017-09-06 | アルセロールミタル | 鋼板の熱処理方法およびその実施のための装置 |
US10590501B2 (en) * | 2013-02-06 | 2020-03-17 | Arcelormittal | Method of treatment of a running ferrous alloy sheet and treatment line for its implementation |
DE102013005301A1 (de) * | 2013-03-21 | 2014-09-25 | Salzgitter Flachstahl Gmbh | Verfahren zur Verbesserung der Schweißbarkeit von hochmanganhaltigen Stahlbändern und beschichtetes Stahlband |
CA2924765A1 (en) | 2013-09-18 | 2015-03-26 | Thyssenkrupp Steel Ag | Method and device for determining the abrasion properties of a coated flat product |
KR102148062B1 (ko) * | 2013-09-18 | 2020-08-25 | 티센크루프 스틸 유럽 악티엔게젤샤프트 | 합금화아연도금 평강 제품의 연마 특성을 결정하는 방법 및 장치 |
JP6164280B2 (ja) * | 2015-12-22 | 2017-07-19 | Jfeスチール株式会社 | 表面外観および曲げ性に優れるMn含有合金化溶融亜鉛めっき鋼板およびその製造方法 |
WO2017203310A1 (en) | 2016-05-24 | 2017-11-30 | Arcelormittal | Method for producing a twip steel sheet having an austenitic microstructure |
WO2017203315A1 (en) | 2016-05-24 | 2017-11-30 | Arcelormittal | Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts |
WO2017203309A1 (en) * | 2016-05-24 | 2017-11-30 | Arcelormittal | Twip steel sheet having an austenitic matrix |
ES2842293T3 (es) * | 2016-11-23 | 2021-07-13 | Outokumpu Oy | Método para fabricar un componente de forma compleja |
WO2019092468A1 (en) | 2017-11-08 | 2019-05-16 | Arcelormittal | A hot-dip coated steel sheet |
DE102018128131A1 (de) * | 2018-11-09 | 2020-05-14 | Thyssenkrupp Ag | Gehärtetes Bauteil umfassend ein Stahlsubstrat und eine Korrosionsschutzbeschichtung, entsprechendes Bauteil zur Herstellung des gehärteten Bauteils sowie Herstellverfahren und Verwendung |
WO2021084304A1 (en) * | 2019-10-30 | 2021-05-06 | Arcelormittal | A press hardening method |
WO2021224662A1 (en) * | 2020-05-07 | 2021-11-11 | Arcelormittal | Annealing method of steel |
CN115074616A (zh) * | 2021-03-16 | 2022-09-20 | 上海梅山钢铁股份有限公司 | 一种冰箱底板用热镀铝锌钢板及其制造方法 |
US11890004B2 (en) | 2021-05-10 | 2024-02-06 | Cilag Gmbh International | Staple cartridge comprising lubricated staples |
Family Cites Families (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
AT377287B (de) * | 1982-04-13 | 1985-02-25 | Ver Edelstahlwerke Ag | Kaltverfestigender austenitischer manganhartstahl und verfahren zur herstellung desselben |
JPH04259325A (ja) * | 1991-02-13 | 1992-09-14 | Sumitomo Metal Ind Ltd | 加工性に優れた高強度熱延鋼板の製造方法 |
JPH06240431A (ja) * | 1993-02-12 | 1994-08-30 | Kawasaki Steel Corp | 溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板及び複層めっき鋼板の製造方法 |
JPH07278772A (ja) * | 1994-04-11 | 1995-10-24 | Nippon Steel Corp | Mn含有高強度溶融亜鉛めっき鋼板の製造法 |
US6177140B1 (en) * | 1998-01-29 | 2001-01-23 | Ispat Inland, Inc. | Method for galvanizing and galvannealing employing a bath of zinc and aluminum |
FR2796083B1 (fr) * | 1999-07-07 | 2001-08-31 | Usinor | Procede de fabrication de bandes en alliage fer-carbone-manganese, et bandes ainsi produites |
JP2001140051A (ja) * | 1999-11-12 | 2001-05-22 | Kawasaki Steel Corp | 溶融めっき鋼帯及び合金化溶融めっき鋼帯の製造方法並びに溶融めっき装置 |
JP3716718B2 (ja) * | 2000-07-31 | 2005-11-16 | 住友金属工業株式会社 | 合金化溶融亜鉛めっき鋼板とその製造方法 |
US6572713B2 (en) * | 2000-10-19 | 2003-06-03 | The Frog Switch And Manufacturing Company | Grain-refined austenitic manganese steel casting having microadditions of vanadium and titanium and method of manufacturing |
JP3503594B2 (ja) * | 2000-12-05 | 2004-03-08 | 住友金属工業株式会社 | 耐黒変性に優れた溶融Zn−Al合金めっき鋼板とその製造方法 |
JP3636132B2 (ja) * | 2001-11-22 | 2005-04-06 | 住友金属工業株式会社 | 溶融亜鉛めっき鋼板の製造方法 |
JP3882679B2 (ja) * | 2002-05-23 | 2007-02-21 | Jfeスチール株式会社 | めっき外観の良好な深絞り性に優れた複合組織型高張力溶融亜鉛めっき冷延鋼板の製造方法 |
CA2513298C (en) * | 2003-01-15 | 2012-01-03 | Nippon Steel Corporation | High-strength hot-dip galvanized steel sheet and method for producing the same |
FR2876708B1 (fr) * | 2004-10-20 | 2006-12-08 | Usinor Sa | Procede de fabrication de toles d'acier austenitique fer-carbone-manganese laminees a froid a hautes caracteristiques mecaniques, resistantes a la corrosion et toles ainsi produites |
-
2004
- 2004-10-20 FR FR0411190A patent/FR2876711B1/fr not_active Expired - Fee Related
-
2005
- 2005-10-10 WO PCT/FR2005/002491 patent/WO2006042930A1/fr active IP Right Grant
- 2005-10-10 EP EP05809221A patent/EP1805341B1/fr active Active
- 2005-10-10 RU RU2007118637/02A patent/RU2363756C2/ru not_active IP Right Cessation
- 2005-10-10 AT AT05809221T patent/ATE394517T1/de active
- 2005-10-10 CN CNB2005800418609A patent/CN100554487C/zh active Active
- 2005-10-10 DE DE602005006603T patent/DE602005006603D1/de active Active
- 2005-10-10 US US11/577,536 patent/US7556865B2/en active Active
- 2005-10-10 PL PL05809221T patent/PL1805341T3/pl unknown
- 2005-10-10 BR BRPI0516997-6A patent/BRPI0516997A/pt not_active IP Right Cessation
- 2005-10-10 MX MX2007004728A patent/MX2007004728A/es active IP Right Grant
- 2005-10-10 JP JP2007537321A patent/JP4828544B2/ja active Active
- 2005-10-10 ES ES05809221T patent/ES2306247T3/es active Active
- 2005-10-10 CA CA2584449A patent/CA2584449C/fr not_active Expired - Fee Related
-
2007
- 2007-04-23 ZA ZA200703345A patent/ZA200703345B/en unknown
- 2007-05-18 KR KR1020077011318A patent/KR100911639B1/ko active IP Right Grant
Also Published As
Publication number | Publication date |
---|---|
EP1805341B1 (fr) | 2008-05-07 |
US20080083477A1 (en) | 2008-04-10 |
MX2007004728A (es) | 2007-06-15 |
DE602005006603D1 (de) | 2008-06-19 |
JP2008517157A (ja) | 2008-05-22 |
ATE394517T1 (de) | 2008-05-15 |
RU2363756C2 (ru) | 2009-08-10 |
KR100911639B1 (ko) | 2009-08-12 |
US7556865B2 (en) | 2009-07-07 |
ZA200703345B (en) | 2008-04-30 |
JP4828544B2 (ja) | 2011-11-30 |
CA2584449A1 (fr) | 2006-04-27 |
RU2007118637A (ru) | 2008-11-27 |
CN101072892A (zh) | 2007-11-14 |
PL1805341T3 (pl) | 2008-10-31 |
CA2584449C (fr) | 2010-08-24 |
EP1805341A1 (fr) | 2007-07-11 |
FR2876711A1 (fr) | 2006-04-21 |
FR2876711B1 (fr) | 2006-12-08 |
WO2006042930A1 (fr) | 2006-04-27 |
CN100554487C (zh) | 2009-10-28 |
ES2306247T3 (es) | 2008-11-01 |
KR20070064373A (ko) | 2007-06-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BRPI0516997A (pt) | processo de revestimento à têmpera quente em um banho de zinco das cintas em aço ferro - carbono - manganês | |
BRPI0518623A2 (pt) | processo para revestimento em banho quente de uma fita de aÇo forte | |
US20200255916A1 (en) | Flat Steel Product with an Al-Coating, Method for Producing the Same, Steel Component and Method for Producing the Same | |
ZA200808424B (en) | Method for continuously annealing and preparing strip of high-strength steel for the purpose of hot-dip galvanizing it | |
BRPI0517630A (pt) | processo para produção de uma chapa de aço protegida contra corrosão | |
BRPI0412601A (pt) | método para produção de uma peça de aço endurecido | |
Frandsen et al. | Simultaneous surface engineering and bulk hardening of precipitation hardening stainless steel | |
KR20100113492A (ko) | 코팅경화된 강철의 부품의 제조방법 및 코팅경화가능한 강철 스트립 | |
BRPI0102747B1 (pt) | processo de realização de uma peça com altas características mecânicas, conformada por embutimento, a partir de uma tira de chapa de aço laminada e notadamente laminada a quente e revestida | |
GB2170824A (en) | Corrosion resistant steel components and method of manufacture thereof | |
BRPI0822326A2 (pt) | instalalção de galvanização à têmpera de uma cinta de aço | |
RU2647419C2 (ru) | Способ отжига листовой стали | |
BRPI0603946A (pt) | método para diminuir o coeficiente de atrito da superfìcie de cintas metálicas com um revestimento e dispositivo para aplicar um revestimento metálico por sobre uma cinta de aço | |
MX2013010431A (es) | Baño de sales fundidas para nitruracion de piezas mecanicas de acero y metodo de aplicacion del mismo. | |
Sen | The characterization of vanadium boride coatings on AISI 8620 steel | |
TW201708562A (zh) | 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法 | |
Horn et al. | Functional optimization of hot-stamped components by local carburization | |
CN103774085B (zh) | 一种在低碳合金钢表面制备的高氮奥氏体层及制备方法 | |
Lee et al. | Solid lubrication coating of FeS layer on the surface of SKD 61 steel produced by plasma sulfnitriding | |
Kaouka et al. | Properties of boride layer on boridesae 1035 steel by molten salt | |
Caliari et al. | An investigation into the effects of different oxy-nitrocarburizing conditions on hardness profiles and corrosion behavior of 16MnCr5 steels | |
Nová et al. | Monitoring of the diffusion processes during carburizing automotive steel parts | |
BR112017002172B1 (pt) | Método de produção de um aço de embalagem nitretado | |
KR20200087817A (ko) | 노 챔버 내에 배치된 반응 챔버 내에서 스트립 강의 사전 산화 방법 | |
BR0113848A (pt) | Instalação de finalidade dupla para recozimento continuo e chapeamento por imersão a quente |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B08F | Application dismissed because of non-payment of annual fees [chapter 8.6 patent gazette] |
Free format text: REFERENTE A 10A ANUIDADE. |
|
B08K | Patent lapsed as no evidence of payment of the annual fee has been furnished to inpi [chapter 8.11 patent gazette] |
Free format text: EM VIRTUDE DO ARQUIVAMENTO PUBLICADO NA RPI 2327 DE 11-08-2015 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDO O ARQUIVAMENTO DO PEDIDO DE PATENTE, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013. |