WO2024042847A1 - Produit d'encollage pour fibres et son utilisation - Google Patents

Produit d'encollage pour fibres et son utilisation Download PDF

Info

Publication number
WO2024042847A1
WO2024042847A1 PCT/JP2023/023691 JP2023023691W WO2024042847A1 WO 2024042847 A1 WO2024042847 A1 WO 2024042847A1 JP 2023023691 W JP2023023691 W JP 2023023691W WO 2024042847 A1 WO2024042847 A1 WO 2024042847A1
Authority
WO
WIPO (PCT)
Prior art keywords
compound
sizing agent
fiber
resin
acetylene
Prior art date
Application number
PCT/JP2023/023691
Other languages
English (en)
Japanese (ja)
Inventor
昌彦 吉田
Original Assignee
松本油脂製薬株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 松本油脂製薬株式会社 filed Critical 松本油脂製薬株式会社
Priority to JP2023566915A priority Critical patent/JP7429827B1/ja
Priority to JP2024007117A priority patent/JP2024045274A/ja
Publication of WO2024042847A1 publication Critical patent/WO2024042847A1/fr

Abstract

Le problème à résoudre par la présente invention est de fournir : un produit d'encollage qui améliore la mouillabilité d'une résine de matrice par rapport à des brins de fibres ; et un matériau composite renforcé par des fibres et des brins de fibres mettant en œuvre le produit d'encollage. La solution selon l'invention porte sur un produit d'encollage pour fibres, contenant un composé (A) et un composé à base d'acétylène (B), le composé (A) étant au moins un composé choisi parmi une résine thermodurcissable (A1), une résine thermoplastique (A2) et du caoutchouc (A3), et le rapport en poids ((B)/(A)) du composé à base d'acétylène (B) au composé (A) allant de 0,0005 à 0,13.
PCT/JP2023/023691 2022-08-25 2023-06-27 Produit d'encollage pour fibres et son utilisation WO2024042847A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2023566915A JP7429827B1 (ja) 2022-08-25 2023-06-27 繊維用サイジング剤及びその用途
JP2024007117A JP2024045274A (ja) 2022-08-25 2024-01-22 繊維用サイジング剤及びその用途

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2022-133901 2022-08-25
JP2022133901 2022-08-25

Publications (1)

Publication Number Publication Date
WO2024042847A1 true WO2024042847A1 (fr) 2024-02-29

Family

ID=90012962

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/023691 WO2024042847A1 (fr) 2022-08-25 2023-06-27 Produit d'encollage pour fibres et son utilisation

Country Status (2)

Country Link
TW (1) TW202421888A (fr)
WO (1) WO2024042847A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007063739A (ja) * 2005-08-03 2007-03-15 Nisshin Chem Ind Co Ltd 硝子繊維処理剤及び硝子繊維処理剤組成物
JP2009084116A (ja) * 2007-10-01 2009-04-23 Nippon Electric Glass Co Ltd ガラス繊維用集束剤、ガラス繊維、ガラス繊維の製造方法及びガラス繊維強化熱可塑性樹脂材料
JP2013129946A (ja) * 2011-12-22 2013-07-04 Sumitomo Seika Chem Co Ltd 炭素繊維用サイジング剤および該サイジング剤で処理された炭素繊維束
WO2022209895A1 (fr) * 2021-04-01 2022-10-06 松本油脂製薬株式会社 Agent de collage pour fibres de renforcement et son utilisation

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007063739A (ja) * 2005-08-03 2007-03-15 Nisshin Chem Ind Co Ltd 硝子繊維処理剤及び硝子繊維処理剤組成物
JP2009084116A (ja) * 2007-10-01 2009-04-23 Nippon Electric Glass Co Ltd ガラス繊維用集束剤、ガラス繊維、ガラス繊維の製造方法及びガラス繊維強化熱可塑性樹脂材料
JP2013129946A (ja) * 2011-12-22 2013-07-04 Sumitomo Seika Chem Co Ltd 炭素繊維用サイジング剤および該サイジング剤で処理された炭素繊維束
WO2022209895A1 (fr) * 2021-04-01 2022-10-06 松本油脂製薬株式会社 Agent de collage pour fibres de renforcement et son utilisation

Also Published As

Publication number Publication date
TW202421888A (zh) 2024-06-01

Similar Documents

Publication Publication Date Title
KR101557568B1 (ko) 탄소섬유용 사이징제, 그의 수분산액, 사이징제가 부착된 탄소섬유속, 시트상물, 및 탄소섬유 강화 복합재
JP7147107B1 (ja) 強化繊維用サイジング剤及びその用途
TW591157B (en) Sizing agent for carbon fiber, its water dispersing solution, carbon fiber with sizing handling, sheet matter with using the carbon fiber and carbon fiber reinforced composite
JP7350745B2 (ja) 繊維用集束剤組成物、繊維束、繊維製品及び複合材料
WO2013099707A1 (fr) Fibre de carbone revêtue de colle, processus de production d'une fibre de carbone revêtue de colle, pré-imprégné et matériau composite renforcé par une fibre de carbone
JP5561350B2 (ja) プリプレグおよび炭素繊維強化複合材料
WO2015194457A1 (fr) Faisceau de fibres renforcées et son procédé de production
JP4866701B2 (ja) 炭素繊維用サイジング剤、サイジング処理炭素繊維、シート状物
JP2016160549A (ja) 炭素繊維用サイジング剤、炭素繊維束、シート状基材及び炭素繊維強化複合材
JP2009074229A (ja) 繊維用集束剤
JP2014139360A (ja) サイジング剤塗布炭素繊維およびその製造方法、炭素繊維強化熱可塑性樹脂組成物
JP6381527B2 (ja) 強化繊維用サイジング剤及びその用途
JP7429827B1 (ja) 繊維用サイジング剤及びその用途
JP7018692B2 (ja) 繊維強化材及び繊維強化ポリプロピレン樹脂複合材料
JP2005320641A (ja) サイジング剤、炭素繊維および炭素繊維強化複合材料
WO2024042847A1 (fr) Produit d'encollage pour fibres et son utilisation
JP6116503B2 (ja) 炭素繊維用サイジング剤及びその用途
JP2001316980A (ja) 繊維の集束用樹脂組成物
JP2014163000A (ja) 炭素繊維束、及びそれを用いた炭素繊維強化複合材料
JP7502579B1 (ja) 繊維用サイジング剤及びその用途
JP2001019496A (ja) ガラス繊維用集束剤
JP2014074255A (ja) サイジング剤塗布炭素繊維、サイジング剤塗布炭素繊維の製造方法、プリプレグおよび炭素繊維強化複合材料
WO2024127878A1 (fr) Agent de collage pour des fibres et son utilisation
TW202436727A (zh) 纖維用上漿劑及其用途
JP4887208B2 (ja) 炭素繊維用サイズ剤、その水分散液、炭素繊維、及び炭素繊維強化複合材料

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2023566915

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23856964

Country of ref document: EP

Kind code of ref document: A1