WO2022158374A1 - スチレン系樹脂組成物 - Google Patents

スチレン系樹脂組成物 Download PDF

Info

Publication number
WO2022158374A1
WO2022158374A1 PCT/JP2022/000990 JP2022000990W WO2022158374A1 WO 2022158374 A1 WO2022158374 A1 WO 2022158374A1 JP 2022000990 W JP2022000990 W JP 2022000990W WO 2022158374 A1 WO2022158374 A1 WO 2022158374A1
Authority
WO
WIPO (PCT)
Prior art keywords
styrene
mass
resin composition
composition according
content
Prior art date
Application number
PCT/JP2022/000990
Other languages
English (en)
French (fr)
Inventor
晶太 滝口
直人 大久保
誠太 木村
幸夫 安澤
Original Assignee
出光興産株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 出光興産株式会社 filed Critical 出光興産株式会社
Priority to CN202280010407.5A priority Critical patent/CN116848188A/zh
Priority to KR1020237023630A priority patent/KR20230135058A/ko
Priority to JP2022576636A priority patent/JPWO2022158374A1/ja
Priority to US18/262,289 priority patent/US20240101806A1/en
Priority to DE112022000730.3T priority patent/DE112022000730T5/de
Publication of WO2022158374A1 publication Critical patent/WO2022158374A1/ja

Abstract

シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％である、スチレン系樹脂組成物である。

Description

スチレン系樹脂組成物
　本発明は、スチレン系樹脂組成物に関する。
　シンジオタクチック構造を有するスチレン系樹脂（シンジオタクチックポリスチレン。以下、ＳＰＳともいう。）は、機械的強度、耐熱性、電気特性、吸水寸法安定性、及び耐薬品性等の優れた性能を有する。そのため、ＳＰＳは、電気・電子機器材料、車載・電装部品、家電製品、各種機械部品、産業用資材等の様々な用途に使用される樹脂として非常に有用である。
　ＳＰＳの特性に対して、強度、靭性、耐熱性、耐薬品性、成形加工性等の複数の性質のバランスを取るために他の樹脂とのブレンドが検討されている。
　たとえば、特許文献１には、耐熱水性と離型性、低ガス性の両立を目的として、特定量のガラスフィラー、シンジオタクチック構造を有するスチレン系樹脂、ゴム状弾性体、フェノール系酸化防止剤及び硫黄系酸化防止剤から選択される酸化防止剤、ポリフェニレンエーテル及び変性ポリフェニレンエーテルから選択される化合物と、核剤及び離型剤から選択される少なくとも１種とを含む、スチレン系樹脂組成物等が開示されている。
　一方、ＳＰＳは、前記の特徴を活かし、家庭用品材料としても有用であり、食器への応用も検討されている。たとえば、特許文献２には、耐熱性、汎用性の確保とデザインを容易に付すことを目的として、ＳＰＳ樹脂により成形した生地成形品の表面に、コロナ放電により発生したコロナの放射により改質処理した表面に塗料を塗布してなる食器類が開示されている。
国際公開２０１９／１０７５２６号 特開２０１５－２１７０１１号公報
　前記のようにＳＰＳの優れた性質を活かして、ＳＰＳを含む樹脂組成物の食器等の家庭用品への検討も行われている。物性のバランスを取るためにエラストマー等の他の樹脂を配合したり、外観を装飾するために着色剤を混合することも行われている。特に食器などに用いられる際には、高い意匠性が求められ、着色剤による色むらを抑制し、表面の光沢性を高める必要性があった。更に、最近では、コンビニエンスストアの総菜やインスタント食品の利用の増加に伴い、食器類は電子レンジ調理に使用されることが多く、食品を効率的に加熱するために電磁波の透過損失が低いことが求められる。また、繰り返し利用される場合は、高含有油食品の加熱時に油が高温となった際にも容器表面が溶融することなく、食器としての強度や耐熱性を有するものが求められる。
　したがって、本発明は、色むらがなく、光沢に優れ、更に強度と耐熱性にも優れるスチレン系樹脂組成物を提供することを課題とする。
　本発明者らは鋭意検討の結果、ＳＰＳと、スチレン系エラストマー、相溶化剤、無機フィラー、着色剤を含有し、更にスチレン系エラストマーと着色剤の含有量を特定の量とした樹脂組成物が前記課題を解決することを見出した。すなわち、本発明は以下の［１］～［１９］に関する。
［１］シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％である、スチレン系樹脂組成物。
［２］スチレン系エラストマー（Ｂ）が、スチレン－ジエンブロック共重合体、水素添加スチレン－ジエンブロック共重合体、スチレン－ジエンランダム共重合体、水素添加スチレン－ジエンランダム共重合体、及びスチレン－オレフィンランダム共重合体からなる群より選ばれる少なくとも一種である、上記［１］に記載のスチレン系樹脂組成物。
［３］スチレン系エラストマー（Ｂ）が、スチレン－ブタジエンブロック共重合体、水素添加スチレン－ブタジエンブロック共重合体、スチレン－ブタジエン－スチレンブロック共重合体、水素添加スチレン－ブタジエン－スチレンブロック共重合体、スチレン－イソプレンブロック共重合体、水素添加スチレン－イソプレンブロック共重合体、スチレン－イソプレン－スチレンブロック共重合体、水素添加スチレン－イソプレン－スチレンブロック共重合体、スチレン－ブタジエンランダム共重合体、水素添加スチレン－ブタジエンランダム共重合体、スチレン－エチレン－プロピレンランダム共重合体、及びスチレン－エチレン－ブチレンランダム共重合体からなる群より選ばれる少なくとも一種である、上記［１］又は［２］に記載のスチレン系樹脂組成物。
［４］スチレン系エラストマー（Ｂ）を構成する、スチレンに由来する構成単位と、ジエン、水素添加ジエン及びオレフィンに由来する構成単位の合計との質量比［（スチレン）／（ジエン、水素添加ジエン、オレフィン）］が、２０／８０～７０／３０である、上記［２］又は［３］に記載のスチレン系樹脂組成物。
［５］相溶化剤（Ｃ）が変性ポリフェニレンエーテルである、上記［１］～［４］のいずれか１つに記載のスチレン系樹脂組成物。
［６］シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときの相溶化剤（Ｃ）の含有量が０．４～５．０質量％である、上記［１］～［５］のいずれか１つに記載のスチレン系樹脂組成物。
［７］無機フィラー（Ｄ）がガラスフィラーである、上記［１］～［６］のいずれか１つに記載のスチレン系樹脂組成物。
［８］スチレン系樹脂組成物の全量を１００質量％としたときの無機フィラー（Ｄ）の含有量が５～５０質量％である、上記［１］～［７］のいずれか１つに記載のスチレン系樹脂組成物。
［９］無機フィラー（Ｄ）がシラン系カップリング剤又はチタン系カップリング剤により処理されている、上記［１］～［８］のいずれか１つに記載のスチレン系樹脂組成物。
［１０］着色剤（Ｅ）が、カーボンブラック、無機顔料、有機顔料及び有機染料からなる群より選ばれる少なくとも一種である、上記［１］～［９］のいずれか１つに記載のスチレン系樹脂組成物。
［１１］無機顔料が、二酸化チタン、酸化鉄、ニッケルチタンイエロー、硫化亜鉛、硫酸バリウム、群青からなる群より選ばれる少なくとも一種である、上記［１０］に記載のスチレン系樹脂組成物。
［１２］有機顔料が、モノアゾ顔料、ペリレン顔料、キナクリドン顔料、及びフタロシアニン顔料からなる群より選ばれる少なくとも一種である、上記［１０］に記載のスチレン系樹脂組成物。
［１３］着色剤（Ｅ）が、カーボンブラック、無機顔料、有機顔料及び有機染料からなる群より選ばれる少なくとも一種であり、スチレン系樹脂組成物の全量を１００質量％としたときの着色剤（Ｅ）の含有量が０．０００１質量％以上であり、かつ、該カーボンブラックの含有量が２．５質量％以下であり、該無機顔料の含有量が３．０質量％以下であり、該有機顔料及び該有機染料の含有量の合計が１．０質量％以下である、上記［１］～［１２］のいずれか１つに記載のスチレン系樹脂組成物。
［１４］オレフィン系エラストマーを実質的に含まない、上記［１］～［１３］のいずれか１つに記載のスチレン系樹脂組成物。
［１５］上記［１］～［１４］のいずれか１つに記載のスチレン系樹脂組成物からなる、食器用樹脂成形材料。
［１６］上記［１］～［１４］のいずれか１つに記載のスチレン系樹脂組成物からなる、電子レンジ調理器用樹脂成形材料。
［１７］上記［１］～［１４］のいずれか１つに記載のスチレン系樹脂組成物を含有する成形体。
［１８］上記［１］～［１４］のいずれか１つに記載のスチレン系樹脂組成物を含有する食器。
［１９］上記［１］～［１４］のいずれか１つに記載のスチレン系樹脂組成物を含有する電子レンジ調理器。
　本発明によれば、色むらがなく、光沢に優れ、更に強度と耐熱性にも優れるスチレン系樹脂組成物を提供することができる。したがって、本発明のスチレン系樹脂組成物は、特に食器用樹脂成形材料として優れる。
［スチレン系樹脂組成物］
　本発明のスチレン系樹脂組成物は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％である。
　以下、各項目について詳細に説明する。
　尚、本明細書において、「ｘ～ｙ」は「ｘ以上、ｙ以下」の数値範囲を表すものとする。数値範囲に関して記載された上限値及び下限値は任意に組み合わせることができる。また、以下において記載される本発明に係る態様の個々の実施形態のうち、互いに相反しない２つ以上の実施形態を組み合わせることが可能であり、２つ以上の実施形態を組み合わせた実施形態もまた、本発明に係る態様の実施形態である。
＜シンジオタクチック構造を有するスチレン系樹脂（Ａ）＞
　スチレン系樹脂（Ａ）（以下、ＳＰＳ（Ａ）ともいう）は、高度なシンジオタクチック構造を有するスチレン系樹脂である。本明細書において「シンジオタクチック」とは、隣り合うスチレン単位におけるフェニル環が、重合体ブロックの主鎖によって形成される平面に対して交互に配置（以下において、シンジオタクティシティと記載する）されている割合が高いことを意味する。
　タクティシティは、同位体炭素による核磁気共鳴法（13Ｃ－ＮＭＲ法）により定量同定できる。13Ｃ－ＮＭＲ法により、連続する複数の構成単位、例えば連続した２つのモノマーユニットをダイアッド、３つのモノマーユニットをトリアッド、５つのモノマーユニットをペンタッドとしてその存在割合を定量することができる。
　本発明において、「高度なシンジオタクチック構造を有するスチレン系樹脂」とは、ラセミダイアッド（ｒ）で通常７５モル％以上、好ましくは８５モル％以上、又はラセミペンタッド（ｒｒｒｒ）で通常３０モル％以上、好ましくは５０モル％以上のシンジオタクティシティを有するポリスチレン、ポリ（炭化水素置換スチレン）、ポリ（ハロゲン化スチレン）、ポリ（ハロゲン化アルキルスチレン）、ポリ（アルコキシスチレン）、ポリ（ビニル安息香酸エステル）等のスチレン系重合体、これらの水素化重合体若しくは混合物、又はこれらを主成分とする共重合体を意味する。
　ポリ（炭化水素置換スチレン）としては、ポリ（メチルスチレン）、ポリ（エチルスチレン）、ポリ（イソプロピルスチレン）、ポリ（ｔｅｒｔ－ブチルスチレン）、ポリ（フェニルスチレン）、ポリ（ビニルナフタレン）及びポリ（ビニルスチレン）等を挙げることができる。ポリ（ハロゲン化スチレン）としては、ポリ（クロロスチレン）、ポリ（ブロモスチレン）及びポリ（フルオロスチレン）等を、ポリ（ハロゲン化アルキルスチレン）としては、ポリ（クロロメチルスチレン）等を挙げることができる。ポリ（アルコキシスチレン）としては、ポリ（メトキシスチレン）及びポリ（エトキシスチレン）等が挙げられる。
　前記の構成単位を含む共重合体のコモノマー成分としては、前記スチレン系重合体のモノマーの他、エチレン、プロピレン、ブテン、ヘキセン及びオクテン等のオレフィンモノマー；ブタジエン、イソプレン等のジエンモノマー；環状オレフィンモノマー；環状ジエンモノマー；メタクリル酸メチル、無水マレイン酸及びアクリロニトリル等の極性ビニルモノマーが挙げられる。
　スチレン系樹脂（Ａ）として、好適に用いられる共重合体としては、スチレンとｐ－メチルスチレンとの共重合体、スチレンとｐ－ｔｅｒｔ－ブチルスチレンとの共重合体、スチレンとジビニルベンゼンとの共重合体等が挙げられ、スチレンとｐ－メチルスチレンとの共重合体が好ましい。
　前記スチレン系樹脂のなかでは、ポリスチレン、ポリ（ｐ－メチルスチレン）、ポリ（ｍ－メチルスチレン）、ポリ（ｐ－ｔｅｒｔ－ブチルスチレン）、ポリ（ｐ－クロロスチレン）、ポリ（ｍ－クロロスチレン）、ポリ（ｐ－フルオロスチレン）、スチレンとｐ－メチルスチレンとの共重合体から選ばれる１種以上が好ましく、ポリスチレン、ポリ（ｐ－メチルスチレン）、ポリ（ｍ－メチルスチレン）、スチレンとｐ－メチルスチレンとの共重合体から選ばれる１種以上がより好ましく、ポリスチレン、スチレンとｐ－メチルスチレンとの共重合体から選ばれる１種以上が更に好ましく、ポリスチレンが最も好ましい。
　ＳＰＳ（Ａ）は、温度３００℃、荷重１．２ｋｇの条件下でメルトフローレート（ＭＦＲ）測定を行った場合に、好ましくは２ｇ／１０分以上、より好ましくは４ｇ／１０分以上であり、好ましくは５０ｇ／１０分以下、より好ましくは３５ｇ／１０分以下である。ＳＰＳ（Ａ）の前記ＭＦＲ値が２ｇ／１０分以上であれば、成形時の樹脂の流動性にも問題がなく、また、５０ｇ／１０分以下、好ましくは３５ｇ／１０分以下であれば十分な強度を有する成形品を得ることができる。
　ＳＰＳ（Ａ）は、成形時の樹脂の流動性及び得られる成形体の強度の観点から、重量平均分子量が１×１０4以上１×１０6以下であることが好ましく、５０，０００以上５００，０００以下であることがより好ましく、５０，０００以上２００，０００以下であることがさらに好ましい。重量平均分子量が１×１０4以上であれば、十分な強度を有する成形品を得ることができる。一方、重量平均分子量が１×１０6以下であれば成形時の樹脂の流動性にも問題がない。
　本明細書において、重量平均分子量とは、特段の記載がない限り、東ソー株式会社製ＧＰＣ装置（ＨＬＣ－８３２１ＧＰＣ／ＨＴ）、東ソー株式会社製ＧＰＣカラム（ＧＭＨＨＲ－Ｈ（Ｓ）ＨＴＣ／ＨＴ）を用い、溶離液として１，２，４－トリクロロベンゼンを用いて１４５℃でゲル浸透クロマトグラフィー測定法により測定し、標準ポリスチレンの検量線を用いて換算した値である。
　ＳＰＳ（Ａ）は、例えば不活性炭化水素溶媒中又は溶媒の不存在下で、チタン化合物、及び水とトリアルキルアルミニウムの縮合生成物（アルミノキサン）を触媒として、スチレン系単量体（上記スチレン系重合体に対応する単量体）を重合することにより製造することができる（例えば、特開２００９－０６８０２２号公報）。
　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときの、スチレン系樹脂組成物中のシンジオタクチック構造を有するスチレン系樹脂（Ａ）（ＳＰＳ（Ａ））の含有量は、好ましくは６５～９７．６質量％であり、より好ましくは７８～９７．６質量％であり、更に好ましくは８２～９７．６質量％であり、より更に好ましくは８５．５～９７．６質量％である。
＜スチレン系エラストマー（Ｂ）＞
　本発明のスチレン系樹脂組成物は、スチレン系エラストマー（Ｂ）を含有する。スチレン系エラストマー（Ｂ）の含有量は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、２．０～３０．０質量％である。
　スチレン系エラストマー（Ｂ）はＳＰＳ（Ａ）との相溶性が高いためか、本発明のスチレン系樹脂組成物がスチレン系エラストマー（Ｂ）を含有することで、色むらを抑制し、強度を著しく向上させることができる。
　スチレン系エラストマー（Ｂ）は、スチレンに由来する構成単位を含むエラストマーであれば制限はないが、好ましくはスチレン－ジエンブロック共重合体、水素添加スチレン－ジエンブロック共重合体、スチレン－ジエンランダム共重合体、水素添加スチレン－ジエンランダム共重合体、及びスチレン－オレフィンランダム共重合体からなる群より選ばれる少なくとも一種である。ここで、スチレンと共重合されるジエンとしては、ブタジエン及びイソプレンが挙げられ、スチレンと共重合されるオレフィンとしては、エチレン、プロピレン及びブチレンが挙げられる。
　スチレン系エラストマー（Ｂ）は、より好ましくはスチレン－ブタジエンブロック共重合体（ＳＢＲ）、水素添加スチレン－ブタジエンブロック共重合体（ＳＥＢ）、スチレン－ブタジエン－スチレンブロック共重合体（ＳＢＳ）、水素添加スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）、スチレン－イソプレンブロック共重合体（ＳＩＲ）、水素添加スチレン－イソプレンブロック共重合体（ＳＥＰ）、スチレン－イソプレン－スチレンブロック共重合体（ＳＩＳ）、水素添加スチレン－イソプレン－スチレンブロック共重合体（ＳＥＰＳ）、スチレン－ブタジエンランダム共重合体、水素添加スチレン－ブタジエンランダム共重合体、スチレン－エチレン－プロピレンランダム共重合体、及びスチレン－エチレン－ブチレンランダム共重合体からなる群より選ばれる少なくとも一種であり、更に好ましくはスチレン－ブタジエンブロック共重合体（ＳＢＲ）、水素添加スチレン－ブタジエンブロック共重合体（ＳＥＢ）、スチレン－ブタジエン－スチレンブロック共重合体（ＳＢＳ）、水素添加スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）、スチレン－イソプレンブロック共重合体（ＳＩＲ）、水素添加スチレン－イソプレンブロック共重合体（ＳＥＰ）、スチレン－イソプレン－スチレンブロック共重合体（ＳＩＳ）、及び水素添加スチレン－イソプレン－スチレンブロック共重合体（ＳＥＰＳ）からなる群より選ばれる少なくとも一種であり、より更に好ましくはスチレン－ブタジエン－スチレンブロック共重合体（ＳＢＳ）、水素添加スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）、スチレン－イソプレン－スチレンブロック共重合体（ＳＩＳ）、及び水素添加スチレン－イソプレン－スチレンブロック共重合体（ＳＥＰＳ）からなる群より選ばれる少なくとも一種であり、より更に好ましくは水素添加スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）、及びスチレン－イソプレン－スチレンブロック共重合体（ＳＩＳ）、及び水素添加スチレン－イソプレン－スチレンブロック共重合体（ＳＥＰＳ）からなる群より選ばれる少なくとも一種であり、より更に好ましくは水素添加スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）である。
　スチレン系エラストマー（Ｂ）を構成する、スチレンに由来する構成単位と、ジエン、水素添加ジエン及びオレフィンに由来する構成単位の合計との質量比［（スチレン）／（ジエン、水素添加ジエン、オレフィン）］は、好ましくは２０／８０～７０／３０であり、より好ましくは２５／７５～６０／４０、さらに好ましくは２５／７５～４５／５５である。スチレン系エラストマー（Ｂ）のスチレン含有量は、スチレン系エラストマー（Ｂ）中、２０～７０質量％であることが好ましく、２５～６０質量％であることがより好ましく、２５～４５質量％であることが更に好ましい。
　スチレン含有量、あるいはスチレンに由来する構成単位と、ジエン、水素添加ジエン及びオレフィンに由来する構成単位の合計との質量比を上記の範囲にすることで、ＳＰＳ（Ａ）との相溶性を高め、色むらを抑制しつつ、強度を著しく向上させることができる。
　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときの、スチレン系樹脂組成物中のスチレン系エラストマー（Ｂ）の含有量は、２．０～３０．０質量％である。スチレン系エラストマー（Ｂ）の量が２．０質量％以上であれば、得られる樹脂組成物の機械強度が向上し、スチレン系エラストマー（Ｂ）の量が３０．０質量％以下であれば、得られる樹脂組成物の耐熱性が良好となる。
　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときのスチレン系エラストマー（Ｂ）の含有量は、好ましくは２．０～１８．０質量％であり、より好ましくは２．０～１５．０質量％であり、更に好ましくは２．０～１２．０質量％であり、より更に好ましくは４．０～１２．０質量％であり、より更に好ましくは７．０～１１．０質量％である。
　また、本発明のスチレン系樹脂組成物は、オレフィン系エラストマーの含有量が少ないことが好ましく、オレフィン系エラストマーを実質的に含まないことがより好ましい。
　オレフィン系エラストマーのなかでも、エチレン－オクテン共重合体の含有量が少ないことが好ましく、エチレン－オクテン共重合体を実質的に含まないことがより好ましい。
　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときのオレフィン系エラストマーの含有量は、好ましくは２５質量％以下であり、より好ましくは１５質量％以下であり、更に好ましくは５質量％以下であり、より更に好ましくは０質量％である。オレフィン系エラストマーを実質的に含まないことで、着色剤（Ｅ）のスチレン系樹脂組成物への分散性が向上し、色むらが抑制される。
＜相溶化剤（Ｃ）＞
　本発明のスチレン系樹脂組成物は、相溶化剤（Ｃ）を含有する。
　本発明のスチレン系樹脂組成物に用いられる相溶化剤（Ｃ）は、スチレン系樹脂（Ａ）と相溶性を有し、その他の成分との相溶性を向上させるものであり、無機フィラー（Ｄ）と反応可能な極性基を有することが好ましい。
　このように相溶化剤（Ｃ）はＳＰＳ（Ａ）と、その他の成分、特に無機フィラー（Ｄ）との相溶性を向上させ、各成分間の界面強度を向上させることを目的として配合される。
　相溶化剤（Ｃ）は、ＳＰＳ（Ａ）と相溶性を有するが、相溶性に寄与する構造としては、ポリマー鎖中にＳＰＳとの相溶性を有する連鎖を含有する構造であることが好ましい。
　たとえば、ポリスチレン、ポリフェニレンエーテル、ポリビニルメチルエーテル等がポリマー鎖の主鎖又はグラフト鎖として有する構造が挙げられ、ポリフェニレンエーテル構造であることが好ましい。
　無機フィラー（Ｄ）と反応可能な極性基とは、無機フィラー（Ｄ）が有する極性基と反応しうる官能基を指す。具体例としては、酸無水物基、カルボン酸基、カルボン酸エステル基、カルボン酸ハライド基、カルボン酸アミド基、カルボン酸塩基、スルホン酸基、スルホン酸エステル基、スルホン酸塩化物基、スルホン酸アミド基、スルホン酸塩基、エポキシ基、アミノ基、イミド基、オキサゾリン基等が挙げられ、カルボン酸基が好ましい。
　相溶化剤（Ｃ）としては、変性ポリフェニレンエーテル等が挙げられ、変性ポリフェニレンエーテルが好ましい。
　変性ポリフェニレンエーテルとしては、フマル酸変性ポリフェニレンエーテル、無水マレイン酸変性ポリフェニレンエーテル、（スチレン－無水マレイン酸）－ポリフェニレンエーテル－グラフトポリマー、グリシジルメタクリレート変性ポリフェニレンエーテル、アミン変性ポリフェニレンエーテル等が挙げられ、フマル酸変性ポリフェニレンエーテル及び無水マレイン酸変性ポリフェニレンエーテルが好ましく、フマル酸変性ポリフェニレンエーテルがより好ましい。
　変性ポリフェニレンエーテルの変性量（変性剤含有量）は、好ましくは０．１～２０質量％であり、より好ましくは０．２～１５質量％であり、更に好ましくは０．３～１０質量％であり、より更に好ましくは０．５～５．０質量％である。変性量が前記範囲であると良好な強度と耐熱性を有するスチレン系樹脂組成物及び成形体を得ることができる。
　変性ポリフェニレンエーテルの変性量（変性剤含有量）は、ＪＩＳ　Ｋ　００７０－１９９２に準拠して測定された中和滴定量によって求めることができる。
　前記変性ポリフェニレンエーテルは、変性剤を用いて公知のポリフェニレンエーテルを変性することにより得ることができるが、本発明の目的に使用可能であれば、変性ポリフェニレンエーテルを得る方法はこの方法に限定されない。該ポリフェニレンエーテルは、公知の化合物であり、この目的のため、米国特許第３，３０６，８７４号、同３，３０６，８７５号、同３，２５７，３５７号及び同３，２５７，３５８号の各明細書を参照することができる。ポリフェニレンエーテルは、通常、銅アミン錯体触媒の存在下で、二置換または三置換フェノールを用いた酸化カップリング反応によって調製される。銅アミン錯体は、第一、第二及び第三アミンから誘導される銅アミン錯体を使用できる。
　ポリフェニレンエーテルの例としては、ポリ（２，６－ジメチル－１，４－フェニレンエーテル）、ポリ（２，３－ジメチル－６－エチル－１，４－フェニレンエーテル）、ポリ（２－メチル－６－クロロメチル－１，４－フェニレンエーテル）、ポリ（２－メチル－６－ヒドロキシエチル－１，４－フェニレンエーテル）、ポリ（２－メチル－６－ｎ－ブチル－１，４－フェニレンエーテル）、ポリ（２－エチル－６－イソプロピル－１，４－フェニレンエーテル）、ポリ（２－エチル－６－ｎ－プロピル－１，４－フェニレンエーテル）、ポリ（２，３，６－トリメチル－１，４－フェニレンエーテル）、ポリ〔２－（４’－メチルフェニル）－１，４－フェニレンエーテル〕、ポリ（２－ブロモ－６－フェニル－１，４－フェニレンエーテル）、ポリ（２－メチル－６－フェニル－１，４－フェニレンエーテル）、ポリ（２－フェニル－１，４－フェニレンエーテル）、ポリ（２－クロロ－１，４－フェニレンエーテル）、ポリ（２－メチル－１，４－フェニレンエーテル）、ポリ（２－クロロ－６－エチル－１，４－フェニレンエーテル）、ポリ（２－クロロ－６－ブロモ－１，４－フェニレンエーテル）、ポリ（２，６－ジ－ｎ－プロピル－１，４－フェニレンエーテル）、ポリ（２－メチル－６－イソプロピル－１，４－フェニレンエーテル）、ポリ（２－クロロ－６－メチル－１，４－フェニレンエーテル）、ポリ（２－メチル－６－エチル－１，４－フェニレンエーテル）、ポリ（２，６－ジブロモ－１，４－フェニレンエーテル）、ポリ（２，６－ジクロロ－１，４－フェニレンエーテル）、ポリ（２，６－ジエチル－１，４－フェニレンエーテル）等が挙げられ、ポリ（２，６－ジメチル－１，４－フェニレンエーテル）が好ましい。
　ポリフェニレンエーテルの変性に用いられる変性剤としては、同一分子内にエチレン性二重結合と極性基とを有する化合物が挙げられ、具体的には例えば無水マレイン酸、マレイン酸、フマル酸、マレイン酸エステル、フマル酸エステル、マレイミド及びそのＮ置換体、マレイン酸塩、フマル酸塩、アクリル酸、アクリル酸エステル、アクリル酸アミド、アクリル酸塩、メタクリル酸、メタクリル酸エステル、メタクリル酸アミド、メタクリル酸塩、グリシジルメタクリレートなどが挙げられる。これらのうち特に無水マレイン酸、フマル酸及びグリシジルメタクリレートが好ましく用いられ、フマル酸がより好ましく用いられる。上記各種の変性剤は１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
　変性ポリフェニレンエーテルは、前記ポリフェニレンエーテルと変性剤とを反応させることにより得られる。変性の方法に特に制限はなく、公知の方法を用いることができる。
　好ましい変性方法として、溶融変性及び溶液変性が挙げられ、なかでもより高い変性量が得られること、生産性が高いことから、より好ましくは溶融変性である。すなわち、前記変性ポリフェニレンエーテルは、好ましくは溶融変性によって製造された変性ポリフェニレンエーテル又は溶液変性によって製造された変性ポリフェニレンエーテルであり、より好ましくは溶融変性によって製造された変性ポリフェニレンエーテルである。
　溶融変性は、ラジカル発生剤の存在下あるいは不存在下で、ポリフェニレンエーテルと、変性剤とを、溶融混練することにより、変性ポリフェニレンエーテルを得る方法であり、具体的には、ロールミル、バンバリーミキサー、押出機などを用いて１５０～３５０℃の範囲の温度において溶融混練して反応させる方法である。
　具体的には、ポリフェニレンエーテル、変性剤、及び任意のラジカル発生剤を室温で均一にドライブレンドした後、実質的にポリフェニレンエーテルの混練温度である３００～３５０℃の範囲で溶融反応を行う方法が好ましい。３００℃以上であれば、溶融粘度を適切に維持することができ、３５０℃以下であれば、ポリフェニレンエーテルの分解を抑制することができる。
　溶融変性における変性剤の使用量は、ポリフェニレンエーテル１００質量部に対して、好ましくは０．１～２２質量部であり、より好ましくは０．２～１７質量部であり、更に好ましくは０．３～１２質量部であり、より更に好ましくは０．５～７．０質量部である。変性剤の使用量が前記範囲であると良好な強度と耐熱性を有するスチレン系樹脂組成物及び成形体を得ることができる。
　溶融変性に用いられるラジカル発生剤は、半減期１分間を示す温度が３００℃以上のものが好ましく、具体的には、例えば２，３－ジメチル－２，３－ジフェニルブタン、２，３－ジエチル－２，３－ジフェニルブタン、２，３－ジエチル－２，３－ジフェニルヘキサン、２，３－ジメチル－２，３－ジ（ｐ－メチルフェニル）ブタン等が挙げられ、なかでも、半減期１分間を示す温度が３３０℃である２，３－ジメチル－２，３－ジフェニルブタンが好適に用いられる。
　ラジカル発生剤の使用割合は、ポリフェニレンエーテル１００質量部に対して、好ましくは０．１～３質量部、より好ましくは０．５～２質量部の範囲で選定される。０．１質量部以上であれば高い変性効果が得られ、３質量部以下であれば、効率よくポリフェニレンエーテルを変性することができ、不溶成分も生じにくい。
　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときの、本発明のスチレン系樹脂組成物中の相溶化剤（Ｃ）の含有量は、好ましくは０．４～５．０質量％である。相溶化剤（Ｃ）の量が０．４質量％以上であれば、得られる樹脂組成物は優れた機械強度を得ることができる。相溶化剤（Ｃ）の量が５．０質量％以下であれば、得られる樹脂組成物中の異物量を低減させることができ、樹脂組成物により得られる成形体の外観を良好に保つことができる。
　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときの相溶化剤（Ｃ）の含有量は、より好ましくは０．４～４．０質量％であり、更に好ましくは０．４～３．０質量％であり、より更に好ましくは０．４～２．５質量％であり、より更に好ましくは０．４～１．７質量％であり、より更に好ましくは０．４～０．７質量％である。
＜無機フィラー（Ｄ）＞
　本発明のスチレン系樹脂組成物は、無機フィラー（Ｄ）を含有する。
　無機フィラー（Ｄ）の形状としては、繊維状、粒状、粉状等が挙げられる。優れた強度を得る観点から、繊維状フィラーを用いることが好ましい。
　無機フィラー（Ｄ）としては、ガラスフィラー、セラミックフィラー等が挙げられ、ガラスフィラーが好ましい。
　ガラスフィラーは、ガラス繊維、ガラスパウダー、ガラスフレーク、ミルドファイバー、ガラスクロス及びガラスビーズより選ばれる１種以上であることがより好ましく、優れた機械強度が得られるため、ガラス繊維が更に好ましい。ガラス繊維を用いることで、スチレン系樹脂組成物及び成形体の強度及び耐熱性を向上させることができ、スチレン系樹脂組成物を食器用樹脂成形材料として好適に用いることができる。
　ガラス繊維の長さは、ハンドリングの観点から、０．０５～５０ｍｍであることが好ましく、０．０５～１０ｍｍであることがより好ましい。さらにこの範囲であれば、成形体にした時に含まれるガラス繊維の長さが０．０１ｍｍ～１．０ｍｍ程度となり、優れた光沢を得ることができる。また、ガラス繊維の径は５～２０μｍであることが好ましい。
　セラミックフィラーとしては、タルク、二酸化チタン、マイカ、ホウ素、アルミナ、炭酸カルシウム、シリカ、炭化ケイ素、セッコウ、チタン酸カリウム、硫酸カルシウム、炭酸バリウム、硫酸マグネシウム、硫酸バリウム、酸化マグネシウム、カオリン等が挙げられる。
　セラミックフィラーの形状としては、繊維状、粒状、粉状等があげられる。
　無機フィラー（Ｄ）はガラスフィラーとセラミックフィラーを併用することもできる。
　無機フィラー（Ｄ）は、ＳＰＳ（Ａ）との接着性を高めるために、カップリング剤で表面処理を施されていることが好ましく、シラン系カップリング剤又はチタン系カップリング剤により処理されていることがより好ましく、シラン系カップリング剤で処理されていることが樹脂成分との相溶性の観点から更に好ましい。
　シラン系カップリング剤の具体例としては、トリエトキシシラン、ビニルトリス（β－メトキシエトキシ）シラン、γ－メタクリロキシプロピルトリメトキシシラン、γ－グリシドキシプロピルトリメトキシシラン、β－（１，１－エポキシシクロヘキシル）エチルトリメトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルトリメトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルメチルジメトキシシラン、γ－アミノプロピルトリエトキシシラン、Ｎ－フェニル－γ－アミノプロピルトリメトキシシラン、γ－メルカプトプロピルトリメトキシシラン、γ－クロロプロピルトリメトキシシラン、γ－アミノプロピルトリメトキシシラン、γ－アミノプロピル－トリス（２－メトキシ－エトキシ）シラン、Ｎ－メチル－γ－アミノプロピルトリメトキシシラン、Ｎ－ビニルベンジル－γ－アミノプロピルトリエトキシシラン、３－ウレイドプロピルトリメトキシシラン、３－４，５－ジヒドロイミダゾールプロピルトリエトキシシラン、ヘキサメチルジシラザン、Ｎ，Ｎ－ビス（トリメチルシリル）ウレア、３－トリエトキシシリル－Ｎ－（１，３－ジメチルーブチリデン）プロピルアミン等が挙げられる。これらの中でも、γ－アミノプロピルトリメトキシシラン、Ｎ－β－（アミノエチル）－γ－アミノプロピルトリメトキシシラン、γ－グリシドキシプロピルトリメトキシシラン、β－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン等のアミノシラン、エポキシシランが好ましい。
　チタン系カップリング剤の具体例としては、イソプロピルトリイソステアロイルチタネート、イソプロピルトリドデシルベンゼンスルホニルチタネート、イソプロピルトリス（ジオクチルパイロホスフェート）チタネート、テトライソプロピルビス（ジオクチルホスファイト）チタネート、テトラオクチルビス（ジトリデシルホスファイト）チタネート、テトラ（１，１－ジアリルオキシメチル－１－ブチル）ビス（ジトリデシル）ホスファイトチタネート、ビス（ジオクチルパイロホスフェート）オキシアセテートチタネート、ビス（ジオクチルパイロホスフェート）エチレンチタネート、イソプロピルトリオクタノイルチタネート、イソプロピルジメタクリルイソステアロイルチタネート、イソプロピルイソステアロイルジアクリルチタネート、イソプロピルトリ（ジオクチルホスフェート）チタネート、イソプロピルトリクミルフェニルチタネート、イソプロピルトリ（Ｎ－アミドエチル，アミノエチル）チタネート、ジクミルフェニルオキシアセテートチタネート、ジイソステアロイルエチレンチタネートなどが挙げられる。これらの中でも、イソプロピルトリ（Ｎ－アミドエチル，アミノエチル）チタネートが好ましい。
　前記カップリング剤を用いた無機フィラーの表面処理は、通常の公知の方法で行うことができる。例えば、前記カップリング剤の有機溶媒溶液若しくは懸濁液を塗布するサイジング処理、乾式混合処理、スプレー法、インテグラルブレンド法、ドライコンセントレート法が挙げられ、サイジング処理、乾式混合処理、スプレー法が好ましい。
　スチレン系樹脂組成物の全量を１００質量％としたときの、スチレン系樹脂組成物中の無機フィラー（Ｄ）の含有量は、好ましくは５～５０質量％である。無機フィラー（Ｄ）の量が５質量％以上であれば、十分な離型剛性を得ることができる。無機フィラー（Ｄ）の量が５０質量％以下であれば、スチレン系樹脂組成物の機械物性及び光沢度に悪影響を与えない。
　スチレン系樹脂組成物の全量を１００質量％としたときの無機フィラー（Ｄ）の含有量は、より好ましくは５～４０質量％であり、更に好ましくは５～３５質量％であり、より更に好ましくは５～２０質量％である。
＜着色剤（Ｅ）＞
　本発明のスチレン系樹脂組成物は、着色剤（Ｅ）を含有し、着色剤（Ｅ）の含有量は、スチレン系樹脂組成物の全量を１００質量％としたとき、０．０００１～６．５質量％である。
　着色剤（Ｅ）の量が０．０００１質量％以上であれば得られる樹脂組成物の発色性が良好となり、着色剤（Ｅ）の量が６．５質量％以下であれば、食品接触用途に使用した場合に使用条件等により万が一溶出や浸出して食品へ移行しても人体に影響を及ぼす懸念がない。着色剤（Ｅ）を前記の量で含有することで、本発明のスチレン系樹脂組成物は成形加工性に優れるものとなる。また、このスチレン系樹脂組成物を用いて得られる成形体は色むらの影響が少なく、意匠性に優れるものとなる。
　着色剤（Ｅ）の含有量は、上記の観点から、スチレン系樹脂組成物の全量を１００質量％としたとき、好ましくは０．０００１質量％以上３．０質量％以下であり、より好ましくは０．０１質量％以上２．５質量％以下であり、更に好ましくは０．１質量％以上１．０質量％以下であり、より更に好ましくは０．１質量％以上０．４質量％以下である。
　着色剤（Ｅ）としては、カーボンブラック、無機着色剤、有機着色剤からなる群より選ばれる少なくとも一種である。無機着色剤としては、無機顔料が挙げられ、有機着色剤としては、有機顔料、及び有機染料等が挙げられる。
　すなわち、着色剤（Ｅ）は、好ましくはカーボンブラック、無機顔料、有機顔料及び有機染料からなる群より選ばれる少なくとも一種である。
　なかでも黒色の樹脂組成物を得る場合には、カーボンブラックがより好ましい。
　無機顔料は、好ましくは、二酸化チタン、酸化鉄、ニッケルチタンイエロー、硫化亜鉛、硫酸バリウム、群青からなる群より選ばれる少なくとも一種である、
　有機顔料は、好ましくは、モノアゾ顔料、ペリレン顔料、キナクリドン顔料、及びフタロシアニン顔料からなる群より選ばれる少なくとも一種である。有機顔料の好適な具体例として、Ｐｉｇｍｅｎｔ　Ｙｅｌｌｏｗ　１８３及びＰｉｇｍｅｎｔ　Ｙｅｌｌｏｗ　１５０等のモノアゾ顔料、Ｐｉｇｍｅｎｔ　Ｒｅｄ　１７８及びＰｉｇｍｅｎｔ　Ｒｅｄ　１４９等のペリレン顔料、Ｐｉｇｍｅｎｔ　Ｖｉｏｌｅｔ　１９、Ｐｉｇｍｅｎｔ　Ｒｅｄ　１２２、Ｐｉｇｍｅｎｔ　Ｒｅｄ　２０９、Ｐｉｇｍｅｎｔ　Ｒｅｄ　２０２、Ｐｉｇｍｅｎｔ　Ｏｒａｎｇｅ　４８及びＰｉｇｍｅｎｔ　Ｏｒａｎｇｅ　４９等のキナクリドン顔料、並びにＰｉｇｍｅｎｔ　Ｂｌｕｅ　１５、Ｐｉｇｍｅｎｔ　Ｂｌｕｅ　１６、Ｐｉｇｍｅｎｔ　Ｇｒｅｅｎ　７及びＰｉｇｍｅｎｔ　Ｇｒｅｅｎ　３６等のフタロシアニン顔料が挙げられる。
　着色剤（Ｅ）の含有量は、本発明のスチレン系樹脂組成物を用いて得られる成形体及び製品の外観に応じて、前記の範囲内で適宜調整すればよい。また、着色剤の種類によって、着色度合いが異なるため、着色剤の着色度合いによっても前記の範囲内で適宜調整すればよい。
　着色剤（Ｅ）が、カーボンブラック、無機顔料、有機顔料及び有機染料からなる群より選ばれる少なくとも一種である場合、スチレン系樹脂組成物の全量を１００質量％としたときの着色剤（Ｅ）の含有量は、好ましくは０．０００１質量％以上であり、かつ、該カーボンブラックの含有量は、好ましくは２．５質量％以下であり、該無機顔料の含有量は、好ましくは３．０質量％以下であり、該有機顔料及び該有機染料の含有量の合計は、好ましくは１．０質量％以下である。
　すなわち、着色剤（Ｅ）が、カーボンブラック、無機顔料、有機顔料及び有機染料からなる群より選ばれる少なくとも一種である場合、スチレン系樹脂組成物の全量を１００質量％としたときのカーボンブラック、無機顔料、有機顔料及び有機染料の合計の含有量は、好ましくは０．０００１質量％以上６．５質量％以下であり、かつ、該カーボンブラックの含有量は、好ましくは０質量％以上２．５質量％以下であり、該無機顔料の含有量は、好ましくは０質量％以上３．０質量％以下であり、該有機顔料及び該有機染料の含有量の合計は、好ましくは０質量％以上１．０質量％以下である。
　着色剤（Ｅ）としてカーボンブラックを用いた場合のカーボンブラックの含有量は、スチレン系樹脂組成物の全量を１００質量％としたとき、好ましくは０．０００１質量％以上２．５質量％以下であり、より好ましくは０．０１質量％以上１．８質量％以下であり、更に好ましくは０．１質量％以上１．０質量％以下であり、より更に好ましくは０．１質量％以上０．４質量％以下である。
　これらの着色剤は必要に応じて複数種類を併用して用いることもできる。
　着色剤（Ｅ）は市販品も好適に使用することができる。カーボンブラックの市販品の例として、ＭＯＮＡＲＣＨ　８００、Ｂｌａｃｋ　Ｐｅａｒｌｓ　８００、Ｂｌａｃｋ　Ｐｅａｒｌｓ　４３５０（以上、キャボット・コーポレーション製）等が挙げられる。二酸化チタンの市販品の例として、ＣＲ－６０（石原産業株式会社製）等が挙げられる。酸化鉄の市販品の例として、トダカラー　１２０ＥＤ（戸田工業株式会社製）等が挙げられる。群青の市販品の例として、群青　＃８０００（第一化成株式会社製）等が挙げられる。モノアゾ顔料の市販品の例として、Ｐａｌｉｏｔｏｌ　Ｙｅｌｌｏｗ　Ｋ１８００（ＢＡＳＦ社製）等が挙げられる。ペリレン顔料の市販品の例として、ＰＶ　Ｆａｓｔ　Ｒｅｄ　Ｂ（クラリアント社製）等が挙げられる。キナクリドン顔料の市販品の例として、Ｃｉｎｑａｓｉａ　Ｍａｚｅｎｔａ　ｋ４５３５ＦＰ（ＢＡＳＦ社製）等が挙げられる。
＜その他の成分＞
　本発明のスチレン系樹脂組成物には、本発明の目的を阻害しない範囲で任意のその他の成分を添加することができる。
　すなわち、本発明のスチレン系樹脂組成物は、その他の成分として、任意の成分である酸化防止剤、架橋剤、架橋助剤、結晶化核剤、分散剤、可塑剤、離型剤、防汚剤、紫外線吸収剤、光安定剤、難燃剤、難燃助剤及び帯電防止剤を含むことができる。
　酸化防止剤は、フェノール系化合物、リン系化合物及びイオウ系化合物より選ばれる１種以上を用いることが好ましく、耐熱性の観点から、フェノール系化合物がより好ましい。
　フェノール系酸化防止剤の具体例としては、２，６－ジ－ｔｅｒｔ－ブチル－４－メチルフェノール、２，６－ジフェニル－４－メトキシフェノール、２，２’－メチレンビス（６－ｔｅｒｔ－ブチル－４－メチルフェノール）、２，２’－メチレンビス〔４－メチル－６－（α－メチルシクロヘキシル）フェノール〕、１，１－ビス（５－ｔｅｒｔ－ブチル－４－ヒドロキシ－２－メチルフェニル）ブタン、２，２’－メチレンビス（４－メチル－６－シクロヘキシルフェノール）、２，２’－メチレンビス（４－メチル－６－ノニルフェノール）、１，１，３－トリス（５－ｔｅｒｔ－ブチル－４－ヒドロキシ－２－メチルフェニル）ブタン、２，２－ビス（５－ｔｅｒｔ－ブチル－４－ヒドロキシ－２－メチルフェニル）－４－ｎ－ドデシルメルカプトブタン、エチレングリコール－ビス〔３，３－ビス（３－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）ブチレート〕、１，１－ビス（３，５－ジメチル－２－ヒドロキシフェニル）－３－（ｎ－ドデシルチオ）－ブタン、４，４’－チオビス（６－ｔｅｒｔ－ブチル－３－メチルフェノール）、１，３，５－トリス（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシベンジル）－２，４，６－トリメチルベンゼン、２，２－ビス（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシベンジル）マロン酸ジオクタデシルエステル、ｎ－オクタデシル－３－（４－ヒドロキシ－３，５－ジ－ｔｅｒｔ－ブチルフェニル）プロピオネート、ペンタエリスリトールテトラキス｛３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート｝等が挙げられる。特に、ペンタエリスリトールテトラキス｛３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート｝が好ましい。
　リン系化合物としては、トリス（２，４－ジ－ｔｅｒｔ－ブチルフェニル）ホスファイト、トリス（モノおよびジ－ノニルフェニル）ホスファイト等のモノホスファイトやジホスファイト等が挙げられる。
　本発明のスチレン系樹脂組成物中の酸化防止剤の含有量について、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量部としたときの酸化防止剤の含有量は、０．０５質量部以上が好ましく、０．１質量部以上がより好ましく、０．１５質量部以上が更に好ましい。また、２．０質量部以下が好ましく、１．０質量部以下がより好ましく、０．７質量部以下が更に好ましい。酸化防止剤の量が前記の範囲であれば、加工時の耐熱変色性が良好となり、さらに長期耐熱性を得ることができ、酸化防止剤のブリードも抑制することができ、外観に悪影響を与えない。
　本発明のスチレン系樹脂組成物は、好ましくは結晶化核剤を含む。
　結晶化核剤は、好ましくは無機系の結晶化核剤および有機系の結晶化核剤からなる群より選ばれる一種以上である。中でも有機系の結晶化核剤が好ましい。
　有機系の結晶化核剤としては、例えば、有機カルボン酸アルカリ金属塩、有機カルボン酸アルカリ土類金属塩、リン酸または亜リン酸の有機化合物及びそれらの金属塩、フタロシアニン誘導体、ソルビトール誘導体などが挙げられる。
　さらに具体的には、例えば、アルミニウムジ（ｐ－ｔｅｒｔ－ブチルベンゾエート）、安息香酸のナトリウム塩、ｐ－ｔｅｒｔ－ブチル安息香酸のヒドロキシアルミニウム塩、ヒドロキシ－ジ（ｐ－ｔｅｒｔ－ブチル安息香酸）アルミニウムをはじめとするカルボン酸の金属塩、メチレンビス（２，４－ジ－ｔｅｒｔ－ブチルフェノール）ホスフェートナトリウム、ナトリウム－２，２’－メチレンビス（４，６－ジ－ｔｅｒｔ－ブチルフェニル）ホスフェート、［リン酸［２，２’－メチレンビス（４，６－ジ－ｔｅｒｔ－ブチルフェニル）］］リチウム、［リン酸［２，２’－メチレンビス（４，６－ジ－ｔｅｒｔ－ブチルフェニル）］］カリウム、リン酸ビス（４－ｔｅｒｔ－ブチルフェニル）ナトリウム、リン酸メチレン（２，４－ｔｅｒｔ－ブチルフェニル）ナトリウム、アルミニウム＝ビス（４，６’，６，６’－テトラ－ｔｅｒｔ－ブチル－２，２’－メチレンジフェニル＝ホスファート）＝ヒドロキシドをはじめとするリン酸の金属塩、［リン酸［２，２’－メチレンビス（４，６－ジ－ｔｅｒｔ－ブチルフェニル）］］アンモニウム等公知のものから任意に選択して用いることができる。また、これらを含む複合体も用いることができる。
　本発明のスチレン系樹脂組成物中の結晶化核剤の含有量について、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量部としたときの結晶化核剤の含有量は、０．０１質量部以上が好ましく、０．１質量部以上がより好ましく、０．１５質量部以上が更に好ましい。また、２．０質量部以下が好ましく、１．０質量部以下がより好ましく、０．７質量部以下が更に好ましい。前記結晶化核剤を用いることで、本発明の効果をより高め、色むらがなく、光沢に優れ、更に強度と耐熱性にも優れる組成物を得ることができる。
　本発明のスチレン系樹脂組成物は、好ましくは離型剤を含む。
　離型剤としては、ポリエチレンワックス、シリコーンオイル、長鎖カルボン酸等公知のものから任意に選択して用いることができる。なかでもシリコーンオイルが好ましい。
　本発明のスチレン系樹脂組成物中の離型剤の含有量について、スチレン系樹脂組成物の全量を１００質量％としたときの離型剤の含有量は、好ましくは０．０５～３．０質量％であり、好ましくは０．１～２．０質量％であり、好ましくは０．１～１．０質量％であり、好ましくは０．１～０．５質量％である。前記離型剤を用いることで、本発明の効果をより高め、色むらを抑制し、光沢に優れる成形体を得ることができる。
　分散剤としては、メチレンビスステアリン酸アマイド、ポリアクリル酸、ポリアクリル酸ナトリウム、カルボン酸ナトリウム、ポリアクリル酸アンモニウム、ポリアクリル酸系共重合体、ポリカルボン酸ナトリウム、カルボン酸系共重合体、スルホン酸系共重合体等、公知のものから任意に選択して用いることができる。
　紫外線吸収剤としては、２－（２Ｈ－ｂｅｎｚｏｔｒｉａｚｏｌ－２－ｙｌ）－４，６－ｂｉｓ（１－ｍｅｔｈｙｌ－１－ｐｈｅｎｙｌｅｔｈｙｌ）ｐｈｅｎｏｌ、２－（２Ｈ－ｂｅｎｚｏｔｒｉａｚｏｌ－２－ｙｌ）－４－（１，１，３，３－ｔｅｔｒａｍｅｔｈｙｌｂｕｔｙｌ）ｐｈｅｎｏｌ、２，２’－ｍｅｔｈｙｌｅｎｅｂｉｓ［６－（２Ｈ－ｂｅｎｚｏｔｒｉａｚｏｌ－２－ｙｌ）－４－（１，１，３，３－ｔｅｔｒａｍｅｔｈｙｌｂｕｔｙｌ）ｐｈｅｎｏｌ］、２－（２Ｈ－ｂｅｎｚｏｔｒｉａｚｏｌ－２－ｙｌ）－ｐ－ｃｒｅｓｏｌ、２－（５－ｃｈｌｏｒｏ－２Ｈ－ｂｅｎｚｏｔｒｉａｚｏｌ－２－ｙｌ）－６－ｔｅｒｔ－ｂｕｔｙｌ－４－ｍｅｔｈｙｌｐｈｅｎｏｌ、２－（４，６－ｄｉｐｈｅｎｙｌ－１，３，５－ｔｒｉａｚｉｎ－２－ｙｌ）－５－［２－（２－ｅｔｈｙｌｈｅｘａｎｏｙｌｏｘｙ）ｅｔｈｏｘｙ］ｐｈｅｎｏｌ、２，４，６－ｔｒｉｓ（２－ｈｙｄｒｏｘｙ－４－ｈｅｘｙｌｏｘｙ－３－ｍｅｔｈｙｌｐｈｅｎｙｌ）－１，３，５－ｔｒｉａｚｉｎｅ、［２－ｈｙｄｒｏｘｙ－４－（ｏｃｔｙｌｏｘｙ）ｐｈｅｎｙｌ］（ｐｈｅｎｙｌ）ｍｅｔｈａｎｏｎｅ等、公知のものから任意に選択して用いることができる。
　光安定剤としては、ｔｅｔｒａｋｉｓ（１，２，２，６，６－ｐｅｎｔａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｙｌ）ｂｕｔａｎｅ－１，２，３，４－ｔｅｔｒａｃａｒｂｏｘｙｌａｔｅ、ｔｅｔｒａｋｉｓ（２，２，６，６－ｔｅｔｒａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｙｌ）ｂｕｔａｎｅ－１，２，３，４－ｔｅｔｒａｃａｒｂｏｘｙｌａｔｅ、１，２，３，４－ｂｕｔａｎｅｔｅｔｒａｃａｒｂｏｘｙｌｉｃ　ａｃｉｄ，　ｔｅｔｒａｍｅｔｈｙｌ　ｅｓｔｅｒ，　ｒｅａｃｔｉｏｎ　ｐｒｏｄｕｃｔｓ　ｗｉｔｈ　１，２，２，６，６－ｐｅｎｔａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｉｎｏｌ　ａｎｄ　β，β，β’，β’－ｔｅｔｒａｍｅｔｈｙｌ－２，４，８，１０－ｔｅｔｒａｏｘａｓｐｉｒｏ［５．５］ｕｎｄｅｃａｎｅ－３，９－ｄｉｅｔｈａｎｏｌ、１，２，３，４－ｂｕｔａｎｅｔｅｔｒａｃａｒｂｏｘｙｌｉｃ　ａｃｉｄ，　ｔｅｔｒａｍｅｔｈｙｌ　ｅｓｔｅｒ，　ｒｅａｃｔｉｏｎ　ｐｒｏｄｕｃｔｓ　ｗｉｔｈ　２，２，６，６－ｔｅｔｒａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｉｎｏｌ　ａｎｄ　β，β，β’，β’－ｔｅｔｒａｍｅｔｈｙｌ－２，４，８，１０－ｔｅｔｒａｏｘａｓｐｉｒｏ［５．５］ｕｎｄｅｃａｎｅ－３，９－ｄｉｅｔｈａｎｏｌ、ｂｉｓ（１，２，２，６，６－ｐｅｎｔａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｙｌ）ｓｅｂａｃａｔｅ、ｂｉｓ（２，２，６，６－ｔｅｔｒａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｙｌ）ｓｅｂａｃａｔｅ、ｂｉｓ（１－ｕｎｄｅｃａｎｏｘｙ－２，２，６，６－ｔｅｔｒａｍｅｔｈｙｌｐｉｐｅｒｉｄｉｎ－４－ｙｌ）ｃａｒｂｏｎａｔｅ、１，２，２，６，６－ｐｅｎｔａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｙｌ　ｍｅｔｈａｃｒｙｌａｔｅ、２，２，６，６－ｔｅｔｒａｍｅｔｈｙｌ－４－ｐｉｐｅｒｉｄｙｌ　ｍｅｔｈａｃｒｙｌａｔｅ、２，２，６，６－ｔｅｔｒａｍｅｔｈｙｌｐｉｐｅｒｉｄｉｎ－４－ｙｌ　ｈｅｘａｄｅｃａｎｏａｔｅ，２，２，６，６－ｔｅｔｒａｍｅｔｈｙｌｐｉｐｅｒｉｄｉｎ－４－ｙｌ　ｏｃｔａｄｅｃａｎｏａｔｅ等、公知のものから任意に選択して用いることができる。
＜スチレン系樹脂組成物の製造＞
　本発明のスチレン系樹脂組成物は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）と、必要に応じて上記その他成分とを配合・混練して組成物を得る。
　配合及び混練は、通常用いられている機器、例えば、リボンブレンダー、ドラムタンブラー、ヘンシェルミキサーなどで予備混合して、バンバリーミキサー、単軸スクリュー押出機、二軸スクリュー押出機、多軸スクリュー押出機及びコニーダ等を用いる方法で行うことができる。
　溶融混練した本発明のスチレン系樹脂組成物は、ペレット状にして保管し、成形体、食器、電子レンジ調理器等の原料として、成形体、食器、電子レンジ調理器等の製造に用いることが好ましい。
［食器用樹脂成形材料及び電子レンジ調理器用樹脂成形材料］
　本発明の食器用樹脂成形材料は、前記スチレン系樹脂組成物からなる。すなわち、本発明の食器用樹脂成形材料は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％であるスチレン系樹脂組成物からなる。
　本発明の食器用樹脂成形材料には、本発明の効果を損なわない範囲で、他の熱可塑性樹脂等を含んでいてもよいが、本発明の食器用樹脂成形材料は、実質的に前記スチレン系樹脂組成物からなる。具体的には、本発明の食器用樹脂成形材料における、前記スチレン系樹脂組成物の含有量は、好ましくは９０質量％以上であり、より好ましくは９５質量％以上であり、更に好ましくは９９質量％以上である。上限には制限はなく、１００質量％以下であればよく、１００質量％であることが好ましく、スチレン系樹脂組成物のみからなっていてもよい。
　本発明の食器用樹脂成形材料は、色むらがなく、光沢に優れ、更に強度と耐熱性にも優れるため、成形体としての食器の材料として好適に用いられる。
　本発明の電子レンジ調理器用樹脂成形材料は、前記スチレン系樹脂組成物からなる。すなわち、本発明の電子レンジ調理器用樹脂成形材料は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％であるスチレン系樹脂組成物からなる。
　本発明の電子レンジ調理器用樹脂成形材料には、本発明の効果を損なわない範囲で、他の熱可塑性樹脂等を含んでいてもよいが、本発明の電子レンジ調理器用樹脂成形材料は、実質的に前記スチレン系樹脂組成物からなる。具体的には本発明の電子レンジ調理器用樹脂成形材料における、前記スチレン系樹脂組成物の含有量は、好ましくは９０質量％以上であり、より好ましくは９５質量％以上であり、更に好ましくは９９質量％以上である。上限には制限はなく、１００質量％以下であればよく、１００質量％であることが好ましく、スチレン系樹脂組成物のみからなっていてもよい。
　本発明の電子レンジ調理器用樹脂成形材料は、色むらがなく、光沢に優れ、更に強度と耐熱性にも優れるため、成形体としての電子レンジ調理器の材料として好適に用いられる。
［成形体、食器及び電子レンジ調理器］
　本発明の成形体は、前記スチレン系樹脂組成物を含有する。すなわち、本発明の成形体は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％であるスチレン系樹脂組成物を含有する。
　本発明の成形体は、前述のスチレン系樹脂組成物を原料として、射出成形法、射出圧縮成形法、押出成形法、ブロー成形法、プレス成形法、真空成形法及び発泡成形法等により製造することができる。特に、ペレット状のスチレン系樹脂組成物を用いて、射出成形及び射出圧縮成形によって得られる射出成形体であることが好ましい。
　本発明の成形体における、前記スチレン系樹脂組成物の含有量は、好ましくは９０質量％以上であり、より好ましくは９５質量％以上であり、更に好ましくは９９質量％以上である。上限には制限はなく、１００質量％以下であればよく、１００質量％であることが好ましく、スチレン系樹脂組成物のみからなっていてもよい。
　本発明の前記スチレン系樹脂組成物は、前記の通り、食器用の材料として用いることが好ましい。
　したがって、本発明の食器は、前記スチレン系樹脂組成物を含有する。すなわち、本発明の食器は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％であるスチレン系樹脂組成物を含有する。
　本発明の食器における、前記スチレン系樹脂組成物の含有量は、好ましくは９０質量％以上であり、より好ましくは９５質量％以上であり、更に好ましくは９９質量％以上である。上限には制限はなく、１００質量％以下であればよく、１００質量％であることが好ましく、スチレン系樹脂組成物のみからなっていてもよい。
　本発明の食器は、前記成形体で説明した各種成形方法によって得ることが好ましく、その形状としては、皿状、椀状、鉢状、盤状、トレー状、棒状、箱状等が挙げられる。
　本発明の食器には、衛生上、意匠上の点から必要な表面処理を施してもよいが、本発明の食器は色むらがなく、光沢に優れるため、表面に印刷や塗装などを行わなくても意匠性が高い。
　本発明の前記スチレン系樹脂組成物は、強度と耐熱性に優れることから、前記の通り、電子レンジ調理器用の材料として用いることが好ましい。
　したがって、本発明の電子レンジ調理器は、前記スチレン系樹脂組成物を含有する。すなわち、本発明の電子レンジ調理器は、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％であるスチレン系樹脂組成物を含有する。
　本発明の電子レンジ調理器における、前記スチレン系樹脂組成物の含有量は、好ましくは９０質量％以上であり、より好ましくは９５質量％以上であり、更に好ましくは９９質量％以上である。上限には制限はなく、１００質量％以下であればよく、１００質量％であることが好ましく、スチレン系樹脂組成物のみからなっていてもよい。
　本発明の電子レンジ調理器は、前記成形体で説明した各種成形方法によって得ることが好ましく、その形状としては、皿状、椀状、鉢状、盤状、棒状、トレー状、箱状等が挙げられる。
　本発明の電子レンジ調理器には、衛生上、意匠上の点から必要な表面処理を施してもよいが、本発明の電子レンジ調理器は色むらがなく、光沢に優れるため、表面に印刷や塗装などを行わなくても意匠性が高い。
　本発明を実施例によりさらに具体的に説明するが、本発明はこれらに何ら制限されるものではない。
　実施例及び比較例で用いた原料は次の通りである。
＜ＳＰＳ（Ａ）＞
・ＳＰＳ：シンジオタクチックポリスチレン樹脂、ラセミペンタッド：９８モル％、ＭＦＲ：１３ｇ／１０分（温度３００℃、荷重１．２ｋｇｆ）、融点２７０℃、出光興産株式会社製
＜エラストマー＞
・ＳＥＰＴＯＮ８００６：ＳＥＰＴＯＮ８００６、水素添加スチレン－ブタジエン－スチレンブロック共重合体（スチレン系エラストマー（Ｂ）に該当）、スチレン含有量３３％、株式会社クラレ製
・ＥＮＧＡＧＥ８１５０：ＥＮＧＡＧＥ８１５０、エチレン－オクテン共重合体（オレフィン系エラストマーに該当）、ダウ社製
＜相溶化剤（Ｃ）＞
・フマル酸変性ポリフェニレンエーテル（ＰＰＥ）、溶融変性により製造、変性量１．５質量％、出光興産株式会社製
＜無機フィラー（Ｄ）＞
・Ｔ－２４９Ｈ：ＥＣＳ０３Ｔ－２４９Ｈ、Ｅガラス、繊維状（チョップドストランド長さ３ｍｍ）、繊維断面略真円形状（φ１０．５μｍ）、シランカップリング剤処理、日本電気硝子株式会社製
＜着色剤（Ｅ）＞
・カーボンブラック、Ｃａｂｏｔ　Ｂｌａｃｋ　Ｐｅａｒｌｓ　４３５０、Ｃａｂｏｔ　Ｃｏｒｐｏｒａｔｉｏｎ社製
＜その他の原料＞
・酸化防止剤、Ｉｒｇａｎｏｘ１０１０：Ｉｒｇａｎｏｘ１０１０、ペンタエリスリトールテトラキス［３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、ＢＡＳＦ株式会社製
・結晶化核剤、ＮＡ－１１：アデカスタブ　ＮＡ－１１、ナトリウム－２，２’－メチレンビス（４，６－ジ－ｔｅｒｔ－ブチルフェニル）ホスフェート、株式会社ＡＤＥＫＡ製
・離型剤、ＳＨ２００ＣＶ：ＳＨ２００ＣＶ－１３，０００ｓｃｔ、シリコーンオイル、東レ・ダウコーニング株式会社製
実施例１～４、比較例１～２
（スチレン系樹脂組成物及び成形体の製造）
　無機フィラー（Ｄ）以外の各成分を表１に記載する割合で配合し、ヘンシェルミキサーでドライブレンドした。続いて、３７ｍｍのシリンダー径を有する二軸スクリュー混練機（芝浦機械株式会社製：ＴＥＭ３７ＳＳ）を用いて、スクリュー回転数２２０ｒｐｍ、バレル温度２７０～２９０℃で、無機フィラー（Ｄ）を表１に記載する割合でサイドフィードしながら樹脂組成物を混練し、ペレットを作製した。得られたペレットを、熱風乾燥機を用いて１２０℃で５時間乾燥し、スチレン系樹脂組成物ペレットを得た。得られたスチレン系樹脂組成物ペレットを用いて評価を行った。評価方法は以下の通りである。
（１）シャルピー衝撃強さ（ノッチ有）
　上記のスチレン系樹脂組成物ペレットを用いて、射出成形機（住友重機械工業株式会社製：ＳＥ１００ＥＶ）により、シリンダー温度２９０℃、金型表面温度１５０℃の条件で、下記の成形体（厚さ４ｍｍ、縦１０ｍｍ×横８０ｍｍの短冊状）を成形した。得られた成形体にノッチングマシーンにてノッチ加工をして、ＩＳＯ　１７９：２０１０に準拠して、温度２３℃でシャルピー衝撃強さを測定した。数値が大きいほど、耐衝撃性（強度、機械強度）が良好であることを示す。
（２）誘電正接（ｔａｎδ）
　上記のスチレン系樹脂組成物ペレットを用いて、射出成形機（住友重機械工業株式会社製：ＳＥ１００ＥＶ）により、シリンダー温度２９０℃、金型表面温度１５０℃の条件で、下記の成形体（縦１．５ｍｍ×横１．５ｍｍ×高さ８０ｍｍの柱状）を成形した。得られた成形体を用いてＡＳＴＭ　Ｄ２５２０に準拠してネットワークアナライザ（アジレントテクノロジー株式会社製：８７５７Ｄ）及び２．４５ＧＨｚ用空洞共振器（ＥＭラボ株式会社開発製）を用いて、空洞共振摂動法にて２．４５ＧＨｚにおける誘電正接（ｔａｎδ）を測定した。数値が小さいほど電磁波の透過損失が低く、食材の加熱効率が高いことを示す。
（３）電子レンジ調理時耐熱性
　上記のスチレン系樹脂組成物ペレットを用いて、射出成形機（住友重機械工業株式会社製：ＳＥ１００ＥＶ）により、シリンダー温度２９０℃、金型表面温度１５０℃の条件で、下記の成形体（厚さ２ｍｍ、縦１００ｍｍ×横１５０ｍｍ×深さ１０ｍｍの箱形状）を成形した。得られた成形体に高含油食品である塩サバ（油含有率：１４質量％）を入れ、電子レンジにて８００Ｗ、６分間加熱したのち、内容物を取り出し、成形体内側の表面を観察し、下記の基準で評価した。
（評価基準）
　Ａ：表面が溶融していない（耐熱性が高い）
　Ｂ：表面が溶融している（耐熱性が低い）
（４）異物
　上記のスチレン系樹脂組成物ペレットを用いて、射出成形機（住友重機械工業株式会社製：ＳＥ１００ＥＶ）により、シリンダー温度２９０℃、金型表面温度１５０℃の条件で、下記の成形体（厚さ２ｍｍ、縦８０ｍｍ×横８０ｍｍのシート状）を成形した。得られた成形体の表面、裏面に存在する黒点（異物）の数を目視にて観察し、成形体表面１００ｃｍ2内に存在する異物数を算出した。数値が小さいほど外観が良好であることを示す。
（５）光沢度
　上記のスチレン系樹脂組成物ペレットを用いて、射出成形機（住友重機械工業株式会社製：ＳＥ１００ＥＶ）により、シリンダー温度２９０℃、金型表面温度１５０℃の条件で、下記の成形体（厚さ２ｍｍ、縦８０ｍｍ×横８０ｍｍのシート状）を成形した。得られた成形体表面の光沢度を、光沢計（日本電色工業株式会社製、ＶＧ２０００）を用いて、ＪＩＳ　Ｚ　８７４１：１９９７に記載された測定方法３に準拠して測定した。数値が大きいほど外観が良好であることを示す。
（６）色むら
　上記のスチレン系樹脂組成物ペレットを用いて、射出成形機（住友重機械工業株式会社製：ＳＥ１００ＥＶ）により、シリンダー温度２９０℃、金型表面温度１５０℃の条件で、下記の成形体（厚さ２ｍｍ、縦１００ｍｍ×横１５０ｍｍ×深さ１０ｍｍの箱形状）を成形した。得られた成形体の表面のうちランダムな１５ヵ所（１ヵ所の測定範囲は縦５ｍｍ×横１０ｍｍの範囲）を積分球分光光度計（ＧｒｅｔａｇＭａｃｂｅｔｈ社製：ＣＥ－７０００Ａ）を用いて測色し、Ｌ*、ａ*、ｂ*の平均値を算出した。その後、平均値と各測色点との色差ΔＥの平均値と標準偏差を算出し、ΔＥの標準偏差によって色むらを評価した。標準偏差が０．２未満のものは色むらが発生しておらず、標準偏差が０．２以上のものは色むらが発生しているとした。標準偏差が小さいほど色むらが発生していないことを示す。
（７）荷重たわみ温度
　上記のスチレン系樹脂組成物ペレットを用いて、射出成形機（住友重機械工業株式会社製：ＳＥ１００ＥＶ）により、シリンダー温度２９０℃、金型表面温度１５０℃の条件で、下記の成形体（厚さ４ｍｍ、縦１０ｍｍ×横８０ｍｍの短冊状）を成形した。得られた成形体を用いて、ＩＳＯ７５－１，２：２００４の測定方法に準拠し、荷重たわみ温度（荷重１．８ＭＰａ）を測定した。荷重たわみ温度が高いほど、耐熱性が良好であることを示す。
　スチレン系樹脂組成物及び成形体の評価結果を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　実施例の結果から、本発明のスチレン系樹脂組成物及び成形体は、色むらがなく、光沢に優れ、更に強度と耐熱性にも優れることがわかる。特に、耐衝撃性といった機械強度にも優れることがわかる。したがって、本発明のスチレン系樹脂組成物は、食器用の成形材料として有用である。また、電磁波の透過損失も低く、高含油食品を保存した際の耐熱性にも優れることから、特に電子レンジ調理器用の成形材料として有用である。
　上記に本発明の実施形態及び／又は実施例を幾つか詳細に説明したが、当業者は、本発明の新規な教示及び効果から実質的に離れることなく、これら例示である実施形態及び／又は実施例に多くの変更を加えることが容易である。従って、これらの多くの変更は本発明の範囲に含まれる。
　この明細書に記載の文献、及び本願のパリ条約による優先権の基礎となる出願の内容を全て援用する。

Claims (19)

  1. 　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）、相溶化剤（Ｃ）、無機フィラー（Ｄ）及び着色剤（Ｅ）を含有し、
    　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたとき、スチレン系エラストマー（Ｂ）の含有量が２．０～３０．０質量％であり、スチレン系樹脂組成物の全量を１００質量％としたとき、着色剤（Ｅ）の含有量が０．０００１～６．５質量％である、スチレン系樹脂組成物。
  2. 　スチレン系エラストマー（Ｂ）が、スチレン－ジエンブロック共重合体、水素添加スチレン－ジエンブロック共重合体、スチレン－ジエンランダム共重合体、水素添加スチレン－ジエンランダム共重合体、及びスチレン－オレフィンランダム共重合体からなる群より選ばれる少なくとも一種である、請求項１に記載のスチレン系樹脂組成物。
  3. 　スチレン系エラストマー（Ｂ）が、スチレン－ブタジエンブロック共重合体、水素添加スチレン－ブタジエンブロック共重合体、スチレン－ブタジエン－スチレンブロック共重合体、水素添加スチレン－ブタジエン－スチレンブロック共重合体、スチレン－イソプレンブロック共重合体、水素添加スチレン－イソプレンブロック共重合体、スチレン－イソプレン－スチレンブロック共重合体、水素添加スチレン－イソプレン－スチレンブロック共重合体、スチレン－ブタジエンランダム共重合体、水素添加スチレン－ブタジエンランダム共重合体、スチレン－エチレン－プロピレンランダム共重合体、及びスチレン－エチレン－ブチレンランダム共重合体からなる群より選ばれる少なくとも一種である、請求項１又は２に記載のスチレン系樹脂組成物。
  4. 　スチレン系エラストマー（Ｂ）を構成する、スチレンに由来する構成単位と、ジエン、水素添加ジエン及びオレフィンに由来する構成単位の合計との質量比［（スチレン）／（ジエン、水素添加ジエン、オレフィン）］が、２０／８０～７０／３０である、請求項２又は３に記載のスチレン系樹脂組成物。
  5. 　相溶化剤（Ｃ）が変性ポリフェニレンエーテルである、請求項１～４のいずれか１つに記載のスチレン系樹脂組成物。
  6. 　シンジオタクチック構造を有するスチレン系樹脂（Ａ）、スチレン系エラストマー（Ｂ）及び相溶化剤（Ｃ）の合計量を１００質量％としたときの相溶化剤（Ｃ）の含有量が０．４～５．０質量％である、請求項１～５のいずれか１つに記載のスチレン系樹脂組成物。
  7. 　無機フィラー（Ｄ）がガラスフィラーである、請求項１～６のいずれか１つに記載のスチレン系樹脂組成物。
  8. 　スチレン系樹脂組成物の全量を１００質量％としたときの無機フィラー（Ｄ）の含有量が５～５０質量％である、請求項１～７のいずれか１つに記載のスチレン系樹脂組成物。
  9. 　無機フィラー（Ｄ）がシラン系カップリング剤又はチタン系カップリング剤により処理されている、請求項１～８のいずれか１つに記載のスチレン系樹脂組成物。
  10. 　着色剤（Ｅ）が、カーボンブラック、無機顔料、有機顔料及び有機染料からなる群より選ばれる少なくとも一種である、請求項１～９のいずれか１つに記載のスチレン系樹脂組成物。
  11. 　無機顔料が、二酸化チタン、酸化鉄、ニッケルチタンイエロー、硫化亜鉛、硫酸バリウム、及び群青からなる群より選ばれる少なくとも一種である、請求項１０に記載のスチレン系樹脂組成物。
  12. 　有機顔料が、モノアゾ顔料、ペリレン顔料、キナクリドン顔料、及びフタロシアニン顔料からなる群より選ばれる少なくとも一種である、請求項１０に記載のスチレン系樹脂組成物。
  13. 　着色剤（Ｅ）が、カーボンブラック、無機顔料、有機顔料及び有機染料からなる群より選ばれる少なくとも一種であり、スチレン系樹脂組成物の全量を１００質量％としたときの着色剤（Ｅ）の含有量が０．０００１質量％以上であり、かつ、該カーボンブラックの含有量が２．５質量％以下であり、該無機顔料の含有量が３．０質量％以下であり、該有機顔料及び該有機染料の含有量の合計が１．０質量％以下である、請求項１～１２のいずれか１つに記載のスチレン系樹脂組成物。
  14. 　オレフィン系エラストマーを実質的に含まない、請求項１～１３のいずれか１つに記載のスチレン系樹脂組成物。
  15. 　請求項１～１４のいずれか１つに記載のスチレン系樹脂組成物からなる、食器用樹脂成形材料。
  16. 　請求項１～１４のいずれか１つに記載のスチレン系樹脂組成物からなる、電子レンジ調理器用樹脂成形材料。
  17. 　請求項１～１４のいずれか１つに記載のスチレン系樹脂組成物を含有する成形体。
  18. 　請求項１～１４のいずれか１つに記載のスチレン系樹脂組成物を含有する食器。
  19. 　請求項１～１４のいずれか１つに記載のスチレン系樹脂組成物を含有する電子レンジ調理器。
PCT/JP2022/000990 2021-01-22 2022-01-13 スチレン系樹脂組成物 WO2022158374A1 (ja)