WO2022071430A1 - 配線基板の製造方法、半導体装置の製造方法、及び樹脂シート - Google Patents

配線基板の製造方法、半導体装置の製造方法、及び樹脂シート Download PDF

Info

Publication number
WO2022071430A1
WO2022071430A1 PCT/JP2021/035957 JP2021035957W WO2022071430A1 WO 2022071430 A1 WO2022071430 A1 WO 2022071430A1 JP 2021035957 W JP2021035957 W JP 2021035957W WO 2022071430 A1 WO2022071430 A1 WO 2022071430A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
resin
wiring
resin sheet
manufacturing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2021/035957
Other languages
English (en)
French (fr)
Inventor
正也 鳥羽
一行 満倉
真樹 山口
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Corp
Original Assignee
Showa Denko Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Showa Denko Materials Co Ltd filed Critical Showa Denko Materials Co Ltd
Priority to CN202180067236.5A priority Critical patent/CN116325127A/zh
Priority to KR1020237010627A priority patent/KR20230074735A/ko
Priority to US18/247,077 priority patent/US20240030044A1/en
Priority to JP2022554059A priority patent/JP7848687B2/ja
Publication of WO2022071430A1 publication Critical patent/WO2022071430A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

配線基板２０の製造方法は、表面に銅層２を設けた支持体１上に有機樹脂中にガラスクロスを配置した樹脂シート３が取り付けられた構造体１ａを準備する工程と、樹脂シート３の表面側であってガラスクロスが存在しない第１樹脂層領域４に対してエキシマレーザにより凹部７を形成する工程と、樹脂シート３の表面から支持体１上の銅層２に到る開口部８を形成する工程と、凹部７及び開口部８に銅層１０～１２を形成して配線層１３を形成する工程と、を備える。

Description

配線基板の製造方法、半導体装置の製造方法、及び樹脂シート
　本発明は、配線基板の製造方法、半導体装置の製造方法、及び樹脂シートに関する。より詳しくは、微細化又は高密度化の要求が高い配線基板及び半導体装置を効率よく且つ低コストに製造するための製造方法に関する。
　半導体パッケージの高密度化及び高性能化を目的に、異なる性能のチップを一つのパッケージに混載する実装形態が提案されており、コスト面に優れたチップ間の高密度インターコネクト技術が重要になっている（例えば特許文献１参照）。
　パッケージ上に異なるパッケージをフリップチップ実装によって積層することで接続するパッケージ・オン・パッケージがスマートフォン及びタブレット端末に広く採用されている（例えば非特許文献１及び非特許文献２参照）。さらに高密度で実装するための形態として、高密度配線を有する有機基板を用いたパッケージ技術（有機インターポーザ）、スルーモールドビア（ＴＭＶ）を有するファンアウト型のパッケージ技術（ＦＯ－ＷＬＰ）、シリコン又はガラスインターポーザを用いたパッケージ技術、シリコン貫通電極（ＴＳＶ）を用いたパッケージ技術、基板に埋め込まれたチップをチップ間伝送に用いるパッケージ技術等が提案されている。
　特に有機インターポーザ又はＦＯ―ＷＬＰでは、半導体チップ同士を並列して搭載する場合には、高密度で導通させるために微細配線層が必要となる（例えば特許文献２参照）。
特表２０１２―５２９７７０号公報 米国特許出願公開第２００１／０２２１０７１号明細書
Ａｐｐｌｉｃａｔｉｏｎ ｏｆ Ｔｈｒｏｕｇｈ Ｍｏｌｄ Ｖｉａ （ＴＭＶ） ａｓ ＰｏＰ Ｂａｓｅ Ｐａｃｋａｇｅ， Ｅｌｅｃｔｒｏｎｉｃ Ｃｏｍｐｏｎｅｎｔｓ ａｎｄ Ｔｅｃｈｎｏｌｏｇｙ Ｃｏｎｆｅｒｅｎｃｅ （ＥＣＴＣ）， ２００８ Ａｄｖａｎｃｅｄ Ｌｏｗ Ｐｒｏｆｉｌｅ ＰｏＰ Ｓｏｌｕｔｉｏｎ ｗｉｔｈ Ｅｍｂｅｄｄｅｄ Ｗａｆｅｒ Ｌｅｖｅｌ ＰｏＰ （ｅＷＬＢ－ＰｏＰ） Ｔｅｃｈｎｏｌｏｇｙ， ＥＣＴＣ， ２０１２
　上記の微細配線層の形成には、スパッタによるシード層形成、レジスト形成、電気めっき、レジスト除去、及び、シード層除去の工程が必要となり、製造プロセスが煩雑化してしまっている。そこで、より簡素化された微細配線層の形成方法が望まれている。
　そこで、本発明は、簡素化された微細配線層の形成方法を提供することを目的とする。
　本発明は、一側面として、配線基板の製造方法に関する。この配線基板の製造方法は、表面に金属層を設けた支持体上に又は支持体に設けた内蔵配線層上に有機樹脂中にガラスクロスを配置した樹脂シートが取り付けられた構造体を準備する工程と、樹脂シートの表面側であってガラスクロスが存在しない第１樹脂層領域に対してエキシマレーザにより凹部を形成する工程と、樹脂シートの表面から支持体上の金属層に到る開口部を形成する工程と、凹部及び開口部に配線層を形成する工程と、を備える。
　この配線基板の製造方法では、有機樹脂中にガラスクロスを配置した樹脂シートを用い、その樹脂シートにおいてガラスクロスが存在しない第１樹脂層領域にエキシマレーザで凹部を形成し、その凹部等に配線層を形成している。この場合、エキシマレーザによる凹部の微細加工が可能となり、微細配線層を容易に形成することができる。この製造方法において、凹部を形成する工程と開口部を形成する工程は、何れの工程を先に行ってもよく、また同時に行ってもよい。また、この製造方法において、凹部及び開口部に配線層を形成するには、めっき処理を用いてもよいし、他の方法を用いてもよい。
　本発明は、別側面として、もう一つの配線基板の製造方法に関する。この配線基板の製造方法は、表面に金属層を設けた支持体上に又は支持体に設けた内蔵配線層上に外側に位置する第１樹脂層領域と第１樹脂層領域より弾性率が高く内側に位置する高弾性層領域とが順に形成された樹脂シートが取り付けられた構造体を準備する工程と、樹脂シートの表面側であって第１樹脂層領域にレーザ又はインプリントにより凹部を形成する工程と、樹脂シートの表面から支持体上の金属層に到る開口部を形成する工程と、凹部及び開口部に配線層を形成する工程と、を備える。
　この配線基板の製造方法では、外側に位置する第１樹脂層領域と高弾性層領域とが設けられた樹脂シートを用い、その樹脂シートにおいて第１樹脂層領域にレーザ又はインプリントで凹部を形成し、その凹部等に配線層を形成している。この場合、レーザ又はインプリントによる凹部の微細加工が可能となり、微細配線層を容易に形成することができる。この製造方法において、凹部を形成する工程と開口部を形成する工程は、何れの工程を先に行ってもよく、また同時に行ってもよい。また、この製造方法において、凹部及び開口部に配線層を形成するには、めっき処理を用いてもよいし、他の方法を用いてもよい。また、この製造方法において、高弾性層領域は、無機繊維及び有機繊維の少なくとも一方が有機樹脂材料中に配置されることにより形成されていてもよい。無機繊維は、ガラス繊維、セラミック繊維、及び炭素繊維の少なくとも１つであってもよく、有機繊維は、アラミド繊維、及びポリエチレン繊維の少なくとも１つであってもよい。
　上記何れかの配線基板の製造方法において、樹脂シートの表面側における第１樹脂層領域の厚みは２０μｍ以下であってもよい。この場合、微細な配線層を形成する層領域を薄くして、製造される配線基板の低背化を図ることができる。この場合において、第１樹脂層領域の厚みは５μｍ以上であってもよい。これにより、適切な深さの凹部を形成し、導通性に優れた微細な配線層を形成することができる。
　上記何れかの配線基板の製造方法において、第１樹脂層領域に形成される凹部のライン幅は０．５μｍ以上５μｍ以下であってもよい。この場合、導通性に優れた微細な配線層を形成することができる。
　上記何れかの配線基板の製造方法において、樹脂シートは、第１樹脂層領域とは逆側に第２樹脂層領域を有しており、構造体を準備する工程では、支持体上又は内蔵配線層上に樹脂シートを第２樹脂層領域によって貼り付けて、構造体を準備してもよい。この場合、構造体の準備をラミネート等の簡易な手法により行うことができ、製造方法を簡素化することができる。なお、構造体を準備する工程では、支持体上又は内蔵配線層上に樹脂シートが予め取り付けられた構造体を準備し、その後の工程に用いてもよい。
　上記何れかの配線基板の製造方法において、第１樹脂層領域にエキシマレーザにより凹部を形成する場合、エキシマレーザのパルス幅が１０ナノ秒以上５０ナノ秒以下であってもよく、エキシマレーザの出力が１０ｍＪ／パルス以上１０００ｍＪ／パルス以下であってもよい。この場合、より微細な凹部を容易に形成することができる。
　上記何れかの配線基板の製造方法において、配線層を形成する工程では、凹部及び開口部にめっき金属層を形成して配線層を形成し、樹脂シートは、めっき金属層を形成するためのシード層を構成する金属材料と配位結合が可能な複素芳香族環からなる成分を含んでもよい。この場合、より微細な配線層を形成し易くなる。なお、シード層を構成する金属材料と配位結合が可能な複素芳香族環からなる成分は、例えば、マレイミド化合物、ビスマレイミド化合物、トリアゾール化合物、ベンゾトリアゾール化合物、及び、ベンゾオキサゾール化合物からなる群から選ばれる少なくとも１つの化合物であってもよい。
　上記何れかの配線基板の製造方法において、樹脂シート又は樹脂シートを覆う被覆層は、無機染料、無機顔料、有機染料、及び有機顔料の少なくとも１つからなるレーザ光吸収性着色成分を含んでもよい。この場合、レーザによる凹部の加工をより確実に行うことができる。なお、レーザ光吸収性着色成分は、例えば、黒鉛、グラフェン、カーボンナノチューブ、カーボンファイバー、カーボンブラック、フタロシアニン、シアニン、アルカリ土類金属、及び、金属錯体の少なくとも１つであってもよい。
　上記何れかの配線基板の製造方法において、配線層を形成する工程では、凹部及び開口部に無電解めっきによるシード層を設けてめっき金属層を形成して配線層を形成し、樹脂シートは、無電解めっきを形成するための触媒を含んでもよい。この場合、より微細な配線層を形成し易くなる。なお、無電解めっきを形成するための触媒は、パラジウム粒子、パラジウム錯体、銅粒子、及び、銅錯体の少なくとも１つであってもよい。
　上記何れかの配線基板の製造方法において、配線層を形成する工程は、凹部及び開口部に導電性材料を充填すると共に凹部及び開口部を除く第１樹脂層領域の表面上に導電性材料を設けて、導電層を形成する工程と、導電性を平坦化する工程と、を有してもよい。平坦化する工程では、第１樹脂層領域の表面上に設けられた導電層の第１部分を少なくとも研磨し、凹部及び開口部に充填された導電性材料から形成される導電層の第２部分から配線層を形成してもよい。この場合、微細な配線層をより効率的に形成することができる。
　上記何れかの配線基板の製造方法は、支持体上に、内蔵配線層を少なくとも一層有する内蔵配線部を形成する工程を更に備えてもよく、構造体を準備する工程は、当該内蔵配線部上に樹脂シートを貼り付けることにより取り付けを行い、構造体を準備してもよい。この場合、例えば、内蔵配線層をビルドアップ材から構成し、表面の微細な配線層をプリプレグ等の有機樹脂材料から構成するといったように異なる材料を用いて最適な層構成の配線基板を作製することができる。また、配線基板の設計自由度を高めることもできる。
　上記何れかの配線基板の製造方法は、配線層が形成された樹脂シートの上に別の樹脂シートを取り付ける工程と、別の樹脂シートの第１樹脂層領域に対してレーザにより別の凹部を形成する工程と、別の樹脂シートの表面から開口部のめっき金属層又は配線層に到る別の開口部を形成する工程と、別の凹部及び別の開口部に別のめっき金属層を形成して別の配線層を形成する工程と、を更に備え、別の樹脂シートを取り付ける工程、別の凹部を形成する工程、別の開口部を形成する工程、及び、別の配線層を形成する工程を少なくとも一回以上繰り返してもよい。この場合、微細な配線層を２層以上備えた配線基板の製造方法を簡素化することができる。
　上記何れかの配線基板の製造方法において、配線層を形成する工程は、少なくとも開口部及び凹部に対してデスミア処理を行う工程と、少なくとも開口部及び凹部に対して無電解めっきによりシード層を形成する工程と、シード層上に電解めっきを施してめっき金属層を形成する工程と、第１樹脂層領域の表面とシード層とめっき金属層とが平坦化するように第１樹脂層領域の表面上のシード層及びめっき金属層を除去する工程と、を有してもよい。この場合、微細な配線層の導通部分をより確実に形成することができる。
　本発明は、更に別の側面として、半導体装置の製造方法に関する。この半導体装置の製造方法は、上記何れかの配線基板の製造方法によって製造される配線基板を準備する工程と、配線層又は別の配線層上に半導体素子を実装し、半導体素子を配線層又は別の配線層に電気的に接続する工程と、備える。この場合、微細な配線層を備えた配線基板を有する半導体装置を簡素化された方法で作製することができる。また、簡素化された方法で作製するため、製造歩留まりの向上又は製造品のコスト低減等を図ることも可能となる。更に、これに限定されないが、複数の半導体素子（チップ）を実装する場合（特に高密度に実装する場合）、半導体素子同士の間を伝送性に優れた微細な配線層で接続することができ、より性能の優れた小型の半導体装置を提供することが可能となる。
　本発明は、更に別の側面として、樹脂シートに関する。この樹脂シートは、上記の何れかの配線基板の製造方法に使用される樹脂シートであって、外側に位置する第１樹脂層領域と、第１樹脂層領域より弾性率が高く内側に位置する高弾性層領域又はガラスクロスを有し内側に位置する高弾性層領域と、を備える。このような樹脂シートを予め設けておくことにより、上述した配線基板の製造方法及び半導体装置の製造方法をより簡素化して、製造される配線基板及び半導体装置の歩留まり向上又は製造品のコスト低減等を図ることが可能となる。
　上記の樹脂シートは、第１樹脂層領域とは高弾性層領域を介して反対側に位置する第２樹脂層領域を更に備えてもよく、第２樹脂層領域が粘着性を有していてもよい。この場合、樹脂シートを含む構造体をより容易に形成することが可能となり、上述した配線基板の製造方法及び半導体装置の製造方法をより簡素化することができる。
　本発明によれば、微細な配線層を備えた配線基板及び半導体装置の簡素化された製造方法を提供することができる。
図１の（ａ）～（ｄ）は、本発明の一実施形態に係る配線基板の製造方法の一部を示す図である。 図２の（ａ）～（ｃ）は、本発明の一実施形態に係る配線基板の製造方法の一部を示す図であり、図１の工程の後に続いて行われる工程を示す図である。 図３は、図１及び図２に示す製造方法によって製造される配線基板に半導体素子を実装した半導体装置の一例を示す図である。 図４の（ａ）は、変形例に係る配線基板を示す図であり、図４の（ｂ）は、変形例に係る半導体装置を示す図である。
　以下、図面を参照しながら本発明に係る実施形態について詳細に説明する。以下の説明では、同一又は相当部分には同一の符号を付し、重複する説明は省略する。また、上下左右等の位置関係は、特に断らない限り、図面に示す位置関係に基づくものとする。更に、図面の寸法比率は図示の比率に限られるものではない。
　本明細書の記載及び請求項において「左」、「右」、「正面」、「裏面」、「上」、「下」、「上方」、「下方」等の用語が利用されている場合、これらは、説明を意図したものであり、必ずしも永久にこの相対位置である、という意味ではない。また、「層」との語は、平面図として観察したときに、全面に形成されている形状の構造に加え、一部に形成されている形状の構造も包含される。また、本明細書において「工程」との語は、独立した工程だけではなく、他の工程と明確に区別できない場合であってもその工程の所期の作用が達成されれば、本用語に含まれる。また、「～」を用いて示された数値範囲は、「～」の前後に記載される数値をそれぞれ最小値及び最大値として含む範囲を示す。
　本発明の一実施形態に係る配線基板の製造方法及び半導体装置の製造方法について説明する。本実施形態に係る配線基板の製造方法及び半導体装置の製造方法は、微細化及び多ピン化が必要とされる形態に適用されることが好ましいが、これに限定されない。また、本実施形態に係る製造方法は、異種チップを混載するためのインターポーザが必要なパッケージ形態に適用することが好ましいが、これに限定されない。なお、以下では説明を容易にするため、実装される半導体素子が１つの場合で説明しているが、２以上（又は２種以上）の半導体素子が実装される形態でも同様である。
＜構造体の準備工程＞
　図１及び図２は、本実施形態に係る配線基板の製造方法を示す図である。図１の（ａ）に示すように、まず、表面に銅層２（金属層）を設けた支持体１上に樹脂シート３が取り付けられた構造体１ａを準備する。樹脂シート３は、例えば、ガラスクロスに有機樹脂を含浸させたシートであり、表面側であってガラスシートが存在しない第１樹脂層領域４と、第１樹脂層領域４の内側に位置する高弾性層領域５と、第１樹脂層領域４とは高弾性層領域５（ガラスクロス）を介して反対側に位置する第２樹脂層領域６とを、有している。樹脂シート３は、例えば有機樹脂中にガラスクロス等の高弾性体が配置されている構成であればよく、ガラスクロスの両面を樹脂シートでラミネートした構成のものであってもよい。第２樹脂層領域６は、例えば粘着性を有しており、第２樹脂層領域６を介して支持体１の銅層２に樹脂シート３が貼り付けられることで取り付けられる。構造体１ａの準備工程では、支持体１上の銅層２に樹脂シート３を貼り付けてもよいし、樹脂シート３が銅層２を介して支持体１上に予め取り付けられた構造体１ａを用意しておき、それを用いてもよい。
　支持体１は、特に限定されないが、例えば、シリコン板、ガラス板、ＳＵＳ板、ガラスクロス入り基板、又は、半導体素子入り封止樹脂基板等であり、高剛性からなる基板である。支持体１の厚みは０．２ｍｍ以上２．０ｍｍ以下であってもよい。支持体１が０．２ｍｍ以上であることによりハンドリング性をよくすることができ、支持体１が２．０ｍｍ以下であることにより、配線基板を低背化しやすくなり、また材料費を低減してコスト低減を行うことが可能となる。また、支持体１はウェハ状又はパネル状の何れの形態を有してよく、支持体１のサイズは特に限定されない。支持体１は、直径２００ｍｍ、直径３００ｍｍ若しくは直径４５０ｍｍのウェハ、又は、一辺が３００ｍｍ以上７００ｍｍ以下の矩形パネルであってもよい。
　樹脂シート３は、例えばプリプレグ等の半硬化されたフィルム状部材である。樹脂シート３に含まれる有機樹脂材料は、電気絶縁性を確保するため、熱硬化性材料及び熱可塑性材料の少なくとも一方を含んでもよい。ここで用いる熱硬化性材料は、例えばエポキシ樹脂であり、熱可塑性樹脂は、例えば、アクリル樹脂であるが、これらに限定されない。樹脂シート３に含まれる有機樹脂材料は、膜厚平坦性とコストの観点から、フィルム状の複合体であってもよい。また、有機樹脂材料は、微細な凹部を形成できる点で、熱硬化性材料を含んでいてもよい。熱硬化性材料に含有するフィラ（充填材）のサイズは、平均粒径５００ｎｍ以下であってもよい。熱硬化性材料はフィラを含有しなくてもよい。樹脂シート３の第１樹脂層領域４及び第２樹脂層領域６は、このような有機樹脂材料から形成され、ガラスクロスが存在しない領域となっている。第１樹脂層領域４は、後述する凹部の形成工程において、微細なトレンチ構造を形成するため、その膜厚が２０μｍ以下であってもよく、１０μｍ以下であってもよい。第１樹脂層領域４の膜厚は、微細配線構造における導通性を確保するため、５μｍ以上であってもよい。
　樹脂シート３に含まれるガラスクロスは、ガラス繊維を含む織布又は不織布から構成される。ガラス繊維は、例えばＥガラス、Ｓガラス、又は石英ガラスであってもよい。ガラスクロスの厚みは、例えば０．０１μｍ以上０．２μｍ以下であってもよい。このようなガラスクロスが上述した有機樹脂材料に含浸されて、高弾性層領域５を構成する。即ち、高弾性層領域５は、ガラスクロスと、ガラスクロスに含浸又は入り込んでいる有機樹脂材料とから構成される。高弾性層領域５は、ガラス等の剛性材料を含むため、第１樹脂層領域４及び第２樹脂層領域６よりも弾性率、具体的にはヤング率が高くなるように構成されている。なお、ガラス繊維に代えて、他の無機繊維及び有機繊維の少なくとも一方を有機樹脂材料に含浸させて高弾性層領域５を形成してもよい。無機繊維は、例えば、セラミック繊維又は炭素繊維等であり、有機繊維は、例えば、アラミド繊維又はポリエチレン繊維である。
　樹脂シート３に含まれる有機樹脂材料は、後の工程で形成するシード層との密着性を高めるため、例えばマレイミド化合物、ビスマレイミド化合物、トリアゾール化合物、ベンゾトリアゾール化合物、ベンゾオキサゾール化合物等の金属と配位結合ができる複素芳香族環からなる成分を含んでいてもよい。ここでいう金属は、シード層を構成する金属材料である。本成分は、フィラ表面処理剤に含めてもよい。なお、後述するシード層を無電解めっきで形成する場合、樹脂シート３に、無電解めっきで触媒となるパラジウム粒子、パラジウム錯体、銅粒子、銅錯体を含ませてもよい。
　樹脂シート３は、レーザ光との吸収性を高めるため、例えば黒鉛、グラフェン、カーボンナノチューブ、カーボンファイバー、カーボンブラック等の無機染料若しくは無機顔料、又は、フタロシアニン系、シアニン系、アルカリ土類金属塩、金属錯体等の有機染料若しくは有機顔料からなるレーザ光吸収性着色成分を含んでいてもよい。本成分はフィラ表面処理剤に含めてもよい。
　樹脂シート３は、上述した構成を備えており、例えばその厚みが１０μｍ以上１００μｍ以下であってもよい。樹脂シート３の厚みが１０μｍ以上であることにより、ハンドリング性を高めることができる。また、樹脂シート３の厚みが１００μｍ以下であることにより、製造される配線基板または半導体装置を薄型パッケージにすることができる。
　樹脂シート３は、例えば、ガラスクロスを有機樹脂（ワニス）中に含浸させて第１樹脂層領域４、高弾性層領域５、及び第２樹脂層領域６を有する構造に形成してもよいし、第１樹脂層領域４に対応する樹脂層と、第２樹脂層領域６に対応する樹脂層との間にガラスクロスを配置してラミネート又はプレスすることにより形成してもよい。樹脂シート３のラミネート等の形成方法としては、真空ラミネート、ロールラミネート、真空ロールラミネート、大気圧プレス、又は真空プレスなどを用いることができる。なお、真空プレスを用いた場合、樹脂シート３に含まれる熱硬化性材料の酸化を容易に抑制でき、膜厚平坦性をより向上することが可能である。また、樹脂シート３の形成の際の温度は、樹脂シート３に含まれる熱硬化性材料が熱硬化する温度であってもよく、例えば１００℃以上２５０℃以下であってもよい。形成温度を１００℃以上とすることにより、樹脂シート３の有機樹脂材料のタック性を弱めて取り扱い性を向上することができる。形成温度を２５０℃以下とすることにより、樹脂シート３の反りを抑制することができる。
　このような樹脂シート３としては、例えば、「ＭＣＬ－Ｅ－７０５Ｇ、厚み０．４ｍｍ又は０．６ｍｍ、２５５ｍｍ角（日立化成株式会社製）」、又は「Ｒ－１７６６　厚み０．４ｍｍ又は０．６ｍｍ、２５５ｍｍ角」、「Ｒ－５７１５ＥＳ　厚み０．４ｍｍ又は０．６ｍｍ、２５５ｍｍ角」、「Ｒ－５６７０Ｋｊ　厚み０．４ｍｍ又は０．６ｍｍ、２５５ｍｍ角（以上、パナソニック株式会社製）」、又は、「ＧＨＰＬ８３０ＮＳ　厚み０．４ｍｍ又は０．６ｍｍ　２５５ｍｍ角」、「８３０ＮＳ　厚み０．４ｍｍ又は０．６ｍｍ、２５５ｍｍ角」、「８３０ＮＳＦ　厚み０．４ｍｍ又は０．６ｍｍ、２５５ｍｍ角（以上、三菱ガス化学株式会社製）」を用いることが可能である。
　樹脂シート３の表面（凹部を形成する側）に被覆層を設けることもできる。被覆層は、例えば、ポリエチレンテレフタレート（ＰＥＴ）樹脂、ポリエチレンナフタレート（ＰＥＮ）樹脂、ポリエーテルエーテルケトン（ＰＥＥＫ）樹脂、ポリイミド（ＰＩ）樹脂等を含む有機樹脂フィルム、又は、Ｃｕ箔、Ｎｉ箔、ＳＵＳ箔等の金属箔であってもよい。レーザ光の吸収を高めるため、被覆層を構成する有機樹脂フィルムは、黒鉛、グラフェン、カーボンナノチューブ、カーボンファイバー、カーボンブラック等の無機染料若しくは無機顔料、又は、フタロシアニン系、シアニン系、アルカリ土類金属塩、金属錯体等の有機染料若しくは有機顔料からなるレーザ光吸収性着色成分を含んでいてもよい。また、前記金属箔の表面は、黒化処理されていてもよい。
＜凹部の形成工程＞
　次に、構造体１ａの準備工程が終了すると、図１の（ｂ）に示すように、樹脂シート３の表面側であってガラスクロスが存在しない第１樹脂層領域４に対してエキシマレーザにより複数の凹部７を形成する。凹部７は、第１樹脂層領域４の表面に対して、第１樹脂層領域４の厚さ方向に凹んだ部位をいい、この凹んだ部位の内壁（側壁及び底壁等）を含んでいる。凹部７は、図示の左右方向に沿った幅で、図示垂直方向等に伸びる溝のように形成されており、平面方向において微細配線に対応する形状を有している。熱硬化性材料又は熱可塑性材料から形成される第１樹脂層領域４に凹部を形成するには、微細化の観点からはエキシマレーザを用いて加工してもよいが、炭酸ガスレーザ若しくはＵＶ－ＹＡＧレーザを用いた加工、又は、インプリントを用いてもよい。
　凹部の形成工程では、開口幅が０．５μｍ以上２０μｍ以下となるように凹部７を形成してもよく、微細化の観点からは、開口幅が０．５μｍ以上５μｍ以下となるように凹部７を形成してもよい。これにより、微細な配線層を形成して高密度化した半導体装置を提供することができる。このような微細な開口幅の凹部を形成するには、上述したようにエキシマレーザを用いてもよい。使用されるエキシマレーザの媒質は、アルゴン・フッ素(ＡｒＦ)又はクリプトン・フッ素(ＫｒＦ)であり、汎用性の観点からは、ＫｒＦを媒質としたエキシマレーザを用いてもよい。また、エキシマレーザによる加工条件として、パルスエネルギーは２０ｍＪ以上１００ｍＪ以下であってもよい。パルス繰り返し周波数は、１Ｈｚ以上４０００Ｈｚ以下であってもよい。パルス幅は、１０ナノ秒以上５０ナノ秒以下であってもよい。レーザ照射量は、０より大きく１０００ｍＪ／ｃｍ２以下であってもよい。エキシマレーザの出力は、１０ｍＪ／パルス以上１０００ｍＪ／パルス以下であってもよい。
　凹部の形成工程では、凹部７を形成した後、第１樹脂層領域４を含む樹脂シート３を更に加熱硬化させてもよい。この際の加熱温度は１００℃以上２５０℃以下であってもよく、加熱時間は３０分以上３時間以下であってもよい。なお、凹部７は、高弾性層領域５には到達しないように構成されている。
＜開口部の形成工程＞
　次に、凹部７の形成が終了すると、図１の（ｃ）に示すように、樹脂シート３の表面から支持体1の銅層２に到る開口部８を形成する。開口部の形成工程では、樹脂シート３においてガラスクロスを含んで構成される高弾性層領域５と、有機樹脂材料から構成される第１樹脂層領域４及び第２樹脂層領域６とをまとめて貫通して開口部８が形成される。開口部８を形成する方法としては、例えば、炭酸ガスレーザ加工又はドリル加工を用いることができるが、微細化の観点からは、炭酸ガスレーザを用いてもよい。
　開口部の形成工程では、例えば、直径が３０μｍ以上２００μｍ以下の開口径を有する開口部８を形成する。このような大きさの開口部８により、高密度化を実現する半導体装置を提供でき、また、微細配線層を有する半導体装置を良好な歩留まり、かつ低コストで製造できる。開口部の形成工程は、上述した凹部の形成工程より先に行ってもよく、後に行ってもよく、又は、同時に行ってもよく、その順番は特に限定されない。
<デスミアする工程>
　次に、凹部７及び開口部８の形成が終了すると、レーザ開口で形成されたスミアを除去する目的で、デスミアする工程を行う。デスミア液は、市販の前処理液及びデスミア液を用いてもよい。前処理液としては、例えば膨潤液（株式会社アトテックジャパン製、商品名：スウェリングディップセキュリガント）を用いることができる。デスミア液として、例えば粗化液（株式会社アトテックジャパン製、商品名：コンセントレートコンパクトＣＰ）を用いることができる。デスミア後の中和に使用する薬液として、例えば中和液（株式会社アトテックジャパン製、商品名：リダクションセキュリガント）を用いることができる。
　デスミア処理における膨潤条件として、膨潤液の温度は５０℃以上８０℃以下であり、浸漬時間１分以上３０分以下であってもよい。膨潤処理後に、凹部７及び開口部８等を純水または市水によって洗浄してもよい。また、膨潤処理後、デスミア液で粗化処理する工程を実施する。デスミア条件として、デスミア液の温度は３０℃以上８０℃以下であり、浸漬時間１分以上３０分以下で実施されてもよい。デスミア処理後、純水または市水によって洗浄してもよい。デスミア液によって粗化後、純水または市水によってドラッグアウト工程を実施する。ドラッグアウト温度は２５℃以上５０℃以下であり、浸漬時間は１分以上５分以下であってもよい。そして、ドラッグアウト後、中和工程を実施する。中和温度は２５℃以上５０℃以下であり、浸漬時間は１分以上１０分以下であってもよい。中和処理後、純水または市水によって洗浄してもよい。以上により、デスミア処理が終了する。
＜シード層の形成工程＞
　デスミア処理が終了すると、図１（ｄ）に示すように、第１樹脂層領域４の表面と、凹部７の側壁及び底壁と、開口部８の側壁と、開口部８に露出する銅層２の表面とにシード層９を形成する工程を行う。シード層の形成工程では、銅ペーストを用いた方法、スパッタリング方法、又は無電解めっき法を用いて、シード層９を形成することができる。パネル化に適した方法としては、無電解めっき法を用いることができる。
　シード層９を形成するには、まず、無電解銅めっきの触媒となるパラジウムを、第１樹脂層領域４の表面と、凹部７の側壁及び底壁と、開口部８の側壁と、開口部８に露出する銅層２の表面（以下「第１樹脂層領域４の表面等」とも記す）とに吸着させるため、第１樹脂層領域４の表面等を前処理液で洗浄する。前処理液は、例えば水酸化ナトリウム又は水酸化カリウムを含む市販のアルカリ性前処理液である。前処理は、水酸化ナトリウム又は水酸化カリウムの濃度が１％以上３０％以下の間で実施してもよく、前処理液への浸漬時間が１分以上６０分以下の間で実施してもよく、前処理液への浸漬温度が２５℃以上８０℃以下の間で実施されてもよい。前処理した後、余分な前処理液を除去するため、市水、純水、超純水又は有機溶剤で洗浄してもよい。
　前処理液を除去した後、第１樹脂層領域４の表面等からアルカリイオンを除去するために、酸性水溶液で浸漬洗浄する。浸漬洗浄は、酸性水溶液として硫酸水溶液を用いて実施されてもよく、濃度が１％以上２０％以下の間、浸漬時間が１分以上６０分以下の間で実施されてもよい。酸性水溶液を除去するため、市水、純水、超純水又は有機溶剤で洗浄してもよい。その後、酸性水溶液で浸漬洗浄がなされた後の第１樹脂層領域４等にパラジウムを付着させる。パラジウムの付着には、市販のパラジウムースズコロイド溶液、パラジウムイオンを含む水溶液、又はパラジウムイオン懸濁液等を用いてもよいが、改質層に効果的に吸着するパラジウムイオンを含む水溶液を用いてもよい。パラジウムイオンを含む水溶液に浸漬する際、パラジウムイオンを含む水溶液の温度が２５℃以上８０℃以下の間で、吸着させるための浸漬時間が１分以上６０分以下の間で実施されてもよい。パラジウムイオンを吸着させた後、余分なパラジウムイオンを除去するため、市水、純水、超純水又は有機溶剤で洗浄してもよい。
　続いて、パラジウムイオンを吸着した後、パラジウムイオンを触媒として作用させるための活性化を行う。パラジウムイオンを活性化させる試薬は、市販の活性化剤（活性化処理液）を用いてもよい。パラジウムイオンを活性化させるために浸漬する活性化剤の温度は、２５℃以上８０℃以下の間であり、活性化させるために浸漬する時間は、１分以上６０分以下の間であってもよい。パラジウムイオンを活性化した後、余分な活性化剤を除去するため、市水、純水、超純水又は有機溶剤で洗浄してもよい。その後、パラジウムを触媒として、無電解めっきによりシード層９を形成する。シード層９は、例えば、銅層、ニッケル層、銅ニッケル合金層、ニッケルリン合金層、及び銅ニッケルリン合金層からなる群から選ばれる無電解めっき層である。コストの観点から、シード層９の材質は、銅層であってもよい。
　シード層９として銅層を形成する場合、無電解めっき液として市販のめっき液を使用すればよく、例えば、無電解銅めっき液（株式会社アトテックジャパン製、商品名：カッパーソリューションプリントガントＭＳＫ）を用いることができる。無電解銅めっきの形成は、２０℃以上４０℃以下の間で無電解銅めっき液中で実施される。シード層９の厚さは、０．１ｎｍ以上５００ｎｍ以下であってもよく、０．１ｎｍ以上４００ｎｍ以下であってもよく、０．１ｎｍ以上３００ｎｍ以下であってもよい。シード層９の厚さを０．１ｎｍ以上にすることで、その後の電解めっきにおいて均一な厚さで配線を形成し易くなる。他方、シード層９の厚さを５００ｎｍ以下にすることで、シード層９のエッチング工程において配線への過剰なエッチングを防ぐことができ、微細な配線を歩留まり良く形成できる。
　無電解めっきを行った後、余分なめっき液を除去するため、水又は有機溶剤で洗浄してもよい。無電解めっき後、シード層９と第１樹脂層領域４の表面との密着力を高めるため、熱硬化（アニーリング：加熱による時効硬化処理）を行ってもよい。熱硬化温度が８０℃以上２００℃以下となるように加熱してもよい。より反応性を早めるために、熱硬化温度が１２０℃以上２００℃以下となるように加熱してもよく、熱硬化温度が１２０℃以上１８０℃以下となるように加熱してもよい。熱硬化時間は、５分以上６０分以下であってもよく、１０分以上６０分以下であってもよく、２０分以上６０分以下であってもよい。
＜銅層の形成工程＞
　シード層の形成工程が終了すると、図２の（ａ）に示すように、シード層９上に電解銅めっき（導電性材料）により銅層１０，１１，１２（めっき金属層、導電層）を形成する工程を行う。より具体的には、無電解銅めっきで形成した銅層をシード層９として、その上に電解銅めっきにより、銅層１０～１２を形成する。なお、本実施形態では、銅層１０～１２を形成する方法として、電解銅めっきを用いるが、これ以外に、例えば、無電解めっきを用いてもよい。
　銅層の形成工程では、銅層１０（第２部分）が第１樹脂層領域４の表面に設けられた凹部７内に充填され、銅層１１（第２部分）が第１樹脂層領域４の表面から銅層２に到るように設けられた開口部８内に充填され、銅層１２（第１部分）が凹部７及び開口部８を除く第１樹脂層領域４の表面に形成される。銅層１０が凹部７内に充填され、また銅層１１が開口部８内に充填されることで、この後の工程で第１樹脂層領域４の凹部７及び開口部８を除く表面から、銅層１２、シード層、パラジウム吸着層を除去するだけで、第１樹脂層領域４の表面を削ることなく、第１樹脂層領域４の表面と凹部７及び開口部８にそれぞれ形成された銅層１０～１２を平坦化することが可能になる。銅層、シード層、パラジウム吸着層を除去した後、さらに第１樹脂層領域４の表面を削って、第１樹脂層領域４の表面と、凹部７及び開口部８それぞれに形成された銅層１０，１１とを平坦化してもよい。
　電解銅めっきによって、銅層１０を凹部７内に充填したり又は銅層１１を開口部８に充填したりするには、第１樹脂層領域４の表面に比べて凹部７内及び開口部８への電解銅めっきの析出量（めっき厚）が大きい、いわゆるフィルドめっきを用いてもよい。銅層１０，１１は、凹部７内又は開口部８内に充填されなくてもよく、凹部７又は開口部８の内壁（底壁及び側壁）に沿って形成されてもよい。この場合は、第１樹脂層領域４の凹部７及び開口部８を除く表面から、銅層１２、シード層、パラジウム吸着層を除去するだけでなく、さらに第１樹脂層領域４の表面を削ることによって、凹部７内（凹部７の底壁）の銅層１０及び開口部８内の銅層１１を露出させて、第１樹脂層領域４の表面と凹部７及び開口部８に形成された銅層１０～１２を平坦化することが可能になる。
＜配線層の形成工程＞
　次に、銅層の形成が終了すると、図２の（ｂ）に示すように、第１樹脂層領域４の凹部７及び開口部８を除く表面から、銅層１２、シード層及びパラジウム触媒を除去することによって、凹部７に形成された銅層１０及び開口部８に形成された銅層１１からなる配線層１３を形成する工程を行う。すなわち、第１樹脂層領域４の表面の銅層１２、シード層、パラジウム吸着層を除去することによって、第１樹脂層領域４の凹部７等を含む表面においては、凹部７及び開口部８にのみ銅層１０,１１（詳細には、銅層１０,１１に対応するシード層、パラジウム吸着層を含む）が残され、凹部７及び開口部８の銅層１０、１１等が配線層１３を形成する。配線層１３の主要部は、複数の凹部７に形成された銅層１０から形成される。配線層１３は、後述する半導体素子２２の接続端子に接続される。
　第１樹脂層領域４の凹部７を除く表面から、銅層１２、シード層及びパラジウム吸着層を除去する際に、第１樹脂層領域４の表面と凹部７に形成された銅層１０とを平坦化してもよい。また、これらの第１樹脂層領域４の上部の銅層１２、シード層、パラジウム吸着層を除去する際に、第１樹脂層領域４の上部（表面）側から厚さ方向の一部を除去してもよい。第１樹脂層領域４の上部の銅層１２、シード層、パラジウム吸着層及び第１樹脂層領域４の除去方法としては、バックグラインド法、フライカット法、又は化学的機械研磨（ＣＭＰ）を用いることができる。また、複数の除去方法を併用してもよい。フライカット法では、例えば、ダイヤモンドバイトによる研削装置を使用する。具体例としては、３００ｍｍウェハ対応のオートマチックサーフェースプレーナ（株式会社ディスコ製、商品名「ＤＡＳ８９３０」）を用いることができる。フライカット法による金属層、パラジウム吸着層の除去は、第１樹脂層領域４の上部側（表面側）から面全体を均一に研磨するので、研磨面が平坦となるため、平坦化処理であるともいえる。
　化学的機械研磨（ＣＭＰ）で研磨する場合、具体例として、３００ｍｍウェハ対応のＣＭＰ研磨装置（Applied Materials社製、商品名「F-REX300X」）を用いることができる。ＣＭＰ研磨の際、シリカ、アルミナ、セリア等の砥粒成分を含む研磨液を用いて研磨することができる。また、複数の研磨液を併用してもよいし、順次行っても良い。研磨後、純水、溶剤等の洗浄液で研磨屑、余分な砥粒を除去してもよい。
　次の工程である無電解めっきを行う際に、シード層と銅層１０上にパラジウムを吸着させやすくするために、第１樹脂層領域４の上部の銅層１２、シード層、パラジウム吸着層及び第１樹脂層領域４を除去した後、露出したシード層と銅層１０，１１の表面を化学的又は物理的に粗化してもよい。
＜キャップめっきする工程＞
　次に、配線層の形成工程が終了すると、図２（ｃ）に示すように、露出したシード層、銅層１０、１１（配線層１３）、パラジウム吸着層上に、無電解めっきによってキャップめっき１４，１５を形成してもよい。キャップめっき１４，１５の金属種としては、Ｃｕ、Ｎｉ，Ｃｒ，Ｗのいずれか一種類を含む金属を用いてもよい。以上により、微細な配線層１３を有する配線基板２０が作製される。
＜半導体装置の製造方法＞
　次に、図３に示すように、配線基板２０上の配線層１３上に半導体素子２２を実装し、半導体素子２２の接続端子を配線層１３に電気的に接続する。これにより、微細な配線層１３によって接続された半導体装置２５が作製される。
　以上、本実施形態に係る配線基板及び半導体装置の製造方法では、有機樹脂中にガラスクロスを配置した樹脂シート３を用い、樹脂シート３においてガラスクロスが存在しない第１樹脂層領域４にエキシマレーザで凹部７を形成し、凹部７等に配線層１３を形成している。この場合、レーザによる凹部７の微細加工が可能となり、微細配線層を容易に形成することができる。
　本実施形態に係る配線基板及び半導体装置の製造方法では、樹脂シート３の表面側における第１樹脂層領域４の厚みが２０μｍ以下であってもよい。この場合、微細な配線層１３を形成する層領域を薄くして、製造される配線基板２０の低背化を図ることができる。また、この製造方法では、第１樹脂層領域４の厚みが５μｍ以上であってもよい。これにより、適切な深さの凹部７を形成して、導通性に優れた微細な配線層１３を形成することができる。
　本実施形態に係る配線基板及び半導体装置の製造方法では、第１樹脂層領域４に形成される凹部７のライン幅が０．５μｍ以上５μｍ以下であってもよい。この場合、導通性に優れた微細な配線層１３を形成することができる。
　本実施形態に係る配線基板及び半導体装置の製造方法では、樹脂シート３は、第１樹脂層領域４とは逆側に第２樹脂層領域６を有しており、構造体を準備する工程では、支持体１上に樹脂シート３を第２樹脂層領域６によって貼り付けることにより構造体１ａを準備している。この場合、構造体１ａの準備をラミネート等の簡易な手法により行うことができ、製造方法を簡素化することができる。
　本実施形態に係る配線基板及び半導体装置の製造方法では、めっき層を形成する工程は、凹部７及び開口部８と第１樹脂層領域の表面とに対してデスミア処理を行う工程と、凹部７及び開口部８と第１樹脂層領域の表面とに対して無電解めっきによりシード層９を形成する工程と、シード層９上に電解めっきを施して銅層１０～１２を形成する工程と、第１樹脂層領域４の表面とシード層９と銅層１０～１２とが平坦化するように第１樹脂層領域４の表面上のシード層９及び銅層１０～１２を除去する工程と、を有している。これにより、微細な配線層１３の導通部分をより確実に形成することができる。
　なお、本実施形態に係る半導体装置の製造方法では、上述した各種の方法により、微細な配線層１３を備えた配線基板２０を有する半導体装置２５を簡素化された方法で作製することができる。また、簡素化された方法で作製するため、製造歩留まりの向上又は製造品のコスト低減等を図ることも可能となる。更に、これに限定されないが、複数の半導体素子（チップ）を実装する場合（特に高密度に実装する場合）、半導体素子同士の間を伝送性に優れた微細な配線層で接続することができ、より性能の優れた小型の半導体装置を提供することが可能となる。
　本実施形態に係る樹脂シート３は、外側に位置する第１樹脂層領域４と、第１樹脂層領域４より弾性率が高く内側に位置する高弾性層領域５と、を備える。このような樹脂シート３を予め作製しておくことにより、上述した配線基板の製造方法及び半導体装置の製造方法をより簡素化して、製造される配線基板２０及び半導体装置２５の歩留まり向上又は製造品のコスト低減等を図ることが可能となる。
　本実施形態に係る樹脂シート３は、第１樹脂層領域４とは高弾性層領域５を介して反対側に位置する第２樹脂層領域６を更に備えており、第２樹脂層領域６が粘着性を有している。このため、樹脂シート３を含む構造体１ａをより容易に形成することが可能となり、上述した配線基板２０の製造方法及び半導体装置２５の製造方法をより簡素化することができる。
　以上、本発明の実施形態について詳細に説明してきたが、本発明は、上記実施形態に限定されるものではなく、様々な実施形態に適用することができる。例えば、上記実施形態では、図１～図３に示すように、配線層１３を１層設けて、その上に半導体素子２２を配置して半導体装置２５を作製したが、配線層１３は２層以上であってもよい。この場合、図２の（ｂ）に示す配線層１３の形成工程を行った後、さらに、別の樹脂シート３を配線層１３が形成された第１樹脂層領域４上に貼り付け等により取り付ける工程と、別の凹部７を別の樹脂シート３の第１樹脂層領域４に形成する工程と、別の開口部８を別の樹脂シート３に形成する工程と、別の配線層１３を別の凹部７及び別の開口部８に形成する工程とを１回以上繰り返して、配線層１３を多層化してもよい。多層化する際、別の開口部８は、別の樹脂シート３の表面側から内側の開口部８の銅層１１又は配線層１３に到るように形成される。これにより、微細な配線層１３が多層化された配線基板及び半導体装置を得ることができる。
　また、図４の（ａ）に示すように、支持体１上に内蔵配線層３１を１層以上設けて内蔵配線部を形成し、その上に樹脂シート３を貼り付け等により取り付けて、凹部７を形成する工程と、開口部８を形成する工程と、配線層１３を形成する工程とを行い、多層の配線基板３０を形成してもよい。そして、図４の（ｂ）に示すように、多層の配線基板３０に半導体素子３２を実装して半導体装置３５としてもよい。この場合、ビルドアップ工法を用いて、内蔵配線層３１を形成することができる。これにより、内蔵配線層３１に従来の工法を用いて多層化し、表層（即ち半導体素子との接続部分）の配線層１３のみ、より微細化した配線層とすることも可能である。この場合、例えば、内蔵配線層３１をビルドアップ材から構成し、表面の微細な配線層１３をプリプレグ等の有機樹脂材料をレーザ加工して凹部形成するといったように異なる材料を用いて最適な構成の配線基板を作製することができる。また、このような変形例に係る製造方法によれば、配線基板の設計自由度を高めることもできる。
　１…支持体、１ａ…構造体、２…銅層（金属層）、３…樹脂シート、４…第１樹脂層領域、５…高弾性層領域、６…第２樹脂層領域、７…凹部、８…開口部、９…シード層、１０，１１…銅層（めっき金属層、第２部分）、１２…銅層（第１部分）、１３…配線層、１４，１５…キャップめっき、２０…配線基板、２２…半導体素子、２５…半導体装置、３０…配線基板、３１…内蔵配線層、３２…半導体素子、３５…半導体装置。

Claims (22)

  1. 　表面に金属層を設けた支持体上に又は前記支持体に設けた内蔵配線層上に有機樹脂中にガラスクロスを配置した樹脂シートが取り付けられた構造体を準備する工程と、
    　前記樹脂シートの表面側であって前記ガラスクロスが存在しない第１樹脂層領域に対してエキシマレーザにより凹部を形成する工程と、
    　前記樹脂シートの表面から前記支持体上の前記金属層に到る開口部を形成する工程と、
    　前記凹部及び前記開口部に配線層を形成する工程と、
    を備える、配線基板の製造方法。
  2. 　表面に金属層を設けた支持体上に又は前記支持体に設けた内蔵配線層上に外側に位置する第１樹脂層領域と前記第１樹脂層領域より弾性率が高く内側に位置する高弾性層領域とが順に形成された樹脂シートが取り付けられた構造体を準備する工程と、
    　前記樹脂シートの表面側であって前記第１樹脂層領域にレーザ又はインプリントにより凹部を形成する工程と、
    　前記樹脂シートの表面から前記支持体上の前記金属層に到る開口部を形成する工程と、
    　前記凹部及び前記開口部に配線層を形成する工程と、
    を備える、配線基板の製造方法。
  3. 　前記高弾性層領域は、無機繊維及び有機繊維の少なくとも一方が有機樹脂材料中に配置されることにより形成されている、
    請求項２に記載の配線基板の製造方法。
  4. 　前記無機繊維は、ガラス繊維、セラミック繊維、及び炭素繊維の少なくとも１つであり、前記有機繊維は、アラミド繊維、及びポリエチレン繊維の少なくとも１つである、
    請求項３に記載の配線基板の製造方法。
  5. 　前記樹脂シートの表面側における前記第１樹脂層領域の厚みが５μｍ以上２０μｍ以下である、
    請求項１～４の何れか一項に記載の配線基板の製造方法。
  6. 　前記第１樹脂層領域に形成される前記凹部のライン幅が０．５μｍ以上５μｍ以下である、
    請求項１～５の何れか一項に記載の配線基板の製造方法。
  7. 　前記樹脂シートは、前記第１樹脂層領域とは逆側に第２樹脂層領域を有しており、
    　前記構造体を準備する工程では、前記支持体上又は前記内蔵配線層上に前記樹脂シートを前記第２樹脂層領域によって貼り付けて、前記構造体を準備する、
    請求項１～６の何れか一項に記載の配線基板の製造方法。
  8. 　前記第１樹脂層領域にエキシマレーザにより前記凹部を形成する場合において、前記エキシマレーザのパルス幅が１０ナノ秒以上５０ナノ秒以下であり、前記エキシマレーザの出力が１０ｍＪ／パルス以上１０００ｍＪ／パルス以下である、
    請求項１～７の何れか一項に記載の配線基板の製造方法。
  9. 　前記配線層を形成する工程では、前記凹部及び前記開口部にめっき金属層を形成して前記配線層を形成し、
    　前記樹脂シートは、前記めっき金属層を形成するためのシード層を構成する金属材料と配位結合が可能な複素芳香族環からなる成分を含む、
    請求項１～８の何れか一項に記載の配線基板の製造方法。
  10. 　前記樹脂シート又は前記樹脂シートを覆う被覆層は、無機染料、無機顔料、有機染料、及び有機顔料の少なくとも１つからなるレーザ光吸収性着色成分を含む、
    請求項１～９の何れか一項に記載の配線基板の製造方法。
  11. 　前記配線層を形成する工程では、前記凹部及び前記開口部に無電解めっきによるシード層を設けてめっき金属層を形成して前記配線層を形成し、
    　前記樹脂シートは、前記無電解めっきを形成するための触媒を含む、
    請求項１～１０の何れか一項に記載の配線基板の製造方法。
  12. 　前記配線層を形成する工程は、
    　前記凹部及び前記開口部に導電性材料を充填すると共に前記凹部及び前記開口部を除く前記第１樹脂層領域の表面上に導電性材料を設けて、導電層を形成する工程と、
    　前記導電性を平坦化する工程と、を有し、
    　前記平坦化する工程では、前記第１樹脂層領域の表面上に設けられた前記導電層の第１部分を少なくとも研磨し、前記凹部及び前記開口部に充填された前記導電性材料から形成される前記導電層の第２部分から前記配線層を形成する、
    請求項１～１１の何れか一項に記載の配線基板の製造方法。
  13. 　前記支持体上に、前記内蔵配線層を少なくとも一層有する内蔵配線部を形成する工程を更に備え、
    　前記構造体を準備する工程は、当該内蔵配線部上に前記樹脂シートを貼り付けることにより取り付けを行い、前記構造体を準備する、
    請求項１～１２の何れか一項に記載の配線基板の製造方法。
  14. 　前記配線層が形成された前記樹脂シートの上に別の樹脂シートを取り付ける工程と、
    　前記別の樹脂シートの第１樹脂層領域に対してレーザにより別の凹部を形成する工程と、
    　前記別の樹脂シートの表面から前記開口部の前記めっき金属層又は前記配線層に到る別の開口部を形成する工程と、
    　前記別の凹部及び前記別の開口部に別のめっき金属層を形成して別の配線層を形成する工程と、を更に備え、
    　前記別の樹脂シートを取り付ける工程、前記別の凹部を形成する工程、前記別の開口部を形成する工程、及び、前記別の配線層を形成する工程を少なくとも１回以上繰り返す、
    請求項１～１３の何れか一項に記載の配線基板の製造方法。
  15. 前記配線層を形成する工程は、
    　少なくとも前記開口部及び前記凹部に対してデスミア処理を行う工程と、
    　少なくとも前記開口部及び前記凹部に対して無電解めっきによりシード層を形成する工程と、
    　前記シード層上に電解めっきを施してめっき金属層を形成する工程と、
    　前記第１樹脂層領域の表面と前記シード層と前記めっき金属層とが平坦化するように前記第１樹脂層領域の表面上の前記シード層及び前記めっき金属層を除去する工程と、を有する、
    請求項１～１４の何れか一項に記載の配線基板の製造方法。
  16. 　請求項１～１５の何れか一項に記載の配線基板の製造方法によって製造される配線基板を準備する工程と、
    　前記配線層又は前記別の配線層上に半導体素子を実装し、前記半導体素子を前記配線層又は前記別の配線層に電気的に接続する工程と、
    備える、半導体装置の製造方法。
  17. 　請求項１６に記載の製造方法を用いて製造される構造を有する、半導体装置。
  18. 　請求項１～１５の何れか一項に記載の配線基板の製造方法に使用される樹脂シートであって、外側に位置する第１樹脂層領域と、前記第１樹脂層領域より弾性率が高く内側に位置する高弾性層領域又はガラスクロスを有し内側に位置する高弾性層領域と、を備える樹脂シート。
  19. 　前記第１樹脂層領域とは前記高弾性層領域を介して反対側に位置する第２樹脂層領域を更に備え、前記第２樹脂層領域が粘着性を有している、
    請求項１５に記載の樹脂シート。
  20. 　前記第１樹脂層領域は、マレイミド化合物、ビスマレイミド化合物、トリアゾール化合物、ベンゾトリアゾール化合物、及び、ベンゾオキサゾール化合物からなる群から選ばれる少なくとも１つの化合物を含む、
    請求項１８又は１９に記載の樹脂シート。
  21. 　前記第１樹脂層領域は、黒鉛、グラフェン、カーボンナノチューブ、カーボンファイバー、カーボンブラック、フタロシアニン、シアニン、アルカリ土類金属、及び、金属錯体の少なくとも１つを含む、
    請求項１８～２０の何れか一項に記載の樹脂シート。
  22. 　前記第１樹脂層領域は、パラジウム粒子、パラジウム錯体、銅粒子、及び、銅錯体の少なくとも１つを含む、
    請求項１８～２１の何れか一項に記載の樹脂シート。
PCT/JP2021/035957 2020-10-01 2021-09-29 配線基板の製造方法、半導体装置の製造方法、及び樹脂シート Ceased WO2022071430A1 (ja)