WO2022050003A1 - Stratifié optique, et plaque de polarisation ellipsoïdale le comrpenant - Google Patents

Stratifié optique, et plaque de polarisation ellipsoïdale le comrpenant Download PDF

Info

Publication number
WO2022050003A1
WO2022050003A1 PCT/JP2021/029483 JP2021029483W WO2022050003A1 WO 2022050003 A1 WO2022050003 A1 WO 2022050003A1 JP 2021029483 W JP2021029483 W JP 2021029483W WO 2022050003 A1 WO2022050003 A1 WO 2022050003A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
liquid crystal
group
optical laminate
polymerizable liquid
Prior art date
Application number
PCT/JP2021/029483
Other languages
English (en)
Japanese (ja)
Inventor
伸行 幡中
耕太 村野
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to CN202180056410.6A priority Critical patent/CN116057430A/zh
Priority to KR1020237004603A priority patent/KR20230062548A/ko
Publication of WO2022050003A1 publication Critical patent/WO2022050003A1/fr

Abstract

L'objectif de la présente invention est de fournir un stratifié optique dans lequel une contrainte ne se produit pas facilement lorsque le stratifié est plié, et qui a une flexibilité élevée et une réflectance oblique exceptionnelle, et en particulier de fournir un stratifié optique qui est approprié pour un affichage souple.　Le stratifié optique comprend un film à différence de phase, un polariseur, et un film protecteur transparent dans l'ordre indiqué, dans lequel : le film à différence de phase comprend un film de base ayant une perméabilité à l'humidité de 100 g/m2/24 heures ou plus, et un film durci à cristaux liquides qui est formé sur le film de base, a une épaisseur de 0,5 à 3 µm (inclus), et satisfait, en tant que couche unique, les formules (1) et (2) (formule (1) : Re (450)/Re (550) ≤ 1,00, et formule (2) : 1,00≤Re(650)/Re(550), où Re (λ) représente la valeur de différence de phase dans le plan à la longueur d'onde λ) ; le polariseur est configuré à partir d'un film de résine d'alcool polyvinylique qui contient un pigment dichroïque ; le film protecteur transparent a une transmittance de lumière totale de 90 % ou plus et une transmittance de 380 nm de 30 % ou moins ; et le film à différence de phase, le polariseur et le film protecteur transparent sont adjacents à des couches adhésives interposées entre ceux-ci.
PCT/JP2021/029483 2020-09-07 2021-08-10 Stratifié optique, et plaque de polarisation ellipsoïdale le comrpenant WO2022050003A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202180056410.6A CN116057430A (zh) 2020-09-07 2021-08-10 光学层叠体及包含其的椭圆偏光板
KR1020237004603A KR20230062548A (ko) 2020-09-07 2021-08-10 광학 적층체 및 이것을 포함하는 타원 편광판

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-149847 2020-09-07
JP2020149847A JP2022044293A (ja) 2020-09-07 2020-09-07 光学積層体およびこれを含む楕円偏光板

Publications (1)

Publication Number Publication Date
WO2022050003A1 true WO2022050003A1 (fr) 2022-03-10

Family

ID=80491999

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/029483 WO2022050003A1 (fr) 2020-09-07 2021-08-10 Stratifié optique, et plaque de polarisation ellipsoïdale le comrpenant

Country Status (5)

Country Link
JP (1) JP2022044293A (fr)
KR (1) KR20230062548A (fr)
CN (1) CN116057430A (fr)
TW (1) TW202214429A (fr)
WO (1) WO2022050003A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2024024890A1 (fr) * 2022-07-29 2024-02-01 住友化学株式会社 Stratifié optique

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005049698A (ja) * 2003-07-30 2005-02-24 Fuji Photo Film Co Ltd 偏光板
JP2005309382A (ja) * 2004-02-16 2005-11-04 Fuji Photo Film Co Ltd 液晶表示装置
JP2006195363A (ja) * 2005-01-17 2006-07-27 Fuji Photo Film Co Ltd 液晶表示装置、さらにそれに用いる光学補償シート、及び偏光板
JP2006308954A (ja) * 2005-04-28 2006-11-09 Fuji Photo Film Co Ltd セルロースアシレートフィルム、並びにそれを用いた光学補償フィルム、偏光板及び液晶表示装置
JP2007171815A (ja) * 2005-12-26 2007-07-05 Fujifilm Corp 液晶表示装置
JP2007279083A (ja) * 2006-04-03 2007-10-25 Fujifilm Corp 光学補償フィルム、偏光板及び液晶表示装置
JP2007310128A (ja) * 2006-05-18 2007-11-29 Fujifilm Corp 光学フィルム、光学フィルムの製造方法、光学補償フィルム、偏光板および液晶表示装置
JP2008503763A (ja) * 2004-06-25 2008-02-07 富士フイルム株式会社 光学補償シート、その製造方法、それを用いた偏光板及び液晶表示装置
JP2009009079A (ja) * 2007-05-30 2009-01-15 Nippon Zeon Co Ltd 偏光板および液晶表示装置
WO2009016888A1 (fr) * 2007-07-30 2009-02-05 Konica Minolta Opto, Inc. Élément de polarisation circulaire et élément électroluminescent
JP2010262098A (ja) * 2009-05-01 2010-11-18 Fujifilm Corp 光学補償フィルム、光学補償フィルムの製造方法、偏光板、及び液晶表示装置
WO2019103143A1 (fr) * 2017-11-27 2019-05-31 富士フイルム株式会社 Film à cristaux liquides long, plaque de polarisation longue, dispositif d'affichage d'image et procédé de production de film à cristaux liquides long
JP2020056988A (ja) * 2018-09-28 2020-04-09 住友化学株式会社 光学積層体、偏光板複合体、及び画像表示装置

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5899607B2 (ja) 2009-03-16 2016-04-06 住友化学株式会社 化合物、光学フィルム及び光学フィルムの製造方法

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005049698A (ja) * 2003-07-30 2005-02-24 Fuji Photo Film Co Ltd 偏光板
JP2005309382A (ja) * 2004-02-16 2005-11-04 Fuji Photo Film Co Ltd 液晶表示装置
JP2008503763A (ja) * 2004-06-25 2008-02-07 富士フイルム株式会社 光学補償シート、その製造方法、それを用いた偏光板及び液晶表示装置
JP2006195363A (ja) * 2005-01-17 2006-07-27 Fuji Photo Film Co Ltd 液晶表示装置、さらにそれに用いる光学補償シート、及び偏光板
JP2006308954A (ja) * 2005-04-28 2006-11-09 Fuji Photo Film Co Ltd セルロースアシレートフィルム、並びにそれを用いた光学補償フィルム、偏光板及び液晶表示装置
JP2007171815A (ja) * 2005-12-26 2007-07-05 Fujifilm Corp 液晶表示装置
JP2007279083A (ja) * 2006-04-03 2007-10-25 Fujifilm Corp 光学補償フィルム、偏光板及び液晶表示装置
JP2007310128A (ja) * 2006-05-18 2007-11-29 Fujifilm Corp 光学フィルム、光学フィルムの製造方法、光学補償フィルム、偏光板および液晶表示装置
JP2009009079A (ja) * 2007-05-30 2009-01-15 Nippon Zeon Co Ltd 偏光板および液晶表示装置
WO2009016888A1 (fr) * 2007-07-30 2009-02-05 Konica Minolta Opto, Inc. Élément de polarisation circulaire et élément électroluminescent
JP2010262098A (ja) * 2009-05-01 2010-11-18 Fujifilm Corp 光学補償フィルム、光学補償フィルムの製造方法、偏光板、及び液晶表示装置
WO2019103143A1 (fr) * 2017-11-27 2019-05-31 富士フイルム株式会社 Film à cristaux liquides long, plaque de polarisation longue, dispositif d'affichage d'image et procédé de production de film à cristaux liquides long
JP2020056988A (ja) * 2018-09-28 2020-04-09 住友化学株式会社 光学積層体、偏光板複合体、及び画像表示装置

Also Published As

Publication number Publication date
TW202214429A (zh) 2022-04-16
CN116057430A (zh) 2023-05-02
JP2022044293A (ja) 2022-03-17
KR20230062548A (ko) 2023-05-09

Similar Documents

Publication Publication Date Title
JP7356480B2 (ja) 光学フィルム及びその製造方法
JP6876638B2 (ja) 楕円偏光板
JP6763916B2 (ja) 楕円偏光板
JP7491660B2 (ja) 光学補償機能付き位相差板
JP7398868B2 (ja) 組成物
JP2024045211A (ja) 重合性液晶混合組成物、位相差板、楕円偏光板および有機ｅｌ表示装置
JP7443413B2 (ja) 垂直配向液晶硬化膜
WO2021054031A1 (fr) Stratifié et polariseur elliptique le comprenant
WO2021006068A1 (fr) Film long
WO2022050003A1 (fr) Stratifié optique, et plaque de polarisation ellipsoïdale le comrpenant
JP2019035952A (ja) フレキシブルディスプレイ用光学補償機能付き位相差板
WO2021193131A1 (fr) Composé de cristaux liquides polymérisable, composition de cristaux liquides polymérisable, film à différence de phase, plaque de polarisation elliptique et dispositif d'affichage électroluminescent organique
JP7302954B2 (ja) 水平配向液晶硬化膜を含む積層体
US11971566B2 (en) Horizontally oriented liquid crystal cured film and laminate including the same
WO2021205726A1 (fr) Corps stratifié optique
JP2022017912A (ja) 重合性液晶組成物、液晶硬化膜およびその製造方法
JP2021175785A (ja) 重合性液晶組成物、液晶硬化膜、楕円偏光板及び有機ｅｌ表示装置
JP2021081651A (ja) 光学異方性膜

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21864061

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21864061

Country of ref document: EP

Kind code of ref document: A1