WO2021210392A1 - 半導体基板の製造方法、半導体基板、及び、成長層を形成する方法 - Google Patents

半導体基板の製造方法、半導体基板、及び、成長層を形成する方法 Download PDF

Info

Publication number
WO2021210392A1
WO2021210392A1 PCT/JP2021/013745 JP2021013745W WO2021210392A1 WO 2021210392 A1 WO2021210392 A1 WO 2021210392A1 JP 2021013745 W JP2021013745 W JP 2021013745W WO 2021210392 A1 WO2021210392 A1 WO 2021210392A1
Authority
WO
WIPO (PCT)
Prior art keywords
base substrate
growth
semiconductor substrate
hole
forming
Prior art date
Application number
PCT/JP2021/013745
Other languages
English (en)
French (fr)
Inventor
忠昭 金子
大地 堂島
Original Assignee
学校法人関西学院
豊田通商株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 学校法人関西学院, 豊田通商株式会社 filed Critical 学校法人関西学院
Priority to CN202180028149.9A priority Critical patent/CN115461501A/zh
Priority to EP21788842.9A priority patent/EP4137615A4/en
Priority to US17/996,184 priority patent/US20230193507A1/en
Priority to JP2022515287A priority patent/JPWO2021210392A1/ja
Publication of WO2021210392A1 publication Critical patent/WO2021210392A1/ja

Abstract

本発明の解決しようとする課題は、大口径な半導体基板を製造可能な新規の技術を提供することを課題とする。 本発明は、貫通孔１１を有する下地基板１０に成長層２０を形成する結晶成長工程Ｓ３０を含む、半導体基板の製造方法である。また、本発明は、下地基板１０の表面上に成長層２０を形成する前に、下地基板１０に貫通孔１１を形成する貫通孔形成工程Ｓ１０を含む、成長層２０を形成する方法である。

Description

半導体基板の製造方法、半導体基板、及び、成長層を形成する方法
　本発明は、半導体基板の製造方法、半導体基板、及び、成長層を形成する方法に関する。
　一般に半導体基板は、下地基板上に成長層を結晶成長させることで製造される。しかしながら、結晶成長させる半導体材料の組成によっては、大口径な半導体基板を得ることが難しいという問題が報告されている。
　例えば、窒化アルミニウム（ＡｌＮ）基板や炭化ケイ素（ＳｉＣ）基板等の下地基板上に、昇華法によりＡｌＮ結晶を成長させる場合が挙げられる。単に昇華法で結晶成長させた場合には、ＡｌＮ結晶が成長しない領域が存在してしまい、大口径で結晶性のよい半導体基板を得ることが困難であるという問題がある。
　このような問題に対し、特許文献１には、「気相成長法により、反応容器内に設けられた結晶成長容器内の結晶成長室内に配置した種結晶基板上にＡｌＮ結晶を成長させる方法であって、結晶成長の際に、前記結晶成長室内にカーボン含有ガスを供給することを特徴とするＡｌＮ結晶の成長方法」の技術が記載されている。
特開２００７－５５８８１号公報
　本発明の解決しようとする課題は、大口径な半導体基板を製造可能な新規の技術を提供することにある。
　また、本発明の解決しようとする課題は、大口径で結晶性のよい半導体基板を製造可能な新規の技術を提供することにある。
　上述した課題を解決する本発明は、貫通孔を有する下地基板に成長層を形成する結晶成長工程を含む、半導体基板の製造方法である。
　このように、貫通孔を有する下地基板に成長層を形成することで、下地基板の径と同等の径を有する半導体基板を製造することができる。そのため、大きな径の下地基板を採用することで、大口径な半導体基板を得ることができる。
　なお、本明細書における「大口径」の語は、貫通孔を有さない下地基板に成長層を形成した場合と比較して、大面積な成長層を得られていることを意味する。
　本発明の好ましい形態では、前記結晶成長工程は、前記下地基板の垂直方向に沿って温度勾配が形成されるよう加熱する工程である。
　本発明の好ましい形態では、前記結晶成長工程は、前記下地基板と前記成長層の原料とを相対させて配置し、前記下地基板と前記原料との間に温度勾配が形成されるよう加熱する工程である。
　本発明の好ましい形態では、前記結晶成長工程は、前記下地基板の水平方向に前記成長層が成長する横方向成長工程と、前記下地基板の垂直方向に前記成長層が成長する縦方向成長工程と、を有する。
　本発明の好ましい形態では、前記下地基板に貫通孔を形成する貫通孔形成工程と、
　前記貫通孔形成工程により導入された歪層を除去する歪層除去工程と、をさらに含む。
　本発明の好ましい形態では、前記貫通孔形成工程は、レーザーを前記下地基板に照射することにより貫通孔を形成する工程である。
　本発明の好ましい形態では、前記歪層除去工程は、熱処理することにより前記下地基板の歪層を除去する工程である。
　本発明の好ましい形態では、前記下地基板は炭化ケイ素であり、前記歪層除去工程は、前記下地基板をシリコン雰囲気下でエッチングする工程である。
　また、本発明は成長層を形成する方法にも関する。すなわち、上述した課題を解決する本発明は、下地基板の表面上に成長層を形成する前に、前記下地基板に貫通孔を形成する貫通孔形成工程を含む、成長層を形成する方法である。
　本発明の好ましい形態では、前記貫通孔形成工程により導入された歪層を除去する歪層除去工程を含む。
　本発明の好ましい形態では、前記歪層除去工程は、熱処理することにより前記下地基板をエッチングする工程である。
　開示した技術によれば、大口径な半導体基板を製造可能な新規の技術を提供することができる。
　また、開示した技術によれば、大口径で結晶性のよい半導体基板を製造可能な新規の技術を提供することができる。
　他の課題、特徴および利点は、図面および特許請求の範囲と共に取り上げられる際に、以下に記載される発明を実施するための形態を読むことにより明らかになるであろう。
実施の形態にかかる半導体基板の製造方法の工程を説明する説明図である。 実施の形態にかかる貫通孔形成工程および歪層除去工程を説明する説明図である。 実施の形態にかかる貫通孔形成工程の説明図である 実施の形態にかかる結晶成長工程を説明する説明図である。 実施の形態にかかる結晶成長工程を説明する説明図である。 実施例１にかかる貫通孔形成工程の説明図である。 実施例１にかかる歪層除去工程の説明図である。 実施例１にかかる結晶成長工程の説明図である。 実施例１にかかる結晶成長工程の説明図である。 比較例１にかかる結晶成長工程の説明図である。
　以下に添付図面を参照して、この発明にかかる半導体基板の製造方法の好適な実施の形態を詳細に説明する。本発明の技術的範囲は、添付図面に示した実施の形態に限定されるものではなく、特許請求の範囲に記載された範囲内において、適宜変更が可能である。また、添付の図面は概念図であり、各部材の相対的な寸法等は、本発明を限定するものではない。また、本明細書においては、発明の説明の目的で、図面の上下に基づいて、上または下と指称する場合があるが、本発明の半導体基板の使用態様等との関係で上下を限定するものではない。なお、以下の実施の形態の説明および添付図面において、同様の構成には同一の符号を付し、重複する説明を省略する。
《半導体基板の製造方法》
　図１ないし図４は、本発明の実施の形態にかかる半導体基板の製造方法の工程を説明する説明図である。
　実施の形態にかかる半導体基板の製造方法は、下地基板１０に貫通孔１１を形成する貫通孔形成工程Ｓ１０と、貫通孔形成工程Ｓ１０により導入された歪層１２を除去する歪層除去工程Ｓ２０と、この貫通孔１１を有する下地基板１０に成長層２０を形成する結晶成長工程Ｓ３０と、を含み得る。
　また、この実施の形態は、下地基板１０の表面上に成長層２０を形成する前に、下地基板１０に貫通孔１１を形成する貫通孔形成工程Ｓ１０を含む、成長層２０を大面積に形成する方法として把握できる。
　以下、実施の形態の各工程について詳細に説明する。
<貫通孔形成工程>
　貫通孔形成工程Ｓ１０は、下地基板１０に貫通孔１１を形成する工程である。この貫通孔形成工程Ｓ１０は、下地基板１０に貫通孔１１を形成可能な手法であれば当然に採用することができる。
　貫通孔１１の形成手法は、例として、レーザー加工、集束イオンビーム（Ｆｏｃｕｓｅｄ　Ｉｏｎ　Ｂｅａｍ　Ｓｙｓｔｅｍ：ＦＩＢ）、反応性イオンエッチング（Ｒｅａｃｔｉｖｅ　Ｉｏｎ　Ｅｔｃｈｉｎｇ：ＲＩＥ）等のプラズマエッチングを採用することができる。なお、本実施の形態を示した図２においては、レーザーＬを下地基板１０に照射することにより貫通孔１１を形成する手段を例示している。
　下地基板１０は、半導体基板を製造する際に、一般的に用いられる材料であれば当然に採用することができる。下地基板１０の材料は、例として、シリコン（Ｓｉ）、ゲルマニウム（Ｇｅ）、ダイヤモンド（Ｃ）等の既知のＩＶ族材料である。また、下地基板１０の材料は、例として、炭化ケイ素（ＳｉＣ）等の既知のＩＶ－ＩＶ族化合物材料である。また、下地基板１０の材料は、酸化亜鉛（ＺｎＯ）、硫化亜鉛（ＺｎＳ）、セレン化亜鉛（ＺｎＳｅ）、硫化カドミウム（ＣｄＳ）、テルル化カドミウム（ＣｄＴｅ）等の既知のＩＩ－ＶＩ族化合物材料である。また、下地基板１０の材料は、例として、窒化ホウ素（ＢＮ）、ガリウムヒ素（ＧａＡｓ）、窒化ガリウム（ＧａＮ）、窒化アルミニウム（ＡｌＮ）、窒化インジウム（ＩｎＮ）、リン化ガリウム（ＧａＰ）、リン化インジウム（ＩｎＰ）、アンチモン化インジウム（ＩｎＳｂ）等の既知のＩＩＩ－Ｖ族化合物材料である。また、下地基板１０の材料は、例として、酸化アルミニウム（Ａｌ２Ｏ３）、酸化ガリウム（Ｇａ２Ｏ３）等の酸化物材料である。また、下地基板１０の材料は、例として、銅（Ｃｕ）、ニッケル（Ｎｉ）等の金属材料である。なお、下地基板１０は、その材料に応じて用いられる既知の添加原子が、適宜添加されている構成であってよい。
　なお、下地基板１０は、バルク結晶から加工したウェハや基板を用いてもよいし、別途上述した半導体材料からなるバッファ層を有する基板を用いても良い。
　貫通孔１１は、成長させる半導体材料に適した任意の形状を採用すればよく、単数又は複数形成しても良い。また、複数の貫通孔１１を配列させた貫通孔群（パターン）を採用しても良い。
　以下、六方晶系の半導体材料を成長させる際のパターンの一例について、詳細に説明する。
　図３は、実施の形態にかかるパターン１００を説明する説明図である。パターン１００が示す線分は、下地基板１０である。パターン１００は、好ましくは、３回対称である正６角形変位形を呈する。本明細書中の説明における「正６角形変位形」を、図３を交えて、詳細に以下に説明する。正６角形変位形は、１２角形である。また、正６角形変位形は、等しい長さを呈し直線状である１２個の線分により構成される。正６角形変位形を呈するパターン１００は、正３角形であり面積１０１ａを有し３個の頂点１０４を含む基準図形１０１を内包する。当該３個の頂点１０４のそれぞれは、パターン１００の頂点に含まれる。ここで、当該３個の頂点１０４は、パターン１００を構成する線分上に位置する場合がある、と把握することができる。パターン１００は、頂点１０４から延伸し頂点１０４を含む線分１０２（第１線分に相当。）と、頂点１０４から延伸せず頂点１０４を含まず線分１０２と隣接する線分１０３（第２線分に相当。）と、を含む。ここで、パターン１００における２つの隣接し合う線分１０２がなす角度θは、一定であり、パターン１００における２つの隣接し合う線分１０３がなす角度θと等しい。なお、本明細書中の説明における「正６角形変位形」は、正６角形が、凹凸の程度を示す角度θに基づき、当該正６角形の面積を維持しながら変位（変形）されてなる１２角形である、と把握することができる。
　角度θは、好ましくは６０°より大きく、また好ましくは６６°以上であり、また好ましくは８０°以上であり、また好ましくは８３°以上であり、また好ましくは１２０°以上であり、また好ましくは１５０°以上であり、また好ましくは１５５°以上である。また、角度θは、好ましくは１８０°以下であり、また好ましくは１５５°以下であり、また好ましくは１５０°以下であり、また好ましくは１２０°以下であり、また好ましくは８３°以下であり、また好ましくは８０°以下であり、また好ましくは６６°以下である。
　実施の形態にかかるパターン１００は、３回対称である正６角形変位形に代えて、６回対称である正１２角形変位形である構成であってよい。正１２角形変位形は、２４角形である。また、正１２角形変位形は、等しい長さを呈し直線状である２４個の線分により構成される。正１２角形変位形を呈するパターン１００は、正６角形であり面積１０１ａを有し６個の頂点１０４を含む基準図形１０１を内包する。当該６個の頂点１０４のそれぞれは、パターン１００の頂点に含まれる。なお、正６角形変位形と同様、パターン１００における２つの隣接し合う線分１０２がなす角度θは、一定であり、パターン１００における２つの隣接し合う線分１０３がなす角度θと等しい。つまり、本明細書中の説明における「正１２角形変位形」は、正１２角形が、凹凸の程度を示す角度θに基づき、当該正１２角形の面積を維持しながら変位（変形）されてなる２４角形である、と把握することができる。なお、パターン１００は、正２ｎ角形が、凹凸の程度を示す角度θに基づき、当該正２ｎ角形の面積を維持しながら変位（変形）されてなる４ｎ角形である２ｎ角形変位形を呈する、という構成であってよい。このとき、２ｎ角形変位形は正ｎ角形（基準図形１０１に相当。）を内包する、と把握することができる。ここで、基準図形１０１は、ｎ個の頂点を含む、と把握することができる。
　実施の形態にかかるパターン１００は、正２ｎ角形変位形（正６角形変位形、正１２角形変位形を含む。）を含む構成であってよい。また、パターン１００は、正２ｎ角形変位形を構成する線分に加えて、正２ｎ角形変位形における隣接し合う２つの線分１０３の交点と、基準図形１０１の重心と、を結ぶ線分（第３線分に相当。）を少なくとも１つさらに含む構成であってよい。また、パターン１００は、正２ｎ角形変位形を構成する線分に加えて、正２ｎ角形変位形における隣接し合う２つの線分１０３の交点と、基準図形１０１を構成する頂点１０４と、を結ぶ線分を少なくとも１つさらに含む構成であってよい。また、パターン１００は、正２ｎ角形変位形を構成する線分に加えて、正２ｎ角形変位形に含まれる基準図形１０１を構成する線分を少なくとも１つさらに含む構成であってよい。
　また、貫通孔形成工程Ｓ１０は、好ましくは下地基板１０の有効面積の５０％以上を除去する工程である。また、より好ましくは、有効面積の６０％以上を除去する工程であり、さらに好ましくは有効面積の７０％以上を除去する工程であり、さらに好ましくは有効面積の８０％以上を除去する工程である。
　なお、本明細書における有効面積とは、結晶成長工程Ｓ３０において、原料が付着する下地基板１０の表面のことをいう。言い換えれば、下地基板１０の成長面において、貫通孔１１により除去された領域以外の残された領域のことをいう。
　なお、下地基板１０の有効面積や貫通孔１１の形状・パターンは、下地基板１０と成長層２０の格子定数差や熱膨張係数差、成長層２０の結晶構造、成長手法を考慮して設定することが望ましい。
〈歪層除去工程〉
　歪層除去工程Ｓ２０は、貫通孔形成工程Ｓ１０により下地基板１０に形成された歪層１２を除去する工程である。この歪層除去工程Ｓ２０として、下地基板１０を熱処理することにより、下地基板１０をエッチングする手段を例示することができる。
　また、歪層１２を除去可能な手段であれば、当然に採用することができる。
　歪層１２を除去する手法は、例として、水素ガスをエッチングガスとして用いる水素エッチング法や、Ｓｉ雰囲気下で加熱するＳｉ蒸気圧エッチング（Ｓｉ－Ｖａｐｏｒ　Ｅｔｃｈｉｎｇ：ＳｉＶＥ）法、後述する実施例１に記載のエッチング手法を採用することができる。
<結晶成長工程>
　結晶成長工程Ｓ３０は、貫通孔１１が形成された下地基板１０上に、成長層２０を形成する工程である。
　成長層２０の半導体材料は、下地基板１０と同じ半導体材料であっても良いし（ホモエピタキシャル成長）、下地基板１０と異なる半導体材料であっても良い（ヘテロエピタキシャル成長）。
　成長層２０の材料としては、一般に半導体材料としてエピタキシャル成長させる材料であれば、当然に採用することができる。成長層２０の材料は、下地基板１０の材料であってよく、下地基板１０の材料として採用され得る既知の材料であってよく、下地基板１０上にエピタキシャル成長され得る既知の材料であってよい。
　成長層２０の材料は、例として、Ｓｉ、Ｇｅ、ＧａＮ、ＡｌＮ、ＩｎＮ、ＺｎＳ、ＺｎＳｅ、ＣｄＴｅ、ＧａＰ、ＧａＡｓ、ＩｎＰ、ＩｎＡｓ、ＩｎＳｂ、ＳｉＣ、等を採用することができる。
　下地基板１０の材料と成長層２０の材料の組合せは、両素材の格子定数や熱膨張係数の差を考慮して、適宜選択することができる。
　結晶成長工程Ｓ３０は、成長層２０の成長手法として、物理気相輸送法（Ｐｈｙｓｉｃａｌ　Ｖａｐｏｒ　Ｔｒａｎｓｐｏｒｔ:ＰＶＴ）、昇華再結晶法、改良レイリー法、化学気相輸送法（Ｃｈｅｍｉｃａｌ　Ｖａｐｏｒ　Ｔｒａｎｓｐｏｒｔ：ＣＶＴ）、有機金属気相成長法（Ｍｏｌｅｃｕｌａｒ－Ｏｒｇａｎｉｃ　Ｖａｐｏｒ　Ｐｈａｓｅ　Ｅｐｉｔａｘｙ：ＭＯＶＰＥ）、ハイドライド気相成長法（Ｈｙｄｒｉｄｅ　Ｖａｐｅｒ　Ｐｈａｓｅ　Ｅｐｉｔａｘｙ：ＨＶＰＥ）等の既知の気相成長法（気相エピタキシャル法に相当。）を採用することができる。なお、結晶成長工程Ｓ３０は、ＰＶＴに代えて、物理気相成長法（Ｐｈｙｓｉｃａｌ　Ｖａｐｏｒ　Ｄｅｐｏｓｉｔｉｏｎ:ＰＶＤ）を採用することができる。なお、結晶成長工程Ｓ３０は、ＣＶＴに代えて、化学気相成長法（Ｃｈｅｍｉｃａｌ　Ｖａｐｏｒ　Ｄｅｐｏｓｉｔｉｏｎ:ＣＶＤ）を採用することができる。また、結晶成長工程Ｓ３０は、成長層２０の成長手法として、ＴＳＳＧ法（Ｔｏｐ－Ｓｅｅｄｅｄ　Ｓｏｌｕｔｉｏｎ　Ｇｒｏｗｔｈ法）、準安定溶媒エピタキシー法（Ｍｅｔａｓｔａｂｌｅ　Ｓｏｌｖｅｎｔ　Ｅｐｉｔａｘｙ:ＭＳＥ）等の既知の液相成長法（液相エピタキシャル法に相当。）を採用することができる。また、結晶成長工程Ｓ３０は、成長層２０の成長手法として、ＣＺ法（Ｃｚｏｃｈｒａｌｓｋｉ法）を採用することができる。結晶成長工程Ｓ３０は、下地基板１０及び成長層２０のそれぞれの材料に応じて、適宜成長手法を選択し採用することができる。
　図３および図４は、実施の形態にかかる結晶成長工程Ｓ３０を説明する説明図である。
　実施の形態にかかる結晶成長工程Ｓ３０は、下地基板１０と、成長層２０の原料となる半導体材料４０とを、準閉鎖空間を有した坩堝３０内に相対（対峙）させて配置し加熱する工程である。なお、本明細書における「準閉鎖空間」とは、容器内の真空引きは可能であるが、容器内に発生した蒸気の少なくとも一部を閉じ込め可能な空間のことをいう。
　また、結晶成長工程Ｓ３０は、下地基板１０の垂直方向に沿って温度勾配が形成されるよう加熱する工程である。この温度勾配中で坩堝３０（下地基板１０および半導体材料４０）を加熱することにより、半導体材料４０から下地基板１０上へ、原料輸送空間３１を介して原料が輸送される。
　原料を輸送する駆動力としては、上述した温度勾配や、下地基板１０と半導体材料４０間の化学ポテンシャル差を採用することができる。
　具体的には、準閉鎖空間内で、半導体材料４０から昇華した元素からなる蒸気が、原料輸送空間３１中を拡散することにより輸送され、半導体材料４０より温度が低く設定された下地基板１０上に過飽和となって凝結する。その結果、下地基板１０上に成長層２０が形成される。
　また、結晶成長工程Ｓ３０は、下地基板１０の水平方向に成長層２０が成長する横方向成長工程Ｓ３１と、下地基板１０の垂直方向に成長層２０が成長する縦方向成長工程Ｓ３２と、を有する。
　なお、横方向成長工程Ｓ３１は、水平方向への成長成分が垂直方向への成長成分より大きければよく、垂直方向への成長成分を含んでいても良い（成長成分：水平方向＞垂直方向）。
　また、縦方向成長工程Ｓ３２は、垂直方向への成長成分が水平方向への成長成分より大きければよく、水平方向への成長成分を含んでいても良い（成長成分：垂直方向＞水平方向）。
　すなわち、図４に示すように、横方向成長工程Ｓ３１は、下地基板１０の貫通孔１１から熱が逃げることにより、下地基板１０の表面上に水平方向の温度勾配が形成されることで、貫通孔１１に向かって成長層２０が成長する工程である。
　その後、横方向成長工程Ｓ３１により貫通孔１１上に成長層２０が形成されると、下地基板１０の表面上に水平方向の温度勾配が減少・消滅し、自動的に縦方向成長工程Ｓ３２に移行する。
　なお、この結晶成長工程Ｓ３０においては、不活性ガスやドーピングガスを原料輸送空間３１に導入して、成長層２０のドーピング濃度や成長環境を制御しても良い。
　本発明によれば、貫通孔１１を有する下地基板１０に成長層２０を結晶成長させることで、大口径な半導体基板を製造することができる。すなわち、貫通孔１１を形成した領域から熱が逃げることにより、下地基板１０の水平方向に成長駆動力が働く。その結果、貫通孔１１を形成した領域上で成長層２０の結合が促進され、下地基板１０の径と同等の径を有する成長層２０を形成することができる。そのため、大きな径の下地基板１０を採用することで、大口径な半導体基板を得ることができる。
　また、本発明によれば、貫通孔１１を形成した領域上に成長層２０を形成することにより、成長層２０の結晶性をよくすることができる。すなわち、貫通孔１１を形成した領域上に形成される成長層２０は、下地基板１０の直上に位置しない。そのため、下地基板１０に存在する貫通系の転位（例えば、貫通螺旋転位や貫通刃状転位、マイクロパイプ等）を引き継ぐことがなく、成長層２０における貫通系の転位を低減することができる。
　本発明にかかる半導体基板の製造方法の一つの形態として、以下の実施例に示すように、ＳｉＣ基板上にＡｌＮを成長させる形態が挙げられる。
　また、本発明にかかる半導体基板の製造方法の一つの形態として、ＳｉＣ基板上にＡｌＮを成長させる形態を含まない形態が挙げられる。
　実施例１、比較例１を挙げて本発明をより具体的に説明する。
　なお、実施例１及び比較例１は、ＳｉＣの下地基板１０の上にＡｌＮの成長層２０を成長させて半導体基板を製造した。
《実施例１》
〈貫通孔形成工程〉
　以下の条件で、下地基板１０にレーザーを照射し貫通孔１１を形成した。
（下地基板１０）
　半導体材料:４Ｈ－ＳｉＣ
　基板サイズ:横幅１１ｍｍ×縦幅１１ｍｍ×厚み５２４μｍ
　成長面：Ｓｉ－ｆａｃｅ
　オフ角：ｏｎ－ａｘｉｓ
（レーザー加工条件）
　種類：グリーンレーザー
　波長：５３２ｎｍ
　スポット径：４０μｍ
　平均出力：４Ｗ（３０ｋＨｚにて）
（パターンの詳細）
　図６は、実施例１にかかる貫通孔形成工程Ｓ１０で形成した貫通孔１１のパターンを説明する説明図である。図６（ａ）は、複数の貫通孔１１を配列した様子を示す説明図である。この図６（ａ）においては、黒く示した領域が貫通孔１１の部分を示し、白く示した領域が下地基板１０として残されている。
　図６（ｂ）は、図６（ａ）の貫通孔１１を拡大した様子を示す説明図である。この図６（ｂ）においては、白く示した領域が貫通孔１１の部分を示し、黒く示した領域が下地基板１０として残されている。
　なお、図６のパターンにおいては、下地基板１０の有効面積の８０％以上を除去して、下地基板１０の強度を低下させている。
〈歪層除去工程Ｓ２０〉
　図７は、実施例１にかかる歪層除去工程Ｓ２０を説明する説明図である。
　貫通孔形成工程Ｓ１０により貫通孔１１を形成した下地基板１０をＳｉＣ容器５０内に収容し、さらにＳｉＣ容器５０をＴａＣ容器６０に収容し、以下の条件で加熱した。
（加熱条件）
　加熱温度：１８００℃
　加熱時間：２ｈ
　エッチング量：８μｍ
（ＳｉＣ容器５０）
　材料:多結晶ＳｉＣ
　容器サイズ:直径６０ｍｍ×高さ４ｍｍ
　下地基板１０とＳｉＣ容器５０の底面との距離：２ｍｍ
（ＳｉＣ容器５０の詳細）
　ＳｉＣ容器５０は、図５に示すように、互いに嵌合可能な上容器５１と下容器５２とを備える嵌合容器である。上容器５１と下容器５２の嵌合部には、微小な間隙５３が形成されており、この間隙５３からＳｉＣ容器５０内の排気（真空引き）が可能なよう構成されている。
　ＳｉＣ容器５０は、下地基板１０が温度勾配の高温側に配置された状態で、温度勾配の低温側に配置されるＳｉＣ容器５０の一部と、下地基板１０とを相対させることで形成されるエッチング空間５４を有する。このエッチング空間５４は、下地基板１０とＳｉＣ容器５０の底面の間に設けられた温度差を駆動力として、下地基板１０からＳｉＣ容器５０へＳｉ原子およびＣ原子を輸送しエッチングする空間である。
　また、ＳｉＣ容器５０は、下地基板１０を中空に保持してエッチング空間５４を形成する基板保持具５５を有している。なお、この基板保持具５５は、加熱炉の温度勾配の方向によっては設けなくても良い。例えば、加熱炉が下容器５２から上容器５１に向かって温度が下がるよう温度勾配を形成する場合には、基板保持具５５を設けずに、下容器５２の底面に下地基板１０を配置しても良い。
（ＴａＣ容器６０）
　材料:ＴａＣ
　容器サイズ:直径１６０ｍｍ×高さ６０ｍｍ
　Ｓｉ蒸気供給源６４（Ｓｉ化合物）:ＴａＳｉ２
（ＴａＣ容器６０の詳細）
　ＴａＣ容器６０は、ＳｉＣ容器５０と同様に、互いに嵌合可能な上容器６１と下容器６２とを備える嵌合容器であり、ＳｉＣ容器５０を収容可能に構成されている。上容器６１と下容器６２の嵌合部には、微小な間隙６３が形成されており、この間隙６３からＴａＣ容器６０内の排気（真空引き）が可能なよう構成されている。
　ＴａＣ容器６０は、ＴａＣ容器６０内にＳｉ元素を含む気相種の蒸気圧を供給可能なＳｉ蒸気供給源６４を有している。Ｓｉ蒸気供給源６４は、加熱処理時にＳｉ元素を含む気相種の蒸気圧をＴａＣ容器６０内に発生させる構成であれば良い。
〈結晶成長工程Ｓ３０〉
　図８は、実施例１にかかる結晶成長工程Ｓ３０を説明する説明図である。
　歪層除去工程Ｓ２０により歪層１２を除去した下地基板１０を半導体材料４０と相対させて坩堝３０内に収容し、以下の条件で加熱した。
（加熱条件）
　加熱温度：２０４０℃
　加熱時間:７０ｈ
　成長厚み：５００μｍ
　Ｎ２ガス圧力：１０ｋＰａ
（坩堝３０）
　材料：炭化タンタル（ＴａＣ）及び／又はタングステン（Ｗ）
　容器サイズ：１０ｍｍ×１０ｍｍ×１．５ｍｍ
　下地基板１０－半導体材料４０間距離：１ｍｍ
（坩堝３０の詳細）
　坩堝３０は、下地基板１０と半導体材料４０との間に原料輸送空間３１を有している。この原料輸送空間３１を介して、半導体材料４０から下地基板１０上に原料に輸送している。
　図８（ａ）は、結晶成長工程Ｓ３０で用いる坩堝３０の一例である。この坩堝３０は、ＳｉＣ容器５０及びＴａＣ容器６０と同様に、互いに嵌合可能な上容器３２と下容器３３とを備える嵌合容器である。上容器３２と下容器３３の嵌合部には、微小な間隙３４が形成されており、この間隙３４から坩堝３０内の排気（真空引き）が可能なよう構成されている。
　さらに、坩堝３０は、原料輸送空間３１を形成する基板保持具３５を有している。この基板保持具３５は、下地基板１０と半導体材料４０との間に設けられ、半導体材料４０を高温側に、下地基板１０を低温側に配置して原料輸送空間３１を形成している。
　図８（ｂ）及び図８（ｃ）は、結晶成長工程Ｓ３０で用いる坩堝３０の他の例である。この図８（ｂ）及び図８（ｃ）の温度勾配は、図８（ａ）の温度勾配と逆に設定されており、下地基板１０が上側に配置されている。すなわち、図８（ａ）と同様に、半導体材料４０を高温側に、下地基板１０を低温側に配置して原料輸送空間３１を形成している。
　図８（ｂ）は、下地基板１０を上容器３２側に固定することで、半導体材料４０との間に原料輸送空間３１を形成する例を示している。
　図８（ｃ）は、上容器３２に貫通窓を形成し下地基板１０を配置することで、半導体材料４０との間に原料輸送空間３１を形成する例を示している。また、この図８（ｃ）に示すように、上容器３２と下容器３３との間に中間部材３６を設けることで、原料輸送空間３１を形成しても良い。
（半導体材料４０）
　材料：ＡｌＮ焼結体
　サイズ：横幅２０ｍｍ×縦幅２０ｍｍ×厚み５ｍｍ
（半導体材料４０の詳細）
　半導体材料４０のＡｌＮ焼結体は、以下の手順により焼結した。
　ＡｌＮ粉末をＴａＣブロックの枠内に入れ、適度な力で押し固めた。その後、熱分解炭素坩堝に押し固めたＡｌＮ粉末およびＴａＣブロックを収納し、以下の条件で加熱した。
　加熱温度：１８５０℃
　Ｎ２ガス圧力：１０ｋＰａ
　加熱時間：３ｈ
　図９は、実施例１の結晶成長工程Ｓ３０を示す模式図である。貫通孔１１を形成した下地基板１０に対して成長層２０を結晶成長させることにより、下地基板１０の水平方向に温度勾配を形成して、成長層２０の横方向成長の駆動力とすることができる。すなわち、水平方向への結晶成長がなされ難いＡｌＮ等の半導体材料であっても、貫通孔１１を形成した領域上に成長層２０を形成することができ、大口径な半導体基板を製造することができる。
　なお、実施例１により製造された半導体基板は、貫通孔１１を形成した領域上に形成された成長層２０においては、貫通系の転位は見受けられなかった。
《比較例１》
　比較例１にかかる下地基板１０は、実施例１の貫通孔１１に代わりに、溝１３を形成した。この下地基板１０に対して、実施例１と同様の条件で結晶成長工程Ｓ３０を施した。すなわち、比較例１は貫通孔形成工程Ｓ１０を行わず、結晶成長工程Ｓ３０を行った。
　図１０は、比較例１の結晶成長工程Ｓ３０を示す模式図である。比較例１により製造された半導体基板は、溝１３上において成長層２０が成長しない領域が形成された。
　すなわち、貫通孔１１に代わり溝１３を形成した場合には、溝１３の領域の温度が低下せず下地基板１０の水平方向に温度勾配が形成されない。その結果、横方向の成長駆動力が生じず、溝１３の領域に成長層２０が形成されないものと考えられる。
　実施例１および比較例１の結果から、貫通孔１１を有する下地基板１０に成長層２０を形成することで、大口径な半導体基板を製造できることが把握できる。
　１０　下地基板
　１１　貫通孔
　１２　歪層
　１３　溝
　２０　成長層
　３０　坩堝
　３１　原料輸送空間
　４０　半導体材料
　５０　ＳｉＣ容器
　６０　ＴａＣ容器
　Ｓ１０　貫通孔形成工程
　Ｓ２０　歪層除去工程
　Ｓ３０　結晶成長工程
　Ｓ３１　横方向成長工程
　Ｓ３２　縦方向成長工程

Claims (12)

  1. 　貫通孔を有する下地基板に成長層を形成する結晶成長工程を含む、半導体基板の製造方法。
  2. 　前記結晶成長工程は、前記下地基板の垂直方向に沿って温度勾配が形成されるよう加熱する工程である、請求項１に記載の半導体基板の製造方法。
  3. 　前記結晶成長工程は、前記下地基板と前記成長層の原料とを相対させて配置し、前記下地基板と前記原料との間に温度勾配が形成されるよう加熱する工程である、請求項１又は請求項２に記載の半導体基板の製造方法。
  4. 　前記結晶成長工程は、前記下地基板の水平方向に前記成長層が成長する横方向成長工程と、前記下地基板の垂直方向に前記成長層が成長する縦方向成長工程と、を有する、請求項１～３の何れか一項に記載の半導体基板の製造方法。
  5. 　前記下地基板に貫通孔を形成する貫通孔形成工程と、
    　前記貫通孔形成工程により導入された歪層を除去する歪層除去工程と、をさらに含む、請求項１～４の何れか一項に記載の半導体基板の製造方法。
  6. 　前記貫通孔形成工程は、レーザーを前記下地基板に照射することにより貫通孔を形成する工程である、請求項５に記載の半導体基板の製造方法。
  7. 　前記歪層除去工程は、熱処理することにより前記下地基板の歪層を除去する工程である、請求項５又は請求項６に記載の半導体基板の製造方法。
  8. 　前記下地基板は炭化ケイ素であり、
    　前記歪層除去工程は、前記下地基板をシリコン雰囲気下でエッチングする工程である、請求項５～７の何れか一項に記載の半導体基板の製造方法。
  9. 　請求項１～８の何れか一項に記載の製造方法により製造された半導体基板。
  10. 　下地基板の表面上に成長層を形成する前に、前記下地基板に貫通孔を形成する貫通孔形成工程を含む、成長層を形成する方法。
  11. 　前記貫通孔形成工程により導入された歪層を除去する歪層除去工程を含む、請求項１０に記載の方法。
  12. 　前記歪層除去工程は、熱処理することにより前記下地基板をエッチングする工程である、請求項１１に記載の方法。

     
PCT/JP2021/013745 2020-04-14 2021-03-30 半導体基板の製造方法、半導体基板、及び、成長層を形成する方法 WO2021210392A1 (ja)