WO2021194327A1 - 자연치아와 유사한 구조를 가진 치과용 보철물 및 그 제조 방법 - Google Patents

자연치아와 유사한 구조를 가진 치과용 보철물 및 그 제조 방법 Download PDF

Info

Publication number
WO2021194327A1
WO2021194327A1 PCT/KR2021/095002 KR2021095002W WO2021194327A1 WO 2021194327 A1 WO2021194327 A1 WO 2021194327A1 KR 2021095002 W KR2021095002 W KR 2021095002W WO 2021194327 A1 WO2021194327 A1 WO 2021194327A1
Authority
WO
WIPO (PCT)
Prior art keywords
natural teeth
ceramic particles
dental prosthesis
structure similar
material layer
Prior art date
Application number
PCT/KR2021/095002
Other languages
English (en)
French (fr)
Inventor
김용수
오경식
임형봉
김준형
김성민
손시원
김예나
Original Assignee
주식회사 하스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 하스 filed Critical 주식회사 하스
Priority to JP2022556521A priority Critical patent/JP2023519211A/ja
Priority to EP21775834.1A priority patent/EP4129232A4/en
Priority to CN202180023909.7A priority patent/CN115605160A/zh
Publication of WO2021194327A1 publication Critical patent/WO2021194327A1/ko
Priority to US17/934,315 priority patent/US20230021279A1/en

Abstract

본 발명은 자연치아와 유사한 구조를 가진 치과용 보철물 및 이를 제조하는 방법에 관한 것으로, 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하는 경화물이며, 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화물층과, 상기 제1 경화물층의 내측에 인접하며, 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화물층을 포함하여, 자연치아와 유사한 구조, 즉 표면이 법랑질이며 그 내부가 상아질인 자연치아와 유사한 구조 및 물성을 발현할 수 있는 치과용 보철물과, 이를 3차원 인쇄법을 이용하여 제조하는 방법을 개시한다.

Description

자연치아와 유사한 구조를 가진 치과용 보철물 및 그 제조 방법
본 발명은 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하는 경화물로 이루어진 치과용 보철물과 이를 제조하는 방법에 관한 것으로, 보다 구체적으로는 자연치아와 유사한 구조를 갖는 치과용 보철물과 이를 3차원 인쇄기법을 이용하여 제조하는 방법에 관한 것이다.
치과 산업은 치과에서 사용되는 장비 및 소재의 발전에 따라 같이 성장해 나가고 있는 것으로 볼 수 있다. 예를 들어 열간가압성형(heat-pressing)이나 Computer Aided Design/Computer Aided Manufacturing (CAD/CAM) 등의 장비로 인해 치과 산업의 발전이 이루어져 왔으며, 여기에 맞는 소재인 글라스-세라믹과 지르코니아 등의 소재발전이 이루어지고 있다.
이러한 변화로 인해 치과에서는 환자가 요구하는 심미적인 부분에서의 향상 및 원데이 보철로 인한 치과 치료에서의 시간단축 등의 개선을 이루어 오고 있지만, 자연치아와의 물성 차이로 인접치나 대합치의 마모, 그리고 음식물 저작 과정에서 파절 등의 문제점이 나타날 수 있으며, 이로 인해 구강 내의 2차 감염 등의 추가적인 문제점이 나타나고 있다.
이를 해결하기 위해 많은 연구가 이루어지고 있는 분야가 보철물의 자연치아와 유사한 구조 및 물성 등에 관한 것이다. 자연치아는 크라운 부분이 법랑질과 상아질로 이루어져 있으며, 각각의 물성 및 구조는 상이한 모습을 나타낸다. 법랑질의 경우, 무기물의 함량이 85 vol% 이상을 차지하며 밀집된(dense) 구조를 가지고 있으며(도 1 참조), 상아질의 경우에는 무기물과 유기물의 비율이 거의 유사하며 기공이 있는(porous) 구조를 가지고 있는 것이 특징이다(도 2 참조). 이런 소재 및 구조의 차이로 인해 법랑질과 상아질의 물성 또한 차이가 나는데, 예를 들어 탄성계수의 경우에는 법랑질이 약 50 내지 110 GPa의 값을 나타내며, 상아질은 약 20 GPa 이하의 값을 나타내고 있다. 또한 경도의 경우 법랑질에서 약 3 내지 6 GPa의 값을 나타내며, 상아질은 약 0.5 내지 1.5 GPa의 값을 나타내는 것으로 보고되고 있다.
이와 같은 자연치아와 가장 유사한 물성 및 구조를 가지는 소재의 개발은 기존에도 많은 연구가 이뤄지고 있어 다양한 소재들이 개발되어 오고 있다.
그 일예로, 한국등록특허 10-2037401호에는 자연치의 법랑질 수준의 광투과율을 나타내는 인공치아 소재에 대해 개시하고 있는데, 여기에서는 지르코니아와의 결합을 위해 젖음성을 향상시키는 ZrO 2가 3~5 중량%, 유리의 구조체 역할을 하는 SiO 2 69~79 중량%, Li 2O 10~13중량%, P 2O5 3~7중량%, Al 2O 3 1~4중량%, K 2O 1.0~2.5 중량%, MO(M= Ca, Zn 및 Mg 중 어느 하나) 0.1~3 중량% 및 조색제 0.5~2.0 중량%를 포함하는 실리케이트 유리 조성물을 300℃ ~ 600℃ 구간에서 1분 ~ 2시간동안 열처리하며, 상기 열처리에 의해 가시광선 투과율이 40~70%인 SiO 2를 기반으로 하는 실리케이트 유리를 기재하고 있다. 이러한 SiO 2를 기반으로 하는 실리케이트 유리를 지르코니아 외곽에 열간가압하면, 지르코니아 보철물을 거의 절삭하지 않고, 그 표면에 얇게 열간접합함으로써 기계 구조적 안정성을 유지할 수 있으며, 지르코니아의 색상이 얇은 코팅층을 투과하여 우러나오기 때문에 매우 역동적이고 깊이 있는 색감을 얻음으로써 보다 자연치아와 유사한 광학적 특성을 낼 수 있음을 기재하고 있다.
한편, 한국특허등록 10-1840142호에는 치과용 광경화성 수지 조성물을 이용하여 인공 치아를 제조하는 방법을 기재하고 있는데, 라디칼 중합성 유기 화합물, 충전제 및 광감수성 라디칼 중합 개시제를 포함하는 치과용 광경화성 수지조성물을 이용하여 인공 치아에 요구되는 강도, 내마모성, 경도, 저흡수성 등의 제반 특성을 갖추고, 게다가 심미성 및 기능성 등에도 뛰어난 인공 치아를 짧은 시간 특히 1 시간 미만의 짧은 시간 내에 원활하고용이하게 제조할 수 있는 방법을 기재하고 있으며, 특히 3차원 CAD 데이터를 기반으로 하는 제조방법을 기재하고 있다.
하지만 구조적으로 법랑질과 상아질의 이중구조를 가지는 보철물에 대한 기술은 아직 미흡한 실정이다.
본 발명은 법랑질과 상아질의 이중구조를 나타내는 자연치아와 유사한 구조와 물성을 발현할 수 있는 치과용 보철물을 제공하고자 한다.
또한 본 발명은 3차원 인쇄를 이용하여 자연치아와 유사한 법랑질의 밀집한 구조와 상아질의 기공이 있는 구조를 구현하여 이중구조를 가지고 각각의 물성을 구현하여 자연치아와 유사한 구조와 물성을 발현할 수 있는 치과용 보철물을 제조하는 방법을 제공하고자 한다.
본 발명은, 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하는 경화물이며, 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화물층과; 상기 제1 경화물층의 내측에 인접하며, 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화물층을 포함하는, 자연치아와 유사한 구조를 가진 치과용 보철물을 제공한다.
본 발명의 바람직한 일 구현예에 있어서, 제1 경화물층은 이축굴곡강도 300 내지 500 MPa, 탄성계수 50 내지 110 GPa이며, 경도가 3 내지 6 GPa을 만족하는 것일 수 있다.
본 발명의 바람직한 일 구현예에 있어서, 제2 경화물층은 이축굴곡강도 100 내지 300 MPa이고, 탄성계수 5 내지 20 GPa이며, 경도가 0.5 내지 1.5 GPa을 만족하는 것일 수 있다.
본 발명의 일 구현예에 있어서, 세라믹 입자는 바륨 실리케이트계 결정화 유리, 류사이트계 결정화 유리, 알루미나, 지르코니아 및 유리질 중에서 선택된 적어도 1종의 것일 수 있다.
본 발명의 일 구현예에 있어서, 세라믹 입자는 그 표면이 실란 처리된 것일 수 있다.
본 발명의 일 구현예에 있어서, 고분자 매트릭스는 하이드록시 에틸 메타크릴레이트 (hydroxy ethyl methacrylate, HEMA), 2,2-비스 [4-(2-하이드록시-3-메타크릴록시 프로폭시) 페닐] 프로판(2,2-bis [4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane, Bis-GMA), 트리에틸렌 글리콜디메타크릴레이트 (Triethylene glycoldimethacrylate, TEGDMA), 디우레탄디메타크릴레이트(diurethanedimethacrylate, UDMA), 우레탄 디메타크릴레이트(urethane dimethacrylate, UDM), 바이페닐디메타크릴레이트(biphenyldimethacrylate, BPDM), n-톨릴글리신-글리시딜메타크릴레이트(n-tolyglycine-glycidylmethacrylate, NTGE), 폴리에틸렌 글리콜 디메타크릴레이트(polyethylene glycol dimethacrylate, PEG-DMA) 및 올리고카보네이트 디메타크릴릭 에스테르(oligocarbonate dimethacrylic esters) 중에서 선택된 적어도 하나의 중합성 유기 화합물의 경화물일 수 있다.
본 발명의 바람직한 일 구현예에 있어서, 제1 경화물층은 밀집한 구조를 가지며, 제2 경화물층은 기공이 있는 구조를 가지는 것일 수 있다.
본 발명의 일 구현예에 있어서, 경화물은 광경화 또는 열경화에 의한 경화물인 것일 수 있다.
본 발명의 바람직한 일 구현예에서, 보철물은 3차원 인쇄를 통해 제조된 것일 수 있다.
본 발명의 다른 일 구현예에서는, 세라믹 입자와 중합성 유기화합물을 포함하는 경화성 조성물을 이용하여 3차원 인쇄를 통해 치과용 보철물을 제조하는 데 있어서, 경화성 조성물로 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화성 조성물과; 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화성 조성물을 이용하여 소정의 형상에 따라 적층하는 단계 및 경화시키는 단계를 포함하는, 자연치아와 유사한 구조를 가진 치과용 보철물의 제조방법을 제공한다.
본 발명의 일 구현예에 의한 제조방법에 있어서, 세라믹 입자로는 바륨 실리케이트계 결정화 유리, 류사이트계 결정화 유리, 알루미나, 지르코니아 및 유리질 중에서 선택된 적어도 1종의 것을 사용할 수 있다.
본 발명의 일 구현예에 의한 제조방법에 있어서, 중합성 유기 화합물은 하이드록시 에틸 메타크릴레이트 (hydroxy ethyl methacrylate, HEMA), 2,2-비스 [4-(2-하이드록시-3-메타크릴록시 프로폭시) 페닐] 프로판(2,2-bis [4-(2-hydroxy-3- methacryloyloxy propoxy) phenyl] propane, Bis-GMA), 트리에틸렌 글리콜디메타크릴레이트 (Triethylene glycoldimethacrylate, TEGDMA), 디우레탄디메타크릴레이트(diurethanedimethacrylate, UDMA), 우레탄 디메타크릴레이트(urethane dimethacrylate, UDM), 바이페닐디메타크릴레이트(biphenyldimethacrylate, BPDM), n-톨릴글리신-글리시딜메타크릴레이트(n-tolylglycine-glycidylmethacrylate, NTGE), 폴리에틸렌 글리콜 디메타크릴레이트(polyethylene glycol dimethacrylate, PEG-DMA) 및 올리고카보네이트 디메타크릴릭 에스테르(oligocarbonate dimethacrylic esters) 중에서 선택된 적어도 하나의 것을 사용할 수 있다.
본 발명의 바람직한 일 구현예에 의한 제조방법에 있어서, 소정의 형상은 제1 경화성 조성물의 경우 자연치아의 법랑질을 모사한 밀집한 구조이며, 제2 경화성 조성물의 경우 자연치아의 상아질을 모사한 기공을 갖는 구조일 수 있다.
본 발명의 일 구현예에 의한 제조방법에 있어서, 경화시키는 단계는 광경화 또는 열경화에 의해 수행될 수 있다.
본 발명은 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하여 치과용 보철물에 있어서 자연치아의 법랑질 및 상아질과 유사한 구조 및 물성을 가지는 보철물과 이를 3차원 인쇄기법을 이용하여 제조하는 방법을 제안함으로써, 치과용 보철 소재에서 요구되는 높은 심미성 및 인접치나 대합치와 유사한 물성을 갖는 치과용 보철물의 제조가 가능해지고, 치과용 보철물이 자연치아와 유사한 구조와 물성을 가짐에 따라 환자의 구강 내에 식립되어 인접치나 대합치인 자연치아를 마모시키는 것과 이로 인해 나타날 수 있는 2차 감염 등의 문제점을 사전에 예방할 수 있는 효과를 기대할 수 있다.
도 1 내지 2는 자연치아의 법랑질(도 1)과 상아질(도 2)의 미세구조를 나타낸 SEM 사진이다.
전술한, 그리고 추가적인 본 발명의 양상들은 첨부된 도면을 참조하여 설명되는 바람직한 실시 예들을 통하여 더욱 명백해질 것이다. 이하에서는 본 발명의 이러한 실시 예를 통해 당업자가 용이하게 이해하고 재현할 수 있도록 상세히 설명하기로 한다.
도 1 내지 2는 자연치아의 법랑질(도 1)과 상아질(도 2)의 미세구조를 나타낸 SEM 사진이다.
본 발명은 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하는 경화물을 통해 이와 같은 이중 구조를 갖는 자연치아를 최대한 구현하기 위한 일환으로, 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화물층과; 상기 제1 경화물층의 내측에 인접하며, 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화물층을 포함하는 치과용 보철물을 제안한다.
본 발명에서는 자연치아에 있어서 법랑질과 상아질의 미세구조적 차이 및 물성적 차이가 무기물과 유기물의 함량 및 구조에 따른 영향인 것으로 파악하였으며, 이를 구조적으로 발현할 수 있는 재료로서 중합성 유기 화합물과 세라믹 입자를 포함하는 경화성 조성물을 고려하였으며, 이러한 경화성 조성물을 이용하여 3차원 인쇄기법(3D printing)을 이용하는 것이 미세구조를 구현하는 데 있어서 최적함을 확인하였다. 특히 이중 구조를 구현하는 데 있어서 세라믹 입자의 크기 및 함량이 제어된 2종의 경화성 조성물을 이용하는 경우 물성적으로 자연치아의 법랑질과 상아질과 근접한 경화물을 얻을 수 있음을 확인하였다.
이러한 측면에서 바람직한 치과용 보철물은, 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화물층과 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화물층을 포함한다. 이때, 제2 경화물층은 제1 경화물층의 내측에 인접하여 형성되는바, 이는 자연치아의 법랑질과 상아질의 층 구조를 반영하여 구현해낼 수 있는 것으로 그 층의 형상에 제한을 두는 것은 아니다.
본 발명의 치과용 보철물에 있어서 세라믹 입자의 함량이 높을수록, 그리고 세라믹 입자의 크기가 작을수록 경화 후 세라믹 입자의 치밀함이 증가하여 물성의 증가를 나타낼 수 있다.
구체적으로, 세라믹 입자의 크기가 작고 함량이 높을수록 혼합체에서 나타나는 성질이 세라믹과 유사한 모습을 나타내어 높은 물성을 기대할 수 있으며, 반면 고분자의 함량이 높을수록 혼합체의 물성은 떨어지는 것을 확인할 수 있다. 또한, 고분자 내에 세라믹의 함량이 유사하더라도 세라믹 입자 크기가 작을수록 세라믹의 분포도가 증가하게 되고 이는 물성 향상의 변화를 나타낼 수 있다.
이러한 측면에서 제1 경화물층에 포함되는 세라믹 입자의 함량은 제1 경화물층 전체 조성 중 70중량% 내지 90중량%이며, 제1 경화물층에 포함되는 세라믹 입자는 그 평균입경이 100nm 내지 1,000nm인 것이 바람직하다.
한편, 제2 경화물층에 포함되는 세라믹 입자의 함량은 제2 경화물층 전체 조성 중 40중량% 내지 60중량%이며, 제2 경화물층에 포함되는 세라믹 입자는 그 평균입경이 10㎛ 내지 500㎛인 것이 바람직하다.
이와 같이 고분자 매트릭스 내에 분산된 세라믹 입자의 함량과 크기가 제어된 2종의 경화물층을 포함하는 경우, 제1 경화물층은 이축굴곡강도 300 내지 500 MPa, 탄성계수 50 내지 110 GPa이며, 경도가 3 내지 6 GPa을 만족하는 물성을 나타낼 수 있고, 제2 경화물층은 이축굴곡강도 100 내지 300 MPa이고, 탄성계수 5 내지 20 GPa이며, 경도가 0.5 내지 1.5 GPa을 만족하는 물성을 나타낼 수 있다. 이는 각각 자연치아의 법랑질과 상아질과 대응되는 정도의 대등한 물성으로, 음식물의 저작 및 인접치 및 대합치와의 맞닿는 부분으로서의 역할을 수행하기 위해 구조적으로 밀집되며 높은 물성을 나타내는 법랑질과, 저작과정에서 나타나는 응력을 적절한 탄성 및 유연성을 가지는 상아질의 물성을 구현해낼 수 있다.
상기 및 이하의 기재에 있어서 '세라믹 입자'는 치과용 보철물의 제조에서 사용할 수 있는 다양한 무기물을 들 수 있으며, 이에 한정이 있는 것은 아니나 구체적인 일례로 바륨 실리케이트계 결정화 유리, 류사이트계 결정화 유리, 알루미나, 지르코니아 및 유리질 중에서 선택된 적어도 1종의 것을 들 수 있다.
한편, 이러한 세라믹 입자는 그 표면을 실란 처리하는 것이 고분자 매트릭스와의 결합력을 향상시켜, 궁극적으로 치과용 보철물의 기계적 물성을 향상시키는 점에서 바람직할 수 있음은 물론이다. 이때 사용할 수 있는 실란 커플링제의 일례로는 (메타)아크릴기, 에폭시기, 비닐기, 아미노기, 메르캅토기 등의 반응성 관능기를 갖는 실란 커플링제를 들 수 있으며, 이들의 1 종 또는 2 종 이상을 사용할 수 있으나, 이에 한정되는 것은 아니다.
본 발명의 치과용 보철물에 있어서 매트릭스를 구성하는 고분자는, 당업계에 잘 알려져 있는 열중합성 또는 광중합성의 중합성 유기 화합물의 경화물을 들 수 있으며, 그 한정이 있는 것은 아니나, 일례로 하이드록시 에틸 메타크릴레이트 (hydroxy ethyl methacrylate, HEMA), 2,2-비스 [4-(2-하이드록시-3-메타크릴록시 프로폭시) 페닐] 프로판(2,2-bis [4-(2-hydroxy-3- methacryloyloxy propoxy) phenyl] propane, Bis-GMA), 트리에틸렌 글리콜디메타크릴레이트 (Triethylene glycoldimethacrylate, TEGDMA), 디우레탄디메타크릴레이트(diurethanedimethacrylate, UDMA), 우레탄 디메타크릴레이트(urethane dimethacrylate, UDM), 바이페닐디메타크릴레이트(biphenyldimethacrylate, BPDM), n-톨릴글리신-글리시딜메타크릴레이트(n-tolyglycine-glycidylmethacrylate, NTGE), 폴리에틸렌 글리콜 디메타크릴레이트(polyethylene glycol dimethacrylate, PEG-DMA) 및 올리고카보네이트 디메타크릴릭 에스테르(oligocarbonate dimethacrylic esters) 중에서 선택된 적어도 하나의 중합성 유기 화합물의 경화물을 들 수 있다.
본 발명에서는 이와 같은 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하는 경화물로 치과용 보철물을 제조하는 데 있어서, 3차원 인쇄를 이용하여 자연치아와 유사한 법랑질과 상아질로 이루어진 이중구조를 가진 보철물을 제조할 수 있다.
현재 치과용 보철물 제조에 있어서 3차원 인쇄는 금속과 고분자를 이용한 3차원 인쇄 방법이 많이 사용되고 있으며 금속을 이용한 3차원 인쇄는 레이저를 이용하여 금속을 녹여 녹인 물을 적층해서 제조하는 방법이며, 고분자는 광경화제를 이용하여 고분자를 적층하고 광원을 이용하여 고분자를 경화시키는 방법이다.
3차원 인쇄에서는 아직 세라믹만을 사용해서 인쇄하는 것은 연구 중에 있으며, 대부분 유기 화합물을 혼합하여 경화시키는 방법을 이용하고 있다. 이때 중요한 변수로는 세라믹과 고분자의 함량비와 세라믹의 입자 크기 등이 있으며, 이를 통해 경화 후의 물성 또한 조절이 가능하다. 본 발명에서는 상기와 같이 세라믹 입자의 함량비와 입자크기를 제어하고, 3차원 인쇄를 이용하여 자연치아 구조를 재현한다.
자연치아의 경우 법랑질은 도 1로 도시한 것과 같이 밀집한(dense)한 구조를 가지며, 상아질의 경우는 도 2로 도시한 것과 같이 기공의 구조, 보다 상세하게는 약 100 내지 1000 nm의 크기를 가지는 관모양의(tubular) 기공 구조를 갖는다. 본 발명에서 이러한 자연치아를 유사하게 구현해내기 위해 3차원 인쇄를 이용하여 이러한 미세 구조의 구현이 가능해지도록 한다.
본 발명에 따르면 자연치아와 같은 이중 구조를 3차원 인쇄를 이용하여 구현하며, 각 구조를 이루는 소재 및 각 소재의 함량 그리고 소재의 입자 크기에 따라서 경화 후 나타나는 물성의 변화를 줄 수 있다. 본 발명의 치과용 보철물은 치아와 매우 유사한 색상 및 물성을 나타내므로 치아용 보철재료로 사용하기에 적합하다.
치아 보철물은 자연 치아와 가장 유사한 심미성 및 물성을 나타내도록 하여, 구강 내 식립하였을 때 주변 치아와 가장 자연스럽게 어울림을 나타내는 것이 최종 목적 중의 하나이다.
이를 위해서 본 발명에서는 3차원 인쇄 방법을 이용하여 자연치아와 유사한 이중 구조를 나타내고 세라믹과 고분자의 함량 및 세라믹 입자 크기의 조절로 물성을 조절함으로써 자연치아의 법랑질과 상아질을 구현해낼 수 있는 치과용 보철물을 제조하는 방법을 제안한다.
구체적으로, 본 발명에 따른 자연치아와 유사한 구조를 가진 치과용 보철물의 제조방법은, 세라믹 입자와 중합성 유기화합물을 포함하는 경화성 조성물을 이용하여 3차원 인쇄를 통해 치과용 보철물을 제조하는 것으로, 경화성 조성물로 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화성 조성물과; 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화성 조성물을 이용하여 소정의 형상에 따라 적층하는 단계 및 경화시키는 단계를 포함한다.
자연치아와 유사한 구조를 가지는 세라믹을 이용한 치과용 보철물을 제조하기에는 3차원 인쇄 중에서 Stereo Lithography Apparatus(SLA), Digital Lighting Process(DLP) 등의 방법이 적합하며, 이 방법은 자연치아의 법랑질과 상아질의 구조를 가지게 각 층을 인쇄하고 이를 광원이나 열원을 이용하여 중합성 유기화합물을 경화시켜 고분자화하는 방법이다. 이때 광원의 일례로는 300 내지 600 nm의 광원을 들 수 있으나, 이에 한정이 있는 것은 아니다.
자연치아의 법랑질과 상아질 각각의 유사한 물성을 가지기 위해서는 세라믹 입자 크기의 변화와 세라믹과 고분자의 함량을 제어하여 다양한 물성을 확보할 수 있는데, 이러한 측면에서 경화성 조성물로 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화성 조성물과; 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화성 조성물을 이용하여 각 층을 인쇄하고 적층한다.
이때 사용하는 세라믹 입자는 상술한 것과 같이 바륨 실리케이트계 결정화 유리, 류사이트계 결정화 유리, 알루미나, 지르코니아 및 유리질 중에서 선택된 적어도 1종의 것을 사용할 수 있고, 이러한 세라믹 입자는 그 표면이 실란 처리된 것일 수 있음은 물론이다.
또한, 중합성 유기 화합물은 하이드록시 에틸 메타크릴레이트 (hydroxy ethyl methacrylate, HEMA), 2,2-비스 [4-(2-하이드록시-3-메타크릴록시 프로폭시) 페닐] 프로판(2,2-bis [4-(2-hydroxy-3- methacryloyloxy propoxy) phenyl] propane, Bis-GMA), 트리에틸렌 글리콜디메타크릴레이트 (Triethylene glycoldimethacrylate, TEGDMA), 디우레탄디메타크릴레이트(diurethanedimethacrylate, UDMA), 우레탄 디메타크릴레이트(urethane dimethacrylate, UDM), 바이페닐디메타크릴레이트(biphenyldimethacrylate, BPDM), n-톨릴글리신-글리시딜메타크릴레이트(n-tolyglycine-glycidylmethacrylate, NTGE), 폴리에틸렌 글리콜 디메타크릴레이트(polyethylene glycol dimethacrylate, PEG-DMA) 및 올리고카보네이트 디메타크릴릭 에스테르(oligocarbonate dimethacrylic esters) 중에서 선택된 적어도 하나의 것을 사용할 수 있다.
이러한 중합성 유기 화합물의 용액에 일례로 실란을 처리한 세라믹 입자를 상술한 2종의 경화성 조성물의 세라믹 입자 크기 및 세라믹 입자의 함량비에 따라 각각 혼합하고 이들 각각의 경화성 조성물을 3차원 인쇄 장비에 넣어 준다.
이러한 각각의 경화성 조성물을 이용하여 소정의 형상으로 적층을 진행하는데, 여기서 소정의 형상이란 제1 경화성 조성물의 경우 치아의 외부를 구성하는 조성으로 자연치아의 법랑질을 모사하여 밀집한 구조로, 그리고 제2 경화성 조성물의 경우는 내부를 구성하는 조성으로 자연치아의 상아질을 모사하여 기공이 있는 구조, 구체적으로는 관형상의 기공이 있는 구조로 적층을 진행하고, 적층을 진행하면서 경화시킨다.
이때 경화는 광경화 또는 열경화일 수 있는데, 광경화의 경우 광원을 조사하여 광경화가 나타나게 진행한다.
광경화제를 이용할 경우에는 필요한 광원을 공급함으로써 경화가 일어날 수 있으며, 열경화제의 경우에는 필요한 온도를 공급함으로써 경화를 진행시킬 수 있음은 물론이다.
본 발명에 따르면 3차원 인쇄법에 의해 제1 경화성 조성물과 제2 경화성 조성물을 이용하여 도 1로 도시한 법랑질을 모사한 미세구조를 갖는 제1 경화물층과 도 2로 도시한 상아질을 모사한 미세구조를 갖는 제2 경화물층을 포함하는 보철물을 얻을 수 있다. 이러한 보철물은 다음 표 1로 나타낸 것과 같은 물성을 발현할 수 있는 경화물층을 얻어낼 수 있으며, 이는 자연치아의 법랑질과 상아질에 대응되는 물성으로서, 본 발명에 따르면 자연치아와 유사한 구조를 갖는 치과용 보철물을 제공할 수 있게 되었다.
이축굴곡강도 (MPa) 탄성계수 (GPa) 비커스 경도 (GPa)
제1 경화물층 300 - 500 50 - 110 3.0 - 6.0
제 2 경화물층 100 - 300 5 - 20 0.5 - 1.5
본 발명은 도면에 도시된 일실시 예를 참고로 설명되었으나, 이는 예시적인 것에 불과하며, 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다.
본 발명은 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하는 경화물로 이루어진 치과용 보철물과 이를 제조하는 방법에 관한 것으로, 보다 구체적으로는 자연치아와 유사한 구조를 갖는 치과용 보철물과 이를 3차원 인쇄기법을 이용하여 제조하는 방법에 관한 것이다.
본 발명은 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하여 치과용 보철물에 있어서 자연치아의 법랑질 및 상아질과 유사한 구조 및 물성을 가지는 보철물과 이를 3차원 인쇄기법을 이용하여 제조하는 방법을 제안함으로써, 치과용 보철 소재에서 요구되는 높은 심미성 및 인접치나 대합치와 유사한 물성을 갖는 치과용 보철물의 제조가 가능해지고, 치과용 보철물이 자연치아와 유사한 구조와 물성을 가짐에 따라 환자의 구강 내에 식립되어 인접치나 대합치인 자연치아를 마모시키는 것과 이로 인해 나타날 수 있는 2차 감염 등의 문제점을 사전에 예방할 수 있는 효과를 기대할 수 있다.

Claims (14)

  1. 고분자 매트릭스 내에 분산된 세라믹 입자를 포함하는 경화물이며,
    세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화물층과;
    상기 제1 경화물층의 내측에 인접하며, 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화물층을 포함하는,
    자연치아와 유사한 구조를 가진 치과용 보철물.
  2. 제 1 항에 있어서, 제1 경화물층은 이축굴곡강도 300 내지 500 MPa, 탄성계수 50 내지 110 GPa이며, 경도가 3 내지 6 GPa을 만족하는 것임을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  3. 제 1 항에 있어서, 제2 경화물층은 이축굴곡강도 100 내지 300 MPa이고, 탄성계수 5 내지 20 GPa이며, 경도가 0.5 내지 1.5 GPa을 만족하는 것임을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  4. 제 1 항에 있어서, 세라믹 입자는 바륨 실리케이트계 결정화 유리, 류사이트계 결정화 유리, 알루미나, 지르코니아 및 유리질 중에서 선택된 적어도 1종의 것임을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  5. 제 1 항 또는 제 4 항에 있어서, 세라믹 입자는 그 표면이 실란 처리된 것임을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  6. 제 1 항에 있어서, 고분자 매트릭스는 하이드록시 에틸 메타크릴레이트 (hydroxy ethyl methacrylate, HEMA), 2,2-비스 [4-(2-하이드록시-3-메타크릴록시 프로폭시) 페닐] 프로판(2,2-bis [4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane, Bis-GMA), 트리에틸렌 글리콜디메타크릴레이트 (Triethylene glycoldimethacrylate, TEGDMA), 디우레탄디메타크릴레이트(diurethanedimethacrylate, UDMA), 우레탄 디메타크릴레이트(urethane dimethacrylate, UDM), 바이페닐디메타크릴레이트(biphenyldimethacrylate, BPDM), n-톨릴글리신-글리시딜메타크릴레이트(n-tolylglycine-glycidylmethacrylate, NTGE), 폴리에틸렌 글리콜 디메타크릴레이트(polyethylene glycol dimethacrylate, PEG-DMA) 및 올리고카보네이트 디메타크릴릭 에스테르(oligocarbonate dimethacrylic esters) 중에서 선택된 적어도 하나의 중합성 유기 화합물의 경화물인 것임을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  7. 제 1 항에 있어서, 제1 경화물층은 밀집한 구조를 가지며, 제2 경화물층은 기공이 있는 구조를 가지는 것을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  8. 제 1 항에 있어서, 경화물은 광경화 또는 열경화에 의한 경화물인 것임을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  9. 제 1 항에 있어서, 3차원 인쇄를 통해 제조된 것임을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물.
  10. 세라믹 입자와 중합성 유기화합물을 포함하는 경화성 조성물을 이용하여 3차원 인쇄를 통해 치과용 보철물을 제조하는 데 있어서,
    경화성 조성물로 세라믹 입자의 함량이 70 내지 90%이고, 세라믹 입자는 그 평균입경이 100 내지 1,000 nm인 제 1 경화성 조성물과; 세라믹 입자의 함량이 40 내지 60 중량%이고, 세라믹 입자는 그 평균입경이 10 내지 500 ㎛인 제2 경화성 조성물을 이용하여 소정의 형상에 따라 적층하는 단계 및
    경화시키는 단계를 포함하는,
    자연치아와 유사한 구조를 가진 치과용 보철물의 제조방법.
  11. 제 10 항에 있어서, 세라믹 입자로는 바륨 실리케이트계 결정화 유리, 류사이트계 결정화 유리, 알루미나, 지르코니아 및 유리질 중에서 선택된 적어도 1종의 것을 사용하는 것을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물의 제조방법.
  12. 제 10 항에 있어서, 중합성 유기 화합물은 하이드록시 에틸 메타크릴레이트 (hydroxy ethyl methacrylate, HEMA), 2,2-비스 [4-(2-하이드록시-3-메타크릴록시 프로폭시) 페닐] 프로판(2,2-bis [4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane, Bis-GMA), 트리에틸렌 글리콜디메타크릴레이트 (Triethylene glycoldimethacrylate, TEGDMA), 디우레탄디메타크릴레이트(diurethanedimethacrylate, UDMA), 우레탄 디메타크릴레이트(urethane dimethacrylate, UDM), 바이페닐디메타크릴레이트(biphenyldimethacrylate, BPDM), n-톨릴글리신-글리시딜메타크릴레이트(n-tolyglycine-glycidylmethacrylate, NTGE), 폴리에틸렌 글리콜 디메타크릴레이트(polyethylene glycol dimethacrylate, PEG-DMA) 및 올리고카보네이트 디메타크릴릭 에스테르(oligocarbonate dimethacrylic esters) 중에서 선택된 적어도 하나의 것을 사용하는 것을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물의 제조방법.
  13. 제 10 항에 있어서, 소정의 형상은 제1 경화성 조성물의 경우 자연치아의 법랑질을 모사한 밀집한 구조이며, 제2 경화성 조성물의 경우 자연치아의 상아질을 모사한 기공을 갖는 구조인 것을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물의 제조방법.
  14. 제 10 항에 있어서, 경화시키는 단계는 광경화 또는 열경화에 의해 수행되는 것을 특징으로 하는, 자연치아와 유사한 구조를 가진 치과용 보철물의 제조방법.
PCT/KR2021/095002 2020-03-26 2021-01-20 자연치아와 유사한 구조를 가진 치과용 보철물 및 그 제조 방법 WO2021194327A1 (ko)