WO2021149803A1 - 化粧シート、化粧板及び化粧シートの製造方法 - Google Patents

化粧シート、化粧板及び化粧シートの製造方法 Download PDF

Info

Publication number
WO2021149803A1
WO2021149803A1 PCT/JP2021/002264 JP2021002264W WO2021149803A1 WO 2021149803 A1 WO2021149803 A1 WO 2021149803A1 JP 2021002264 W JP2021002264 W JP 2021002264W WO 2021149803 A1 WO2021149803 A1 WO 2021149803A1
Authority
WO
WIPO (PCT)
Prior art keywords
recess
layer
decorative sheet
pattern layer
pattern
Prior art date
Application number
PCT/JP2021/002264
Other languages
English (en)
French (fr)
Inventor
雄一 伊勢森
貴矢 大野
勝利 田畑
一葉 大竹
誠司 谷定
靖弘 鈴木
勇二 大原
勇樹 高木
遼 中澤
Original Assignee
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大日本印刷株式会社 filed Critical 大日本印刷株式会社
Priority to KR1020227027523A priority Critical patent/KR20220130722A/ko
Priority to JP2021572818A priority patent/JPWO2021149803A1/ja
Priority to US17/794,762 priority patent/US20230071952A1/en
Priority to EP21744624.4A priority patent/EP4108450A1/en
Priority to CN202180009775.3A priority patent/CN114981075A/zh
Publication of WO2021149803A1 publication Critical patent/WO2021149803A1/ja

Abstract

本発明は、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を有する化粧シートを提供する。 本発明は、基材の一方に、絵柄層と、透明性樹脂層とを少なくともこの順に有し、上記絵柄層は、特徴部分と非特徴部分とを備え、上記透明性樹脂層は、上記絵柄層を有する側と反対側に、上記絵柄層の特徴部分と同調した凹部（Ｄ１）を有し、上記絵柄層は、上記基材を有する側と反対側に、上記凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を有し、上記凹部（Ｄ１）の深さＨは、上記凹部（Ｄ２）の深さｈよりも大きいことを特徴とする化粧シートに関する。

Description

化粧シート、化粧板及び化粧シートの製造方法
本発明は、化粧シート、化粧板及び化粧シートの製造方法に関する。
建材、家具、家電製品等において、使用する部材を加飾したい場合には、意匠が施された化粧シートを貼着した化粧板が一般的に用いられている。
化粧板に視覚による意匠性を付与するために、化粧シートにエンボス加工等を施して、凹凸形状を形成し、立体的な視覚効果を付与することがある。
例えば、特許文献１では、基材シートの一方の面側に、絵柄が印刷された絵柄印刷層、上記絵柄と同調する凹凸模様を有する透明熱可塑性樹脂層、上記透明熱可塑性樹脂層の表面を保護する表面保護層、及び上記絵柄と同調する艶状態による模様を有する艶調整層をこの順に積層してなり、上記凹凸模様の凹凸に上記表面保護層を構成する樹脂が入り込んでいることを特徴とする化粧シートが開示されている。
特許文献１の化粧シートでは、透明熱可塑性樹脂層の表面保護層を有する側の面に凹凸模様が形成されている。これにより、絵柄印刷層の絵柄と透明熱可塑性樹脂層の凹凸模様とを同調させて、触感及び立体感を向上させ、絵柄のリアルさを向上させている。
近年、絵柄層の絵柄模様と、化粧シートに形成された凹凸形状とが更に同調した極めて優れた意匠性が求められており、特許文献１の化粧シートでは未だ十分であるとはいえず、更なる改善の余地があった。
特開２０１６－１８２７４８号公報
本発明は、上述した課題を解決するものであり、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を有する化粧シートを提供することを目的とする。
本発明者らは、上述した課題を解決するため鋭意検討したところ、基材の一方に、絵柄層と、透明性樹脂層とを少なくともこの順に有する化粧シートにおいて、上記透明性樹脂層が上記絵柄層の特徴部分と同調した凹部（Ｄ１）を有し、上記絵柄層が上記凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を有しており、上記凹部（Ｄ１）の深さＨが上記凹部（Ｄ２）の深さｈよりも大きいことにより、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を奏することを見出し、本発明を完成するに至った。
すなわち、本発明の化粧シートは、基材の一方に、絵柄層と、透明性樹脂層とを少なくともこの順に有し、上記絵柄層は、特徴部分と非特徴部分とを備え、上記透明性樹脂層は、上記絵柄層を有する側と反対側に、上記絵柄層の特徴部分と同調した凹部（Ｄ１）を有し、上記絵柄層は、上記基材を有する側と反対側に、上記凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を有し、上記凹部（Ｄ１）の深さＨは、上記凹部（Ｄ２）の深さｈよりも大きいことを特徴とする。
本発明の化粧シートにおいて、上記凹部（Ｄ１）の深さＨに対する上記凹部（Ｄ２）の深さｈの比率（ｈ／Ｈ）は、０．２５以上０．６０以下であることが好ましい。
また、本発明の化粧シートは、上記透明性樹脂層の上記絵柄層を有する側と反対側に表面保護層を有することが好ましい。
また、本発明の化粧シートにおいて、上記絵柄層の特徴部分は、木目の導管、節、年輪及び斑、又は、岩石の中の異なった結晶成分の縞や割れ模様であることが好ましい。
また、本発明の化粧シートにおいて、上記絵柄層の特徴部分と非特徴部分との色差ΔＥは、１．３以上であることが好ましい。
また、本発明の化粧板は、被着材上に本発明の化粧シートを備えることを特徴とする。
また、本発明の化粧シートの製造方法は、基材の一方に、特徴部分と非特徴部分とを備えた絵柄層と、透明性樹脂層とを少なくともこの順に積層する積層工程と、上記透明性樹脂層の上記絵柄層を有する側と反対側からエンボス加工を施し、上記透明性樹脂層の上記絵柄層を有する側と反対側に上記絵柄層の特徴部分と同調した凹部（Ｄ１）、及び、上記絵柄層の上記基材を有する側と反対側に上記凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を賦形する賦形工程とを有し、上記凹部（Ｄ１）の深さＨは、上記凹部（Ｄ２）の深さｈよりも大きいことを特徴とする。
本発明は、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を有する化粧シートを提供することができる。
本発明の化粧シートの一例を模式的に示す断面図である。 （ａ）及び（ｂ）は、本発明の化粧シートの好ましい一例を模式的に示す断面図である。 （ａ）～（ｃ）は、本発明の化粧シートの一例を模式的に示す断面図である。 （ａ）は、本発明の化粧シートの一例を模式的に示す斜視図であり、（ｂ）は、本発明の化粧シートの一例を模式的に示す上面図であり、（ｃ）は、本発明の化粧シートの一例を模式的に示す断面図である。 本発明の化粧シートの好ましい一例を模式的に示す断面図である。
＜化粧シート＞
以下、本発明の化粧シートについて説明する。
なお、以下の記載において、「～」で表される数値範囲の下限上限は「以上以下」を意味する（例えば、α～βならば、α以上β以下である）。
本発明の化粧シートは、基材の一方に、少なくとも絵柄層と、透明性樹脂層と、透明熱可塑性樹脂層と、表面保護層とをこの順に有する。
図１は、化粧シートの一例を模式的に示す断面図である。
図１に示す本発明の化粧シートの一例において、化粧シート１０は、基材１の一方に、少なくとも絵柄層２と、透明性樹脂層３とをこの順に有する。
絵柄層２は、特徴部分２ａと、非特徴部分２ｂを有している。
また、透明性樹脂層３は、絵柄層２を有する側と反対側に、絵柄層２の特徴部分と同調した凹部（Ｄ１）を有し、絵柄層２は、基材１を有する側と反対側に、凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を有する。
まずは、化粧シート１０を構成する各層について説明する。
（基材）
本発明の化粧シート１０は、基材１を有する。
上記基材１としては、特に限定されないが、非ハロゲン系熱可塑性樹脂を含有することが好ましい。
上記非ハロゲン系熱可塑性樹脂としては、低密度ポリエチレン（線状低密度ポリエチレンを含む）、中密度ポリエチレン、高密度ポリエチレン、エチレン－αオレフィン共重合体、ホモポリプロピレン、ポリメチルペンテン、ポリブテン、エチレン－プロピレン共重合体、プロピレン－ブテン共重合体、エチレン－酢酸ビニル共重合体、エチレン－酢酸ビニル共重合体ケン化物、又は、これらの混合物等のオレフィン系熱可塑性樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリエチレンナフタレート－イソフタレート共重合体、ポリカーボネート、ポリアリレート等の熱可塑性エステル系樹脂、ポリメタアクリル酸メチル、ポリメタアクリル酸エチル、ポリアクリル酸エチル、ポリアクリル酸ブチル等のアクリル系熱可塑性樹脂、ナイロン－６、ナイロン－６６等のポリアミド系熱可塑性樹脂、又は、ポリイミド、ポリウレタン、ポリスチレン、アクリロニトリル－ブタジエン－スチレン樹脂等が挙げられる。
これらの非ハロゲン系熱可塑性樹脂は単独で用いてもよいし、２種以上を混合して用いてもよい。
なかでも、絵柄層２の印刷適性に優れ、安価である点で、オレフィン系熱可塑性樹脂が好ましい。
基材１は、着色されていてもよい。この場合は、上記非ハロゲン系熱可塑性樹脂に対して着色剤（顔料又は染料）を添加して着色することができる。
上記着色剤としては、例えば、二酸化チタン、カーボンブラック、酸化鉄等の無機顔料、フタロシアニンブルー等の有機顔料のほか、各種の染料も使用することができる。
これらは、公知又は市販のものから１種又は２種以上を選ぶことができる。また、着色剤の添加量も、所望の色合い等に応じて適宜設定すれば良い。
基材１は、必要に応じて、充填剤、艶消し剤、発泡剤、難燃剤、滑剤、帯電防止剤、酸化防止剤、紫外線吸収剤、光安定化剤等の各種の添加剤が含まれていてもよい。
基材１の厚みは、特に限定されないが、４０μｍ以上２００μｍ以下が好ましい。
基材１は、単層又は多層のいずれで構成されていてもよい。
（絵柄層）
化粧シート１０は、絵柄層２を有する。
絵柄層２は、化粧シート１０に装飾性を付与する層である。
絵柄層２としては、例えば、種々の模様をインキと印刷機を使用して印刷することにより形成される図柄層であってもよいし、隠蔽層と図柄層とを組み合わせた層であってもよい。
上記隠蔽層を設けることにより、上述した基材１が着色していたり色ムラがあったりする場合に、意図した色彩を与えて表面の色を整えることができる。
また、図柄層を設けることで、木目模様、大理石模様（例えばトラバーチン大理石模様）等の岩石の表面を模した石目模様、布目や布状の模様を模した布地模様、タイル貼模様、煉瓦積模様等、あるいはこれらを複合した寄木、パッチワーク等の絵柄模様を化粧シートに付与することができる。
これらの絵柄模様は通常の黄色、赤色、青色、及び黒色のプロセスカラーによる多色印刷によって形成される他、模様を構成する個々の色を用意して行う特色による多色印刷等によっても形成される。
絵柄層２に用いられるインキ組成物としては、バインダー樹脂に顔料、染料等の着色剤、体質顔料、溶剤、安定剤、可塑剤、触媒、硬化剤等を適宜混合したものが使用される。
上記バインダー樹脂としては特に制限はなく、例えば、ウレタン樹脂、アクリル樹脂、ウレタン－アクリル樹脂、ウレタン－アクリル共重合体樹脂、塩化ビニル／酢酸ビニル共重合体樹脂、塩化ビニル／酢酸ビニル／アクリル共重合体樹脂、アクリル樹脂、ポリエステル樹脂、ニトロセルロース樹脂等が好ましく挙げられる。上記バインダー樹脂としてはこれらの中から任意のものを、１種単独で又は２種以上を混合して用いることができる。
上記着色剤としては、カーボンブラック（墨）、鉄黒、チタン白、アンチモン白、黄鉛、チタン黄、弁柄、カドミウム赤、群青、コバルトブルー等の無機顔料、キナクリドンレッド、イソインドリノンイエロー、フタロシアニンブルー等の有機顔料、又は染料、アルミニウム、真鍮等の鱗片状箔片からなる金属顔料、二酸化チタン被覆雲母、塩基性炭酸鉛等の鱗片状箔片からなる真珠光沢（パール）顔料等が好ましく挙げられる。
これらは１種単独で又は２種以上を併用して用いることができる。
絵柄層２は、特徴部分２ａと非特徴部分２ｂとを有する。
特徴部分２ａとは、絵柄層２の絵柄模様を認識させ得る特徴を有する部分をいい、例えば、絵柄層２が木目模様の場合には、木目の導管、節及び年輪及び斑が該当し、絵柄層２が石目模様の場合には、岩石の中の異なった結晶成分の縞や割れによって表現される模様（割れ模様）が該当する。
また、非特徴部分２ｂとは、上記特徴部分２ａ以外の部分をいう。
絵柄層２において、特徴部分２ａと非特徴部分２ｂとの色差ΔＥは、１．３以上であることが好ましい。
このような色差ΔＥとすることにより、意匠性をより優れたものとすることができる。
上記色差ΔＥは、１．５以上であることがより好ましく、１．８以上であることが更に好ましく、２．０以上であることが特に好ましい。
本明細書において、色差ΔＥの測定方法及び算出方法は以下の通りである。
化粧シート１０において、特徴部分２ａと非特徴部分２ｂのＬ＊ａ＊ｂ＊表色系のＬ＊、ａ＊及びｂ＊を、分光測色計（日本電色工業社製ＳＥ６０００）を使用して、化粧シート１０の透明性樹脂層３を有する側（表面保護層４を有する場合には表面保護層を有する側）の表面へ入射角１０度（透明樹脂層３側表面の法線方向を０度とする）で光（Ｄ６５光源）を照射し、全光線反射光（鏡面反射光＋拡散反射光）に基づいて測定する。
ここで、特徴部分２ａにおけるＬ＊、ａ＊及びｂ＊をそれぞれＬ１ ＊、ａ１ ＊及びｂ１ ＊とし、非特徴部分２ｂにおけるＬ＊、ａ＊及びｂ＊をそれぞれＬ２ ＊、ａ２ ＊及びｂ２ ＊とする。
なお、「Ｌ＊ａ＊ｂ＊表色系」は、ＣＩＥ（国際照明委員会）で規格化され、ＪＩＳ　Ｚ８７８１－４：２０１３で採用されている表色系を意味する。また、Ｌ＊ａ＊ｂ＊表色系において、明度はＬ＊で表され、色相及び彩度を示す色度はａ＊、ｂ＊で表される。
上記測定した数値を下記式に代入することにより算出することができる。
色差ΔＥ＝（（Ｌ１ ＊－Ｌ２ ＊）２＋（ａ１ ＊－ａ２ ＊）２＋（ｂ１ ＊－ｂ２ ＊）２）１／２
絵柄層２の厚みとしては、特に限定されず、例えば、０．１μｍ以上が好ましく、０．５μｍ以上６００μｍ以下がより好ましい。絵柄層２の厚みが上記範囲内にあれば、化粧シート１０に優れた意匠を付与することができ、また隠蔽性を付与することができる。
絵柄層２を形成する方法としては、例えば、グラビア印刷法、オフセット印刷法、スクリーン印刷法、フレキソ印刷法、静電印刷法、インクジェット印刷法等が挙げられる。また、隠蔽層を形成する場合には、例えば、ロールコート法、ナイフコート法、エアーナイフコート法、ダイコート法、リップコート法、コンマコート法、キスコート法、フローコート法、ディップコート法等の各種コーティング法等も挙げられる。
（透明性樹脂層）
化粧シート１０は、透明性樹脂層３を有する。
透明性樹脂層３としては、熱可塑性樹脂により形成された層であることが好ましい。
透明性樹脂層３は、絵柄層２を可視できれば特に限定されず、無色透明、着色透明、半透明等のいずれも含む。
上記熱可塑性樹脂としては、例えば、ポリエチレン、ポリプロピレン、ポリブテン、ポリメチルペンテン、オレフィン系熱可塑性エラストマー等のオレフィン樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナレフタレート、エチレングリコール－テレフタル酸－イソフタール酸共重合体樹脂、テレフタル酸－エチレングリコール－１，４シクロヘキサンジメタノール共重合体樹脂、ポリエステル系熱可塑性エラストマー等のポリエステル樹脂、ポリメチル（メタ）アクリレート、メチル（メタ）アクリレート－ブチル（メタ）アクリレート共重合体樹脂、メチル（メタ）アクリレート－スチレン共重合体樹脂等のアクリル樹脂、ポリカーボネート樹脂、ポリ塩化ビニル、ポリスチレン、アイオノマー等が挙げられる。
なかでも、引張強度が高く、耐薬品性能に優れ、生産工程面で優れていることからポリエチレン又はポリプロピレンがより好ましい。
なお、本明細書において、（メタ）アクリレートとは、アクリレート又はメタクリレートを意味する。
上記ポリエチレンは、エチレンの単独重合体であってもよいし、エチレンと、エチレンと共重合可能な他のコモノマー（例えば、プロピレン、１－ブテン、１－ヘキセン、１－オクテン等のα－オレフィン、酢酸ビニル、ビニルアルコール等）との共重合体であってもよい。
ポリエチレン樹脂としては、例えば、高密度ポリエチレン（ＨＤＰＥ）、中密度ポリエチレン（ＭＤＰＥ）、低密度ポリエチレン（ＬＤＰＥ）、直鎖低密度ポリエチレン（ＬＬＤＰＥ）、超低密度ポリエチレン（ＶＬＤＰＥ）、超高分子量ポリエチレン（ＵＨＭＷＰＥ）、架橋ポリエチレン（ＰＥＸ）等が挙げられる。
これらのポリエチレンは、１種単独で使用してもよいし、２種以上を併用してもよい。
上記ポリプロピレンは、プロピレンの単独重合体であってもよいし、プロピレンと、プロピレンと共重合可能な他のコモノマー（例えば、エチレン、１－ブテン、１－ヘキセン、１－オクテン等のα－オレフィン；酢酸ビニル、ビニルアルコール等）との共重合体であってもよい。
これらのポリプロピレンは１種単独で使用してもよいし、２種以上を併用してもよい。
本発明においては、優れた耐擦傷性と曲げ加工性の観点から、プロピレンの単独重合体（ホモポリプロピレン）であることが特に好ましい。
透明性樹脂層３は、１層により構成されていてもよいし、２層以上の層により構成されてもよい。
透明性樹脂層３の厚みは、優れた耐擦傷性と曲げ加工性とを得る観点から、３０μｍ以上１５０μｍ以下が好ましく、４０μｍ以上１２０μｍ以下がより好ましい。
透明性樹脂層３が２層以上の層により構成される場合、透明性樹脂層３の総厚みは、３０μｍ以上１５０μｍ以下が好ましく、４０μｍ以上１２０μｍ以下がより好ましい。
透明性樹脂層３が複数の層から構成される場合、形成する樹脂の種類は同じであっても異なっていてもよく、また複数の樹脂からなる基材の厚みは同じであっても異なっていてもよい。
透明性樹脂層３を２層以上に積層する方法としては、一般的な方法であれば限定されず、ドライラミネート法や押出し熱ラミネート等が挙げられる。
透明性樹脂層３は、本発明の趣旨を逸脱しない範囲で、けん化処理、グロー放電処理、コロナ放電処理、プラズマ放電処理、紫外線（ＵＶ）処理、及び火炎処理等の表面処理を行ってもよい。
（表面保護層）
化粧シート１０は、透明性樹脂層３の絵柄層２を有する側と反対側に表面保護層を有することが好ましい。
図２（ａ）及び（ｂ）は、本発明の化粧シートの好ましい一例を模式的に示す断面図である。
図２（ａ）及び（ｂ）に示す本発明の化粧シートの好ましい一例において、化粧シート１０は、基材１の一方に、少なくとも絵柄層２と、透明性樹脂層３と、表面保護層４とをこの順に有する。
表面保護層４は、図２（ａ）のように、凹部を有していてもよいし、図２（ｂ）のように、凹部を有さなくてもよい。
表面保護層４は、化粧シート１０に耐久性（耐傷性、耐汚染性、耐候性等）を付与する層であり、表面保護層４を有することにより、より好適に絵柄層２の保護が可能となり、化粧シート１０自体の傷付きによる意匠性の低下を好適に防止できる。
なお、表面保護層４は、単一の層構成であってもよく、同一又は異なる材料からなる複数の層構成であってもよいし、下記に示す材料を適宜混合させてもよい。
表面保護層４としては、特に限定されないが、例えば、２液硬化性樹脂や電離放射線硬化性樹脂組成物の架橋硬化物からなるものが挙げられる。
上記架橋硬化物は透明であることが好ましく、透明である限り、絵柄層２が視認できる範囲であれば、半透明でも着色されていてもよい。
上記２液硬化性樹脂としては、上記接着用プライマー層のバインダー樹脂を用いればよい。
上記電離放射線硬化性樹脂としては、例えば、分子中にラジカル重合性不飽和結合又はカチオン重合性官能基を有するオリゴマー（以下、所謂プレポリマー、マクロモノマー等も包含する）及び／又は分子中にラジカル重合性不飽和結合又はカチオン重合性官能基を有するモノマーが好ましく用いられる。なお、ここで電離放射線とは、分子を重合或いは架橋させ得るエネルギーを有する電磁波又は荷電粒子を意味し、通常は、電子線（ＥＢ）又は紫外線（ＵＶ）が一般的である。
上記オリゴマー又はモノマーとしては、例えば、分子中に（メタ）アクリロイル基、（メタ）アクリロイルオキシ基等のラジカル重合性不飽和基、エポキシ基等のカチオン重合性官能基等を有する化合物が挙げられる。これらオリゴマー、モノマーは、単独で用いるか、或いは複数種混合して用いることができる。なお、本明細書において、上記（メタ）アクリロイル基とは、アクリロイル基又はメタクリロイル基を意味する。
上記分子中にラジカル重合性不飽和基を有するオリゴマーとしては、例えば、ウレタン（メタ）アクリレート、ポリエステル（メタ）アクリレート、エポキシ（メタ）アクリレート、メラミン（メタ）アクリレート、トリアジン（メタ）アクリレート等のオリゴマーが好ましく使用でき、ウレタン（メタ）アクリレートオリゴマーがさらに好ましい。分子量としては、通常２５０～１０万程度のものが用いられる。
上記分子中にラジカル重合性不飽和基を有するモノマーとしては、例えば、多官能モノマーが好ましく、多官能（メタ）アクリレートがより好ましい。
上記多官能（メタ）アクリレートとしては、例えば、ジエチレングリコールジ（メタ）アクリレート、プロピレングリコールジ（メタ）アクリレート、ビスフェノールＡエチレンオキサイド変性ジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、トリメチロールプロパンエチレンオキサイドトリ（メタ）アクリレート、ジペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート｛５官能（メタ）アクリレート｝、ジペンタエリスリトールヘキサ（メタ）アクリレート｛６官能（メタ）アクリレート｝等が挙げられる。ここで、多官能モノマーとは、複数のラジカル重合性不飽和基を有するモノマーをいう。
上記電離放射線硬化性樹脂組成物が、ウレタンアクリレートオリゴマー及び多官能モノマーからなる電離放射線硬化性樹脂成分を含むことがさらに好ましく、電離放射線硬化性樹脂成分として、ウレタンアクリレートオリゴマー／多官能モノマー（質量比）が６／４～９／１であることが特に好ましい。この質量比の範囲であれば、耐擦傷性により優れたものにできる。
なお、必要に応じ、上記電離放射線硬化性樹脂成分に加えて、単官能モノマーを適宜使用しても良い。
上記単官能モノマーとしては、例えば、メチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、フェノキシエチル（メタ）アクリレート等が挙げられる。
上記電離放射線硬化性樹脂組成物を紫外線にて架橋させる場合、電離放射線硬化性樹脂組成物に光重合開始剤を添加することが好ましい。
上記電離放射線硬化性樹脂組成物がラジカル重合性不飽和基を有する樹脂系の場合、上記光重合開始剤として、アセトフェノン類、ベンゾフェノン類、チオキサントン類、ベンゾイン類、ベンゾインメチルエーテル類を単独又は混合して用いることができる。
また、上記電離放射線硬化性樹脂組成物がカチオン重合性不飽和基を有する樹脂系の場合、上記光重合開始剤として、芳香族ジアゾニウム塩、芳香族スルホニウム塩、芳香族ヨードニウム塩、メタセロン化合物、ベンゾインスルホン酸エステル等を単独又は混合物として用いることができる。なお、これらの光重合開始剤の添加量としては、電離放射線硬化性樹脂成分１００質量部に対して０．１～１０質量部程度である。
なお、上記電離放射線硬化性樹脂組成物には、更に必要に応じて各種添加剤を加えても良い。これらの添加剤としては、例えば、ウレタン樹脂、ポリビニルアセタール樹脂、ポリエステル樹脂、ポリオレフィン樹脂、スチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、アセタール樹脂、塩化ビニル－酢酸ビニル共重合体樹脂、酢酸ビニル樹脂、アクリル樹脂、セルロース系樹脂等の熱可塑性樹脂、シリコーン樹脂、ワックス、弗素樹脂等の滑剤、ベンゾトリアゾール、ベンゾフェノン、トリアジン等の紫外線吸収剤、ヒンダードアミン系ラジカル捕捉剤等の光安定剤、染料、顔料等の着色剤等である。
なお、電離放射線の電子線源としては、例えば、コッククロフトワルトン型、バンデグラフト型、共振変圧器型、絶縁コア変圧器型、或いは、直線型、ダイナミトロン型、高周波型等の各種電子線加速器を用い、７０～１０００ｋｅＶのエネルギーをもつ電子を照射するものが使用できる。また、電離放射線の照射線量は、例えば、１～１０Ｍｒａｄ程度であることが好ましい。
また、上記電離放射線の紫外線源としては、例えば、超高圧水銀灯、高圧水銀灯、低圧水銀灯、カーボンアーク灯、ブラックライト、メタルハライドランプ等の光源が使用でき、上記紫外線の波長としては通常１９０～３８０ｎｍの波長域が主として用いられる。
表面保護層４の厚みとしては、特に限定されないが、好ましい下限は０．１μｍ、好ましい上限は５０μｍであり、より好ましい下限は１μｍ、より好ましい上限は３５μｍである。
表面保護層４の厚みが０．１μｍ未満であると、十分に耐久性（耐傷性、耐汚染性、耐候性等）を付与することができないことがあり、５０μｍを超えると、透過率が低下し絵柄層の絵柄の視認性が低下してしまうことがある。
（その他の層）
化粧シート１０は、必要に応じて、プライマー層、接着剤層及びバッカー層等を有してもよい。
上記プライマー層としては、公知のプライマー剤を塗布することにより形成できる。プライマー剤としては、例えば、アクリル変性ウレタン樹脂（アクリルウレタン系樹脂）等からなるウレタン樹脂系プライマー剤、ウレタン－セルロース系樹脂（例えば、ウレタンと硝化綿の混合物にヘキサメチレンジイソシアネートを添加してなる樹脂）からなるプライマー剤、アクリルとウレタンのブロック共重合体からなる樹脂系プライマー剤等が挙げられる。プライマー剤には、必要に応じて、添加剤を配合してもよい。添加剤としては、例えば、炭酸カルシウム、クレー等の充填剤、水酸化マグネシウム等の難燃剤、酸化防止剤、滑剤、発泡剤、紫外線吸収剤、光安定化剤などが挙げられる。添加剤の配合量は、製品特性に応じて適宜設定できる。
上記プライマー層は、必要に応じて紫外線吸収剤を含有してもよい。
上記紫外線吸収剤としては、公知の紫外線吸収剤を適宜選択して用いることができる。
上記プライマー層の厚みは、特に限定されないが、例えば、０．０１～１０μｍが好ましく、０．１～１μｍがより好ましい。
上記接着剤層としては、特に限定されず、公知の接着剤を用いればよい。例えば、ポリウレタン、アクリル、ポリオレフィン、ポリ酢酸ビニル、ポリ塩化ビニル、塩化ビニル－酢酸ビニル共重合体、エチレン－アクリル酸共重合体、アイオノマー等のほか、ブタジエン－アクリルニトリルゴム、ネオプレンゴム、天然ゴム等が挙げられる。これら接着剤は、単独で又は２種以上を組み合わせて用いる。
上記接着剤層は、乾燥後の厚みが０．１～３０μｍ程度が好ましく、１～５μｍ程度がより好ましい。
化粧シート１０は、耐傷性、耐衝撃性を付与する観点から、基材１の最下層（上記絵柄層２が積層される側と反対側）にバッカー層を有してもよい。
上記バッカー層としては、特開２０１４－１８８９４１号公報等に開示された公知のバッカー層を適宜選択して用いることができる。
（凹部（Ｄ１）及び（Ｄ２））
化粧シート１０において、透明性樹脂層３は、絵柄層２を有する側と反対側に、絵柄層２の特徴部分２ａと同調した凹部（Ｄ１）を有し、絵柄層２は、基材１を有する側と反対側に、凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を有する。
凹部（Ｄ１）は、絵柄層２の特徴部分２ａと同調した形状である。
凹部（Ｄ１）は、絵柄層２の模様の特徴部分２ａの外郭を型取った形状であってもよいし、絵柄層２の模様の特徴部分２ａの外郭を簡略化した形状や、特徴部分２ａの外郭を縮小又は拡大した相似形状であってもよい。
凹部（Ｄ１）は、絵柄層２の特徴部分２ａと同調するように位置している。
図３（ａ）～（ｃ）は、本発明の化粧シートの一例を模式的に示す断面図である。
凹部（Ｄ１）と、絵柄層２の特徴部分２ａとの位置関係は、図３（ａ）～（ｃ）のいずれであってもよい。
すなわち、図３（ａ）に示すように、積層方向において、絵柄層２の特徴部分２ａと、凹部（Ｄ１）とが、重複するように位置してもよく、図３（ｂ）に示すように、絵柄層２の特徴部分２ａと、凹部（Ｄ１）とが、一部重複するように位置していてもよく、図３（ｃ）に示すように、絵柄層２の特徴部分２ａと、凹部（Ｄ１）とが重複していないように位置してもよい。
ただし、図３（ｃ）であっても、平面視した場合に、凹部（Ｄ１）は、絵柄層２の特徴部分２ａの近傍に位置している。上記近傍とは、平面視した場合に、上記特徴部分２ａの位置と、上記特徴部分２ａに該当する形状の凹部（Ｄ１）との位置が７０ｍｍ以下であることをいう。
これらは、絵柄層２のデザインによって適宜設定することができる。
なお、上記凹部（Ｄ１）と特徴部分２ａとの同調関係は、必ずしも意匠全面において成立させる必要は無く、全体の意匠感を損なわないのであれば、同調していない領域が部分的に存在していてもよい。
なお、凹部（Ｄ１）の幅については後述する。
凹部（Ｄ２）は、凹部（Ｄ１）の積層方向に位置する。
図３（ａ）～（ｃ）に示すように、凹部（Ｄ２）は、積層方向において凹部（Ｄ１）と重複する位置に有する。
また、凹部（Ｄ２）は、図３（ａ）に示すように、絵柄層２の特徴部分２ａに、凹部（Ｄ２）が形成されていてもよく、図３（ｂ）に示すように、絵柄層２の特徴部分２ａから非特徴部分２ｂにまたがって凹部（Ｄ２）が形成されていてもよく、図３（ｃ）に示すように、絵柄層２の特徴部分２ａに凹部（Ｄ２）が形成されていなくてもよい（非特徴部分２ｂに凹部（Ｄ２）が形成されている）。
化粧シート１０において、凹部（Ｄ１）の深さＨは、凹部（Ｄ２）の深さｈよりも大きい。
このような凹部（Ｄ１）及び凹部（Ｄ２）を有することにより、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を奏する。
なお、上記凹部（Ｄ１）の深さＨと、凹部（Ｄ２）の深さｈとの関係は、互いに積層方向に位置する（平面視した場合に重複する）凹部（Ｄ１）と凹部（Ｄ２）との間でそれぞれ成立する。
化粧シート１０において、立体感を好適に付与する観点から、凹部（Ｄ１）の深さＨに対する凹部（Ｄ２）の深さｈの比率（ｈ／Ｈ）は、０．２５以上０．６０以下であることが好ましく、０．２６以上０．５５以下であることがより好ましく、０．２８以上０．５０以下であることが更に好ましく、０．３０以上０．４８以下であることが特に好ましい。
凹部（Ｄ１）の深さＨとしては、立体感を好適に付与できる大きさであればよく、例えば、５０μｍ以上２００μｍ以下であることが好ましく、５５μｍ以上１９０μｍ以下であることがより好ましい。
また、凹部（Ｄ２）の深さｈとしては、例えば、１３μｍ以上１００μｍ以下であることが好ましく、１７μｍ以上９２μｍ以下であることがより好ましい。
なお、上記深さＨ及び深さｈの数値範囲は、必ずしも全ての凹部（Ｄ１）及び凹部（Ｄ２）において成立させる必要は無く、全体の意匠感を損なわないのであれば、上記数値範囲を満たさない凹部（Ｄ１）、凹部（Ｄ２）が存在していてもよい。
例えば、全体の意匠感を損なわないのであれば、同調する凹部（Ｄ１）及び凹部（Ｄ２）において深さＨ＞深さｈの大小関係を満たさないものが一部存在してもよい。
ただし、意匠性を好適に付与する観点からは、化粧シート１０を平面視し、任意の１０ｃｍ×１０ｃｍの面積の互いに積層方向に位置する凹部（Ｄ１）と凹部（Ｄ２）を確認した場合に、深さＨ＞深さｈの大小関係を満たさないものが全体の３０％未満であることが好ましい。このような確認は、後述する電子顕微鏡とその測定条件を適用して行うことができる。
凹部（Ｄ１）の幅Ｗとしては、絵柄層２に形成された絵柄模様にもよるが、例えば、４００μｍ以上２０００μｍ以下であることが好ましく、５００μｍ以上１５００μｍ以下であることがより好ましい。
凹部（Ｄ２）の幅ｗとしては、例えば、５μｍ以上４００μｍ以下であることが好ましく、１０μｍ以上１００μｍ以下であることがより好ましい。
化粧シート１０では、凹部（Ｄ１）及び凹部（Ｄ２）の積層方向に位置する、基材１の絵柄層２側の凹部（Ｄ３とする）、基材１の絵柄層２と反対側の凹部（Ｄ４とする）を有することが好ましい。
この場合、凹部の深さは、凹部（Ｄ１）、凹部（Ｄ２）、凹部（Ｄ３）、凹部（Ｄ４）の順に小さくなることが好ましい。
また、化粧シート１０が、表面保護層４を有し、凹部（Ｄ１）及び凹部（Ｄ２）の積層方向に位置する表面保護層４の透明性樹脂層３と反対側の凹部（Ｄ５とする）を有する場合には、凹部の深さは、凹部（Ｄ５）、凹部（Ｄ１）、凹部（Ｄ２）、凹部（Ｄ３）、凹部（Ｄ４）の順に小さくなることが好ましい。
このような凹部（Ｄ１～Ｄ５）を有することにより、絵柄層の絵柄模様と、凹部とが同調した意匠性を好適に奏することができる。
このような凹部（Ｄ１～Ｄ５）は、後述する本発明の化粧シートの製造方法により好適に形成することができる。
なお、上記凹部（Ｄ１～Ｄ５）の深さの関係は、互いに積層方向に位置する（平面視した場合に重複する）凹部（Ｄ１～Ｄ５）の間でそれぞれ成立する。
凹部（Ｄ１）の幅Ｗ及び深さＨ、並びに、凹部（Ｄ２）の幅ｗ及び深さｈの測定方法について説明する。
図４（ａ）は、本発明の化粧シートの一例を模式的に示す斜視図であり、（ｂ）は、本発明の化粧シートの一例を模式的に示す上面図であり、（ｃ）は、本発明の化粧シートの一例を模式的に示す断面図である。
図４（ａ）に示すように、化粧シート１０の表面に形成された凹部を選択する。図４（ｂ）に示すように、選択した凹部の長軸及び短軸を決定する。次いで、図４（ｃ）に示すように、短軸に沿って切断し、その切断面を電子顕微鏡で観察し、凹部（Ｄ１）及び（Ｄ２）の幅（Ｗ及びｗ）及び深さ（Ｈ及びｈ）を測定する。
図４（ｃ）に示すように、凹部（Ｄ１）の深さＨとは、透明性樹脂層３の表面から凹部（Ｄ１）の最深部までの垂直距離を意味し、凹部（Ｄ２）の深さｈとは、絵柄層２の表面から凹部（Ｄ２）の最深部までの垂直距離を意味する。
なお、凹部の長軸とは、凹部の外周の２点を結ぶ直線の長さが最大となる箇所をいい、凹部の短軸とは、上記長軸の垂直方向で最大となる箇所をいう。
透明性樹脂層３が最外層である場合には、化粧シート１０の表面に形成された凹部の短軸は、凹部（Ｄ１）の幅Ｗと一致する。
一方で、図５に示すように、化粧シート１０が、基材１の一方に、少なくとも絵柄層２と、透明性樹脂層３と、表面保護層４とをこの順に有する場合、凹部（Ｄ１）の幅Ｗは、化粧シート１０の表面に形成された凹部の短軸よりも小さな値となる。この場合は、凹部の短軸で切断した断面を電子顕微鏡で観察し、測定することができる。
なお、凹部（Ｄ１）の幅Ｗ及び深さＨ、並びに、凹部（Ｄ２）の幅ｗ及び深さｈは、化粧シート１０の表面に形成された凹部を無作為に１０箇所選択し、上述した方法により測定して算出した平均値を意味する。
電子顕微鏡での測定条件としては、例えば、形状解析レーザ顕微鏡（測定部『ＶＫ－Ｘ１０５０』、台座『ＶＫ－Ｄ１』、コントローラ『ＶＫ－Ｘ１０００』（ＫＥＹＥＮＣＥ社製））を用い、倍率３００倍で観察する等により測定することができる。
上記樹脂塗料としては、例えば、ウレタン樹脂、アクリルウレタン樹脂、エポキシ樹脂、ポリエステル樹脂等からなる、速乾性に優れた有機溶剤系塗料や、自然環境・作業環境等にやさしい水系塗料等が使用可能であり、その中でも、ウレタン系樹脂が混合された水系塗料が好ましい。
また、着色剤としては、上述した絵柄層で記載したもの等を用いることができる。
また、上記樹脂塗料により着色する方法としては、例えば、特許第４５６９７２０号に記載される方法を適用することができる。
＜化粧シートの製造方法＞
本発明の化粧シートの製造方法は、基材の一方に、特徴部分と非特徴部分とを備えた絵柄層と、透明性樹脂層とを少なくともこの順に積層する積層工程と、上記透明性樹脂層の上記絵柄層を有する側と反対側からエンボス加工を施し、上記透明性樹脂層の上記絵柄層を有する側と反対側に上記絵柄層の特徴部分と同調した凹部（Ｄ１）、及び、上記絵柄層の上記基材を有する側と反対側に上記凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を賦形する賦形工程とを有し、上記凹部（Ｄ１）の深さＨは、上記凹部（Ｄ２）の深さｈよりも大きいことを特徴とする。
上記積層工程は、基材の一方に、絵柄層と、透明性樹脂層とを少なくともこの順に積層する工程である。
上記積層工程では、上述した基材１、絵柄層２及び透明性樹脂層３を用いることができ、基材１の一方に、絵柄層２と、透明性樹脂層３とを少なくともこの順に積層すればよい。
また、透明性樹脂層３の絵柄層２を有する側と反対側に表面保護層４を積層することが好ましい。
上述した各層の一方の面や層間には、上述した接着剤層やプライマー層を設けてもよい。
上記賦形工程は、透明性樹脂層の絵柄層を有する側と反対側からエンボス加工を施し、絵柄層の特徴部分と同調した凹部を賦形する工程である。
上記賦形工程を有することにより、上記絵柄層の特徴部分と同調した凹部（Ｄ１）と、凹部（Ｄ１）の積層方向の位置に、凹部（Ｄ１）よりも小さい凹部（Ｄ２）が、凹部（Ｄ１）に追従して形成される。
上記エンボス加工としては、例えば、周知の枚葉、又は、輪転式のエンボス機によるエンボス加工を施す方法等が挙げられる。
上記エンボス加工で用いる柄模様としては、上述した絵柄層２と同調するデザインを適宜選択して用いることができる。
上記エンボス加工する際の温度としては特に限定されないが、加熱圧着成形時に凹部が消失する所謂エンボス戻りが少なくなる温度が好ましい。
なお、表面保護層４を積層する場合には、表面保護層４を積層した後、上記賦形工程を行うことが好ましい。
本発明の化粧シートの製造方法により製造された化粧シートは、基材の一方に、絵柄層と、透明性樹脂層とを少なくともこの順に有しており、透明性樹脂層が絵柄層の特徴部分と同調した凹部（Ｄ１）を有し、絵柄層が凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を有しており、凹部（Ｄ１）の深さＨが凹部（Ｄ２）の深さｈよりも大きいことにより、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を備えたものである。
＜化粧板＞
本発明の化粧板は、被着材上に本発明の化粧シートを備えることを特徴とする。
上記被着材としては、例えば、木材単板、木材合板、パーチクルボード、ＭＤＦ（中密度繊維板）等の木質板；石膏板、石膏スラグ板等の石膏系板；珪酸カルシウム板、石綿スレート板、軽量発泡コンクリート板、中空押出セメント板等のセメント板；パルプセメント板、石綿セメント板、木片セメント板等の繊維セメント板；陶器、磁器、土器、硝子、琺瑯等のセラミックス板；鉄板、亜鉛メッキ鋼板、ポリ塩化ビニルゾル塗布鋼板、アルミニウム板、銅板等の金属板；ポリオレフィン樹脂板、ポリ塩化ビニル樹脂板、アクリル樹脂板、ＡＢＳ板、ポリカーボネート板等の熱可塑性樹脂板；フェノール樹脂板、尿素樹脂板、不飽和ポリエステル樹脂板、ポリウレタン樹脂板、エポキシ樹脂板、メラミン樹脂板等の熱硬化性樹脂板；フェノール樹脂、尿素樹脂、不飽和ポリエステル樹脂、ポリウレタン樹脂、エポキシ樹脂、メラミン樹脂、ジアリルフタレート樹脂等の樹脂を、硝子繊維不織布、布帛、紙、その他の各種繊維質基材に含浸硬化して複合化したいわゆるＦＲＰ板等が挙げられ、これらを単独で用いてもよく、これらの２種以上を積層した複合基板として用いてもよい。
また、熱可塑性樹脂板や熱硬化性樹脂板は必要に応じて、着色材（顔料又は染料）、木粉や炭酸カルシウム等の充填剤、シリカ等の艶消し剤、発泡剤、難燃剤、タルク等の滑剤、帯電防止剤、酸化防止剤、紫外線吸収剤、光安定化剤等の各種の添加剤が含まれていてもよい。
なお、上記被着材の厚みは特に限定されない。
上記被着材へ本発明の化粧シートを積層する方法としては特に限定されず、例えば、上述したプライマー層を介して積層したり、上述した接着剤層を介して積層したりする手段等が挙げられる。
次に、本発明を実施例により、さらに詳細に説明するが、本発明は、この例によって限定されるものではない。
（実施例１）
両面にコロナ放電処理を施した基材（６０μｍ厚、着色ポリプロピレンシート）を準備し、その一方の面にウレタン－硝化綿混合樹脂１００質量部にヘキサメチレンジイソシアネート５質量部を添加するインキを塗布して２μｍ厚さのプライマー層を形成し、他方の面にアクリルウレタン系樹脂１００質量部にヘキサメチレンジイソシアネート８質量部、酸化チタン７０質量部を添加するインキを塗布して２μｍ厚さの隠蔽層を形成した。
次いで、上記隠蔽層上にアクリルウレタン系樹脂に着色顔料を添加したインキを塗布して１μｍ厚さの図柄層（木目模様）を形成した。
次いで、アクリルポリオール－ウレタン混合樹脂１００質量部にヘキサメチレンジイソシアネート１１質量部を添加したインキを塗布して２μｍ厚さの接着剤層を形成し、
上記接着剤層上に、Ｔダイ押出機でポリプロピレン樹脂を加熱溶融押出しして１００μｍ厚さの透明性樹脂層を形成すると共に、該透明樹脂層上にアクリルポリオール－ウレタン混合樹脂１００質量部にヘキサメチレンジイソシアネート６質量部を添加したインキを塗布して２μｍ厚さのプライマー層を形成し、次いで該プライマー層上に、アクリレート系電子線硬化性樹脂をグラビアコート法により固形分が３０ｇ／ｍ２となるように塗布・乾燥した後、酸素濃度２００ｐｐｍ、加速電圧１６５ＫｅＶ、５Ｍｒａｄの条件で電子線を照射して電子線硬化性樹脂からなる表面保護層を形成し、さらに該表面保護層側からエンボス加工を施して、上記図柄層と同調した凹部を賦形し、化粧シートを作製した。
なお、絵柄層（図柄層）の特徴部分と非特徴部分との色差ΔＥは、３．０であった。
（実施例２～１０、比較例１）
賦形する凹部の大きさをそれぞれ変更したこと以外は、実施例１と同様にして化粧シートを作製した。
＜凹部の幅及び深さの測定＞
作製した化粧シートについて、表面に形成された凹部を無作為に１０箇所選択し、選択した凹部の長軸及び短軸を決定した。次いで、決定した短軸に沿ってそれぞれ切断し、形状解析レーザ顕微鏡（測定部『ＶＫ－Ｘ１０５０』、台座『ＶＫ－Ｄ１』、コントローラ『ＶＫ－Ｘ１０００』（すべてＫＥＹＥＮＣＥ社製））を用い、倍率３００倍で観察し、凹部（Ｄ１）及び（Ｄ２）の幅（Ｗ及びｗ）及び深さ（Ｈ及びｈ）をそれぞれ測定し、その平均値を算出した。
また、上記平均値に基づいて、凹部（Ｄ１）の深さＨに対する凹部（Ｄ２）の深さｈの比率（ｈ／Ｈ）を算出した。
その測定結果を、表１に示した。
＜意匠性の評価＞
作製した化粧シートを上面から目視にて観察し、絵柄層の絵柄模様と、凹部とが同調しているか否かを以下に示す判断基準により、人の感性に基づいて評価を行った。
その評価結果を、表１に示す。
＋：同調しているように感じる。
－：同調しているように感じない。
Figure JPOXMLDOC01-appb-T000001
表１に示すように、透明性樹脂層が絵柄層の特徴部分と同調した凹部（Ｄ１）と、凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）とを有し、凹部（Ｄ１）の深さＨが凹部（Ｄ２）の深さｈよりも大きいことにより、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を奏することが確認された。
本発明によれば、絵柄層の絵柄模様と、凹部とが同調した極めて優れた意匠性を有する化粧シートを提供することができる。
　１　　基材
　２　　絵柄層
　２ａ　特徴部分
　２ｂ　非特徴部分
　３　　透明性樹脂層
　４　　表面保護層
　１０　化粧シート

Claims (7)

  1. 基材の一方に、絵柄層と、透明性樹脂層とを少なくともこの順に有し、
    前記絵柄層は、特徴部分と非特徴部分とを備え、
    前記透明性樹脂層は、前記絵柄層を有する側と反対側に、前記絵柄層の特徴部分と同調した凹部（Ｄ１）を有し、
    前記絵柄層は、前記基材を有する側と反対側に、前記凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を有し、
    前記凹部（Ｄ１）の深さＨは、前記凹部（Ｄ２）の深さｈよりも大きい
    ことを特徴とする化粧シート。
  2. 前記凹部（Ｄ１）の深さＨに対する前記凹部（Ｄ２）の深さｈの比率（ｈ／Ｈ）は、０．２５以上０．６０以下である請求項１に記載の化粧シート。
  3. 前記透明性樹脂層の前記絵柄層を有する側と反対側に表面保護層を有する請求項１又は２に記載の化粧シート。
  4. 前記絵柄層の特徴部分は、木目の導管、節、年輪及び斑、又は、岩石の中の異なった結晶成分の縞や割れ模様である請求項１～３の何れか１項に記載の化粧シート。
  5. 前記絵柄層の特徴部分と非特徴部分との色差ΔＥは、１．３以上である請求項１～４の何れか１項に記載の化粧シート。
  6. 被着材上に請求項１～５の何れか１項に記載の化粧シートを備えることを特徴とする化粧板。
  7. 基材の一方に、特徴部分と非特徴部分とを備えた絵柄層と、透明性樹脂層とを少なくともこの順に積層する積層工程と、
    前記透明性樹脂層の前記絵柄層を有する側と反対側からエンボス加工を施し、
    前記透明性樹脂層の前記絵柄層を有する側と反対側に前記絵柄層の特徴部分と同調した凹部（Ｄ１）、及び、
    前記絵柄層の前記基材を有する側と反対側に前記凹部（Ｄ１）の積層方向に位置する凹部（Ｄ２）を賦形する賦形工程とを有し、
    前記凹部（Ｄ１）の深さＨは、前記凹部（Ｄ２）の深さｈよりも大きい
    ことを特徴とする化粧シートの製造方法。

     
PCT/JP2021/002264 2020-01-24 2021-01-22 化粧シート、化粧板及び化粧シートの製造方法 WO2021149803A1 (ja)