WO2021127996A1 - 二次电池及含有该二次电池的装置 - Google Patents
二次电池及含有该二次电池的装置 Download PDFInfo
- Publication number
- WO2021127996A1 WO2021127996A1 PCT/CN2019/127971 CN2019127971W WO2021127996A1 WO 2021127996 A1 WO2021127996 A1 WO 2021127996A1 CN 2019127971 W CN2019127971 W CN 2019127971W WO 2021127996 A1 WO2021127996 A1 WO 2021127996A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- secondary battery
- electrolyte
- battery according
- organic solvent
- silicon
- Prior art date
Abstract
Description
Claims (16)
- 一种二次电池,包括:负极极片,包括负极集流体以及设置于负极集流体至少一个表面上且包括负极活性材料的负极膜片;隔离膜,包括基材和设置在基材至少一个表面上的涂层;以及电解液,包括有机溶剂;其中,所述负极活性材料包括硅基材料和碳材料;所述隔离膜的基材的厚度为7μm~12μm;所述有机溶剂包括碳酸乙烯酯(EC),所述碳酸乙烯酯(EC)的含量在所述有机溶剂中的重量占比≤20%。
- 根据权利要求1所述的二次电池,其中,所述碳酸乙烯酯(EC)的含量在所述有机溶剂中的重量占比≤15%;优选地,所述碳酸乙烯酯(EC)的含量在所述有机溶剂中的重量占比≤10%。
- 根据权利要求1-2任一项所述的二次电池,其中,所述隔离膜的基材的厚度为7μm~10μm。
- 根据权利要求1-3任一项所述的二次电池,其中,所述隔离膜的孔隙率为25%~50%;优选地,所述隔离膜的孔隙率为30%~48%。
- 根据权利要求1-4任一项所述的二次电池,其中,所述有机溶剂还包括碳酸甲乙酯(EMC)、碳酸二乙酯(DEC)、碳酸二甲酯(DMC)中的一种或几种。
- 根据权利要求5所述的二次电池,其中,所述碳酸甲乙酯(EMC) 的含量在所述有机溶剂中的重量占比为60%~95%;优选地,所述碳酸甲乙酯(EMC)的含量在所述有机溶剂中的重量占比为75%~95%。
- 根据权利要求5-6任一项所述的二次电池,其中,所述碳酸二乙酯(DEC)的含量在所述有机溶剂中的重量占比≤30%;优选地,所述碳酸二乙酯(DEC)的含量在所述有机溶剂中的重量占比≤20%。
- 根据权利要求5-6任一项所述的二次电池,其中,所述碳酸二甲酯(DMC)的含量在所述有机溶剂中的重量占比≤15%;优选地,所述碳酸二甲酯(DMC)的含量在所述有机溶剂中的重量占比≤10%。
- 根据权利要求1-8任一项所述的二次电池,其中,所述电解液还包括电解质盐,所述电解质盐包括双氟磺酰亚胺锂(LiFSI)和六氟磷酸锂(LiPF 6);所述双氟磺酰亚胺锂(LiFSI)在所述电解液中的体积摩尔浓度为0.8mol/L~1.3mol/L,所述六氟磷酸锂(LiPF 6)在所述电解液中的体积摩尔浓度为0.15mol/L~0.4mol/L。
- 根据权利要求9所述的二次电池,其中,所述双氟磺酰亚胺锂(LiFSI)在所述电解液中的体积摩尔浓度为0.9mol/L~1.2mol/L,所述六氟磷酸锂(LiPF 6)在所述电解液中的体积摩尔浓度为0.15mol/L~0.3mol/L。
- 根据权利要求1-10任一项所述的二次电池,其中,所述电解液在25℃时的电导率为6.5mS/cm~9.5mS/cm,优选地,所述电解液在25℃时的电导率为7mS/cm~9mS/cm;和/或,所述电解液在25℃时的粘度为3.5mPa·s~5.5mPa·s,优选地,所述 电解液在25℃时的粘度为4mPa·s~5mPa·s。
- 根据权利要求1-11任一项所述的二次电池,其中,所述硅基材料包括硅单质、硅合金、硅氧化合物、硅碳化合物、硅氮化合物中的一种或几种,优选地,所述硅基材料包括硅氧化合物;和/或,所述碳材料包括石墨、软碳、硬碳中的一种或几种,优选地,所述碳材料包括石墨,所述石墨选自人造石墨、天然石墨中的一种或几种。
- 根据权利要求1-12任一项所述的二次电池,其中,所述硅基材料在所述负极活性材料中的质量占比≤50%,优选为15%~30%。
- 根据权利要求1-13任一项所述的二次电池,其中,所述隔离膜的厚度为11μm~16μm,优选地,所述隔离膜的厚度为12μm~14μm。
- 根据权利要求1-14任一项所述的二次电池,其中,所述二次电池还包括正极极片,所述正极极片包括正极集流体以及设置于正极集流体至少一个表面上且包括正极活性材料的正极膜片,所述正极活性材料包括锂镍钴锰氧化合物、锂镍钴铝氧化物中的一种或几种;优选地,所述正极活性材料包括Li aNi bCo cM dM’ eO fA g或表面至少一部分设置有包覆层的Li aNi bCo cM dM’ eO fA g中的一种或几种,其中,0.8≤a≤1.2,0.5≤b<1,0<c<1,0<d<1,0≤e≤0.1,1≤f≤2,0≤g≤1,M选自Mn、Al中的一种或两种,M’选自Zr、Al、Zn、Cu、Cr、Mg、Fe、V、Ti、B中的一种或几种,A选自N、F、S、Cl中的一种或几种。
- 一种装置,包括根据权利要求1-15任一项所述的二次电池。