Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
  • H01M4/624—Electric conductive fillers
  • H01M4/625—Carbon or graphite
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/052—Li-accumulators
  • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
  • H01M10/0564—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of organic materials only
  • H01M10/0566—Liquid materials
  • H01M10/0568—Liquid materials characterised by the solutes
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
  • H01M4/131—Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
  • H01M4/133—Electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
  • H01M4/136—Electrodes based on inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/36—Selection of substances as active materials, active masses, active liquids
  • H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
  • H01M4/5825—Oxygenated metallic salts or polyanionic structures, e.g. borates, phosphates, silicates, olivines
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B82—NANOTECHNOLOGY
  • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
  • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M2004/021—Physical characteristics, e.g. porosity, surface area
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M2004/026—Electrodes composed of, or comprising, active material characterised by the polarity
  • H01M2004/028—Positive electrodes
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/36—Selection of substances as active materials, active masses, active liquids
  • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
  • H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
  • H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/36—Selection of substances as active materials, active masses, active liquids
  • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
  • H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
  • H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/36—Selection of substances as active materials, active masses, active liquids
  • H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
  • H01M4/583—Carbonaceous material, e.g. graphite-intercalation compounds or CFx
  • H01M4/587—Carbonaceous material, e.g. graphite-intercalation compounds or CFx for inserting or intercalating light metals
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/10—Energy storage using batteries

Definitions

• This invention relates to the use of purified single wall carbon nanotubes (SWCNT) as a conductive additive in lithium ion battery cathodes, for significantly improved performance characteristics of the fully assembled cell, compared to lithium ion battery cells using only a conventional conductive carbon additive such as carbon black in the cathode.
• SWCNT single wall carbon nanotubes
• Li-ion batteries are commonly used in consumer electronics, and are attractive for use in hybrid gas-electric and all-electric vehicles.
• improvements in battery performance are needed for widespread vehicle application. Specifically, increased energy density, power density, lighter weight, and better reliability are desirable.
• Particularly attractive are thinner and/or lighter electrode materials having lower electrical resistance, more efficient ion transfer capability, and sufficient mechanical strength for battery use.
• the US DOE has set such performance targets for LiB cells - capacity of 350 Wh/kg (750 Wh/L), continuous operation for at least 1,000 cycles, and a lifetime expectancy of 10+ years.
• the targets are equally lofty; fast charge in 15 - 30 mins (80% state of charge), with battery pack cost reduction to $125 - $80 per kWh.
• new battery chemistries will be critical, particularly for the cathode formulation of such energy storage devices.
• the conventional LiB makeup consists of cathodes with Li metal oxides as active material (e.g.
• Li-NiMnCo-Oxide NMC
• Li- NiCoAl-Oxide NCA
• Li-Fe-Phosphate LFP
• Li-Cobalt-Oxide LCO
• Li -Manganese- Oxide LMO
• PVDF binder is insulating.
• the Li metal oxides are resistive.
• a conductive additive such as carbon black is therefore included in the cathode formulation to lower the overall electrode resistance.
• Carbon nanotubes are one-dimensional cylindrical graphitic nanostructures composed predominantly of sp 2 hybridized carbon atoms. CNT are classified according to the number of cylindrical graphitic sheets or “walls” that compose their individual nanotube structure. Nanotubes possessing one wall are referred to as single-wall carbon nanotubes (SWCNT), to differentiate them from their counterparts possessing two or more walls, called multi-wall carbon nanotubes (MW CNT). MW CNT with two walls are also called double wall carbon nanotubes (DWCNT). Both types of CNT, SWCNT and MWCNT, possess nanometer-size diameters and micron-size lengths, offering high surface to volume ratio and giving rise to a high aspect ratio characteristic. Since the typical diameter of an individual SWCNT is 5 - 50 times smaller than the diameter of an individual MWCNT, SWCNT have significantly higher aspect ratio than MWCNT.
• Figure 1 shows images of slot-die roll-to-roll coatings of LiB cathode material containing SWCNT as conductive additive, on A1 foil; (A) Coating for LiB energy cell, (B) Coating for LiB power cell.
• Figure 2 is a set of two charts illustrating performance gains in type 18650 LiB energy cells containing purified SWCNT as conductive additive compared to LiB cells with conventional carbon black conductive additive (Super-P® or “SP”, Imerys Graphite & Carbon, Terrebonne, Quebec, Canada).
• Figure 3 is a chart comparing the life cycle capacity of type 18650 LiB energy cells containing 6 wt % standard carbon black (SP) conductive additive (labeled Control), 1 wt % purified SWCNT + 1 wt % carbon black (SP), and 2 wt % purified SWCNT.
• SP standard carbon black
• SP conductive additive
• SP 2 wt % purified SWCNT.
• Figure 4 is a set of two charts showing charge and discharge capacity performance gains achieved in LiB power cells upon use of purified SWCNT as conductive additive at different concentrations, compared to conventional carbon black additive (standard cell at 6 wt % SP).
• Figure 5 is a chart showing the difference in discharge capacity performance gains achieved in LiB power cells upon use of as-received SWCNT (CNT) or purified SWCNT as a conductive additive, compared to conventional carbon black (SP) additive.
• CNT as-received SWCNT
• SP carbon black
• Figure 6 is a chart showing reduction in cell impedance achieved in LiB power cells upon use of purified SWCNT as conductive additive at different concentrations compared to conventional carbon black additive (standard cell at 6 wt % SP).
• Figure 7 is a set of two charts showing improved discharge rate performance at increasing discharge currents of (B) LiB power cells containing purified SWCNT as conductive additive compared to (A) conventional carbon black additive (6 wt % SP).
• Figure 8 is a chart showing improved discharge rate performance at 20A discharge current of LiB power cells containing purified SWCNT as conductive additive at 2 wt % and 3 wt %, compared to cells containing carbon black additive (standard cell at 6 wt % SP).
• Figure 9 is a chart showing a comparison of discharge rate performance at 20A discharge current of LiB power cells containing purified SWCNT as conductive additive at 2 wt % us. as-received SWCNT additive also at 2 wt %.
• Figure 10 is a chart showing improved life cycle performance (normalized discharge capacity) of representative LiB power cells containing purified SWCNT as conductive additive at 2 wt %, compared with cells containing carbon black additive (standard cell at 6 wt %).
• Figure 11 is a chart showing superior early life cycle performance (normalized discharge capacity) of LiB power cells containing 2 wt % purified SWCNT + 2 wt % carbon black (SP) as conductive additive compared to cells containing 2 wt % as-received SWCNT + 2 wt % carbon black (SP) as conductive additive
• Figure 12 is a set of charts showing improved performance of LiB parameters of charge capacity (top), discharge capacity (middle) and cell impedance (bottom) upon inclusion of SWCNT as conductive additive to either reduce or completely replace the carbon black content. indicates the best performance in each category of energy cells or power cells.
• Figure 13 is a chart showing superior early life cycle performance (normalized discharge capacity) of LiB power cells containing highly purified SWCNT as conductive additive at 2 wt %, compared to cells containing purified SWCNT or as-received SWCNT as conductive additive at 2 wt %, each with 2 wt % carbon black (SP).
• SP carbon black
• Figure 14 is a chart showing a comparison of discharge rate performance at 20A discharge current of LiB power cells containing various grades of SWCNT as conductive additive at 2 wt %: as-received, purified, and highly purified SWCNT (each with 2 wt % SP).
• Figure 15 is a chart showing life cycle performance (normalized discharge capacity) of LiB power cells containing as-received MWCNT vs. cells containing as-received, purified, or highly purified SWCNT as conductive additive at 2 wt % (each with 2 wt% SP), or containing no CNT (6 wt% SP).
• Figure 16 is a chart showing a comparison of discharge rate performance at 20 A discharge current of LiB power cells containing MWCNT vs. cells containing various grades of SWCNT as conductive additive at 2 wt % (each with 2 wt % SP), or containing no CNT (6 wt% SP).
• the inventors have discovered that the use of high purity and well-dispersed conductive carbon nanotubes, in particular single wall carbon nanotubes (SWCNT), as a conductive additive material to cathode formulations of Li ion batteries enhances the performance characteristics of the fully assembled LiB cell.
• the high aspect ratio of the carbon nanotubes in contrast to conventional carbon black particles, provides good contact between active metal oxides and allows conductive percolation at lower incorporated levels.
• the control of cathode morphology and porosity is essential. Lower porosity results in lower surface area and thus higher diffusion coefficient which decreases response time (Chang Kyoo Park et al, Bull. Korean Chem. Soc. 2011, Vol. 32, No. 3, p. 836-840).
• the SWCNT need to be of high purity with ⁇ 5 wt % inorganic impurities, possess a BET specific surface area of between 400 and about 1300 m 2 /g, preferably between 800 and about 1300 m 2 /g, and they need to be highly graphitized with minimal tube defects (as evidenced by Raman G/D ratio > 20, as measured using a laser having a wavelength of 532 nm).
• the incorporation of conductive SWCNT with these specific criteria to cathode formulations of LiB cells provides the necessary performance gains of increased capacity, increased rate capability, increased cycle lifetime, and reduced impedance to enable next generation battery systems that meet the set target criteria.
• SWCNT rather than MWCNT
• MWCNT metal-oxide-semiconductor
• the advantages of using SWCNT over MWCNT as a conductive additive material in cathode formulations of LiB are due to higher aspect ratio and higher surface area afforded by SWCNT.
• SWCNT typically have 5-50 times higher aspect ratio than MWCNT.
• SWCNT typically have several hundred to more than a thousand m 2 /g more surface area than MWCNT. This combination of higher aspect ratio and higher surface area provided by SWCNT make these nanotubes more attractive than MWCNT for use in the present invention as conductive carbon additive.
• LiB cells typically comprise a carbon-based anode, a cathode, and an electrolyte comprising a lithium salt in an organic solvent.
• the present invention is directed to a LiB cell having a cathode comprising an active material and about 1-5% by weight (wt %) of single wall carbon nanotubes (SWCNT) as a conductive additive, wherein the SWCNT have an inorganic impurity content of less than 5 wt %, or less than 4.5 wt %.
• SWCNT single wall carbon nanotubes
• % in this application refers to % by weight (wt).
• the active material of the cathode of the LiB of the present invention typically contains a material selected from the group consisting of: Li-NiMnCo-Oxide (NMC), Li- NiCoAl-Oxide (NCA), Li-Fe-Phosphate (LFP), Li-Cobalt-Oxide (LCO), Li-Manganese- Oxide (LMO), and any combination thereof.
• the LiB cathode of the present invention typically contains 91-99 wt % of active materials, preferably 92-98 or 92-97 wt %.
• the cathode of LiB of the present invention may contain a polymeric binder.
• a polymeric binder for example, polyvinylidene difluoride (PVDF), can be used as a binder in the cathode.
• PVDF polyvinylidene difluoride
• the binder may be in an amount of 0.5-8 wt %, preferably 1-6 wt %, or more preferably 1 - 2 wt % in the LiB cathode.
• the LiB cathode comprises a polymeric binder.
• the LiB cathode does not comprise a polymeric binder.
• carbon nanotubes in the LiB cathode composition act as a binder to hold together the active oxide particles and any other components, such as carbon black.
• the polymeric binder does not contribute to the capacity of the LiB cell, and it is advantageous to minimize the amount of the polymeric binder in the cathode composition, or to eliminate it entirely.
• the SWCNT is purified and comprises inorganic impurities ⁇ 5%, or ⁇ 4.5%, or ⁇ 4%, or ⁇ 3%, or ⁇ 2%, or ⁇ 1% by weight.
• commercial SWCNT typically contain more than 10% (e.g., 10-25%) inorganic impurities by weight including iron (Fe), nickel (Ni), silicon (Si) and/or other metals. These metallic impurities are usually present as residues of the manufacturing process.
• the cathode comprises about 0.5 - 4.5 wt % SWCNT. In another embodiment, the cathode comprises about 1 - 4.5 wt %, or 1.5 - 4.5 wt %, or 2 - 4 wt % SWCNT. For example, the cathode comprises about 1, 2, 3, or 4 wt % SWCNT.
• the cathode comprises SWCNT as the only conductive additive.
• the cathode comprises SWCNT as a conductive additive, and does not comprise a substantial amount of carbon black.
• the cathode does not comprise more than 0.1% by weight of carbon black or does not comprise any carbon black.
• the cathode further comprises a second conductive additive such as carbon black.
• a second conductive additive such as carbon black.
• Acetylene black which is a form of carbon black and is highly crystallized, can be used as a second conductive additive.
• the ratio of the two conductive additives SWCNT to carbon black in the cathode may be in the range of 1:3 to 3:1; preferably in the range of 1:2 to 2:1, and more preferably about 1:1.
• the amounts of conductive carbon additives in the cathode vary depending on the requirement of the application for which the battery is used. Power cells have higher conductive carbon content (4 - 10% by weight) and lower active material content to achieve lower cell resistance. However, this comes at the price of losing storage capacity. Energy cells have lower conductive carbon content (2 - 4% by weight) and higher active material content to achieve high storage capacity. However, this comes at the price of losing rate capability.
• the combined content of SWCNT and carbon black is between 1% and 8% by weight, preferably between 2% and 6% by weight in the cathode.
• the cell is a power cell, and the combined content of SWCNT and carbon black in the cathode is between 4% and 10% by weight, preferably between 4% and 8% by weight, and more preferably between 4% and 6% by weight.
• the cell is an energy cell, and the combined content of SWCNT and carbon black in the cathode is between 2% and 4% by weight, preferably between 2% and 3% by weight, and more preferably about 2% by weight.
• the LiB power cell cathode may contain about 92 wt % NMC, about 2 wt % PVDF, about 3 wt % SWCNT, and about 3 wt % carbon black.
• the LiB power cell cathode may contain about 94 wt % NMC, about 2 wt % PVDF, about 2 wt % SWCNT, and about 2 wt % carbon black.
• the LiB power cell cathode may contain about 94 wt % NMC, about 2 wt % PVDF, and about 4 wt % SWCNT. In one embodiment, this cathode contains less than 0.1 wt % carbon black. In another embodiment, this cathode does not contain any carbon black.
• the LiB energy cell cathode may contain about 96 wt % NMC, about 2 wt % PVDF, and about 2 wt % SWCNT. In one embodiment, this cathode contains less than 0.1 wt % carbon black. In another embodiment, this cathode does not contain any carbon black.
• the LiB energy cell cathode may contain about 96 wt % NMC, about 2 wt % PVDF, about 1 wt % SWCNT, and about 1 wt % carbon black.
• the thickness of the cathode is at least 100 pm.
• the present invention uses purified SWCNT to either supplement or replace the carbon black material as a conductive additive in the cathode of LiB cells.
• SWCNT have substantially higher aspect ratio than multi-wall carbon nanotubes (MWCNT) due to their smaller diameter. Consequently, one of the challenges faced with processing high aspect ratio SWCNT into solution is overcoming the substantial van der Waals interaction in order to achieve a stable dispersion of SWCNT.
• the common approach is to utilize a suitable dispersant or surfactant to minimize agglomeration and re-bundling of the nanotubes after processing in solution.
• the presence of such agents adversely impacts inherent CNT properties such as high electronic conductivity, and adds additional post-processing time and cost for removing the dispersant from the processed CNT.
• the present invention describes the processing of high aspect ratio, purified SWCNT into a stable dispersion without the use of a dispersant or surfactant. Aggregates and large bundles of SWCNT are sufficiently reduced in size by high shear processing, such that they remain suspended and dispersed in the carrier solvent over long periods without separating or settling.
• the mechanically processed SWCNT dispersion is stable in that the dispersed nanotubes are not observed to agglomerate nor show any sedimentation after standing for at least 24 hours, or for at least several weeks at room temperature.
• the cathode material composition of the present invention is completely free of these substances. If present in the cathode material, such substances might detrimentally affect the performance of the cathode in an assembled LiB cell.
• the elimination of these substances from the SWCNT dispersion process ensures that they are not present in the cathode material, and therefore, do not cause any such performance losses when the cathode material is used in an assembled LiB cell.
• the effectiveness of processing SWCNT into stable dispersion by the present invention is manifested in the superior cycling and rate performance of assembled LiB cells with the processed SWCNT as additive to the cathode compared to cells containing MWCNT as an additive.
• the SWCNT in the present invention can be metallic SWCNT or semiconducting SWCNT or preferably a mixture of metallic and semiconducting SWCNT.
• this mixture of high aspect ratio, high purity metallic and semiconducting SWCNT has a relatively high electrical conductivity.
• the SWCNT are purified to the extent that their content of detectable metallic and other impurities is less than 5 wt % and their Raman G/D integrated peak area ratio is at least 20, preferably >30, > 40, > 50, or > 60, as measured using a laser with a wavelength of 532 nm.
• the purified SWCNT possess a BET specific surface area of between 400 m 2 /g and about 1300 m 2 /g, preferably between 800 m 2 /g and about 1300 m 2 /g, more preferably between 900 m 2 /g and about 1300 m 2 /g, or between 1000 and about 1300 m 2 /g, or between 1100 and about 1300 m 2 /g.
• high aspect ratio purified SWCNT generally affords a reduction in the total conductive additive content in the cathode to lower overall levels than when using only carbon black, particularly in the case of LiB power cells.
• This feature allows a higher percentage of active material which results not only in increased capacity but also in better utilization of cell capacity compared to standard LiB cells.
• This design allows for increased capacity (energy density) at given impedance and power density.
• capacity energy density
• the resulting performance gains achieved with LiB cells of the present invention containing the SWCNT additive are significant with respect to increased capacity, lower impedance, improved capacity retention at high discharge rates, and superior life cycling characteristics compared to the performance of LiB cells with standard carbon black conductive additive. Moreover, these multiple and significant performance enhancements are greatly heightened with the incorporation of purified SWCNT into the LiB electrode. Similar performance gains were not attainable using MWCNT as conductive additive.
• Commercially available SWCNT can contain between 10 and 25 wt % of inorganic impurities and varying amount of amorphous carbon.
• As-received commercial SWCNT (with ⁇ 14 wt %, typically 10-25 wt % inorganic impurities), purified SWCNT (with ⁇ 5 wt %, typically 2-4 wt % inorganic impurities), and highly purified SWCNT (with ⁇ 1 wt % inorganic impurities) were used to prepare dispersions of SWCNT in N-methyl-2-pyrrolidone (NMP).
• NMP N-methyl-2-pyrrolidone
• purified SWCNT ( ⁇ 5 wt % inorganic impurities) was used as the conductive additive to completely replace the traditional carbon black additive, at 2 wt % and 4 wt % for an LiB energy cell and an LiB power cell, respectively.
• the purified SWCNT- NMP dispersion prepared in Example 1 was incorporated into a cathode formulation mix containing commercial Li metal oxide active material - Nio.33 Mno.33 C00 . 33, referred to as NMC1 11.
• 2 wt % PVDF binder dissolved into NMP solvent was used in the formulation mix.
• the entire mixture was introduced into a 60 L mixer equipped for both high shear and planetary mixing and processed overnight under vacuum.
• Formulation B Purified SWCNT + carbon black (SP)
• purified SWCNT was used as a conductive additive to partially replace and reduce the amount of traditional carbon black additive.
• Purified SWCNT ( ⁇ 5 wt % inorganic impurities) was incorporated in varying amounts: 1 wt % SWCNT + 1 wt % carbon black (Super-P® or “SP”, Imerys Graphite & Carbon, Terrebonne, Quebec, Canada) for LiB energy cells, and 2 wt % and 3 wt % SWCNT with 2 wt % and 3 wt % carbon black respectively, for LiB power cells.
• 1 wt % SWCNT + 1 wt % carbon black Super-P® or “SP”, Imerys Graphite & Carbon, Terrebonne, Quebec, Canada
• carbon black was present in the respective formulations but in reduced quantity compared to standard LiB cells typically comprising between about 4 and 10 wt % carbon black for LiB power cells. Also 2 wt % PVDF binder dissolved into NMP solvent was used in the formulation mix.
• Formulation C As-received SWCNT + carbon black (SP)
• Formulation C as-received commercial SWCNT (about 14 wt % inorganic impurities) was used as a conductive additive to partially replace and reduce the amount of traditional carbon black additive. As-received commercial SWCNT (about 14 wt % inorganic impurities) was incorporated in the amount of 2 wt % SWCNT + 2 wt % carbon black for LiB power cells. This formulation was otherwise identical to the above Formulation B with 2 wt % purified SWCNT + 2 wt % carbon black, and was prepared in order to compare the effect of SWCNT purity on the performance characteristics of LiB cells. Also 2 wt % PVDF binder dissolved into NMP solvent was used in the formulation mix.
• Formulation D Standard LiB cells: Carbon black control (SP)
• Standard LiB energy cells were formulated to contain 2 wt % carbon black, and standard LiB power cells were formulated to contain 6 wt % carbon black. These served as respective control cells. Also 2 wt % PVDF binder dissolved into NMP solvent was used in the formulation mix.
• Table 1 summarizes all the prepared Formulations A through D above, and their compositions. Table 1. Cathode Formulations.
• Table 2 shows the differences in inorganic (metal) impurity content among one batch each of as-received commercial SWCNT, purified SWCNT, and highly purified SWCNT used as conductive additives in the LiB cells.
• the freshly processed cathode Formulations A through D prepared in Example 2 were coated onto both sides of a roll of battery-grade A1 foil (15 pm thick) via slot-die coating using a Dynacoat Lab Coater and dryer (Frontier Industrial Tech Inc.). The wet coating was subsequently dried in an eight-zone convective oven drying chamber of the slot-die coater, with the temperature through the zones ranging from 93.3 to 127°C.
• the resulting dry electrode thickness was about 300 pm on average, which decreased to about 170 pm after calendering.
• the coating weight per side was about 25 mg/cm 2 , corresponding to a density greater than 3 g/cm 3 .
• Figure 1(A) shows a representative wet cathode coating on A1 foil for a LiB energy cell.
• the resulting dry electrode thickness was about 195 pm, which was reduced to about 98 pm after calendering.
• the coating weight per side was about 13 mg/cm 2 , corresponding again to a density greater than 3 g/cm 3 .
• Figure 1(B) shows a representative wet cathode coating for a LiB power cell.
• the LiB cathodes containing SWCNT additive prepared in Example 3 were slit and each coupled with a standard graphitic intercalation anode composed of BTR 918 graphite powder (BTR New Energy Materials, China), carbon black conductive additive (Super P®), carboxy methylcellulose (CMC) gelling agent and styrene-butadiene rubber (SBR) as binder.
• This anode formulation was also slot-die coated onto battery grade Cu foil to yield anode electrodes.
• Each respective cathode was paired with an anode and assembled into type 18650 cells filled with LiPF 6 electrolyte. Using the respective fabricated cathodes from above, type 18650 cells were assembled for operation and testing as full LiB energy cells and LiB power cells.
• the coulometric capacity of the LiB is the total Amp-hours available when the battery is discharged at a certain discharge current (specified as a C-rate) from 100 percent state-of- charge to the cut-off voltage. Discharge capacity is calculated by multiplying the discharge current (in Amps) by the discharge time (in hours). In this Example, all LiB cells were discharged from an initial voltage of 4.2 V to a cut-off voltage of 3.0 V.
• Figure 2 shows a performance data comparison between standard LiB energy cells containing 96 wt % NMC, 2 wt % binder and 2 wt % carbon black in the cathode versus a LiB energy cell of the present invention with 96 wt % NMC, 2 wt % binder, and 2 wt % SWCNT in the cathode.
• 2 wt % carbon black additive By replacing the 2 wt % carbon black additive with 2 wt % SWCNT, there was an observed 5% increase in cell capacity and a parallel 6% reduction in cell ESR.
• Electrode formulation changes typically evoke a corresponding change in one performance criteria in LiB cells.
• the uniqueness in the present case was in achieving simultaneous performance gains of both increased capacity and impedance reduction from the same cathode formulation comprising 2 wt % SWCNT.
• the inclusion of 1 wt % SWCNT and 1 wt % carbon black resulted in a 4.5% reduction in cell ESR compared to the standard cell with 2 wt % carbon black.
• the increase in cell capacity by using 2 wt % purified SWCNT as conductive additive was not only observed initially, but was also sustained upon life cycling, as illustrated in Figure 3.
• the LiB cell containing 1 wt % SWCNT + 1 wt % carbon black which showed initial cell discharge capacity similar to that of a standard cell with 2 wt % carbon black, displayed better retention of cell capacity with cycling compared to the standard cell.
• the cell with 6 wt % carbon black exhibited a steep drop in capacitance within the initial few cycles followed by a more gradual decrease in capacitance. A less steep drop in capacitance within the initial few cycles was observed for the cell with 1 wt% carbon black and 1 wt % SWCNT. On the contrary, no steep drop in capacitance within the initial few cycles was observed in the cell with 2 wt% SWCNT and no carbon black. Instead only a gradual decrease in capacitance was observed.
• LiB power cells were assembled from cathodes incorporating purified SWCNT as a conductive additive.
• the LiB power cells of the present invention with cathodes containing an optimized amount of 2 wt % purified SWCNT + 2 wt % carbon black, exhibited a charge capacity gain of about 9.6% and a discharge capacity gain of 6.7% over standard LiB power cells with cathodes containing 6 wt % carbon black.
• Smaller increases in capacity and discharge capacity were also observed for amounts of 3 wt % purified SWCNT + 3 wt % carbon black in the cathode and 4 wt % purified SWCNT without carbon black in the cathode.
• the results show that the addition of purified SWCNT to the cathode is beneficial, and the total content and the ratio of SWCNT and carbon black may be optimized to achieve maximum gains in both charge capacity and discharge capacity.
• FIG. 7 illustrates the advantageous high current discharge performance characteristics of the LiB cell with 2 wt % purified SWCNT + 2 wt % carbon black. These cells show 50% increase in capacity over standard carbon black cells at the high discharge current of 20A with significantly less capacity fade.
• FIG. 8 A comparison of discharge curves among LiB power cells at 20 A discharge current is shown in Figure 8.
• the improved high current performance of LiB power cells containing purified SWCNT additive was observed in cells with either 2 wt % purified SWCNT + 2 wt % carbon black or 3 wt % purified SWCNT + 3 wt % carbon black.
• the most improved 20A discharge performance from the LiB power cells was achieved at lower total conductive carbon content (4 wt % vs. 6 wt %).
• Comparative life cycle data for the LiB power cells are shown in Figure 10.
• the initial increased capacity of a cell containing 2 wt % purified SWCNT additive + 2 wt% carbon black compared to a standard control cell with 6 wt % carbon black was sustained even after nearing 1,000 cycles at high current.
• Figure 11 compares the initial life cycle behavior of LiB cells assembled from the two grades of SWCNT additives. The results show that a power cell incorporating as- received SWCNT as conductive additive (open symbols) had a quicker fade in capacity after a given amount of cycles compared to a cell with purified SWCNT as conductive additive (solid symbols).
• Example 7 Improved performance of LiB energy and power cells as to charge capacity, discharge capacity, and cell impedance upon inclusion of SWCNT as conductive additive
• Figure 12 summarizes the results of Examples 1-6.
• the cell that shows the best performance as to Charge Capacity, Discharge Capacity, and Impedance is marked with a star ( ⁇ ) symbol.
• Addition of purified SWCNT to the cathode formulation of Li ion battery cells in described quantities enables improved performance characteristics of increased cell capacity and simultaneous reduced or similar cell impedance compared to cells using conventional carbon black conductive additive.
• These significant performance gains are realized at lower overall conductive additive content than is typical for cells with standard carbon black additive, thus allowing increased amount of active material in the electrode formulation with a potential to further increase the LiB cell capacity.
• the improved performance of the LiB cells with purified SWCNT additive is retained over life cycle testing.
• such significant gains to LiB performance depend on the purity level of SWCNT, as greater purity of the SWCNT additive results in greater performance gains in the LiB cell.
• the nominal battery energy per unit mass is referred to as its specific energy, or gravimetric energy density.
• Specific energy is a characteristic of the LiB chemistry and packaging, and is calculated by dividing the battery energy in Wh (watt-hours) by the mass of the packaged cell in kg.
• specific power, or gravimetric power density is the maximum available power per unit mass of a battery, and is calculated by dividing the battery power in W (watts) by the mass of the packaged cell in kg.
• Table 3 Summary of performance data for standard LiB cells compared with cells containing purified SWCNT.
• Figure 15 compares the initial life cycle behavior of LiB cells assembled from MWCNT additive compared to individual cells containing the three grades of SWCNT additives, as-received SWCNT, purified SWCNT, and highly purified SWCNT.
• LiB power cells incorporating as-received MWCNT as additive had the quickest fade in capacity after initial cycling, with retention of ⁇ 85% capacity after 400 cycles, compared to cells with three different grades of SWCNT as additive which all exhibited superior cycling performance compared to the cells containing MWCNT.
• Figure 16 compares the 20A discharge rate behavior of LiB power cells with cathodes comprising MWCNT additive to corresponding high current discharge curves from cells comprising various grades of SWCNT as additive.
• Power cells incorporating MWCNT as additive displayed lowest high current discharge rate capability and inferior to similar LiB cells containing all grades of SWCNT additive.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Electrochemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Inorganic Chemistry (AREA)
• Materials Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Physics & Mathematics (AREA)
• Condensed Matter Physics & Semiconductors (AREA)
• General Physics & Mathematics (AREA)
• Crystallography & Structural Chemistry (AREA)
• Battery Electrode And Active Subsutance (AREA)
• Secondary Cells (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Related Child Applications (1)

Publications (1)

Family

ID=75338511

Family Applications (1)

Country Status (6)

Cited By (6)

Families Citing this family (3)

Citations (4)

Family Cites Families (26)

• 2020
  • 2020-09-25 JP JP2022519365A patent/JP2022550742A/ja active Pending
  • 2020-09-25 CN CN202080068657.5A patent/CN114503320A/zh active Pending
  • 2020-09-25 WO PCT/US2020/052678 patent/WO2021067127A1/en not_active Ceased
  • 2020-09-25 EP EP20870748.9A patent/EP4038683B1/en active Active
  • 2020-09-25 KR KR1020227015089A patent/KR20220074955A/ko not_active Ceased
• 2022
  • 2022-03-30 US US17/657,333 patent/US20220223877A1/en active Pending
• 2025
  • 2025-11-26 JP JP2025203983A patent/JP2026020326A/ja active Pending

Patent Citations (4)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events