WO2021002379A1 - 有機ｅｌ表示素子用封止剤セット及び有機ｅｌ表示素子 - Google Patents

有機ｅｌ表示素子用封止剤セット及び有機ｅｌ表示素子 Download PDF

Info

Publication number
WO2021002379A1
WO2021002379A1 PCT/JP2020/025771 JP2020025771W WO2021002379A1 WO 2021002379 A1 WO2021002379 A1 WO 2021002379A1 JP 2020025771 W JP2020025771 W JP 2020025771W WO 2021002379 A1 WO2021002379 A1 WO 2021002379A1
Authority
WO
WIPO (PCT)
Prior art keywords
organic
display element
sealant
weight
peripheral
Prior art date
Application number
PCT/JP2020/025771
Other languages
English (en)
French (fr)
Inventor
俊隆 吉武
穣 末▲崎▼
真理子 安部
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to JP2020545739A priority Critical patent/JPWO2021002379A1/ja
Priority to KR1020217020553A priority patent/KR20220023748A/ko
Priority to CN202080062455.XA priority patent/CN114365303A/zh
Publication of WO2021002379A1 publication Critical patent/WO2021002379A1/ja

Abstract

本発明は、有機ＥＬ表示素子の基板等の反りを抑制できる有機ＥＬ表示素子用封止剤セットを提供することを目的とする。また、本発明は、該有機ＥＬ表示素子用封止剤セットの硬化物を有する有機ＥＬ表示素子を提供することを目的とする。 本発明は、有機ＥＬ表示素子の周縁部を囲んで封止する周辺封止剤と、該周辺封止剤の内側において有機発光材料層を有する積層体を被覆して封止する面内封止剤とを組み合わせてなる有機ＥＬ表示素子用封止剤セットであって、前記面内封止剤の硬化収縮率に対する前記周辺封止剤の硬化収縮率の比率が１．００以下である有機ＥＬ表示素子用封止剤セットである。

Description

有機ＥＬ表示素子用封止剤セット及び有機ＥＬ表示素子
本発明は、有機ＥＬ表示素子の基板等の反りを抑制できる有機ＥＬ表示素子用封止剤セットに関する。また、本発明は、該有機ＥＬ表示素子用封止剤セットの硬化物を有する有機ＥＬ表示素子に関する。
有機エレクトロルミネッセンス表示素子（有機ＥＬ表示素子）は、互いに対向する一対の電極間に有機発光材料層が挟持された薄膜構造体を有する。この有機発光材料層に一方の電極から電子が注入されるとともに他方の電極から正孔が注入されることにより有機発光材料層内で電子と正孔とが結合して自己発光を行う。バックライトを必要とする液晶表示素子等と比較して視認性がよく、より薄型化が可能であり、かつ、直流低電圧駆動が可能であるという利点を有する。
ところが、このような有機ＥＬ表示素子は、有機発光材料層や電極が外気に曝されるとその発光特性が急激に劣化し寿命が短くなるという問題がある。従って、有機ＥＬ表示素子の安定性及び耐久性を高めることを目的として、有機ＥＬ表示素子においては、有機発光材料層や電極を大気中の水分や酸素から遮断する封止技術が不可欠となっている。
特許文献１には、有機発光材料層を有する積層体を被覆して封止する有機充填層と、該有機充填層の側面を覆う吸湿シール層（封止壁）とを有する構成により、有機ＥＬ表示素子を封止する方法が開示されている。通常、有機ＥＬ表示素子用封止剤として、上記有機充填層には面内封止剤が用いられ、上記封止壁には面内封止剤とは構成成分の異なる周辺封止剤が用いられている。
特開２０１４－６７５９８号公報
本発明は、有機ＥＬ表示素子の基板等の反りを抑制できる有機ＥＬ表示素子用封止剤セットを提供することを目的とする。また、本発明は、該有機ＥＬ表示素子用封止剤セットの硬化物を有する有機ＥＬ表示素子を提供することを目的とする。
本発明は、有機ＥＬ表示素子の周縁部を囲んで封止する周辺封止剤と、該周辺封止剤の内側において有機発光材料層を有する積層体を被覆して封止する面内封止剤とを組み合わせてなる有機ＥＬ表示素子用封止剤セットであって、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率が１．００以下である有機ＥＬ表示素子用封止剤セットである。
以下に本発明を詳述する。
周辺封止剤と面内封止剤とを用いて大型の有機ＥＬ表示素子を作製した場合、基板等に反りが生じて剥離することがあった。本発明者らは、基板等の反りの原因が、周辺封止剤の硬化収縮率が面内封止剤の硬化収縮率に対して大きいことであると考えた。そこで本発明者らは、面内封止剤の硬化収縮率に対する周辺封止剤の硬化収縮率の比率を１．００以下となるようにした有機ＥＬ表示素子用封止剤セットを用いることにより、有機ＥＬ表示素子の基板等の反りを抑制できることを見出し、本発明を完成させるに至った。
本発明の有機ＥＬ表示素子用封止剤セットは、有機ＥＬ表示素子の周縁部を囲んで封止する周辺封止剤と、該周辺封止剤の内側において有機発光材料層を有する積層体を被覆して封止する面内封止剤とを組み合わせてなる。
本発明の有機ＥＬ表示素子用封止剤セットは、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率（周辺封止剤の硬化収縮率／面内封止剤の硬化収縮率）が１．００以下である。上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率が１．００以下であることにより、本発明の有機ＥＬ表示素子用封止剤セットは、有機ＥＬ表示素子の基板等の反りを抑制できるものとなる。上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率の好ましい上限は０．９８である。
なお、本明細書において上記「硬化収縮率」は、硬化前の封止剤の２５℃における比重をＧＡ、封止剤の硬化物の２５℃における比重をＧＢとしたとき、下記式により算出される値である。
　硬化収縮率（％）＝（（ＧＢ－ＧＡ）／ＧＢ）×１００
上記比重の測定を行う硬化物としては、光硬化性の封止剤であれば、封止剤を厚さ１０μｍに成膜した後、ＵＶ－ＬＥＤ照射装置を用いて波長３６５ｎｍの紫外線を３０００ｍＪ／ｃｍ２照射して硬化させたものが用いられる。また、熱硬化性の封止剤であれば、封止剤を厚さ１０μｍに成膜した後、１００℃で３０分加熱して硬化させたものが用いられる。更に、光熱硬化性の封止剤であれば、封止剤を厚さ１０μｍに成膜した後、ＵＶ－ＬＥＤ照射装置を用いて波長３６５ｎｍの紫外線を３０００ｍＪ／ｃｍ２照射した後、１００℃で３０分加熱して硬化させたものが用いられる。
本発明の有機ＥＬ表示素子用封止剤セットにおいて、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率を上述した範囲とする方法としては、それぞれの封止剤に含まれる各構成成分の種類及びその含有割合を調整する方法が好適である。
（周辺封止剤）
上記周辺封止剤は、ポリオレフィンを含有することが好ましい。
上記ポリオレフィンを含有することにより、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率を上述した範囲とすることが容易となる。また、得られる周辺封止剤が硬化物の透湿防止性に優れるものとなる。
硬化物の透湿防止性を更に向上させる観点から、上記ポリオレフィンとしては、ポリイソブチレン、ポリブテン、及び、ポリブタジエンからなる群より選択される少なくとも１種を含むことが好ましく、ポリイソブチレンを含むことがより好ましい。
上記ポリオレフィンは、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記ポリオレフィンの重量平均分子量の好ましい下限は１万、好ましい上限は４０万である。上記ポリオレフィンの重量平均分子量がこの範囲であることにより、得られる周辺封止剤が塗布性、接着性、及び、硬化物の透湿防止性により優れるものとなる。
なお、本明細書において上記「重量平均分子量」は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）で溶媒としてテトラヒドロフランを用いて測定を行い、ポリスチレン換算により求められる値である。ＧＰＣによってポリスチレン換算による重量平均分子量を測定する際に用いるカラムとしては、例えば、Ｓｈｏｄｅｘ　ＬＦ－８０４（昭和電工社製）等が挙げられる。
上記周辺封止剤１００重量部中における上記ポリオレフィンの含有量の好ましい下限は５重量部、好ましい上限は７０重量部である。上記ポリオレフィンの含有量が５重量部以上であることにより、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率を上述した範囲とすることがより容易となる。また、得られる周辺封止剤が硬化物の透湿防止性により優れるものとなる。上記ポリオレフィンの含有量が７０重量部以下であることにより、得られる周辺封止剤が塗布性や接着性により優れるものとなる。上記ポリオレフィンの含有量のより好ましい下限は１０重量部、より好ましい上限は４０重量部である。
上記周辺封止剤は、硬化性樹脂を含有することが好ましい。
硬化性や接着性の観点から、上記硬化性樹脂としては、エポキシ化合物、オキセタン化合物、（メタ）アクリル化合物、及び、ウレタン化合物からなる群より選択される少なくとも１種を含むことが好ましく、エポキシ化合物及び／又は（メタ）アクリル化合物を含むことがより好ましい。
なお、本明細書において、上記「（メタ）アクリル」は、アクリル又はメタクリルを意味し、上記「（メタ）アクリル化合物」は、（メタ）アクリロイル基を有する化合物を意味し、上記「（メタ）アクリロイル」は、アクリロイル又はメタクリロイルを意味する。
上記エポキシ化合物としては、例えば、グリシジルエーテル化合物、脂環式エポキシ化合物等が挙げられる。
上記グリシジルエーテル化合物としては、例えば、ジエチレングリコールジグリシジルエーテル等が挙げられる。
上記脂環式エポキシ化合物としては、例えば、３，４－エポキシシクロヘキシルメチル（３，４－エポキシ）シクロヘキサンカルボキシレート、２，２－ビス（ヒドロキシメチル）－１－ブタノールの１，２－エポキシ－４－（２－オキシラニル）シクロヘキサン付加物等が挙げられる。
上記オキセタン化合物としては、例えば、１，４－ビス｛［（３－エチル－３－オキセタニル）メトキシ］メチル｝ベンゼン、ジ［２－（３－オキセタニル）ブチル］エーテル、３－エチル－３－ヒドロキシメチルオキセタン等が挙げられる。
上記（メタ）アクリル化合物としては、面内封止剤と相溶し難いものとする観点から、（メタ）アクリル酸エステル化合物が好適に用いられる。
上記（メタ）アクリル酸エステル化合物としては、例えば、イソボルニル（メタ）アクリレート、トリシクロデカンジメタノールジ（メタ）アクリレート、（メタ）アクリル酸アダマンチル、（メタ）アクリル酸メチルシクロヘキシル、（メタ）アクリル酸ノルボルニルメチル、（メタ）アクリル酸ジシクロペンタニル、（メタ）アクリル酸ジシクロペンテニル、（メタ）アクリル酸ジシクロペンテニルオキシエチル、（メタ）アクリル酸シクロデシル、（メタ）アクリル酸４－ｔ－ブチルシクロヘキシル、（メタ）アクリル酸トリメチルシクロヘキシル等が挙げられる。
なお、本明細書において、上記「（メタ）アクリレート」は、アクリレート又はメタクリレートを意味する。
上記ウレタン化合物としては、例えば、イソシアネート化合物と任意のポリオール化合物の反応物等が挙げられる。
上記イソシアネート化合物としては、例えば、トルエンジイソシアネート化合物、ジフェニルメタンジイソシアネート化合物等が挙げられる。
上記トルエンジイソシアネート化合物としては、例えば、２，４－トリレンジイソシアネート（２，４－ＴＤＩ）、２，６－トリレンジイソシアネート、又は、これらの混合物等が挙げられる。
上記ジフェニルメタンジイソシアネート化合物としては、例えば、４，４’－ジフェニルメタンジイソシアネート（４，４’－ＭＤＩ）、２，４’－ジフェニルメタンジイソシアネート（２，４’－ＭＤＩ）、又は、これらの混合物等が挙げられる。
上記周辺封止剤１００重量部中における上記硬化性樹脂の含有量の好ましい下限は５重量部、好ましい上限は７０重量部である。上記硬化性樹脂の含有量が５重量部以上であることにより、得られる周辺封止剤が硬化性や接着性により優れるものとなる。上記硬化性樹脂の含有量が７０重量部以下であることにより、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率を上述した範囲とすることがより容易となる。また、得られる周辺封止剤が硬化物の透湿防止性により優れるものとなる。上記硬化性樹脂の含有量のより好ましい下限は１０重量部、より好ましい上限は３０重量部である。
上記周辺封止剤は、接着性を更に向上させること等を目的として、粘着付与樹脂を含有することが好ましい。
上記粘着付与樹脂としては、例えば、テルペン樹脂、変性テルペン樹脂、クマロン樹脂、インデン樹脂、石油樹脂等が挙げられる。
上記変性テルペン樹脂としては、例えば、水素添加テルペン樹脂、テルペンフェノール共重合樹脂、芳香族変性テルペン樹脂等が挙げられる。
上記石油樹脂としては、例えば、脂肪族系石油樹脂、水添脂環式石油樹脂、芳香族系石油樹脂、脂肪族芳香族共重合系石油樹脂、脂環族系石油樹脂、ジシクロペンタジエン系石油樹脂及びその水素化物等が挙げられる。
なかでも、上記粘着付与樹脂としては、有機ＥＬ表示素子用封止剤の接着性、耐透湿性、相溶性等の観点から、テルペン樹脂、芳香族変性テルペン樹脂、テルペンフェノール共重合樹脂、水添脂環式石油樹脂、芳香族系石油樹脂、脂肪族芳香族共重合系石油樹脂、脂環族系石油樹脂が好ましく、脂環族系石油樹脂がより好ましく、脂環族飽和炭化水素樹脂、脂環族不飽和炭化水素樹脂が更に好ましく、シクロヘキシル環含有飽和炭化水素樹脂、ジシクロペンタジエン変性炭化水素樹脂が特に好ましい。
これらの粘着付与樹脂は、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記周辺封止剤１００重量部中における上記粘着付与樹脂の含有量の好ましい下限は１重量部、好ましい上限は２５重量部である。上記粘着付与樹脂の含有量が１重量部以上であることにより、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率を上述した範囲とすることがより容易となる。また、得られる周辺封止剤が接着性により優れるものとなる。上記粘着付与樹脂の含有量が２５重量部以下であることにより得られる周辺封止剤が透湿防止性により優れるものとなる。上記粘着付与樹脂の含有量のより好ましい下限は３重量部、より好ましい上限は１５重量部である。
上記周辺封止剤は、重合開始剤及び／又は熱硬化剤を含有することが好ましい。
上記周辺封止剤は、なかでも、ラジカル重合開始剤、カチオン重合開始剤、及び、熱硬化剤からなる群より選択される少なくとも１種を含有することが好ましい。
上記ラジカル重合開始剤としては、光ラジカル重合開始剤や熱ラジカル重合開始剤が挙げられる。
上記光ラジカル重合開始剤としては、例えば、ベンゾフェノン化合物、アセトフェノン化合物、アシルフォスフィンオキサイド化合物、チタノセン化合物、オキシムエステル化合物、ベンゾインエーテル化合物、チオキサントン化合物等が挙げられる。
上記光ラジカル重合開始剤としては、具体的には例えば、１－ヒドロキシシクロヘキシルフェニルケトン、２－ベンジル－２－ジメチルアミノ－１－（４－モルフォリノフェニル）－１－ブタノン、２－（ジメチルアミノ）－２－（（４－メチルフェニル）メチル）－１－（４－（４－モルホリニル）フェニル）－１－ブタノン、２，２－ジメトキシ－２－フェニルアセトフェノン、ビス（２，４，６－トリメチルベンゾイル）フェニルホスフィンオキサイド、２－メチル－１－（４－メチルチオフェニル）－２－モルフォリノプロパン－１－オン、１－（４－（２－ヒドロキシエトキシ）－フェニル）－２－ヒドロキシ－２－メチル－１－プロパン－１－オン、１－（４－（フェニルチオ）フェニル）－１，２－オクタンジオン２－（Ｏ－ベンゾイルオキシム）、２，４，６－トリメチルベンゾイルジフェニルホスフィンオキサイド、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル等が挙げられる。
上記熱ラジカル重合開始剤としては、例えば、アゾ化合物、有機過酸化物等が挙げられる。
上記アゾ化合物としては、例えば、２，２’－アゾビス（２，４－ジメチルバレロニトリル）、アゾビスイソブチロニトリル等が挙げられる。
上記有機過酸化物としては、例えば、過酸化ベンゾイル、ケトンパーオキサイド、パーオキシケタール、ハイドロパーオキサイド、ジアルキルパーオキサイド、パーオキシエステル、ジアシルパーオキサイド、パーオキシジカーボネート等が挙げられる。
上記熱ラジカル重合開始剤のうち市販されているものとしては、例えば、ＶＰＥ－０２０１、ＶＰＥ－０４０１、ＶＰＥ－０６０１、ＶＰＳ－０５０１、ＶＰＳ－１００１、Ｖ－５０１（いずれも富士フイルム和光純薬社製）等が挙げられる。
上記カチオン重合開始剤としては、光カチオン重合開始剤や熱カチオン重合開始剤が挙げられる。
上記光カチオン重合開始剤は、光照射によりプロトン酸又はルイス酸を発生するものであれば特に限定されず、イオン性光酸発生型であってもよいし、非イオン性光酸発生型であってもよい。
上記イオン性光酸発生型の光カチオン重合開始剤のアニオン部分としては、例えば、ＢＦ４ －、ＰＦ６ －、ＳｂＦ６ －、又は、（ＢＸ４）－（但し、Ｘは、少なくとも２つ以上のフッ素又はトリフルオロメチル基で置換されたフェニル基を表す）等が挙げられる。
上記イオン性光酸発生型の光カチオン重合開始剤としては、例えば、上記アニオン部分を有する、芳香族スルホニウム塩、芳香族ヨードニウム塩、芳香族ジアゾニウム塩、芳香族アンモニウム塩、（２，４－シクロペンタジエン－１－イル）（（１－メチルエチル）ベンゼン）－Ｆｅ塩等が挙げられる。
上記芳香族スルホニウム塩としては、例えば、ビス（４－（ジフェニルスルホニオ）フェニル）スルフィドビスヘキサフルオロホスフェート、ビス（４－（ジフェニルスルホニオ）フェニル）スルフィドビスヘキサフルオロアンチモネート、ビス（４－（ジフェニルスルホニオ）フェニル）スルフィドビステトラフルオロボレート、ビス（４－（ジフェニルスルホニオ）フェニル）スルフィドテトラキス（ペンタフルオロフェニル）ボレート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロホスフェート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロアンチモネート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムテトラフルオロボレート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、トリフェニルスルホニウムヘキサフルオロホスフェート、トリフェニルスルホニウムヘキサフルオロアンチモネート、トリフェニルスルホニウムテトラフルオロボレート、トリフェニルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、トリアリールスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、ビス（４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル）スルフィドビスヘキサフルオロホスフェート、ビス（４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル）スルフィドビスヘキサフルオロアンチモネート、ビス（４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル）スルフィドビステトラフルオロボレート、ビス（４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル）スルフィドテトラキス（ペンタフルオロフェニル）ボレート、トリス（４－（４－アセチルフェニル）チオフェニル）スルホニウムテトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
上記芳香族ヨードニウム塩としては、例えば、ジフェニルヨードニウムヘキサフルオロホスフェート、ジフェニルヨードニウムヘキサフルオロアンチモネート、ジフェニルヨードニウムテトラフルオロボレート、ジフェニルヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、ビス（ドデシルフェニル）ヨードニウムヘキサフルオロホスフェート、ビス（ドデシルフェニル）ヨードニウムヘキサフルオロアンチモネート、ビス（ドデシルフェニル）ヨードニウムテトラフルオロボレート、ビス（ドデシルフェニル）ヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムヘキサフルオロホスフェート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムヘキサフルオロアンチモネート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムテトラフルオロボレート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムテトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
上記芳香族ジアゾニウム塩としては、例えば、フェニルジアゾニウムヘキサフルオロホスフェート、フェニルジアゾニウムヘキサフルオロアンチモネート、フェニルジアゾニウムテトラフルオロボレート、フェニルジアゾニウムテトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
上記芳香族アンモニウム塩としては、例えば、１－ベンジル－２－シアノピリジニウムヘキサフルオロホスフェート、１－ベンジル－２－シアノピリジニウムヘキサフルオロアンチモネート、１－ベンジル－２－シアノピリジニウムテトラフルオロボレート、１－ベンジル－２－シアノピリジニウムテトラキス（ペンタフルオロフェニル）ボレート、１－（ナフチルメチル）－２－シアノピリジニウムヘキサフルオロホスフェート、１－（ナフチルメチル）－２－シアノピリジニウムヘキサフルオロアンチモネート、１－（ナフチルメチル）－２－シアノピリジニウムテトラフルオロボレート、１－（ナフチルメチル）－２－シアノピリジニウムテトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
上記（２，４－シクロペンタジエン－１－イル）（（１－メチルエチル）ベンゼン）－Ｆｅ塩としては、例えば、（２，４－シクロペンタジエン－１－イル）（（１－メチルエチル）ベンゼン）－Ｆｅ（ＩＩ）ヘキサフルオロホスフェート、（２，４－シクロペンタジエン－１－イル）（（１－メチルエチル）ベンゼン）－Ｆｅ（ＩＩ）ヘキサフルオロアンチモネート、（２，４－シクロペンタジエン－１－イル）（（１－メチルエチル）ベンゼン）－Ｆｅ（ＩＩ）テトラフルオロボレート、（２，４－シクロペンタジエン－１－イル）（（１－メチルエチル）ベンゼン）－Ｆｅ（ＩＩ）テトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
上記非イオン性光酸発生型の光カチオン重合開始剤としては、例えば、ニトロベンジルエステル、スルホン酸誘導体、リン酸エステル、フェノールスルホン酸エステル、ジアゾナフトキノン、Ｎ－ヒドロキシイミドスルホネート等が挙げられる。
上記光カチオン重合開始剤のうち市販されているものとしては、例えば、みどり化学社製の光カチオン重合開始剤、ユニオンカーバイド社製の光カチオン重合開始剤、ＡＤＥＫＡ社製の光カチオン重合開始剤、３Ｍ社製の光カチオン重合開始剤、ＢＡＳＦ社製の光カチオン重合開始剤、ローディア社製の光カチオン重合開始剤等が挙げられる。
上記みどり化学社製の光カチオン重合開始剤としては、例えば、ＤＴＳ－２００等が挙げられる。
上記ユニオンカーバイド社製の光カチオン重合開始剤としては、例えば、ＵＶＩ６９９０、ＵＶＩ６９７４等が挙げられる。
上記ＡＤＥＫＡ社製の光カチオン重合開始剤としては、例えば、ＳＰ－１５０、ＳＰ－１７０等が挙げられる。
上記３Ｍ社製の光カチオン重合開始剤としては、例えば、ＦＣ－５０８、ＦＣ－５１２等が挙げられる。
上記ＢＡＳＦ社製の光カチオン重合開始剤としては、例えば、ＩＲＧＡＣＵＲＥ２６１、ＩＲＧＡＣＵＲＥ２９０等が挙げられる。
上記ローディア社製の光カチオン重合開始剤としては、例えば、ＰＩ２０７４等が挙げられる。
上記熱カチオン重合開始剤としては、アニオン部分がＢＦ４ －、ＰＦ６ －、ＳｂＦ６ －、又は、（ＢＸ４）－（但し、Ｘは、少なくとも２つ以上のフッ素又はトリフルオロメチル基で置換されたフェニル基を表す）で構成される、スルホニウム塩、ホスホニウム塩、アンモニウム塩等が挙げられる。なかでも、スルホニウム塩、アンモニウム塩が好ましい。
上記スルホニウム塩としては、トリフェニルスルホニウムテトラフルオロボレート、トリフェニルスルホニウムヘキサフルオロアンチモネート等が挙げられる。
上記ホスホニウム塩としては、エチルトリフェニルホスホニウムヘキサフルオロアンチモネート、テトラブチルホスホニウムヘキサフルオロアンチモネート等が挙げられる。
上記アンモニウム塩としては、例えば、ジメチルフェニル（４－メトキシベンジル）アンモニウムヘキサフルオロホスフェート、ジメチルフェニル（４－メトキシベンジル）アンモニウムヘキサフルオロアンチモネート、ジメチルフェニル（４－メトキシベンジル）アンモニウムテトラキス（ペンタフルオロフェニル）ボレート、ジメチルフェニル（４－メチルベンジル）アンモニウムヘキサフルオロホスフェート、ジメチルフェニル（４－メチルベンジル）アンモニウムヘキサフルオロアンチモネート、ジメチルフェニル（４－メチルベンジル）アンモニウムヘキサフルオロテトラキス（ペンタフルオロフェニル）ボレート、メチルフェニルジベンジルアンモニウムヘキサフルオロホスフェート、メチルフェニルジベンジルアンモニウムヘキサフルオロアンチモネート、メチルフェニルジベンジルアンモニウムテトラキス（ペンタフルオロフェニル）ボレート、フェニルトリベンジルアンモニウムテトラキス（ペンタフルオロフェニル）ボレート、ジメチルフェニル（３，４－ジメチルベンジル）アンモニウムテトラキス（ペンタフルオロフェニル）ボレート、Ｎ，Ｎ－ジメチル－Ｎ－ベンジルアニリニウムヘキサフルオロアンチモネート、Ｎ，Ｎ－ジエチル－Ｎ－ベンジルアニリニウムテトラフルオロボレート、Ｎ，Ｎ－ジメチル－Ｎ－ベンジルピリジニウムヘキサフルオロアンチモネート、Ｎ，Ｎ－ジエチル－Ｎ－ベンジルピリジニウムトリフルオロメタンスルホン酸等が挙げられる。
上記熱カチオン重合開始剤のうち市販されているものとしては、例えば、三新化学工業社製の熱カチオン重合開始剤、Ｋｉｎｇ　Ｉｎｄｕｓｔｒｉｅｓ社製の熱カチオン重合開始剤等が挙げられる。
上記三新化学工業社製の熱カチオン重合開始剤としては、例えば、サンエイドＳＩ－６０、サンエイドＳＩ－８０、サンエイドＳＩ－Ｂ３、サンエイドＳＩ－Ｂ３Ａ、サンエイドＳＩ－Ｂ４等が挙げられる。
上記Ｋｉｎｇ　Ｉｎｄｕｓｔｒｉｅｓ社製の熱カチオン重合開始剤としては、例えば、ＣＸＣ－１６１２、ＣＸＣ－１８２１等が挙げられる。
上記周辺封止剤１００重量部中における上記重合開始剤の含有量の好ましい下限は０．０５重量部、好ましい上限は３重量部である。上記重合開始剤の含有量が０．０５重量部以上であることにより、得られる周辺封止剤が硬化性により優れるものとなる。上記重合開始剤の含有量が３重量部以下であることにより、得られる周辺封止剤の硬化反応が速くなり過ぎず、作業性により優れるものとなり、硬化物をより均一なものとすることができる。上記重合開始剤の含有量のより好ましい下限は０．３重量部、より好ましい上限は２重量部である。
上記熱硬化剤としては、例えば、ヒドラジド化合物、イミダゾール誘導体、酸無水物、ジシアンジアミド、グアニジン誘導体、変性脂肪族ポリアミン、各種アミンとエポキシ樹脂との付加生成物等が挙げられる。
上記ヒドラジド化合物としては、例えば、１，３－ビス（ヒドラジノカルボエチル）－５－イソプロピルヒダントイン、セバシン酸ジヒドラジド、イソフタル酸ジヒドラジド、アジピン酸ジヒドラジド、マロン酸ジヒドラジド等が挙げられる。
上記イミダゾール誘導体としては、例えば、１－シアノエチル－２－フェニルイミダゾール、Ｎ－（２－（２－メチル－１－イミダゾリル）エチル）尿素、２，４－ジアミノ－６－（２’－メチルイミダゾリル－（１’））－エチル－ｓ－トリアジン、Ｎ，Ｎ’－ビス（２－メチル－１－イミダゾリルエチル）尿素、Ｎ，Ｎ’－（２－メチル－１－イミダゾリルエチル）－アジポアミド、２－フェニル－４－メチル－５－ヒドロキシメチルイミダゾール、２－フェニル－４，５－ジヒドロキシメチルイミダゾール等が挙げられる。
上記酸無水物としては、例えば、テトラヒドロ無水フタル酸、エチレングリコールビス（アンヒドロトリメリテート）等が挙げられる。
これらの熱硬化剤は、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記熱硬化剤のうち市販されているものとしては、例えば、ＳＤＨ（日本ファインケム社製）、ＡＤＨ（大塚化学社製）、アミキュアＶＤＨ、アミキュアＶＤＨ－Ｊ、アミキュアＵＤＨ（いずれも味の素ファインテクノ社製）等が挙げられる。
上記周辺封止剤１００重量部中における上記熱硬化剤の含有量の好ましい下限は０．０５重量部、好ましい上限は５重量部である。上記熱硬化剤の含有量が０．０５重量部以上であることにより、得られる周辺封止剤が熱硬化性により優れるものとなる。上記熱硬化剤の含有量が５重量部以下であることにより、得られる周辺封止剤が保存安定性により優れるものとなる。上記熱硬化剤の含有量のより好ましい下限は０．５重量部、より好ましい上限は３重量部である。
上記周辺封止剤は、吸水性フィラーを含有することが好ましい。上記吸水性フィラーを含有することにより、上記周辺封止剤は、硬化物の透湿防止性により優れるものとなる。
上記吸水性フィラーとしては、例えば、アルカリ土類金属の酸化物、酸化マグネシウム、モレキュラーシーブ等が挙げられる。
上記アルカリ土類金属の酸化物としては、例えば、酸化カルシウム、酸化ストロンチウム、酸化バリウム等が挙げられる。
なかでも、吸水性の観点から、アルカリ土類金属の酸化物が好ましく、酸化カルシウムがより好ましい。
これらの吸水性フィラーは、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記周辺封止剤１００重量部中における上記吸水性フィラーの含有量の好ましい下限は３重量部、好ましい上限は６５重量部である。上記吸水性フィラーの含有量がこの範囲であることにより、得られる周辺封止剤がパネル剥がれを抑制しつつ、硬化物がより優れた透湿防止性を有するものとなる。上記吸水性フィラーの含有量のより好ましい下限は１５重量部である。
上記周辺封止剤は、接着性を向上させること等を目的として、本発明の目的を阻害しない範囲において、上記吸水性フィラーに加えて、その他のフィラーを含有してもよい。
上記その他のフィラーとしては、無機フィラーや有機フィラーを用いることができる。
上記無機フィラーとしては、例えば、シリカ、タルク、アルミナ等が挙げられる。
上記有機フィラーとしては、例えば、ポリエステル微粒子、ポリウレタン微粒子、ビニル重合体微粒子、アクリル重合体微粒子等が挙げられる。なかでも、タルクが好ましい。
これらのその他のフィラーは、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記周辺封止剤は、増感剤を含有してもよい。上記増感剤は、上記重合開始剤の重合開始効率をより向上させて、上記周辺封止剤の硬化反応をより促進させる役割を有する。
上記増感剤としては、例えば、アントラセン系化合物、チオキサントン系化合物、２，２－ジメトキシ－１，２－ジフェニルエタン－１－オン、ベンゾフェノン、２，４－ジクロロベンゾフェノン、ｏ－ベンゾイル安息香酸メチル、４，４’－ビス（ジメチルアミノ）ベンゾフェノン、４－ベンゾイル－４’－メチルジフェニルサルファイド等が挙げられる。
上記アントラセン系化合物としては、例えば、９，１０－ジブトキシアントラセン等が挙げられる。
上記チオキサントン系化合物としては、例えば、２，４－ジエチルチオキサントン等が挙げられる。
これらの増感剤は、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記周辺封止剤１００重量部中における上記増感剤の含有量の好ましい下限は０．０５重量部、好ましい上限は３重量部である。上記増感剤の含有量が０．０５重量部以上であることにより、増感効果がより発揮される。上記増感剤の含有量が３重量部以下であることにより、吸収が大きくなり過ぎずに深部まで光を伝えることができる。上記増感剤の含有量のより好ましい下限は０．１重量部、より好ましい上限は１重量部である。
上記周辺封止剤は、安定剤を含有してもよい。上記安定剤を含有することにより、上記周辺封止剤は、より保存安定性に優れるものとなる。
上記安定剤としては、例えば、芳香族アミン化合物、４－ヒドロキシ－２，２，６，６－テトラメチルピペリジン－１－オキシル等が挙げられる。
上記芳香族アミン化合物としては、例えば、ベンジルアミン、アミノフェノール型エポキシ樹脂等が挙げられる。
なかでも、芳香族系アミン化合物が好ましく、ベンジルアミンがより好ましい。
これらの安定剤は、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記周辺封止剤１００重量部中における上記安定剤の含有量の好ましい下限は０．００１重量部、好ましい上限は２重量部である。上記安定剤の含有量がこの範囲であることにより、得られる周辺封止剤が優れた硬化性を維持したまま保存安定性により優れるものとなる。上記安定剤の含有量のより好ましい下限は０．００５重量部、より好ましい上限は１重量部である。
上記周辺封止剤は、シランカップリング剤を含有してもよい。上記シランカップリング剤は、上記周辺封止剤と基板等との接着性を向上させる役割を有する。
上記シランカップリング剤としては、例えば、３－アミノプロピルトリメトキシシラン、３－メルカプトプロピルトリメトキシシラン、３－グリシドキシプロピルトリメトキシシラン、３－イソシアネートプロピルトリメトキシシラン等が挙げられる。
これらのシランカップリング剤は、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記周辺封止剤１００重量部中における上記シランカップリング剤の含有量の好ましい下限は０．１重量部、好ましい上限は１０重量部である。上記シランカップリング剤の含有量がこの範囲であることにより、余剰のシランカップリング剤のブリードアウトを防止しつつ、得られる周辺封止剤の接着性を向上させる効果により優れるものとなる。上記シランカップリング剤の含有量のより好ましい下限は０．３重量部、より好ましい上限は３重量部である。
上記周辺封止剤は、本発明の目的を阻害しない範囲において、表面改質剤を含有してもよい。上記表面改質剤を含有することにより、上記周辺封止剤の塗膜の平坦性を向上させることができる。
上記表面改質剤としては、例えば、界面活性剤やレベリング剤等が挙げられ、例えば、シリコーン系、アクリル系、フッ素系等のものを用いることができる。
上記表面改質剤のうち市販されているものとしては、例えば、ビックケミー・ジャパン社製の表面改質剤、楠本化成社製の表面改質剤、ＡＧＣセイミケミカル社製の表面改質剤等が挙げられる。
上記ビックケミー・ジャパン社製の表面改質剤としては、例えば、ＢＹＫ－３００、ＢＹＫ－３０２、ＢＹＫ－３３１等が挙げられる。
上記楠本化成社製の表面改質剤としては、例えば、ＵＶＸ－２７２等が挙げられる。
上記ＡＧＣセイミケミカル社製の表面改質剤としては、例えば、サーフロンＳ－６１１等が挙げられる。
上記周辺封止剤は、本発明の目的を阻害しない範囲で、周辺封止剤中に発生した酸と反応する化合物及び／又はイオン交換樹脂を含有してもよい。
上記発生した酸と反応する化合物としては、酸と中和する物質、例えば、アルカリ金属の炭酸塩若しくは炭酸水素塩、又は、アルカリ土類金属の炭酸塩若しくは炭酸水素塩等が挙げられる。具体的には例えば、炭酸カルシウム、炭酸水素カルシウム、炭酸ナトリウム、炭酸水素ナトリウム等が用いられる。
上記イオン交換樹脂としては、陽イオン交換型、陰イオン交換型、両イオン交換型のいずれも使用することができるが、特に塩化物イオンを吸着することのできる陽イオン交換型又は両イオン交換型が好適である。
上記周辺封止剤は、本発明の目的を阻害しない範囲で、必要に応じて、硬化遅延剤、補強剤、軟化剤、可塑剤、粘度調整剤、紫外線吸収剤、酸化防止剤、スペーサー等の公知の各種添加剤を含有してもよい。
上記周辺封止剤は、アウトガスの発生を抑制する観点から、溶剤を含有しないことが好ましい。
なお、本明細書において「溶剤を含有しない」とは、溶剤の含有量が１０００ｐｐｍ未満であることを意味する。
上記周辺封止剤を製造する方法としては、例えば、混合機を用いて、ポリオレフィンと、硬化性樹脂と、重合開始剤及び／又は熱硬化剤と、吸水性フィラーや必要に応じて添加するシランカップリング剤等の添加剤とを混合する方法等が挙げられる。
上記混合機としては、例えば、ホモディスパー、ホモミキサー、万能ミキサー、プラネタリーミキサー、ニーダー、３本ロール等が挙げられる。
（面内封止剤）
上記面内封止剤は、硬化性樹脂を含有することが好ましい。
上記硬化性樹脂としては、脂環式エポキシ化合物及び／又はオキセタン化合物を用いることが好ましい。なかでも、保存安定性と速硬化性とを両立する観点から、上記硬化性樹脂として上記脂環式エポキシ化合物と上記オキセタン化合物とを組み合わせて用いることがより好ましい。
上記脂環式エポキシ化合物としては、例えば、３，４－エポキシシクロヘキシルメチル（メタ）アクリレート、１，２：８，９－ジエポキシリモネン、４－ビニルシクロヘキセンモノオキサイド、ビニルシクロヘキセンジオキサイド、メチル化ビニルシクロヘキセンジオキサイド、（３，４－エポキシシクロヘキシル）メチル－３，４－エポキシシクロヘキシルカルボキシレート、ビス（３，４－エポキシシクロヘキシルメチル）エーテル、３，４，３’，４’－ジエポキビシクロヘキシル、ビス（３，４－エポキシシクロヘキシル）アジペート、ビス（２，３－エポキシシクロペンチル）エーテル、ビス（３，４－エポキシ－６－メチルシクロヘキシルメチル）アジペート、ジシクロペンタジエンジオキサイド等が挙げられる。なかでも、上記脂環式エポキシ化合物は、下記式（１）で表される脂環式エポキシ化合物を含むことが好ましい。
Figure JPOXMLDOC01-appb-C000001
式（１）中、Ｘは、－Ｃ（＝Ｏ）Ｏ－若しくは－Ｃ（＝Ｏ）－で中断又は直結されていてもよい炭素数１～６の直鎖状又は分岐鎖状の炭化水素基、或いは、結合手を表す。
上記オキセタン化合物としては、例えば、４，４’－ビス（（３－エチル－３－オキセタニル）メトキシメチル）ビフェニル、３－エチル－３－（（（３－エチルオキセタン－３－イル）メトキシ）メチル）オキセタン、フェノキシメチルオキセタン、３－エチル－３－ヒドロキシメチルオキセタン、３－エチル－３－（フェノキシメチル）オキセタン、３－エチル－３－（（２－エチルヘキシルオキシ）メチル）オキセタン、３－エチル－３－（（３－（トリエトキシシリル）プロポキシ）メチル）オキセタン、オキセタニルシルセスキオキサン、フェノールノボラックオキセタン、１，４－ビス（（（３－エチル－３－オキセタニル）メトキシ）メチル）ベンゼン等が挙げられる。なかでも、上記オキセタン化合物は、３－エチル－３－（（（３－エチルオキセタン－３－イル）メトキシ）メチル）オキセタンを含むことが好ましい。
上記硬化性樹脂は、本発明の目的を阻害しない範囲で、粘度調整等の目的で他の硬化性樹脂を含有してもよい。
上記他の硬化性樹脂としては、例えば、上記脂環式エポキシ化合物以外のその他のエポキシ化合物や、ビニルエーテル化合物等が挙げられる。
上記その他のエポキシ化合物としては、例えば、ジシクロペンタジエンジメタノールジグリシジルエーテル、ビスフェノールＡジグリシジルエーテル、ビスフェノールＦジグリシジルエーテル、水添ビスフェノールＡジグリシジルエーテル、水添ビスフェノールＦジグリシジルエーテル等が挙げられる。
上記ビニルエーテル化合物としては、例えば、ベンジルビニルエーテル、シクロヘキサンジメタノールモノビニルエーテル、ジシクロペンタジエンビニルエーテル、１，４－ブタンジオールジビニルエーテル、シクロヘキサンジメタノールジビニルエーテル、ジエチレングリコールジビニルエーテル、トリエチレングリコールジビニルエーテル、ジプロピレングリコールジビニルエーテル、トリプロピレングリコールジビニルエーテル等が挙げられる。
上記面内封止剤１００重量部中における上記硬化性樹脂の含有量の好ましい下限は７０重量部、好ましい上限は９９．９９重量部である。上記硬化性樹脂の含有量がこの範囲であることにより、上記面内封止剤の硬化収縮率に対する上記周辺封止剤の硬化収縮率の比率を上述した範囲とすることが容易となる。また、得られる面内封止剤が硬化性や接着性により優れるものとなる。上記硬化性樹脂の含有量のより好ましい下限は８０重量部、より好ましい上限は９９．９８重量部である。
上記面内封止剤は、重合開始剤を含有することが好ましく、カチオン重合開始剤を含有することがより好ましい。
上記面内封止剤に用いられるカチオン重合開始剤としては、上記周辺封止剤において挙げたものと同様のものを用いることができる。
上記面内封止剤１００重量部中における上記重合開始剤の含有量の好ましい下限は０．０５重量部、好ましい上限は１０重量部である。上記重合開始剤の含有量がこの範囲であることにより、得られる面内封止剤が硬化性及び保存安定性により優れるものとなる。上記重合開始剤の含有量のより好ましい下限は０．２重量部、より好ましい上限は５重量部である。
上記面内封止剤は、増感剤を含有してもよい。上記増感剤は、上記重合開始剤の重合開始効率をより向上させて、上記面内封止剤の硬化反応をより促進させる役割を有する。
上記面内封止剤に用いられる増感剤としては、上記周辺封止剤において挙げたものと同様のものを用いることができる。
上記面内封止剤１００重量部中における上記増感剤の含有量の好ましい下限は０．０５重量部、好ましい上限は３重量部である。上記増感剤の含有量が０．０５重量部以上であることにより、増感効果がより発揮される。上記増感剤の含有量が３重量部以下であることにより、吸収が大きくなり過ぎずに深部まで光を伝えることができる。上記増感剤の含有量のより好ましい下限は０．１重量部、より好ましい上限は１重量部である。
上記面内封止剤は、熱硬化剤を含有してもよい。
上記面内封止剤に用いられる熱硬化剤としては、上記周辺封止剤において挙げたものと同様のものを用いることができる。
上記面内封止剤１００重量部中における上記熱硬化剤の含有量の好ましい下限は０．０１重量部、好ましい上限は１０重量部である。上記熱硬化剤の含有量が０．０１重量部以上であることにより、得られる周辺封止剤が熱硬化性により優れるものとなる。上記熱硬化剤の含有量が１０重量部以下であることにより、得られる周辺封止剤が保存安定性により優れるものとなる。上記熱硬化剤の含有量のより好ましい下限は０．５重量部、より好ましい上限は５重量部、更に好ましい下限は１重量部、更に好ましい上限は３重量部である。
上記面内封止剤は、安定剤を含有してもよい。
上記安定剤としては、例えば、芳香族アミン化合物、４－ヒドロキシ－２，２，６，６－テトラメチルピペリジン－１－オキシル等が挙げられる。
上記芳香族アミン化合物としては、例えば、ベンジルアミン、アミノフェノール型エポキシ樹脂等が挙げられる。
なかでも、芳香族アミン化合物が好ましく、ベンジルアミンがより好ましい。
これらの安定剤は、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
上記面内封止剤１００重量部中における上記安定剤の含有量の好ましい下限は０．００１重量部、好ましい上限は２重量部である。上記安定剤の含有量がこの範囲であることにより、得られる周辺封止剤が優れた硬化性を維持したまま保存安定性により優れるものとなる。上記安定剤の含有量のより好ましい下限は０．００５重量部、より好ましい上限は１重量部である。
上記面内封止剤は、接着性を向上させること等を目的として、本発明の目的を阻害しない範囲において、フィラーを含有してもよい。
上記面内封止剤が含有してもよいフィラーとしては、無機フィラーや有機フィラーを用いることができる。
上記無機フィラーとしては、例えば、シリカ、タルク、アルミナ等が挙げられる。
上記有機フィラーとしては、例えば、ポリエステル微粒子、ポリウレタン微粒子、ビニル重合体微粒子、アクリル重合体微粒子等が挙げられる。
上記面内封止剤１００重量部中における上記フィラーの含有量の好ましい下限は０．００１重量部、好ましい上限は２重量部である。上記フィラーの含有量がこの範囲であることにより、優れた塗布性を維持しつつ、得られる面内封止剤の接着性を向上させる効果により優れるものとなる。
上記面内封止剤は、シランカップリング剤を含有してもよい。上記シランカップリング剤は、上記面内封止剤と基板等との接着性を向上させる役割を有する。
上記面内封止剤に用いられるシランカップリング剤としては、上記周辺封止剤において挙げたものと同様のものを用いることができる。
上記面内封止剤１００重量部中における上記シランカップリング剤の含有量の好ましい下限は０．１重量部、好ましい上限は１０重量部である。上記シランカップリング剤の含有量がこの範囲であることにより、余剰のシランカップリング剤のブリードアウトを防止しつつ、得られる面内封止剤の接着性を向上させる効果により優れるものとなる。上記シランカップリング剤の含有量のより好ましい下限は０．３重量部、より好ましい上限は５重量部である。
上記面内封止剤は、本発明の目的を阻害しない範囲において、表面改質剤を含有してもよい。上記表面改質剤を含有することにより、上記面内封止剤の塗膜の平坦性を向上させることができる。
上記面内封止剤に用いられる表面改質剤としては、上記周辺封止剤において挙げたものと同様のものを用いることができる。
本発明の有機ＥＬ表示素子用面内封止剤は、本発明の目的を阻害しない範囲で、素子電極の耐久性を向上させるために、有機ＥＬ表示素子用面内封止剤中に発生した酸と反応する化合物及び／又はイオン交換樹脂を含有してもよい。
上記面内封止剤に用いられる上記発生した酸と反応する化合物及び上記イオン交換樹脂としては、上記周辺封止剤において挙げたものと同様のものを用いることができる。
また、上記面内封止剤は、本発明の目的を阻害しない範囲で、必要に応じて、硬化遅延剤、補強剤、軟化剤、可塑剤、粘度調整剤、紫外線吸収剤、酸化防止剤等の公知の各種添加剤を含有してもよい。
上記面内封止剤は、アウトガスの発生を抑制する観点から、溶剤を含有しないことが好ましい。
上記面内封止剤を製造する方法としては、混合機を用いて、硬化性樹脂と、重合開始剤と、必要に応じて添加するシランカップリング剤等の添加剤とを混合する方法等が挙げられる。
上記混合機としては、例えば、ホモディスパー、ホモミキサー、万能ミキサー、プラネタリーミキサー、ニーダー、３本ロール等が挙げられる。
上記面内封止剤は、Ｅ型粘度計を用いて、２５℃、２０ｒｐｍの条件で測定した全体の粘度の好ましい下限が５０ｍＰａ・ｓ、好ましい上限が１５０ｍＰａ・ｓである。上記面内封止剤の粘度がこの範囲であることにより、塗布性により優れるものとなる。上記面内封止剤の粘度のより好ましい下限は６０ｍＰａ・ｓ、より好ましい上限は１４０ｍＰａ・ｓである。
なお、上記Ｅ型粘度計としては、例えば、ＶＩＳＣＯＭＥＴＥＲ　ＴＶ－２２（東機産業社製）等が挙げられる。
上記面内封止剤は、表面張力の好ましい下限が１５ｍＮ／ｍ、好ましい上限が４５ｍＮ／ｍである。上記面内封止剤の表面張力がこの範囲であることにより、塗布性により優れるものとなる。上記面内封止剤の表面張力のより好ましい下限は２０ｍＮ／ｍ、より好ましい上限は３５ｍＮ／ｍである。
なお、本明細書において、上記表面張力は、２５℃において動的濡れ性試験機により測定される値である。
（有機ＥＬ表示素子）
本発明の有機ＥＬ表示素子用封止剤セットにおける上記周辺封止剤の硬化物と上記面内封止剤の硬化物とを有する有機ＥＬ表示素子もまた、本発明の１つである。
本発明の有機ＥＬ表示素子において、上記周辺封止剤の硬化物は、有機ＥＬ表示素子の周縁部を囲む封止壁に用いられる。
上記周辺封止剤の硬化物を用いてなる封止壁は、得られる有機ＥＬ表示素子の表示領域を広く確保する等の観点から、厚さが５ｍｍ以下であることが好ましい。
本発明の有機ＥＬ表示素子としては、表示領域の大きさが対角４０インチ以上６０インチ以下であるものが好適である。
本発明によれば、有機ＥＬ表示素子の基板等の反りを抑制できる有機ＥＬ表示素子用封止剤セットを提供することができる。また、本発明によれば、該有機ＥＬ表示素子用封止剤セットの硬化物を有する有機ＥＬ表示素子を提供することができる。
以下に実施例を掲げて本発明を更に詳しく説明するが、本発明はこれら実施例のみに限定されない。
（実施例１～３、比較例１、２）
表１に記載された配合比に従い、スペーサー粒子以外の各材料を、撹拌混合機を用い、撹拌速度２０００ｒｐｍで３分間撹拌混合した後、更に３本ロールにて混練した。なお、表１における酸化カルシウムとしては、粒径が１０μｍ以下になるようにボールミル（日陶科学社製、「ＡＮＺ－５３Ｄ」）によって乾式バッチ粉砕したものを使用した。その後、スペーサー粒子を加え、撹拌混合機を用いて均一に分散させることにより、周辺封止剤を作製した。
また、表１に記載された配合比に従い、各材料を、撹拌混合機を用い、撹拌速度２０００ｒｐｍで３分間撹拌混合して面内封止剤を作製した。
上記撹拌混合機としては、ＡＲ－２５０（シンキー社製）を用い、上記３本ロールとしては、ＮＲ－４２Ａ（ノリタケ社製）を用いた。
得られた各周辺封止剤と各面内封止剤とを、表１に記載したように組み合わせて、有機ＥＬ表示素子用封止剤セットを得た。
得られた各周辺封止剤を１０μｍの厚さとなるように成膜した後、ＵＶ－ＬＥＤ照射装置を用いて波長３６５ｎｍの紫外線を３０００ｍＪ／ｃｍ２照射することにより硬化物を得た。また、得られた各面内封止剤を１０μｍの厚さとなるように成膜した後、１００℃で３０分オーブンで加熱することにより硬化物を得た。
得られた各周辺封止剤、各面内封止剤、及び、それらの硬化物について、電子はかり式比重計を用いて２５℃における比重を測定し、上述した式により硬化収縮率を測定した。上記電子はかり式比重計としては、ＤＭＥ－２２０Ｈ（新光電子社製）を用いた。各硬化収縮率の測定結果、及び、面内封止剤の硬化収縮率に対する周辺封止剤の硬化収縮率の比率（周辺封止剤の硬化収縮率／面内封止剤の硬化収縮率）を表１に示した。
＜評価＞
実施例及び比較例で得られた各有機ＥＬ表示素子用封止剤セットについて、以下の評価を行った。結果を表１に示した。
（反り防止性）
（１）有機発光材料層を有する積層体が配置された基板の作製
長さ５０ｍｍ、幅７０ｍｍ、厚さ０．７ｍｍのガラスにＩＴＯ電極を１０００Åの厚さとなるように成膜したものを基板とした。上記基板をアセトン、アルカリ水溶液、イオン交換水、及び、イソプロピルアルコールにてそれぞれ１５分間超音波洗浄した後、煮沸させたイソプロピルアルコールにて１０分間洗浄し、更に、ＵＶ－オゾンクリーナにて直前処理を行った。ＵＶ－オゾンクリーナとしては、ＮＬ－ＵＶ２５３（日本レーザー電子社製）を用いた。
次に、直前処理後の基板を真空蒸着装置の基板ホルダーに固定し、素焼きの坩堝にＮ，Ｎ’－ジ（１－ナフチル）－Ｎ，Ｎ’－ジフェニルベンジジン（α－ＮＰＤ）を２００ｍｇ入れ、別の素焼き坩堝にトリス（８－キノリノラト）アルミニウム（Ａｌｑ３）を２００ｍｇ入れ、真空チャンバー内を、１×１０－４Ｐａまで減圧した。その後、α－ＮＰＤの入った坩堝を加熱し、α－ＮＰＤを蒸着速度１５Å／ｓで基板に堆積させ、膜厚６００Åの正孔輸送層を成膜した。次いで、Ａｌｑ３の入った坩堝を加熱し、１５Å／ｓの蒸着速度で膜厚６００Åの有機発光材料層を成膜した。その後、正孔輸送層及び有機発光材料層が形成された基板を、タングステン製抵抗加熱ボートを有する別の真空蒸着装置に移し、真空蒸着装置内のタングステン製抵抗加熱ボートの１つにフッ化リチウム２００ｍｇを入れ、別のタングステン製抵抗加熱ボートにアルミニウム線１．０ｇを入れた。その後、真空蒸着装置の蒸着器内を２×１０－４Ｐａまで減圧してフッ化リチウムを０．２Å／ｓの蒸着速度で５Å成膜した後、アルミニウムを２０Å／ｓの速度で１０００Å成膜した。窒素により蒸着器内を常圧に戻し、１０ｍｍ×１０ｍｍの有機発光材料層を有する積層体が配置された基板を取り出した。
（２）有機ＥＬ表示素子の作製
積層体が配置された基板の周縁部に、周辺封止剤を線幅（硬化後の封止壁の厚さ）が５ｍｍとなるよう塗布し、その内側に面内封止剤を、積層体全体を覆うように塗布した後、長さ５０ｍｍ、幅５０ｍｍ、厚さ０．７ｍｍのガラスを重ね合わせた。その後、ＵＶ－ＬＥＤ照射装置を用いて波長３６５ｎｍの紫外線を３０００ｍＪ／ｃｍ２照射した後、１００℃で３０分加熱することで周辺封止剤及び面内封止剤を硬化させて有機ＥＬ表示素子を作製した。
（３）基板の反りの確認
得られた有機ＥＬ表示素子を９０℃で６０日間オーブンで加熱した後、平坦な面に置き、基板の反りの有無を確認した。基板の反りは、下側の基板の中心部が０．１ｍｍ以上浮いているか否かによって判定した。基板に反りが確認されなかった場合を「○」、基板に反りが確認された場合を「×」として反り防止性を評価した。
Figure JPOXMLDOC01-appb-T000002
本発明によれば、有機ＥＬ表示素子の基板等の反りを抑制できる有機ＥＬ表示素子用封止剤セットを提供することができる。また、本発明によれば、該有機ＥＬ表示素子用封止剤セットの硬化物を有する有機ＥＬ表示素子を提供することができる。

Claims (3)

  1. 有機ＥＬ表示素子の周縁部を囲んで封止する周辺封止剤と、該周辺封止剤の内側において有機発光材料層を有する積層体を被覆して封止する面内封止剤とを組み合わせてなる有機ＥＬ表示素子用封止剤セットであって、
    前記面内封止剤の硬化収縮率に対する前記周辺封止剤の硬化収縮率の比率が１．００以下である
    ことを特徴とする有機ＥＬ表示素子用封止剤セット。
  2. 前記周辺封止剤は、ポリオレフィンを含有する請求項１記載の有機ＥＬ表示素子用封止剤セット。
  3. 請求項１又は２記載の有機ＥＬ表示素子用封止剤セットにおける前記周辺封止剤の硬化物と前記面内封止剤の硬化物とを有する有機ＥＬ表示素子。
PCT/JP2020/025771 2019-07-04 2020-07-01 有機ｅｌ表示素子用封止剤セット及び有機ｅｌ表示素子 WO2021002379A1 (ja)