WO2021001691A4 - 透明導電性フィルム - Google Patents

透明導電性フィルム Download PDF

Info

Publication number
WO2021001691A4
WO2021001691A4 PCT/IB2020/000799 IB2020000799W WO2021001691A4 WO 2021001691 A4 WO2021001691 A4 WO 2021001691A4 IB 2020000799 W IB2020000799 W IB 2020000799W WO 2021001691 A4 WO2021001691 A4 WO 2021001691A4
Authority
WO
WIPO (PCT)
Prior art keywords
transparent conductive
base material
conductive layer
conductive film
less
Prior art date
Application number
PCT/IB2020/000799
Other languages
English (en)
French (fr)
Other versions
WO2021001691A3 (ja
WO2021001691A2 (ja
Inventor
才将 西森
智剛 梨木
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Publication of WO2021001691A2 publication Critical patent/WO2021001691A2/ja
Publication of WO2021001691A3 publication Critical patent/WO2021001691A3/ja
Publication of WO2021001691A4 publication Critical patent/WO2021001691A4/ja

Abstract

【解決手段】透明導電性フィルム１は、ガラス基材２と、透明導電層３とを順に備える。ガラス基材２の厚みは、１５０μｍ以下である。透明導電層３が結晶性である。透明導電層３の残留応力は、－１００ＭＰａ以上１００ＭＰａ以下である。

Description

透明導電性フィルム
　本発明は、透明導電性フィルムに関し、詳しくは、光学用途に好適に用いられる透明導電性フィルムに関する。
　従来から、インジウムスズ複合酸化物（ＩＴＯ）からなる透明導電層を所望の電極パターンに形成した透明導電性フィルムが、タッチパネルなどの光学用途に用いられる。
　このような透明導電性フィルムは、通常、基材と透明導電層とを順に備えている。
　従来、基材として、比較的厚いガラス基材を用いることが知られている。
　しかし、基材として、比較的厚いガラス基材を用いると可撓性が低下するため、可撓性を向上させる観点から、基材として、高分子フィルムを用いることが検討されている。
　一方で、先に基材の温度を上昇させてから、成膜することで、成膜と同時にＩＴＯを結晶化（「アズデポ結晶化」とも呼ばれる）させることができる。かかるアズデポ結晶化によって、一度アモルファスで成膜した後に、結晶化するよりも、透明電極層の表面抵抗値を低くできることが知られている。しかし、このような場合には、基板の温度を高温にして成膜するため、高分子フィルムの耐熱性の観点から、高分子フィルムを使用することはできない。
　そこで、可撓性を向上しつつ、表面抵抗値を低くする観点から、基材として、薄ガラスを用いることが検討されている。
　例えば、極薄ガラス透明基板と、透明導電性酸化物層とを備える透明積層基材が提案されている（例えば、特許文献１参照。）。
特開２０１７－１０６１２４公報
　しかるに、特許文献１のように、基材として、薄ガラスを用い、透明電極層を高温で結晶化すると、薄ガラスおよび透明導電性酸化物層との線膨張係数の差によって、透明導電性酸化物層がカールするという不具合がある。
　このようなカールは、基材として、高分子フィルムを用いた場合であっても生じるが、とりわけ、薄ガラスは、カールすることによって破損する場合があるため、高分子フィルムと比べて、より一層、カールの抑制が要求される。
　本発明は、カールを抑制することができる透明導電性フィルムを提供することにある。
　本発明［１］は、ガラス基材と、透明導電層とを順に備え、前記ガラス基材の厚みは、１５０μｍ以下であり、前記透明導電層が結晶性であり、前記透明導電層の残留応力が、－１００ＭＰａ以上１００ＭＰａ以下である、透明導電性フィルムである。
　本発明［２］は、前記透明導電層の表面抵抗値が、１０Ω／□以下である、請求項１に記載の透明導電性フィルムを含んでいる。
　本発明［３］は、前記透明導電層は、金属酸化物を含有する、上記［１］または［２］に記載の透明導電性フィルムを含んでいる。
　本発明［４］は、前記金属酸化物がインジウムスズ複合酸化物であることを特徴とする、上記［３］に記載の透明導電性フィルムを含んでいる。
　本発明の透明導電性フィルムは、ガラス基材と、透明導電層とを順に備え、ガラス基材の厚みは、１５０μｍ以下である。そのため、可撓性に優れる。
　また、この透明導電性フィルムにおいて、透明導電層が結晶性である。そのため、表面抵抗値を低くできる。また、この透明導電性フィルムにおいて、透明導電層の残留応力が、－１００ＭＰａ以上１００ＭＰａ以下である。そのため、カールを抑制できる。
図１は、本発明の透明導電性フィルムの一実施形態の断面図を示す。
　図１を参照して、本発明の透明導電性フィルムの一実施形態を説明する。
　図１において、紙面上下方向は、上下方向（厚み方向）であって、紙面上側が、上側（厚み方向一方側）、紙面下側が、下側（厚み方向他方側）である。また、紙面左右方向および奥行き方向は、上下方向に直交する面方向である。具体的には、各図の方向矢印に準拠する。
　１．透明導電性フィルム
　透明導電性フィルム１は、所定の厚みを有するフィルム形状（シート形状を含む）を有し、厚み方向と直交する面方向に延び、平坦な上面および平坦な下面を有する。透明導電性フィルム１は、例えば、画像表示装置に備えられるタッチパネル用基材や電磁波シールドなどの一部品であり、つまり、画像表示装置ではない。すなわち、透明導電性フィルム１は、画像表示装置などを作製するための部品であり、ＯＬＥＤモジュールなどの画像表示素子を含まず、部品単独で流通し、産業上利用可能なデバイスである。
　具体的には、図１に示すように、透明導電性フィルム１は、ガラス基材２と、透明導電層３とをこの順に備える。透明導電性フィルム１は、より具体的には、ガラス基材２と、ガラス基材２の上面（厚み方向一方面）に配置される透明導電層３とを備える。
　透明導電性フィルム１の厚みは、例えば、２００μｍ以下、好ましくは、１５０μｍ以下であり、また、例えば、２０μｍ以上、好ましくは、３０μｍ以上である。
　２．ガラス基材
　ガラス基材２は、透明導電性フィルム１の機械強度を確保するための透明な基材である。すなわち、ガラス基材２は、透明導電層３を支持している。
　ガラス基材２は、フィルム形状を有する。ガラス基材２は、透明導電層３の下面に接触するように、透明導電層３の下面全面に、配置されている。
　ガラス基材２は、可撓性を有し、透明なガラスから形成されている。
　ガラスとしては、例えば、無アルカリガラス、ソーダガラス、ホウケイ酸ガラス、アルミノケイ酸ガラスなどが挙げられる。
　ガラス基材２の厚みは、１５０μｍ以下、好ましくは、１２０μｍ以下、より好ましくは、１００μｍ以下である。また、例えば、１０μｍ以上、好ましくは、５０μｍ以上である。ガラス基材２の厚みが上記上限以下であれば、可撓性に優れる。また、ガラス基材２の厚みが上記下限以上であれば、機械的強度に優れ、搬送時の破損を抑制することができる。
　ガラス基材２の厚みは、ダイヤルゲージ（ＰＥＡＣＯＣＫ社製、「ＤＧ－２０５」）を用いて測定することができる。
　ガラス基材２の全光線透過率（ＪＩＳ　Ｋ　７３７５－２００８）は、例えば、８０％以上、好ましくは、８５％以上である。
　３．透明導電層
　透明導電層３は、結晶質であり、優れた導電性を発現する透明な層である。
　透明導電層３は、フィルム形状を有する。透明導電層３は、ガラス基材２の上面全面に、ガラス基材２の上面に接触するように、配置されている。
　透明導電層３の材料としては、例えば、Iｎ、Ｓｎ、Ｚｎ、Ｇａ、Ｓｂ、Ｔｉ、Ｓｉ、Ｚｒ、Ｍｇ、Ａｌ、Ａｕ、Ａｇ、Ｃｕ、Ｐｄ、Ｗからなる群より選択される少なくとも１種の金属を含む金属酸化物が挙げられる。金属酸化物には、必要に応じて、さらに上記群に示された金属原子をドープしていてもよい。
　透明導電層３としては、具体的には、例えば、インジウムスズ複合酸化物（ＩＴＯ）などのインジウム含有酸化物、例えば、アンチモンスズ複合酸化物（ＡＴＯ）などのアンチモン含有酸化物などが挙げられ、好ましくは、インジウム含有酸化物、より好ましくは、ＩＴＯが挙げられる。
　透明導電層３の材料としてＩＴＯを用いる場合、酸化スズ（ＳｎＯ２）含有量は、酸化スズおよび酸化インジウム（Ｉｎ２Ｏ３）の合計量に対して、例えば、０．５質量％以上、好ましくは、３質量％以上であり、また、例えば、１５質量％以下、好ましくは、１３質量％以下である。酸化スズの含有量が上記下限以上であれば、ＩＴＯ層の耐久性をより一層良好にすることができる。酸化スズの含有量が上記上限以下であれば、ＩＴＯ層の結晶転化を容易にし、透明性や比抵抗の安定性を向上させることができる。
　本明細書中における「ＩＴＯ」とは、少なくともインジウム（Ｉｎ）とスズ（Ｓｎ）とを含む複合酸化物であればよく、これら以外の追加成分を含んでもよい。追加成分としては、例えば、Ｉｎ、Ｓｎ以外の金属元素が挙げられ、具体的には、Ｚｎ、Ｇａ、Ｓｂ、Ｔｉ、Ｓｉ、Ｚｒ、Ｍｇ、Ａｌ、Ａｕ、Ａｇ、Ｃｕ、Ｐｄ、Ｗ、Ｆｅ、Ｐｂ、Ｎｉ、Ｎｂ、Ｃｒ、Ｇａなどが挙げられる。
　透明導電層３は、結晶質である。
　透明導電層３が、結晶質であれば、後述する表面抵抗率を低くできる。
　透明導電層３の結晶質性は、例えば、透明導電性フィルム１を塩酸（２０℃、濃度５質量％）に１５分間浸漬し、続いて、水洗および乾燥した後、透明導電層３側の表面に対して１５ｍｍ程度の間の端子間抵抗を測定することにより判断できる。上記浸漬・水洗・乾燥後の透明導電性フィルム１において、１５ｍｍ間の端子間抵抗が１０ｋΩ以下である場合、透明導電層は結晶質であり、一方、上記抵抗が１０ｋΩを超過する場合、透明導電層３は非晶質である。
　透明導電層３の上面の表面抵抗率は、例えば、３０Ω／□以下、好ましくは、１０Ω／□以下であり、また、例えば、１Ω／□以上である。表面抵抗率は、ＪＩＳ　Ｋ７１９４に準拠して、４端子法により測定することができる。
　表面抵抗率が、上記上限以下であれば、この透明導電性フィルム１を大型のタッチパネルなどに好適に用いることができる。
　透明導電層３の残留応力は、－１００ＭＰａ以上、好ましくは、－５０ＭＰａ以上、より好ましくは、－３０ＭＰａ以上、さらに好ましくは、－１０ＭＰａ以上であり、また、１００ＭＰａ以下、好ましくは、６０ＭＰａ以下、より好ましくは、１０ＭＰａ以下、さらに好ましくは、－５ＭＰａ以下である。
　なお、負の残留応力は、圧縮方向の残留応力を意味し、正の残留応力は、伸長方向の残留応力を意味する。
　なお、残留応力は、後述する実施例で詳述するが、Ｘ線回折法によって求めることができる。
　具体的には、残留応力は、特開２０１７－１０６１２４号公報の残留応力の測定方法に準拠して求めることができる。
　また、残留応力は、詳しくは後述するが、後述する反応性ガス導入量、後述する成膜圧力、および、後述する基材温度を所定の範囲に調整することで、上記した範囲に調整される。
　透明導電層３の厚みは、例えば、１５ｎｍ以上、好ましくは、３０ｎｍ以上、より好ましくは、１００ｎｍ以上であり、また、例えば、３００ｎｍ以下、好ましくは、２５０ｎｍ以下、より好ましくは、１５０ｎｍ以下である。透明導電層３の厚みは、例えば、透過型電子顕微鏡を用いて、透明導電性フィルム１の断面を観察することにより測定することができる。
４．透明導電性フィルムの製造方法
　透明導電性フィルム１を製造するには、例えば、ロールトゥロール工程において、ガラス基材２の上面に、透明導電層３を設ける。具体的には、長尺なガラス基材２を送出ロールから送出して搬送方向下流側に搬送しながら、ガラス基材２の上面に透明導電層３を設け、巻取ロールにて導電性フィルム１を巻き取る。以下、詳述する。
　まず、送出ロールに巻回された長尺なガラス基材２を用意し、巻取ロールに巻回されるようにガラス基材２を搬送する。
　搬送速度は、例えば、０．１ｍ／分以上、好ましくは、０．２ｍ／分以上であり、また、例えば、１．０ｍ／分以下、好ましくは、０．５ｍ／分以下である。
　その後、必要に応じて、ガラス基材２と透明導電層３との密着性の観点から、ガラス基材２の表面に、例えば、スパッタリング、コロナ放電、火炎、紫外線照射、電子線照射、化成、酸化などのエッチング処理や下塗り処理を実施することができる。また、溶剤洗浄、超音波洗浄などによりガラス基材２を除塵、清浄化することができる。
　次いで、ガラス基材２の上面に透明導電層３を設ける。例えば、乾式方法により、ガラス基材２の上面に透明導電層３を形成する。
　乾式方法としては、例えば、真空蒸着法、スパッタリング法、イオンプレーティング法などが挙げられる。好ましくは、スパッタリング法が挙げられる。この方法により、薄膜であり、かつ、厚みが均一である透明導電層３を形成することができる。
　スパッタリング法は、真空チャンバー内にターゲットおよび被着体（ガラス基材２）を対向配置し、ガスを供給するとともに電源から電圧を印加することによりガスイオンを加速しターゲットに照射させて、ターゲット表面からターゲット材料をはじき出して、そのターゲット材料を被着体表面に積層させる。
　スパッタリング法としては、例えば、２極スパッタリング法、ＥＣＲ（電子サイクロトロン共鳴）スパッタリング法、マグネトロンスパッタリング法、イオンビームスパッタリング法などが挙げられる。好ましくは、マグネトロンスパッタリング法が挙げられる。
　スパッタリング法を採用する場合、ターゲット材料としては、透明導電層３を構成する上述の金属酸化物などが挙げられ、好ましくは、ＩＴＯが挙げられる。ＩＴＯの酸化スズ濃度は、ＩＴＯ層の耐久性、結晶化などの観点から、例えば、０．５質量％以上、好ましくは、３質量％以上であり、また、例えば、１５質量％以下、好ましくは、１３質量％以下である。
　ガスとしては、例えば、Ａｒなどの不活性ガスが挙げられる。また、必要に応じて、酸素ガスなどの反応性ガスを併用することができる。
　不活性ガスに対する反応性ガスの導入割合（以下、反応性ガス導入量とする。）は、例えば、０．１体積％以上、好ましくは、１体積％以上であり、また、例えば、１０体積％以下、好ましくは、３体積％以下、より好ましくは、２．５体積％未満である。
　スパッタリング時の気圧（以下、成膜気圧とする。）は、例えば、１Ｐａ以下であり、好ましくは、０．５Ｐａ以下であり、また、例えば、０．１Ｐａ以上、好ましくは、０．２Ｐａ以上である。
　電源は、例えば、ＤＣ電源、ＡＣ電源、ＭＦ電源およびＲＦ電源のいずれであってもよく、また、これらの組み合わせであってもよい。
　そして、このスパッタリングでは、スパッタリング前に、ガラス基材２を予め高温に加熱する。これにより、ガラス基材２の表面において透明導電層３を形成する粒子は高いエネルギー状態に置かれ、スパッタリングによる成膜と同時に結晶化（アズデポ結晶化）できる。
　ガラス基材２の加熱温度（以下、基材温度とする。）は、例えば、３５０℃以上であり、また、例えば、６００℃以下、好ましくは、５５０℃以下である。
　ガラス基材２の加熱時間は、例えば、１０秒以上、好ましくは、２０秒以上であり、また、例えば、１２０秒以下、好ましくは、６０秒以下である。
　そして、上記した透明導電層３の残留応力を上記した所定の範囲に調整する観点から、好ましくは、上記した反応性ガス導入量、成膜圧力、および、基材温度を所定の範囲に調整する。
　具体的には、基材温度が３５０℃以上４５０℃未満である場合には、反応性ガス導入量が、例えば、１体積％以上３体積％以下であり、また、成膜圧力が、例えば、０．２Ｐａ以上０．５Ｐａ以下である。
　また、基材温度が４５０℃以上５５０℃以下である場合には、反応性ガス導入量が、例えば、１．５体積％以上２．５体積％未満であり、また、成膜圧力が、例えば、０．１Ｐａ以上０．５Ｐａ以下である。または、基材温度が４５０℃以上５５０℃以下である場合には、反応性ガス導入量が、例えば、２．５体積％以上３．５体積％以下であり、また、成膜圧力が、例えば、０．１Ｐａ以上０．２Ｐａ以下である。
　これにより、上記した透明導電層３の残留応力を上記した所定の範囲に調整することができる。
　そして、透明導電層３の加熱後に、透明導電層３を冷却する。
　これにより、ガラス基材２の上面に透明導電層３を形成され、ガラス基材２と、透明導電層３とを順に備える透明導電性フィルム１が得られる。
　得られる透明導電性フィルム１の厚みは、例えば、２μｍ以上、好ましくは、２０μｍ以上であり、また、例えば、１００μｍ以下、好ましくは、５０μｍ以下である。
５．作用効果
　透明導電性フィルム１は、ガラス基材２と、透明導電層３とを順に備え、ガラス基材２の厚みは、１５０μｍ以下である。そのため、可撓性に優れる。
　また、透明導電性フィルム１において、透明導電層３が結晶性である。そのため、表面抵抗値を低くできる。
　また、透明導電性フィルム１において、透明導電層３の残留応力が、－１００ＭＰａ以上１００ＭＰａ以下である。
　この透明導電性フィルム１では、透明導電層３を十分に結晶化させるために、基材温度を高温にする。
　しかし、基材温度を高温とすると、ガラス基材２と、透明導電層３との線膨張係数の差によって、透明導電層３がカールする場合がある。
　しかし、この透明導電性フィルム１では、透明導電層３の残留応力が、－１００ＭＰａ以上１００ＭＰａ以下に調整されているため、カールを抑制できる。
６．変形例
　上記した説明では、透明導電性フィルム１は、ガラス基材２と、透明導電層３とからなるが、ガラス基材２と透明導電層３と間に中間層を介在させることもできる。
　中間層としては、ハードコート層が挙げられる。
　ハードコート層は、透明導電性フィルム１を製造する際に、ガラス基材２に傷が発生することを抑制するための保護層である。また、ハードコート層は、透明導電性フィルム１を積層した場合に、透明導電層３に擦り傷が発生することを抑制するための耐擦傷層である。
　ハードコート層は、例えば、ハードコート組成物から形成される。
　ハードコート組成物は、樹脂成分を含有する。
　樹脂成分としては、例えば、硬化性樹脂、熱可塑性樹脂（例えば、ポリオレフィン樹脂）などが挙げられる。
　また、ハードコート組成物は、粒子を含有することもできる。
　粒子としては、架橋アクリル系粒子などの有機粒子、シリカ粒子などの無機粒子などが挙げられる。
　ハードコート層の厚みは、耐擦傷性の観点から、例えば、０．１μｍ以上、好ましくは、０．５μｍ以上であり、また、例えば、１０μｍ以下、好ましくは、３μｍ以下である。ハードコート層の厚みは、例えば、瞬間マルチ測光システム（例えば、大塚電子社製、「ＭＣＰＤ２０００」）を用いて観測される干渉スペクトルの波長に基づいて算出することができる。
　また、中間層としては、光学調整層が挙げられる。
　光学調整層は、透明導電層３のパターン視認を抑制したり、透明導電性フィルム１内の界面での反射を抑制しつつ、透明導電性フィルム１に優れた透明性を確保するために、透明導電性フィルム１の光学物性（例えば、屈折率）を調整する層である。
　光学調整層は、例えば、光学調整組成物から形成される。
　光学調整組成物は、上記の樹脂成分および上記の粒子を含有する。
　光学調整層の厚みは、例えば、５ｎｍ以上、好ましくは、１０ｎｍ以上であり、また、例えば、２００ｎｍ以下、好ましくは、１００ｎｍ以下である。光学調整層の厚みは、例えば、瞬間マルチ測光システムを用いて観測される干渉スペクトルの波長に基づいて算出することができる。
　つまり、透明導電性フィルム１は、ガラス基材２と透明導電層３と間に、ハードコート層または光学調整層を介在させることもでき、また、透明導電性フィルム１は、ガラス基材２と透明導電層３と間に、ハードコート層および光学調整層を介在させることもできる。
　好ましくは、透明導電性フィルム１は、ガラス基材２と透明導電層３と間に、光学調整層を介在させ、より好ましくは、透明導電性フィルム１は、ガラス基材２と透明導電層３と間に、ハードコート層および光学調整層を介在させず、すなわち、透明導電性フィルム１は、ガラス基材２と、透明導電層３とからなる。
　詳しくは、透明導電性フィルム１では、基材として、ガラス基材２を用いるため、基材として、高分子フィルムを用いる場合と比べて、ガラス基材２と、透明導電層３との間に中間層（特に、ハードコート層）を介在させなくても、密着性および透過性に優れる。
　以下に実施例および比較例を示し、本発明をさらに具体的に説明する。なお、本発明は、何ら実施例および比較例に限定されない。また、以下の記載において用いられる配合割合（含有割合）、物性値、パラメータなどの具体的数値は、上記の「発明を実施するための形態」において記載されている、それらに対応する配合割合（含有割合）、物性値、パラメータなど該当記載の上限値（「以下」、「未満」として定義されている数値）または下限値（「以上」、「超過」として定義されている数値）に代替することができる。
１．透明導電性フィルムの製造
　　実施例１
　ガラス基材として、ロール状に巻回された長尺な透明ガラス基材(厚み５０μｍ、日本電気硝子社製、「Ｇ－Ｌｅａｆ」)を準備した。
　この透明ガラス基材を送出ロールにセットして、搬送速度０．２７ｍ／分にて送り出し、スパッタリング装置（ターゲット部）を通過させて、巻取ロールに巻回した。ＤＣスパッタリング法により、厚みが１３０ｎｍであるＩＴＯ層（透明導電層）をガラス基材の上面に形成した。スパッタリングは、アルゴンガス９８％および酸素ガス２％（すなわち、酸素ガス導入量２体積％）を導入した気圧（成膜気圧）０．３Ｐａの真空雰囲気下で、実施した。放電出力は、３ｋＷとした。ターゲットは、８７．５質量％の酸化インジウムおよび１２．５質量％の酸化スズの焼結体を用いた。また、スパッタリング前に、スパッタリング装置内で、赤外線ヒータ（加熱部）を作動し、ヒーター温度（基材温度）を５００℃に設定し、ガラス基材を２５秒加熱した。
　これにより、ガラス基材とＩＴＯ層とを備え、ロール状に巻回された透明導電性フィルムを製造した。
　　実施例２～実施例４および比較例１～比較例４
　表１に従って、基材温度、成膜気圧および酸素ガス導入量を変更した以外は、実施例１と同様にして、透明導電性フィルムを製造した。
２．評価
１）表面抵抗率
　各実施例および各比較例のＩＴＯ層の表面抵抗率を、ＪＩＳ　Ｋ７１９４に準拠して、４端子法により測定した。その結果を表１に示す。
２）残留応力
　各実施例および各比較例のＩＴＯ層の残留応力を、Ｘ線散乱法により、ＩＴＯ膜の結晶格子歪みから間接的に求めた。
　具体的には、まず、株式会社リガク製の粉末Ｘ線回折装置により、測定散乱角２θ＝５９～６２°の範囲で０．０４°おきに回折強度を測定した。各測定角度における積算時間（露光時間）は１００秒とした。
　そして、得られた回折像のピーク（ＩＴＯの（６２２）面のピーク）角２θ、およびＸ線源の波長λから、ＩＴＯ膜の結晶格子間隔ｄを算出し、ｄを基に格子歪みεを算出した。算出にあたっては下記式（１）および下記式（２）を用いた。
　ここで、λはＸ線源（Ｃｕ　Ｋα線）の波長（＝０．１５４１８ｎｍ）であり、ｄ０は無応力状態のＩＴＯの格子面間隔（＝０．１５２４１ｎｍ）である。なお、ｄ０はＩＣＤＤ（Ｔｈｅ　Ｉｎｔｅｒｎａｔｉｏｎａｌ　Ｃｅｎｔｒｅ　ｆｏｒ　Ｄｉｆｆｒａｃｔｉｏｎ　Ｄａｔａ）データベースから取得した値である。
　上記のＸ線回折測定を、フィルム面法線とＩＴＯ結晶面法線とのなす角Ψが４５°、５０°、５５°、６０°、６５°、７０°、７７°、９０°のそれぞれについて実施し、それぞれのΨにおける格子歪みεを算出した。なお、フィルム面法線とＩＴＯ結晶面法線とのなす角Ψは、ＴＤ方向を回転軸中心として試料を回転することによって、調整した。ＩＴＯ膜面内方向の残留応力σは、ｓｉｎ２Ψと格子歪εとの関係をプロットした直線の傾きから下記式（３）により求めた。
　なお、上記式において、ＥはＩＴＯのヤング率（１１６ＧＰａ）、νはポアソン比（０．３５）である。これらの値は、Ｄ．Ｇ．　Ｎｅｅｒｉｎｃｋ　ａｎｄ　Ｔ．Ｊ．Ｖｉｎｋ、“Ｄｅｐｔｈ　ｐｒｏｆｉｌｉｎｇ　ｏｆ　ｔｈｉｎ　ＩＴＯ　ｆｉｌｍｓ　ｂｙ　ｇｒａｚｉｎｇ　ｉｎｃｉｄｅｎｃｅ　Ｘ－ｒａｙ　ｄｉｆｆｒａｃｔｉｏｎ”、Ｔｈｉｎ　Ｓｏｌｉｄ　Ｆｉｌｍｓ、２７８（１９９６）、ＰＰ１２－１７．に記載されている既知の実測値である。
　得られた残留応力を表１に示す。
３）カール量
　まず、透明導電性フィルムを幅１００ｍｍ×長さ１００ｍｍに切断し、切断した透明導電性フィルムを平滑な台に置いた。次いで、切断した透明導電性フィルムの各角の頂点が台から浮いている距離を測長し、４頂点の平均値を求め、カール量とした。その結果を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　なお、上記発明は、本発明の例示の実施形態として提供したが、これは単なる例示にすぎず、限定的に解釈してはならない。当該技術分野の当業者によって明らかな本発明の変形例は、後記請求の範囲に含まれるものである。
　本発明の透明導電性フィルムは、光学用途において好適に用いられる。
　１　　　透明導電性フィルム
　２　　　ガラス基材
　３　　　透明導電層

Claims (4)

  1. 　ガラス基材と、透明導電層とを順に備え、
    　前記ガラス基材の厚みは、１５０μｍ以下であり、
    　前記透明導電層が結晶性であり、
    　前記透明導電層の残留応力が、－１００ＭＰａ以上１００ＭＰａ以下であることを特徴とする、透明導電性フィルム。
  2. 　前記透明導電層の表面抵抗値が、１０Ω／□以下であることを特徴とする、請求項１に記載の透明導電性フィルム。
  3. 　前記透明導電層は、金属酸化物を含有することを特徴とする、請求項１に記載の透明導電性フィルム。
  4. 　前記金属酸化物がインジウムスズ複合酸化物であることを特徴とする、請求項３に記載の透明導電性フィルム
PCT/IB2020/000799 2019-06-21 2020-06-16 透明導電性フィルム WO2021001691A2 (ja)