WO2020210700A1 - Gaufrage mécanique sur revêtement sublimable organique pigmenté pour a la fois des panneaux plats et des extrusions - Google Patents

Gaufrage mécanique sur revêtement sublimable organique pigmenté pour a la fois des panneaux plats et des extrusions Download PDF

Info

Publication number
WO2020210700A1
WO2020210700A1 PCT/US2020/027766 US2020027766W WO2020210700A1 WO 2020210700 A1 WO2020210700 A1 WO 2020210700A1 US 2020027766 W US2020027766 W US 2020027766W WO 2020210700 A1 WO2020210700 A1 WO 2020210700A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
substrate
embossed
sublimation
pressing
Prior art date
Application number
PCT/US2020/027766
Other languages
English (en)
Inventor
Enrico PIVA
Cristian PANDOLFI
Original Assignee
Decoral System Usa Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Decoral System Usa Corporation filed Critical Decoral System Usa Corporation
Publication of WO2020210700A1 publication Critical patent/WO2020210700A1/fr

Abstract

La présente invention concerne un procédé de fabrication d'un substrat gaufré approprié pour la sublimation comprenant les étapes consistant à appliquer un traitement de revêtement sur un substrat ; revêtir le substrat traité ; chauffer le substrat revêtu pour durcir au moins partiellement le revêtement ; presser une plaque ayant des dépressions en relief sur le revêtement au moins partiellement durci pour former des dépressions dans le revêtement en poudre ; facultativement, chauffer le substrat, pendant ou après l'étape de pressage ; et retirer la plaque ayant des dépressions en relief pour produire un substrat gaufré.
PCT/US2020/027766 2019-04-12 2020-04-10 Gaufrage mécanique sur revêtement sublimable organique pigmenté pour a la fois des panneaux plats et des extrusions WO2020210700A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201962833279P 2019-04-12 2019-04-12
US62/833,279 2019-04-12

Publications (1)

Publication Number Publication Date
WO2020210700A1 true WO2020210700A1 (fr) 2020-10-15

Family

ID=72751674

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2020/027766 WO2020210700A1 (fr) 2019-04-12 2020-04-10 Gaufrage mécanique sur revêtement sublimable organique pigmenté pour a la fois des panneaux plats et des extrusions

Country Status (1)

Country Link
WO (1) WO2020210700A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022245723A1 (fr) 2021-05-17 2022-11-24 Greentech Composites Llc Articles polymères ayant des images imprimées par sublimation de colorant, et leur procédé de formation
WO2023038856A1 (fr) 2021-09-08 2023-03-16 Greentech Composites Llc Composite thermoplastique non polaire présentant une image imprimée par sublimation de colorant et procédé permettant de les former

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5015516A (en) * 1985-09-09 1991-05-14 Tarkett Inc. Decorative inlaid types of sheet materials
US5031525A (en) * 1989-12-22 1991-07-16 Armstrong World Industries, Inc. Embossing plate and method for using
US20010027839A1 (en) * 1998-04-15 2001-10-11 Italo Goffi Process for the production of variously painted and/or decorated artefacts by means of the technique of transfer from a sublimable colour support
US20080009412A1 (en) * 2004-04-06 2008-01-10 Dai Nippon Printing Co., Ltd. Receptor Layer Transfer Material, Transfer Sheet, and Coloring Material Receptor Sheet With Relief Layer, and Image Forming Method Using the Same
WO2018167000A1 (fr) * 2017-03-13 2018-09-20 Tiger Coatings Gmbh & Co. Kg Matériau de revêtement durcissable pour impression sans impact

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5015516A (en) * 1985-09-09 1991-05-14 Tarkett Inc. Decorative inlaid types of sheet materials
US5031525A (en) * 1989-12-22 1991-07-16 Armstrong World Industries, Inc. Embossing plate and method for using
US20010027839A1 (en) * 1998-04-15 2001-10-11 Italo Goffi Process for the production of variously painted and/or decorated artefacts by means of the technique of transfer from a sublimable colour support
US20080009412A1 (en) * 2004-04-06 2008-01-10 Dai Nippon Printing Co., Ltd. Receptor Layer Transfer Material, Transfer Sheet, and Coloring Material Receptor Sheet With Relief Layer, and Image Forming Method Using the Same
WO2018167000A1 (fr) * 2017-03-13 2018-09-20 Tiger Coatings Gmbh & Co. Kg Matériau de revêtement durcissable pour impression sans impact

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022245723A1 (fr) 2021-05-17 2022-11-24 Greentech Composites Llc Articles polymères ayant des images imprimées par sublimation de colorant, et leur procédé de formation
WO2023038856A1 (fr) 2021-09-08 2023-03-16 Greentech Composites Llc Composite thermoplastique non polaire présentant une image imprimée par sublimation de colorant et procédé permettant de les former

Similar Documents

Publication Publication Date Title
US11717850B2 (en) Method and apparatus for producing a decorative workpiece and workpiece
EP0921953B1 (fr) Procede permettant de decorer des profiles de metal, de matiere plastique et profiles similaires, et appareil associe
AU2016256168B2 (en) Method for producing structured surfaces and articles structured in such a way
CN105189138B (zh) 用于转移层压的方法和装置
WO2020210700A1 (fr) Gaufrage mécanique sur revêtement sublimable organique pigmenté pour a la fois des panneaux plats et des extrusions
WO2008152137A2 (fr) Revêtement décoratif pour substrats et procédé de décoration associé
JPH04241943A (ja) メンブレンプレス成形用ポリ塩化ビニルシートの製造方法
CN207362117U (zh) 一种高清彩色立体触感装饰彩板
EP1592567B1 (fr) Realisation d'images sur des surfaces
JPH0284327A (ja) 艶変化模様を有する金属化粧板の製造方法
JP3075057B2 (ja) 被加飾物のホットスタンピング印刷方法およびホットスタンピング印刷が施された被加飾物
CN209305218U (zh) 一种复合材料
JP2678835B2 (ja) 塩化ビニル化粧金属板とその製造方法
JP2797789B2 (ja) エンボス装飾化粧板の製造方法
JP2004202807A (ja) 転写シート及びその製造方法
JP2816194B2 (ja) 転写シートの製造法
EP4265434A1 (fr) Procédé et machine pour la décoration numérique d'un substrat
JPH0221306B2 (fr)
US20200178718A1 (en) Process for Producing Printed Solid Objects
JPH0699550A (ja) 化粧板の製造方法
JPH05270199A (ja) 化粧板の製造方法
JP2833390B2 (ja) 化粧板の製造方法
JPH02175198A (ja) 転写箔およびその製造方法
WO2021181419A1 (fr) Peinture de bordure de cuir et procédé associé
JPH0729516B2 (ja) 凹凸模様を有する金属化粧板の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20787222

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20787222

Country of ref document: EP

Kind code of ref document: A1