WO2020189431A1 - 化粧シート - Google Patents

化粧シート Download PDF

Info

Publication number
WO2020189431A1
WO2020189431A1 PCT/JP2020/010443 JP2020010443W WO2020189431A1 WO 2020189431 A1 WO2020189431 A1 WO 2020189431A1 JP 2020010443 W JP2020010443 W JP 2020010443W WO 2020189431 A1 WO2020189431 A1 WO 2020189431A1
Authority
WO
WIPO (PCT)
Prior art keywords
recycled
value
layer
decorative sheet
resin layer
Prior art date
Application number
PCT/JP2020/010443
Other languages
English (en)
French (fr)
Inventor
金子　純
Original Assignee
タキロンシーアイ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by タキロンシーアイ株式会社 filed Critical タキロンシーアイ株式会社
Priority to EP20773864.2A priority Critical patent/EP3939786B1/en
Publication of WO2020189431A1 publication Critical patent/WO2020189431A1/ja

Abstract

再生樹脂原料を用いても、明度が高く、色調のムラが少なく鮮明に絵柄層の絵柄を表現可能な化粧シートを提供する。再生ポリエステル系樹脂を含む透明再生樹脂層と、任意の絵柄が施された絵柄層と、再生ポリエステル系樹脂を含み、任意の色調に着色した着色再生樹脂層と、が順に重ねられてなる化粧シートであって、前記透明再生樹脂層は、曇り度であるヘーズ値が４％以下であり、かつ、ＣＩＥ　１９７６　Ｌａｂにおける測色台Ｌ＊：９９．１７、ａ＊：－０．０９、ｂ＊：０．５３をバックに測色したＬ＊値が９８．５以上、ｂ＊値が１．８以下であり、前記絵柄層は、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０以上９７．０未満、かつ、ｂ＊値が３．０以上であるか、または、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０未満であることを特徴とする。

Description

化粧シート
　本発明は、化粧シートに関する。
　本願は、２０１９年３月１５日に日本に出願された特願２０１９－０４８６３６号に基づき優先権を主張し、その内容をここに援用する。
　壁材、床材、建具（扉、戸等）、家具、シンク台、洗面化粧台等の表層に用いられる化粧シートとしては、かつてはポリ塩化ビニルシートが主流であった。近年、焼却時のダイオキシン発生の防止など環境問題への関心の高まりから、化粧シートとして塩素を含まないポリエチレン等のポリオレフィンを主体とするシートやポリエチレンテレフタレート（以下、「ＰＥＴ」とも記す。）等のポリエステルを主体とするシートが主流となっている。
　また、リサイクル促進の観点から、廃プラスチックからなる再生樹脂原料を用いた化粧シートの開発が強く要望されている。例えば、特許文献１には、再生ポリエステル樹脂とバージンポリエステル樹脂とを含む化粧シートが開示されている。
特開平１１－１３０８７７号公報
　再生樹脂原料、例えば廃ペットボトルのメカニカルリサイクル原料は、雑貨やラベル、容器、梱包資材、クリアファイルなど多種多様な用途に用いられている。しかしながら、廃ペットボトルはその性質上、紙、ガラス、着色剤、オレフィン樹脂などの異物混入が避けられない。加えて、再生を行う過程で熱履歴を受けることで変色するため、チップやペレットとして成型される段階で既に着色されている。このため、再生樹脂原料の製造ロッドどうしでも色調にバラつきがあり、再生樹脂原料を用いた化粧シートは、色や絵柄を鮮明に表現することが困難であるという課題があった。
　本発明は、前述した事情に鑑みてなされたものであって、任意の絵柄が施された絵柄層を有する化粧シートにおいて、再生樹脂原料を用いても、色調のムラが少なく鮮明に絵柄層の絵柄を表現可能な化粧シートを提供することを目的とする。
　本発明は、下記の態様を有する。
　＜１＞再生ポリエステル系樹脂を含む透明再生樹脂層と、任意の絵柄が施された絵柄層と、ポリエステル系樹脂を含み、任意の色調に着色した着色再生樹脂層と、が順に重ねられてなる化粧シートであって、前記透明再生樹脂層は、曇り度であるヘーズ値が４％以下であり、かつ、ＣＩＥ　１９７６　Ｌａｂにおける測色台Ｌ＊：９９．１７、ａ＊：－０．０９、ｂ＊：０．５３をバックに測色したＬ＊値が９８．５以上、ｂ＊値が１．８以下であり、前記絵柄層は、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０以上９７．０未満、かつ、ｂ＊値が３．０以上であるか、または、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０未満であることを特徴とする化粧シート。
＜２＞　前記透明再生樹脂層のＬ＊値と前記絵柄層のＬ＊値の差が２．０以上であることを特徴とする＜１＞に記載の化粧シート。
＜３＞前記透明再生樹脂層と前記絵柄層との間、または前記絵柄層と前記着色再生樹脂層との間に、接着層が形成されていることを特徴とする＜１＞または＜２＞に記載の化粧シート。
＜４＞前記再生ポリエステル系樹脂はペットボトルを原料に含むことを特徴とする＜１＞から＜３＞のいずれかに記載の化粧シート。
＜５＞前記透明再生樹脂層は、前記再生ポリエステル系樹脂を５０質量％以上９５質量％以下の範囲で含むことを特徴とする＜１＞から＜４＞のいずれかに記載の化粧シート。
＜６＞前記化粧シート全体に含まれる前記再生ポリエステル系樹脂が５０質量％以上であることを特徴とする＜１＞から＜５＞のいずれかに記載の化粧シート。
　本発明によれば、任意の絵柄が施された絵柄層を有する化粧シートにおいて、再生樹脂原料を用いても、色調のムラが少なく鮮明に絵柄層の絵柄を表現可能な化粧シートを提供することができる。
本発明の一実施形態の化粧シートの層構成を示す断面図である。 本発明の他の実施形態の化粧シートの層構成を示す断面図である。
　以下の用語の定義は、本明細書及び特許請求の範囲にわたって適用される。
　「Ｌ＊」は、ＪＩＳ　Ｚ　８７８１－４：２０１３「測色－第４部：ＣＩＥ　１９７６
　Ｌ＊ａ＊ｂ＊色空間」（対応国際規格ＩＳＯ　１１６６４－４：２００８）に定義される明度の相関量である。
　「ａ＊」および「ｂ＊」は、ＪＩＳ　Ｚ　８７８１－４：２０１３「測色－第４部：ＣＩＥ　１９７６　Ｌ＊ａ＊ｂ＊色空間」（対応国際規格ＩＳＯ　１１６６４－４：２００８）に定義される色座標である。
　数値範囲を示す「～」は、その前後に記載された数値を下限値及び上限値として含むことを意味する。
　以下、本発明の一実施形態の化粧シートについて説明する。なお、以下に示す実施形態は、発明の趣旨をより良く理解させるために具体的に説明するものであり、特に指定のない限り、本発明を限定するものではない。
　図１は、本発明の一実施形態の化粧シートの層構成を示す断面図である。
　本実施形態の化粧シート１０は、再生ＰＥＴ系樹脂を含む透明再生樹脂層１１と、任意の絵柄が施された絵柄層１２と、再生ＰＥＴ系樹脂を含み、任意の色調に着色した着色再生樹脂層１３とが順に重ねられて構成される。また、本実施形態では、絵柄層１２と着色再生樹脂層１３との間に、更に接着層１４が形成されている。なお、絵柄層１２を接着層として用いることもできる。
（透明再生樹脂層）
　透明再生樹脂層１１は、曇り度であるヘーズ値が４％以下である。ヘーズ値は、測定対象の樹脂層を透過する正透過光と拡散透過光の全光線の透過率をＴ１、測定対象の樹脂層を透過する正透過光をライトトラップで除去した拡散光の透過率をＴ２とした時に、Ｔ１／Ｔ２×１００で示される値であり、透明度の指標とされる。こうしたヘーズ値が４％以下である透明再生樹脂層１１から化粧シート１０を観察すると、下層である絵柄層１２に施された絵柄を曇りが無く鮮明に視認することができる。
　また、透明再生樹脂層１１は、ＣＩＥ　１９７６　Ｌａｂにおける測色台Ｌ＊：９９．１７、ａ＊：－０．０９、ｂ＊：０．５３をバックに測色したＬ＊値が９８．５以上、ｂ＊値が１．８以下である。これにより、透明再生樹脂層１１は着色が殆ど無く、下層である絵柄層１２に施された絵柄を色調が変化することなく鮮明に視認することができる。なお、透明再生樹脂層１１のＬ＊、ｂ＊は、ＪＩＳ　Ｋ　７３９０：２００３に記載の試験方法によって測定される。
　透明再生樹脂層１１は、厚みが例えば１２μｍ～１５０μｍとなるように形成され、より好ましくは２５μｍ～１２５μｍとなるように形成される。なお、透明再生樹脂層１１の表面には、更にプライマー層やハードコート層が形成されていても良い。
　透明再生樹脂層１１を構成する再生ポリエステル系樹脂は、ペットボトルを原料に含む再生樹脂であり、透明再生樹脂層１１は、再生ポリエステル系樹脂を５０質量％以上９５質量％以下、より好ましくは７０質量％以上８５質量％以下の範囲で含んでいる。なお、再生ポリエステル系樹脂を除いた残りの樹脂成分は、新たに製造したバージンポリエステル系樹脂であればよい。
　透明再生樹脂層１１に含まれる再生ポリエステル系樹脂が５０質量％未満の場合、バージンポリエステル系樹脂の割合が相対的に多くなり、環境対策として再生ポリエステル系樹脂を使用する意義が低下する。また、透明再生樹脂層１１に含まれる再生ポリエステル系樹脂が９５質量％を超える場合、透明度が低下する懸念がある。
　このように透明再生樹脂層１１で再生ポリエステル系樹脂の含有割合を高めることによって、環境対策として再生ポリエステル系樹脂の使用をより促進し、環境に配慮した化粧シート１０を実現できる。
　本実施形態の透明再生樹脂層１１や、後述する着色再生樹脂層１３に用いる再生ポリエステル系樹脂は、ＰＥＴボトルに由来する再生樹脂であり、特に、リサイクル回収プロセスが成熟している廃ＰＥＴボトルのメカニカルリサイクル原料を用いることが好ましい。
　再生ポリエステル系樹脂は、安価でかつ入手しやすい点から、ＰＥＴボトルの粉砕物が好ましい。再生ポリエステル系樹脂は、本発明の効果を損なわない範囲において、ＰＥＴボトルに付属していたラベル（印刷・接着剤等を含む）、キャップ等の粉砕物を含んでいてもよい。
　例えば、日本国においては、再利用品の品質低下を防ぐために、以下に説明する自主設計ガイドラインに、指定ＰＥＴボトルについては、ＰＥＴ単体（ＰＥＴ主材以外の物質を添加、複合等をして用いていない。）と定められ、着色はしない（口栓部の結晶化による白色は除く。）と定められている。したがって、現在、日本国内では着色ＰＥＴボトルは生産されておらず、海外で生産される日本国向けの着色ＰＥＴボトルについても無着色ＰＥＴボトルへの変更が要請されている（ｈｔｔｐ：／／ｗｗｗ．ｐｅｔｂｏｔｔｌｅ－ｒｅｃ．ｇｒ．ｊｐ／ｑａｎｄａ／ｓｅｃ１３．ｈｔｍｌ）。
　日本国内で流通するＰＥＴボトルについては、国の指導を受けてＰＥＴボトルリサイクル推進協議会によって制定された「指定ＰＥＴボトルの自主設計ガイドライン」に詳細が規定されている（ｈｔｔｐ：／／ｗｗｗ．ｐｅｔｂｏｔｔｌｅ－ｒｅｃ．ｇｒ．ｊｐ／ｇｕｉｄｅｌｉｎｅ／ｊｉｓｙｕ．ｈｔｍｌ）。
　こうした自主設計ガイドラインは、ＰＥＴボトルリサイクル推進協議会が、資源有効利用促進法規定の指定表示製品（清涼飲料、乳飲料、酒類、特定調味料）に使用されているＰＥＴボトル（指定ＰＥＴボトル）を、使用後の再処理、衛生性を含めた再利用適性に優れた容器とするために、使用するボトル、ラベル（印刷・接着剤等を含む）、キャップ等について規定したものである。
　ＰＥＴボトルリサイクル推進協議会の会員（団体、企業）が自主設計ガイドラインを遵守することは当然として、会員以外においても、指定ＰＥＴボトル入り飲料・酒類・特定調味料を製造・輸入・販売する場合、あるいは指定ＰＥＴボトルおよび附属包材を製造・輸入する場合は、日本国内で販売・使用されるものであれば、自主設計ガイドラインに適合することが必要とされている。
　したがって、国内で流通するＰＥＴボトルは、無着色のものがほとんどであり、また、ＰＥＴボトルに由来する再生ポリエステル系樹脂は、ほぼ透明である。
　なお、再生ポリエステル系樹脂は、ほぼ透明であるものの、熱成形加工時に受ける熱履歴や、ラベル等の混在によって、黄黒い（ＣＩＥ　１９７６　Ｌ＊ａ＊ｂ＊色空間におけるｂ＊値が高く、Ｌ＊値が低い）傾向にある。そのため、透明再生樹脂層１１に用いる再生ポリエステル系樹脂は、ｂ＊値が低く、Ｌ＊値が高いものを選別して用いることも好ましい。
　再生ポリエステル系樹脂は、結晶化温度が１４５℃以下のものが好ましく、１２０～１４５℃のものがより好ましく、１２５～１４０℃のものがさらに好ましい。
　なお、再生ポリエステル系樹脂の結晶化温度は、熱分析装置（示差走査熱量計（ＤＳＣ）等）を用いて測定される。
　再生ポリエステル系樹脂は、固有粘度（ＩＶ値）が例えば、０．６０以上のものが好ましく、０．６５～０．８５のものがより好ましく、０．７０～０．８３のものがさらに好ましい。再生ポリエステル系樹脂の固有粘度（ＩＶ値）が前記範囲の下限値未満では、粘度が低すぎて押出成形性に問題が生じるおそれがある。再生ポリエステル系樹脂の固有粘度（ＩＶ値）が前記範囲の上限値超では、粘度が高くて押出成形性に問題が生じるおそれがある。
　なお、再生ポリエステル系樹脂の固有粘度（ＩＶ値）は、ＪＩＳ　Ｋ　７３９０：２００３に記載の試験方法によって測定される。
　なお、透明再生樹脂層１１は、透明度を低下させない範囲で、他の成分として相溶化剤、紫外線吸収剤、光安定剤、酸化防止剤、帯電防止剤、保存安定剤、滑剤、充填材等を更に含んでいても良い。
（絵柄層）
　絵柄層１２は、任意の絵柄が形成された樹脂層であり、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０以上９７．０未満、かつ、ｂ＊値が３．０以上であるか、または、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０未満である。
　このように、絵柄層１２は任意の絵柄を表示することができる。　
　また、透明再生樹脂層１１のＬ＊値と絵柄層１２のＬ＊値の差を２．０以上に保つことが好ましい。これにより、透明再生樹脂層１１から化粧シート１０を見た時に、絵柄層１２の絵柄をより明瞭に視認することができる。
　絵柄層１２は、厚みが例えば０．１μｍ～１０μｍとなるように形成され、より好ましくは１μｍ～５μｍとなるように形成される。
　絵柄層１２において絵柄を構成するインクは、特に限定されないが、例えば、アクリル樹脂、塩化ビニル－酢酸ビニル共重合体を主成分とするバインダーからなる着色インキを用いることができる。
　なお、本実施形態では絵柄層１２は１層であるが、これ以外にも、絵柄層を２層以上、複数層形成することもできる。絵柄層を複数層形成することで、複雑で奥行き感のある絵柄を形成することが可能になる。
　また、絵柄層１２にヒートシールが可能な材料を含ませることにより、絵柄層１２と着色再生樹脂層１３とを接合する接着層１４を兼ねることもできる。
（着色再生樹脂層）
　着色再生樹脂層１３を構成する再生ポリエステル系樹脂は、透明再生樹脂層１１と同様にペットボトルを原料に含む再生樹脂であり、着色再生樹脂層１３は、再生ポリエステル系樹脂を１０質量％以上１００質量％以下、より好ましくは７０質量％以上９５質量％以下の範囲で含んでいる。なお、再生ポリエステル系樹脂を除いた残りの樹脂成分は、新たに製造したバージンポリエステル系樹脂であればよい。
　また、着色再生樹脂層１３は、１種以上の着色顔料を含むことが好ましい。例えば、白色の着色顔料としては、酸化チタン、酸化亜鉛、炭酸カルシウム、酸化マグネシウム、リトボン等が挙げられる。白色の着色顔料としては、隠蔽力が高い点から、酸化チタンが好ましい。酸化チタンとしては、ルチル型酸化チタン、アナターゼ型酸化チタン等が挙げられ、触媒としての活性が低い点から、ルチル型酸化チタンが好ましい。
　なお、絵柄層１２によって化粧シート１０を形成する下地基材（例えば木材）の色ブレを隠蔽できる場合には、着色再生樹脂層１３は着色顔料を含まなくてもよい。
　着色再生樹脂層１３は、厚みが例えば５０μｍ～３００μｍとなるように形成され、より好ましくは１００μｍ～２５０μｍとなるように形成される。
（接着層）
　接着層１４は、本実施形態では絵柄層１２と着色再生樹脂層１３とを接合する接着剤からなる層であり、例えば、ドライラミネート用の接着剤を用いることができる。ドライラミネート用の接着剤としては、例えば、ポリエステルポリオール／ポリシソシアネート系の２液混合硬化型接着剤が挙げられる。
　なお、図１に示すように絵柄層１２と着色再生樹脂層１３との間に接着層１４を形成する以外にも、図２に示すように、透明再生樹脂層１１と絵柄層１２との間に接着層１４を形成することもできる。また、接着層１４を絵柄層１２の一部として形成することもできる。
（化粧シート）
　化粧シート１０全体、即ち透明再生樹脂層１１と着色再生樹脂層１３に含まれる再生ポリエステル系樹脂は、５０質量％以上となるようにする。化粧シート１０全体に含まれる再生ポリエステル系樹脂が５０質量％未満の場合、バージンポリエステル系樹脂の割合が相対的に多くなり、環境対策として再生ポリエステル系樹脂を使用する意義が低下する。
　化粧シート１０全体で再生ポリエステル系樹脂の含有割合を高めることによって、環境対策として再生ポリエステル系樹脂の使用をより促進し、環境に配慮した化粧シート１０を実現できる。
　また、化粧シート１０全体は、厚みが例えば０．１５ｍｍ～０．４０ｍｍ、より好ましくは０．２０ｍｍ～０．３５ｍｍとなるように形成される。
　（作用機序）
　以上説明した本実施形態の化粧シート１０にあっては、透明再生樹脂層１１や着色再生樹脂層１３に再生ポリエステル系樹脂を含むことにより、ポリ塩化ビニルを含む化粧シートや、全樹脂成分中の再生樹脂の割合が低い化粧シートに比べ、親環境的である。
　そして、本実施形態の化粧シート１０にあっては、透明再生樹脂層１１のＣＩＥ　１９７６　Ｌａｂにおける測色台Ｌ＊：９９．１７、ａ＊：－０．０９、ｂ＊：０．５３をバックに測色したＬ＊値が９８．５以上、ｂ＊値が１．８以下にしている。これにより、透明再生樹脂層１１は着色が殆ど無く、下層である絵柄層１２に施された絵柄を色調が変化することなく鮮明に視認することができる。よって、外観上、高い明度が保たれ、色調のムラが少ない化粧シート１０を実現できる。
　また、本実施形態の化粧シート１０にあっては、絵柄層１２のＣＩＥ　１９７６　Ｌａｂにおける測色台Ｌ＊：９９．１７、ａ＊：－０．０９、ｂ＊：０．５３をバックに測色したＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０以上９７．０未満、かつ、ｂ＊値が３．０以上であるか、または、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０未満にしている。これにより、絵柄層１２は任意の絵柄が鮮明に表示された化粧シート１０を実現できる。
　本発明の化粧シートは、壁材、床材、建具（扉、戸等）、家具、シンク台、洗面化粧台等の表層に用いられ、好適には家具、シンク台、洗面化粧台等の扉の表層に用いられる。
　以上、本発明の実施形態を具体的に説明したが、これらの実施形態は、例として提示したものであり、発明の範囲を限定することは意図していない。これら実施形態は、その他の様々な形態で実施されることが可能であり、発明の要旨を逸脱しない範囲で、種々の省略、置き換え、変更を行うことができる。これら実施形態やその変形は、発明の範囲や要旨に含まれると同様に、特許請求の範囲に記載された発明とその均等の範囲に含まれるものである。
　以下、実施例を挙げて、本発明をより具体的に説明するが、本発明はこれら実施例に限定されるものではない。
　「透明樹脂層のヘーズ測定方法」
　ヘーズメーター（日本電色工業株式会社製：ＮＤＨ２０００）を用いてヘーズ値を測定した。
「透明樹脂層の測色方法」
　分光光度計（ＣＣＭ）（クラボウ社製、ＣＯＬＯＲ－７）を用い、光源Ｄ６５、視野角１０°、測色範囲φ２８ｍｍの条件にて、白バック架台に載せた化粧シートの３ヶ所を測定し、ＣＩＥ　１９７６　Ｌ＊ａ＊ｂ＊色空間におけるＬ＊、ａ＊、ｂ＊を求め、３箇所の平均値を用いた。白バック架台の色調はＬ＊：９９．１７、ａ＊：－０．０９、ｂ＊：０．５３である。
「絵柄の評価方法」
　透明再生樹脂層および着色再生樹脂層の再生原料率が０．０ｗｔ％である比較例７で採取したバージンポリエステル系樹脂のみを使用した化粧シートと比較して、目視により評価した。
「使用材料」
　（１）透明再生樹脂層
　　Ａ：東洋紡株式会社製　リシャイン（登録商標）０．０５ｍｍ厚の透明フィルムを使用した（再生ポリエステル系樹脂比率８０ｗｔ％）、ヘーズ値２．２０％、ｂ＊値１．１０、Ｌ＊値９８．７８
　　Ｂ：東洋紡株式会社製　リシャイン（登録商標）０．１２５ｍｍ厚の透明フィルムを使用した（再生ポリエステル系樹脂比率８０ｗｔ％）、ヘーズ値１．８１％、ｂ＊値１．７８、Ｌ＊値９８．５１
　　Ｃ：東洋紡株式会社製　リシャイン（登録商標）０．１８８ｍｍ厚の透明フィルムを使用した（再生ポリエステル系樹脂比率８０ｗｔ％）、ヘーズ値１．９４％、ｂ＊値１．９４、Ｌ＊値９８．３８
　　Ｄ：東洋紡株式会社製　リシャイン（登録商標）０．１２５ｍｍ厚の透明フィルムを使用した（再生ポリエステル系樹脂比率６０ｗｔ％）、ヘーズ値１．７０％、ｂ＊値１．６０、Ｌ＊値９８．６０
　　※なお、Ａ～Ｄは全て易接着処理済品を使用した。
　（２）着色再生樹脂層
　再生ポリエステル系樹脂（イタリア・ＡＬＩＰＬＡＳＴ社製、Ａｌｉｍｐｅｔ）にマスターバッチ（白色顔料およびバージンＡ－ＰＥＴ樹脂（華潤社製、ＣＲ８８１６）を含む。）を添加して再生ポリエステル系樹脂混合物を調製した。この再生ポリエステル系樹脂混合物について、長田製作所株式会社製の押出機（ＯＳＥ－３５φｍｍ押出機）を使用して、温度２６５℃、スクリュー回転数４４ｒｐｍで成形加工を行い、再生ポリエステル系樹脂を含む白色の着色再生樹脂層（幅３４０ｍｍ、厚さ０．１００ｍｍ、もしくは０．２００ｍｍ）を得た。また、着色再生樹脂層として、再生ポリエステル系樹脂比率が１５、５０、８５ｗｔ％のものを用意した。
　（３）接着層（接着剤）
　大日精化工業株式会社製　ドライラミネート用ポリエステルポリオール／ポリシソシアネート系２液硬化型（主剤：セイカボンド　Ｅ－２９５ＮＴ　１００重量部、硬化剤：セイカボンド　Ｃ－７５Ｎ－１．５　１０重量部、溶剤：酢酸エチル　ザーンカップ＃３で１９秒に希釈（固形分約３０％）を用いた。
　（４）絵柄層（絵柄印刷用インク）
　アクリル樹脂、塩化ビニル－酢酸ビニル共重合体を主成分とするバインダーからなる着色インキを用いた。
［実施例１］
　予め上記（２）の再生ポリエステル系樹脂比率が５０ｗｔ％、厚さ０．２００ｍｍのホワイト着色シート（着色再生樹脂層）に上記（４）の絵柄印刷用インクを用いて白系の抽象柄の印刷を施した。この印刷済シートと、上記（１）のＡを上記（３）の接着剤を用いて接合して積層し、実施例１の化粧シートを製作した。５箇所測色平均値（Ｌ＊９６．５１、ａ＊０．１８、ｂ＊５．５３）。また、接合はドライラミネートを用い、接着剤をコンマコーターを用いて、上記（１）のＡに１０ｇ／ｍ２塗工し、乾燥炉で接着剤の溶剤を揮発させた後、５０℃に加温されたニップロールで絵柄層を接着した。その後、３５℃で７２時間養生を行った。
［実施例２］
　透明再生樹脂層として、上記（１）のＢを用いた以外は実施例１と同様である。
［実施例３］
　上記（１）のＡの裏面に、上記（４）の絵柄印刷用インクを用いて白系の抽象柄の印刷を施した。これを再生樹脂含有率が５０ｗｔ％、厚さ０．２００ｍｍである上記（２）のホワイト着色シート（着色再生樹脂層）に上記（３）の接着剤を用いて接合して積層し、実施例３の化粧シートを製作した。なお、接合はドライラミネートを用い、接着剤をコンマコーターを用いて、裏面に印刷が施された上記（１）のＡに１０ｇ／ｍ２塗工し、乾燥炉で接着剤の溶剤を揮発させた後、５０℃に加温されたニップロールで着色再生樹脂層を接着した。その後、３５℃で７２時間養生を行った。
［実施例４］
　透明再生樹脂層として、上記（１）のＢを用いた以外は実施例３と同様である。
［実施例５］
　着色再生樹脂層として、再生樹脂含有率が８５ｗｔ％であり、厚さ０．２０ｍｍであるホワイト着色シートを用いて絵柄層を変更した以外は実施例４と同様である。
［実施例６］
　着色再生樹脂層として、再生樹脂含有率が１５ｗｔ％であり、厚さ０．１０ｍｍであるホワイト着色シートを用いた以外は実施例３と同様である。
［実施例７］
　透明再生樹脂層として、上記（１）のＤを用い、着色再生樹脂層として厚さ０．１０ｍｍであるホワイト着色シートを用いた以外は実施例３と同様である。
［比較例１］
　透明再生樹脂層として、上記（１）のＣを用いた以外は実施例１と同様である。
［比較例２］
　透明再生樹脂層として、上記（１）のＣを用いた以外は実施例３と同様である。
［比較例３］
　ヘーズ値の範囲を決めるために透明再生樹脂層として、０．０５ｍｍ厚のバージンポリエステル系を用いた２軸延伸ＰＥＴ（ユニチカ株式会社製　Ｓ５０）を使用して絵柄の評価を行った。それ以外の構成は実施例１と同様である。
　※ユニチカ株式会社製　Ｓ５０：０．０５ｍｍ厚の透明フィルム（再生ポリエステル系樹脂比率０ｗｔ％）、ヘーズ値４．８９％、ｂ＊値１．０２、Ｌ＊値９８．７７
［比較例４］
　ヘーズ値の範囲を決めるために透明再生樹脂層として、０．１０ｍｍ厚のバージンポリエステル系樹脂を用いた２軸延伸ＰＥＴ（ユニチカ株式会社製　ＳＡ１００）を使用して絵柄の評価を行った。それ以外の構成は実施例１と同様である。
　※ユニチカ株式会社製　ＳＡ１００：０．１０ｍｍ厚の透明フィルム（再生ポリエステル系樹脂比率０ｗｔ％）、ヘーズ値４．０１％、ｂ＊値１．２２、Ｌ＊値９８．７０
［比較例５］
　絵柄層として、印刷絵柄を実施例１より白度の高い絵柄（５箇所測色平均値：Ｌ＊９６．６６、ａ＊－０．６３、ｂ＊２．０５）とした。それ以外の構成は実施例１と同様である。
［比較例６］
　絵柄層として、印刷絵柄を実施例３より白度の高い絵柄（５箇所測色平均値：Ｌ＊９６．６６、ａ＊－０．６３、ｂ＊２．０５）とした。それ以外の構成は実施例３と同様である。
［比較例７］
　押し出し成形法により得たバージンＡ－ＰＥＴ樹脂（華潤社製、ＣＲ８８１６）を主原料とする着色樹脂層（０．２ｍｍ厚）に、上記（４）の絵柄印刷用インクを用いて白系の抽象柄の絵柄を施した。この絵柄層の形成済みの着色樹脂層と、東洋紡株式会社製の２軸延伸ポリエステルフィルム（コスモシャイン（登録商標）Ａ４１００）とを、上記（３）の接着剤を用いて接合し、比較例７の化粧シートを製作した。なお、接合はドライラミネートを用い、接着剤をコンマコーターを用いて、絵柄層の形成済みの着色再生樹脂層に１０ｇ／ｍ２塗工し、乾燥炉で接着剤の溶剤を揮発させた後、５０℃に加温されたニップロールで着色再生樹脂層を接着した。その後、３５℃で７２時間養生を行った。
　※東洋紡株式会社製　コスモシャイン（登録商標）Ａ４１００：０．０５０ｍｍ厚の透明フィルム（再生ポリエステル系樹脂比率０ｗｔ％）、ヘーズ値１．００％、ｂ＊値０．８８、Ｌ＊値９８．９４
　実施例１～７の試料の構成および評価結果を表１に、比較例１～７の試料の構成および評価結果を表２に、それぞれ示す。また、表２には、本発明に即した実際の設計品例（実設計）を併せて示す。表１、表２において、それぞれの実施例、比較例、参考例の評価は、（ａ）絵柄の鮮明さ、（ｂ）絵柄の色目、（ｃ）透明再生樹脂層のＬ＊値と絵柄層のＬ＊値の差、（ｄ）再生ポリエステル系樹脂重量率に関して、（ａ）鮮明、（ｂ）異状なし、（ｃ）２．００以上、（ｄ）５０ｗｔ％以上、を全て満たすものを可、それ以外のものを不可とした。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　実施例１～７の化粧シートは、いずれも絵柄が鮮明で、絵柄の色目のくすみや黄ばみなどの変色がなく、美観が比較例１～７よりも優れていた。また、再生ポリエステル系樹脂を多く含むことによって、ポリエステル系樹脂のリサイクル利用の面で優れており、環境に配慮した化粧シートが得られた。
　一方、比較例１～７の化粧シートは、絵柄の色目がくすんでいたり、黄ばみなどの変色が発生し、美観が実施例１～７よりも劣っていた。また、比較例３、４は、再生ポリエステル系樹脂の含有割合が低く、ポリエステル系樹脂のリサイクル利用の面でも実施例１～５よりも劣っていた。
　本発明の化粧シートは、親環境的であり、かつ絵柄を鮮明に表現可能な化粧シートとして有用である。
　１０…化粧シート
　１１…透明再生樹脂層
　１２…絵柄層
　１３…着色再生樹脂層
　１４…接着層

Claims (6)

  1. 　再生ポリエステル系樹脂を含む透明再生樹脂層と、任意の絵柄が施された絵柄層と、再生ポリエステル系樹脂を含み、任意の色調に着色した着色再生樹脂層と、が順に重ねられてなる化粧シートであって、
    　前記透明再生樹脂層は、曇り度であるヘーズ値が４％以下であり、かつ、ＣＩＥ　１９７６　Ｌａｂにおける測色台Ｌ＊：９９．１７、ａ＊：－０．０９、ｂ＊：０．５３をバックに測色したＬ＊値が９８．５以上、ｂ＊値が１．８以下であり、
    　前記絵柄層は、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０以上９７．０未満、かつ、ｂ＊値が３．０以上であるか、または、ＣＩＥ　１９７６　ＬａｂにおけるＬ＊値が９５．０未満であることを特徴とする化粧シート。
  2. 　前記透明再生樹脂層のＬ＊値と前記絵柄層のＬ＊値の差が２．０以上であることを特徴とする請求項１に記載の化粧シート。
  3. 　前記透明再生樹脂層と前記絵柄層との間、または前記絵柄層と前記着色再生樹脂層との間に、接着層が形成されていることを特徴とする請求項１または２に記載の化粧シート。
  4. 　前記再生ポリエステル系樹脂はペットボトルを原料に含むことを特徴とする請求項１から３のいずれか一項に記載の化粧シート。
  5. 　前記透明再生樹脂層は、前記再生ポリエステル系樹脂を５０質量％以上９５質量％以下の範囲で含むことを特徴とする請求項１から４のいずれか一項に記載の化粧シート。
  6. 　前記化粧シート全体に含まれる前記再生ポリエステル系樹脂が５０質量％以上であることを特徴とする請求項１から５のいずれか一項に記載の化粧シート。
PCT/JP2020/010443 2019-03-15 2020-03-11 化粧シート WO2020189431A1 (ja)