WO2019069802A1 - Résine de polyuréthanne, article moulé, et procédé de production d'une résine de polyuréthanne - Google Patents

Résine de polyuréthanne, article moulé, et procédé de production d'une résine de polyuréthanne Download PDF

Info

Publication number
WO2019069802A1
WO2019069802A1 PCT/JP2018/036241 JP2018036241W WO2019069802A1 WO 2019069802 A1 WO2019069802 A1 WO 2019069802A1 JP 2018036241 W JP2018036241 W JP 2018036241W WO 2019069802 A1 WO2019069802 A1 WO 2019069802A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyol
less
polyurethane resin
molecular weight
mass
Prior art date
Application number
PCT/JP2018/036241
Other languages
English (en)
Japanese (ja)
Inventor
大輔 長谷川
浩明 田子
宏 金山
山崎　聡
Original Assignee
三井化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三井化学株式会社 filed Critical 三井化学株式会社
Priority to CN201880058242.2A priority Critical patent/CN111065666B/zh
Priority to KR1020207007191A priority patent/KR102351760B1/ko
Priority to JP2019546671A priority patent/JP6946447B2/ja
Publication of WO2019069802A1 publication Critical patent/WO2019069802A1/fr

Abstract

Dans un produit de réaction d'un constituant polyisocyanate contenant du bis(isocyanatométhyl)cyclohexane et un constituant polyol contenant un polyol à faible masse moléculaire ayant une masse moléculaire inférieure à 400 et un polyol contenant un groupe carbonyle ayant une masse moléculaire moyenne en nombre de 400 à 1200, la température de coagulation, mesurée par analyse calorimétrique différentielle, est supérieure ou égale à la température de coagulation T1 de la phase segment dur représentée par la formule, et inférieure ou égale à la température de coagulation T2 de la phase segment dur représentée par la formule. Température de coagulation T1 du segment dur (unité : °C) : 80 + 1,2 x concentration du segment dur (% en masse). Température de coagulation du segment dur T2 (unité : °C) : 115 + 1,2 x concentration du segment dur (% en masse).
PCT/JP2018/036241 2017-10-05 2018-09-28 Résine de polyuréthanne, article moulé, et procédé de production d'une résine de polyuréthanne WO2019069802A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201880058242.2A CN111065666B (zh) 2017-10-05 2018-09-28 聚氨酯树脂、成型品、及聚氨酯树脂的制造方法
KR1020207007191A KR102351760B1 (ko) 2017-10-05 2018-09-28 폴리유레테인 수지, 성형품, 및 폴리유레테인 수지의 제조 방법
JP2019546671A JP6946447B2 (ja) 2017-10-05 2018-09-28 ポリウレタン樹脂、成形品、および、ポリウレタン樹脂の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017194810 2017-10-05
JP2017-194810 2017-10-05

Publications (1)

Publication Number Publication Date
WO2019069802A1 true WO2019069802A1 (fr) 2019-04-11

Family

ID=65994602

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/036241 WO2019069802A1 (fr) 2017-10-05 2018-09-28 Résine de polyuréthanne, article moulé, et procédé de production d'une résine de polyuréthanne

Country Status (5)

Country Link
JP (1) JP6946447B2 (fr)
KR (1) KR102351760B1 (fr)
CN (1) CN111065666B (fr)
TW (1) TWI802596B (fr)
WO (1) WO2019069802A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2021065783A1 (fr) * 2019-09-30 2021-04-08
CN114502612A (zh) * 2019-09-30 2022-05-13 大日精化工业株式会社 热塑性聚氨酯及其制造方法、以及成型物
WO2022215650A1 (fr) 2021-04-09 2022-10-13 三井化学株式会社 Feuille de résine renforcée par des fibres
WO2023140229A1 (fr) * 2022-01-18 2023-07-27 三井化学株式会社 Composition de prépolymère, résine de polyuréthane, article moulé élastique et procédé de production de composition de prépolymère
WO2023153398A1 (fr) * 2022-02-09 2023-08-17 三井化学株式会社 Composition de prépolymère, résine de polyuréthane, article moulé élastique et procédé de production de composition de prépolymère
WO2023181514A1 (fr) * 2022-03-23 2023-09-28 三菱電機株式会社 Composition de résine antimicrobienne

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102287235B1 (ko) * 2019-10-30 2021-08-06 에스케이씨솔믹스 주식회사 가교도가 조절된 연마패드 및 이의 제조방법
CN113480709B (zh) * 2021-07-15 2022-02-22 盛鼎高新材料有限公司 聚氨酯树脂组合物及制备方法、成型体及用途

Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS4913231A (fr) * 1972-03-08 1974-02-05
JPS51106197A (fr) * 1975-03-14 1976-09-20 Bridgestone Tire Co Ltd
JPS58118815A (ja) * 1982-01-05 1983-07-15 Toyo Tire & Rubber Co Ltd 耐熱性の改良されたウレタンエラストマ−
JPH0459809A (ja) * 1990-06-29 1992-02-26 Dainippon Ink & Chem Inc 塩化ビニル樹脂組成物
JPH05331255A (ja) * 1992-06-02 1993-12-14 Sanko Chem Co Ltd 熱可塑性ポリウレタンの製造方法
JPH0649409A (ja) * 1992-08-04 1994-02-22 Mitsui Toatsu Chem Inc スプレー成形によるポリウレタン・ポリウレア・エラス トマー積層物の製造方法
JPH09504564A (ja) * 1993-11-06 1997-05-06 ビーエーエスエフ ラッケ ウント ファルベン アクチエンゲゼルシャフト 水性ラッカー及び自動車塗装における充填層を製造するためのその使用
JP2004506762A (ja) * 2000-08-11 2004-03-04 アクゾ　ノーベル　ナムローゼ　フェンノートシャップ 水性の架橋性バインダー組成物及びラッカーコーティングの製造にそれを使用する方法
WO2004067582A1 (fr) * 2003-01-28 2004-08-12 Akzo Nobel Coatings International B.V. Composition durcissable comprenant un compose possedant des groupes olefiniquement insatures et polymerisables par polymerisation radicalaire, une enzyme d'oxydoreduction et un groupe a fonction thiol
JP2010513596A (ja) * 2006-12-14 2010-04-30 インターフェース バイオロジクス，インコーポレーテッド 高い分解温度を有する表面改質用高分子及びその使用
WO2010098316A1 (fr) * 2009-02-26 2010-09-02 宇部興産株式会社 Dispersion aqueuse de résine polyuréthanne et son procédé de préparation
JP2010235805A (ja) * 2009-03-31 2010-10-21 Nhk Spring Co Ltd 独泡ウレタンシート及びその製造方法
JP2011012141A (ja) * 2009-06-30 2011-01-20 Mitsui Chemicals Inc 光学用ポリウレタン樹脂組成物、光学用ポリウレタン樹脂およびその製造方法
US20150051328A1 (en) * 2012-07-09 2015-02-19 Shanghai Huihai Chemical Technology Co., Ltd. Alkyl phosphinate polymer and methods for preparing and using the same
WO2016152545A1 (fr) * 2015-03-24 2016-09-29 富士フイルム株式会社 Préparation cosmétique pour ongles et kit de décoration d'ongles

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101111990B1 (ko) * 2002-10-31 2012-02-17 다우 글로벌 테크놀로지스 엘엘씨 폴리우레탄 분산액 및 이로부터 제조된 제품
US20040087754A1 (en) * 2002-10-31 2004-05-06 Paul Foley Polyurethane compounds and articles prepared therefrom
DE602008002592D1 (de) * 2007-05-21 2010-10-28 Lubrizol Advanced Mat Inc Harte, aliphatische thermoplastische Polyurethane
WO2009051104A1 (fr) * 2007-10-15 2009-04-23 Mitsui Chemicals Polyurethanes, Inc. Composition de résine de polyuréthane granulaire et article moulé de celle-ci
CN103641989B (zh) * 2007-10-15 2016-05-18 三井化学株式会社 聚氨酯树脂
JP5335559B2 (ja) * 2009-05-29 2013-11-06 三井化学株式会社 硬化性ポリウレタン樹脂組成物および硬化物
JP2011213867A (ja) * 2010-03-31 2011-10-27 Mitsui Chemicals Inc 熱可塑性ポリウレタン樹脂、成形品、および、熱可塑性ポリウレタン樹脂の製造方法
SG10201702552YA (en) * 2012-06-05 2017-05-30 Mitsubishi Chem Corp Polyester and polyurethane production method
JP6068265B2 (ja) 2013-05-30 2017-01-25 三井化学株式会社 ポリウレタンエラストマー
JP5997665B2 (ja) * 2013-06-19 2016-09-28 三井化学株式会社 熱硬化性ポリウレタンウレア樹脂組成物および成形品
EP3168256B1 (fr) 2013-09-26 2019-08-07 Mitsui Chemicals, Inc. Matériau de lunettes comprenant une resine de polyurethane, monture de lunettes et lentille

Patent Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS4913231A (fr) * 1972-03-08 1974-02-05
JPS51106197A (fr) * 1975-03-14 1976-09-20 Bridgestone Tire Co Ltd
JPS58118815A (ja) * 1982-01-05 1983-07-15 Toyo Tire & Rubber Co Ltd 耐熱性の改良されたウレタンエラストマ−
JPH0459809A (ja) * 1990-06-29 1992-02-26 Dainippon Ink & Chem Inc 塩化ビニル樹脂組成物
JPH05331255A (ja) * 1992-06-02 1993-12-14 Sanko Chem Co Ltd 熱可塑性ポリウレタンの製造方法
JPH0649409A (ja) * 1992-08-04 1994-02-22 Mitsui Toatsu Chem Inc スプレー成形によるポリウレタン・ポリウレア・エラス トマー積層物の製造方法
JPH09504564A (ja) * 1993-11-06 1997-05-06 ビーエーエスエフ ラッケ ウント ファルベン アクチエンゲゼルシャフト 水性ラッカー及び自動車塗装における充填層を製造するためのその使用
JP2004506762A (ja) * 2000-08-11 2004-03-04 アクゾ　ノーベル　ナムローゼ　フェンノートシャップ 水性の架橋性バインダー組成物及びラッカーコーティングの製造にそれを使用する方法
WO2004067582A1 (fr) * 2003-01-28 2004-08-12 Akzo Nobel Coatings International B.V. Composition durcissable comprenant un compose possedant des groupes olefiniquement insatures et polymerisables par polymerisation radicalaire, une enzyme d'oxydoreduction et un groupe a fonction thiol
JP2010513596A (ja) * 2006-12-14 2010-04-30 インターフェース バイオロジクス，インコーポレーテッド 高い分解温度を有する表面改質用高分子及びその使用
WO2010098316A1 (fr) * 2009-02-26 2010-09-02 宇部興産株式会社 Dispersion aqueuse de résine polyuréthanne et son procédé de préparation
JP2010235805A (ja) * 2009-03-31 2010-10-21 Nhk Spring Co Ltd 独泡ウレタンシート及びその製造方法
JP2011012141A (ja) * 2009-06-30 2011-01-20 Mitsui Chemicals Inc 光学用ポリウレタン樹脂組成物、光学用ポリウレタン樹脂およびその製造方法
US20150051328A1 (en) * 2012-07-09 2015-02-19 Shanghai Huihai Chemical Technology Co., Ltd. Alkyl phosphinate polymer and methods for preparing and using the same
WO2016152545A1 (fr) * 2015-03-24 2016-09-29 富士フイルム株式会社 Préparation cosmétique pour ongles et kit de décoration d'ongles

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2021065783A1 (fr) * 2019-09-30 2021-04-08
WO2021065783A1 (fr) * 2019-09-30 2021-04-08 三井化学株式会社 Résine de polyuréthane thermoplastique et film
CN114375312A (zh) * 2019-09-30 2022-04-19 三井化学株式会社 热塑性聚氨酯树脂及膜
CN114502612A (zh) * 2019-09-30 2022-05-13 大日精化工业株式会社 热塑性聚氨酯及其制造方法、以及成型物
JP7257541B2 (ja) 2019-09-30 2023-04-13 三井化学株式会社 熱可塑性ポリウレタン樹脂およびフィルム
CN114375312B (zh) * 2019-09-30 2024-04-09 三井化学株式会社 热塑性聚氨酯树脂及膜
WO2022215650A1 (fr) 2021-04-09 2022-10-13 三井化学株式会社 Feuille de résine renforcée par des fibres
WO2023140229A1 (fr) * 2022-01-18 2023-07-27 三井化学株式会社 Composition de prépolymère, résine de polyuréthane, article moulé élastique et procédé de production de composition de prépolymère
WO2023153398A1 (fr) * 2022-02-09 2023-08-17 三井化学株式会社 Composition de prépolymère, résine de polyuréthane, article moulé élastique et procédé de production de composition de prépolymère
WO2023181514A1 (fr) * 2022-03-23 2023-09-28 三菱電機株式会社 Composition de résine antimicrobienne

Also Published As

Publication number Publication date
KR20200041348A (ko) 2020-04-21
CN111065666A (zh) 2020-04-24
KR102351760B1 (ko) 2022-01-14
TWI802596B (zh) 2023-05-21
JP6946447B2 (ja) 2021-10-06
TW201922834A (zh) 2019-06-16
CN111065666B (zh) 2022-04-22
JPWO2019069802A1 (ja) 2020-10-15

Similar Documents

Publication Publication Date Title
JP6946447B2 (ja) ポリウレタン樹脂、成形品、および、ポリウレタン樹脂の製造方法
KR102205059B1 (ko) 폴리유레테인 수지의 제조 방법, 폴리유레테인 수지 및 성형품
EP3805287B1 (fr) Résine de polyuréthane thermoplastique, résine de polyuréthane optique, plaque de couverture pour panneau d'affichage, matériau de lunettes, verre de lunettes, monture de lunettes, composants intérieurs et extérieurs d'automobile, et procédé de production de résine de polyuréthane thermoplastique
TWI778062B (zh) 聚胺基甲酸酯樹脂、聚胺基甲酸酯樹脂之製造方法及成形品
JP7257541B2 (ja) 熱可塑性ポリウレタン樹脂およびフィルム
JP7280954B2 (ja) ポリウレタン樹脂組成物および成形品
JP7296249B2 (ja) 熱可塑性ポリウレタン樹脂
JP7246910B2 (ja) 熱可塑性ポリウレタン樹脂、成形品、および、熱可塑性ポリウレタン樹脂の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18863990

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019546671

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20207007191

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18863990

Country of ref document: EP

Kind code of ref document: A1