WO2017145903A1 - 光吸収部材および水素製造用部材ならびに水素製造装置 - Google Patents
光吸収部材および水素製造用部材ならびに水素製造装置 Download PDFInfo
- Publication number
- WO2017145903A1 WO2017145903A1 PCT/JP2017/005626 JP2017005626W WO2017145903A1 WO 2017145903 A1 WO2017145903 A1 WO 2017145903A1 JP 2017005626 W JP2017005626 W JP 2017005626W WO 2017145903 A1 WO2017145903 A1 WO 2017145903A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ceramic
- hydrogen production
- hydrogen
- porous composite
- absorbing member
- Prior art date
Abstract
Description
光吸収部材の方の組成は、ペロブスカイト材料の粉末が50体積%、ガラス粉末が50体積%の割合となるようにした。
1・・・・・・・・・・・・・第1セラミックス
3・・・・・・・・・・・・・第1セラミック粒子
5・・・・・・・・・・・・・セラミック複合体
B1~B8・・・・・・・・・水素製造用部材
10A・・・・・・・・・・・光吸収部
10B・・・・・・・・・・・水素生成部
11・・・・・・・・・・・・第2セラミック粒子
13・・・・・・・・・・・・第2セラミックス
15・・・・・・・・・・・・セラミック多孔質複合体
16・・・・・・・・・・・・開気孔
19・・・・・・・・・・・・金属膜
C1、C2・・・・・・・・・水素製造装置
21・・・・・・・・・・・・反応部
23・・・・・・・・・・・・水蒸気供給部
25・・・・・・・・・・・・回収部
27・・・・・・・・・・・・水蒸気回収部
29・・・・・・・・・・・・遮蔽板
31・・・・・・・・・・・・遮蔽層
33・・・・・・・・・・・・水素分離モジュール
35a、35b・・・・・・・ポンプ
37・・・・・・・・・・・・容器
39・・・・・・・・・・・・集光板
Claims (17)
- 開気孔率が5%以下の第1セラミックス中に、正の抵抗温度特性を示す第1セラミック粒子を複数有するセラミック複合体によって構成されている、光吸収部材。
- 前記第1セラミック粒子がABO3として表されるペロブスカイト型の複合酸化物である、請求項1に記載の光吸収部材。
- 前記第1セラミック粒子は、前記ABO3のAサイトの元素としてLaを含み、Bサイトの元素としてMnを含むものである、請求項2に記載の光吸収部材。
- 前記第1セラミックスの色の明度が、マンセルカラーシステムで区別される明度表示で5以上である、請求項1乃至3のうちいずれかに記載の光吸収部材。
- 多孔質の第2セラミックス中に、第2セラミック粒子を含むセラミック多孔質複合体によって構成されている水素生成部と、光吸収部とで構成されている水素製造用部材であって、前記光吸収部が請求項1乃至4のうちいずれかに記載の光吸収部材によって構成されている、水素製造用部材。
- 前記第1セラミック粒子および前記第2セラミック粒子は、平均粒径が5~200nmである、請求項5に記載の水素製造用部材。
- 前記第2セラミック粒子が、AXO3±δ(但し、0≦δ≦1、A:希土類元素、アルカリ土類元素、およびアルカリ金属元素のうちの少なくとも一種、X:遷移金属元素およびメタロイド元素のうちの少なくとも一種、O:酸素)、酸化セリウムおよび酸化ジルコニウムのうちのいずれかである、請求項5または6に記載の水素製造用部材。
- 前記セラミック多孔質複合体中における前記第2セラミック粒子の割合が20~80体積%である、請求項5乃至7のうちいずれかに記載の水素製造用部材。
- 前記第2セラミック粒子のうち、個数比で90%以上が孤立して存在している、請求項5乃至8のうちいずれかに記載の水素製造用部材。
- 前記光吸収部材および前記セラミック多孔質複合体がともに筒状を成しており、前記光吸収部材の内側に前記セラミック多孔質複合体が配置されている、請求項5乃至9のうちいずれかに記載の水素製造用部材。
- 前記セラミック多孔質複合体が円柱体または角柱体であり、前記光吸収部材が前記セラミック多孔質複合体の側面を取り巻くように設けられていることを特徴とする請求項5乃至9のうちいずれかに記載の水素製造用部材。
- 前記光吸収部材および前記セラミック多孔質複合体がともに平板型であり、前記光吸収部材が前記セラミック多孔質複合体を上下から挟んだ積層構造体である、請求項5乃至9のうちいずれかに記載の水素製造用部材。
- 前記光吸収部材と前記セラミック多孔質複合体との間に遮蔽層が設けられている、請求項10または11に記載の水素製造用部材。
- 前記遮蔽層は、金属材料、セラミック材料およびガラス材料の群のうちのいずれかである、請求項13に記載の水素製造用部材。
- 太陽光エネルギーを受けて酸化・還元反応を起こす反応部と、該反応部に水を供給する水蒸気供給部と、前記反応部から発生する水素ガスを回収する回収部とを備えている水素製造装置であって、前記反応部に請求項5乃至14のうちいずれかに記載の水素製造用部材が設置されている、水素製造装置。
- 前記反応部と前記回収部との間に水素分離モジュールが設置されている、請求項15に記載の水素製造装置。
- 前記反応部が減圧可能な容器内に収容されている、請求項15または16に記載の水素製造装置。