WO2017122251A1 - Batterie secondaire à électrolyte non aqueux - Google Patents

Batterie secondaire à électrolyte non aqueux Download PDF

Info

Publication number
WO2017122251A1
WO2017122251A1 PCT/JP2016/005175 JP2016005175W WO2017122251A1 WO 2017122251 A1 WO2017122251 A1 WO 2017122251A1 JP 2016005175 W JP2016005175 W JP 2016005175W WO 2017122251 A1 WO2017122251 A1 WO 2017122251A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
current collector
positive electrode
active material
electrode plate
Prior art date
Application number
PCT/JP2016/005175
Other languages
English (en)
Japanese (ja)
Inventor
広太 小川
孝一 草河
長谷川　和弘
Original Assignee
三洋電機株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三洋電機株式会社 filed Critical 三洋電機株式会社
Publication of WO2017122251A1 publication Critical patent/WO2017122251A1/fr

Abstract

Une batterie secondaire à électrolyte non aqueux selon un mode de réalisation de la présente invention comprend : un corps d'électrode dans lequel une plaque d'électrode négative et une plaque d'électrode positive sont enroulées avec un séparateur intercalé entre celles-ci ; un électrolyte non aqueux ; un boîtier extérieur ; et un corps à ouverture scellée. Une partie de collecteur d'électrode négative exposée est disposée à chaque extrémité d'un côté de début d'enroulement et d'un côté de fin d'enroulement de la plaque d'électrode négative, et ne comporte pas de couche de substance active d'électrode négative formée dans celle-ci. Un conducteur d'électrode négative est connecté à la partie de collecteur d'électrode négative exposée sur le côté de début d'enroulement de la plaque d'électrode négative, et le conducteur d'électrode négative est connecté à une partie inférieure du boîtier extérieur. La partie de collecteur d'électrode négative exposée sur le côté de fin d'enroulement de la plaque d'électrode négative est en contact avec la surface de côté interne du boîtier extérieur. La couche de substance active d'électrode positive de la plaque d'électrode positive contient un oxyde de complexe de lithium-nickel.
PCT/JP2016/005175 2016-01-12 2016-12-19 Batterie secondaire à électrolyte non aqueux WO2017122251A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016003153 2016-01-12
JP2016-003153 2016-01-12

Publications (1)

Publication Number Publication Date
WO2017122251A1 true WO2017122251A1 (fr) 2017-07-20

Family

ID=59310929

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/005175 WO2017122251A1 (fr) 2016-01-12 2016-12-19 Batterie secondaire à électrolyte non aqueux

Country Status (1)

Country Link
WO (1) WO2017122251A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020084986A1 (fr) * 2018-10-26 2020-04-30 パナソニックＩｐマネジメント株式会社 Batterie secondaire cylindrique
CN111183542A (zh) * 2017-09-29 2020-05-19 松下电器产业株式会社 非水电解质二次电池
WO2021100282A1 (fr) * 2019-11-20 2021-05-27 日本碍子株式会社 Plaque de corps fritté de titanate de lithium
CN113039662A (zh) * 2018-12-19 2021-06-25 三洋电机株式会社 二次电池用的电极板和使用了该电极板的二次电池
WO2021153441A1 (fr) * 2020-01-31 2021-08-05 三洋電機株式会社 Batterie secondaire à électrolyte non aqueux
CN114365315A (zh) * 2019-10-07 2022-04-15 株式会社Lg新能源 电极组件及其制造方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001110453A (ja) * 1999-10-04 2001-04-20 Sony Corp 非水電解液二次電池
WO2012042830A1 (fr) * 2010-09-30 2012-04-05 パナソニック株式会社 Batterie secondaire à électrolyte non aqueux
WO2016147564A1 (fr) * 2015-03-13 2016-09-22 三洋電機株式会社 Batterie secondaire à électrolyte non aqueux

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001110453A (ja) * 1999-10-04 2001-04-20 Sony Corp 非水電解液二次電池
WO2012042830A1 (fr) * 2010-09-30 2012-04-05 パナソニック株式会社 Batterie secondaire à électrolyte non aqueux
WO2016147564A1 (fr) * 2015-03-13 2016-09-22 三洋電機株式会社 Batterie secondaire à électrolyte non aqueux

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111183542A (zh) * 2017-09-29 2020-05-19 松下电器产业株式会社 非水电解质二次电池
CN111183542B (zh) * 2017-09-29 2023-06-02 松下控股株式会社 非水电解质二次电池
WO2020084986A1 (fr) * 2018-10-26 2020-04-30 パナソニックＩｐマネジメント株式会社 Batterie secondaire cylindrique
JPWO2020084986A1 (ja) * 2018-10-26 2021-09-09 パナソニックＩｐマネジメント株式会社 円筒型二次電池
JP7320738B2 (ja) 2018-10-26 2023-08-04 パナソニックＩｐマネジメント株式会社 円筒型二次電池
CN113039662A (zh) * 2018-12-19 2021-06-25 三洋电机株式会社 二次电池用的电极板和使用了该电极板的二次电池
CN113039662B (zh) * 2018-12-19 2023-05-05 三洋电机株式会社 二次电池用的电极板和使用了该电极板的二次电池
CN114365315A (zh) * 2019-10-07 2022-04-15 株式会社Lg新能源 电极组件及其制造方法
WO2021100282A1 (fr) * 2019-11-20 2021-05-27 日本碍子株式会社 Plaque de corps fritté de titanate de lithium
JPWO2021100282A1 (fr) * 2019-11-20 2021-05-27
WO2021153441A1 (fr) * 2020-01-31 2021-08-05 三洋電機株式会社 Batterie secondaire à électrolyte non aqueux

Similar Documents

Publication Publication Date Title
WO2017122251A1 (fr) Batterie secondaire à électrolyte non aqueux
JP4743752B2 (ja) リチウムイオン二次電池
CN108352491B (zh) 非水电解质二次电池
JP6138436B2 (ja) 非水電解質二次電池及びその製造方法
JP6165425B2 (ja) 非水電解質二次電池及びその製造方法
WO2016013179A1 (fr) Batterie secondaire à électrolyte non aqueux
JP2014035929A (ja) 非水電解質二次電池
JP2014035923A (ja) 非水電解質二次電池
JP2014035922A (ja) 非水電解質二次電池
JP2016085838A (ja) リチウムイオン二次電池
JP2015082381A (ja) 非水電解質二次電池
US11456460B2 (en) Nonaqueous electrolyte secondary battery
JP5296971B2 (ja) 二次電池用負極の製造方法
JP2012174387A (ja) 電池用電極板およびそれを用いた電池
JP5782869B2 (ja) 非水電解質二次電池および非水電解質二次電池用集電体
JP5413945B2 (ja) 積層型ラミネート非水電解質二次電池
JP2001229970A (ja) 円筒形リチウムイオン電池
JP2014035924A (ja) 非水電解質二次電池
WO2017051516A1 (fr) Accumulateur à électrolyte non aqueux
JP2017016905A (ja) リチウム二次電池の充放電方法
JP6392566B2 (ja) 非水電解質二次電池
WO2020137818A1 (fr) Batterie secondaire à électrolytique non aqueux et son procédé de fabrication
JP5985272B2 (ja) 非水電解質二次電池
JP2016085884A (ja) 電池
JP2019153539A (ja) 非水電解質二次電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16884855

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16884855

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP