WO2016208353A1 - Procédé et appareil pour la fabrication d'un film structuré en surface - Google Patents

Procédé et appareil pour la fabrication d'un film structuré en surface Download PDF

Info

Publication number
WO2016208353A1
WO2016208353A1 PCT/JP2016/066460 JP2016066460W WO2016208353A1 WO 2016208353 A1 WO2016208353 A1 WO 2016208353A1 JP 2016066460 W JP2016066460 W JP 2016066460W WO 2016208353 A1 WO2016208353 A1 WO 2016208353A1
Authority
WO
WIPO (PCT)
Prior art keywords
mold
film
surface structure
roll
thermosetting material
Prior art date
Application number
PCT/JP2016/066460
Other languages
English (en)
Japanese (ja)
Inventor
冨永善章
箕浦潔
和田浩光
佐枝暁
Original Assignee
東レ株式会社
東レエンジニアリング株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東レ株式会社, 東レエンジニアリング株式会社 filed Critical 東レ株式会社
Priority to CN201680018786.7A priority Critical patent/CN107428072B/zh
Priority to KR1020177027496A priority patent/KR102454079B1/ko
Priority to JP2016540697A priority patent/JP6738732B2/ja
Publication of WO2016208353A1 publication Critical patent/WO2016208353A1/fr

Abstract

L'invention concerne un appareil et un procédé pour le transfert en continu de structures sur une surface de film à une grande précision et un faible coût de moule. Cet appareil pour la fabrication d'un film structuré en surface, dans lequel des structures de surface comprenant un matériau thermodurcissable sont situées sur une surface d'un film, est pourvu d'au moins : (1) un moule en forme de courroie sans fin présentant des structures sur une surface correspondante ; (2) un moyen de transport de moule pour provoquer le transport du moule, maintenu par deux rouleaux chauffants ou plus, de manière circulante par la rotation des rouleaux chauffants ; (3) un mécanisme de pressage pourvu d'au moins un rouleau pinceur et d'un moyen de pincement qui utilise le rouleau pinceur et l'un des rouleaux chauffants du moyen de transport de moule, le rouleau pinceur étant agencé parallèlement audit un rouleau chauffant et présentant une surface couverte d'un corps élastique ; (4) une unité de revêtement installée en amont du mécanisme de pressage dans la direction de transport du moule ; (5) un moyen de fourniture de film pour fournir un film sur une surface du moule ; et (6) un moyen de séparation de film pour séparer le film de la surface du moule.
PCT/JP2016/066460 2015-06-23 2016-06-02 Procédé et appareil pour la fabrication d'un film structuré en surface WO2016208353A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201680018786.7A CN107428072B (zh) 2015-06-23 2016-06-02 表面结构薄膜的制造方法和制造装置
KR1020177027496A KR102454079B1 (ko) 2015-06-23 2016-06-02 표면 구조 필름의 제조 방법 및 제조 장치
JP2016540697A JP6738732B2 (ja) 2015-06-23 2016-06-02 表面構造フィルムの製造方法および製造装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015-125458 2015-06-23
JP2015125458 2015-06-23

Publications (1)

Publication Number Publication Date
WO2016208353A1 true WO2016208353A1 (fr) 2016-12-29

Family

ID=57585025

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/066460 WO2016208353A1 (fr) 2015-06-23 2016-06-02 Procédé et appareil pour la fabrication d'un film structuré en surface

Country Status (5)

Country Link
JP (1) JP6738732B2 (fr)
KR (1) KR102454079B1 (fr)
CN (1) CN107428072B (fr)
TW (1) TWI698320B (fr)
WO (1) WO2016208353A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110000058A (zh) * 2019-04-11 2019-07-12 中山市旭森涂层材料有限公司 一种即时贴涂布系统及涂布工艺
CN111175878A (zh) * 2020-01-03 2020-05-19 陈明亮 一种液晶显示屏用偏光片生产制造涂布处理工艺
TWI754978B (zh) * 2019-08-09 2022-02-11 日商艾美柯技術股份有限公司 微小構造轉印裝置及微小構造轉印方法

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE112018003347A5 (de) * 2017-06-30 2020-03-05 Kiefel Gmbh Verfahren zum kristallisieren einer folie, verfahren und vorrichtung zum formen einer folie sowie anlage zum herstellen von produkten aus thermoplastischem folienmaterial
WO2019116951A1 (fr) * 2017-12-15 2019-06-20 東レ株式会社 Appareil et procédé de production de film mince de polymère
JP7178600B2 (ja) * 2019-03-11 2022-11-28 パナソニックＩｐマネジメント株式会社 フィルム構造体の製造方法及び製造装置
CN111703174A (zh) * 2020-06-29 2020-09-25 江西安源包装印务有限公司 一种均匀热压的覆膜机

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS49125472A (fr) * 1973-04-03 1974-11-30
JP2001277354A (ja) * 2000-04-04 2001-10-09 Idemitsu Petrochem Co Ltd エンボスシートの製造方法およびエンボスシート
WO2008075811A1 (fr) * 2006-12-20 2008-06-26 Cheil Industries Inc. Dispositif de fabrication d'un film optique et procédé de fabrication du dispositif
JP2012210760A (ja) * 2011-03-31 2012-11-01 Toray Ind Inc 微細構造転写フィルムの製造方法および製造装置
JP2013116622A (ja) * 2011-10-31 2013-06-13 Jx Nippon Oil & Energy Corp ゾルゲル法を用いた凹凸基板の製造方法、それに用いるゾル溶液、及びそれを用いた有機ｅｌ素子の製造方法並びにそれから得られた有機ｅｌ素子
WO2014010516A1 (fr) * 2012-07-10 2014-01-16 旭硝子株式会社 Procédé d'impression et dispositif d'impression

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008137282A (ja) 2006-12-01 2008-06-19 Fujifilm Corp 凹凸状シートの製造方法及び光学フィルム
KR101604664B1 (ko) * 2011-10-31 2016-03-18 제이엑스 닛코닛세키 에네루기 가부시키가이샤 졸겔법을 이용한 요철 기판의 제조 방법, 이에 사용하는 졸 용액, 및 이를 사용한 유기 el 소자의 제조 방법과 이로부터 얻어진 유기 el 소자
CA2886852C (fr) 2012-10-05 2017-07-25 Jx Nippon Oil & Energy Corporation Procede de fabrication de substrat optique utilisant un moule pelliculaire, dispositif de fabrication et substrat optique ainsi obtenu

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS49125472A (fr) * 1973-04-03 1974-11-30
JP2001277354A (ja) * 2000-04-04 2001-10-09 Idemitsu Petrochem Co Ltd エンボスシートの製造方法およびエンボスシート
WO2008075811A1 (fr) * 2006-12-20 2008-06-26 Cheil Industries Inc. Dispositif de fabrication d'un film optique et procédé de fabrication du dispositif
JP2012210760A (ja) * 2011-03-31 2012-11-01 Toray Ind Inc 微細構造転写フィルムの製造方法および製造装置
JP2013116622A (ja) * 2011-10-31 2013-06-13 Jx Nippon Oil & Energy Corp ゾルゲル法を用いた凹凸基板の製造方法、それに用いるゾル溶液、及びそれを用いた有機ｅｌ素子の製造方法並びにそれから得られた有機ｅｌ素子
WO2014010516A1 (fr) * 2012-07-10 2014-01-16 旭硝子株式会社 Procédé d'impression et dispositif d'impression

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110000058A (zh) * 2019-04-11 2019-07-12 中山市旭森涂层材料有限公司 一种即时贴涂布系统及涂布工艺
TWI754978B (zh) * 2019-08-09 2022-02-11 日商艾美柯技術股份有限公司 微小構造轉印裝置及微小構造轉印方法
CN111175878A (zh) * 2020-01-03 2020-05-19 陈明亮 一种液晶显示屏用偏光片生产制造涂布处理工艺

Also Published As

Publication number Publication date
CN107428072A (zh) 2017-12-01
JPWO2016208353A1 (ja) 2018-04-12
JP6738732B2 (ja) 2020-08-12
TWI698320B (zh) 2020-07-11
CN107428072B (zh) 2019-09-27
KR102454079B1 (ko) 2022-10-14
KR20180019064A (ko) 2018-02-23
TW201714726A (zh) 2017-05-01

Similar Documents

Publication Publication Date Title
WO2016208353A1 (fr) Procédé et appareil pour la fabrication d'un film structuré en surface
JP6738743B2 (ja) 表面構造フィルムの製造方法および製造装置
TWI379760B (en) Apparatus for forming film with intermittent interval and method for forming film with intermittent interval
JP2008105407A (ja) 間欠式フィルム成形装置及び成型方法
JP5372708B2 (ja) 微細構造転写装置
JP5712733B2 (ja) 微細構造転写フィルムの製造方法および製造装置
JP6064667B2 (ja) 両面構造フィルムの製造方法および製造装置
JP4135769B2 (ja) 間欠式フィルム成形装置および成形方法
JP5293318B2 (ja) 間欠式フィルム成形方法および間欠式フィルム成形装置
JP5104232B2 (ja) 微細形状転写シートの成形装置
JP5884596B2 (ja) 微細構造転写フィルムの製造方法および製造装置
JP4552716B2 (ja) 樹脂シートの製造方法
JP6085193B2 (ja) 微細構造フィルムの製造方法および製造装置
WO2014109164A1 (fr) Dispositif de transfert de microstructure et procédé de transfert de microstructure
JP2008137380A (ja) 微細形状転写シートの製造装置および微細形状転写シートの製造方法
JP5304303B2 (ja) 微細形状転写シートの製造装置および微細形状転写シートの製造方法
JP2014151636A (ja) エンドレスベルト状金属金型およびその製造方法
JP2009166409A (ja) 微細形状転写用シート
JP5683579B2 (ja) 微細表面構造を有するフィルムの製造方法および製造装置
TWI798447B (zh) 液體塗布裝置
JP2009029061A (ja) 微細形状転写シートの製造装置および微細形状転写シートの製造方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2016540697

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16814124

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20177027496

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16814124

Country of ref document: EP

Kind code of ref document: A1