WO2016186073A1 - 補強テープ、及びこれを用いたフレキシブルフラットケーブル - Google Patents

補強テープ、及びこれを用いたフレキシブルフラットケーブル Download PDF

Info

Publication number
WO2016186073A1
WO2016186073A1 PCT/JP2016/064455 JP2016064455W WO2016186073A1 WO 2016186073 A1 WO2016186073 A1 WO 2016186073A1 JP 2016064455 W JP2016064455 W JP 2016064455W WO 2016186073 A1 WO2016186073 A1 WO 2016186073A1
Authority
WO
WIPO (PCT)
Prior art keywords
reinforcing tape
conductor
flat cable
flexible flat
mass
Prior art date
Application number
PCT/JP2016/064455
Other languages
English (en)
French (fr)
Inventor
博史 田口
Original Assignee
リケンテクノス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by リケンテクノス株式会社 filed Critical リケンテクノス株式会社
Priority to PL16796466T priority Critical patent/PL3300085T3/pl
Priority to JP2017519205A priority patent/JP6457078B2/ja
Priority to CN201680027901.7A priority patent/CN107960129B/zh
Priority to EP16796466.7A priority patent/EP3300085B1/en
Priority to US15/575,084 priority patent/US20180147822A1/en
Priority to KR1020177035192A priority patent/KR20180008537A/ko
Publication of WO2016186073A1 publication Critical patent/WO2016186073A1/ja

Abstract

本発明は、導体との接着性に優れ、導体端末に金メッキなどの処理を行う際に、補強テープが導体から剥離するなどのトラブルを抑止することのできる補強テープ、及びこれを用いたフレキシブルフラットケーブルを提供することを提供する。絶縁フィルム（Ａ）の片面の上に、厚み５～５０μｍのアンカーコートの層（Ｂ）、及び厚み１０～３０μｍのホットメルト接着剤の層（Ｃ）をこの順に有する補強テープ。上記アンカーコートの層（Ｂ）は、好ましくは、（ｂ１）熱可塑性飽和共重合ポリエステル系樹脂 １００質量部；と（ｂ２）１分子中に２以上のイソシアネート基を有する化合物 ３～２５質量部；を含む塗料からなる補強テープとする。

Description

補強テープ、及びこれを用いたフレキシブルフラットケーブル
　本発明は、フレキシブルフラットケーブルの補強テープに関する。更に詳しくは、導体との接着性に優れ、導体端末に金メッキなどの処理を行う際に、補強テープが導体から剥離するなどのトラブルを抑止することのできる補強テープに関する。
　フレキシブルフラットケーブルは、配列させた複数の導体を、絶縁基材フィルムと接着性樹脂組成物層とを有する積層体などにより挟持し、被覆した構造を有する。上記導体の端末は、ケーブルを電子機器にコネクター接続できるようにするため、しばしば補強テープが貼合され補強されている。また上記導体の端末は、ケーブルの性能を向上させるため、補強テープが貼合された後、しばしば金メッキなどが施される。
　従来から、上記補強テープとしては、厚肉の絶縁フィルムの片面にホットメルト接着剤層を設けたもの、典型的には厚み１５０～２５０μｍ程度の二軸延伸ポリエチレンテレフタレートフィルムの片面にポリエステル系ホットメルト接着剤層を設けたものが使用されている。ところが従来の補強テープには、導体接着力が経時的に低下する、及び耐湿熱性が低いという問題があった。そこでこれらの問題を解決する技術として、ホットメルト接着剤として改質されたポリエステル系ホットメルト接着剤層を用いることが提案されている（例えば、特許文献１及び２）。しかし、これらのホットメルト接着剤を補強テープに適用しても、導体端末に金メッキなどの処理を行う際に、補強テープが導体から剥離するなどのトラブルを抑止することはできなかった。
特開２００２－３７１２５８号公報 特開２００５－２５５７５２号公報
　本発明の課題は、導体との接着性に優れ、導体端末に金メッキなどの処理を行う際に、補強テープが導体から剥離するなどのトラブルを抑止することのできる補強テープ、及びこれを用いたフレキシブルフラットケーブルを提供することにある。
　本発明者は、鋭意研究した結果、驚くべきことに、厚肉の絶縁フィルムとホットメルト接着剤層との間に、厚肉のアンカーコート層を設けることにより、上記課題を達成できることを見出した。
　すなわち、本発明は、フレキシブルフラットケーブル用補強テープであって、絶縁フィルム（Ａ）の片面の上に、厚み５～５０μｍのアンカーコートの層（Ｂ）、及び厚み１０～３０μｍのホットメルト接着剤の層（Ｃ）をこの順に有する補強テープである。
　第２の発明は、前記アンカーコートの層（Ｂ）が、（ｂ１）熱可塑性飽和共重合ポリエステル系樹脂 １００質量部；と（ｂ２）１分子中に２以上のイソシアネート基を有する化合物 ３～２５質量部；を含む塗料からなる第１の発明に記載の補強テープである。
　第３の発明は、前記ホットメルト接着剤が、熱可塑性飽和共重合ポリエステル系の接着剤である第１の発明又は第２の発明に記載の補強テープである。
　第４の発明は、軟化温度が９５℃以上である第１～３の発明の何れか１に記載の補強テープである。
　第５の発明は、第１～４の発明の何れか１に記載の補強テープを含むフレキシブルフラットケーブルである。
　本発明の補強テープは、導体との接着性に優れ、導体端末に金メッキなどの処理を行う際に、補強テープが導体から剥離するなどのトラブルを抑止することができる。そのため本発明の補強テープは、フレキシブルフラットケーブルの導体端末の補強に好適に用いることができる。
フレキシブルフラットケーブルの導体端末に補強テープを貼合した状態の一例を示す部分斜視図である。 軟化温度の測定例を示すチャートである。
　本発明のフレキシブルフラットケーブル用補強テープは、絶縁フィルム（Ａ）の片面の上に、厚み５～５０μｍのアンカーコートの層（Ｂ）、及び厚み１０～３０μｍのホットメルト接着剤の層（Ｃ）をこの順に有する。
（Ａ）絶縁フィルム：
　上記絶縁フィルムは、本発明の補強テープに剛性と強度を付与し、フレキシブルフラットケーブルの導体端末を電子機器にコネクター接続できるようにする働きをする。
　上記絶縁フィルムとしては、例えば、ポリエチレンテレフタレート系樹脂、ポリエチレンナフタレート系樹脂などのポリエステル系樹脂；ポリフェニレンスルフィド系樹脂；ポリカーボネート系樹脂；ポリプロピレン系樹脂、ポリエチレン系樹脂などのポリオレフィン系樹脂；ポリアミド系樹脂；及び、ポリスチレン系樹脂；などの樹脂の１種以上からなるフィルムをあげることができる。これらのフィルムは無延伸フィルム、一軸延伸フィルム、及び二軸延伸フィルムを包含する。またこれらの１種以上を２層以上積層した積層フィルムを包含する。これらの中で、剛性、強度、及びコストの観点から、ポリエチレンテレフタレート系樹脂の二軸延伸フィルム、及びこれを２層以上積層した積層フィルムが好ましい。
　上記絶縁フィルムの厚みは、特に制限されないが、剛性と強度を付与する観点から、通常１００μｍ以上、好ましくは１２５μｍ以上であってよい。加工性の観点から、通常５００μｍ以下、好ましくは２５０μｍ以下であってよい。
　上記絶縁フィルムは、着色剤を含む樹脂からなる着色層を含むものであってよい。上記絶縁フィルムは、これを構成するフィルムの何れか１以上の面の上に、印刷を施されたものであってよい。
（Ｂ）アンカーコートの層：
　上記層（Ｂ）は、上記絶縁フィルムと上記ホットメルト接着剤の層との接着強度を向上させるとともに、導体接着性を高める働きをする。
　上記アンカーコートの層を形成するための塗料としては、特に制限されないが、好ましくは、（ｂ１）熱可塑性飽和共重合ポリエステル系樹脂 １００質量部；と（ｂ２）１分子中に２以上のイソシアネート基を有する化合物 ３～２５質量部；を含む塗料をあげることができる。
　上記成分（ｂ１）は、アンカーコート形成用塗料のベース材となる樹脂である。上記成分（ｂ１）としては、例えば、任意の多価カルボン酸と任意の多価オールを用い、公知の方法で得られた熱可塑性飽和共重合ポリエステル系樹脂を用いることができる。
　上記多価カルボン酸としては、例えば、テレフタル酸、イソフタル酸、オルソフタル酸、及びナフタレンジカルボン酸、ジフェニル－４、４’－ジカルボン酸、ジフェノキシエタンジカルボン酸、ジフェニル－３、３’－ジカルボン酸、ジフェニル－４、４’－ジカルボン酸、アントラセンジカルボン酸などの芳香族多価カルボン酸；１，２－シクロヘキサンジカルボン酸、１，３－シクロヘキサンジカルボン酸、１，４－シクロヘキサンジカルボン酸などの脂環式ジカルボン酸；マロン酸、コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、及びセバシン酸などの脂肪族多価カルボン酸；及びこれらのエステル形成性誘導体などをあげることができる。上記カルボン酸としてはこれらの１種以上を用いることができる。
　上記多価オールとしては、例えば、エチレングリコール、ジエチレングリコール、トリメチレングリコール、テトラメチレングリコール、ネオペンチルグリコール、ポリエチレングリコール、１，２－プロパンジオール、１，３－プロパンジオール、ポリプロピレングリコール、１，２－ブタンジオール、１，３－ブタンジオール、１，４－ブタンジオール、１，５－ペンタンジオール、１，６－ヘキサンジオール、ネオペンチルグリコール、デカメチレングリコール、３－メチル－１，５－ペンタンジオール、２－メチル－１，３－プロパンジオール、１，２－シクロヘキサンジオール、１，４－シクロヘキサンジオール、１，４－シクロヘキサンジメタノール、２，２，４，４'－テトラメチル－１，３－シクロブタンジオール、グリセリン、及びトリメチロールプロパンなどの脂肪族多価アルコール；キシリレングリコール、４，４'－ジヒドロキシビフェニル、２，２－ビス（４－ヒドロキシフェニル）プロパン、ビス（４－ヒドロキシフェニル）スルホン、ビスフェノールＡ、ビスフェノールＡのアルキレンオキサイド付加物などの芳香族多価オール；及びこれらのエステル形成性誘導体などをあげることができる。上記多価オールとしてはこれらの１種以上を用いることができる。
　上記成分（ｂ１）の数平均分子量は、導体接着性、及びフレキシブルフラットケーブル用難燃絶縁フィルムとの接着性の観点から、１０,０００～３５,０００であることが好ましく、１５,０００～３０,０００であることがより好ましい。
　上記成分（ｂ１）の数平均分子量は、ゲル浸透クロマトグラフィ（ＧＰＣ）の測定した値である。
　ＧＰＣの測定は、システムとして、日本分光株式会社の高速液体クロマトグラフィシステム「ＬＣ－２０００Ｐｌｕｓ（商品名）」（デガッサー、送液ポンプ「ＰＵ－２０８０（商品名）」、オートサンプラー「ＡＳ－２０５５（商品名）」、カラムオーブン及びＲＩ（示差屈折率）検出器を含むシステム。）を使用し；カラムとして、昭和電工株式会社のスチレンジビニルベンゼン共重合体充填カラム「Ｓｈｏｄｅｘ　ＧＰＣ　Ｋ-８０６Ｌ（商品名）」２本を連結して用い；和光純薬工業株式会社の高速液体クロマトグラフ用クロロホルム（安定剤としてエタノールを含む。）を移動相として；流速１．０ミリリットル／分、カラム温度４０℃、試料濃度１ミリグラム／ミリリットル、試料注入量１００マイクロリットルの条件で行う。
　各保持容量における溶出量は、上記成分（ｂ１）の屈折率の分子量依存性が無いと見なしてＲＩ検出器の検出量から求める。
　また保持容量からポリスチレン換算分子量への較正曲線は、アジレントテクノロジー（Ａｇｉｌｅｎｔ　Ｔｅｃｈｎｏｌｏｇｙ）株式会社の標準ポリスチレン「ＥａｓｉＣａｌ　ＰＳ－１（商品名）」（Ｐｌａｉｎ　Ａの分子量６８７００００、８４１７００、１５２８００、２８７７０、２９３０；Ｐｌａｉｎ　Ｂの分子量２３４８０００、３２７３００、７４８００、１０１１０、５８０）を使用して作成する。
　解析プログラムは、日本分光株式会社の「ＣｈｒｏｍＮＡＶ　ＧＰＣ（商品名）」を使用する。
　なおＧＰＣの理論及び測定の実際については、共立出版株式会社の「サイズ排除クロマトグラフィー　高分子の高速液体クロマトグラフィー、著者：森定雄、初版第１刷１９９１年１２月１０日」などの参考書を参照することができる。
　上記成分（ｂ１）は、結晶性であってもよく、非結晶性であってもよい。上記成分（ｂ１）は、補強テープが導体から剥離するなどのトラブルを抑止する観点から、非結晶性であってよい。
　本明細書では、株式会社パーキンエルマージャパンのＤｉａｍｏｎｄ ＤＳＣ型示差走査熱量計を使用し、試料を５０℃／分の昇温速度で２００℃まで昇温し、２００℃で１０分間保持した後、２０℃／分の降温速度で５０℃まで冷却し、５０℃で１０分間保持した後、２０℃／分の昇温速度で２００℃まで加熱するという温度プログラムで測定されるセカンド融解曲線（最後の昇温過程において測定される融解曲線）の融解熱量が、１０Ｊ／ｇ以下のポリエステルを非結晶性、１０Ｊ／ｇを超えるポリエステルを結晶性と定義した。
　上記成分（ｂ２）は、１分子中に２以上のイソシアネート基を有し、アンカーコートの層に弾性体としての性質を付与し、本発明の補強テープの導体接着性を向上させる働きをする。
　上記成分（ｂ２）としては、例えば、メチレンビス－４－シクロヘキシルイソシアネート；トリレンジイソシアネートのトリメチロールプロパンアダクト体、ヘキサメチレンジイソシアネートのトリメチロールプロパンアダクト体、イソホロンジイソシアネートのトリメチロールプロパンアダクト体、トリレンジイソシアネートのイソシアヌレート体、ヘキサメチレンジイソシアネートのイソシアヌレート体、イソホロンジイソシアネートのイソシアヌレート体、ヘキサメチレンジイソシアネートのビウレット体等のポリイソシアネート；及び、上記ポリイソシアネートのブロック型イソシアネート等のウレタン架橋剤などをあげることができる。上記成分（ｂ２）としては、これらの１種又は２種以上の混合物を用いることができる。
　上記成分（ｂ２）の配合量は、導体接着性の観点から、上記成分（ｂ１）１００質量部に対して、好ましくは３～２５質量部、より好ましくは１０～２３質量部、更に好ましくは１４～２０質量部である。
　上記アンカーコート形成用塗料は、塗工し易い濃度に希釈するため、所望に応じて溶剤を含んでいてもよい。溶剤は上記成分（ｂ１）、上記成分（ｂ２）、及びその他の任意成分と反応したり、これらの成分の自己反応（劣化反応を含む）を触媒（促進）したりしないものであれば、特に制限されない。例えば、１－メトキシ－２－プロパノール、酢酸エチル、酢酸ｎブチル、トルエン、メチルエチルケトン、メチルイソブチルケトン、ダイアセトンアルコール、及びアセトンなどをあげることができる。
　上記アンカーコート形成用塗料には、所望に応じて、帯電防止剤、界面活性剤、レベリング剤、チクソ性付与剤、汚染防止剤、印刷性改良剤、酸化防止剤、耐候性安定剤、耐光性安定剤、紫外線吸収剤、熱安定剤、着色剤、及びフィラーなどの添加剤を１種、又は２種以上含ませてもよい。
　上記アンカーコート形成用塗料は、これらの成分を混合攪拌することにより得ることができる。
　上記アンカーコート形成用塗料を用いて上記層（Ｂ）を形成する方法は特に制限されず、公知のウェブ塗布方法を使用することができる。具体的には、ロールコート、グラビアコート、リバースコート、ロールブラッシュ、スプレーコート、エアナイフコート、及びダイコートなどの方法をあげることができる。
　上記アンカーコートの層（Ｂ）の厚みは、導体接着性の観点から、５～５０μｍ、好ましくは１０～４０μｍ、より好ましくは１５～３０μｍである。
（Ｃ）ホットメルト接着剤の層：
　上記層（Ｃ）は、導体接着性を直接的に担保する働きをする。
　上記ホットメルト接着剤としては、例えば、ポリエステル系、エチレン酢酸ビニル系、ポリウレタン系、ポリアミド系、ポリスチレン系、及びポリオレフィン系の接着剤をあげることができる。これらの中で、ポリエステル系接着剤が好ましく、熱可塑性飽和共重合ポリエステル系接着剤がより好ましく、結晶性の熱可塑性飽和共重合ポリエステル系接着剤であって、融点が１００～１５０℃のものが更に好ましい。
　本明細書において、融点は、株式会社パーキンエルマージャパンのＤｉａｍｏｎｄ ＤＳＣ型示差走査熱量計を使用し、試料を５０℃／分の昇温速度で２００℃まで昇温し、２００℃で１０分間保持した後、２０℃／分の降温速度で５０℃まで冷却し、５０℃で１０分間保持した後、２０℃／分の昇温速度で２００℃まで加熱するという温度プログラムにおけるセカンド融解曲線（最後の昇温過程において測定される曲線）に現れる最も高い温度側のピークのピークトップ温度である。またセカンド融解曲線の融解熱量が、１０Ｊ／ｇ以下のポリエステルを非結晶性、１０Ｊ／ｇを超えるポリエステルを結晶性と定義した。
　上記ホットメルト接着剤の層を形成する方法は、特に制限されない。例えば、押出機、Ｔダイ、及び引巻取機を備えた装置を使用し、溶融押出する方法；ホットメルト接着剤を溶剤、例えば、１－メトキシ－２－プロパノール、酢酸エチル、酢酸ｎブチル、トルエン、メチルエチルケトン、メチルイソブチルケトン、ダイアセトンアルコール、及びアセトンなどに溶解し、公知のウェブ塗布方法、例えば、ロールコート、グラビアコート、リバースコート、ロールブラッシュ、スプレーコート、エアナイフコート、及びダイコートなどにより、所望のウェブ基材の上に塗膜として形成する方法；などをあげることができる。
　上記ホットメルト接着剤の層の厚みは、導体接着性の観点から、１０～３０μｍ、好ましくは１５～２０μｍである。
　本発明の補強テープは、導体接着性の観点から、軟化温度が好ましくは９５℃以上、より好ましくは１００℃以上である。
　本明細書において、上記軟化温度は、熱機械測定装置を用い、補強テープの上記層（Ｃ）の側から圧子を侵入させたときの温度－侵入深さ曲線において、侵入深さ変化率の絶対値が最大となる温度である。圧子として株式会社リガクのペネトレーション用円錐ピン（ＰＮ／Ｐ１Ｘ０７Ｒ）を用いたこと以外はＪＩＳ Ｋ７１９６－１９９１に準拠し、株式会社リガクの熱機械測定装置「ＴＭＡ８３１０（商品名）」を使用し、直径５ｍｍの円形に裁断されたサンプル、荷重４９１ｍＮ、及び温度３０℃から１５０℃まで昇温速度２０℃／分で昇温する条件で得られた温度－侵入深さ曲線を、温度で微分して算出した曲線のピークトップ温度として求めた。測定例を図２に示す。
　理論に拘束される意図はないが、本発明の構成とすることにより、補強テープが導体から剥離するなどのトラブルを抑止することができるのは、成形加工時に厚肉のアンカーコートがクッションとなり、ホットメルト接着剤が、導体の周囲から流出しないようになるためと考えられる。
　本発明のフレキシブルフラットケーブルを得る方法は、特に制限されず、公知の方法で得ることができる。上記方法としては、例えば、以下のような方法をあげることができる。絶縁フィルムの片面に難燃性ホットメルト接着剤の層を設けた公知のフレキシブルフラットケーブル用難燃絶縁フィルムを２ロール用い、公知のフレキシブルフラットケーブル製造装置を使用し、上記難燃絶縁フィルムを上記ホットメルト接着剤の層が対向するように送り出し、その間に平行に引き揃えた導電体の平角線を挟み込み、上記装置の熱プレスロールで熱プレスして上記ホットメルト接着剤の層同士を互いに融着させる。上記難燃絶縁フィルムには、導電体の平角線を挟み込む前に、孔を打抜くとともに、孔を打抜いた所に上記絶縁フィルムの層の側から、本発明の補強テープを貼着する。次に、両側端をスリットして所定の仕上げ幅とし、孔と本発明の補強テープの部分で切断して、本発明のフレキシブルフラットケーブルとして完成することができる。図１は、フレキシブルフラットケーブルの一例を示す部分斜視図である。
　上記導電体の平角線としては、特に制限されないが、ケーブルの摺動性の観点から、厚さ１２～５０μｍ、幅０．２～２ｍｍの軟銅線、硬銅線、及びこれらの錫メッキ線やニッケルメッキ線であってよい。
　以下、本発明を実施例により説明するが、本発明はこれらに限定されるものではない。
測定方法
（イ）導体接着力１（未処理）：
（イ－１）フレキシブルフラットケーブルの製造：
　フレキシブルフラットケーブル装置を使用し、リケンテクノス株式会社のフレキシブルフラットケーブル用難燃絶縁フィルム「ＮＣ５２２４（商品名）」を２ロール用い、導体幅１．４ｍｍ、厚み０．０３５ｍｍの硬銅線を１２本配列させたものを、一方の上記難燃絶縁フィルムのホットメルト接着剤層と他方の上記難燃絶縁フィルムのホットメルト接着剤層とで挟持し、温度１８０℃に予熱された押圧ロールと温度１８０℃に予熱された受けロールとで、ライン速度０．５ｍ／分、圧力３ＭＰａの条件で押圧し、融着させた後、両側端をスリットして幅２４ｍｍの仕上げ幅とし、孔と補強テープの部分におけるマシン方向の中央の線において切断して、長さ１００ｍｍ、幅２４ｍｍのフレキシブルフラットケーブルを得た。その際に、上記難燃絶縁フィルムには、マシン方向２０ｍｍ×横方向２４ｍｍの孔を、マシン方向に１００ｍｍ間隔で打抜き、そこに長さ１５０ｍｍに裁断した補強テープを、絶縁フィルムの層の側から貼着した。
（イ－２）
　上記で得たフレキシブルフラットケーブルの補強テープと銅線との接着力を、試験速度５０ｍｍ／分の条件で、銅線を補強テープから１８０度剥離を行い測定した。
（ロ）導体接着力２（酸浸漬後の導体接着力）：
　上記（イ－１）で得たフレキシブルフラットケーブルの補強テープ部分を、５質量％塩酸水溶液に温度６０℃で２時間浸漬後、上記（イ－２）と同様にして測定した。
（ハ）導体接着力３（アルカリ浸漬後の導体接着力）：
　上記（イ－１）で得たフレキシブルフラットケーブルの補強テープ部分を、５質量％水酸化ナトリウム水溶液に温度６０℃で２時間浸漬後、上記（イ－２）と同様にして測定した。
（ニ）導体接着力４（塩水に浸漬後の導体接着力）：
　上記（イ－１）で得たフレキシブルフラットケーブルの補強テープ部分を、５質量％塩化ナトリウム水溶液に温度６０℃で２時間浸漬後、上記（イ－２）と同様にして測定した。
（ホ）導体接着力５（金メッキ処理液浸漬後の導体接着力）：
　上記（イ－１）で得たフレキシブルフラットケーブルの補強テープ部分を、フレキシブルフラットケーブルの端末金メッキ用の金メッキ処理液（シアン化金カリウム、シアン化カリウム、リン酸水素カリウム、及び炭酸カリウムの混合水溶液。ｐＨ１１。）に温度６０℃で２時間浸漬後、上記（イ－２）と同様にして測定した。
（ヘ）導体接着力６（金メッキ処理液浸漬後の導体接着力２）：
　上記（ホ）と全て同様にして金メッキ処理液浸漬後の導体接着力を、１００本のケーブルについて、各２本の銅線について測定（合計データ数２００個）し、接着力が１．５Ｎ／１４ｍｍ以下のデータ数を数え、以下の基準で評価した。
　　◎：０個
　　○：１～４個
　　△：５～１０個
　　×：１１個以上
使用した原材料
（Ａ）絶縁フィルム：
（Ａ－１）厚み１８８μｍの片面易接着処理二軸延伸ポリエチレンテレフタレート系樹脂フィルム。
（Ｂ）アンカーコート用塗料：
（Ｂ－１）下記（ｂ１）１００質量部、下記（ｂ２）１７質量部、下記（ｂ３）３３質量部、及び下記（ｂ４）２３０質量部を混合攪拌して得た塗料。
（Ｂ－２）下記（ｂ１）１００質量部、下記（ｂ２）１２質量部、下記（ｂ３）３３質量部、及び下記（ｂ４）２３０質量部を混合攪拌して得た塗料。
（ｂ１）東洋紡株式会社の非結晶性の熱可塑性飽和共重合ポリエステル系樹脂「バイロン５００（商品名）」、分子量２３０００、ガラス転移温度 ４℃。
（ｂ２）東ソー株式会社のポリイソシアヌレート「コロネートＨＸ（商品名）」。
（ｂ３）大日精化工業株式会社のインキ「ＮＢ５００　７３９藍（商品名）」。
（ｂ４）トルエン。
（Ｃ）ホットメルト接着剤：
（Ｃ－１）東亜合成株式会社の結晶性の熱可塑性飽和共重合ポリエステル系樹脂「アロンメルトＰＥＳ－１１１ＥＥ（商品名）」。
（Ｄ）セパレーターフィルム：
（Ｄ－１）厚み１２μｍの二軸延伸ポリプロピレン系樹脂フィルム。
例１
　上記（Ａ－１）の易接着面の上に、ロールコーターを使用し、上記（Ｂ－１）を用い、乾燥後厚みが１５μｍとなるようにアンカーコートの層を形成した。上記（Ｃ－１）を、下記（Ｄ－１）の上に、押出ラミネートして厚み１５μｍのフィルム状ホットメルト接着剤を得た。上記で得た上記（Ａ－１）と上記（Ｂ－１）との積層体の上記（Ｂ－１）側の面の上に、上記で得た上記（Ｃ－１）と上記（Ｄ－１）との積層体の上記（Ｃ－１）側の面を重ねて熱ラミネートした。こうして得られた積層体を幅２５ｍｍにスリットし、補強テープを得た。上記試験（イ）～（ホ）を行った。結果を表１に示す。
例２～４、例１Ｃ、２Ｃ
　上記（Ｂ）層の厚み、及び上記（Ｃ）層の厚みを表１に示すように変更したこと以外は、全て例１と同様に行った。結果を表１に示す。
例５
　上記（Ｂ－１）の替わりに、上記（Ｂ－２）を用いたこと以外は、全て例１と同様に行った。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　本発明の補強テープは、導体との接着力が良好であり、導体端末に金メッキなどの処理を行う際に、補強テープが導体から剥離するなどのトラブルを抑止するができる。
　　１：フレキシブルフラットケーブル
　　２：補強テープ
　　３：導体端末

Claims (5)

  1. 　フレキシブルフラットケーブル用補強テープであって、
    　絶縁フィルム（Ａ）の片面の上に、
    　厚み５～５０μｍのアンカーコートの層（Ｂ）、及び
    　厚み１０～３０μｍのホットメルト接着剤の層（Ｃ）をこの順に有する、補強テープ。
  2. 　前記アンカーコートの層（Ｂ）が、
    （ｂ１）熱可塑性飽和共重合ポリエステル系樹脂 １００質量部；と
    （ｂ２）１分子中に２以上のイソシアネート基を有する化合物 ３～２５質量部；
    を含む塗料からなる、請求項１に記載の補強テープ。
  3. 　前記ホットメルト接着剤が、熱可塑性飽和共重合ポリエステル系の接着剤である、請求項１又は２に記載の補強テープ。
  4. 　軟化温度が９５℃以上である、請求項１～３の何れか１項に記載の補強テープ。
  5. 　請求項１～４の何れか１項に記載の補強テープを含むフレキシブルフラットケーブル。
PCT/JP2016/064455 2015-05-20 2016-05-16 補強テープ、及びこれを用いたフレキシブルフラットケーブル WO2016186073A1 (ja)