WO2016121372A1 - Isolant thermique et procédé de fabrication d'isolant thermique - Google Patents

Isolant thermique et procédé de fabrication d'isolant thermique Download PDF

Info

Publication number
WO2016121372A1
WO2016121372A1 PCT/JP2016/000360 JP2016000360W WO2016121372A1 WO 2016121372 A1 WO2016121372 A1 WO 2016121372A1 JP 2016000360 W JP2016000360 W JP 2016000360W WO 2016121372 A1 WO2016121372 A1 WO 2016121372A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat insulating
insulating material
xerogel
fiber
weight
Prior art date
Application number
PCT/JP2016/000360
Other languages
English (en)
Japanese (ja)
Inventor
孝太郎 中西
笑美子 中西
源 植田
Original Assignee
オゾンセーブ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by オゾンセーブ株式会社 filed Critical オゾンセーブ株式会社
Publication of WO2016121372A1 publication Critical patent/WO2016121372A1/fr

Abstract

La présente invention concerne un isolant thermique qui est moins volumineux que dans l'art connexe, présente une excellente aptitude au traitement, et peut être appliqué à une microstructure, et concerne également un procédé de fabrication par lequel un tel isolant thermique peut être fabriqué. L'isolant thermique selon la présente invention comprend une fibre principale, un xérogel et/ou un aérogel, au moins un polymère hydrosoluble choisi dans le groupe constitué par un polymère cationique et un polymère ampholyte, et/ou un liant comprenant une fibre synthétique à point de fusion bas, et est caractérisé en ce que le xérogel et l'aérogel ont une densité inférieure à 0,5 g/cm3 et une conductivité thermique inférieure ou égale à 0,02 W/(m·K) et, en termes de poids brut, 35 à 210 parties en poids du xérogel et/ou de l'aérogel sont combinées avec 100 parties en poids de la fibre principale.
PCT/JP2016/000360 2014-01-30 2016-01-25 Isolant thermique et procédé de fabrication d'isolant thermique WO2016121372A1 (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2014015388 2014-01-30
JP2015013731A JP6188245B2 (ja) 2014-01-30 2015-01-27 断熱材及び断熱材の製造方法
JP2015-013731 2015-01-27

Publications (1)

Publication Number Publication Date
WO2016121372A1 true WO2016121372A1 (fr) 2016-08-04

Family

ID=54186811

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/000360 WO2016121372A1 (fr) 2014-01-30 2016-01-25 Isolant thermique et procédé de fabrication d'isolant thermique

Country Status (3)

Country Link
JP (1) JP6188245B2 (fr)
TW (1) TWI619807B (fr)
WO (1) WO2016121372A1 (fr)

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017010551A1 (fr) * 2015-07-15 2017-01-19 日立化成株式会社 Matériau composite d'aérogel
CN108609911A (zh) * 2018-04-28 2018-10-02 无锡市辰元科技有限公司 隔热砂浆及其制备方法、隔热软瓷及其制备方法和建筑材料
CN110258188A (zh) * 2019-06-21 2019-09-20 苏州卓纳纳米技术有限公司 一种气凝胶超疏水隔热超薄毡的制备方法
KR20190120228A (ko) 2017-03-02 2019-10-23 미쯔비시 케미컬 주식회사 적층 필름, 화상 표시 장치용 적층체 및 화상 표시 장치
JP2019189519A (ja) * 2018-04-23 2019-10-31 オゾンセーブ株式会社 断熱材および断絶材の製造方法
CN111819387A (zh) * 2018-03-14 2020-10-23 松下知识产权经营株式会社 隔热薄片、使用其的隔热体及其制造方法
US20210115622A1 (en) * 2018-11-15 2021-04-22 Panasonic Intellectual Property Management Co., Ltd. Heat-insulating sheet and manufacturing method therefor
EP3743464A4 (fr) * 2018-01-23 2022-01-19 Bronx Creative&Design Centre Pte Ltd Composites d'aérogels organiques-inorganiques, procédés et utilisations associés
CN114008835A (zh) * 2019-04-05 2022-02-01 电化株式会社 绝热材料组合物、绝热材料及其制造方法
US11247446B2 (en) 2018-10-01 2022-02-15 Triple Point Innovations Llc Re-pulpable insulated paper products and methods of making and using the same
US11377798B2 (en) 2018-10-01 2022-07-05 Triple Point Innovations Llc Re-pulpable thermally insulated paper products and methods of making and using the same
CN115538217A (zh) * 2022-11-02 2022-12-30 山东鲁阳节能材料股份有限公司 一种可溶纤维复合纸及其制备方法

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111499274B (zh) * 2016-04-04 2022-06-10 菲博林科技有限公司 用于在天花板、地板和建筑产品中提供增加的强度的组合物和方法
JP7027894B2 (ja) * 2017-09-13 2022-03-02 王子ホールディングス株式会社 発泡断熱紙容器用紙基材、発泡断熱紙容器用シートおよび発泡断熱紙容器
JP7027897B2 (ja) * 2017-09-13 2022-03-02 王子ホールディングス株式会社 発泡断熱紙容器用紙基材、発泡断熱紙容器用シートおよび発泡断熱紙容器
JP7121595B2 (ja) * 2017-09-28 2022-08-18 住友理工株式会社 断熱材用塗料および断熱材
CN108570723B (zh) * 2018-04-18 2020-11-24 浙江梵彼斯特轻纺发展有限公司 一种气凝胶填充凤梨麻基复合纤维及其制备工艺
JP7119916B2 (ja) * 2018-11-05 2022-08-17 トヨタ自動車株式会社 内燃機関の遮熱コーティングおよび遮熱コーティングの形成方法
JP7285085B2 (ja) * 2019-01-31 2023-06-01 住友理工株式会社 断熱材およびその製造方法
JP7223600B2 (ja) * 2019-02-28 2023-02-16 住友理工株式会社 断熱部材およびその製造方法
JP6864384B2 (ja) * 2019-06-11 2021-04-28 オゾンセーブ株式会社 断熱材および断絶材の製造方法
JP2022082216A (ja) * 2020-11-20 2022-06-01 黒崎播磨株式会社 エアロゲル複合成形体
WO2024203355A1 (fr) * 2023-03-29 2024-10-03 イビデン株式会社 Protection de couvercle et procédé de fabrication associé, et module de batterie

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002333092A (ja) * 2001-05-09 2002-11-22 Kanegafuchi Chem Ind Co Ltd 繊維・微粒子複合断熱材
US20040180176A1 (en) * 2003-03-14 2004-09-16 Rusek Stanley J. Vaccum insulation article
JP2009299893A (ja) * 2008-05-15 2009-12-24 Nichias Corp 断熱材、これを用いた断熱構造及びその製造方法
JP2010038288A (ja) * 2008-08-06 2010-02-18 Nichias Corp 断熱体
JP2014035044A (ja) * 2012-08-09 2014-02-24 Panasonic Corp 断熱材及びその製造方法
US20140273701A1 (en) * 2013-03-15 2014-09-18 Cabot Corporation Aerogel blanket and method of production
JP2015124779A (ja) * 2013-12-25 2015-07-06 パナソニックＩｐマネジメント株式会社 断熱材及びその製造方法
JP2016028880A (ja) * 2014-07-18 2016-03-03 パナソニックＩｐマネジメント株式会社 複合シートとその製造方法および複合シートを用いた電子機器

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6099029B2 (ja) * 2011-11-08 2017-03-22 オゾンセーブ株式会社 断熱用塗料、該塗料を用いた断熱方法、及び該塗料を塗布したシート材
WO2013141189A1 (fr) * 2012-03-23 2013-09-26 井前工業株式会社 Composition d'isolant thermique, isolant thermique l'utilisant et procédé de fabrication d'un isolant thermique
CN103113043B (zh) * 2013-02-04 2015-09-09 四川大学 无机微纳米粒子/聚合物复合建筑保温气凝胶材料及制备方法
CN103523789B (zh) * 2013-10-11 2015-05-27 余煜玺 一种二氧化硅气凝胶微球的制备方法

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002333092A (ja) * 2001-05-09 2002-11-22 Kanegafuchi Chem Ind Co Ltd 繊維・微粒子複合断熱材
US20040180176A1 (en) * 2003-03-14 2004-09-16 Rusek Stanley J. Vaccum insulation article
JP2009299893A (ja) * 2008-05-15 2009-12-24 Nichias Corp 断熱材、これを用いた断熱構造及びその製造方法
JP2010038288A (ja) * 2008-08-06 2010-02-18 Nichias Corp 断熱体
JP2014035044A (ja) * 2012-08-09 2014-02-24 Panasonic Corp 断熱材及びその製造方法
US20140273701A1 (en) * 2013-03-15 2014-09-18 Cabot Corporation Aerogel blanket and method of production
JP2015124779A (ja) * 2013-12-25 2015-07-06 パナソニックＩｐマネジメント株式会社 断熱材及びその製造方法
JP2016028880A (ja) * 2014-07-18 2016-03-03 パナソニックＩｐマネジメント株式会社 複合シートとその製造方法および複合シートを用いた電子機器

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2017010551A1 (ja) * 2015-07-15 2018-02-22 日立化成株式会社 エアロゲル複合材料
WO2017010551A1 (fr) * 2015-07-15 2017-01-19 日立化成株式会社 Matériau composite d'aérogel
KR20190120228A (ko) 2017-03-02 2019-10-23 미쯔비시 케미컬 주식회사 적층 필름, 화상 표시 장치용 적층체 및 화상 표시 장치
EP3743464A4 (fr) * 2018-01-23 2022-01-19 Bronx Creative&Design Centre Pte Ltd Composites d'aérogels organiques-inorganiques, procédés et utilisations associés
CN111819387A (zh) * 2018-03-14 2020-10-23 松下知识产权经营株式会社 隔热薄片、使用其的隔热体及其制造方法
JP2019189519A (ja) * 2018-04-23 2019-10-31 オゾンセーブ株式会社 断熱材および断絶材の製造方法
CN108609911A (zh) * 2018-04-28 2018-10-02 无锡市辰元科技有限公司 隔热砂浆及其制备方法、隔热软瓷及其制备方法和建筑材料
US11377798B2 (en) 2018-10-01 2022-07-05 Triple Point Innovations Llc Re-pulpable thermally insulated paper products and methods of making and using the same
US11806973B2 (en) 2018-10-01 2023-11-07 Triple Point Innovations Llc Re-pulp able insulated paper products and methods of making and using the same
US11247446B2 (en) 2018-10-01 2022-02-15 Triple Point Innovations Llc Re-pulpable insulated paper products and methods of making and using the same
US20210115622A1 (en) * 2018-11-15 2021-04-22 Panasonic Intellectual Property Management Co., Ltd. Heat-insulating sheet and manufacturing method therefor
CN114008835A (zh) * 2019-04-05 2022-02-01 电化株式会社 绝热材料组合物、绝热材料及其制造方法
CN110258188A (zh) * 2019-06-21 2019-09-20 苏州卓纳纳米技术有限公司 一种气凝胶超疏水隔热超薄毡的制备方法
CN115538217A (zh) * 2022-11-02 2022-12-30 山东鲁阳节能材料股份有限公司 一种可溶纤维复合纸及其制备方法

Also Published As

Publication number Publication date
TW201629184A (zh) 2016-08-16
JP6188245B2 (ja) 2017-08-30
TWI619807B (zh) 2018-04-01
JP2015163815A (ja) 2015-09-10

Similar Documents

Publication Publication Date Title
WO2016121372A1 (fr) Isolant thermique et procédé de fabrication d'isolant thermique
JP2017155402A (ja) 可撓性絶縁構造体ならびにその作成および使用方法
CN107709663B (zh) 包括两亲性聚合物的膜产品或膜的制造方法
KR20150047120A (ko) 세그먼트화 겔 복합체 및 이로부터 제조된 리지드 패널
WO2016120528A1 (fr) Matériaux fibreux thermoplastiques et procédé de production
JP2010255173A5 (fr)
EP2464796A2 (fr) Matériau non tissé de faible densité utile avec des carreaux de plafond insonorisant
CN109072560A (zh) 防护纸、纸杯
KR102134072B1 (ko) 실리카 에어로겔 분말층으로 이루어진 단열성 및 내화성 포장재용 에어로겔 접착코팅제
EP3108060B1 (fr) Procédé de production de matériau d'isolation sous forme de mousse
US11839069B2 (en) Electromagnetic wave absorbing sheet and method of manufacturing the same
JP6864384B2 (ja) 断熱材および断絶材の製造方法
JP6450201B2 (ja) 断熱容器用シート、断熱容器及び断熱容器用シートの製造方法
CN103572644A (zh) 一种多组分纤维混杂的复合材料毡及其制作方法
JP2022055295A (ja) 断熱材用組成物および断熱材
JP2009133030A (ja) 発泡板紙
JP2011241303A (ja) ガスバリア性コーティング剤及びそれを用いたガスバリア性材料
JP2008214779A (ja) 不燃シート又は不燃成形体
JP6674761B2 (ja) 断熱容器用シート及び断熱容器
JP2014070319A (ja) 板紙、段ボールシート及び箱
JP2022542714A (ja) 温度制御パッケージまたはそれに関連する改良
JP2010090489A (ja) 多層抄き板紙
KR20200037990A (ko) 실리카 에어로겔 분말층으로 이루어진 단열성 및 내화성 골판지 포장박스
JP2011058128A (ja) 加熱膨張性不織布
JPH11241297A (ja) 断熱性シート

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16742976

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16742976

Country of ref document: EP

Kind code of ref document: A1