WO2016047606A1 - カーボン被覆二酸化バナジウム粒子 - Google Patents
カーボン被覆二酸化バナジウム粒子 Download PDFInfo
- Publication number
- WO2016047606A1 WO2016047606A1 PCT/JP2015/076722 JP2015076722W WO2016047606A1 WO 2016047606 A1 WO2016047606 A1 WO 2016047606A1 JP 2015076722 W JP2015076722 W JP 2015076722W WO 2016047606 A1 WO2016047606 A1 WO 2016047606A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- vanadium dioxide
- carbon
- dioxide particles
- film
- coating layer
- Prior art date
Abstract
Description
上記自動調光材料の形態としては薄膜又はフィルムが望ましい。薄膜状の自動調光材料を製造する方法としては、従来、スパッタ等の乾式製膜法が検討されていたが、高コストの問題や、大面積の成膜が困難である等の問題から、微粒子を用いた塗布法や印刷法による製造方法が提案されている。
例えば、特許文献1には、二酸化バナジウム微粒子と、透光性樹脂と、該当透光性樹脂を溶解可能な有機溶剤とを含有する組成物を適切な基材に塗布することにより、二酸化バナジウム分散樹脂層を形成する方法が開示されている。
また、フィルム状の自動調光材料を製造する方法としては、二酸化バナジウムの微粒子を樹脂に分散・混練し、プレスや押出成形などの工程により製造することができる。
更に、上記フィルムを二枚のガラスに挟んだ合わせガラスを製造することもできる。
このような合わせガラス用中間膜では、二酸化バナジウムの微粒子を分散させることにより、二酸化バナジウムの相転移温度未満では赤外線を多く透過し、相転移温度以上になると赤外線が遮断される性質を示す合わせガラス用中間膜が得られることが期待される。
しかしながら、このような二酸化バナジウム粒子を分散させた合わせガラス用中間膜は、保管又は使用する時に、経時によりサーモクロミック性が低下し、耐久性が低いという問題があった。
一方で、透明性を向上するためには、粒子径が100nm以下のナノ粒子を用いる必要があるが、小粒径化によってサーモクロミック性が著しく低下するという課題もあった。
以下、本発明を詳述する。
上記二酸化バナジウム粒子は、サーモクロミック特性を有するものである。
上記二酸化バナジウム粒子を構成する二酸化バナジウムは、A型、B型、M型等様々な結晶構造が存在することが知られている。その中で上記ルチル型構造を形成した場合のみ相転移挙動を発現する。転移温度以下では単斜晶構造になり半導体特性を示し、転移温度以上では正方晶構造になり金属特性に変わる。その結果、温度変化に応じて光学特性、電気特性、熱的特性が可逆的に変化する。この可逆的変化を利用して、例えば環境温度の変化のみで自動的に調光するなどの利点がある。
この置換二酸化バナジウム粒子である置換二酸化バナジウムとしては、例えば、下記一般式(1)に示す構造を有するものが好ましい。
式(1)中、Mはタングステン、モリブデン、タンタル、ニオブ、クロム、鉄、ガリウム、アルミニウム、フッ素及びリンから選択される少なくとも1種の元素である。また、xは0~0.05の数値を表す。
上記置換二酸化バナジウムを用いる場合、金属原子の置換率の好ましい下限は0.1原子%、好ましい上限は10原子%である。置換率が0.1原子%以上であると、上記置換二酸化バナジウムの相転移温度を容易に調整することができ、10原子%以下であると、優れたサーモクロミック性を得ることができる。
なお、置換率とは、バナジウム原子数と置換された原子数との合計に占める、置換された原子数の割合を百分率で示した値である。
上記コア粒子として、例えば、酸化ケイ素、シリカゲル、酸化チタン、ガラス、酸化亜鉛、水酸化亜鉛、酸化アルミニウム、水酸化アルミニウム、水酸化チタン、酸化ジルコニウム、水酸化ジルコニウム、リン酸ジルコニウム、ハイドロタルサイト化合物、ハイドロタルサイト化合物の焼成物、及び、炭酸カルシウム等の無機粒子が挙げられる。
上記平均結晶子径が1nm未満であると、粒子全体の結晶性が低く、高いサーモクロミック性は望めない。また、100nmを超えると、これを用いて作製したサーモクロミック材料の透明性が低くなる恐れがある。
本明細書中、結晶子径とは、X線回折法における回折ピークの半価幅から求められる結晶子のサイズを意味する。結晶子径は、例えば、X線回折装置(リガク社製、RINT1000)から得られる回折データから半価幅を算出し、Scherrerの式をあてはめることで結晶子サイズを算出できる。具体的には、ルチル型VO2の最強ピーク2θ=27.86°の時の半価幅から算出した結晶子サイズを採用することで測定できる。
これら一連の解析は、例えば、解析ソフト(リガク社製PDXL)を用いて半価幅、結晶子サイズを算出できる。
本願発明者らは、酸素による二酸化バナジウム粒子の酸化、及び、紫外線照射下でポリビニルブチラール樹脂等の樹脂から発生した還元性物質(アルデヒド類)による二酸化バナジウム粒子の還元が、サーモクロミック性の低下(劣化)を引き起こす二つの主な原因であることを見出した。
これに対して、本発明では、緻密性の高い被覆層が形成されることで、二酸化バナジウム粒子と、酸素や還元性物質との接触が遮断され、粒子の酸化又は還元を抑制することができる。
なお、緻密な被覆層としての“緻密性”の厳密な定義はないが、本発明では、高解像度の透過電子顕微鏡を用いて一個一個のナノ粒子を観察した時に、図1のように、粒子表面の被覆層がはっきり観察され、かつ、被覆層が連続に形成されていることを“緻密”と定義する。
上記アモルファスカーボンをラマン分光で測定した場合、sp2結合に対応したGバンド(1580cm-1付近)及びsp3結合に対応したDバンド(1360cm-1付近)の2つのピークが明確に観察される。なお、炭素材料が結晶性の場合には、上記の2バンドのうち、何れかのバンドが極小化してゆく。例えば、単結晶ダイヤモンドの場合は1580cm-1付近のGバンドが殆ど観察されない。一方、高純度グラファイト構造の場合は、1360cm-1付近のDバンドが殆ど現れない。
本発明では、特にGバンドとDバンドのピーク強度比(Gバンドでのピーク強度/Dバンドでのピーク強度)が1.5以上であることで、形成されたアモルファスカーボン膜の緻密性が高く、高温における粒子間の焼結抑制効果も優れることとなる。
上記ピーク強度比が1.5未満であると、膜の緻密性と高温における焼結抑制効果が不十分であることだけではなく、膜の密着性及び膜強度も低下することとなる。
上記ピーク強度比は1.7以上であることが好ましく、10以下であることが好ましい。
上記被覆層は、カーボン以外の元素を含有しても良い。カーボン以外の元素としては、例えば、窒素、水素、酸素等が挙げられる。このような元素の含有量は、カーボンとカーボン以外の元素との合計に対して、10原子%以下であることが好ましい。
上記オキサジン樹脂は、一般にフェノール樹脂に分類される樹脂であるが、フェノール類とホルムアルデヒドに加えて、さらにアミン類を加えて反応させることで得られる熱硬化樹脂である。なお、フェノール類において、フェノール環にさらにアミノ基があるようなタイプ、例えば、パラアミノフェノールのようなフェノールを用いる場合には、上記反応でアミン類を加える必要はなく、炭化もしやすい傾向にある。炭化のしやすさでは、ベンゼン環ではなく、ナフタレン環を用いることで、さらに炭化がしやすくなる。
このように、オキサジン樹脂とは、ベンゼン環又はナフタレン環に付加した6員環をもつ樹脂のことをさし、その6員環には、酸素と窒素が含まれ、これが名前の由来となっている。
このように、オキサジン樹脂を用いて、より低温で炭化させることにより、アモルファスカーボンを有し、緻密性の高い被覆層を形成することができる。
アモルファスカーボンを有し、緻密性の高い被覆層を形成できる理由については明らかではないが、例えば、オキサジン樹脂としてナフタレンオキサジン樹脂を使用した場合、樹脂中のナフタレン構造が低温加熱によって局部的に繋がり、分子レベルで層状構造が形成されるためであると考えられる。上記層状構造は、高温処理されていないため、グラファイトのような長距離の周期構造までは進展しないため、結晶性は示さない。
得られたカーボンが、グラファイトのような構造であるか、アモルファス構造であるかは、後述するX線回折法によって、2θが26.4°の位置にピークが検出されるか否かにより確認することができる。
このように低温で得られることで、従来より低コスト、且つ簡便なプロセスで作製できるという利点がある。
上記熱処理の温度は170~300℃であることが好ましい。
膜厚のCV値(%)とは、標準偏差を平均膜厚で割った値を百分率で表したものであり、下記式により求められる数値のことである。CV値が小さいほど膜厚のばらつきが小さいことを意味する。
膜厚のCV値(%)=(膜厚の標準偏差/平均膜厚)×100
平均膜厚及び標準偏差は、例えば、FE-TEMを用いて測定することができる。
このようなベンゼン環、ナフタレン環に由来する質量スペクトルが検出されることで、オキサジン樹脂が含有するカーボンに由来するものであることを確認できると同時に、緻密性の高い被覆膜を得ることができる。
本願発明において、ベンゼン環に由来する質量スペクトルとは、77.12付近の質量スペクトルをいい、ナフタレン環に由来する質量スペクトルとは、127.27付近の質量スペクトルをいう。
TOF-SIMSによって測定を行った場合における測定結果の一例を図5に示す。図5では、77.16にベンゼン環に由来する質量スペクトル、127.27にナフタレン環に由来する質量スペクトルが検出されている。
なお、上記測定は、例えば、TOF-SIMS装置(ION-TOF社製)等を用いて行うことができる。
上記2θが26.4°の位置のピークは、グラファイトの結晶ピークであり、このような位置にピークが検出されないことで、被覆層を形成するカーボンがアモルファス構造であるということができる。
なお、上記測定は、例えば、X線回折装置(SmartLab Multipurpose、リガク社製)等を用いて行うことができる。
上記ホルムアルデヒドは不安定であるので、ホルムアルデヒド溶液であるホルマリンを用いることが好ましい。ホルマリンは、通常、ホルムアルデヒド及び水に加えて、安定剤として少量のメタノールが含有されている。本発明で用いられるホルムアルデヒドは、ホルムアルデヒド含量が明確なものであれば、ホルマリンであっても構わない。
また、ホルムアルデヒドには、その重合形態としてパラホルムアルデヒドがあり、こちらの方も原料として使用可能であるが、反応性が劣るため、好ましくは上記したホルマリンが用いられる。
分子量を小さくする方が好ましいので、置換基Rは、メチル基、エチル基、プロピル基などが好ましく、実際の化合物名としては、メチルアミン、エチルアミン、プロピルアミン等が好ましく使用できる。最も好ましいものは、分子量が一番小さなメチルアミンである。
このうち、反応性の高さから、1,5-ジヒドロキシナフタレン、2,6-ジヒドロキシナフタレンが好ましい。さらに1,5-ジヒドロキシナフタレンが最も反応性が高いので好ましい。
反応条件によっては、反応中に揮発などにより原料を失うので、最適な配合比は正確に上記比率とは限らないが、ジヒドロキシナフタレン1モルに対して、脂肪族アミンを0.8~1.2モル、ホルムアルデヒドを1.6~2.4モルの配合比の範囲で配合することが好ましい。
上記脂肪族アミンを0.8モル以上とすることにより、オキサジン環を十分に形成することができ、重合を好適に進めることができる。また1.2モル以下とすることにより、反応に必要なホルムアルデヒドを余計に消費することがないため、反応が順調に進み、所望のナフトキサジンを得ることができる。同様に、ホルムアルデヒドを1.6モル以上とすることで、オキサジン環を充分に形成することができ、重合を好適に進めることができる。また2.4モル以下とすることで、副反応の発生を低減できるため好ましい。
上記溶媒としては、例えば、メタノール、エタノール、イソプロパノール等のアルコール類、テトラヒドロフラン、ジオキサン、ジメチルホルムアミド、ジメチルアセトアミド、ジメチルスルホキシド、N-メチルピロリドン等の通常樹脂を溶解するために用いられる溶媒が挙げられる。
上記混合溶液中の溶媒の添加量は特に限定されないが、ジヒドロキシナフタレン、脂肪族アミン及びホルムアルデヒドを含む原料を100質量部とした場合は、通常300~20000質量部で配合することが好ましい。300質量部以上とすることで、溶質を充分に溶解することができるため、皮膜を形成した際に均一な皮膜とすることができ、20000質量部以下とすることで、被覆層の形成に必要な濃度を確保することができる。
上記反応は常温でも進行するが、反応時間を短縮することができるため、40℃以上に加温することが好ましい。加温を続けることで、作製されたオキサジン環が開き、重合が起こると分子量が増加し、いわゆるポリナフトキサジン樹脂となる。反応が進みすぎると溶液の粘度が増し被覆に適さないため注意を要する。
また、粒子への被覆を均一に行うためには、被覆反応時に粒子が分散された状態が好ましい。分散方法としては、撹拌、超音波、回転など公知の方法が利用できる。また、分散状態を改善するために、適当な分散剤を添加しても良い。
更に、反応工程を行った後に、熱風等により溶媒を乾燥除去することにより、樹脂を二酸化バナジウム粒子表面に均一に被覆してもよい。加熱乾燥方法についても特に制限はない。
これにより、前工程で被覆した樹脂が炭化されてアモルファスカーボンからなる被覆層とすることができる。
上記熱処理における温度は、150~350℃である。本発明では、低温で炭化が可能なナフトキサジン樹脂を用いていることから、更に低温でアモルファスカーボンとすることが可能となる。この場合の加熱温度の好ましい上限は250℃である。
上記加熱処理は、空気中で行っても良いし、窒素、アルゴンなどの不活性ガス中で行っても良い。熱処理温度が250℃以上の場合は、不活性ガス雰囲気の方がより好ましい。
また、本発明のカーボン被覆二酸化バナジウム粒子と、熱可塑性樹脂とを含有するフィルムは、優れたサーモクロミック性を有するフィルムとなる。このようなフィルムもまた本発明の1つである。
上記貼り付け用フィルムは、更に接着層を有していてもよい。上記接着層としては、特に限定されず、上記貼り付け用フィルムを窓ガラス等に接着し得る公知の接着剤を含む層を挙げることができる。
(二酸化バナジウム粒子の作製)
1.299gのメタバナジル酸アンモニウム(NH4VO3)を含有する50mlの水分散液に、10%のヒドラジン水溶液4mlをゆっくり滴下し、室温で1時間反応させた。その後、反応液をフッ素樹脂内筒付のステンレス製の耐圧容器に移し、270℃で48時間を反応させた。反応後に、粒子を遠心分離により溶液から分離し、3回洗浄した。その後、50℃で乾燥により粒子を回収した。
また、粒度分布計(日機装社製、マイクロトラックUAM-1)を用いて、得られた二酸化バナジウム粒子の粒子径(体積平均粒子径)を測定した。
1,5-ジヒドロキシナフタレン(東京化成社製)0.1gと、40%メチルアミン(和光純薬工業社製)0.05gと、37%ホルムアルデヒド水溶液(和光純薬工業社製)0.1gとをエタノールに順次溶解し、20gのエタノール混合溶液を作製した。
次に、得られた混合液に、二酸化バナジウム粒子0.2gを添加し、超音波槽にて4時間を処理した。溶液を濾過し、エタノールで3回洗浄した後に、50℃で3時間真空乾燥した。更に、上記乾燥した粒子を150℃で2時間加熱することにより、カーボン被覆二酸化バナジウム粒子を得た。
なお、核磁気共鳴スペクトル測定は、Varian Inova社製の1H-NMR(600MHz)を用いて行い、測定に際して、重水素ジメチルスルホキシドを使用し、スペクトル積算回数は256回、緩和時間は10秒とした。
また、GバンドとDバンドのピーク強度比は1.72であった。なお、レーザー光は530nmとした。
下記に示す方法で二酸化バナジウム粒子を作製した以外は実施例1と同様にしてカーボン被覆二酸化バナジウム粒子を作製した。なお、実施例1の「(被覆層の形成)」において、「150℃で2時間加熱」は、「200℃で2時間加熱」に変更した。
1.299gメタバナジル酸アンモニウム(NH4VO3)と0.0329gタングステン酸アンモニウムの水和物((NH4)10W12O41・5H2O)とを含有した50mlの水分散液に、10%のヒドラジン水溶液4.5mlをゆっくり滴下し、室温で1時間反応させた。その後、反応液をフッ素樹脂内筒付のステンレス製の耐圧容器に移し、270℃で48時間を反応させた。反応後に、粒子を遠心分離により溶液から分離し、3回洗浄した。その後、50℃で乾燥により二酸化バナジウム粒子を回収した。
蛍光X線による粒子の組成を測定したところ、二酸化バナジウム粒子中に約1モル%のタングステンが含まれていることが分かった。
実施例2で得られた二酸化バナジウム粒子を用い、下記の方法で被覆層を形成した以外は実施例1と同様にしてカーボン被覆二酸化バナジウム粒子を作製した。
1,5-ジヒドロキシナフタレン(東京化成社製)0.07gと、40%メチルアミン(和光純薬工業社製)0.03gと、37%ホルムアルデヒド水溶液(和光純薬工業社製)0.07gをエタノールに順次溶解し、20gのエタノール混合溶液を作製した。
次に、得られた混合液に、タングステンドープした二酸化バナジウム粒子0.2gを添加し、超音波槽にて6時間を処理した。溶液を濾過し、エタノールで3回洗浄した後に、50℃で3時間真空乾燥した。更に、上記乾燥した粒子を150℃で2時間加熱することにより、カーボン被覆二酸化バナジウム粒子を得た。
実施例2で得られた二酸化バナジウム粒子を用い、下記の方法で被覆層を形成した以外は実施例1と同様にしてカーボン被覆二酸化バナジウム粒子を作製した。
1,5-ジヒドロキシナフタレン(東京化成社製)0.5gと、40%メチルアミン(和光純薬工業社製)0.5gと、37%ホルムアルデヒド水溶液(和光純薬工業社製)0.25gをエタノールに順次溶解し、20gのエタノール混合溶液を作製した。
次に、得られた混合液に、タングステンドープした二酸化バナジウム粒子0.2gを添加し、超音波槽にて3時間を処理した。溶液を濾過し、エタノールで3回洗浄した後に、50℃で3時間真空乾燥した。更に、上記乾燥した粒子を300℃で2時間加熱することにより、カーボン被覆二酸化バナジウム粒子を得た。
下記に示す方法で二酸化バナジウム粒子を作製した以外は実施例1と同様にしてカーボン被覆二酸化バナジウム粒子を作製した。
1.299gメタバナジル酸アンモニウム(NH4VO3)と0.02gモリブデン酸アンモニウムの水和物((NH4)6Mo7O24・4H2O)とを含有した50mlの水分散液に、10%のヒドラジン水溶液4.5mlをゆっくり滴下し、室温で1時間反応させた。その後、反応液をフッ素樹脂内筒付のステンレス製の耐圧容器に移し、270℃で48時間を反応させた。反応後に、粒子を遠心分離により溶液から分離し、3回洗浄した。その後、50℃で乾燥により粒子を回収した。
蛍光X線による粒子の組成を測定したところ、粒子中に約1モル%のモリブデンが含まれていることが分かった。
実施例2で作製した二酸化バナジウム粒子について、「(被覆層の形成)」を行わずにそのまま使用した。
実施例2で得られた二酸化バナジウム粒子を用い、下記の方法でTiO2被覆層を形成させた。
実施例2で得られた二酸化バナジウム粒子1.0gを分散した無水エタノール100mlに、チタンイソプロポキシド(関東化学)3.0gを溶解した。次に、2.5gの水(アンモニア水でpHを9.0まで調整)を含有したエタノール溶液50mlを0.5ml/分の速度で上記分散液に滴下した。滴下終了後、更に1時間を撹拌し反応させた。その後、濾過し、洗浄乾燥工程を経て、TiO2被覆二酸化バナジウム粒子を得た。
実施例2で得られた二酸化バナジウム粒子を用い、下記の方法で被覆層を形成した以外は実施例1と同様にしてカーボン被覆二酸化バナジウム粒子を作製した。
1.5gのグルコースを溶解した70mlの水に、実施例2で得られた二酸化バナジウム粒子0.5gを添加し、撹拌によって粒子を分散させた。
その後、分散液をフッ化樹脂内筒付のステンレス耐圧容器に移し、180℃で8時間熱処理した。
反応後、室温まで冷却し、遠心分離、洗浄工程を経て、カーボン被覆二酸化バナジウム粒子を得た。
被覆処理した後に、熱処理条件を135℃で4時間にした以外は、実施例2と同様にしてカーボン被覆二酸化バナジウム粒子を作製した。
(1)被覆層膜厚測定(平均膜厚及びCV値)
被覆層の平均膜厚及びCV値を、透過顕微鏡(FE-TEM)を用いて評価した。
具体的には、FE-TEMにより任意の20個の粒子について被覆層の断面写真を撮影した後、得られた断面写真から、各粒子の異なる10箇所の膜厚をランダムに測定し、平均膜厚、標準偏差を算出した。得られた数値から膜厚の変動係数を算出した。
なお、表面被覆したカーボンと中のバナジウムとは原子量の差が大きいため、TEM像のコントラストの差から被覆層(カーボン層)の膜厚を見積もることができる。
実施例と比較例で得られた粒子のFE-SEM像を画像解析ソフト(WINROOF、三谷商事社製)を用いて解析することにより、平均粒子径を測定した。
また、800℃で2時間焼成した後の平均粒子径も測定した。
なお、実施例3で得られた二酸化バナジウム粒子について、焼成前(図2)と焼成後(図3)の粒子の電子顕微鏡写真を撮影した。これらを比較したところ、焼成前後で二酸化バナジウム粒子のサイズには変化が殆ど見られなかった。
一方で、被覆層を形成しない場合(比較例1)では、焼成後に粒子が粗大化している(図4)ことから、被覆層を形成することで、高温での粒子間の焼結防止効果を示すことが分かった。
得られた粒子の被覆層について、TOF-SIMS 5型装置(ION-TOF社製)を用いて、飛行時間型二次イオン質量分析法(Time-of-Flight Secondary Ion Mass Spectrometry,TOF-SIMS)によるベンゼン環に由来する質量スペクトル(77.12付近)、及び、ナフタレン環に由来する質量スペクトル(127.27付近)の確認を行った。なお、TOF-SIMS測定は、下記のような条件で行った。また、空気中や保管ケースに由来するコンタミをできるだけ避けるために、サンプル作製後に、シリコンウェハー保管用クリーンケースにて保管した。
一次イオン:209Bi+1
イオン電圧:25kV
イオン電流:1pA
質量範囲:1~300mass
分析エリア:500×500μm
チャージ防止:電子照射中和
ランダムラスタスキャン
X線回折装置(SmartLab Multipurpose、リガク社製)を用い、以下の測定条件で測定した。X線波長:CuKα1.54A、測定範囲:2θ=10~70°、スキャン速度:4°/min、ステップ:0.02°
得られた回折データについて、2θ=26.4°の位置にピークが検出されるか否かを確認した。
また、得られる回折データから半価幅を算出し、Scherrerの式をあてはめることで結晶子サイズを求めた。具体的には、2θ=27.86°の時の半価幅から算出した平均結晶子径を採用した。また、800℃で2時間焼成した後の平均結晶子径も測定した。
なお、一連の解析は、解析ソフト(PDXL2)を用いて行った。
得られた粒子の相転移時の吸熱量ΔH(mJ/mg)を、示差走査熱量計DSC(エスアイアイ・ナノテクノロジー社製「DSC6220」)を用い0℃~100℃までの温度範囲、昇温速度5℃/min、窒素雰囲気下にて測定した。
実施例及び比較例で得られた二酸化バナジウム粒子を空気雰囲気において、300℃で2時間熱処理し、熱処理後の粒子の相転移エネルギーの保持率(%)で評価した。
二酸化バナジウム粒子の耐久性は、その粒子を含有した合せガラス中間膜の促進耐候性試験より評価した。実施例及び比較例で得られた二酸化バナジウム粒子と、ブチラール樹脂と、可塑剤(トリエチレングリコールジ2-エチルヘキサノエート)とを含有した樹脂組成物をホットプレスによりフィルムを形成し、更に、そのフィルムを二枚のガラス板の間に真空ラミネーターにより挟むことにより、合せガラス中間膜を作製した。なお、フィルム中のブチラール樹脂と可塑剤の重量比は3:1であり、フィルム中の二酸化バナジウム粒子の濃度は0.05%であった。上記合わせガラス中間膜をウェザーメーター(スーパーキセノンSX-75、スガ試験機社製)を用いて、下記条件にて促進耐候性試験を行った。放射強度:180W/m2(300~400nm)、温度(BPT):63℃、散水:18分/120分の条件で500時間テストした。耐久性はテスト後の中間膜のサーモクロミック性の保持率で評価した。
なお、本発明で得られたカーボン被覆二酸化バナジウム粒子は、樹脂組成物、塗布膜、フィルム、合わせガラス用中間膜、合わせガラス、貼り付け用フィルム等に使用することができる。
Claims (11)
- 二酸化バナジウム粒子の表面に、アモルファスカーボンからなる被覆層を有するカーボン被覆二酸化バナジウム粒子であり、
前記アモルファスカーボンは、オキサジン樹脂が含有するカーボンに由来するものであり、
ラマンスペクトルで測定した場合のGバンドとDバンドのピーク強度比が1.5以上、
前記被覆層の平均膜厚が50nm以下、かつ、
前記被覆層の膜厚の変動係数(CV値)が7%以下である
ことを特徴とするカーボン被覆二酸化バナジウム粒子。 - 飛行時間型二次イオン質量分析法(TOF-SIMS)によって被覆層を測定した場合、ベンゼン環に由来する質量スペクトル、及び、ナフタレン環に由来する質量スペクトルのうち少なくとも1つが検出されることを特徴とする請求項1記載のカーボン被覆二酸化バナジウム粒子。
- X線回折法によって被覆層を測定した場合、2θが26.4°の位置にピークが検出されないことを特徴とする請求項1記載のカーボン被覆二酸化バナジウム粒子。
- オキサジン樹脂は、ナフトオキサジン樹脂であることを特徴とする請求項1、2又は3記載のカーボン被覆二酸化バナジウム粒子。
- 二酸化バナジウム粒子は、下記一般式(1)に示す構造を有することを特徴とする請求項1、2、3又は4記載のカーボン被覆二酸化バナジウム粒子。
V1-xMxO2 (1)
式(1)中、Mはタングステン、モリブデン、タンタル、ニオブ、クロム、鉄、ガリウム、アルミニウム、フッ素及びリンから選択される少なくとも1種の元素である。また、xは0~0.05の数値を表す。 - 請求項1、2、3、4又は5記載のカーボン被覆二酸化バナジウム粒子と、熱硬化性樹脂とを含有することを特徴とする樹脂組成物。
- 請求項6記載の樹脂組成物を用いて得られることを特徴とする塗布膜。
- 請求項1、2、3、4又は5記載のカーボン被覆二酸化バナジウム粒子と、熱可塑性樹脂とを含有することを特徴とするフィルム。
- 請求項8記載のフィルムを用いて得られることを特徴とする合わせガラス用中間膜。
- 請求項9記載の合わせガラス用中間膜が、2枚の透明板の間に挟まれていることを特徴とする合わせガラス。
- 請求項8記載のフィルムを用いることを特徴とする貼り付け用フィルム。