WO2014141912A1 - Plaque d'alliage d'aluminium pour fabrication, son procédé de production et feuille de brasage d'alliage d'aluminium - Google Patents

Plaque d'alliage d'aluminium pour fabrication, son procédé de production et feuille de brasage d'alliage d'aluminium Download PDF

Info

Publication number
WO2014141912A1
WO2014141912A1 PCT/JP2014/055229 JP2014055229W WO2014141912A1 WO 2014141912 A1 WO2014141912 A1 WO 2014141912A1 JP 2014055229 W JP2014055229 W JP 2014055229W WO 2014141912 A1 WO2014141912 A1 WO 2014141912A1
Authority
WO
WIPO (PCT)
Prior art keywords
aluminum alloy
less
brazing
ingot
plate
Prior art date
Application number
PCT/JP2014/055229
Other languages
English (en)
Japanese (ja)
Inventor
祐希 井上
孝宏 成島
田中　宏和
Original Assignee
株式会社Uacj
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社Uacj filed Critical 株式会社Uacj
Publication of WO2014141912A1 publication Critical patent/WO2014141912A1/fr

Abstract

La présente invention concerne une plaque d'alliage d'aluminium qui est destinée à la fabrication, a une aptitude au moulage supérieure, une aptitude au brasage, et une résistance au post-brasage, est favorablement utilisée comme échangeur de chaleur, et est caractérisée en ce qu'elle résulte de laminage à chaud et de laminage à froid d'un lingot d'alliage d'aluminium ayant une composition contenant 1,2-2,0% de Mn, 0,5-1,0% de Si, 0,10-0,20% de Ti, et V en tant qu'impureté limitée à pas plus de 80 ppm, le restant comprenant de l'Al et des impuretés inévitables, n'ayant pas plus de 1/m3 de composés intermétalliques grossiers ayant une taille générée (diamètre équivalent circulaire) d'au moins 4 mm, et n'ayant pas plus de 10/m3 de composés intermétalliques d'au moins 1 mm et inférieurs à 4 mm.
PCT/JP2014/055229 2013-03-11 2014-03-03 Plaque d'alliage d'aluminium pour fabrication, son procédé de production et feuille de brasage d'alliage d'aluminium WO2014141912A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013-047820 2013-03-11
JP2013047820A JP6236207B2 (ja) 2013-03-11 2013-03-11 成形加工用アルミニウム合金板とその製造方法、およびアルミニウム合金ブレージングシート

Publications (1)

Publication Number Publication Date
WO2014141912A1 true WO2014141912A1 (fr) 2014-09-18

Family

ID=51536585

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/055229 WO2014141912A1 (fr) 2013-03-11 2014-03-03 Plaque d'alliage d'aluminium pour fabrication, son procédé de production et feuille de brasage d'alliage d'aluminium

Country Status (2)

Country Link
JP (1) JP6236207B2 (fr)
WO (1) WO2014141912A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110106402A (zh) * 2019-05-24 2019-08-09 北京诺飞新能源科技有限责任公司 一种铝合金电池箱的生产工艺

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016198937A (ja) * 2015-04-09 2016-12-01 株式会社デンソー 炭素材料層含有複合材料および熱交換器

Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04289142A (ja) * 1991-03-18 1992-10-14 Nippon Light Metal Co Ltd 自然発色用アルミニウム合金及びその製造方法
JPH0623535A (ja) * 1991-05-24 1994-02-01 Kobe Steel Ltd ろう付け用アルミニウム合金複合材
JPH0741894A (ja) * 1993-07-26 1995-02-10 Nippon Light Metal Co Ltd 高耐食性熱交換器チューブ用アルミニウム合金材
JPH08246117A (ja) * 1995-03-06 1996-09-24 Furukawa Electric Co Ltd:The 高強度アルミニウムブレージングシートとその製造方法
JPH0978168A (ja) * 1995-09-18 1997-03-25 Kobe Steel Ltd アルミニウム合金板
JPH10259464A (ja) * 1997-03-19 1998-09-29 Mitsubishi Alum Co Ltd 成形加工用アルミニウム合金板の製造方法
JPH11293372A (ja) * 1998-04-07 1999-10-26 Sumitomo Light Metal Ind Ltd 熱交換器用高強度高耐食アルミニウム合金クラッド材
JP2000087165A (ja) * 1998-09-08 2000-03-28 Mitsubishi Alum Co Ltd 耐食性に優れた熱交換器用アルミニウム合金クラッド材
JP2005220425A (ja) * 2004-02-09 2005-08-18 Mitsubishi Alum Co Ltd 熱交換器に用いられるろう付用高強度アルミニウム合金材
JP2006265701A (ja) * 2005-03-25 2006-10-05 Kobe Steel Ltd 高温特性に優れたボトル缶用アルミニウム合金冷延板
JP2008516090A (ja) * 2004-10-13 2008-05-15 アルコア インコーポレイテッド 回復された高強度複層アルミニウムブレージングシート製品
JP2008188616A (ja) * 2007-02-02 2008-08-21 Mitsubishi Alum Co Ltd ろう付性と耐食性に優れた熱交換器管用アルミニウム合金ブレージングシートおよび耐食性に優れた熱交換器管
JP2008231555A (ja) * 2007-03-23 2008-10-02 Furukawa Sky Kk 熱交換器用高耐食アルミニウム合金複合材およびその製造方法
JP2011224656A (ja) * 2010-03-31 2011-11-10 Kobe Steel Ltd アルミニウム合金ブレージングシートおよび熱交換器

Patent Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04289142A (ja) * 1991-03-18 1992-10-14 Nippon Light Metal Co Ltd 自然発色用アルミニウム合金及びその製造方法
JPH0623535A (ja) * 1991-05-24 1994-02-01 Kobe Steel Ltd ろう付け用アルミニウム合金複合材
JPH0741894A (ja) * 1993-07-26 1995-02-10 Nippon Light Metal Co Ltd 高耐食性熱交換器チューブ用アルミニウム合金材
JPH08246117A (ja) * 1995-03-06 1996-09-24 Furukawa Electric Co Ltd:The 高強度アルミニウムブレージングシートとその製造方法
JPH0978168A (ja) * 1995-09-18 1997-03-25 Kobe Steel Ltd アルミニウム合金板
JPH10259464A (ja) * 1997-03-19 1998-09-29 Mitsubishi Alum Co Ltd 成形加工用アルミニウム合金板の製造方法
JPH11293372A (ja) * 1998-04-07 1999-10-26 Sumitomo Light Metal Ind Ltd 熱交換器用高強度高耐食アルミニウム合金クラッド材
JP2000087165A (ja) * 1998-09-08 2000-03-28 Mitsubishi Alum Co Ltd 耐食性に優れた熱交換器用アルミニウム合金クラッド材
JP2005220425A (ja) * 2004-02-09 2005-08-18 Mitsubishi Alum Co Ltd 熱交換器に用いられるろう付用高強度アルミニウム合金材
JP2008516090A (ja) * 2004-10-13 2008-05-15 アルコア インコーポレイテッド 回復された高強度複層アルミニウムブレージングシート製品
JP2006265701A (ja) * 2005-03-25 2006-10-05 Kobe Steel Ltd 高温特性に優れたボトル缶用アルミニウム合金冷延板
JP2008188616A (ja) * 2007-02-02 2008-08-21 Mitsubishi Alum Co Ltd ろう付性と耐食性に優れた熱交換器管用アルミニウム合金ブレージングシートおよび耐食性に優れた熱交換器管
JP2008231555A (ja) * 2007-03-23 2008-10-02 Furukawa Sky Kk 熱交換器用高耐食アルミニウム合金複合材およびその製造方法
JP2011224656A (ja) * 2010-03-31 2011-11-10 Kobe Steel Ltd アルミニウム合金ブレージングシートおよび熱交換器

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110106402A (zh) * 2019-05-24 2019-08-09 北京诺飞新能源科技有限责任公司 一种铝合金电池箱的生产工艺
CN110106402B (zh) * 2019-05-24 2020-06-09 北京诺飞新能源科技有限责任公司 一种铝合金电池箱的生产工艺

Also Published As

Publication number Publication date
JP6236207B2 (ja) 2017-11-22
JP2014173153A (ja) 2014-09-22

Similar Documents

Publication Publication Date Title
JP4166613B2 (ja) 熱交換器用アルミニウム合金フィン材および該フィン材を組付けてなる熱交換器
US7989087B2 (en) Brazing fin material for heat exchangers, heat exchanger, and method of manufacturing same
JP4547032B1 (ja) アルミニウム材のフラックスレスろう付け方法およびフラックスレスろう付け用アルミニウムクラッド材
JP6452626B2 (ja) アルミニウム合金クラッド材及びその製造方法、ならびに、当該アルミニウム合金クラッド材を用いた熱交換器及びその製造方法
JP4702797B2 (ja) 犠牲陽極材面のろう付けによる面接合性に優れたアルミニウム合金クラッド材の製造方法
JP6452627B2 (ja) アルミニウム合金クラッド材及びその製造方法、ならびに、当該アルミニウム合金クラッド材を用いた熱交換器及びその製造方法
JP4623729B2 (ja) 犠牲陽極材面のろう付けによる面接合性に優れたアルミニウム合金クラッド材および熱交換器
JP4993440B2 (ja) ろう付け性に優れた熱交換器用高強度アルミニウム合金クラッド材
WO2014065355A1 (fr) Brasage d'alliage d'aluminium destiné à une ailette, échangeur thermique, et procédé de fabrication d'un échangeur thermique
JP6726371B1 (ja) ろう付用アルミニウム合金板およびアルミニウムブレージングシート
JP6726370B1 (ja) フラックスフリーろう付用アルミニウムブレージングシート
JP2008240084A (ja) 熱交換器用アルミニウム合金クラッド材およびブレージングシート
JP4220410B2 (ja) 熱交換器用アルミニウム合金クラッド材
JP5836695B2 (ja) ろう付け後の強度及び耐食性に優れた熱交換器用アルミニウム合金フィン材
WO2016143119A1 (fr) Tôle à brasage présentant une excellente résistance à la corrosion après brasage
JP5629113B2 (ja) ろう付け性及び耐食性に優れたアルミニウム合金ブレージングシート、及びそれを用いた熱交換器
JP5578702B2 (ja) 熱交換器用アルミニウム合金フィン材および熱交換器
WO2017169633A1 (fr) Feuille de brasage en alliage d'aluminium
JP4220411B2 (ja) 熱交換器用アルミニウム合金クラッド材
JP6236207B2 (ja) 成形加工用アルミニウム合金板とその製造方法、およびアルミニウム合金ブレージングシート
JP5084490B2 (ja) アルミニウム合金クラッド材
JP2001170793A (ja) 造管性および耐食性に優れた熱交換器用高強度アルミニウム合金クラッド材
JP2010209426A (ja) アルミニウム合金ろう付け体およびその熱処理方法ならびに熱交換器
JP2017110266A (ja) ろう付け後の強度に優れたアルミニウム合金製ブレージングシート
JP6624417B2 (ja) ろう付け後の耐食性に優れるブレージングシート

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14765132

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14765132

Country of ref document: EP

Kind code of ref document: A1