WO2014126159A1 - Composition de résine pour une matière d'amortissement de vibration - Google Patents

Composition de résine pour une matière d'amortissement de vibration Download PDF

Info

Publication number
WO2014126159A1
WO2014126159A1 PCT/JP2014/053352 JP2014053352W WO2014126159A1 WO 2014126159 A1 WO2014126159 A1 WO 2014126159A1 JP 2014053352 W JP2014053352 W JP 2014053352W WO 2014126159 A1 WO2014126159 A1 WO 2014126159A1
Authority
WO
WIPO (PCT)
Prior art keywords
vibration damping
resin composition
damping material
parts
polymer
Prior art date
Application number
PCT/JP2014/053352
Other languages
English (en)
Japanese (ja)
Inventor
允彦 齊藤
Original Assignee
株式会社日本触媒
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2014023577A external-priority patent/JP2015034275A/ja
Application filed by 株式会社日本触媒 filed Critical 株式会社日本触媒
Priority claimed from JP2014025651A external-priority patent/JP2014177626A/ja
Publication of WO2014126159A1 publication Critical patent/WO2014126159A1/fr

Abstract

L'invention concerne une composition de résine pour une matière d'amortissement de vibration, qui peut présenter une excellente performance d'amortissement de vibration et peut être utilisée de façon appropriée dans des applications d'utilisation dans lesquelles les films de revêtement doivent avoir un effet d'amortissement de vibration. L'invention concerne une composition de résine pour une matière d'amortissement de vibration, qui comprend un polymère produit par polymérisation d'un composant monomère et d'un plastifiant, ladite composition de résine étant caractérisée en ce qu'elle est une composition aqueuse dans laquelle le polymère existe sous la forme d'une émulsion dans un milieu aqueux.
PCT/JP2014/053352 2013-02-14 2014-02-13 Composition de résine pour une matière d'amortissement de vibration WO2014126159A1 (fr)

Applications Claiming Priority (10)

Application Number Priority Date Filing Date Title
JP2013026961 2013-02-14
JP2013-026961 2013-02-14
JP2013026960 2013-02-14
JP2013-026960 2013-02-14
JP2013-145495 2013-07-11
JP2013145495 2013-07-11
JP2014-023577 2014-02-10
JP2014023577A JP2015034275A (ja) 2013-02-14 2014-02-10 振動減衰材用樹脂組成物
JP2014025651A JP2014177626A (ja) 2013-02-14 2014-02-13 振動減衰材用樹脂組成物
JP2014-025651 2014-02-13

Publications (1)

Publication Number Publication Date
WO2014126159A1 true WO2014126159A1 (fr) 2014-08-21

Family

ID=51354158

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/053352 WO2014126159A1 (fr) 2013-02-14 2014-02-13 Composition de résine pour une matière d'amortissement de vibration

Country Status (1)

Country Link
WO (1) WO2014126159A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018528310A (ja) * 2015-09-29 2018-09-27 ローム アンド ハース カンパニーＲｏｈｍ Ａｎｄ Ｈａａｓ Ｃｏｍｐａｎｙ 水溶性フィルム及び洗剤パケットにおけるその使用

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004503652A (ja) * 2000-06-14 2004-02-05 ザ　ダウ　ケミカル　カンパニー アスファルトエマルションに基づく減衰材
JP2006063190A (ja) * 2004-08-26 2006-03-09 Cemedine Co Ltd 塗布型制振材料組成物及び建築用複合板
JP2009179717A (ja) * 2008-01-31 2009-08-13 Jsr Corp 拘束型制振シート
WO2012010632A1 (fr) * 2010-07-22 2012-01-26 Basf Se Matière antibruit comprenant un polymère en émulsion stabilisé par un colloïde protecteur
JP2012126775A (ja) * 2010-12-14 2012-07-05 Nippon Shokubai Co Ltd 制振材用エマルション樹脂組成物及び制振材

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004503652A (ja) * 2000-06-14 2004-02-05 ザ　ダウ　ケミカル　カンパニー アスファルトエマルションに基づく減衰材
JP2006063190A (ja) * 2004-08-26 2006-03-09 Cemedine Co Ltd 塗布型制振材料組成物及び建築用複合板
JP2009179717A (ja) * 2008-01-31 2009-08-13 Jsr Corp 拘束型制振シート
WO2012010632A1 (fr) * 2010-07-22 2012-01-26 Basf Se Matière antibruit comprenant un polymère en émulsion stabilisé par un colloïde protecteur
JP2012126775A (ja) * 2010-12-14 2012-07-05 Nippon Shokubai Co Ltd 制振材用エマルション樹脂組成物及び制振材

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018528310A (ja) * 2015-09-29 2018-09-27 ローム アンド ハース カンパニーＲｏｈｍ Ａｎｄ Ｈａａｓ Ｃｏｍｐａｎｙ 水溶性フィルム及び洗剤パケットにおけるその使用

Similar Documents

Publication Publication Date Title
JP5485503B2 (ja) 制振材用エマルション
JP5660779B2 (ja) 制振材用エマルション
JP5030778B2 (ja) 制振材用エマルション
JP5030780B2 (ja) 制振材用エマルション
JP5172458B2 (ja) 制振材用エマルション組成物
WO2009139314A1 (fr) Composition d’émulsion pour matériau d’amortissement des vibrations
JP2010106168A (ja) 制振材用エマルション及び制振材配合物
JP5260187B2 (ja) 制振材用エマルション組成物及び制振材配合物
JP5685001B2 (ja) 制振材用エマルション及び制振材配合物
JP2014177626A (ja) 振動減衰材用樹脂組成物
JP5815233B2 (ja) 制振材用エマルション樹脂組成物及び制振材
JP5284914B2 (ja) 制振材用樹脂組成物
JP2009270064A (ja) 制振材用エマルション組成物
JP2015034275A (ja) 振動減衰材用樹脂組成物
JP5770432B2 (ja) 加熱乾燥用エマルション組成物、その製造方法及び制振材組成物
JP5685002B2 (ja) 制振材用エマルション及び制振材組成物
JP2016003252A (ja) 振動減衰材用樹脂組成物
JP6247347B2 (ja) 制振材用エマルション及び制振材配合物
WO2014126159A1 (fr) Composition de résine pour une matière d'amortissement de vibration
JP5977123B2 (ja) 制振材
JP6125799B2 (ja) 制振材用樹脂組成物
JP6243206B2 (ja) 振動減衰材用樹脂組成物
WO2014126212A1 (fr) Composition d'émulsion pour des matières d'amortissement de vibration
JP2014177624A (ja) 振動減衰材用樹脂組成物
JP2015063651A (ja) 制振材用エマルション組成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14751736

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14751736

Country of ref document: EP

Kind code of ref document: A1