WO2014115677A1 - パワーモジュール用基板、ヒートシンク付パワーモジュール用基板、ヒートシンク付パワーモジュール - Google Patents
パワーモジュール用基板、ヒートシンク付パワーモジュール用基板、ヒートシンク付パワーモジュール Download PDFInfo
- Publication number
- WO2014115677A1 WO2014115677A1 PCT/JP2014/050934 JP2014050934W WO2014115677A1 WO 2014115677 A1 WO2014115677 A1 WO 2014115677A1 JP 2014050934 W JP2014050934 W JP 2014050934W WO 2014115677 A1 WO2014115677 A1 WO 2014115677A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- power module
- heat sink
- copper
- aluminum
- Prior art date
Abstract
Description
本願は、2013年1月22日に日本に出願された特願2013-009199号及び2013年10月17日に日本に出願された特願2013-216783号について優先権を主張し、その内容をここに援用する。
このようなパワーモジュール用基板は、セラミックス基板の第二の面側に、熱伝導性の優れたヒートシンクが接合され、ヒートシンク付パワーモジュール用基板とされる。また、回路層上に、はんだ材を介してパワー素子としての半導体素子が搭載され、ヒートシンク付パワーモジュールとされる。
また、特許文献2には、セラミックス基板の下面に接合された2Nアルミニウム層からなる金属層を備えたパワーモジュール用基板が開示されている。
特許文献3には、セラミックス基板の下面に接合されたCu層からなる金属層を備えたパワーモジュール用基板が開示されている。
さらには、Alは変形抵抗が比較的低いため、パワーモジュールに冷熱サイクルが負荷された場合に、パワーモジュール用基板と放熱板との間に生じる熱応力によって、はんだにクラックが生じ、接合信頼性が低下したり、熱抵抗が上昇したりする問題もあった。
しかしながら、Cuは上記のように比較的変形抵抗が高いため、冷熱サイクルが負荷された際にセラミックス基板と金属層との間に生じる熱応力により、セラミックス基板に割れが発生する場合があった。
さらに、セラミックス基板の第二の面に比較的変形抵抗が小さい第一アルミニウム層が接合されているので、冷熱サイクルが負荷されてもセラミックス基板と第一銅層との間に生じる熱応力を第一アルミニウム層で吸収してセラミックス基板に割れが生じることを抑制できる。
そして、第一アルミニウム層と第一銅層とが、固相拡散接合によって接合されているので、第一アルミニウム層と第一銅層との接合信頼性を向上させることが可能である。また、冷熱サイクルが負荷された場合に、第一アルミニウム層と第一銅層との間に剥離が生じることが抑制され、金属層の熱伝導性を維持することができる。
この構成では、回路層が第二銅層を有しており、この第二銅層の上に半導体素子が搭載された場合には、半導体素子から発生する熱をパワーモジュール用基板側へ伝達する際に、回路層の第二銅層で面方向に拡げて効率的に放散することができる。
さらに、セラミックス基板の第一の面に、比較的変形抵抗の小さい第二アルミニウム層が形成されており、冷熱サイクルが負荷された場合にセラミックス基板と回路層との熱膨張係数の差に起因して発生する熱応力を第二アルミニウム層が吸収するので、セラミックス基板に割れが発生することを抑制できる。また、第二アルミニウム層の一方側には、比較的変形抵抗の大きい第二銅層が形成されているので、パワーサイクルが負荷された場合に、回路層の変形を抑制することができる。
また、第二アルミニウム層と第二銅層とは、固相拡散接合によって接合されているので、冷熱サイクルが負荷された場合に、第二アルミニウム層と第二銅層との間に剥離が生じることが抑制され、回路層の熱伝導性及び導電性を維持することができる。
なお、ここで、第二アルミニウム層の一方側とは、セラミックス基板と接合されていない面側のことである。
本発明のヒートシンク付パワーモジュール用基板によれば、パワーモジュール用基板の第一銅層がヒートシンクに接合されるので、金属層にNiめっきを形成することなく金属層とヒートシンクとをはんだによって接合できる。また、金属層とヒートシンクとをはんだによって接合すると、比較的変形抵抗が高い第一銅層とヒートシンクとを接合することになるので、冷熱サイクル負荷時において、はんだにクラックが発生することを抑制し、接合信頼性の低下や熱抵抗の上昇を抑えることができる。さらに、セラミックス基板の第二の面に比較的変形抵抗が小さい第一アルミニウム層が接合されているので、冷熱サイクルが負荷された際に熱応力を第一アルミニウム層で吸収でき、セラミックス基板に割れが生じることを抑制できる。
この場合、金属層の第一銅層と、CuまたはCu合金で構成されたヒートシンクとをはんだによって良好に接合することができる。また、ヒートシンクが熱伝導性の良好なCuまたはCu合金で構成されているので、パワーモジュール用基板からの熱をヒートシンク側に効率的に放散できる。
AlまたはAl合金で構成されたヒートシンクにNiめっきが形成されている場合には、上述のパワーモジュール用基板とヒートシンクとを良好にはんだ接合できる。
この場合、上述のパワーモジュール用基板を備えているので、冷熱サイクルが負荷されても、金属層とヒートシンクを接合するはんだにクラックが生じることを抑制し、接合信頼性の低下や熱抵抗の上昇を抑えることができ、かつセラミックス基板に割れが生じることを抑制できる。
図1に、本発明の実施形態であるヒートシンク付パワーモジュール1、ヒートシンク付パワーモジュール用基板30、パワーモジュール用基板10を示す。
ヒートシンク付パワーモジュール1は、ヒートシンク付パワーモジュール用基板30と、このヒートシンク付パワーモジュール用基板30の一方側(図1において上側)にはんだ層2を介して接合された半導体素子3と、を備えている。
半導体素子3は、半導体を備えた電子部品であり、必要とされる機能に応じて種々の半導体素子が選択される。本実施形態では、IGBT素子とされている。
第一アルミニウム層13Aは、アルミニウム板がセラミックス基板11の第二の面に接合されることにより形成されている。本実施形態においては、第一アルミニウム層13Aは、純度が99.99%以上のアルミニウム(いわゆる4Nアルミニウム)の圧延板からなるアルミニウム板がセラミックス基板11に接合されることにより形成されている。ここで、接合されるアルミニウム板の厚さは0.2mm以上3.0mm以下に設定されていることが好ましい。
そして、これらの第一アルミニウム層13Aと第一銅層13Bとの界面には、図2に示すように、金属間化合物層13Cが形成されている。
金属間化合物層13Cは、CuとAlからなる金属間化合物で構成されており、本実施形態では、複数の金属間化合物が接合界面に沿って積層した構造とされている。ここで、金属間化合物層13Cの厚さtaは、1μm以上80μm以下の範囲内、好ましくは、5μm以上80μm以下の範囲内に設定されている。
本実施形態では、図2に示すように、3種の金属間化合物が積層された構造とされており、第一アルミニウム層13A側から第一銅層13B側に向けて順に、θ相16a、η2相17a、ζ2相18aとされている。
さらに、本実施形態では、第一銅層13Bの平均結晶粒径が50μm以上200μm以下の範囲内とされ、第一アルミニウム層13Aの平均結晶粒径が500μm以上とされている。
第二アルミニウム層12Aは、アルミニウム板がセラミックス基板11の第一の面に接合されることにより形成されている。本実施形態においては、第二アルミニウム層12Aは、純度が99.99%以上のアルミニウム(いわゆる4Nアルミニウム)の圧延板からなるアルミニウム板がセラミックス基板11に接合されることにより形成されている。
ここで、接合されるアルミニウム板の厚さは0.2mm以上3.0mm以下に設定されていることが好ましい。
そして、これらの第二アルミニウム層12Aと第二銅層12Bとの界面には、図3に示すように、金属間化合物層12Cが形成されている。
この金属間化合物層12Cは、CuとAlからなる金属間化合物で構成されており、本実施形態では、複数の金属間化合物が接合界面に沿って積層した構造とされている。ここで、この金属間化合物層12Cの厚さtbは、1μm以上80μm以下の範囲内、好ましくは、5μm以上80μm以下の範囲内に設定されている。
本実施形態では、図3に示すように、3種の金属間化合物が積層された構造とされており、第二アルミニウム層12A側から第二銅層12B側に向けて順に、θ相16b、η2相17b、ζ2相18bとされている(図12)。
さらに、本実施形態では、第二銅層12Bの平均結晶粒径が50μm以上200μm以下の範囲内とされ、第二アルミニウム層12Aの平均結晶粒径が500μm以上とされている。
まず、図4に示すように、セラミックス基板11の第一の面、第二の面に、Al-Si系のろう材(図示なし)を介してアルミニウム板22A、アルミニウム板23Aを積層する。そして、加圧・加熱後冷却することによって、セラミックス基板11とアルミニウム板22A、アルミニウム板23Aを接合し、セラミックス基板11に第二アルミニウム層12A及び第一アルミニウム層13Aを形成する(アルミニウム層形成工程S11)。なお、このろう付けの温度は、640℃~650℃に設定されている。
なお、真空加熱の好ましい加熱温度は、AlとCuの共晶温度-5℃以上、共晶温度未満の範囲とされている。
こうして、回路層12と金属層13が形成され、本実施形態に係るパワーモジュール用基板10が得られる。
次いで、ヒートシンク40(放熱板31)の他方側に(図5において下側)、グリース43を介してヒートシンク40(冷却部41)を配設する(ヒートシンク(冷却部)配設工程S14)。本実施形態においては、ネジ44によって放熱板31と冷却部41とを接合している。こうして、ヒートシンク付パワーモジュール用基板30が得られる。
最後に、ヒートシンク付パワーモジュール用基板30の回路層12の一方の面(図5において上面)に、はんだによって半導体素子3を接合する(半導体素子接合工程S15)。
以上のようにして、本実施形態に係るヒートシンク付パワーモジュール1が得られる。
そして、金属層13の第一アルミニウム層13Aと第一銅層13Bとが、固相拡散接合によって接合されているので、第一アルミニウム層13Aと第一銅層13Bとの接合信頼性を向上させることが可能であり、冷熱サイクルが負荷された場合に、第一アルミニウム層13Aと第一銅層13Bとの間に剥離が生じることが抑制され、金属層13の熱伝導性を維持することができる。
また、セラミックス基板11の第一の面(上面)に、比較的変形抵抗の小さい第二アルミニウム層12Aが形成されているので、冷熱サイクルが負荷された場合にセラミックス基板11と回路層12との熱膨張係数の差に起因して発生する熱応力を第二アルミニウム層12Aが吸収し、セラミックス基板11に割れが発生することを抑制できる。
また、第二アルミニウム層12Aと第二銅層12Bとが、固相拡散接合によって接合されているので、第二アルミニウム層12Aと第二銅層12Bとの接合信頼性を向上させることが可能であり、冷熱サイクルが負荷された場合に、第二アルミニウム層12Aと第二銅層12Bとの間に剥離が生じることが抑制され、回路層12の熱伝導性及び導電性を維持することができる。
また、第一銅層13B、第二銅層12B中のCuと、第一アルミニウム層13A、第二アルミニウム層12A中のAlとが、それぞれ相互拡散することにより、第一銅層13B、第二銅層12B側から、第一アルミニウム層13A、第二アルミニウム層12A側に向けてそれぞれの組成に適した金属間化合物が層状に形成されていることから、接合界面の特性を安定させることができる。
具体的には、金属間化合物層13C、12Cは、第一アルミニウム層13A、第二アルミニウム層12A側から第一銅層13B、第二銅層12B側に向けて順に、θ相16a、16b、η2相17a、17b、ζ2相18a、18bの3種の金属間化合物がそれぞれ積層しているので、金属間化合物層13C、12C内部における体積変動が小さくなり、内部歪みが抑えられることになる。
すなわち、固相拡散しなかった場合、例えば、液相が形成された場合には、金属間化合物が必要以上に発生し、金属間化合物層はその体積の変動が大きくなり、金属間化合物層に内部歪みが生じる。しかし、固相拡散した場合には、脆い金属間化合物層が大きく成長せずに、金属間化合物が層状に形成されるため、その内部歪みが抑えられる。
また、ヒートシンクの放熱板と冷却部とをネジで固定する場合について説明したが、放熱板と冷却部との接合方法に限定はなく、例えば固相拡散接合により接合する構成としても良い。
また、上記の実施形態では、純度99.99%の純アルミニウムの圧延板によって第一アルミニウム層と第二アルミニウム層が構成される場合について説明したが、これに限定されることはなく、純度99%のアルミニウム(2Nアルミニウム)やアルミニウム合金等であっても良い。
また、上記の実施形態では、回路層が第二アルミニウム層と第二銅層とを有する場合について説明したが、これに限定されるものではなく、例えば第二アルミニウム層のみで回路層を構成したり、第二銅層のみで回路層を構成したりしても良い。
例えば図7のパワーモジュール用基板110に示すように、回路層112が、セラミックス基板11の第一の面に形成された第二アルミニウム層112Aと、この第二アルミニウム層112Aの一方側に接合された第二銅層112Bとを備え、この第二銅層112Bは、半導体素子などが接合されるダイパッド152と、外部端子として用いられるリード部153とを有する銅板からなる構成とされても良い。このパワーモジュール用基板110では、ダイパッド152と第二アルミニウム層112Aとが固相拡散接合されている。
ここで、第二アルミニウム層112Aの厚さは、0.1mm以上1.0mm以下とされていることが好ましい。また、第二銅層112Bの厚さは、0.1mm以上6.0mm以下とされていることが好ましい。
また、図7に示すヒートシンク付パワーモジュール用基板130では、ヒートシンク140が、パワーモジュール用基板110の金属層13側に、はんだ層32を介して接合されている。
具体的には、アルミニウム層(第一アルミニウム層、第二アルミニウム層)と銅層(第一銅層、第二銅層)との接合界面において、アルミニウム層(第一アルミニウム層、第二アルミニウム層)側から銅層(第一銅層、第二銅層)側に向けて順に、アルミニウムの比率が低くなるように複数のCu及びAlからなる金属間化合物が積層されていても良い。
以下のようにして、本発明例1~6、比較例1、比較例2となるパワーモジュールを作製した。
本発明例1及び本発明例5については、AlNで構成されたセラミックス基板(厚さ:0.635mm)の第一の面にアルミニウム板(厚さ:0.4mm)をAl-Si系ろう材を介して接合し回路層を形成した。本発明例1では4N-Alのアルミニウム板を用い、本発明例2では2N-Alのアルミニウム板を用いた。次に、セラミックス基板の第二の面に4N-Alのアルミニウム板(厚さ:0.2mm)をAl-Si系ろう材を介して接合して第一アルミニウム層を形成した。さらに、Cu(無酸素銅)で構成された銅板を第一アルミニウム層に固相拡散接合し、金属層を形成した。このようにして得られたパワーモジュール用基板とヒートシンクをSn-Sbはんだによって接合した。なお、本発明例1はヒートシンクが無酸素銅から構成されており、本発明例5ではNiメッキを施したAl合金(A6063)から構成されたヒートシンクを用いた。そして、回路層と半導体素子をはんだによって接合し、本発明例1及び本発明例5となるヒートシンク付パワーモジュールを作製した。
なお、上記の固相拡散接合は、真空加熱炉内の圧力が、10-6Pa以上、10-3Pa以下の範囲内で行った。
比較例2については、AlNで構成されたセラミックス基板(厚さ:0.635mm)の第一の面及び第二の面に無酸素銅で構成された銅板(厚さ:0.4mm)をAg-Cu-Ti系ろう材を用いた活性金属ろう付け法によって接合し、回路層及び金属層が形成されたパワーモジュール用基板を作製した。さらに、パワーモジュール用基板に無酸素銅で構成されたヒートシンクをSn-Sbはんだによって接合した。そして、回路層と半導体素子をはんだによって接合し、比較例2となるヒートシンク付パワーモジュールを得た。
なお、半導体素子は、IGBT素子とし、12.5mm×9.5mm、厚さ0.25mmのものを使用した。
得られたヒートシンク付パワーモジュールに対して、以下の評価試験を行った。
冷熱サイクル試験は、冷熱衝撃試験機エスペック社製TSB-51を使用し、パワーモジュールに対して、液相(フロリナート)で、-40℃×5分及び125℃×5分の繰り返しを3000サイクル実施した。
本発明例1~6、比較例1、比較例2について、冷熱サイクル試験後のパワーモジュールに対し、セラミックス基板と金属層との界面の接合率について超音波探傷装置を用いて評価し、以下の式から算出した。さらに、本発明例1及び本発明例2については、冷熱サイクル試験後のパワーモジュールに対して、セラミックス基板と回路層との界面の接合率を評価した。
ここで、初期接合面積とは、接合前における接合すべき面積、すなわち本実施例では金属層の面積とした。また、セラミックス基板と回路層との界面の接合率を評価する際には回路層の面積を初期接合面積とした。超音波探傷像において剥離は接合部内の白色部で示されることから、この白色部の面積を剥離面積とした。なお、セラミックス基板、金属層、及びはんだ層にクラックが生じた場合、このクラックは超音波探傷像において白色部で示され、クラックも剥離面積として評価されることになる。
(接合率(%))={(初期接合面積)-(剥離面積)}/(初期接合面積)(熱抵抗評価)
熱抵抗は、次のようにして測定した。半導体素子としてヒータチップを用い、100Wの電力で加熱し、熱電対を用いてヒータチップの温度を実測した。また、ヒートシンクを流通する冷却媒体(エチレングリコール:水=9:1)の温度を実測した。そして、ヒータチップの温度と冷却媒体の温度差を電力で割った値を熱抵抗とし、冷熱サイクル試験後の熱抵抗上昇率を求めた。
本発明例2、本発明例1については、パワーサイクル試験を行った。パワーサイクル試験として、冷却部(冷却器)中の冷却水温度、流量を一定とした状態で、IGBT素子への通電を、通電(ON)で素子表面温度140℃、非通電(OFF)で素子表面温度80℃となる1サイクルを10秒毎に繰り返すようにして調整し、これを10万回繰り返すパワーサイクル試験を実施した。
このパワーサイクル試験前後における熱抵抗を測定し、熱抵抗の上昇率を求めた。
上記の評価結果を、表1、表2に示す。
一方、比較例1では、金属層が4N-Alのみで構成されているため、冷熱サイクル試験後のセラミックス基板と金属層の接合率は良好であるが、熱抵抗の上昇率が本発明例1~6に比べ増大した。また、比較例2では、金属層が無酸素銅のみで構成されているため、冷熱サイクル試験後のセラミックス基板に割れが発生した。
また、表2に示すように、回路層が第二アルミニウム層と第二銅層とを有する本発明例2は、回路層が4N-Alのみで構成されている本発明例1と比較して、パワーサイクル後の熱抵上昇率を低くできることが確認された。
3 半導体素子
10、110 パワーモジュール用基板
11 セラミックス基板
12、112 回路層
12A、112A 第二アルミニウム層
12B、112B 第二銅層
13 金属層
13A 第一アルミニウム層
13B 第一銅層
30、130 ヒートシンク付パワーモジュール用基板
31 放熱板(ヒートシンク)
40、140 ヒートシンク
41 冷却部(ヒートシンク)
Claims (6)
- セラミックス基板の一方の面に形成された回路層と、他方の面に形成された金属層と、を備えたパワーモジュール用基板であって、
前記金属層は、前記セラミックス基板の他方の面に接合された第一アルミニウム層と、この第一アルミニウム層に固相拡散接合された第一銅層と、を有していることを特徴とするパワーモジュール用基板。 - 前記回路層は、前記セラミックス基板の一方の面に接合された第二アルミニウム層と、この第二アルミニウム層に固相拡散接合された第二銅層と、を有している請求項1に記載のパワーモジュール用基板。
- 請求項1または請求項2に記載のパワーモジュール用基板と、ヒートシンクとを有し、
前記第一銅層と前記ヒートシンクとが接合されているヒートシンク付パワーモジュール用基板。 - 前記ヒートシンクがCuまたはCu合金で構成され、前記パワーモジュール用基板と前記ヒートシンクとがはんだによって接合されている請求項3に記載のヒートシンク付パワーモジュール用基板。
- 前記ヒートシンクは、Niめっきが形成されたAlまたはAl合金で構成され、前記パワーモジュール用基板と前記ヒートシンクとがはんだによって接合されている請求項3に記載のヒートシンク付パワーモジュール用基板。
- 請求項3から請求項5のいずれか一項に記載のヒートシンク付パワーモジュール用基板と、前記回路層の一方の面に接合された半導体素子と、を備えるヒートシンク付パワーモジュール。