WO2014115057A1 - Amélioration de la performance de cascades magnétocaloriques par agencement de matériau optimisé - Google Patents

Amélioration de la performance de cascades magnétocaloriques par agencement de matériau optimisé Download PDF

Info

Publication number
WO2014115057A1
WO2014115057A1 PCT/IB2014/058251 IB2014058251W WO2014115057A1 WO 2014115057 A1 WO2014115057 A1 WO 2014115057A1 IB 2014058251 W IB2014058251 W IB 2014058251W WO 2014115057 A1 WO2014115057 A1 WO 2014115057A1
Authority
WO
WIPO (PCT)
Prior art keywords
magnetocaloric
different
materials
cascade
curie temperature
Prior art date
Application number
PCT/IB2014/058251
Other languages
English (en)
Inventor
Colman Carroll
Olaf Rogge
Bernard Hendrik Reesink
Andrew Rowe
Danny ARNOLD
Armando Tura
Original Assignee
Basf Se
Basf (China) Company Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se, Basf (China) Company Limited filed Critical Basf Se
Priority to EP14743598.6A priority Critical patent/EP2948962A4/fr
Priority to JP2015554278A priority patent/JP6285463B2/ja
Priority to KR1020157022734A priority patent/KR20150108913A/ko
Priority to BR112015017315A priority patent/BR112015017315A2/pt
Priority to CN201480004706.3A priority patent/CN104919544B/zh
Publication of WO2014115057A1 publication Critical patent/WO2014115057A1/fr

Abstract

L'invention concerne une cascade magnétocalorique contenant au moins trois différents matériaux magnétocaloriques présentant différentes températures de Curie et disposés les uns à la suite des autres par température de Curie décroissante, aucun des différents matériaux magnétocaloriques présentant différentes températures de Curie ne présentant de performance de couche Lp supérieure à celle du matériau magnétocalorique présentant la température de Curie la plus élevée, et au moins un des différents matériaux magnétocaloriques présentant différentes températures de Curie présentant une performance de couche Lp inférieure à celle du matériau magnétocalorique présentant la température de Curie la plus élevée, la performance Lp d'un matériau magnétocalorique particulier étant calculée en fonction de la formule (I) : Lp = m * dTad,max avec dTad,max : changement de température adiabatique maximum que le matériau magnétocalorique particulier subit lorsqu'il est magnétisé d'un faible champ magnétique à un champ magnétique élevé pendant un cyclage magnétocalorique, m : masse du matériau magnétocalorique particulier contenu dans la cascade magnétocalorique.
PCT/IB2014/058251 2013-01-24 2014-01-14 Amélioration de la performance de cascades magnétocaloriques par agencement de matériau optimisé WO2014115057A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
EP14743598.6A EP2948962A4 (fr) 2013-01-24 2014-01-14 Amélioration de la performance de cascades magnétocaloriques par agencement de matériau optimisé
JP2015554278A JP6285463B2 (ja) 2013-01-24 2014-01-14 材料配列の最適化による磁気熱量カスケードの性能改良
KR1020157022734A KR20150108913A (ko) 2013-01-24 2014-01-14 최적화된 재료 배치를 통한 자기열량 캐스케이드의 성능 향상
BR112015017315A BR112015017315A2 (pt) 2013-01-24 2014-01-14 cascata magnetocalórica, processo para produzir cascatas magnetocalóricas, uso de uma cascata magnetocalórica, e, sistemas de refrigeração, unidades de controle de clima e bombas de calor
CN201480004706.3A CN104919544B (zh) 2013-01-24 2014-01-14 通过优化材料排列而改善磁热级联的性能

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP13152519 2013-01-24
EP13152519.8 2013-01-24

Publications (1)

Publication Number Publication Date
WO2014115057A1 true WO2014115057A1 (fr) 2014-07-31

Family

ID=47603441

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2014/058251 WO2014115057A1 (fr) 2013-01-24 2014-01-14 Amélioration de la performance de cascades magnétocaloriques par agencement de matériau optimisé

Country Status (6)

Country Link
EP (1) EP2948962A4 (fr)
JP (1) JP6285463B2 (fr)
KR (1) KR20150108913A (fr)
CN (1) CN104919544B (fr)
BR (1) BR112015017315A2 (fr)
WO (1) WO2014115057A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016096509A1 (fr) 2014-12-18 2016-06-23 Basf Se Cascade magnétocalorique et procédé de fabrication d'une cascade magnétocalorique
WO2016096512A1 (fr) * 2014-12-18 2016-06-23 Basf Se Cascade magnétocalorique et procédé de fabrication d'une cascade magnétocalorique
WO2017002851A1 (fr) * 2015-06-29 2017-01-05 山陽特殊製鋼株式会社 Matériau de cible de pulvérisation cathodique
JP2017014612A (ja) * 2015-06-29 2017-01-19 山陽特殊製鋼株式会社 スパッタリングターゲット材
JP2017067767A (ja) * 2015-10-01 2017-04-06 ジーカー ドクター ジーベルト ウント キューン ゲーエムベーハー ウント コー． カーゲー 温度較正器および温度較正器の冷却および加熱方法
JP2018112360A (ja) * 2017-01-12 2018-07-19 株式会社デンソー 磁気熱量効果素子および熱磁気サイクル装置
US11018488B2 (en) 2015-12-16 2021-05-25 Newsouth Innovations Pty Limited Climate responsive transmission lines

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104457016A (zh) * 2014-11-19 2015-03-25 上海电机学院 超导磁热超低温制冷方法及其装置
WO2017072334A1 (fr) * 2015-10-30 2017-05-04 Basf Se Matériaux magnétocaloriques comprenant du manganèse, du fer, du silicium, du phosphore et de l'azote
EP3839379A3 (fr) * 2016-11-02 2021-06-30 Ngk Insulators, Ltd. Élément magnétique pour réfrigérateur magnétique
JP2018080853A (ja) * 2016-11-14 2018-05-24 サンデンホールディングス株式会社 磁気ヒートポンプ装置
JP6885169B2 (ja) * 2017-04-07 2021-06-09 株式会社デンソー 磁気熱量効果材料、複合材料、カスケード、磁気ヒートポンプシステム、及び磁気熱量効果材料の製造方法
CN107120865A (zh) * 2017-05-12 2017-09-01 卢振华 一种磁热泵装置
CN112863846B (zh) * 2021-01-08 2022-12-09 哈尔滨工业大学 一种磁制冷机回热器的磁相变材料的制备方法及磁制冷循环系统
CN114634359B (zh) * 2022-03-01 2023-01-31 中国科学院赣江创新研究院 一种磁制冷微球及其制备方法与应用

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1997025292A1 (fr) * 1996-01-12 1997-07-17 Empresa Nacional Hidroelectrica Del Ribagorzana, S.A. (Enher) Ceramiques magnetiques et leur application comme refrigerants magnetiques
US20040250550A1 (en) 2001-07-31 2004-12-16 Stichting Voor De Technische Wetenschappen Material for magnetic refrigeration preparation and application
CN101105996A (zh) * 2007-05-18 2008-01-16 北京科技大学 一种高温低磁场大磁熵材料化合物及其制备方法
WO2010121977A1 (fr) * 2009-04-24 2010-10-28 Leibniz-Institut Für Festkörper- Und Werkstoffforschung Dresden E.V. Matériau allié magnétique et son procédé de fabrication
US20110030939A1 (en) 2009-08-10 2011-02-10 Basf Se Heat exchanger beds composed of thermomagnetic material

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004068512A1 (fr) * 2003-01-29 2004-08-12 Stichting Voor De Technische Wetenschappen Materiau magnetique a pouvoir refrigerant, procede de fabrication et methode d'utilisation
CN100386400C (zh) * 2006-05-19 2008-05-07 北京工业大学 具有层状结构的多组元复合室温磁致冷工质的制备方法
US8104293B2 (en) * 2007-06-19 2012-01-31 General Electric Company Magneto-caloric cooling device and method of operation
FR2936364B1 (fr) * 2008-09-25 2010-10-15 Cooltech Applications Element magnetocalorique
CN101831278A (zh) * 2010-02-09 2010-09-15 江苏大学 层状复合磁致冷工质的制备方法
GB2482884B (en) * 2010-08-18 2014-04-30 Vacuumschmelze Gmbh & Co Kg Working component for magnetic heat exchange and method of producing a working component for magnetic refrigeration
JP2013189543A (ja) * 2012-03-13 2013-09-26 Toyama Univ 磁気冷凍材料、蓄冷材料及びそれを用いた冷凍システム

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1997025292A1 (fr) * 1996-01-12 1997-07-17 Empresa Nacional Hidroelectrica Del Ribagorzana, S.A. (Enher) Ceramiques magnetiques et leur application comme refrigerants magnetiques
US20040250550A1 (en) 2001-07-31 2004-12-16 Stichting Voor De Technische Wetenschappen Material for magnetic refrigeration preparation and application
CN101105996A (zh) * 2007-05-18 2008-01-16 北京科技大学 一种高温低磁场大磁熵材料化合物及其制备方法
WO2010121977A1 (fr) * 2009-04-24 2010-10-28 Leibniz-Institut Für Festkörper- Und Werkstoffforschung Dresden E.V. Matériau allié magnétique et son procédé de fabrication
US20110030939A1 (en) 2009-08-10 2011-02-10 Basf Se Heat exchanger beds composed of thermomagnetic material
US20110094243A1 (en) * 2009-08-10 2011-04-28 Basf Se Magneto-caloric heat pump with the use of a cascade of magneto-caloric materials

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP2948962A4 *

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016096509A1 (fr) 2014-12-18 2016-06-23 Basf Se Cascade magnétocalorique et procédé de fabrication d'une cascade magnétocalorique
WO2016096512A1 (fr) * 2014-12-18 2016-06-23 Basf Se Cascade magnétocalorique et procédé de fabrication d'une cascade magnétocalorique
CN107112410A (zh) * 2014-12-18 2017-08-29 巴斯夫欧洲公司 磁热级联和制造磁热级联的方法
CN107112103A (zh) * 2014-12-18 2017-08-29 巴斯夫欧洲公司 磁热级联和制造磁热级联的方法
US10229775B2 (en) 2014-12-18 2019-03-12 Basf Se Magnetocaloric cascade and method for fabricating a magnetocaloric cascade
WO2017002851A1 (fr) * 2015-06-29 2017-01-05 山陽特殊製鋼株式会社 Matériau de cible de pulvérisation cathodique
JP2017014612A (ja) * 2015-06-29 2017-01-19 山陽特殊製鋼株式会社 スパッタリングターゲット材
JP2017067767A (ja) * 2015-10-01 2017-04-06 ジーカー ドクター ジーベルト ウント キューン ゲーエムベーハー ウント コー． カーゲー 温度較正器および温度較正器の冷却および加熱方法
US10209142B2 (en) 2015-10-01 2019-02-19 SIKA Dr. Siebert & Kühn GmbH & Co. KG Temperature calibrator
US11018488B2 (en) 2015-12-16 2021-05-25 Newsouth Innovations Pty Limited Climate responsive transmission lines
JP2018112360A (ja) * 2017-01-12 2018-07-19 株式会社デンソー 磁気熱量効果素子および熱磁気サイクル装置

Also Published As

Publication number Publication date
JP2016514360A (ja) 2016-05-19
CN104919544A (zh) 2015-09-16
KR20150108913A (ko) 2015-09-30
BR112015017315A2 (pt) 2017-07-11
JP6285463B2 (ja) 2018-02-28
EP2948962A4 (fr) 2016-11-02
CN104919544B (zh) 2018-09-28
EP2948962A1 (fr) 2015-12-02

Similar Documents

Publication Publication Date Title
US9915447B2 (en) Performance improvement of magnetocaloric cascades through optimized material arrangement
EP2948962A1 (fr) Amélioration de la performance de cascades magnétocaloriques par agencement de matériau optimisé
US8763407B2 (en) Magneto-caloric heat pump with the use of a cascade of magneto-caloric materials
JP5713889B2 (ja) 熱交換器用の連続気泡多孔性成型物
TW201001895A (en) Thermomagnetic generator
US9784483B2 (en) Use of rotating magnetic shielding system for a magnetic cooling device

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14743598

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2015554278

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112015017315

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 20157022734

Country of ref document: KR

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2014743598

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 112015017315

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20150720